Polymer coating on substrates using thermal spray techniques

Information

  • Patent Grant
  • 9782956
  • Patent Number
    9,782,956
  • Date Filed
    Thursday, December 27, 2012
    11 years ago
  • Date Issued
    Tuesday, October 10, 2017
    6 years ago
Abstract
A laminate article can include a substrate and a layer of a heterogeneous mixture of a non-fluorinated polymer compound and a fluorinated polymer compound. The laminate article can include a gradual concentration gradient along an axis perpendicular to the substrate. The gradual concentration gradient can include the change of the amount of the non-fluorinated polymer and the fluorinated polymer compound relative to the axis perpendicular to the substrate. The layer can further include at least one filler. The laminate can be applied as a bearing material.
Description
FIELD OF THE DISCLOSURE

The disclosure relates to laminates comprising a substrate, a transition layer comprising a non-fluorinated thermoplastic applied directly thereto and a fluorinated polymer, which can serve as a sliding layer applied to the transition layer.


BACKGROUND

Laminates which comprise a layer structure having a metallic support material, an intermediate layer and a sliding layer applied thereto have been known for a long time in a variety of forms from the prior art and are used in a wide variety of technical fields, for example in the field of automotive engineering.


For slide bearings, especially conventional DU® bearing material, a sliding layer composed of a PTFE compound material is in turn applied to the intermediate layer. In this slide bearing material, the intermediate layer, which has the function of establishing firm adhesion of the sliding layer to the support material, is just a bronze layer sintered from bronze particles. However, this process is problematic for a variety of reasons, including performance limitations of the laminate product and failure in ensuring the combination between PTFE and the support material. As such, there is a continued need for improved laminates for applications such as slide bearings.


Therefore, it would be advantageous if a laminate could be produced that has strong adhesion to the metal support and the sliding layer.


SUMMARY

In a first aspect, a laminate article includes a substrate and a layer. The layer can include a heterogeneous mixture of a non-fluorinated polymer compound and a fluorinated polymer compound. The laminate article can include a gradual concentration gradient along an axis perpendicular to the substrate. The gradual concentration gradient can include the change of the amount of the non-fluorinated polymer and the fluorinated polymer compound relative to the axis perpendicular to the substrate.


In a second aspect, a laminate article can include a substrate and a porous non-fluorinated polymer layer overlying the substrate. The laminate can further include a fluorinated polymer compound layer. The fluorinated polymer compound layer can overlie and penetrate the porous non-fluorinated layer.


In a third aspect, bearing article can include a metal substrate and a discontinuous layer of a non-fluorinated polymer overlying the metal substrate. The bearing article can further include a layer of a fluorinated polymer compound. The fluorinated polymer compound can overlie and penetrate the discontinuous layer.


In a fourth aspect, a bearing material can include a metal substrate having a roughened surface. The bearing material can further include a porous PEEK layer. The bearing material can further include a continuous PTFE composition layer. The continuous PTFE composition layer can overlie and penetrate the porous PEEK layer.


In a fifth aspect, a method of manufacturing a bearing article can include providing a substrate having a major surface and roughening the major surface of the substrate. The method can further include applying a layer of a non-fluorinated polymer onto the major surface. The method can further include coating the non-fluorinated polymer layer with a fluoropolymer composition to form a laminate. The method can further include pressing the laminate to form the bearing article.





BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.



FIG. 1 shows an exemplary laminate in sectional view; and



FIG. 2 shows a process for forming a laminate.



FIG. 3 shows results of tribological tests for laminate samples.





The use of the same reference symbols in different drawings indicates similar or identical items.


DETAILED DESCRIPTION

In one embodiment, a laminate article includes a substrate. The laminate can further include a layer comprising a heterogeneous mixture. The heterogeneous mixture can further include a non-fluorinated polymer compound. Moreover, the heterogeneous mixture can include a fluorinated polymer compound. The laminate article can include a gradual concentration gradient along an axis perpendicular to the substrate. The gradual concentration gradient includes a change of an amount of the non-fluorinated polymer and the fluorinated polymer compound relative to the axis perpendicular to the substrate.



FIG. 1 shows an exemplary laminate in sectional view. Layer 102 depicts a fluorinated polymer compound, such as PTFE, overlying non-fluorinated polymer layer material 106, which in this example is PEEK. The fluorinated polymer compound of layer 102 and the fluorinated compound can penetrate layer 106, thereby forming mixed regions 104. Layer 106 overlies substrate 108.


Addressing the substrate 108 of the laminate, in embodiments, the substrate can include a metal substrate or metal alloy substrate. The metal substrate can include a metal or a metal alloy. In one particular embodiment, the metal substrate can include aluminium. In another particular embodiment, the metal alloy substrate can include steel, bronze, or brass. In embodiments, the metal support includes steel, cold-rolled steel material No. 1.0338, cold-rolled steel material No. 1.0347, matt zinc-plated steel, stainless steel material No. 1.4512, stainless steel material No. 1.4720, stainless steel material No. 1.4310, aluminum, alloys, or any combinations thereof.


Further addressing the substrate 108, the substrate can have a surface roughness of at least about 0.5 microns, such as at least about 1 micron, at least about 5 microns, at least about 10 microns, or at least about 100 microns. In another embodiment, the substrate can have a surface roughness of not greater than about 500 microns, such as not greater than about 200 microns, not greater than about 100 microns, not greater than about 80 microns, or even not greater than about 40 microns. Moreover, it will be appreciated that the total surface roughness of substrate 108 can be within a range between any of the minimum and maximum values noted above.


