Polymer ammunition having a projectile made by metal injection molding

Information

  • Patent Grant
  • 10591260
  • Patent Number
    10,591,260
  • Date Filed
    Thursday, September 24, 2015
    9 years ago
  • Date Issued
    Tuesday, March 17, 2020
    4 years ago
Abstract
The present invention provides an ammunition having a metal injection molded projectile and a polymer cartridge case comprising a polymer ammunition cartridge comprising a bottom portion and a top portion that enclose a propellant chamber, wherein the bottom portion comprises a primer recess in communication with a primer flash hole that extends into a propellant chamber and the top portion comprises a projectile aperture; a primer inserted into the primer flash hole aperture; a propellant at least partially filling the propellant chamber; and a metal injection molded projectile frictionally fitted in the projectile aperture, wherein the metal injection molded projectile comprises a nose extending essentially symmetrically to a shoulder, and an essentially cylindrical bearing surface extending from the shoulder to a base.
Description
TECHNICAL FIELD OF THE INVENTION

The present invention relates in general to the field of ammunition, specifically to compositions of matter and methods of making metal projectiles by metal injection molding.


STATEMENT OF FEDERALLY FUNDED RESEARCH

None.


INCORPORATION-BY-REFERENCE OF MATERIALS FILED ON COMPACT DISC

None.


BACKGROUND OF THE INVENTION

Without limiting the scope of the invention, its background is described in connection with projectiles made by injection molding for use in ammunition. Conventional ammunition projectiles for rifles and machine guns, as well as larger caliber weapons, are made from brass or lead that are machined, cast, molded or coated.


For example, U.S. Patent Application Publication No. 2003/0101891 entitled, “Jacketed bullet and methods of making the same” discloses a jacketed firearms projectile having a jacket thickness less than approximately 0.025 inches thick are described, where the density of the projectile core has been selected so that the jacketed projectile has a weight that is at least substantially the same as a reference firearms projectile, such as a lead projectile, having substantially the same size and shape. In one aspect, the projectile is a frangible projectile. In another aspect, the projectile is lead-free. In yet another aspect, the projectile is incorporated in a cartridge. Methods for forming the projectile and forming cartridges containing the projectiles are also disclosed.


U.S. Patent Application Publication No. 2009/0042057 entitled, “Metal composite article and method of manufacturing” discloses a composite metal article includes a higher melting point metal, a lower melting point alloy and at least one other metal with an intermediate melting point between that of the higher melting point metal and the lower melting point alloy. The at least one other metal is selected to aid in sinter-densification of the higher melting point metal in a temperature range above the liquid temperature of the lower melting point alloy and below the melting point of the at least one other metal.


U.S. Pat. No. 7,204,191 entitled, “Lead free, composite polymer based bullet and method of manufacturing” discloses a lead-free, composite polymer based bullet and cartridge case and methods of manufacturing the same, wherein the composite polymer material includes a tungsten metal powder, nylon 6/6, nylon 6, short glass fibers, as well as additives and stabilizers. The cartridge case includes a lip lock configured to matingly engage a cannelure formed along an outer circumferential surface of the bullet.


U.S. Pat. No. 7,392,746 entitled, “Bullet composition” discloses a lead free environmentally friendly ammunition which may be tailored within a range of compositions for specific uses, but generally comprises a mixture of metal powder and mineral filler in combination with a water soluble binder plastic resin and a lubricant. For hunting uses and other uses requiring high level accuracy the amount of metal powder is increased, for other uses where precision shooting is less important such as drug dosing of animals, less metal is used along with increased amounts of mineral filler. The bullets are accurate, and can be frangible.


Shortcomings of the known methods of producing projectiles for ammunition include the limitation of materials that can be used to form projectiles and the lengthy time for manufacturing.


BRIEF SUMMARY OF THE INVENTION

The present invention provides an ammunition having a metal injection molded projectile and a polymer cartridge case comprising a polymer ammunition cartridge comprising a bottom portion and a top portion that enclose a propellant chamber, wherein the bottom portion comprises a primer recess in communication with a primer flash hole that extends into a propellant chamber and the top portion comprises a projectile aperture; a primer inserted into the primer flash hole aperture; a propellant at least partially filling the propellant chamber; and a metal injection molded projectile frictionally fitted in the projectile aperture, wherein the metal injection molded projectile comprises a nose extending essentially symmetrically to a shoulder, and an essentially cylindrical bearing surface extending from the shoulder to a base.


The metal injection molded projectile may comprise stainless steel, brass, ceramic alloys, copper/cobalt/nickel/custom alloys, tungsten, tungsten carbide, carballoy, ferro-tungsten, titanium, copper, cobalt, nickel, uranium, depleted uranium, alumina oxide, zirconia and aluminum. The metal injection molded projectile may further comprise one or more cannelures formed on an outer circumferential surface of the essentially cylindrical bearing surface intermediate the shoulder and the base. The molded ammunition may have a nose with a frustoconical shape, a frustoconical shape with a cavity, a spritzer shape, a blunted shape, a rounded shape, or a flat shape; and the base may have a flat shape or a boattail shape. The molded ammunition may further include an outer coating placed over the projectile to form a metal jacketed projectile. The projectile may be a full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, armor piercing incendiary. The ammunition may be a 5.56 mm, 7.62 mm, 308, 338, 3030, 3006, 50 caliber, 45 caliber, 380 caliber, 38 caliber, 9 mm, 10 mm, 12.7 mm, 14.5 mm, 14.7 mm, 20 mm, 25 mm, 30 mm, 40 mm, 57 mm, 60 mm, 75 mm, 76 mm, 81 mm, 90 mm, 100 mm, 105 mm, 106 mm, 115 mm, 120 mm, 122 mm, 125 mm, 130 mm, 152 mm, 155 mm, 165 mm, 175 mm, 203 mm, 460 mm, 8 inch, or 4.2 inch.


The projectile may include stainless steel, brass, ceramic alloys, copper/cobalt/nickel/custom alloys, tungsten, tungsten carbide, carballoy, ferro-tungsten, titanium, copper, cobalt, nickel, uranium, depleted uranium, alumina oxide, zirconia and aluminum. More specifically, stainless steel, brass, metal alloys, ceramic alloys and even more specifically 102, 174, 201, 202, 300, 302, 303, 304, 308, 309, 316, 316L, 316Ti, 321, 405, 408, 409, 410, 415, 416, 416R, 420, 430, 439, 440, 446 or 601-665 grade stainless steel. The molded metal ammunition projectile may include 1, 2, 3, 4, 5 or more cannelures formed on an outer circumferential surface of the essentially cylindrical bearing surface intermediate the shoulder and the base. The nose may have a frustoconical shape, a frustoconical shape with a cavity to form a hollow point projectile; a spritzer shape; a blunted shape; or rounded shape. The molded metal ammunition projectile may be a full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, and armor piercing incendiary. The base has a flat shape or a boattail configuration. The molded metal ammunition projectile may include an outer coating placed over the projectile to form a metal jacketed projectile. The molded metal ammunition projectile may have a soft metal core, a high energy core, a high density core, a chemical core, or a combination thereof. The molded metal ammunition projectile may include a) 2-16% Ni; 10-20% Cr; 0-5% Mo; 0-0.6% C; 0-6.0% Cu; 0-0.5% Nb+Ta; 0-4.0% Mn; 0-2.0% Si and the balance Fe; b) 2-6% Ni; 13.5-19.5% Cr; 0-0.10% C; 1-7.0% Cu; 0.05-0.65% Nb+Ta; 0-3.0% Mn; 0-3.0% Si and the balance Fe; c) 3-5% Ni; 15.5-17.5% Cr; 0-0.07% C; 3-5.0% Cu; 0.15-0.45% Nb+Ta; 0-1.0% Mn; 0-1.0% Si and the balance Fe; d) 10-14% Ni; 16-18% Cr; 2-3% Mo; 0-0.03% C; 0-2% Mn; 0-1% Si and the balance Fe; e) 12-14% Cr; 0.15-0.4% C; 0-1% Mn; 0-1% Si and the balance Fe; f) 16-18% Cr; 0-0.05% C; 0-1% Mn; 0-1% Si and the balance Fe; g) 3-12% aluminum, 2-8% vanadium, 0.1-0.75% iron, 0.1-0.5% oxygen, and the remainder titanium; or h) about 6% aluminum, about 4% vanadium, about 0.25% iron, about 0.2% oxygen, and the remainder titanium.


The projectile may be 102, 174, 201, 202, 300, 302, 303, 304, 308, 309, 316, 316L, 316Ti, 321, 405, 408, 409, 410, 415, 416, 416R, 420, 430, 439, 440, 446 or 601-665 grade stainless steel. The projectile may be 2-16% Ni; 10-20% Cr; 0-5% Mo; 0-0.6% C; 0-6.0% Cu; 0-0.5% Nb+Ta; 0-4.0% Mn; 0-2.0% Si and the balance Fe; 2-6% Ni; 13.5-19.5% Cr; 0-0.10% C; 1-7.0% Cu; 0.05-0.65% Nb+Ta; 0-3.0% Mn; 0-3.0% Si and the balance Fe; 3-5% Ni; 15.5-17.5% Cr; 0-0.07% C; 3-5.0% Cu; 0.15-0.45% Nb+Ta; 0-1.0% Mn; 0-1.0% Si and the balance Fe; 10-14% Ni; 16-18% Cr; 2-3% Mo; 0-0.03% C; 0-2% Mn; 0-1% Si and the balance Fe; 12-14% Cr; 0.15-0.4% C; 0-1% Mn; 0-1% Si and the balance Fe; 16-18% Cr; 0-0.05% C; 0-1% Mn; 0-1% Si and the balance Fe; 3-12% aluminum, 2-8% vanadium, 0.1-0.75% iron, 0.1-0.5% oxygen, and the remainder titanium; or 6% aluminum, about 4% vanadium, about 0.25% iron, about 0.2% oxygen, and the remainder titanium.


The bottom portion, the top portion or both may be a nylon polymer or a fiber-reinforced polymeric composite. The bottom portion, the top portion or both may be between about 10 and about 70 wt % glass fiber fillers, mineral fillers, or mixtures thereof. The bottom portion and the top portion are welded or bonded together. The bottom portion, the top portion or both may be polyurethane prepolymer, cellulose, fluoro-polymer, ethylene inter-polymer alloy elastomer, ethylene vinyl acetate, nylon, polyether imide, polyester elastomer, polyester sulfone, polyphenyl amide, polypropylene, polyvinylidene fluoride or thermoset polyurea elastomer, acrylics, homopolymers, acetates, copolymers, acrylonitrile-butadinen-styrene, thermoplastic fluoro polymers, inomers, polyamides, polyamide-imides, polyacrylates, polyatherketones, polyaryl-sulfones, polybenzimidazoles, polycarbonates, polybutylene, terephthalates, polyether imides, polyether sulfones, thermoplastic polyimides, thermoplastic polyurethanes, polyphenylene sulfides, polyethylene, polypropylene, polysulfones, polyvinylchlorides, styrene acrylonitriles, polystyrenes, polyphenylene, ether blends, styrene maleic anhydrides, polycarbonates, allyls, aminos, cyanates, epoxies, phenolics, unsaturated polyesters, bismaleimides, polyurethanes, silicones, vinylesters, urethane hybrids, polyphenylsulfones, copolymers of polyphenylsulfones with polyethersulfones or polysulfones, copolymers of poly-phenylsulfones with siloxanes, blends of polyphenylsulfones with polysiloxanes, poly(etherimide-siloxane) copolymers, blends of polyetherimides and polysiloxanes, and blends of polyetherimides and poly(etherimide-siloxane) copolymers.





BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

For a more complete understanding of the features and advantages of the present invention, reference is now made to the detailed description of the invention along with the accompanying figures and in which:



FIG. 1a depicts an exploded view of the polymeric cartridge casing.



FIG. 1b depicts an exploded view of the polymeric cartridge casing.



FIG. 1c depicts a side, cross-sectional view of a polymeric cartridge case according to one embodiment of the present invention.



FIG. 2 is an image of a flat tip boattail projectile.



FIG. 3 is an image of a full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, armor piercing incendiary or a similar projectile having a pointed nose and a boattail configured end.



FIG. 4 is an image of a flat tip projectile with a flat base configured end.



FIG. 5 is an image of a full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, armor piercing incendiary or a similar projectile having a pointed nose and a flat base configured end.



FIG. 6 is an image of a boattail configured end projectile without a cannelure.



FIG. 7 is an image of a flat base configured end projectile without a cannelure.



FIG. 8 is an image of a boattail configured end projectile with rounded nose.



FIG. 9 is an image of a flat base projectile with a rounded nose.



FIG. 10 is an image of a flat base configured end projectile having multiple cannelures.



FIG. 11 is an image of a boattail configured end projectile having multiple cannelures.



FIG. 12 is a cut away image of a jacketed spritzer projectile.



FIG. 13 is a cut away image of a jacketed projectile.



FIG. 14 is a cut away image of a jacketed projectile.



FIG. 15 is a cut away image of a jacketed projectile.



FIG. 16 is a cut away image of a jacketed projectile.



FIG. 17 is a cut away image of a jacketed projectile.



FIG. 18 is a cut away image of a jacketed projectile.



FIGS. 19a-19s are images of a cut away image of different projectile types.



FIGS. 20a-20v are images of different embodiments of the projectiles of the present invention.



FIG. 21 depicts a side, cross-sectional view of a polymeric cartridge case having a diffuser according to one embodiment of the present invention;





DETAILED DESCRIPTION OF THE INVENTION

While the making and using of various embodiments of the present invention are discussed in detail below, it should be appreciated that the present invention provides many applicable inventive concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed herein are merely illustrative of specific ways to make and use the invention and do not delimit the scope of the invention.


As used herein the term “shell,” “bullet” and “projectile” are used interchangeably and denote a projectile that is positioned in an ammunition cartridge until it is expelled from a gun, rifle, or the like and propelled by detonation of a powdered chemical propellant or other propellant that may be non-powdered, solid, gaseous or gelatin. And includes payload-carrying projectiles contains shot, an explosive or other filling, though modern usage sometimes includes large solid projectiles properly termed shot (AP, APCR, APCNR, APDS, APFSDS and proof shot).


