POLYMER COMPOSITION FOR SELECTIVE SINTERING

Information

  • Patent Application
  • 20210079158
  • Publication Number
    20210079158
  • Date Filed
    December 10, 2018
    6 years ago
  • Date Published
    March 18, 2021
    3 years ago
Abstract
The present invention relates to a polymer composition for the production of shaped objects via selective sintering wherein the polymer composition comprises a thermoplastic polyester selected from poly(ethylene terephthalate), polyethylene naphthalate), poly(ethylene furanoate), poly(trimethylene terephthalate), poly(ethylene succinate), or poly(hydroxyl butyrate), wherein ≥10.0 wt % of the thermoplastic polyester has been subjected to a thermal treatment. Such polymer composition allows for the production of an article having a continuous use temperature of ≥100° C., and results in a low change of molecular weight during exposure to selective sintering powder processing temperatures. Further, such polymer composition allows for a significant reduction of the waste material generated during selective sintering as the unsintered material does not have to be disposed of as waste but may be used again fully, or blended with virgin material of the polymer composition and re-used, in a further selective sintering process.
Description

The present invention relates to a polymer composition for selective sintering. The invention also relates to a process for producing shaped objects via selective sintering using a polymer composition according to the present invention. The invention further relates to shaped objects produced via selective sintering using a polymer composition according to the present invention.


Selective sintering is an emerging technology that allows for the production of complex three-dimensional objects. At present, one of the main fabrication techniques of such three-dimensional objects is via injection moulding. However, injection moulding involves the use of expensive moulds, as a result of which injection moulding is only an efficient fabrication technique when the amount of objects produced using the mould is sufficiently large. For the production of objects in smaller series, the production costs are too high. For that reason, there is a need for alternative fabrication techniques that avoid the need for using such expensive moulds.


One such alternative fabrication technique is 3D printing. 3D printing is an additive manufacturing method, allowing to fabricate articles without the use of such expensive moulds. Using computer aided design (CAD), a model of the object to be produced is stored. Using this CAD model, a computer may steer a printing device by means of which a material may be shaped into the desired object. 3D printing further may allow for the production of articles of such complex shapes that may not be possible via injection moulding.


The material used for 3D printing may for example be a thermoplastic material. In that case, the printing may be performed by subjecting a predefined portion of a thermoplastic material, for example a powdery thermoplastic material, to a source of irradiation ensuring the particular portion of the thermoplastic material to reach a condition where it sinters with a neighbouring portion of material. Irradiation may be done by exposing the thermoplastic material to electromagnetic radiation such as infrared or near-infrared radiation. Such irradiation may for example be done using radiation having a wavelength of ≥100 nm and ≤100 μm, preferably ≥500 nm and ≤15 μm, more preferably ≥700 nm and ≤5 μm. Such processes are known as selective sintering processes.


In such selective sintering processes, the irradiation may for example be done using an infrared or near-infrared curing lamp, infrared or near-infrared light emitting diodes, or a laser source. Such irradiation may for example be done using laser irradiation.


Selective sintering processes may for example include processes where only a selected fraction of the material is subjected to radiation; alternatively, selective sintering may be achieved by applying a layer of a radiation absorbing material onto the area of the thermoplastic material that is to be sintered, and subsequently subjecting the surface area of the thermoplastic material, including the area to which the radiation absorbing material is not applied, to an irradiation source. Such selective sintering processes include for example high speed sintering (HSS) processes.


Selective sintering processes where only a selected fraction of the material is subjected to radiation include for example processes where irradiation may for example be done using laser irradiation. One technique for laser irradiation sintering of a predefined portion of a material such as a thermoplastic material is selective laser sintering (SLS). In SLS, a powder such as a powdery thermoplastic is positioned on a bed, where a laser source irradiates those portions of the powdery thermoplastic on the bed as indicated by the CAD model, in that way melting the thermoplastic material in that area. The molten material may then adhere to the thermoplastic material of a lower positioned layer. This positioned lower layer may be a layer previously formed by the SLS process. In this way, the desired object may be produced layer by layer. The unsintered powder material may be removed, for example dusted off, and may be re-used in a subsequent SLS process.


Objects produced using selective sintering processes such as SLS processes may thus be produced cost-efficiently. However, not every thermoplastic material is suitable for production of objects via SLS. Frequently, problems such as curling of the objects, orange peel, undesirable surface roughness or fuming during the process occur.