In yet another embodiment, the substrate 108 can be pretreated to have a desired surface roughness. In one instance, substrate 108 can include a surface feature. For example, for metal or metal alloy substrates, the major surface can include a structured plate, a ribbed sheet, a woven fabric, a mesh, or metal foam. In a particular embodiment, the metal or metal alloy substrate has a honeycomb surface feature. In yet other embodiments, the surface of a metal substrate can be treated by electrolytic zinc-plating to roughen, upgrade, or coat the surface. In other embodiments, the major surface of the metal support can be increased by mechanical structuring. The structuring can include brush-finishing, sand-blasting, etching, perforating, pickling, punching, pressing, curling, deep drawing, decambering, incremental sheet forming, ironing, laser cutting, rolling, hammering, embossing, undercutting, and any combinations thereof.


Addressing layer 106 formed by the non-fluorinated polymer compound, in embodiments, the non-fluorinated polymer compound forms a porous or discontinuous non-fluorinated polymer layer overlying the substrate 108. The non-fluorinated polymer layer can have a porosity, defined as the ratio of void volume over total volume of non-fluorinated polymer and determined after applying the non-fluorinated polymer as layer 106 to the substrate 108 and before any further processing.


The porosity may be in the form of open porosity defining an interconnected network of channels extending throughout the layer 106. Alternatively, the layer 106 may include a content of closed porosity described and characterized by discrete and individual pores separated from each other. In at least one embodiment, layer 106 can include a mix of open porosity and closed porosity.


The amount of porosity within the layer can comprise a majority content, such as greater than 50 vol % for the total volume of layer 106. In still other instances, layer 106 may include a minority content of porosity, which can represent less than 50 vol % of the total volume of the layer. Furthermore, the body may contain a majority content of closed porosity. Still, in other instances, the bonded abrasive body may contain a majority content of open porosity.


In certain instances, the porosity may be not greater than about 70 vol % for the total volume of layer 106. In yet other instances, layer 106 may be formed such that the amount of porosity is not greater than about 60 vol %, such as not greater than about 50 vol %, not greater than about 40 vol %, not greater than about 30 vol %, not greater than about 25 vol %, not greater than about 20 vol %, not greater than about 15 vol %, not greater than about 10 vol %, not greater than about 5 vol %, or even not greater than about 2 vol % In at least one non-limiting embodiment, layer 106 may contain an amount of porosity of at least about 1 vol %, such as at least about 5 vol %, at least at about 10 vol %, at least about 20 vol %, at least about 30 vol %, or even at least about 40 vol % Moreover, it will be appreciated that the total amount of porosity within layer 106 can be within a range between any of the minimum and maximum percentages noted above.


Still referring to layer 106, in other embodiments, the non-fluorinated polymer compound forms a discontinuous layer. A discontinuous layer provides the basis for a concentration gradient. A concentration gradient in a cross-section of a laminate is the difference of the amount of one ingredient between two adjacent unit cells. A gradual concentration gradient is established when the amount of ingredient decreases or increases subsequently in three adjacent unit cells, wherein the three unit cells are aligned along an axis.


As shown in FIG. 1, unit cells 110, 112, and 114 are aligned along an axis that is perpendicular to substrate 108. The unit cells have the edge length a. The edge length a can vary and can be a fraction of the average thickness of layer 106. For example, edge length a can be a third, a fourth, a fifth, or even a sixth of the average thickness of layer 106. In other embodiments, edge length can be at least about 2 microns, such as at least about 4 microns, or even about 8 microns. In other embodiments, edge length a can be not greater than about 20 microns, such as not greater than about 15 microns, or even not greater than about 10 microns. In other embodiments, edge length a is selected in such a way that three adjacent unit cells along an axis perpendicular to substrate 108 cover at least about 0.7, such as at least about 0.8, or even at least about 0.9 of the average thickness of layer 106. In other embodiments, edge length a is selected is such a way that three adjacent unit cells along an axis perpendicular to substrate 108 cover not greater than about 0.99, such as not greater than about 0.98, or even not greater than about 0.95 of the average thickness of layer 106.


For a gradual concentration gradient, unit cells 110, 112, and 114 contain different amounts of the non-fluorinated polymer compound, wherein the amount is decreasing along the axis perpendicular to substrate 108. In one embodiment, for a gradual concentration gradient, the amount of non-fluorinated polymer in unit cell 114 is less than in unit cell 112 and the amount of non-fluorinated polymer in unit cell 112 is less than in unit cell 110. The amount of non-fluorinated polymer compound can be determined by integrating the area occupied by layer 106 over total unit cell area a2.


In another embodiment, layer 106 can occupy a majority, such as at least about 50%, such as at least about 70%, or even at least about 90% and not greater than about 99.9%, such as not greater than about 98%, or not greater than about 95% of unit cell area a2 in unit cell 110. In another embodiment, layer 106 can occupy at least about 30%, such as at least about 40%, or even at least about 50% and not greater than about 90%, such as not greater than about 80%, or even not greater than about 70% of unit cell area a2 in unit cell 112. In another embodiment, layer 106 can occupy a minority, such as at least about 1%, such as at least about 2%, or even at least about 5% and not greater than about 50%, such as not greater than about 40%, or even not greater than about 30% of unit cell area a in unit cell 114.


Further addressing layer 106 and the material comprising that layer, the non-fluorinated polymer compound can include a poly-ether-ether-ketone (PEEK), an ultra-high-molecular-weight polyethylene (UHMWPE), a polyimide (PI), a polyamide (PA), a polyamideimde (PAI), a polyphenylsulfide (PPS), a polyhydroxybutyrate (PHB), and any combination thereof. In one particular embodiment, the non-fluorinated polymer compound consists essentially of a poly-ether-ether-ketone (PEEK).