As used herein AP denotes Armor Piercing (has a steel or other hard metal core Military); API denotes Armor Piercing Incendiary (Military); APT denotes Armor Piercing Tracer (Military); APTI denotes Armor Piercing Tracer Incendiary (Military); BBWC denotes Bevel Base Wad Cutter; BT denotes Boat Tail; BTBT denotes Ballistic Tip Boat Tail; BTHP denotes Boat Tail Hollow Point; BTSP denotes Boat Tail Soft Point; FEB denotes Fully Encased Bullet; FMC denotes Full Metal Case; FMJ denotes Full Metal Jacket; FMJBT denotes Full Metal Jacket Boat Tail; FMJFN denotes Full Metal Jacket Flat Nose; FMJFP denotes Full Metal Jacket Flat Point; FMJRN denotes Full Metal Jacket Round Nose; FMJRP denotes Full Metal Jacket Round Point; FMJSWC denotes Full Metal Jacket Semi-Wad Cutter; FMJTC denotes Full Metal Jacket Truncated Cone; FN denotes Flat Nose; FNEB denotes Flat Nose Enclosed Base; FNSP denotes Flat Nose Soft Point; FP denotes Flat Point; HE denotes High Energy or high explosive; HP denotes Hollow Point; HPBT denotes Hollow Point Boat Tail; J denotes Jacketed; JFP denotes Jacketed Flat Point; JHP denotes Jacketed Hollow Point; JHPBT denotes Jacketed Hollow Point Boat Tail; JSP denotes Jacketed Soft Point; JSPF denotes Jacketed Soft Point Flat; L denotes Lead; LFN denotes Lead Flat Nose; LFP denotes Lead Flat Point; LHP denotes Lead Hollow Point; LRN denotes Lead Round Nose; LSWC denotes Lead Semi-Wad Cutter; LSWC-GC denotes Lead Semi-Wad Cutter, Gas Checked; LTC denotes Lead Truncated Cone; LWC denotes Lead Wad Cutter; RN denotes Round Nose; RNFP denotes Round Nose Flat Point; RNL denotes Round Nosed Lead; RNSP denotes Round Nose Soft Point; SJHP denotes Semi Jacketed Hollow Point, Soft Jacket Hollow Point; SJSP denotes Soft Jacket Soft Point; SLAP denotes Saboted Light Armor Penetrating; SPTZ denotes Spitzer; Sub denotes Subsonic; SWC denotes Semi Wad Cutter; TC denotes Truncated Cone; TCMJ denotes Truncated Cone Metal Jacket; WC denotes Wad Cutter; AP denotes Armor piercing; API denotes Armor piercing incendiary; APIT denotes Armor piercing incendiary tracer; APT denotes Armor piercing tracer; CA denotes Copper Alloy; CAL denotes Caliber; GMCS denotes Gilding metal clad steel; HEAT denotes High-explosive anti-tank; HEI denotes High explosive incendiary; HEIT denotes High explosive, incendiary, tracer; RAP denotes Rocket Assisted Projectile; and TPT Target practice, tracer.


Reliable projectile manufacture requires uniformity from one projectile to the next in order to obtain consistent ballistic performance. In addition to projectile shape, other considerations, proper projectile seating and bullet-to-casing fit is required. In this manner, a desired pressure develops within the casing during firing prior to bullet and casing separation. Historically, projectile employ a cannelure, which is a slight annular depression formed in a surface of the projectile at a location determined to be the optimal seating depth for the bullet. In this manner, a visual inspection of a cartridge could determine whether or not the bullet is seated at the proper depth. Once the bullet is inserted into the casing to the proper depth, one of two standard procedures is incorporated to lock the bullet in its proper location. One method is the crimping of the entire end of the casing into the cannelure. A second method does not crimp the casing end; rather the bullet is pressure fitted into the casing, another method employs adhesive bonding to join the bullet to the casing.



FIG. 1a depicts an exploded view of the polymeric cartridge casing having an over-molded primer insert. A cartridge casing 10 suitable for use with rifles is shown manufactured with a casing 12 showing a propellant chamber 14 with a projectile 56 inserted into the forward end opening 16. The cartridge casing 12 has a substantially cylindrical open-ended bullet-end component 18 extending from the forward end opening 16 rearward to the opposite end 20. The forward end of bullet-end component 18 has a shoulder 24 forming a chamber neck 26. The bullet-end component 18 may be formed with coupling end 22 formed on substantially cylindrical opposite end 20 or formed as a separate component. These and other suitable methods for securing individual pieces of a two-piece or multi-piece cartridge casing are useful in the practice of the present invention. Coupling end 22 is shown as a male element, but may also be configured as a female element in alternate embodiments of the invention. In some embodiments the forward end of bullet-end component 18 includes the forward end opening 16 without a shoulder 24 forming chamber neck 26. The bullet-end component typically has a wall thickness between about 0.003 and about 0.200 inches and more preferably between about 0.005 and more preferably between about 0.150 inches about 0.010 and about 0.050 inches. The middle body component 28 is substantially cylindrical and connects the forward end of bullet-end component 18 to the substantially cylindrical opposite end 20 and forms the propellant chamber 14. The substantially cylindrical opposite end 20 includes a substantially cylindrical insert 32 that partially seals the propellant chamber 14. In a two piece design as shown in FIG. 1a the substantially cylindrical insert 32 is molded into the middle body component 28. The substantially cylindrical insert 32 includes a bottom surface (not shown) located in the propellant chamber 14 that is opposite a top surface (not shown). The substantially cylindrical insert 32 includes a primer recess (not shown) positioned in the top surface (not shown) extending toward the bottom surface (not shown) with a primer flash hole aperture (not shown) is located in the primer recess (not shown) and extends through the bottom surface (not shown) into the propellant chamber 14 to combust the propellant in the propellant chamber 14. A primer (not shown) is located in the primer recess (not shown) and extends through the bottom surface (not shown) into the propellant chamber 14. In some embodiments the coupling end 22 extends the polymer through the primer flash hole aperture (not shown) to form the primer flash hole (not shown) while retaining a passage from the top surface (not shown) through the bottom surface (not shown) and into the propellant chamber 14 to provide support and protection about the primer flash hole aperture (not shown). In other embodiments the coupling end 22 extends the polymer up to but not into the primer flash hole aperture (not shown) to form the primer flash hole (not shown) while retaining a passage from the top surface (not shown) through the bottom surface (not shown) and into the propellant chamber 14. The bullet-end 18, middle body 28 and bottom surface (not shown) define the interior of propellant chamber 14 in which the powder charge (not shown) is contained. The interior volume of propellant chamber 14 may be varied to provide the volume necessary for complete filling of the propellant chamber 14 by the propellant chosen so that a simplified volumetric measure of propellant can be utilized when loading the cartridge. The bullet-end and bullet components can then be welded or bonded together using solvent, adhesive, sintering, brazing, soldering, spin-welding, vibration-welding, ultrasonic-welding or laser-welding techniques. The welding or bonding increases the joint strength so the casing can be extracted from the hot gun casing after firing at the cook-off temperature. An optional first and second annular grooves (cannelures) may be provided in the bullet-end in the interlock surface of the male coupling element to provide a snap-fit between the two components. The cannelures formed in a surface of the bullet at a location determined to be the optimal seating depth for the bullet. Once the bullet is inserted into the casing to the proper depth to lock the bullet in its proper location. One method is the crimping of the entire end of the casing into the cannelures. The bullet-end and middle body components can then be welded or bonded together using solvent, adhesive, sintering, brazing, soldering, spin-welding, vibration-welding, ultrasonic-welding or laser-welding techniques. The welding or bonding increases the joint strength so the casing can be extracted from the hot gun casing after firing at the cook-off temperature.



FIG. 1b depicts an exploded view of a three piece polymeric cartridge casing. A cartridge casing 10 suitable for use with rifles is shown manufactured with a casing 12 showing a propellant chamber 14 with a projectile 56 inserted into the forward end opening 16. The cartridge casing 12 has a substantially cylindrical open-ended bullet-end component 18 extending from the forward end opening 16 rearward to the opposite end 20. The forward end of bullet-end component 18 has a shoulder 24 forming a chamber neck 26. The bullet-end component 18 may be formed with coupling end 22 formed on substantially cylindrical opposite end 20 or formed as a separate component. These and other suitable methods for securing individual pieces of the multi-piece cartridge casing are useful in the practice of the present invention. Coupling end 22 is shown as a male element, but may also be configured as a female element in alternate embodiments of the invention. In some embodiments the forward end of bullet-end component 18 includes the forward end opening 16 without a shoulder 24 forming chamber neck 26. The bullet-end component typically has a wall thickness between about 0.003 and about 0.200 inches and more preferably between about 0.005 and more preferably between about 0.150 inches about 0.010 and about 0.050 inches. The middle body component 28 is substantially cylindrical and connects the forward end of bullet-end component 18 to the substantially cylindrical opposite end 20 and forms the propellant chamber 14. The substantially cylindrical opposite end 20 includes a substantially cylindrical insert 32 that partially seals the propellant chamber 14. The substantially cylindrical insert 32 includes a bottom surface 34 located in the propellant chamber 14 that is opposite a top surface (not shown). The substantially cylindrical insert 32 includes a primer recess (not shown) positioned in the top surface (not shown) extending toward the bottom surface 34 with a primer flash hole aperture (not shown) is located in the primer recess (not shown) and extends through the bottom surface 34 into the propellant chamber 14 to combust the propellant in the propellant chamber 14. A primer (not shown) is located in the primer recess (not shown) and extends through the bottom surface 34 into the propellant chamber 14. When molded the coupling end 22 extends the polymer through the primer flash hole aperture (not shown) to form the primer flash hole (not shown) while retaining a passage from the top surface (not shown) through the bottom surface 34 and into the propellant chamber 14 to provide support and protection about the primer flash hole aperture (not shown). In other embodiments the coupling end 22 extends the polymer up to but not into the primer flash hole aperture (not shown) to form the primer flash hole (not shown) while retaining a passage from the top surface (not shown) through the bottom surface 34 and into the propellant chamber 14. The bullet-end 18, middle body 28 and bottom surface 34 define the interior of propellant chamber 14 in which the powder charge (not shown) is contained. The interior volume of propellant chamber 14 may be varied to provide the volume necessary for complete filling of the propellant chamber 14 by the propellant chosen so that a simplified volumetric measure of propellant can be utilized when loading the cartridge. The bullet-end and bullet components can then be welded or bonded together using solvent, adhesive, sintering, brazing, soldering, spin-welding, vibration-welding, ultrasonic-welding or laser-welding techniques. The welding or bonding increases the joint strength so the casing can be extracted from the hot gun casing after firing at the cook-off temperature. An optional first and second annular groove (first and second cannelures) may be provided in the bullet-end in the interlock surface of the male coupling element to provide a snap-fit between the two components. The cannelures formed in a surface of the bullet at a location determined to be the optimal seating depth for the bullet. Once the bullet is inserted into the casing to the proper depth to lock the bullet in its proper location. One method is the crimping of the entire end of the casing into the cannelures. The bullet-end and middle body components can then be welded or bonded together using solvent, adhesive, sintering, brazing, soldering, spin-welding, vibration-welding, ultrasonic-welding or laser-welding techniques. The welding or bonding increases the joint strength so the casing can be extracted from the hot gun casing after firing at the cook-off temperature.


Although FIGS. 1a and 1b describe a polymer cartridge the present invention also applies to metal cartridges (e.g., made by metal injection molding, casting, machining, forging, 3-D printing, and any other mechanism used to make a cartridge) and hybrid cartridges that include a cartridge made from a combination of polymers and metal or any combination of polymers or copolymers and metals and/or alloys. The present invention may also be used in a traditional metal cartridge casing. The metal cartridge casing includes a metal casing having a propellant chamber with a forward end opening for insertion of a projectile. The forward end opening may include a shoulder forming chamber neck. The opposite end of the forward end opening in the metal cartridge casing includes a flange around the parameter and a primer recess with a primer flash aperture formed therein for ease of insertion of the primer (not shown). A primer flash hole aperture is located in the primer recess and extends into the propellant chamber to combust the propellant in the propellant chamber.



FIG. 1c depicts a side, cross-sectional view of a polymeric cartridge case according to one embodiment of the present invention. A cartridge 10 suitable for use with high velocity rifles is shown manufactured with a polymer casing 12 showing a propellant chamber 14 with projectile (not shown) inserted into the forward end opening 16. The polymer casing 12 has a substantially cylindrical open-ended polymeric bullet-end 18 extending from forward end opening 16 rearward to opposite end 20. The bullet-end component 18 may be formed with the coupling end 22 formed on the end 20. The coupling end 22 is shown as a female element, but may also be configured as a male element in alternate embodiments of the invention. The forward end of bullet-end component 18 has a shoulder 24 forming chamber neck 26. The bullet-end component typically has a wall thickness between about 0.003 and about 0.200 inches and more preferably between about 0.005 and more preferably between about 0.150 inches about 0.010 and about 0.050 inches. The middle body component 28 is connected to a substantially cylindrical coupling element 30 of the substantially cylindrical insert 32. The coupling element 30, as shown may be configured as a male element, however, all combinations of male and female configurations is acceptable for the coupling elements 30 and the coupling end 22 in alternate embodiments of the invention. The coupling end 22 of bullet-end component 18 fits about and engages the coupling element 30 of a substantially cylindrical insert 32. The substantially cylindrical insert 32 includes a substantially cylindrical coupling element 30 extending from a bottom surface 34 that is opposite a top surface 36. Located in the top surface 36 is a primer recess 38 that extends toward the bottom surface 34. A primer flash hole 40 extends through the bottom surface 34 into the propellant chamber 14. A groove 51 is positioned around the primer flash hole 40 in the primer flash hole 40. The coupling end 22 extends the polymer through the primer flash hole 40 to form an aperture coating 42 while retaining a passage from the top surface 36 through the bottom surface 34 and into the propellant chamber 14 to provide support and protection about the primer flash hole 40. When contacted the coupling end 22 interlocks with the substantially cylindrical coupling element 30, through the coupling element 30 that extends with a taper to a smaller diameter at the tip 44 to form a physical interlock between substantially cylindrical insert 32 and middle body component 28. The polymer casing 12 also has a substantially cylindrical open-ended middle body component 28. The middle body component extends from a forward end opening 16 to the coupling element 22. The middle body component typically has a wall thickness between about 0.003 and about 0.200 inches and more preferably between about 0.005 and more preferably between about 0.150 inches about 0.010 and about 0.050 inches. The bullet-end 16, middle body 18 and bottom surface 34 define the interior of propellant chamber 14 in which the powder charge (not shown) is contained. The interior volume of propellant chamber 14 may be varied to provide the volume necessary for complete filling of the chamber 14 by the propellant chosen so that a simplified volumetric measure of propellant can be utilized when loading the cartridge. Either a particulate or consolidated propellant can be used. The substantially cylindrical insert 32 also has a flange 46 cut therein and a primer recess 38 formed therein for ease of insertion of the primer (not shown). The primer recess 38 is sized so as to receive the primer (not shown) in an interference fit during assembly. A primer flash hole 40 communicates through the bottom surface 34 of substantially cylindrical insert 32 into the propellant chamber 14 so that upon detonation of primer (not shown) the powder in propellant chamber 14 will be ignited. The bullet-end and middle body components can then be welded or bonded together using solvent, adhesive, spin-welding, vibration-welding, ultrasonic-welding or laser-welding techniques. The welding or bonding increases the joint strength so the casing can be extracted from the hot gun casing after firing at the cook-off temperature.