For example, when amorphous polymers are used for production of objects via SLS processes, this may result in objects having an insufficient quality. This may be accounted for in that amorphous polymers do not have a sharp melting point, but instead soften over a wide temperature range, and often have a high viscosity. This may result in objects having an undesirably high porosity and rough surface. Furthermore, the individual particles may still be discernible. When a higher intensity of irradiation is used to overcome the high viscosity, this again may lead to charring, or conduction of heat such that material softens in areas that are not desired, as a result of which the shape of the object obtained would not reflect the desired shape to the desired resolution.


Highly crystalline polymers on the other hand tend to melt at a sharp melting point, absorbing the energy of the source of irradiation to melt crystallites without the being transferred to surrounding areas to an undesirably large degree. However, highly crystalline polymers tend to have such fast crystallisation rate that may result in shrinking and warpage of the objects that are formed. This may be overcome by a very gradual and slow cooling of the material after the irradiation; however, this then leads to an undesirable increase in the time required for the SLS process.


In the SLS processes according to the state of the art, polylaurolactam, also referred to as nylon-12, is commonly used as thermoplastic material. Nylon-12 however has the disadvantage that it has a low melting point of 175° C., which results in a limitation of the continuous use temperature of the shaped objects to below 100° C. For certain applications, the continuous use temperature needs to be higher than 100° C. It is further preferred that the material can withstand a temperature above 200° C. for a short time without losing its desired properties.


There is thus a need for development of a thermoplastic material suitable for selective sintering that may be used in the production of shaped objects requiring a continuous use temperature of ≥100° C. The continuous use temperature may for example in the case of amorphous thermoplastic polymers be defined by the glass transition temperature (Tg); alternatively, in the case of crystalline polymers, it may be defined as 30° C. below the peak melting temperature (Tm).


A further disadvantage of nylon-12 is that the material is vulnerable to change of properties due to temperature exposure. This leads to a limited ability to re-use the left-over material from the SLS process that has not been fused or sintered by the selective irradiation, but that nevertheless has been exposed to heat for prolonged periods during pre-heating, building and cooling stages. The exposure to the powder bed temperatures during SLS leads to a change of the weight average molecular weight Mw of the nylon-12, which in turn negatively influences several material properties, including the melt viscosity.


Further, when using nylon-12, only a minor fraction of the powder that is introduced to the selective sintering process may be formed by a material that has already been subjected to such sintering process (i.e. only a minor amount of unsintered material from a previous build can be used). In the course of a selective sintering process, a powder bed is formed of material at certain elevated temperature but below the melting temperature of the material. As only a certain part of the powder material results as fused or sintered material to form a shaped object, a certain, often even significant, portion of the material remains in powder form. This powder, however, has been subjected to the thermal exposure in the powder bed. For thermoplastic powders of the art, such as nylon-12 powders, this temperature exposure leads to certain changes in the material as a result of which they become unsuitable to be re-used in a further selective sintering process, and thus may need to be discard of as waste materials, or at best may only be used as a minor fraction in a powder used for a further selective sintering process, where the major portion is made up of virgin material. This obviously leads to process inefficiencies, cost increase and the occurrence of an undesired waste stream.


A class of thermoplastic materials that are known to have a high melting point and a high continuous use temperature are certain thermoplastic polyesters, such as semi-aromatic thermoplastic polyesters. For example, US20140221566A1 described the use of poly(butylene terephthalate) (PBT), a specific type of thermoplastic polyester, in SLS processing. A disadvantage of PBT is its fast crystallisation rate, which may lead to curling of the obtained product and slow build rates.


Thermoplastic polyesters for use in SLS processing are also described in US20070126159A1. However, the polyesters disclosed in this publication, prepared by polycondensation of a di- or polyhydric aliphatic alcohol and an aliphatic dicarboxylic acid, do not have a desired high melting point, and thus do not have a desired continuous use temperature of ≥100° C.


The above thus clearly presents the need to provide a thermoplastic material having a continuous use temperature of ≥100° C., and showing a low change of molecular weight during exposure to SLS powder processing temperatures. Furthermore, it is desirable that the article produced via SLS is crystalline rather than amorphous. Particularly, it is desirable that the material can be utilised in a manner such that the quantity of waste material after the sintering process is reduced. Waste material may herein be understood as material that is not suitable for use in a selective sintering shaping process.


This has now been achieved according to the invention by a polymer composition for the production of shaped objects via selective sintering wherein the polymer composition comprises a thermoplastic polyester selected from poly(ethylene terephthalate), poly(ethylene naphthalate), poly(ethylene furanoate), poly(trimethylene terephthalate), poly(ethylene succinate), or poly(hydroxyl butyrate), wherein ≥10.0 wt % of the thermoplastic polyester has been subjected to a thermal treatment.