Moving to element 102 in FIG. 1 which comprises the fluorinated polymer compound, the fluorinated polymer compound can include polytetrafluoroethylene (PTFE), a perfluoroalkoxy polymer (PFA), fluorinated ehylene-propylene (FEP), polyvinylfluoride (PVF), polyvinylidene fluoride (PVDF), polychlorotrifluoroethylene (PCTFE), a polyethylenetetrafluoroethylene (ETFE), a polyethylenechlorotrifluoroethylene (ECTFE), and any combination thereof. In one particular embodiment, the fluorinated polymer compound consists essentially of polytetrafluoroethylene (PTFE).


The combined thickness of layers 106 and 102 (including mixed zones 104) can be at least about 2 microns, such as at least about 5 microns, at least about 10 microns, at least about 20 microns, at least about 40 microns, at least about 80 microns, or even at least about 120 microns. In another embodiment, the combined thickness of layers can be not greater than about 1 mm, such as not greater than about 800 microns, not greater than about 500 microns, not greater than about 300 microns, not greater than about 200 microns, or not greater than about 150 microns. Moreover, it will be appreciated that the combined thickness of layers 106 and 102 can be within a range between any of the minimum and maximum percentages noted above.


Addressing the average thickness of layer 106. In instances, the thickness of the non-fluorinated polymer compound layer 106 can be at least about 1 micron, such as at least about 2 microns, at least about 5 microns, at least about 10 microns, at least about 20 microns, at least about 30 microns, at least about 50 microns, at least about 70 microns, or at least about 100 microns. In other instances, the porous non-fluorinated polymer layer 106 can have a thickness of not greater than about 800 microns, such as not greater than about 500 microns, such as not greater than about 300 microns, not greater than about 200 microns, not greater than about 180 microns, not greater than about 150 microns, or not greater than about 120 microns. Moreover, it will be appreciated that the average thickness of layer 106 can be within a range between any of the minimum and maximum thicknesses noted above.


Addressing the average thickness of layer 102, the fluorinated polymer compound layer can have a thickness of at least about 2 microns, such as at least about 5 microns, at least about 10 microns, at least about 20 microns, at least about 30 microns, at least about 50 microns, at least about 70 microns, or at least about 90 microns. In other instances, the fluorinated polymer compound layer 102 can have a thickness of not greater than about 800 microns, such as not greater than about 500 microns, not greater than 300 microns, not greater than about 200 microns, not greater than about 180 microns, not greater than about 150 microns, or not greater than about 120 microns. Moreover, it will be appreciated that the average thickness of layer 102 can be within a range between any of the minimum and maximum thicknesses noted above.


Addressing the weight amounts of the various layer materials, in embodiments, the non-fluorinated polymer compound can include at least about 5 wt %, such as at least about 10 wt %, at least about 20 wt %, or at least about 30 wt % of the combined weight of layers 102 and 106 (including mixed zones 104). In other embodiments, the non-fluorinated polymer compound can include not greater than about 80 wt %, such as not greater than about 60 wt %, or not greater than about 40 wt % of the combined weight of layers 102 and 106 (including mixed zones 104).


In yet other embodiments, the amounts of the layer materials included in layer 102 and 106 can be addressed by volumetric amounts. In embodiments, the non-fluorinated polymer comprises at least about 5 vol %, such as at least about 10 vol %, at least about 20 vol %, at least about 30 vol %, or at least about 40 vol % of the total volume of the layers 102 and 106, which includes mixed zones 104 and any closed porosity (not shown in FIG. 1). In other embodiments, the non-fluorinated polymer comprises not greater than about 90 vol %, such as not greater than about 80 vol %, not greater than about 60 vol %, not greater than about 40 vol %, or not greater than about 30 vol % of the total volume of the non-fluorinated polymer layer and the fluorinated layer.


In instances, the non-fluorinated compound or the fluorinated layer can include at least one filler. The filler can include fibers, glass fibers, carbon fibers, aramids, inorganic materials, ceramic materials, carbon, glass, graphite, aluminum oxide, molybdenum sulfide, bronze, silicon carbide, woven fabric, powder, sphere, thermoplastic material, polyimide (PI), polyamidimide (PAI), polyphenylene sulfide (PPS), polyethersulofone (PES), polyphenylene sulfone (PPSO2), liquid crystal polymers (LCP), polyetherketone (PEK), polyether ether ketones (PEEK), aromatic polyesters (Ekonol), mineral materials, wollastonite, barium sulfate, or any combinations thereof.


The filler can be present in different amounts in each polymer compound. In embodiments, the amount of filler can be at least about 1 vol %, such as at least about 2 vol %, at least about 5 vol %, at least about 10 vol %, at least about 20 vol %, or even at least about 30 vol % of the total volume of the polymer compound. In other embodiments, the filler can be present at not greater than about 90 vol %, such as not greater than about 75 vol %, not greater than about 60 vol %, not greater than about 50 vol %, or not greater than about 40 vol % of the total volume of the polymer compound. Moreover, it will be appreciated that the amount of the at least one filler can be within a range between any of the minimum and maximum volume percentages noted above.


In yet further embodiments, the polymer compounds can include an additive. The additives can include softeners, lubricants, plasticizers, dispersants, UV absorbers, or any other agent necessary to improve the applicability of the laminate article. In embodiments, the additives can include fluoropolymers.


In embodiments, the laminate includes bearing articles. In a particular embodiment, the laminate includes slide bearings. Bearings can be prepared in a vast number of very different shapes and sizes. The smallest bearing, also called a pico bearing, is only a few μm in height compared to bearings for other applications that could be up to 500 mm.


Bearings can include plane bearings, annular bearings, bushings, balljoint bearings (half spheres), plain bearings, axial bearings, thrust bearings, linear bearings, bearing shells, bearing cups and combinations thereof.