FIG. 2 is a general image of a bullet or projectile. For the purpose of description the general projectile shape is shown below as the projectile 50. The projectile 50 of the present invention includes all shapes and calibers. The present invention is not limited to the described caliber and is believed to be applicable to other calibers as well. This includes various small and medium caliber munitions, including 5.56 mm, 7.62 mm, 308, 338, 3030, 3006, and .50 caliber ammunition cartridges, as well as medium/small caliber ammunition such as 380 caliber, 38 caliber, 9 mm, 10 mm and military style ammunition including 12.7 mm, 14.5 mm, 14.7 mm, 20 mm, 25 mm, 30 mm, 40 mm, 57 mm, 60 mm, 75 mm, 76 mm, 81 mm, 90 mm, 100 mm, 105 mm, 106 mm, 115 mm, 120 mm, 122 mm, 125 mm, 130 mm, 152 mm, 155 mm, 165 mm, 175 mm, 203 mm, 460 mm, 8 inch, 4.2 inch, 45 caliber and the like. Thus, the present invention is also applicable to the sporting goods industry for use by hunters and target shooters as well as military use.


The projectile 50 may have any profile but generally has an aerodynamic streamlined shape at the head and at the tail, e.g., spritzer, flat base spritzer, boat tail spritzer, tapered-heel spritzer, rounded nose, rounded nose flat base, rounded nose boat tail, rounded nose tapered-heel, flat nose, flat nose flat base, flat nose boat tail, flat nose tapered-heel, hollow point, hollow point boat tail, hollow point flat base, hollow point tapered-heel and so on. Although any head shape can be used, more common shapes include spritzer shape, round, conical, frustoconical, blunted, wadcutter, or hollow point, and the more common tail shape includes flat base, boat tail, tapered-heel expanded bases or banded bases. The bullets of the present invention may have any profile and weight dictated by the particular application. For example, the method and bullets of the present invention may be used in full metal jacket metal cased and full metal jacket both refer to bullets with a metal coating that covers all of, or all but the base of a bullet; metal cased (e.g., as used by REMINGTON® to refer to their full metal jacketed bullets); hollow point bullets have a concave shaped tip that facilitates rapid expansion of the round upon impact; boat tail bullets have a streamlined base to facilitate better aerodynamics; boat tail hollow point; full metal jacketed boat tail; point jacketed hollow point bullets are similar in design to regular hollow point bullets, but have a copper jacket that normally covers everything but the hollowed portion of the round; jacketed flat point rounds have a flat area of exposed lead at the tip; jacketed soft point bullets usually have a spire pointed tip of exposed lead. Jacketed spitzer point can refer to a jacketed spitzer point; spitzer meaning a sharply pointed bullet; jacketed round nose jacketed round nose bullets split the difference between jacketed flat point and jacketed spitzer point bullets and have a rounded tip of exposed lead boat tail soft point sometimes the letters in the acronyms are switched, so boat tail soft point may also be abbreviated as soft point boat tail. Expanding full metal jacketed rounds appear as and feed like a regular full metal jacket bullet, but have a construction that allows the case to collapse and the bullet to flatten upon impact. Wad cutter designs often appear to be nothing more than a cylinder, usually with a hollow base which is used in target practice to punch neat holes in the paper, rather than the ragged holes produced by more rounded designs. Semi wad cutter bullets have a rounded nose that comes down to a cylinder that is slightly larger than the rounded section, giving the bullet a more aerodynamic shape while allowing it to punch clean holes in paper targets. Rounded flat point bullets have a flat tip that is smaller than the bullet diameter and rounded shoulders. Armor piercing ammunition can have bullets with a variety of shapes, though in general they are spire pointed and full metal jacketed rounds that have a strong core designed to penetrate armor. Armor piercing incendiary ammunition has the same penetrating abilities of armor piercing bullets, but with the added function of bursting into an intense flame upon impact. Frangible ammunition is available under a number of trademarks; notably MAGSAFE®, GLASER®, and SINTERFIRE® and are characterized by a design that facilitates the rapid breakup of the bullet upon impact, thus, reducing the chances of over-penetration or a ricochet. Exploding ammunition includes delayed and aerial/above ground exploding ammunition plus ammunition that can penetrate an objective and have a delay before exploding after penetrating. Also included are jacketed designs where the core material is a very hard, high-density metal such as tungsten, tungsten carbide, depleted uranium, or steel.



FIG. 2 is an image of a flat nose boattail projectile. The projectile 50 includes an ogive 52 that extends from the nose 54 (flat tip) to the shoulder 56. The distance from the nose 54 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 54 is the bearing surface 60. The bearing surface 60 may be extended with a boattail 62, which tappers to heal 64 that curves to form a base 66. An optional cannelure 68 may be positioned on the bearing surface 60 below the shoulder 56.



FIG. 3 is an image of an full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, armor piercing incendiary or a similar projectile 50 having a pointed nose 55 and a boattail 62. The ogive 52 extends from the pointed nose 55 (pointed tip) to the shoulder 56. The distance from the pointed nose 55 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the pointed nose 55 is the bearing surface 60. The bearing surface 60 may be extended with a boattail 62, which tappers to heal 64 that curves to form a base 66. An optional cannelure 68 may be positioned on the bearing surface 60 below the shoulder 56.



FIG. 4 is an image of a flat nose flat base projectile. The projectile 50 includes an ogive 52 that extends from the nose 54 (flat tip) to the shoulder 56. The distance from the nose 54 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 54 is the bearing surface 60. The bearing surface 60 ends with a flat base 70. An optional cannelure 68 may be positioned on the bearing surface 60 below the shoulder 56.



FIG. 5 is an image of an full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, armor piercing incendiary or a similar projectile 50 having a pointed nose 55 and a flat base 70. The ogive 52 extends from the pointed nose 55 (pointed tip) to the shoulder 56. The distance from the pointed nose 55 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the pointed nose 55 is the bearing surface 60. The bearing surface 60 ends with a flat base 70. An optional cannelure 68 may be positioned on the bearing surface 60 below the shoulder 56.



FIG. 6 is an image of a boattail projectile without a cannelure. The projectile 50 includes an ogive 52 that extends from the nose 54 to the shoulder 56. The distance from the nose 54 (blunt or pointed (not shown)) to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 54 is the bearing surface 60. The bearing surface 60 may be extended with a boattail 62, which tappers to heal 64 that curves to form a base 66.



FIG. 7 is an image of a flat base projectile without a cannelure. The ogive 52 extends from the nose 54 (blunt or pointed (not shown)) to the shoulder 56. The distance from the nose 54 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 54 is the bearing surface 60. The bearing surface 60 may be extended to flat base 70.



FIG. 8 is an image of a boattail projectile 50 with rounded nose. The projectile 50 includes an ogive 52 that extends from the rounded nose 72 to the shoulder 56. The distance from the rounded nose 72 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 72 is the bearing surface 60. The bearing surface 60 may be extended with a boattail 62, which tappers to heal 64 that curves to form a base 66. An optional cannelure 68 may be positioned on the bearing surface 60 below the shoulder 56.



FIG. 9 is an image of a flat base projectile 50 with a rounded nose 72. The ogive 52 extends from the rounded nose 72 to the shoulder 56. The distance from the rounded nose 72 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the rounded nose 72 is the bearing surface 60. The bearing surface 60 may be extended to flat base 70. An optional cannelure 68 may be positioned on the bearing surface 60 below the shoulder 56.



FIG. 10 is an image of a flat base projectile 50 having multiple cannelures 68a-68c. The ogive 52 extends from the nose 54 to the shoulder 56. The distance from the nose 54 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 54 is the bearing surface 60. The bearing surface 60 terminates in a flat base 70. The cannelures 68a-68c may be positioned on the bearing surface 60 below the shoulder 56. Although 1 and 3 cannelures 68a-68c are shown as representative examples, any number of cannelures may be used, e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or more cannelures having various thicknesses and depths.



FIG. 11 is an image of a boattail projectile 50 having multiple cannelures 68a-68c. The projectile 50 includes an ogive 52 that extends from the nose 54 to the shoulder 56. The distance from the nose 54 to the shoulder 56 is the head or ogive distance 58, with the distance from the shoulder 56 extending away from the nose 54 is the bearing surface 60. The bearing surface 60 may be extended with a boattail 62, which tappers to heal 64 that curves to form a base 66. Although 1 and 3 cannelures 68a-68c are shown as representative examples, any number of cannelures may be used, e.g., 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or more cannelures having various thicknesses and depths.


These projectiles described herein may be made using a metal injection molding process. The metal injection molding process, which generally involves mixing fine metal powders with binders to form a feedstock that is injection molded into a closed mold, may be used to form a substantially cylindrical insert. After ejection from the mold, the binders are chemically or thermally removed from the substantially cylindrical insert so that the part can be sintered to high density. During the sintering process, the individual metal particles metallurgically bond together as material diffusion occurs to remove most of the porosity left by the removal of the binder.



FIG. 12 is a cut away image of a jacketed spritzer projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 is a metal jacket covering a metal core 74 that includes a spiral ridge 76a, 76b and 76c (alternatively it may be a spiral groove). In addition, at least a portion of the ogive 52 of the outer surface 73 may be of a softer metal to allow deformation at impact allowing the metal core 74 to penetrate the target.



FIG. 13 is a cut away image of a jacketed projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 is a metal jacket covering a metal core 74 that encompasses a central projectile 78 having ridges or fins 80a, 80b and 80c that terminate at a tip 82 (alternatively the central projectile 78 may have spiral grooves or ridges). In addition, at least a portion of the ogive 52 of the outer surface 73 may be of a softer metal to allow deformation at impact allowing the metal core 74 to penetrate the target.



FIG. 14 is a cut away image of a jacketed projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 is a metal jacket covering a metal core 74 that includes longitudinal ridges 76a, 76b and 76c (alternatively it may be longitudinal grooves). In addition, at least a portion of the ogive 52 of the outer surface 73 may be of a softer metal to allow deformation at impact allowing the metal core 74 to penetrate the target.



FIG. 15 is a cut away image of a jacketed projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 is a jacket covering a metal core 74 that encompasses a central projectile 78 that terminate at a tip 82. In addition, at least a portion of the ogive 52 of the outer surface 73 may be of a softer metal to allow deformation at impact allowing the metal core 74 to penetrate the target.



FIG. 16 is a cut away image of a jacketed projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 is a jacket covering a metal core 74 that encompasses a central region 84 that terminate at a tip 82. The central region 84 may contain a flammable composition that is ignited by ignition source 86.



FIG. 17 is a cut away image of a jacketed projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 is a jacket covering a metal core 74 that encompasses a central region 84 that terminate at a tip 82. The central region 84 may contain pelleted materials 88 that may be ejected upon impact. In addition, at least a portion of the ogive 52 of the outer surface 73 may be of a softer metal to allow deformation at impact allowing more efficient ejection of the pelleted materials 88.



FIG. 18 is a cut away image of a jacketed projectile. The projectile 50 includes a nose 55 that extends to a shoulder 56. A bearing surface 60 extends from the shoulder 56 to the base 70. The outer surface 73 of the projectile 50 partially covers a central projectile 78 to allow the central projectile 78 to penetrate the target.



FIGS. 19a-19s are images of a cut away image of different projectile types. FIG. 19a is an image of a projectile 50 that is an armor piercing tracer having a boattail 62 configured end, a tracer element 90 and solid shot 92. FIG. 19b is an image of a projectile 50 that is an armor piercing high explosive projectile having a base fuse 94 and high explosive charge 96. FIG. 19c is an image of a projectile 50 that is an armor piercing high explosive projectile having a base fuse 94, high explosive charge 96 and an armor piercing shot 98 and armor piercing cap 100. FIG. 19d is an image of a projectile 50 that is a heat shaped charge projectile having a fuse 102, void space 104 and cavity 106 and a high explosive charge 96 surrounding a flash tube 108 connecting the fuse 102 and the booster 110. FIG. 19e is an image of a projectile 50 that is an anti-concrete projectile having a ballistic cap 112 housing a blunt nose 114 connected to a base fuse 94 and high explosive charge 96. FIG. 19f is an image of a projectile 50 that is a high-explosive and high capacity projectile having a high explosive 50 and a booster 110. FIG. 19g is an image of a projectile 50 that is a shrapnel projectile that includes a shrapnel projectile having a base ejection mechanism 116 and a shrapnel 118. FIG. 19h is an image of a projectile 50 that is a canister projectile having shot 120 disposed in the canister. FIG. 19i is an image of a projectile 50 that is an illuminating projectile that includes an ejection charge 122 and an illumination element 124 connected to a parachute 126 connected to a suspending cord 128. FIG. 19j is an image of a projectile 50 that is an armor piercing cap ballistic cap projectile having a base fuse 94, high explosive charge 96 and an armor piercing shot 98, armor piercing cap 100 and ballistic cap 112. FIG. 19k is an image of a projectile 50 that is a high velocity armor piercing projectile having a tracer element 90 and a light metal casing 130 over a hard dense core 132. FIG. 19l is an image of a projectile 50 that is a high velocity armor piercing arrowhead projectile having a tracer element 90 and a light metal casing 130 over a hard dense core 132. FIG. 19m is an image of a projectile 50 that is a high explosive projectile having a fuse 102, high explosive charge 96, a tracer element 90 and a rotation band 134. FIG. 19n is an image of a projectile 50 that is a high explosive chemical projectile having one or more chemicals 136 with a high explosive charge 96 and a high explosive burster 140, and a centering band 138. FIG. 19o is an image of a projectile 50 that is a smoke projectile having one or more smoke compositions 142 and a high explosive burster 140. FIG. 19p is an image of a projectile 50 that is a discarding sabot projectile having a hard core 132 covered by a outer shell 144 and a discardable carrier 146. FIG. 19q is an image of a projectile 50 that is a tapered bore projectile having a bourrelet 148 and a rotating flange 150. FIG. 19r is an image of a projectile 50 that is a rocket assisted projectile having a high explosive charge 96 and a rocket propellant 152 with venturis 154. FIG. 19s is an image of a projectile 50 that is a discarding sabot projectile having a hard core 132 with one or more fins 156 and a discardable carrier 146.