Such polymer composition allows for the production of an article having a continuous use temperature of ≥100° C., and results in a low change of molecular weight during exposure to selective sintering powder processing temperatures. Further, such polymer composition allows for a significant reduction of the waste material generated during selective sintering as the unsintered material does not have to be disposed of as waste but may be used again fully, or blended with virgin material of the polymer composition and re-used, in a further selective sintering process.


It is preferred that ≥25.0 wt %, preferably ≥50.0 wt %, even more preferably ≥75.0 wt %, even more preferably 100.0 wt % of the thermoplastic polyester, with regard to the total weight of the thermoplastic polyester in the polymer composition, has been subjected to a thermal treatment.


For example, ≥10.0 and ≤90.0 wt %, preferably ≥25.0 and ≤90.0 wt %, more preferably ≥25.0 ands ≤80.0 wt %, even more preferably ≥50.0 and ≤80.0 wt % of the thermoplastic polyester, with regard to the total weight of the thermoplastic polyester in the polymer composition, has been subjected to a thermal treatment. A polymer composition comprising such thermoplastic polyester is understood to have particularly desirable colour appearance. It is also understood that use of such thermoplastic polyester allows for the utilisation of material that has been subjected to heat treatment for a prolonged duration.


The use of such thermoplastic polyester that has been subjected to selective laser sintering in the polymer composition, in particular in such quantities, allows for a desirable reduction of the quantity of the polymer composition that has to be disposed of as unsintered material after a selective sintering process that is not further suitable for use in selective sintering shaping operations, but still results in a shaped object from selective sintering that has the desired material properties.


The thermal treatment may for example involve exposing the thermoplastic polyester to a temperature of more than 100° C. above the glass transition temperature Tg and less than 10° C. below the peak melting temperature Tp,m, wherein Tg is determined in accordance with ISO 11357-2 (2013) and Tp,m in accordance with ISO 11357-3 (2011), first heating run, preferably to more than 125° C. above Tg and less than 20° C. below Tp.m.


The thermal treatment may for example be the exposure of powder material to elevated powder bed temperatures during a selective sintering process. That elevated powder bed temperature may for example be temperature more than 100° C. above the glass transition temperature Tg and less than 10° C. below the peak melting temperature Tp,m, preferably more than 125° C. above Tg and less than 20° C. below Tp.m.


Preferably, the thermoplastic polyester that has been subjected to a thermal treatment is a thermoplastic polyester that has resulted from a selective sintering process as unsintered materials.


Where the thermoplastic polyester is a poly(ethylene terephthalate), the temperature for the thermal treatment may for example be ≥170° C. and ≤230° C., preferably ≥200° C. and ≤230° C. It is particularly preferable that the thermoplastic polyester is a poly(ethylene terephthalate), very particularly preferable a poly(ethylene terephthalate) homopolymer.


Preferably, the thermoplastic polyester that has been subjected to a thermal treatment is a thermoplastic polyester that has resulted from a selective sintering process as unsintered materials, wherein the powder bed temperature during the selective sintering process is a temperature of more than 100° C. above the glass transition temperature Tg and less than 10° C. below the peak melting temperature Tp,m, preferably more than 125° C. above Tg and less than 20° C. below Tp.m.


Particularly preferably, the thermoplastic polyester that has been subjected to a thermal treatment is a poly(ethylene terephthalate) that has resulted from a selective sintering process as unsintered material, wherein the powder bed temperature during the selective sintering process is a temperature of more than 100° C. above the glass transition temperature Tg and less than 10° C. below the peak melting temperature Tp,m, preferably more than 125° C. above Tg and less than 20° C. below Tp.m.


Further particularly preferably, the thermoplastic polyester that has been subjected to a thermal treatment is a poly(ethylene terephthalate) that has resulted from a selective sintering process as unsintered material, wherein the powder bed temperature during the selective sintering process is ≥170° C. and ≤230° C., preferably ≥200° C. and ≤230° C.


The thermal treatment may for example have a duration of ≥1 hour. Preferably, the thermal treatment has a duration of ≥2 hours, more preferably ≥5 hours, and could even be up to 4 days.