In one embodiment, laminates as described herein are maintenance free. The term “maintenance-free” describes laminates that do not need to be greased as was the case for bearings in early car doors. Yet, the life time of maintenance-free bearings exceeds the average life time of the product these bearings are incorporated or the life time of conventional bearings applied for the same purpose.


In one particular embodiment, a bearing article includes a PEEK layer, wherein the PEEK layer is porous. The porosity, which is the ratio of void volume over total volume of the PEEK layer, can be at least about 0.05, such as at least about 0.1, or at least about 0.2. The porosity can be no greater than about 0.8, such as no greater than about 0.7, or not greater than about 0.5.


In one embodiment, the bearing article includes a PTFE composition layer with a thickness of at least about 10 microns, such as at least about 20 microns, at least about 30 microns, at least about 50 microns, or at least about 70 microns. In another embodiment, the bearing article includes a PTFE composition layer with a thickness of not greater than about 500 microns, such as not greater than about 400 microns, not greater than about 300 microns, not greater than about 200 microns, not greater than 180 microns, or not greater than about 150 microns.


In one embodiment, the bearing article includes a PEEK in an amount of at least about 10 vol %, such as at least about 20 vol %, at least about 40 vol %, or at least about 50 vol % of the combined polymer layers, i.e. the combination of the PEEK layer and the PTFE composition layer. In another embodiment, the bearing article includes a PEEK layer in an amount of not greater than about 80 vol %, such as not greater than about 70 vol %, not greater than about 60 vol %, or not greater than about 50 vol % of the combined layers, i.e. the combination of the PEEK layer and the PTFE composition layer.


In yet another embodiment, the bearing article has PTFE composition layer which further includes a filler. The filler can include fibers, glass fibers, carbon fibers, aramids, inorganic materials, ceramic materials, carbon, glass, graphite, aluminum oxide, molybdenum sulfide, bronze, silicon carbide, woven fabric, powder, sphere, thermoplastic material, polyimide (PI), polyamidimide (PAI), polyphenylene sulfide (PPS), polyethersulofone (PES), polyphenylene sulfone (PPSO2), liquid crystal polymers (LCP), polyetherketone (PEK), polyether ether ketones (PEEK), aromatic polyesters (Ekonol), mineral materials, wollastonite, barium sulfate, or any combinations thereof.


In one embodiment, a method of forming a bearing article can include providing a substrate having a major surface. The method can further include roughening the major surface of the substrate. The method can further include applying a layer of a non-fluorinated polymer onto the major surface. The method can also include coating the non-fluorinated polymer layer with a fluoropolymer composition to form a laminate. Furthermore, the method can include pressing the laminate to form the bearing article.



FIG. 2 shows an exemplary process for forming a laminate. A metal substrate 202 including a roughened surface is thermally (205) sprayed with a non-fluorinated powder 204. The spraying is conducted through device 206 capable of thermal spraying. Thermal spraying creates a porous layer 214 of the non-fluorinated polymer. The porous layer 214 can be sprayed to any desired thickness. The amount of non-fluorinated polymer applied can be made dependent from properties such as desired adhesion strength to the metal backing or other properties, e.g., electrical insulation, which may require a thicker layer. After the thermal spraying of the non-fluorinated polymer layer, the layer is smoothened by skimming board 208. Next, a fluorinated polymer compound powder 212 from applicator 210 is applied onto the porous layer 214. The fluorinated polymer compound can include any of the fluorinated polymer compounds described herein or a mixture of a fluoropolymer with another polymer, filler, surface agent, softening agent, plasticizer, or any other beneficial agent.


The fluorinated polymer compound layer can be applied to any desired thickness depending from its application purpose. The fluoropolymer compound layer can be sprayed, brushed, paint coated, or applied by any conventional process onto the porous layer 214. For example, as shown in FIG. 2 the fluoropolymer can be sprayed. In embodiments, the non-fluorinated polymer compound and the fluorinated polymer compound can be sprayed subsequently as shown in FIG. 2, concurrent (not shown in FIG. 2) or partially concurrent (not shown in FIG. 2). With respect to the partial concurrent spraying, there is a phase when the non-fluorinated polymer compound is sprayed, a phase when the non-fluorinated polymer compound and the fluorinated polymer compound is applied concurrently, and a phase when the fluorinated polymer compound is applied.


Upon application of the fluoropolymer compound powder, the assembly undergoes pressure and/or heat treatment. As shown in FIG. 2, the assembly can be pressed through rolls 216. In another embodiment, rolls 216 can also be heated, thereby calendering the assembly. Heat 220 can be applied with heater 218. Optionally, after heat treatment, the assembly can be pressed or calendered by rolls 220 to form compound layer 224. In other embodiments and not shown in FIG. 2, the assembly can undergo cold rolling followed by polymer or plastic sintering.


Addressing the non-fluorinated polymer powder, the non-fluorinated polymer can include a poly-ether-ether-ketone (PEEK), an ultra-high-molecular-weight polyethylene (UHMWPE), a polyimide (PI), a polyamide (PA), a polyamideimde (PAI), a polyphenylsulfide (PPS), a polyhydroxybutyrate (PHB), and any combination thereof. In one embodiment, the non-fluorinated polymer consists essentially of poly-ether-ether-ketone (PEEK).


The non-fluorinated powder can have an average particle size of at least about 1 micron, such as at least about 2 microns, at least about 5 microns, or even about 10 microns. In another embodiment, the non-fluorinated powder can have an average particle size of not greater than about 100 microns, such as not greater than about 80 microns, not greater than about 60 microns, or even not greater than about 40 microns.