FIGS. 20a-20v are images of various projectiles of the present invention. FIG. 20a is a perspective view of a round point projectile. FIGS. 20b-20e are side views of a round point projectile. FIGS. 20f-20g are perspectives view of a blunt point projectile. FIGS. 20h-20k are side views of a blunt point projectile. FIG. 20l is a perspective view of a flat point projectile. FIGS. 20m-20p are side views of a flat point projectile. FIG. 20q is a cut through view of a hollow point projectile having relief grooves. FIG. 20r is a top view of a hollow point projectile having relief grooves. FIG. 20t is a perspective view of a hollow point projectile. FIGS. 20s, 20u and 20v are perspective views of one embodiment of a projectile of the present invention.



FIG. 21 depicts a side, cross-sectional view of a polymeric cartridge case having a diffuser according to one embodiment of the present invention. The diffuser 50 is a device that is used to divert the affects of the primer off of the polymer and directing it to the flash hole. The affects being the impact from igniting the primer as far as pressure and heat. A cartridge 10 suitable for use with high velocity rifles is shown manufactured with a polymer casing 12 showing a powder chamber 14 with projectile (not shown) inserted into the forward end opening 16. Polymer casing 12 has a substantially cylindrical open-ended polymeric bullet-end 18 extending from forward end opening 16 rearward to the opposite end 20. The bullet-end component 18 may be formed with coupling end 22 formed on end 20. Coupling end 22 is shown as a female element, but may also be configured as a male element in alternate embodiments of the invention. The forward end of bullet-end component 18 has a shoulder 24 forming chamber neck 26.


The middle body component 28 is connected to a substantially cylindrical coupling element 30 of the substantially cylindrical insert 32. Coupling element 30, as shown may be configured as a male element, however, all combinations of male and female configurations is acceptable for coupling elements 30 and coupling end 22 in alternate embodiments of the invention. Coupling end 22 of bullet-end component 18 fits about and engages coupling element 30 of a substantially cylindrical insert 32. The substantially cylindrical insert 32 includes a substantially cylindrical coupling element 30 extending from a bottom surface 34 that is opposite a top surface 36. Located in the top surface 36 is a primer recess 38 that extends toward the bottom surface 34. A primer flash hole 40 is located in the primer flash hole 40 and extends through the bottom surface 34 into the powder chamber 14. The coupling end 22 extends the polymer through the primer flash hole 40 to form an aperture coating 42 while retaining a passage from the top surface 36 through the bottom surface 34 and into the powder chamber 14 to provides support and protection about the primer flash hole 40. When contacted the coupling end 22 interlocks with the substantially cylindrical coupling element 30, through the coupling element 30 that extends with a taper to a smaller diameter at the tip 44 to form a physical interlock between substantially cylindrical insert 32 and middle body component 28. Polymer casing 12 also has a substantially cylindrical open-ended middle body component 28. The middle body component extends from a forward end opening 16 to coupling element 22. Located in the top surface 36 is a primer recess 38 that extends toward the bottom surface 34 with a diffuser 50 positioned in the primer recess 38. The diffuser 50 includes a diffuser aperture 52 that aligns with the primer flash hole 40. The diffuser 50 is a device that is used to divert the affects of the primer (not shown) off of the polymer. The affects being the impact from igniting the primer as far as pressure and heat to divert the energy of the primer off of the polymer and directing it to the flash hole.


The present invention also provides MIMs of spin-stabilized projectiles. Spinning a projectile promotes flight stability. Spinning is obtained by firing the projectiles through a rifled tube. The projectile engages the rifling by means of a rotating band normally made of copper. The rotating band is engaged by the lands and grooves. At a nominal muzzle velocity of 2800 feet per second, spin rates on the order of 250 revolutions per second are encountered. Spin-stabilized projectiles are full bore (flush with the bore walls) and are limited approximately to a 5:1 length-to-diameter ratio. They perform very well at relatively low trajectories (less than 45 quadrant elevation). In high trajectory applications they tend to overstabilize (maintain the angle at which they were fired) and, therefore, do not follow the trajectory satisfactorily so other rations may be used to account for this.


The present invention also provides MIMs of fin-stabilized projectiles to obtain stability through the use of fins located at the aft end of the projectile. Normally, four to six fins are employed. Additional stability is obtained by imparting some spin (approximately 20 revolutions/second) to the projectile by canting the leading edge of the fins. Fin-stabilized projectiles are very often subcaliber. A sabot, wood or metal fitted around the projectile, is used to center the projectile in the bore and provide a gas seal. Such projectiles vary from 10:1 to 15:1 in length-to-diameter ratio. Fin-stabilized projectiles are advantageous because they follow the trajectory very well at high-launch angles, and they can be designed with very low drag thereby increasing range and/or terminal velocity.


The present invention also provides MIMs of rocket-assisted projectiles to extend the range over standard gun systems and to allow for lighter mount and barrel design and reduce excessive muzzle flash and smoke by reducing the recoil and setback forces of standard gun systems. Since the ranges are different, the above two objectives represent opposite approaches in the development of rocket-assisted projectiles. Normally, one or the other establishes the performance of the rocket-assisted projectile under development although some compromise in the two approaches may be established by the design objectives.


The raw materials for metal injection molding are metal powders and a thermoplastic binder. There are at least two Binders included in the blend, a primary binder and a secondary binder. This blended powder mix is worked into the plasticized binder at elevated temperature in a kneader or shear roll extruder. The intermediate product is the so-called feedstock. It is usually granulated with granule sizes of several millimeters. In metal injection molding, only the binders are heated up, and that is how the metal is carried into the projectile shaped mold cavity.


Projectiles are molded by filling the mold cavity. Both mold design factors such as runner and gate size, gate placement, venting and molding parameters set on the molding machine affect the molded part. A helium Pycnometer can determine if there are voids trapped inside the parts. During molding, tool that can be used to measure the percent of theoretical density achieved on the “Green” or molded part. By crushing the measured “Green” molded part back to powder, you can now confirm the percent of air (or voids) trapped in the molded part. To measure this, the density of the molded part should be measured in the helium Pycnometer and compared to the theoretical density of the feedstock. Then, take the same molded part that was used in the density test and crush it back to powder. If this granulate shows a density of more than 100% of that of the feedstock, then some of the primary binders have been lost during the molding process. The molding process needs to be corrected because using this process with a degraded feedstock will result in a larger shrinkage and result in a part smaller than that desired. It is vital to be sure that your molded parts are completely filled before continuing the manufacturing process for debinding and sintering. The helium Pycnometer provides this assurance. Primary debinding properly debound parts are extremely important to establish the correct sintering profile. The primary binder must be completely removed before attempting to start to remove the secondary binder as the secondary binder will travel through the pores created by the extraction of the primary binder. Primary debinding techniques depend on the feedstock type used to make the parts. However, the feedstock supplier knows the amount of primary binders that have been added and should be removed before proceeding to the next process step. The feedstock supplier provides a minimum “brown density” that must be achieved before the parts can be moved into a furnace for final debinding and sintering. This minimum brown density will take into account that a small amount of the primary binder remnant may be present and could be removed by a suitable hold during secondary debinding and sintering. The sintering profile should be adjusted to remove the remaining small percent of primary binder before the removal of the secondary binder. Most external feedstock manufacturers provide only a weight loss percent that should be obtained to define suitable debinding. Solvent debound parts must be thoroughly dried, before the helium Pycnometer is used to determine the “brown” density so that the remnant solvent in the part does not affect the measured density value. When the feedstock manufacturer gives you the theoretical density of the “brown” or debound part, can validate the percent of debinding that has been achieved. Most Metal Injection Molding (MIM) operations today perform the secondary debinding and sintering in the same operation. Every MIM molder has gates and runners left over from molding their parts. So, you will be able to now re-use your gates and runners with confidence that they will shrink correctly after sintering. If the feedstock producers have given you the actual and theoretical densities of their feedstock, you can easily measure the densities of the gates and runners and compare the results to the values supplied. Once the regrind densities are higher than that required to maintain the part dimensions, the regrinds are no longer reusable.


Feedstock in accordance with the present invention may be prepared by blending the powdered metal with the binder and heating the blend to form a slurry. Uniform dispersion of the powdered metal in the slurry may be achieved by employing high shear mixing. The slurry may then be cooled to ambient temperature and then granulated to provide the feedstock for the metal injection molding.


The amount of powdered metal and binder in the feedstock may be selected to optimize moldability while insuring acceptable green densities. In one embodiment, the feedstock used for the metal injection molding portion of the invention may include at least about 40 percent by weight powdered metal, in another about 50 percent by weight powdered metal or more. In one embodiment, the feedstock includes at least about 60 percent by weight powdered metal, preferably about 65 percent by weight or more powdered metal. In yet another embodiment, the feedstock includes at least about 75 percent by weight powdered metal. In yet another embodiment, the feedstock includes at least about 80 percent by weight powdered metal. In yet another embodiment, the feedstock includes at least about 85 percent by weight powdered metal. In yet another embodiment, the feedstock includes at least about 90 percent by weight powdered metal.


The binding agent may be any suitable binding agent that does not destroy or interfere with the powdered metals. The binder may be present in an amount of about 50 percent or less by weight of the feedstock. In one embodiment, the binder is present in an amount ranging from 10 percent to about 50 percent by weight. In another embodiment, the binder is present in an amount of about 25 percent to about 50 percent by weight of the feedstock. In another embodiment, the binder is present in an amount of about 30 percent to about 40 percent by weight of the feedstock. In one embodiment, the binder is an aqueous binder. In another embodiment, the binder is an organic-based binder. Examples of binders include, but are not limited to, thermoplastic resins, waxes, and combinations thereof. Non-limiting examples of thermoplastic resins include polyolefins such as acrylic polyethylene, polypropylene, polystyrene, polyvinyl chloride, polyethylene carbonate, polyethylene glycol, and mixtures thereof. Suitable waxes include, but are not limited to, microcrystalline wax, bee wax, synthetic wax, and combinations thereof.


Examples of suitable powdered metals for use in the feedstock include, but are not limited to: stainless steel including martensitic and austenitic stainless steel, steel alloys, tungsten alloys, soft magnetic alloys such as iron, iron-silicon, electrical steel, iron-nickel (50Ni-50F3), low thermal expansion alloys, or combinations thereof. In one embodiment, the powdered metal is a mixture of stainless steel, brass and tungsten alloy. The stainless steel used in the present invention may be any 1 series carbon steels, 2 series nickel steels, 3 series nickel-chromium steels, 4 series molybdenum steels, series chromium steels, 6 series chromium-vanadium steels, 7 series tungsten steels, 8 series nickel-chromium-molybdenum steels, or 9 series silicon-manganese steels, e.g., 102, 174, 201, 202, 300, 302, 303, 304, 308, 309, 316, 316L, 316Ti, 321, 405, 408, 409, 410, 416, 420, 430, 439, 440, 446 or 601-665 grade stainless steel.


As known to those of ordinary skill in the art, stainless steel is an alloy of iron and at least one other component that imparts corrosion resistance. As such, in one embodiment, the stainless steel is an alloy of iron and at least one of chromium, nickel, silicon, molybdenum, or mixtures thereof. Examples of such alloys include, but are not limited to, an alloy containing about 1.5 to about 2.5 percent nickel, no more than about 0.5 percent molybdenum, no more than about 0.15 percent carbon, and the balance iron with a density ranging from about 7 g/cm3 to about 8 g/cm3; an alloy containing about 6 to about 8 percent nickel, no more than about 0.5 percent molybdenum, no more than about 0.15 percent carbon, and the balance iron with a density ranging from about 7 g/cm3 to about 8 g/cm3; an alloy containing about 0.5 to about 1 percent chromium, about 0.5 percent to about 1 percent nickel, no more than about 0.5 percent molybdenum, no more than about 0.2 percent carbon, and the balance iron with a density ranging from about 7 g/cm3 to about 8 g/cm3; an alloy containing about 2 to about 3 percent nickel, no more than about 0.5 percent molybdenum, about 0.3 to about 0.6 percent carbon, and the balance iron with a density ranging from about 7 g/cm3 to about 8 g/cm3; an alloy containing about 6 to about 8 percent nickel, no more than about 0.5 percent molybdenum, about 0.2 to about 0.5 percent carbon, and the balance iron with a density ranging from about 7 g/cm3 to about 8 g/cm3; an alloy containing about 1 to about 1.6 percent chromium, about 0.5 percent or less nickel, no more than about 0.5 percent molybdenum, about 0.9 to about 1.2 percent carbon, and the balance iron with a density ranging from about 7 g/cm3 to about 8 g/cm3; and combinations thereof.


Suitable tungsten alloys include an alloy containing about 2.5 to about 3.5 percent nickel, about 0.5 percent to about 2.5 percent copper or iron, and the balance tungsten with a density ranging from about 17.5 g/cm3 to about 18.5 g/cm3; about 3 to about 4 percent nickel, about 94 percent tungsten, and the balance copper or iron with a density ranging from about 17.5 g/cm3 to about 18.5 g/cm3; and mixtures thereof.


In addition, the binders may contain additives such as antioxidants, coupling agents, surfactants, elasticizing agents, dispersants, and lubricants as disclosed in U.S. Pat. No. 5,950,063, which is hereby incorporated by reference in its entirety. Suitable examples of antioxidants include, but are not limited to thermal stabilizers, metal deactivators, or combinations thereof. In one embodiment, the binder includes about 0.1 to about 2.5 percent by weight of the binder of an antioxidant. Coupling agents may include but are not limited to titanate, aluminate, silane, or combinations thereof. Typical levels range between 0.5 and 15% by weight of the binder.


For example, the metal injection molding process, which generally involves mixing fine metal powders with binders to form a feedstock that is injection molded into a closed mold, may be used to form a substantially cylindrical insert. After ejection from the mold, the binders are chemically or thermally removed from the substantially cylindrical insert so that the part can be sintered to high density. During the sintering process, the individual metal particles metallurgically bond together as material diffusion occurs to remove most of the porosity left by the removal of the binder.


The raw materials for metal injection molding are metal powders and a thermoplastic binder. There are at least two binders included in the blend, a primary binder and a secondary binder. This blended powder mix is worked into the plasticized binder at elevated temperature in a kneader or shear roll extruder. The intermediate product is the so-called feedstock. It is usually granulated with granule sizes of several millimeters. In metal injection molding, only the binders are heated up, and that is how the metal is carried into the mold cavity.