The degree of crystallinity of the thermoplastic polyester as determined according to the formula:






D
=



Δ






H
f



Δ






H

f
,
100




*
100

%





wherein:

    • D=degree of crystallinity of the thermoplastic material (%);
    • ΔHf=enthalpy of fusion of the thermoplastic material as determined in accordance with ISO 11357-3 (2011);
    • ΔHf,100=enthalpy of fusion of the thermoplastic material in a 100% crystalline state;


is preferably ≥10.0%, more preferably ≥12.5%, even more preferably ≥15.0%, and particularly ≥40.0%.


It is preferred that the thermoplastic polyester has such degree of crystallinity. With objects produced using materials having such degree of crystallinity, the continuous use temperature may be understood to be related to the crystalline melt temperature, and thus desirably high, where in objects produced using amorphous materials the continuous use temperature may be understood to be limited to the glass transition temperature.


It is preferred that the polymer composition comprises ≥70.0 wt % of the thermoplastic polyester, with regard to the total weight of the polymer composition, more preferably ≥80.0 wt %, even more preferably ≥90.0 wt %, even more preferably ≥95.0 wt %.


It is particularly preferred that the polymer composition ≥70.0 wt % of the thermoplastic polyester, with regard to the total weight of the polymer composition, more preferably ≥80.0 wt %, even more preferably ≥90.0 wt %, even more preferably ≥95.0 wt %, wherein the thermoplastic material is a polyester selected from poly(ethylene terephthalate), poly(ethylene naphthalate), poly(ethylene furanoate), poly(trimethylene terephthalate), poly(ethylene succinate), or poly(hydroxyl butyrate).


It is further particularly preferred that the polymer composition comprises ≥70.0 wt % of the thermoplastic polyester, with regard to the total weight of the polymer composition, more preferably ≥80.0 wt %, even more preferably ≥90.0 wt %, even more preferably ≥95.0 wt %, wherein the thermoplastic material is a polyester being poly(ethylene terephthalate).


Further particularly, it is preferred that the polymer composition comprises ≥70.0 wt % of the thermoplastic polyester, with regard to the total weight of the polymer composition, more preferably ≥80.0 wt %, even more preferably ≥90.0 wt %, even more preferably ≥95.0 wt %, wherein the thermoplastic polyester is a polyester selected from poly(ethylene terephthalate), poly(ethylene naphthalate), poly(ethylene furanoate), poly(trimethylene terephthalate), poly(ethylene succinate), or poly(hydroxyl butyrate), and wherein ≥10.0 wt % of the thermoplastic polyester, with regard to the total weight of the thermoplastic polyester in the polymer composition, has been subjected to a selective sintering process.


Even further particularly, it is preferred that the polymer composition comprises ≥70.0 wt % of the thermoplastic polyester, with regard to the total weight of the polymer composition, more preferably ≥80.0 wt %, even more preferably ≥90.0 wt %, even more preferably ≥95.0 wt %, wherein the thermoplastic polyester is a poly(ethylene terephthalate), and wherein ≥10.0 wt %, preferably ≥25.0 wt %, more preferably ≥50.0 wt %, even more preferably ≥75.0 wt % of the thermoplastic polyester, with regard to the total weight of the thermoplastic material in the polymer composition, is a thermoplastic polyester that has resulted from a selective sintering process as unsintered material.


It is preferred that the polymer composition is a powder having a mean particle volume size of ≥10 and ≤300 μm as determined in accordance with ISO 9276-2 (2014); more preferably ≥50 and ≤250 μm, or ≥100 and ≤200 μm. Such powder is particularly suitable for processing via SLS sintering, allowing for production of objects having low porosity. It is further preferred that the polymer composition is a powder having a D10 of ≥5 and ≤50 μm, a D50 of ≥60 and ≤150 μm, and a D90 of ≥160 and ≤300 μm as determined in accordance with ISO 9276-2 (2014); more preferably, the powder has a D10 of ≥10 and ≤40 μm, a D50 of ≥75 and ≤100 μm, and a D90 of ≥160 and ≤200 μm. A polymer composition having such particle size distribution is particularly suitable for processing via SLS because it allows for a good flow of materials during the filling of the powder bed, combined with good shape stability of the powder bed. Furthermore, it the particles are too big, the sintering of the material upon exposure to SLS would be insufficient. If particles are too fine, difficulties may occur in the formation of powder layers over the build area may become difficult.