In another embodiment, the method can include spraying the substrate with a non-fluorinated polymer powder to form the layer 214 to a thickness of not greater than about 800 microns, such as not greater than about 500 microns, not greater than about 400 microns, not greater than about 300 microns, not greater than about 200 microns, not greater than 180 microns, or not greater than about 150 microns. In one embodiment, the method includes spraying the metal substrate with a non-fluorinated polymer powder to form layer 214 to a thickness of at least about 5 microns, such as at least 10 microns, at least about 20 microns, at least about 30 microns, at least about 50 microns, or at least about 70 microns. In embodiments, the method includes applying the non-fluorinated polymer by thermal spraying or by flame spraying the non-fluorinated polymer.


Addressing the fluorinated polymer powder, the fluorinated polymer compound can include a polytetrafluoroethylene (PTFE), a perfluoroalkoxy polymer (PFA), fluorinated ehylene-propylene (FEP), polyvinylfluoride (PVF), polyvinylidene fluoride (PVDF), polychlorotrifluoroethylene (PCTFE), a polyethylenetetrafluoroethylene (ETFE), a polyethylenechlorotrifluoroethylene (ECTFE), or any combination thereof. In one embodiment, the fluorinated polymer compound consists essentially of polytetrafluoroethylene.


The fluorinated polymer powder can have an average particle size of at least about 1 micron, such as at least about 2 microns, at least about 5 microns, or even about 10 microns. In another embodiment, the non-fluorinated powder can have an average particle size of not greater than about 100 microns, such as not greater than about 80 microns, not greater than about 60 microns, or even not greater than about 40 microns.


The fluorinated polymer powder can be applied as dispersion or in dry form. The method includes coating the fluorinated polymer powder by spray coating or paint coating.


In another embodiment, the method can further include heat rolling the laminate layer. In another embodiment, the method can include heat pressing or calendaring the laminate.


In one embodiment, the non-fluorinated layer and the fluorinated layer have a combined thickness of at least about 20 microns, such as at least about 40 microns, at least about 80 microns, or at least about 100 microns. In another embodiment, the combined thickness is not greater than about 1 millimeter, such as not greater than about 500 microns, or at not greater than about 300 microns.


EXAMPLES

High performance non-fluorinated polymers, such as PEEK have favorable properties such as chemical resistance, electric insulation, self-lubrication, or durability against stress. Fluorinated polymers such as PTFE have favorable properties such as chemical resistance, heat resistance, and low friction.


Example 1

An aluminum metal backing was sandblasted at 3 bar to a surface roughness Ra of 3 microns to 4 microns. PEEK with an average particle size of about 20 microns was thermally sprayed onto sandblasted aluminum substrate. Thermal spraying was conducted with an ABB robot 4400. PEEK was flame sprayed using a Castodyn 8000 torch with a M40 nozzle. The spraying distance was between 100 and 300 mm and the nozzle scanning speed was regulated between 150 and 400 mm/s. The scanning steps were regulated between 1 and 5 mm. Between 1 and 5 passes were run over the substrate. After that a PTFE compound was applied with a paint spray gun. The PTFE compound was sprayed from a distance between 100 and 300 mm, with a spray speed between 150 and 400 mm/s, and for 1 to 5 passes. Afterwards, the assembly was sintered at 340° C. for 10 minutes and 430° C. for 5 minutes.


Tribological testing was conducted using a CSM ball-on-disk tribometer using a load of 5N at a speed of 70 cm/s, a ball having a radius of 12 mm. The tests were run over a distance of 2000 m. The results for three samples are summarized in FIG. 3.


Tribological testing results show that COF (Coefficient of Friction) all samples of PEEK/PTFE coatings show substantially constant COF values over the complete duration of the testing. The end values for COF were between 0.125 and 0.175. Although not illustrated in FIG. 3, the end of test COF values for all PEEK/PTFE coatings were lower than the end of test COF values for single PEEK layers (no PTFE coating) or for single PTFE layers (no PEEK layer).


Note that not all of the activities described above in the general description or the examples are required, that a portion of a specific activity may not be required, and that one or more further activities may be performed in addition to those described. Still further, the order in which activities are listed are not necessarily the order in which they are performed.


In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below. Accordingly, the specification and FIGS. are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of invention.


As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of features is not necessarily limited only to those features but may include other features not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive-or and not to an exclusive-or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).


Also, the use of “a” or “an” are employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.


The term “averaged,” when referring to a value, is intended to mean an average, a geometric mean, or a median value.


Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.


After reading the specification, skilled artisans will appreciate that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, references to values stated in ranges include each and every value within that range.