In preparing a feedstock, it is important first to measure the actual density of each lot of both the metal powders and binders. This is extremely important especially for the metal powders in that each lot will be different based on the actual chemistry of that grade of powder. For example, 316L is comprised of several elements, such as Fe, Cr, Ni, Cu, Mo, P, Si, S and C. In order to be rightfully called a 316L, each of these elements must meet a minimum and maximum percentage weight requirement as called out in the relevant specification. Hence the variation in the chemistry within the specification results in a significant density variation within the acceptable composition range. Depending on the lot received from the powder producer, the density will vary depending on the actual chemistry received.


In preparing a feedstock, it is important first to measure the actual density of each lot of both the metal powders and binders. This is extremely important especially for the metal powders in that each lot will be different based on the actual chemistry of that grade of powder. For example, 316L is comprised of several elements, such as Fe, Cr, Ni, Cu, Mo, P, Si, S and C. In order to be rightfully called a 316L, each of these elements must meet a minimum and maximum percentage weight requirement as called out in the relevant specification. Tables I-IV below provide other examples of the elemental compositions of some of the metal powders, feed stocks, metals, alloys and compositions of the present invention. Hence the variation in the chemistry within the specification results in a significant density variation within the acceptable composition range. Depending on the lot received from the powder producer, the density will vary depending on the actual chemistry received.










TABLE I







Material



Designation
Chemical Composition, % - Low-Alloy Steels












Code
Fe
Ni
Mo
C
Si (max)





MIM-2200(1)
Bal.
1.5-2.5
0.5 max
0.1 max
1.0


MIM-2700
Bal.
6.5-8.5
0.5 max
0.1 max
1.0


MlM-4605(2)
Bal.
1.5-2.5
0.2-0.5
0.4-0.6
1.0

















TABLE II







Material
Chemical Composition, % - Stainless Steels
















Designation







Mn
Si


Code
Fe
Ni
Cr
Mo
C
Cu
Nb + Ta
(max)
(max)





MIM-316L
Bal.
10-14
16-18
2-3
0.03 max


2.0
1.0


MIM-420
Bal.

12-14

0.15-0.4


1.0
1.0


MIM-430L
Bal.

16-18

0.05 max


1.0
1.0


MIM-17-4 PH
Bal.
3-5
15.5-17.5

0.07 max
3-5
0.15-0.45
1.0
1.0

















TABLE III







Material
Chemical Composition, % - Soft-Magnetic Alloys















Designation





C




Code
Fe
Ni
Cr
Co
Si
(max)
Mn
V





MIM-2200
Bal.
1.5-2.5


1.0 max
0.1 




MIM-Fe—3%Si
Bal.



2.5-3.5
0.05




MIM-Fe50%Ni
Bal.
49-51


1.0 max
0.05




MIM-Fe50%Co
Bal.


48-50
1.0 max
0.05

2.5 max


MIM-430L
Bal.

16-18

1.0 max
0.05
1.0 max



















TABLE IV









Nominal Chemical Composition, % - Controlled-Expansion Alloys




















Material



Mn
Si
C
Al
Mg
Zr
Ti
Cu
Cr
Mo


Designation
Fe
Ni
Co
max
max
max
max
max
max
max
max
max
max





MIM-F15
Bal.
29
17
0.50
0.20
0.04
0.10
0.10
0.10
0.10
0.20
0.20
0.20









In addition to the specific compositions listed herein, the skill artisan recognizes the elemental composition of common commercial designations used by feedstock manufacturers and processors, e.g., C-0000 Copper and Copper Alloys; CFTG-3806-K Diluted Bronze Bearings; CNZ-1818 Copper and Copper Alloys; CNZP-1816 Copper and Copper Alloys; CT-1000 Copper and Copper Alloys; CT-1000-K Bronze Bearings; CTG-1001-K Bronze Bearings; CTG-1004-K Bronze Bearings; CZ-1000 Copper and Copper Alloys; CZ-2000 Copper and Copper Alloys; CZ-3000 Copper and Copper Alloys; CZP-1002 Copper and Copper Alloys; CZP-2002 Copper and Copper Alloys; CZP-3002 Copper and Copper Alloys; F-0000 Iron and Carbon Steel; F-0000-K Iron and Iron-Carbon Bearings; F-0005 Iron and Carbon Steel; F-0005-K Iron and Iron-Carbon Bearings; F-0008 Iron and Carbon Steel; F-0008-K Iron and Iron-Carbon Bearings; FC-0200 Iron-Copper and Copper Steel; FC-0200-K Iron-Copper Bearings; FC-0205 Iron-Copper and Copper Steel; FC-0205-K Iron-Copper-Carbon Bearings; FC-0208 Iron-Copper and Copper Steel; FC-0208-K Iron-Copper-Carbon Bearings; FC-0505 Iron-Copper and Copper Steel; FC-0508 Iron-Copper and Copper Steel; FC-0508-K Iron-Copper-Carbon Bearings; FC-0808 Iron-Copper and Copper Steel; FC-1000 Iron-Copper and Copper Steel; FC-1000-K Iron-Copper Bearings; FC-2000-K Iron-Copper Bearings; FC-2008-K Iron-Copper-Carbon Bearings; FCTG-3604-K Diluted Bronze Bearings; FD-0200 Diffusion-Alloyed Steel; FD-0205 Diffusion-Alloyed Steel; FD-0208 Diffusion-Alloyed Steel; FD-0400 Diffusion-Alloyed Steel; FD-0405 Diffusion-Alloyed Steel; FD-0408 Diffusion-Alloyed Steel; FF-0000 Soft-Magnetic Alloys; FG-0303-K Iron-Graphite Bearings; FG-0308-K Iron-Graphite Bearings; FL-4005 Prealloyed Steel; FL-4205 Prealloyed Steel; FL-4400 Prealloyed Steel; FL-4405 Prealloyed Steel; FL-4605 Prealloyed Steel; FL-4805 Prealloyed Steel; FL-48105 Prealloyed Steel; FL-4905 Prealloyed Steel; FL-5208 Prealloyed Steel; FL-5305 Prealloyed Steel; FLC-4608 Sinter-Hardened Steel; FLC-4805 Sinter-Hardened Steel; FLC-48108 Sinter-Hardened Steel; FLC-4908 Sinter-Hardened Steel; FLC2-4808 Sinter-Hardened Steel; FLDN2-4908 Diffusion-Alloyed Steel; FLDN4C2-4905 Diffusion-Alloyed Steel; FLN-4205 Hybrid Low-Alloy Steel; FLN-48108 Sinter-Hardened Steel; FLN2-4400 Hybrid Low-Alloy Steel; FLN2-4405 Hybrid Low-Alloy Steel; FLN2-4408 Sinter-Hardened Steel; FLN2C-4005 Hybrid Low-Alloy Steel; FLN4-4400 Hybrid Low-Alloy Steel; FLN4-4405 Hybrid Low-Alloy Steel; FLN4-4408 Sinter Hardened Steel; FLN4C-4005 Hybrid Low-Alloy Steel; FLN6-4405 Hybrid Low-Alloy Steel; FLN6-4408 Sinter-Hardened Steel; FLNC-4405 Hybrid Low-Alloy Steel; FLNC-4408 Sinter-Hardened Steel; FN-0200 Iron-Nickel and Nickel Steel; FN-0205 Iron-Nickel and Nickel Steel; FN-0208 Iron-Nickel and Nickel Steel; FN-0405 Iron-Nickel and Nickel Steel; FN-0408 Iron-Nickel and Nickel Steel; FN-5000 Soft-Magnetic Alloys; FS-0300 Soft-Magnetic Alloys; FX-1000 Copper-Infiltrated Iron and Steel; FX-1005 Copper-Infiltrated Iron and Steel; FX-1008 Copper-Infiltrated Iron and Steel; FX-2000 Copper-Infiltrated Iron and Steel; FX-2005 Copper-Infiltrated Iron and Steel; FX-2008 Copper-Infiltrated Iron and Steel; FY-4500 Soft-Magnetic Alloys; FY-8000 Soft-Magnetic Alloys; P/F-1020 Carbon Steel PF; P/F-1040 Carbon Steel PF; P/F-1060 Carbon Steel PF; P/F-10C40 Copper Steel PF; P/F-10050 Copper Steel PF; P/F-10060 Copper Steel PF; P/F-1140 Carbon Steel PF; P/F-1160 Carbon Steel PF; P/F-11C40 Copper Steel PF; P/F-11050 Copper Steel PF; P/F-11060 Copper Steel PF; P/F-4220 Low-Alloy P/F-42XX Steel PF; P/F-4240 Low-Alloy P/F-42XX Steel PF; P/F-4260 Low-Alloy P/F-42XX Steel PF; P/F-4620 Low-Alloy P/F-46XX Steel PF; P/F-4640 Low-Alloy P/F-46XX Steel PF; P/F-4660 Low-Alloy P/F-46XX Steel PF; P/F-4680 Low-Alloy P/F-46XX Steel PF; SS-303L Stainless Steel—300 Series Alloy; SS-303N1 Stainless Steel—300 Series Alloy; SS-303N2 Stainless Steel—300 Series Alloy; SS-304H Stainless Steel—300 Series Alloy; SS-304L Stainless Steel—300 Series Alloy; SS-304N1 Stainless Steel—300 Series Alloy; SS-304N2 Stainless Steel—300 Series Alloy; SS-316H Stainless Steel—300 Series Alloy; SS-316L Stainless Steel—300 Series Alloy; SS-316N1 Stainless Steel—300 Series Alloy; SS-316N2 Stainless Steel—300 Series Alloy; SS-409L Stainless Steel—400 Series Alloy; SS-409LE Stainless Steel—400 Series Alloy; SS-410 Stainless Steel—400 Series Alloy; SS-410L Stainless Steel—400 Series Alloy; SS-430L Stainless Steel—400 Series Alloy; SS-430N2 Stainless Steel—400 Series Alloy; SS-434L Stainless Steel—400 Series Alloy; SS-434LCb Stainless Steel—400 Series Alloy; and SS-434N2 Stainless Steel—400 Series Alloy.


Titanium alloys that may be used in this invention include any alloy or modified alloy known to the skilled artisan including titanium grades 5-38 and more specifically titanium grades 5, 9, 18, 19, 20, 21, 23, 24, 25, 28, 29, 35, 36 or 38. Grades 5, 23, 24, 25, 29, 35, or 36 annealed or aged; Grades 9, 18, 28, or 38 cold-worked and stress-relieved or annealed; Grades 9, 18, 23, 28, or 29 transformed-beta condition; and Grades 19, 20, or 21 solution-treated or solution-treated and aged. Grade 5, also known as Ti6Al4V, Ti-6Al-4V or Ti 6-4, is the most commonly used alloy. It has a chemical composition of 6% aluminum, 4% vanadium, 0.25% (maximum) iron, 0.2% (maximum) oxygen, and the remainder titanium. It is significantly stronger than commercially pure titanium while having the same stiffness and thermal properties (excluding thermal conductivity, which is about 60% lower in Grade 5 Ti than in CP Ti); Grade 6 contains 5% aluminum and 2.5% tin. It is also known as Ti-5Al-2.5Sn. This alloy has good weldability, stability and strength at elevated temperatures; Grade 7 and 7H contains 0.12 to 0.25% palladium. This grade is similar to Grade 2. The small quantity of palladium added gives it enhanced crevice corrosion resistance at low temperatures and high pH; Grade 9 contains 3.0% aluminum and 2.5% vanadium. This grade is a compromise between the ease of welding and manufacturing of the “pure” grades and the high strength of Grade 5; Grade 11 contains 0.12 to 0.25% palladium; Grade 12 contains 0.3% molybdenum and 0.8% nickel; Grades 13, 14, and 15 all contain 0.5% nickel and 0.05% ruthenium; Grade 16 contains 0.04 to 0.08% palladium; Grade 16H contains 0.04 to 0.08% palladium; Grade 17 contains 0.04 to 0.08% palladium; Grade 18 contains 3% aluminum, 2.5% vanadium and 0.04 to 0.08% palladium; Grade 19 contains 3% aluminum, 8% vanadium, 6% chromium, 4% zirconium, and 4% molybdenum; Grade 20 contains 3% aluminum, 8% vanadium, 6% chromium, 4% zirconium, 4% molybdenum and 0.04% to 0.08% palladium; Grade 21 contains 15% molybdenum, 3% aluminum, 2.7% niobium, and 0.25% silicon; Grade 23 contains 6% aluminum, 4% vanadium, 0.13% (maximum) Oxygen; Grade 24 contains 6% aluminum, 4% vanadium and 0.04% to 0.08% palladium. Grade 25 contains 6% aluminum, 4% vanadium and 0.3% to 0.8% nickel and 0.04% to 0.08% palladium; Grades 26, 26H, and 27 all contain 0.08 to 0.14% ruthenium; Grade 28 contains 3% aluminum, 2.5% vanadium and 0.08 to 0.14% ruthenium; Grade 29 contains 6% aluminum, 4% vanadium and 0.08 to 0.14% ruthenium; Grades 30 and 31 contain 0.3% cobalt and 0.05% palladium; Grade 32 contains 5% aluminum, 1% tin, 1% zirconium, 1% vanadium, and 0.8% molybdenum; Grades 33 and 34 contain 0.4% nickel, 0.015% palladium, 0.025% ruthenium, and 0.15% chromium; Grade 35 contains 4.5% aluminum, 2% molybdenum, 1.6% vanadium, 0.5% iron, and 0.3% silicon; Grade 36 contains 45% niobium; Grade 37 contains 1.5% aluminum; and Grade 38 contains 4% aluminum, 2.5% vanadium, and 1.5% iron. Its mechanical properties are very similar to Grade 5, but has good cold workability similar to grade 9. One embodiment includes a Ti6Al4V composition. One embodiment includes a composition having 3-12% aluminum, 2-8% vanadium, 0.1-0.75% iron, 0.1-0.5% oxygen, and the remainder titanium. More specifically, about 6% aluminum, about 4% vanadium, about 0.25% iron, about 0.2% oxygen, and the remainder titanium. For example, one Ti composition may include 10 to 35% Cr, 0.05 to 15% Al, 0.05 to 2% Ti, 0.05 to 2% Y2O5, with the balance being either Fe, Ni or Co, or an alloy consisting of 20±1.0% Cr, 4.5±0.5% Al, 0.5±0.1% Y2O5 or ThO2, with the balance being Fe. For example, one Ti composition may include 15.0-23.0% Cr, 0.5-2.0% Si, 0.0-4.0% Mo, 0.0-1.2% Nb, 0.0-3.0% Fe, 0.0-0.5% Ti, 0.0-0.5% Al, 0.0-0.3% Mn, 0.0-0.1% Zr, 0.0-0.035% Ce, 0.005-0.025% Mg, 0.0005-0.005% B, 0.005-0.3% C, 0.0-20.0% Co, balance Ni. Sample Ti-based feedstock component includes 0-45% metal powder; 15-40% binder; 0-10% Polymer (e.g., thermoplastics and thermosets); surfactant 0-3%; lubricant 0-3%; sintering aid 0-1%. Another sample Ti-based feedstock component includes about 62% TiH2 powder as a metal powder; about 29% naphthalene as a binder; about 2.1-2.3% polymer (e.g., EVA/epoxy); about 2.3% SURFONIC N-100® as a Surfactant; lubricant is 1.5% stearic acid as; about 0.4% silver as a sintering Aid. Examples of metal compounds include metal hydrides, such as TiH2, and intermetallics, such as TiAl and TiAl3. A specific instance of an alloy includes Ti-6Al,4V, among others. In another embodiment, the metal powder comprises at least approximately 45% of the volume of the feedstock, while in still another, it comprises between approximately 54.6% and 70.0%. In addition, Ti—Al alloys may consists essentially of 32-38% of Al and the balance of Ti and contains 0.005-0.20% of B, and the alloy which essentially consists of the above quantities of Al and Ti and contains, in addition to the above quantity of B, up to 0.2% of C, up to 0.3% of O and/or up to 0.3% of N (provided that O+N add up to 0.4%) and c) 0.05-3.0% of Ni and/or 0.05-3.0% of Si, and the balance of Ti.