A particularly preferable embodiment of the invention relates to a polymer composition comprising ≥70.0 wt % of the thermoplastic material, with regard to the total weight of the polymer composition, more preferably ≥80.0 wt %, even more preferably ≥90.0 wt %, even more preferably ≥95.0 wt %, wherein the thermoplastic material is a polyester being poly(ethylene terephthalate), and wherein ≥10.0 wt %, preferably ≥25.0 wt %, even more preferably ≥50.0 wt % of the thermoplastic polyester, with regard to the total weight of the thermoplastic polyester in the polymer composition, is a thermoplastic polyester that has resulted from a selective sintering process as unsintered material, wherein the polymer composition is a powder having a mean particle volume size of ≥10 and ≤300 μm, as determined in accordance with ISO 9276-2 (2014).


The change of molecular weight may for example be determined via gel permeation chromatography, for example according to ISO 16014-1 (2012), thereby obtaining parameters such as the weight average molecular weight (Mw) and the number average molecular weight (Mn). Alternatively, the change in molecular weight may be determined by dilute solution viscometry, for example according to ASTM D2857-95 (2007), thereby obtaining the intrinsic viscosity (IV). The change of molecular weight may be expressed as the difference in Mw, Mn and/or IV determined on the polymer composition before and after exposure to SLS powder bed temperatures.


The DSC curve of the polymer composition preferably is obtained at a rate of heating and cooling of 10° C./min. In a preferred way of determination, the sample is first heated to obtain a melt peak via DSC, wherein with increasing temperature first the melt onset temperature, then the melt peak temperature, and then the melt end temperature according to the definition of ISO 11357-1 (2009) are obtained; during the subsequent cooling, first the crystallisation end temperature, then the crystallisation peak temperature and then the crystallisation onset temperature according to the definition of ISO 11357-1 (2009) are obtained.


Further, the thermoplastic polyester may for example have a glass transition temperature Tg of ≥50° C. as determined in accordance with ISO 11357-2 (2013), preferably ≥60° C., more preferably ≥70° C.


The thermoplastic polyester may for example have a peak melt temperature Tp,m of ≥200° C. as determined in accordance with ISO 11357-3 (2011), first heating run, preferably ≥220° C., more preferably ≥240° C.


Where a poly(ethylene terephthalate) is used in the polymer composition according to the present invention, it is preferred that the poly(ethylene terephthalate) has an intrinsic viscosity of ≥0.80 dl/g, more preferable ≥1.00 dl/g, even preferable ≥1.10 dl/g. It is also preferred that the poly(ethylene terephthalate) has an intrinsic viscosity of ≤2.50 dl/g, further preferable ≤2.00 dl/g, more preferable ≤1.50 dl/g. For example, the poly(ethylene terephthalate) may have an intrinsic viscosity of ≥0.80 dl/g and ≤2.50 dl/g, alternatively ≥1.00 dl/g and ≤1.50 dl/g.


The intrinsic viscosity (IV) is determined in accordance with ASTM D2857-95 (2007).


Poly(ethylene terephthlates) having such intrinsic viscosity may show a good combination of melt flow and strength of the sintered object after the laser irradiation, and may result in objects having desirable dimensional accuracy.


Particularly desirable is the use of a poly(ethylene terephthalate) having an intrinsic viscosity of ≥0.80 dl/g and ≤2.50 dl/g and a degree of crystallinity of ≥15.0%, preferably ≥40.0%. Such poly(ethylene terephthalate) shows a very desirable resistance to molecular weight changes under prolonged thermal treatment, and hence are most suitable to be re-used in selective sintering processes when obtained as unsintered material from such processes.


Further particularly desirable is the use of a polyethylene having a heat of fusion of ≥50 J/g.


The polymer composition according to the present invention may for example comprise a poly(ethylene terephthalate). For example, the polymer composition may comprise ≥80.0 wt %, alternatively ≥90 wt %, alternatively ≥95.0 wt % of a poly(ethylene terephthalate) with regard to the total weight of the polymer composition. The poly(ethylene terephthalate) may be a homopolymer or copolymer. In case the poly(ethylene terephthalate) is a copolymer, the poly(ethylene terephthalate) may for example comprise ≤15.0 wt %, alternatively ≤10.0 wt %, alternatively ≤5.0 wt %, alternatively ≤2.0 wt %, of units derived from a comonomer, with regard to the total weight of the poly(ethylene terephthalate). Preferably, the poly(ethylene terephthalate) comprises ≥0.1 wt % and ≤10.0 wt %, alternatively ≥0.5 wt % and ≤5.0 wt % of units derived from a comonomer, with regard to the total weight of the poly(ethylene terephthalate). The units derived from a comonomer may for example be units derived from an aliphatic diol other than ethanediol. The units derived from a comonomer may for example be units derived from an aromatic dicarboxylic acid other than terephthalic acid. For example, the aromatic dicarboxylic acid other than terephthalic acid may be isophthalic acid. It is preferred that where the poly(ethylene terephthalate) is a copolymer, it comprises ≥0.5 wt % and ≤5.0 wt % of units derived from isophthalic acid, with regard to the total weight of the poly(ethylene terephthalate).