Claims
  • 1. A laminate article, comprising a substrate layer comprising a metal or a metal alloy; anda polymer layer comprising: a stand-alone layer of a non-fluorinated polymer compound having a thickness of at least about 20 microns, the stand-alone layer being disposed directly adjacent to and contacting the substrate without an intervening support layer therebetween, the stand-alone layer comprising a plurality of interconnected voids making up at least 10 vol. % of the total volume of the stand-alone layer, anda fluorinated polymer compound covering the stand-alone layer and filling at least a portion of the interconnected voids of the stand-alone layer;wherein the concentration of the fluorinated polymer compound in the polymer layer increases in a direction perpendicular to, and moving away from, the substrate layer such that the polymer layer includes a gradual concentration gradient that includes a change of an amount of the non-fluorinated polymer compound and the fluorinated polymer compound relative to an axis perpendicular to the substrate.
  • 2. The laminate according to claim 1, wherein the non-fluorinated polymer compound is selected from a poly-ether-ether-ketone (PEEK), an ultra-high-molecular-weight polyethylene (UHMWPE), a polyimide (PI), a polyamide (PA), a polyamideimide (PAI), a polyphenylsulfide (PPS), a polyhydroxybutyrate (PHB), and any combination thereof.
  • 3. The laminate according to claim 1, wherein the non-fluorinated polymer compound consists essentially of a poly-ether-ether-ketone.
  • 4. The laminate according to claim 1, wherein the fluorinated polymer compound is selected from polytetrafluoroethylene (PTFE), a perfluoroalkoxy polymer (PFA), fluorinated ehylene-propylene (FEP), polyvinylfluoride (PVF), polyvinylidene fluoride (PVDF), polychlorotrifluoroethylene (PCTFE), a polyethylenetetrafluoroethylene (ETFE), a polyethylenechlorotrifluoroethylene (ECTFE), or any combination thereof.
  • 5. The laminate according to claim 1, wherein the fluorinated polymer compound consists essentially of polytetrafluoroethylene.
  • 6. The laminate according to claim 1, wherein a combined thickness of the stand-alone layer and the fluorinated polymer compound is at least about 30 microns.
  • 7. The laminate according to claim 1, wherein a combined thickness of the stand-alone layer and the fluorinated polymer compound is not greater than about 1 mm.
  • 8. The laminate according to claim 1, wherein the non-fluorinated polymer compound comprises at least about 10 wt % of the combined weight of the stand-alone layer and the fluorinated polymer compound.
  • 9. The laminate according to claim 1, wherein the non-fluorinated polymer compound comprises not greater than about 80 wt % of the combined weight of the stand-alone layer and the fluorinated polymer compound.
  • 10. The laminate according to claim 1, wherein the stand-alone layer, the fluorinated polymer compound, or both, further includes a filler.
  • 11. The laminate according to claim 10, wherein the filler comprises a filler selected from the group consisting of fibers, glass fibers, carbon fibers, aramids, inorganic materials, ceramic materials, carbon, glass, graphite, aluminum oxide, molybdenum sulfide, bronze, silicon carbide, woven fabric, powder, sphere, thermoplastic material, polyimide (PI), polyamidimide (PAI), polyphenylene sulfide (PPS), polyethersulofone (PES), polyphenylene sulfone (PPSO2), liquid crystal polymers (LCP), polyetherketone (PEK), polyether ether ketones (PEEK), aromatic polyesters (Ekonol), mineral materials, wollastonite, barium sulfate, and any combinations thereof.
  • 12. The laminate according to claim 1, wherein the substrate layer has a surface roughness of from 1 micron to 200 microns.
  • 13. The laminate according to claim 1, wherein the non-fluorinated polymer compound further includes a softener or plasticizer.
  • 14. The laminate according to claim 13, wherein the softener or the plasticizer includes a fluoropolymer.
  • 15. The laminate according to claim 1, wherein the voids make up at least about 20 vol. % of the stand-alone layer.
  • 16. The laminate according to claim 1, wherein the laminate consists of the substrate and the polymer layer.
  • 17. A bearing article, comprising a continuous substrate comprising a metal or a metal alloy;a polymer layer comprising: a stand-alone layer of a non-fluorinated polymer compound having a thickness of at least about 20 microns, the stand-alone layer being disposed directly adjacent to and contacting the substrate without an intervening support layer therebetween, the stand-alone layer comprising a plurality of interconnected voids making up at least 10 vol. % of the total volume of the stand-alone layer, anda fluorinated polymer compound covering the stand-alone layer and filling at least a portion of the interconnected voids of the stand-alone layer;wherein the concentration of the fluorinated polymer compound in the polymer layer increases in a direction perpendicular to, and moving away from, the substrate layer such that the polymer layer includes a gradual concentration gradient that includes a change of an amount of the non-fluorinated polymer compound and the fluorinated polymer compound relative to an axis perpendicular to the substrate.
  • 18. The bearing article of claim 17, wherein the substrate has a roughened surface.
  • 19. The bearing article of claim 18, wherein the substrate layer has a surface roughness in a range of from about 1 micron to about 200 microns.
Priority Claims (1)
Number Date Country Kind
11 04125 Dec 2011 FR national
CROSS-REFERENCE TO RELATED APPLICATIONS

The following disclosure is a non-provisional application which claims priority to French Application No. 11/04125, filed Dec. 28, 2011, entitled “POLYMER COATING ON SUBSTRATES USING THERMAL SPRAY TECHNIQUES” and having named inventors Hanlin Liao, Camelia Demian, Lianxiang Wang and Xiaoye Liu, and further claims priority to U.S. Provisional Application No. 61/681,421, filed Aug. 9, 2012, entitled “POLYMER COATING ON SUBSTRATES USING THERMAL SPRAY TECHNIQUES” and having named inventors Hanlin Liao, Camelia Demian, Lianxiang Wang and Xiaoye Liu, the applications of which are incorporated by reference herein in their entirety.