Both mold design factors such as runner and gate size, gate placement, venting and molding parameters set on the molding machine affect the molded part. A helium Pycnometer can determine if there are voids trapped inside the parts. During molding, you have a tool that can be used to measure the percent of theoretical density achieved on the “Green” or molded part. By crushing the measured “green” molded part back to powder, you can now confirm the percent of air (or voids) trapped in the molded part. To measure this, the density of the molded part should be measured in the helium Pycnometer and compared to the theoretical density of the feedstock. Then, take the same molded part that was used in the density test and crush it back to powder. If this granulate shows a density of more than 100% of that of the feedstock, then some of the primary binders have been lost during the molding process. The molding process needs to be corrected because using this process with a degraded feedstock will result in a larger shrinkage and result in a part smaller than that desired. It is vital to be sure that your molded parts are completely filled before continuing the manufacturing process for debinding and sintering. The helium Pycnometer provides this assurance. Primary debinding properly debound parts are extremely important to establish the correct sintering profile. The primary binder must be completely removed before attempting to start to remove the secondary binder as the secondary binder will travel through the pores created by the extraction of the primary binder. Primary debinding techniques depend on the feedstock type used to make the parts. However the feedstock supplier knows the amount of primary binders that have been added and should be removed before proceeding to the next process step. The feedstock supplier provides a minimum “brown density” that must be achieved before the parts can be moved into a furnace for final debinding and sintering. This minimum brown density will take into account that a small amount of the primary binder remnant may be present and could be removed by a suitable hold during secondary debinding and sintering. The sintering profile should be adjusted to remove the remaining small percent of primary binder before the removal of the secondary binder. Most external feedstock manufacturers provide only a weight loss percent that should be obtained to define suitable debinding. Solvent debound parts must be thoroughly dried, before the helium Pycnometer is used to determine the “brown” density so that the remnant solvent in the part does not affect the measured density value. When the feedstock manufacturer gives you the theoretical density of the “brown” or debound part, can validate the percent of debinding that has been achieved. Most MIM operations today perform the secondary debinding and sintering in the same operation. Every MIM molder has gates and runners left over from molding their parts. So, you will be able to now re-use your gates and runners with confidence that they will shrink correctly after sintering. If the feedstock producers have given you the actual and theoretical densities of their feedstock, you can easily measure the densities of the gates and runners and compare the results to the values supplied. Once the regrind densities are higher than that required to maintain the part dimensions, the regrinds are no longer reusable.


For example, one Ti composition may include 10 to 35% Cr, 0.05 to 15% Al, 0.05 to 2% Ti, 0.05 to 2% Y2O5, with the balance being either Fe, Ni or Co, or an alloy consisting of 20±1.0% Cr, 4.5±0.5% Al, 0.5±0.1% Y2O5 or ThO2, with the balance being Fe. For example, one Ti composition may include 15.0-23.0% Cr, 0.5-2.0% Si, 0.0-4.0% Mo, 0.0-1.2% Nb, 0.0-3.0% Fe, 0.0-0.5% Ti, 0.0-0.5% Al, 0.0-0.3% Mn, 0.0-0.1% Zr, 0.0-0.035% Ce, 0.005-0.025% Mg, 0.0005-0.005% B, 0.005-0.3% C, 0.0-20.0% Co, balance Ni. Sample Ti-based feedstock component includes 0-45% metal powder; 15-40% binder; 0-10% Polymer (e.g., thermoplastics and thermosets); surfactant 0-3%; lubricant 0-3%; sintering aid 0-1%. Another sample Ti-based feedstock component includes about 62% TiH2 powder as a metal powder; about 29% naphthalene as a binder; about 2.1-2.3% polymer (e.g., EVA/epoxy); about 2.3% SURFONIC N-100® as a Surfactant; lubricant is 1.5% stearic acid as a; about 0.4% silver as a sintering Aid. Examples of metal compounds include metal hydrides, such as TiH2, and intermetallics, such as TiAl and TiAl3. A specific instance of an alloy includes Ti-6Al,4V, among others. In another embodiment, the metal powder comprises at least approximately 45% of the volume of the feedstock, while in still another, it comprises between approximately 54.6% and 70.0%. In addition, Ti—Al alloys may consists essentially of 32-38% of Al and the balance of Ti and contains 0.005-0.20% of B, and the alloy which essentially consists of the above quantities of Al and Ti and contains, in addition to the above quantity of B, up to 0.2% of C, up to 0.3% of O and/or up to 0.3% of N (provided that O+N add up to 0.4%) and c) 0.05-3.0% of Ni and/or 0.05-3.0% of Si, and the balance of Ti.


Feedstock in accordance with the present invention may be prepared by blending the powdered metal with the binder and heating the blend to form a slurry. Uniform dispersion of the powdered metal in the slurry may be achieved by employing high shear mixing. The slurry may then be cooled to ambient temperature and then granulated to provide the feedstock for the metal injection molding.


One embodiment of the powdered metal may include a composition where Ni may be 2.0, 2.25, 2.50, 2.75, 3.0, 3.25, 3.5, 3.75, 4.0, 4.25, 4.50, 4.75, 5.0, 5.25, 5.5, 5.75, 6.0, 6.25, 6.50, 6.75, 7.0, 7.25, 7.5, 7.75, 8.0, 8.25, 8.50, 8.75, 9.0, 9.25, 9.5, 9.75, 10.0, 10.25, 10.50, 10.75, 11.0, 11.25, 11.5, 11.75, 12.0, 12.25, 12.50, 12.75, 13.0, 13.25, 13.5, 13.75, 14.0, 14.25, 14.50, 14.75, 15.0, 15.25, 15.5, 15.75, 16.0, 16.25, 16.50, 16.75, or 17.0%; Cr may be 9.0, 9.25, 9.5, 9.75, 10.0, 10.25, 10.50, 10.75, 11.0, 11.25, 11.5, 11.75, 12.0, 12.25, 12.50, 12.75, 13.0, 13.25, 13.5, 13.75, 14.0, 14.25, 14.50, 14.75, 15.0, 15.25, 15.5, 15.75, 16.0, 16.25, 16.50, 16.75, 17.0, 17.25, 17.5, 17.75, 18.0, 18.25, 18.50, 18.75, 19.0, 19.25, 19.5, 19.75, or 20.0%; Mo may be 0.00, 0.025, 0.050, 0.075, 0.10, 0.125, 0.150, 0.175, 0.20, 0.225, 0.250, 0.275, 0.30, 0.325, 0.350, 0.375, 0.40, 0.425, 0.450, 0.475, 0.50, 0.525, 0.550, 0.575, 0.60, 0.625, 0.650, 0.675, 0.70, 0.725, 0.750, 0.775, 0.80, 0.825, 0.850, 0.875, 0.90, 0.925, 0.950, 1.0, 1.25, 1.5, 1.75, 2.0, 2.25, 2.50, 2.75, 3.0, 3.25, 3.5, 3.75, 4.0, 4.25, 4.50, 4.75, 5.0, 5.25, 5.5, 5.75, 6.0, 6.25, 6.50, 6.75, or 7.0%; C may be 0.00, 0.025, 0.050, 0.075, 0.10, 0.125, 0.150, 0.175, 0.20, 0.225, 0.250, 0.275, 0.30, 0.325, 0.350, 0.375, 0.40, 0.425, 0.450, 0.475, 0.50, 0.525, 0.550, 0.575, 0.60, 0.625, 0.650, 0.675, 0.70, 0.725, 0.750, 0.775, 0.80, 0.825, 0.850, 0.875, 0.90, 0.925, 0.950, or 1.00%; Cu may be 0.00, 0.025, 0.050, 0.075, 0.10, 0.125, 0.150, 0.175, 0.20, 0.225, 0.250, 0.275, 0.30, 0.325, 0.350, 0.375, 0.40, 0.425, 0.450, 0.475, 0.50, 0.525, 0.550, 0.575, 0.60, 0.625, 0.650, 0.675, 0.70, 0.725, 0.750, 0.775, 0.80, 0.825, 0.850, 0.875, 0.90, 0.925, 0.950, 1.0, 1.25, 1.5, 1.75, 2.0, 2.25, 2.50, 2.75, 3.0, 3.25, 3.5, 3.75, 4.0, 4.25, 4.50, 4.75, 5.0, 5.25, 5.5, 5.75, 6.0, 6.25, 6.50, 6.75, 7.0, 7.25, 7.5, 7.75, or 8.0%; Nb+Ta may be 0.00, 0.025, 0.050, 0.075, 0.10, 0.125, 0.150, 0.175, 0.20, 0.225, 0.250, 0.275, 0.30, 0.325, 0.350, 0.375, 0.40, 0.425, 0.450, 0.475, 0.50, 0.525, 0.550, 0.575, 0.60, 0.625, 0.650, 0.675, 0.70, 0.725, 0.750, 0.775, or 0.80%; Mn may be 0.00, 0.025, 0.050, 0.075, 0.10, 0.125, 0.150, 0.175, 0.20, 0.225, 0.250, 0.275, 0.30, 0.325, 0.350, 0.375, 0.40, 0.425, 0.450, 0.475, 0.50, 0.525, 0.550, 0.575, 0.60, 0.625, 0.650, 0.675, 0.70, 0.725, 0.750, 0.775, 0.80, 0.825, 0.850, 0.875, 0.90, 0.925, 0.950, 1.0, 1.25, 1.5, 1.75, 2.0, 2.25, 2.50, 2.75, 3.0, 3.25, 3.5, 3.75, 4.0, 4.25, 4.50, 4.75, 5.0, 5.25, 5.5, 5.75, or 6.0%; Si may be 0.00, 0.025, 0.050, 0.075, 0.10, 0.125, 0.150, 0.175, 0.20, 0.225, 0.250, 0.275, 0.30, 0.325, 0.350, 0.375, 0.40, 0.425, 0.450, 0.475, 0.50, 0.525, 0.550, 0.575, 0.60, 0.625, 0.650, 0.675, 0.70, 0.725, 0.750, 0.775, 0.80, 0.825, 0.850, 0.875, 0.90, 0.925, 0.950, 1.0, 1.25, 1.5, 1.75, 2.0, 2.25, 2.50, 2.75, 3.0, 3.25, 3.5, 3.75, or 4.0%; and the balance Fe. For example, one embodiment of the powdered metal may include any amount in the range of 2-16% Ni; 10-20% Cr; 0-5% Mo; 0-0.6% C; 0-6.0% Cu; 0-0.5% Nb+Ta; 0-4.0% Mn; 0-2.0% Si and the balance Fe. One embodiment of the powdered metal may include any amount in the range of 2-6% Ni; 13.5-19.5% Cr; 0-0.10% C; 1-7.0% Cu; 0.05-0.65% Nb+Ta; 0-3.0% Mn; 0-3.0% Si and the balance Fe. One embodiment of the powdered metal may include any amount in the range of 3-5% Ni; 15.5-17.5% Cr; 0-0.07% C; 3-5.0% Cu; 0.15-0.45% Nb+Ta; 0-1.0% Mn; 0-1.0% Si and the balance Fe. One embodiment of the powdered metal may include any amount in the range of 10-14% Ni; 16-18% Cr; 2-3% Mo; 0-0.03% C; 0-2% Mn; 0-1% Si and the balance Fe. One embodiment of the powdered metal may include any amount in the range of 12-14% Cr; 0.15-0.4% C; 0-1% Mn; 0-1% Si and the balance Fe. One embodiment of the powdered metal may include any amount in the range of 16-18% Cr; 0-0.05% C; 0-1% Mn; 0-1% Si and the balance Fe.


The projectiles of the present invention may be made by metal injection molded using alloys include high strength steels, stainless steels plus Ni and Co super alloys; refractory metals, titanium and copper alloys; and low melting point alloys like brass, bronze, zinc and aluminum. The projectiles of the present invention may also be made by metal injection molded using stainless Steel: 304L, 316L, 17-4 PH, 15-5 PH, 420, 430, 440; Super alloys: Inconel, Hastelloy, Co-based Low Alloy Steels, 2-8% Ni (4600, 4650); Magnetic Alloys: 2-6% Si—Fe, 50% Ni—Fe, 50% Co—Fe; Alloys: Fe-36Ni (Invar), F-15 (Kovar); Materials: Pure Copper, Beryllium-Copper, Brass Steels: AISI M2, M3/2, M4, T15, M42, D2; Heavy Alloys: Tungsten-Copper, W—Fe—Ni, Molybdenum-Copper.


The present invention can be used to metal injection mold various materials including Brass compositions include MPIF CZ-1000-10 having a tensile strength of 20,000 PSI, a yield strength of 11,000 PSI, an elongation of 10.5% per inch, and an apparent hardness HRH 70-75; and MPIF CZ-2000-12 having a tensile strength of 30,000 PSI, a yield strength of 13,500 PSI, an elongation of 16% per inch, and an apparent Hardness HRH 75-80.