In a preferred embodiment of the invention, the poly(ethylene terephthalate) has an intrinsic viscosity of ≥1.00 dl/g and ≤1.50 dl/g.


The polymer composition may in certain embodiments further comprise a flow agent. For example, the polymer composition may comprise ≥0.01 wt % and ≤5.00 wt % with regard to the total weight of the polymer composition of a flow agent. Alternatively, the polymer composition may comprise ≥0.05 and ≤3.00 wt %, alternatively ≥0.10 and ≤1.50 wt, or a flow agent, based on the total weight of the polymer composition. The flow agent may for example be selected from silica, alumina, phosphate, borate, titania, talc, mica, kaolin, attapulgite, calcium silicate, magnesium silicate or a combination thereof. For example, the polymer composition may comprise ≥0.01 wt % and ≤5.00 wt % with regard to the total weight of the polymer composition of a flow agent selected from silica, alumina, phosphate, borate, titania, talc, mica, kaolin, attapulgite, calcium silicate, magnesium silicate or a combination thereof.


In a further embodiment, the present invention also relates to a process for production of shaped objects using the polymer composition according to the invention, wherein the process comprises the steps of:

    • (a) providing a quantity of a powder comprising the polymer composition;
    • (b) irradiating a portion of the polymer composition with an irradiation source such that the particles in that portion of the polymer composition absorb sufficient heat to reach a temperature above Tp,m;
    • (c) terminating the exposure of the portion of the polymer composition to the irradiation source so that the temperature of the particles of the polymer composition decreases to below Tp,m; and
    • (d) removal of the portion of the polymer composition that has not been sintered by the irradiation by the energy source; wherein steps (a) through (d) are executed in this sequence.


In another further embodiment, the present invention also relates to a process for production of shaped objects using the polymer composition according to the invention, wherein the process comprises the steps of:

    • (a) providing a quantity of a powder comprising the polymer composition;
    • (b) irradiating a portion of the polymer composition with an irradiation source such that the particles in that portion of the polymer composition absorb sufficient heat to reach a temperature above Tp,m;
    • (c) terminating the exposure of the portion of the polymer composition to the irradiation source so that the temperature of the particles of the polymer composition decreases to below Tp,m; and
    • (d) removal of the portion of the polymer composition that has not been sintered by the irradiation by the energy source;
    • wherein steps (a) through (d) are executed in this sequence;
    • wherein the portion of the polymer composition removed in step (d) is further used in the polymer composition used in a further shaping process according to the steps (a)-(d).


In yet another further embodiment, the present invention also relates to a process for production of shaped objects using the polymer composition according to the invention, wherein the process comprises the steps of:

    • (a) providing a quantity of a powder comprising the polymer composition wherein a fraction of the polymer composition has previously been subjected to selective sintering;
    • (b) irradiating a portion of the polymer composition with an irradiation source such that the particles in that portion of the polymer composition absorb sufficient heat to reach a temperature above Tp,m;
    • (c) terminating the exposure of the portion of the polymer composition to the irradiation source so that the temperature of the particles of the polymer composition decreases to below Tp,m; and
    • (d) removal of the portion of the polymer composition that has not been sintered by the irradiation by the energy source;
    • wherein steps (a) through (d) are executed in this sequence.


Preferably, the polymer composition provided above under (a) comprises ≥10.0 wt % of a thermoplastic polyester that has resulted from a selective sintering process as unsintered material.


In a preferred embodiment,

    • step (a) comprises placing a quantity of powder comprising the polymer composition in a powder bed comprising a horizontal surface and a frame for holding the powder positioned on the surface;
    • step (b) comprises irradiating the portion of the polymer composition by a moving irradiation source; and
    • steps (a), (b) and (c) are repeated in this order to form stacked layers of the polymer composition sintered onto each other prior to execution of step (d).