US Referenced Citations (134)
Number Name Date Kind
3692558 Werner Sep 1972 A
3697309 Werner Oct 1972 A
3911161 Nord et al. Oct 1975 A
4011361 Vassiliou et al. Mar 1977 A
4016125 Vassiliou et al. Apr 1977 A
4039713 Vassiliou et al. Aug 1977 A
4049863 Vassiliou et al. Sep 1977 A
4070525 Vassiliou et al. Jan 1978 A
4319942 Brenner Mar 1982 A
4413019 Brenner Nov 1983 A
4483951 Brenner Nov 1984 A
4548989 Allen et al. Oct 1985 A
4592782 Davies Jun 1986 A
4595718 Allen et al. Jun 1986 A
4624887 Bickle et al. Nov 1986 A
4655944 Mori Apr 1987 A
4812367 Bickle Mar 1989 A
4868234 Tabb et al. Sep 1989 A
4925892 Tabb et al. May 1990 A
5039575 Mori et al. Aug 1991 A
5230961 Tannenbaum Jul 1993 A
5239026 Babirad et al. Aug 1993 A
5364682 Tanaka et al. Nov 1994 A
5573846 Harig et al. Nov 1996 A
5686176 Adam et al. Nov 1997 A
5863657 Kawashima et al. Jan 1999 A
5882466 Grootaert et al. Mar 1999 A
6001205 Mauro Dec 1999 A
6085797 Grabaum et al. Jul 2000 A
6140410 Kolouch Oct 2000 A
6183137 Kojima et al. Feb 2001 B1
6183869 Okuda et al. Feb 2001 B1
6258413 Woelki et al. Jul 2001 B1
6312814 Kolouch Nov 2001 B1
6316534 Shimokusuzono et al. Nov 2001 B1
6372284 Hess et al. Apr 2002 B1
6376061 Adam Apr 2002 B1
6413588 Pettus et al. Jul 2002 B1
6425977 McDonald et al. Jul 2002 B2
6528143 Adam Mar 2003 B1
6531950 Becker et al. Mar 2003 B1
6565257 Kennedy et al. May 2003 B1
6569816 Oohira et al. May 2003 B2
6726994 Araki et al. Apr 2004 B1
6759129 Fukushi Jul 2004 B2
6770378 Lehmann Aug 2004 B1
7022402 Lacourt Apr 2006 B2
7025853 Kesselmayer Apr 2006 B2
7241817 Bonnet et al. Jul 2007 B2
7491446 Ueda et al. Feb 2009 B2
7581734 McLeod Sep 2009 B1
7829618 Longo et al. Nov 2010 B2
7887922 Mayston et al. Feb 2011 B2
7910527 Sawyer et al. Mar 2011 B2
7942581 Leonardelli May 2011 B2
8349773 Takayanagi et al. Jan 2013 B2
8646977 Adam Feb 2014 B2
8802602 Schmitjes et al. Aug 2014 B2
20020117280 Howle et al. Aug 2002 A1
20030024380 Shimo et al. Feb 2003 A1
20030044553 Ramanathan et al. Mar 2003 A1
20030049485 Brupbacher et al. Mar 2003 A1
20030079847 Howle et al. May 2003 A1
20030104223 Ferm et al. Jun 2003 A1
20030158338 Jazenski et al. Aug 2003 A1
20030207118 Fukushi Nov 2003 A1
20040006867 Becker et al. Jan 2004 A1
20040071987 Bate Apr 2004 A1
20040096610 Ramanathan et al. May 2004 A1
20040115465 Bickle et al. Jun 2004 A1
20040115477 Nesbitt Jun 2004 A1
20040116792 Nesbitt Jun 2004 A1
20040167263 Bate Aug 2004 A1
20040228555 Kim et al. Nov 2004 A1
20050025977 Adam et al. Feb 2005 A1
20050048218 Weidman Mar 2005 A1
20050069778 Bonnet et al. Mar 2005 A1
20050090602 Koshikawa Apr 2005 A1
20050228441 Wood et al. Oct 2005 A1
20050233152 Bate Oct 2005 A1
20050266170 Nesbitt Dec 2005 A1
20060029795 Sawyer Feb 2006 A1
20060110601 Hennessey May 2006 A1
20060229424 Griswold et al. Oct 2006 A1
20060247360 Halasa et al. Nov 2006 A1
20060247369 Griswold et al. Nov 2006 A1
20060247370 Frye et al. Nov 2006 A1
20070021544 Yanase et al. Jan 2007 A1
20070031275 Nogawa et al. Feb 2007 A1
20070092173 Tsuji et al. Apr 2007 A1
20070106294 Nesbitt May 2007 A1
20070110937 Lokere et al. May 2007 A1
20070123853 Nesbitt May 2007 A1
20070173590 Longo et al. Jul 2007 A1
20070177833 Egami et al. Aug 2007 A1
20070225177 Murase Sep 2007 A1
20070232502 Tsutsui Oct 2007 A1
20070269151 Nardi Nov 2007 A1
20070281872 Schubert et al. Dec 2007 A1
20070298217 Chen et al. Dec 2007 A1
20080032060 Nesbitt Feb 2008 A1
20080050509 Nesbitt Feb 2008 A1
20080057251 Griswold et al. Mar 2008 A1
20080102307 Zidar May 2008 A1
20080113206 Hoy et al. May 2008 A1
20080159671 Leonardelli Jul 2008 A1
20080226933 Bickle et al. Sep 2008 A1
20090092827 Robinson Apr 2009 A1
20090304957 Jamil et al. Dec 2009 A1
20100028684 Mariscal et al. Feb 2010 A1
20100047467 Nesbitt Feb 2010 A1
20100092119 Angenheister Apr 2010 A1
20100098360 Schmitjes et al. Apr 2010 A1
20100119188 Hsueh et al. May 2010 A1
20100197849 Momose et al. Aug 2010 A1
20100215834 Nesbitt Aug 2010 A1
20100239883 Okladek et al. Sep 2010 A1
20100290726 Schlipf et al. Nov 2010 A1
20100301525 Price et al. Dec 2010 A1
20100304063 McCrea et al. Dec 2010 A1
20110023726 Nesbitt Feb 2011 A1