The present invention can be used to metal injection mold various materials including Copper compositions include MPIF C-0000-5 having a tensile strength of Tensile Strength 23,000 PSI, an elongation of 20% per inch, and an apparent hardness HRH 20-25.


The present invention can be used to metal injection mold various materials including lead. In addition compositions of lead with tin and/or antimony can be formed using the present invention. The present invention can be used to form a cup made of harder metal, such as copper, placed at the base of the bullet (i.e., a gas check) to decrease lead deposits by protecting the rear of the bullet against melting when fired at higher pressures.


The present invention can be used to metal injection mold various materials including jacketed bullets intended for even higher-velocity applications generally have a lead core that is jacketed or plated with gilding metal, cupronickel, copper alloys, or steel; a thin layer of harder metal protects the softer lead core when the bullet is passing through the barrel and during flight, which allows delivering the bullet intact to the target. There, the heavy lead core delivers its kinetic energy to the target. In addition to lead cores other more dense metals including hardened steel, tungsten, or tungsten carbide, and even a core of depleted uranium.


The present invention can be used to metal injection mold various materials including full metal jacket bullets are completely encased in the harder metal jacket, except for the base. Some bullet jackets do not extend to the front of the bullet, to aid expansion and increase lethality; these are called soft point or hollow point bullets. Steel bullets are often plated with copper or other metals for corrosion resistance during long periods of storage. Synthetic jacket materials such as nylon and TEFLON® can also be used as can hollow point bullets with plastic aerodynamic tips that improve accuracy and enhance expansion.


The present invention can be used to metal injection mold various materials including hard cast bullets which includes a hard lead alloy to reduce fouling of rifling grooves.


The present invention can be used to metal injection mold various materials including practice bullets made from lightweight materials including rubber, wax, plastic, or lightweight metal.


The present invention can be used to metal injection mold incendiary rounds from various materials including an explosive or flammable mixture in the tip that is designed to ignite on contact with a target. The intent is to ignite fuel or munitions in the target area, thereby adding to the destructive power of the bullet itself.


The present invention can be used to metal injection mold exploding rounds from various materials. Similar to the incendiary bullet, this type of projectile is designed to explode upon hitting a hard surface, preferably the bone of the intended target. Not to be mistaken for cannon shells or grenades with fuse devices, these bullets have only a cavity filled with a small amount of low explosive depending on the velocity and deformation upon impact to detonate.


The present invention can be used to metal injection mold tracer rounds from various materials. The tracer rounds have a hollow back, filled with a flare material. Usually this is a mixture of magnesium metal, a perchlorate, and strontium salts to yield a bright red color, although other materials providing other colors have also sometimes been used. Tracer material burns out after a certain amount of time. This type of round is also used by all branches of the United States military in combat environments as a signaling device to friendly forces. The flight characteristics of tracer rounds differ from normal bullets due to their lighter weight.


The present invention can be used to metal injection mold armor piercing rounds from various materials. Jacketed designs where the core material is a very hard, high-density metal such as tungsten, tungsten carbide, depleted uranium, or steel. A pointed tip is often used, but a flat tip on the penetrator portion is generally more effective. The most common bullet jacket material is a copper, nickel, or steel jacket over a lead core; however, other core materials may be used including depleted Uranium, Tungsten as well as other jacketing materials.


In addition multiple layer projectiles may be formed using the metal injection molding of the present invention. For example, a steel core may be covered with a layer of lead that is then covered with a layer of copper; a depleted Uranium may be covered with a layer of Tungsten that is then covered with a layer of copper; a steel core may be covered with a layer of lead that is then covered with a polymer layer; a pelleted core (e.g., small lead pellets, plastic, or a silicone rubber material) may be covered with a layer of lead, copper or polymer; or other variations.


The present invention can be used to metal injection mold various materials including nontoxic shot such as steel, bismuth, tungsten, and other exotic bullet alloys prevent release of toxic lead into the environment.


The present invention can be used to metal injection mold rounds from various materials including blended-metals such as bullets made using cores from powdered metals and mixtures of different powered metals.


The present invention can be used to metal injection mold frangible rounds from various materials. These are designed to disintegrate into tiny particles upon impact to minimize their penetration for reasons of range safety, to limit environmental impact, or to limit the shoot-through danger behind the intended target. The bullet may be made from an amalgam of metal and a hard frangible plastic binder designed to penetrate a human target and release its component shot pellets without exiting the target.


The present invention can be used to metal injection mold various materials including solid or monolithic solid metal rounds including mono-metal bullets intended for deep penetration with slender shaped very-low-drag projectiles for long range shooting. Such metals include oxygen free copper and alloys like copper nickel, tellurium copper and brass including UNS C36000 Free-Cutting Brass.


The present invention can be used to metal injection mold sabot rounds from various materials. The sabot round may include a multiple piece bullet having a smaller bullet surrounded by a larger carrier bullet (or sabot) that passes through the barrel and once leaving the barrel the sabot and the smaller bullet separate with the sabot falling to the ground fairly close to the barrel and the light weighted smaller bullet traveling down range at a high velocity without any identifiable rifling characteristics.


The description of the preferred embodiments should be taken as illustrating, rather than as limiting, the present invention as defined by the claims. As will be readily appreciated, numerous combinations of the features set forth above can be utilized without departing from the present invention as set forth in the claims. Such variations are not regarded as a departure from the spirit and scope of the invention, and all such modifications are intended to be included within the scope of the following claims.


It will be understood that particular embodiments described herein are shown by way of illustration and not as limitations of the invention. The principal features of this invention can be employed in various embodiments without departing from the scope of the invention. Those skilled in the art will recognize, or be able to ascertain using no more than routine experimentation, numerous equivalents to the specific procedures described herein. Such equivalents are considered to be within the scope of this invention and are covered by the claims.


All publications and patent applications mentioned in the specification are indicative of the level of skill of those skilled in the art to which this invention pertains. All publications and patent applications are herein incorporated by reference to the same extent as if each individual publication or patent application was specifically and individually indicated to be incorporated by reference.


The use of the word “a” or “an” when used in conjunction with the term “comprising” in the claims and/or the specification may mean “one,” but it is also consistent with the meaning of “one or more,” “at least one,” and “one or more than one.” The use of the term “or” in the claims is used to mean “and/or” unless explicitly indicated to refer to alternatives only or the alternatives are mutually exclusive, although the disclosure supports a definition that refers to only alternatives and “and/or.” Throughout this application, the term “about” is used to indicate that a value includes the inherent variation of error for the device, the method being employed to determine the value, or the variation that exists among the study subjects.


As used in this specification and claim(s), the words “comprising” (and any form of comprising, such as “comprise” and “comprises”), “having” (and any form of having, such as “have” and “has”), “including” (and any form of including, such as “includes” and “include”) or “containing” (and any form of containing, such as “contains” and “contain”) are inclusive or open-ended and do not exclude additional, unrecited elements or method steps.


The term “or combinations thereof” as used herein refers to all permutations and combinations of the listed items preceding the term. For example, “A, B, C, or combinations thereof” is intended to include at least one of: A, B, C, AB, AC, BC, or ABC, and if order is important in a particular context, also BA, CA, CB, CBA, BCA, ACB, BAC, or CAB. Continuing with this example, expressly included are combinations that contain repeats of one or more item or term, such as BB, AAA, AB, BBC, AAABCCCC, CBBAAA, CABABB, and so forth. The skilled artisan will understand that typically there is no limit on the number of items or terms in any combination, unless otherwise apparent from the context.


All of the compositions and/or methods disclosed and claimed herein can be made and executed without undue experimentation in light of the present disclosure. While the compositions and methods of this invention have been described in terms of preferred embodiments, it will be apparent to those of skill in the art that variations may be applied to the compositions and/or methods and in the steps or in the sequence of steps of the method described herein without departing from the concept, spirit and scope of the invention. All such similar substitutes and modifications apparent to those skilled in the art are deemed to be within the spirit, scope and concept of the invention as defined by the appended claims.

Claims
  • 1. An ammunition having a metal injection molded projectile and a polymer cartridge case comprising: a polymer ammunition cartridge comprising a primer insert comprising a top surface opposite a bottom surface, a primer recess extending into the top surface toward the bottom surface,a flash aperture positioned in the primer recess and extending through the bottom surface;a groove positioned inside the primer recess around the flash aperture anda coupler extending away from the bottom surface;a mid-body molded from a mid-body coupler over the coupler and into the flash aperture to from a flash hole;a nose portion comprising a nose coupler connected to the mid-body coupler and extending to a projectile aperture;a propellant chamber formed between the projectile aperture and the flash hole;a primer inserted into the primer recess;a propellant at least partially filling the propellant chamber; anda metal injection molded projectile frictionally fitted in the projectile aperture, wherein the metal injection molded projectile comprises a nose extending essentially symmetrically to a shoulder, and an essentially cylindrical bearing surface extending from the shoulder to a base.
  • 2. The molded ammunition of claim 1, wherein the metal injection molded projectile comprises stainless steel, ceramic alloys, copper/cobalt/nickel/custom alloys, tungsten, tungsten carbide, carballoy, ferro-tungsten, titanium, copper, cobalt, nickel, uranium, depleted uranium, alumina oxide, zirconia and aluminum.
  • 3. The molded ammunition of claim 1, wherein the metal injection molded projectile further comprising a cannelure formed on an outer circumferential surface of the essentially cylindrical bearing surface intermediate the shoulder and the base.
  • 4. The molded ammunition of claim 1, wherein the nose has a frustoconical shape.
  • 5. The molded ammunition of claim 4, wherein the frustoconical shape further comprises a cavity.
  • 6. The molded ammunition of claim 1, wherein the nose has a spritzer shape.
  • 7. The molded ammunition of claim 1, wherein the nose has a blunted shape.
  • 8. The molded ammunition of claim 1, wherein the nose has a rounded shape.
  • 9. The molded ammunition of claim 1, wherein the metal injection molded projectile comprises a base has a flat shape.
  • 10. The molded ammunition of claim 1, wherein the base has a boattail shape.
  • 11. The molded ammunition of claim 1, further comprising an outer coating placed over the projectile to form a metal jacketed projectile.
  • 12. The molded ammunition of claim 1, wherein the projectile is a full metal jacket, expanding full metal jacket, spritzer, jacketed spritzer, armor piercing, armor piercing incendiary.
  • 13. The molded ammunition of claim 1, wherein the metal injection molded projectile includes a soft metal.
  • 14. The molded ammunition of claim 1, wherein the metal injection molded projectile is a 5.56 mm, 7.62 mm, 308, 338, 3030, 3006, 50 caliber, 45 caliber, 380 caliber, 38 caliber, 9 mm, 10 mm, 12.7 mm, 14.5 mm, 14.7 mm, 20 mm, 25 mm, 30 mm, 40 mm, 57 mm, 60 mm, 75 mm, 76 mm, 81 mm, 90 mm, 100 mm, 105 mm, 106 mm, 115 mm, 120 mm, 122 mm, 125 mm, 130 mm, 152 mm, 155 mm, 165 mm, 175 mm, 203 mm, 460 mm, 8 inch, or 4.2 inch.
  • 15. The molded ammunition of claim 1, wherein the metal injection molded projectile comprises 102, 174, 201, 202, 300, 302, 303, 304, 308, 309, 316, 316L, 316Ti, 321, 405, 408, 409, 410, 415, 416, 416R, 420, 430, 439, 440, 446 or 601-665 grade stainless steel.
  • 16. The molded ammunition of claim 1, wherein the metal injection molded projectile comprises 2-16% Ni; 10-20% Cr; 0-5% Mo; 0-0.6% C; 0-6.0% Cu; 0-0.5% Nb+Ta; 0-4.0% Mn; 0-2.0% Si and the balance Fe; 2-6% Ni; 13.5-19.5% Cr; 0-0.10% C; 1-7.0% Cu; 0.05-0.65% Nb+Ta; 0-3.0% Mn; 0-3.0% Si and the balance Fe; 3-5% Ni; 15.5-17.5% Cr; 0-0.07% C; 3-5.0% Cu; 0.15-0.45% Nb+Ta; 0-1.0% Mn; 0-1.0% Si and the balance Fe; 10-14% Ni; 16-18% Cr; 2-3% Mo; 0-0.03% C; 0-2% Mn; 0-1% Si and the balance Fe; 12-14% Cr; 0.15-0.4% C; 0-1% Mn; 0-1% Si and the balance Fe; 16-18% Cr; 0-0.05% C; 0-1% Mn; 0-1% Si and the balance Fe; 3-12% aluminum, 2-8% vanadium, 0.1-0.75% iron, 0.1-0.5% oxygen, and the remainder titanium; or 6% aluminum, about 4% vanadium, about 0.25% iron, about 0.2% oxygen, and the remainder titanium.
  • 17. The molded ammunition of claim 1, wherein the nose portion, the mid-body or both comprise a nylon polymer or a fiber-reinforced polymeric composite.
  • 18. The molded ammunition of claim 1, wherein the nose portion, the mid-body or both comprise between about 10 and about 70 wt % glass fiber fillers, mineral fillers, or mixtures thereof.
  • 19. The molded ammunition of claim 1, wherein the nose portion and the mid-body are welded or bonded together.
  • 20. The molded ammunition of claim 1, wherein the nose portion, the mid-body or both comprise polyurethane prepolymer, cellulose, fluoro-polymer, ethylene inter-polymer alloy elastomer, ethylene vinyl acetate, nylon, polyether imide, polyester elastomer, polyester sulfone, polyphenyl amide, polypropylene, polyvinylidene fluoride or thermoset polyurea elastomer, acrylics, homopolymers, acetates, copolymers, acrylonitrile-butadinen-styrene, thermoplastic fluoro polymers, inomers, polyamides, polyamide-imides, polyacrylates, polyatherketones, polyaryl-sulfones, polybenzimidazoles, polycarbonates, polybutylene, terephthalates, polyether imides, polyether sulfones, thermoplastic polyimides, thermoplastic polyurethanes, polyphenylene sulfides, polyethylene, polypropylene, polysulfones, polyvinylchlorides, styrene acrylonitriles, polystyrenes, polyphenylene, ether blends, styrene maleic anhydrides, polycarbonates, allyls, aminos, cyanates, epoxies, phenolics, unsaturated polyesters, bismaleimides, polyurethanes, silicones, vinylesters, urethane hybrids, polyphenylsulfones, copolymers of polyphenylsulfones with polyethersulfones or polysulfones, copolymers of poly-phenylsulfones with siloxanes, blends of polyphenylsulfones with polysiloxanes, poly(etherimide-siloxane) copolymers, blends of polyetherimides and polysiloxanes, and blends of polyetherimides and poly(etherimide-siloxane) copolymers.
  • 21. The molded ammunition of claim 1, further comprising a diffuser ring positioned within the primer recess.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a Continuation-in-Part of U.S. application Ser. No. 14/011,202 entitled “Lightweight Polymer Ammunition Cartridge Casings” filed on Aug. 27, 2013, which is a Divisional of U.S. patent application Ser. No. 13/292,843 entitled “Lightweight Polymer Ammunition Cartridge Casings” filed on Nov. 9, 2011 which issued as U.S. Pat. No. 8,561,543 on Oct. 22, 2013, which claims priority to U.S. Provisional Application Ser. No. 61/456,664 entitled “Polymer Case Ammunition and Methods of Manufacturing the Same (diffuser and exacter insert)” filed on Nov. 10, 2010. The contents of which are incorporated by reference in their entirety.