Particularly, the present invention also relates to a process for production of shaped objects using the polymer composition according to the invention, wherein the process comprises the steps of:

    • (a) providing a quantity of a powder comprising the polymer composition;
    • (b) irradiating a portion of the polymer composition with a laser energy beam such that the particles in that portion of the polymer composition absorb sufficient heat to reach a temperature above Tp,m;
    • (c) terminating the exposure of the portion of the polymer composition to the irradiation of the laser energy beam so that the temperature of the particles of the polymer composition decreases to below Tp,m; and
    • (d) removal of the portion of the polymer composition that has not been sintered by the irradiation by the energy source;
    • wherein steps (a) through (d) are executed in this sequence.


In a preferred embodiment,

    • step (a) comprises placing a quantity of powder comprising the polymer composition in a powder bed comprising a horizontal surface and a frame for holding the powder positioned on the surface;
    • step (b) comprises irradiating the portion of the polymer composition by a moving laser energy beam; and
    • steps (a), (b) and (c) are repeated in this order to form stacked layers of the polymer composition sintered onto each other prior to execution of step (d).


It is preferred that the process is performed in an atmosphere comprising ≤1.0 wt % of oxygen.


The thermoplastic materials in the powder bed that is subjected to irradiation are commonly pre-heated to a temperature such that the irradiation energy and time needed to soften the material for sintering is minimized, whilst the material remains in a condition that the powder particles that are not subjected to irradiation do not sinter. If the powder bed temperature is too high, it may lead to sintering of the thermoplastic material in undesired locations, resulting in amongst others dimensional inaccuracy of the shaped object. If the powder bed temperature is too low, the thermoplastic material may insufficiently sinter in the desired locations, which may result in amongst others undesired porosity of the shaped object. For example, the powder bed temperature may be kept ≤60° C., more preferable ≤40° C., even more preferable ≥10 and ≤60° C. or ≥20 and ≤40° C., below Tp,m.


In the process according to the present invention, further additives may be applied that may contribute to the selective sintering process. For example, coalescing agents may be added. Such coalescing agents may for example comprise agents that enhance the absorption of the electromagnetic radiation and the conversion of the absorbed energy into thermal energy, thus contributing to the sintering process.


In further embodiments, the invention relates to shaped objects produced via the process according to the present invention, preferably wherein the shaped object has a porosity of ≤5.0%. More preferably, the shaped object has a porosity of ≤4.0%, alternatively ≤3.0%. The porosity may be determined by comparing the density of an article of the same composition and the same crystallinity produced using the material via SLS (ρSLS) with the density of an article produced via injection moulding (ρIM). The porosity (P) in % may for example be calculated as:






P
=




ρ
IM

-

ρ
SLS



ρ
IM


*
100

%










The invention will now be illustrated by the following non-limiting examples.


A poly(ethylene terephthalate) (PET) homopolymer powder was used having the following properties:

    • an intrinsic viscosity (IV) of 1.12 dl/g as determined in accordance with ASTM D2857-95;
    • particle size distribution as determined in accordance with ISO 9276-2 (2014): D10=39 μm; D50=94 μm; D90=188 μm; and mean particle volume size=107 μm;
    • weight average molecular weight (Mw) of 117.1 kg/mol and number average molecular weight (Mn) of 44.8 kg/mol, as determined in accordance with ISO 16014-1 (2012), and a polydispersity index Mw/Mn of 2.62


The PET was a virgin PET, which is to be understood that the PET has not been subjected to any thermal treatment (such as in a selective sintering machine) after the production of the PET.


The PET powder material was divided into 5 sample portions, which were each subjected to a thermal treatment according to table I below. The thermal treatment simulates the level exposure to heat, both as conducted heat and as radiation heating from e.g. infrared lamps) to which material that is not sintered during a selective sintering process is exposed.









TABLE I







Thermal treatment conditions and


molecular weights for PET powders












Sample
A
B
C
D
E





Thermal treatment time
None
24 h
48 h
72 h
96 h


Mw (kg/mol)
117.1
113.9
118.8
125.5
130.0


Mn (kg/mol)
44.8
44.2
46.3
47.3
49.1


Mw/Mn
2.62
2.58
2.56
2.65
2.65









The thermal treatment was performed using an oven is which the powder samples were placed under vacuum at a temperature of 210° C. for a time period at indicated above in table I. The Mw and Mn of the samples were each determined after the thermal treatment.


Sample A can be understood to be a comparative example. It can be observed that the molecular structure as defined by Mw, Mn and the Mw/Mn ratio changes but does so only to a very limited extent. The numerical differences are within the variation of the GPC measurement method (±12%), and hence one can conclude that there is no statistically significant difference. Surprisingly, and unlike other polymer powders for SLS, the thermally treated material of samples B through E are still of such quality that they can be utilized as sinterable material in a selective sintering process, even without addition of virgin PET powder.