20110049834 Hatu Mar 2011 A1
20110159229 Doehle et al. Jun 2011 A1
20110262064 Burgeff et al. Oct 2011 A1
20110268944 Adam et al. Nov 2011 A1
20110305874 Thoumazet et al. Dec 2011 A1
20120008887 Adam Jan 2012 A1
20120275731 Ziegler et al. Nov 2012 A1
20130183488 Liao et al. Jul 2013 A1
20130183539 Guo et al. Jul 2013 A1
20130195388 Ishii et al. Aug 2013 A1
20140010484 Schmitjes Jan 2014 A1
20140024563 Heidecker et al. Jan 2014 A1
20140329728 Peng et al. Nov 2014 A1
Foreign Referenced Citations (87)
Number Date Country
1322747 Oct 1993 CA
2152279 Jul 1994 CA
2684543 Oct 2008 CA
1037481 Feb 1998 CN
1261386 Jul 2000 CN
1401898 Mar 2003 CN
1705830 Dec 2005 CN
1756911 Apr 2006 CN
1823132 Aug 2006 CN
101061191 Oct 2007 CN
101715392 Oct 2010 CN
101126417 Dec 2010 CN
101413543 Jun 2011 CN
102271906 Dec 2011 CN
3021369 Dec 1981 DE
3343697 Jun 1984 DE
3401804 Jul 1985 DE
39 12 716 Oct 1990 DE
19823609 Dec 1999 DE
102005046571 Apr 2007 DE
10 2008 055 194 Jul 2010 DE
0119815 Sep 1984 EP
0232922 Jun 1986 EP
0008542 Nov 1988 EP
0223268 Mar 1989 EP
0394518 Oct 1990 EP
0650987 May 1995 EP
0848031 Jun 1998 EP
0988898 Mar 2000 EP
1077230 Feb 2001 EP
1724104 Jul 2007 EP
1 892 429 Feb 2008 EP
2139675 Jan 2010 EP
2702285 Mar 2014 EP
1354161 Mar 1964 FR
1265140 Mar 1972 GB
1338234 Nov 1973 GB
1472079 Apr 1977 GB
2123430 Feb 1984 GB
61-211525 Sep 1986 JP
10-331855 Dec 1998 JP
2000117888 Apr 2000 JP
2000153575 Jun 2000 JP
2000192961 Jul 2000 JP
2001511502 Aug 2001 JP
2002194380 Jul 2002 JP
2004019758 Jan 2004 JP
2004035890 Feb 2004 JP
2004505335 Feb 2004 JP
2004358904 Dec 2004 JP
2005015793 Jan 2005 JP
2005035300 Feb 2005 JP
2006111885 Apr 2006 JP
2007018035 Jan 2007 JP
2007145894 Jun 2007 JP
2007173446 Jul 2007 JP
2008264305 Nov 2008 JP
2009117095 May 2009 JP
2010525245 Jul 2010 JP
20050106066 Nov 2005 KR
20100012028 Feb 2010 KR
20101237477 Feb 2013 KR
2009011322 Dec 2009 MX
2009139818 May 2011 RU
243887 Jan 2012 RU
9415999 Jul 1994 WO
9727003 Jul 1997 WO
9844545 Oct 1998 WO
9901675 Jan 1999 WO
0029210 May 2000 WO
02096644 Dec 2002 WO
03027522 Apr 2003 WO
2004056751 Jul 2004 WO
2004056754 Jul 2004 WO
2008094652 Aug 2008 WO
2008096097 Aug 2008 WO
2008-121682 Oct 2008 WO
2008128579 Oct 2008 WO
2009144495 Dec 2009 WO
2010038137 Apr 2010 WO
2010076307 Jul 2010 WO
WO 2010076307 Jul 2010 WO
2010138172 Dec 2010 WO
2012149447 Nov 2012 WO
2013101905 Jul 2013 WO
2013101928 Jul 2013 WO
2014001524 Jan 2014 WO
Non-Patent Literature Citations (14)
Entry
International Search Report from PCT Application No. PCT/US2012/071775 dated Apr. 24, 2013, 1 pg.
International Search Report from PCT Application No. PCT/US2012/071814 dated Apr. 12, 2013, 1 pg.
French Search Report from FR Application No. 1104125 dated Sep. 24, 2012, 3 pgs.
Briscoe, B. J., et al., “The friction and wear of Poly(tetrafluoroethylene)-Poly(etheretherketone) composites: an initial appraisal of the optimum composition,” Wear, Elsevier Sequoia, Lausanne, CH, vol. 108, Jan. 1, 1986, pp. 357-374, XP002351273.
Zhang, Z. et al., “Wear of PEEK composites related to their mechanical performances,” Tribology International Butterworth Scientific LDT, Guildford, GB, vol. 37, Jan. 1, 2004, pp. 271-277, XP002351274.
U.S. Appl. No. 13/728,262, filed Dec. 27, 2012, Inventors: Qiang Guo et al., 18 pgs.
Supplementary European Search Report issued Dec. 1, 2015 in European Application No. 12862673 (2 pages).
International Search Report for PCT/EP2013/063672 dated Sep. 25, 2013, 2 pages.
U.S. Appl. No. 12/582,335 filed Oct. 20, 2009, Inventors: Olaf Schmitjes et al., 16 pages.
International Search Report for PCT/EP2007/060736 dated Jan. 18, 2008, 2 pages.
International Search Report for PCT/US2012/035621 dated Nov. 29, 2012, 2 pages.
International Search Report for PCT/EP2013/070239 dated Dec. 19, 2013, 2 pages.
U.S. Appl. No. 13/458,882, filed Apr. 27, 2012, Inventors: Julia Ziegler et al., 27 pages.
French Search Report from FR Application No. 1457516 dated Jan. 13, 2015, 6 pgs.
Related Publications (1)
Number Date Country
20130183488 A1 Jul 2013 US
Provisional Applications (1)
Number Date Country
61681421 Aug 2012 US