US Referenced Citations (262)
Number Name Date Kind
99528 Boyd Feb 1870 A
113634 Crispin Apr 1871 A
130679 Whitmore Aug 1872 A
159665 Gauthey Feb 1875 A
169807 Hart Nov 1875 A
462611 Comte de Sparre Nov 1891 A
498856 Overbaugh Jun 1893 A
640856 Bailey Jan 1900 A
662137 Tellerson Nov 1900 A
676000 Hennegerg Jun 1901 A
865979 Bailey Sep 1907 A
869046 Bailey Oct 1907 A
905358 Peters Dec 1908 A
957171 Loeb May 1910 A
963911 Loeble Jul 1910 A
1060817 Clyne May 1913 A
1940657 Woodford Jan 1933 A
2294822 Albree Sep 1942 A
2465962 Allen et al. Mar 1949 A
2654319 Roske Oct 1953 A
2823611 Thayer Feb 1958 A
2862446 Ringdal Dec 1958 A
2918868 Ringdal Dec 1959 A
3170401 Johnson et al. Sep 1962 A
3099958 Daubenspeck et al. Aug 1963 A
3242789 Woodring Mar 1966 A
3292538 Umbach et al. Dec 1966 A
3485170 Scanlon Dec 1969 A
3485173 Morgan Dec 1969 A
3609904 Scanlon Oct 1971 A
3659528 Santala May 1972 A
3688699 Horn et al. Sep 1972 A
3690256 Schnitzer Sep 1972 A
3745924 Scanlon Jul 1973 A
3749021 Burgess Jul 1973 A
3756156 Schuster Sep 1973 A
3765297 Skochko et al. Oct 1973 A
3768413 Ramsay Oct 1973 A
3797396 Reed Mar 1974 A
3842739 Scanlon et al. Oct 1974 A
3866536 Greenberg Feb 1975 A
3874294 Hale Apr 1975 A
3955506 Luther et al. May 1976 A
3977326 Anderson et al. Aug 1976 A
3990366 Scanlon Nov 1976 A
4020763 Iruretagoyena May 1977 A
4147107 Ringdal Apr 1979 A
4157684 Clausser Jun 1979 A
4173186 Dunham Nov 1979 A
4187271 Rolston et al. Feb 1980 A
4228724 Leigh Oct 1980 A
4475435 Mantel Oct 1984 A
4598445 O'Connor Jul 1986 A
4614157 Grelle et al. Sep 1986 A
4679505 Reed Jul 1987 A
4718348 Ferrigno Jan 1988 A
4719859 Ballreich et al. Jan 1988 A
4726296 Leshner Feb 1988 A
4867065 Kaltmann Sep 1989 A
5021206 Stoops Jun 1991 A
5033386 Vatsvog Jul 1991 A
5063853 Bilgeri Nov 1991 A
5090327 Bilgeri Feb 1992 A
5151555 Vatsvog Sep 1992 A
5165040 Andersson et al. Nov 1992 A
5237930 Belanger et al. Aug 1993 A
5247888 Conil Sep 1993 A
5259288 Vatsvog Nov 1993 A
5265540 Ducros et al. Nov 1993 A
5433148 Barratault et al. Jul 1995 A
5535495 Gutowski Jul 1996 A
5563365 Dineen et al. Oct 1996 A
5770815 Watson, Jr. Jun 1998 A
5798478 Beal Aug 1998 A
5950063 Hens et al. Sep 1999 A
5961200 Friis Oct 1999 A
5969288 Baud Oct 1999 A
6004682 Rackovan et al. Dec 1999 A
6048379 Bray Apr 2000 A
6070532 Halverson Jun 2000 A
6272993 Cook et al. Aug 2001 B1
6283035 Olson Sep 2001 B1
6357357 Glasser Mar 2002 B1
6375971 Hansen Apr 2002 B1
6450099 Desgland Sep 2002 B1
6460464 Attarwala Oct 2002 B1
6523476 Riess et al. Feb 2003 B1
6649095 Buja Nov 2003 B2
6708621 Forichon-Chaumet et al. Mar 2004 B1
6752084 Husseini et al. Jun 2004 B1
6840149 Beal Jan 2005 B2
6845716 Husseini et al. Jan 2005 B2
7000547 Amick Feb 2006 B2
7032492 Meshirer Apr 2006 B2
7056091 Powers Jun 2006 B2
7059234 Husseini Jun 2006 B2
7165496 Reynolds Jan 2007 B2
7204191 Wiley Apr 2007 B2
7213519 Wiley et al. May 2007 B2
7232473 Elliott Jun 2007 B2
7299750 Schikora et al. Nov 2007 B2
7353756 Leasure Apr 2008 B2
7380505 Shiery Jun 2008 B1
7383776 Amick Jun 2008 B2
7392746 Hansen Jul 2008 B2
7441504 Husseini et al. Oct 2008 B2
7585166 Buja Sep 2009 B2
7610858 Chung Nov 2009 B2
7750091 Maljkovic et al. Jul 2010 B2
7841279 Reynolds et al. Nov 2010 B2
7930977 Klein Apr 2011 B2
8007370 Hirsch et al. Aug 2011 B2
8056232 Patel et al. Nov 2011 B2
8156870 South Apr 2012 B2
8201867 Thomeczek Jun 2012 B2
8206522 Sandstrom et al. Jun 2012 B2
8240252 Maljkovic Aug 2012 B2
8408137 Battablia Apr 2013 B2
8443730 Padgett May 2013 B2
8511233 Nilsson Aug 2013 B2
8522684 Davies et al. Sep 2013 B2
8540828 Busky et al. Sep 2013 B2
8561543 Burrow Oct 2013 B2
8573126 Klein et al. Nov 2013 B2
8641842 Hafner et al. Feb 2014 B2
8689696 Seeman et al. Apr 2014 B1
8763535 Padgett Jul 2014 B2
8790455 Borissov et al. Jul 2014 B2
8807008 Padgett et al. Aug 2014 B2
8813650 Maljkovic et al. Aug 2014 B2
D715888 Padgett Oct 2014 S
8857343 Marx Oct 2014 B2
8869702 Padgett Oct 2014 B2
8875633 Padgett Nov 2014 B2
8893621 Escobar Nov 2014 B1
8978559 Davies et al. Mar 2015 B2
9003973 Padgett Apr 2015 B1
9032855 Foren et al. May 2015 B1
9091516 Davies Jul 2015 B2
9103641 Nielson et al. Aug 2015 B2
9170080 Poore Oct 2015 B2
9182204 Maljkovic et al. Nov 2015 B2
9200880 Foren et al. Dec 2015 B1
9212876 Kostka et al. Dec 2015 B1
9212879 Whitworth Dec 2015 B2
9213175 Arnold Dec 2015 B2
9254503 Ward Feb 2016 B2
9255775 Rubin Feb 2016 B1
9329004 Pace May 2016 B2
9335137 Maljkovic et al. May 2016 B2
9337278 Gu et al. May 2016 B1
9347457 Ahrens et al. May 2016 B2
9366512 Burczynski et al. Jun 2016 B2
9377278 Rubin Jun 2016 B2
9389052 Conroy et al. Jul 2016 B2
9395165 Maljkovic et al. Jul 2016 B2
D764624 Masinelli Aug 2016 S
D765214 Padgett Aug 2016 S
9429407 Burrow Aug 2016 B2
9441930 Burrow Sep 2016 B2
9453714 Bosarge et al. Sep 2016 B2
9528799 Maljkovic Dec 2016 B2
D778391 Burrow Feb 2017 S
D778393 Burrow Feb 2017 S
D778394 Burrow Feb 2017 S
D778395 Burrow Feb 2017 S
D779024 Burrow Feb 2017 S
10041770 Burrow Aug 2018 B2
10081057 Burrow Sep 2018 B2
20010013299 Husseini et al. Aug 2001 A1
20030101891 Amick Jun 2003 A1
20030217665 Rennard Nov 2003 A1
20040159262 LeaSure Aug 2004 A1
20050005807 Wiley Jan 2005 A1
20050016411 Amick Jan 2005 A1
20050056183 Meshirer Mar 2005 A1
20050188883 Husseini et al. Sep 2005 A1
20050257711 Husseini et al. Nov 2005 A1
20050257712 Husseini et al. Nov 2005 A1
20050268808 Werner Dec 2005 A1
20060027129 Kolb et al. Feb 2006 A1
20060207464 Maljkovic et al. Sep 2006 A1
20060283314 Cesaroni Dec 2006 A1
20070214992 Dittrich Sep 2007 A1
20070261587 Chung Nov 2007 A1
20090042057 Thomas et al. Feb 2009 A1
20090183850 Morrison et al. Jul 2009 A1
20100016518 El-Hibri et al. Jan 2010 A1
20100258023 Reynolds et al. Oct 2010 A1
20100300319 Guindon Dec 2010 A1
20100305261 Maljkovic et al. Dec 2010 A1
20110016717 Morrison et al. Jan 2011 A1
20110179965 Mason Jul 2011 A1
20110226149 Tepe et al. Sep 2011 A1
20120022418 Gamboa et al. Jan 2012 A1
20120024183 Klein Feb 2012 A1
20120111219 Burrow May 2012 A1
20120152101 Engleman et al. Jun 2012 A1
20120180687 Padgett Jul 2012 A1
20120180688 Padgett Jul 2012 A1
20130014664 Padgett Jan 2013 A1
20130180392 Nuetzman et al. Jul 2013 A1
20130186294 Davies Jul 2013 A1
20140060372 Padgett Mar 2014 A1
20140060373 Maljkovic et al. Mar 2014 A1
20140076188 Maljkovic et al. Mar 2014 A1
20140216293 Klein et al. Aug 2014 A1
20140224144 Neugebauer Aug 2014 A1
20140235784 Maljkovic et al. Aug 2014 A1
20140260925 Beach et al. Sep 2014 A1
20140261046 Marx Sep 2014 A1
20140326157 Conroy Nov 2014 A1
20140345488 Schluckebier et al. Nov 2014 A1
20140373744 Padgett Dec 2014 A1
20150007716 MacVicar et al. Jan 2015 A1
20150033970 Maljkovic et al. Feb 2015 A1
20150033990 Yeager Feb 2015 A1
20150036058 Ng et al. Feb 2015 A1
20150075400 Lemke et al. Mar 2015 A1
20150219573 Lukay et al. Aug 2015 A1
20150226220 Bevington Aug 2015 A1
20150241183 Padgett et al. Aug 2015 A1
20150241184 Burrow Aug 2015 A1
20150260490 Burrow Sep 2015 A1
20150260491 Burrow Sep 2015 A1
20150260495 Burrow Sep 2015 A1
20150330756 Ward Nov 2015 A1
20150360587 Hoffmann et al. Dec 2015 A1
20160003587 Burrow Jan 2016 A1
20160003588 Burrow Jan 2016 A1
20160003589 Burrow Jan 2016 A1
20160003590 Burrow Jan 2016 A1
20160003593 Burrow Jan 2016 A1
20160003594 Burrow Jan 2016 A1
20160003595 Burrow Jan 2016 A1
20160003596 Burrow Jan 2016 A1
20160003597 Burrow Jan 2016 A1
20160003601 Burrow Jan 2016 A1
20160033241 Burrow Feb 2016 A1
20160033246 Burrow Feb 2016 A1
20160102030 Coffey et al. Apr 2016 A1
20160131464 Rubin May 2016 A1
20160153757 Mahnke Jun 2016 A1
20160161232 Rubin Jun 2016 A1
20160238355 Dionne et al. Aug 2016 A1
20160245626 Drieling et al. Aug 2016 A1
20160265886 Aldrich et al. Sep 2016 A1
20160273896 Emary Sep 2016 A1
20160349022 Burrow Dec 2016 A1
20160349023 Burrow Dec 2016 A1
20160349028 Burrow Dec 2016 A1
20160356581 Burrow Dec 2016 A1
20160356588 Burrow Dec 2016 A1
20160377399 Burrow Dec 2016 A1
20170080498 Burrow Mar 2017 A1
20170082409 Burrow Mar 2017 A1
20170082411 Burrow Mar 2017 A1
20170089672 Burrow Mar 2017 A1
20170089673 Burrow Mar 2017 A1
20170089674 Burrow Mar 2017 A1
20170089675 Burrow Mar 2017 A1
20170089679 Burrow Mar 2017 A1
Foreign Referenced Citations (13)
Number Date Country
2813634 Apr 2012 CA
16742 Jan 1882 DE
2625486 Aug 2013 EP
783023 Sep 1957 GB
2000034732 Jun 2000 WO
2007014024 Feb 2007 WO
2012047615 Apr 2012 WO
2012097317 Jul 2012 WO
2012097320 Jul 2012 WO
2013070250 May 2013 WO
2013096848 Jun 2013 WO
2014062256 Apr 2014 WO
2016003817 Jan 2016 WO
Non-Patent Literature Citations (3)
Entry
Korean Intellectual Property Office (ISA), International Search Report and Written Opinion for PCT/US2011/062781 dated Nov. 30, 2012, 16 pp.
Korean Intellectual Property Office (ISA), International Search Report and Written Opinion for PCT/US2015/038061 dated Sep. 21, 2015, 28 pp.
AccurateShooter.com Daily Bulletin “New PolyCase Ammunition and Injection-Molded Bullets” Jan. 11, 2015.
Related Publications (2)
Number Date Country
20170089673 A1 Mar 2017 US
20170191807 A9 Jul 2017 US
Provisional Applications (1)
Number Date Country
61456664 Nov 2010 US
Divisions (1)
Number Date Country
Parent 13292843 Nov 2011 US
Child 14011202 US
Continuation in Parts (1)
Number Date Country
Parent 14011202 Aug 2013 US
Child 14863757 US