The thermally treated samples B-E, which may also be referred to as the aged powder samples, and comparative sample A, were subjected to differential scanning calorimetry (DSC) in accordance with ISO 11357-1 (2009). A first melting curve and a first cooling curve were recorded at a heating and cooling rate of 10° C./min, in nitrogen atmosphere. From the DSC curves, the extrapolated melt onset temperature of first heating (Tei,m) in ° C. the peak melt temperature at first heating (Tp,m) in ° C., the heat of fusion in J/g, the extrapolated crystallisation onset temperature of first heating (Tei,c) in ° C., the peak crystallisation temperature (Tp,c) in ° C., the heat of crystallisation in J/g, and the sintering window in ° C. were determined. The sintering window was calculated as Tei,m−Tei,c. Results are presented in table II.









TABLE II







DSC results












Sample
A
B
C
D
E















Tei, m
238
238
239
238
239


Tp, m
242
242
242
242
242


Heat of fusion
57.0
59.7
60.5
61.2
61.4


Tei, c
186
186
185
185
184


Tp, c
175
176
175
173
173


Heat of crystallisation
28.5
28.8
26.8
28.5
27.1


Sintering window
52
52
54
53
55









From the results in table II, it can further be concluded that the suitability of the samples B-E for use in selective sintering processes is not significantly affected by the thermal treatment. For example, the sintering window even increases, indicating that the temperature range to which the material is exposed during the sintering process even becomes less critical.


To further determine the properties of the sample materials and their suitability for utilisation in selective sintering processes resulting in objects having desired properties, a quantity of sample A and a quantity of sample E, i.e. the material that has undergone the severest thermal treatment, were each subjected to selective laser sintering to produce test bars of 2 cm width, 5 cm length and 3 mm thickness.


The selective laser sintering (SLS) was performed using an SLS machine comprising a CO2 laser source. To each of the powder sample A and E, a quantity of 0.05 wt % Aerosil flow promoter was added. The materials were pre-dried prior to processing via SLS. The SLS process was conducted in an atmosphere having an oxygen content of ≤1.0 wt %. The SLS process conditions are presented in table III.









TABLE III





SLS process conditions.


















Powder bed temperature (° C.)
228



Piston temperature (° C.)
180



Cylinder temperature (° C.)
175



Feed temperature (° C.)
160



Laser power (W)
30



Scan speed (m/s)
5



Hatch distance (μm)
100



Layer thickness (μm)
100










The produced bars were subjected to determination of density and the colour in the form of the yellowness index of the bars. Density in kg/m3 was determined in accordance with ASTM D792 (2013) according to method A; yellowness index (YI) was determined in accordance with ASTM E313 (2010). Results are presented in table IV.









TABLE IV







Results of testing of SLS bars










Test bar
1
2
3





Material used
100 wt % of
Powder blend of 80
100 wt % of


for printing
sample A
wt % sample C, 20
sample E




wt % sample A


Density
1.362
1.369
1.366


YI
0.23

−1.21









These results present the density of the printed bars to be relatively unaffected by the use of either a virgin material or a material comprising thermally treated material.


With regard to the yellowness index, the results show that the YI of the bar produced using the thermally treated material is even better than that of the bar produced using virgin material, indicating that use of such thermally treated material leads to a desirable colour of the produced object.

Claims
  • 1. A polymer composition for the production of shaped objects via selective sintering wherein the polymer composition comprises a thermoplastic polyester selected from poly(ethylene terephthalate), poly(ethylene naphthalate), poly(ethylene furanoate), poly(trimethylene terephthalate), poly(ethylene succinate), or poly(hydroxyl butyrate), wherein ≥10.0 wt % of the thermoplastic polyester has been subjected to a thermal treatment.
  • 2. The polymer composition according to claim 1, wherein the thermal treatment involves exposing the thermoplastic polyester to a temperature of more than 100° C. above the glass transition temperature Tg and less than 10° C. below the peak melting temperature Tp,m, wherein Tg is determined in accordance with ISO 11357-2 (2013) and Tp,m is determined in accordance with ISO 11357-3 (2011), first heating run.
  • 3. The polymer composition according to claim 1, wherein the thermal treatment is performed for ≥1 hour.
  • 4. The polymer composition according to claim 1, wherein the thermoplastic polyester is poly(ethylene terephthalate).
  • 5. The polymer composition according to claim 4 wherein the thermal treatment involves exposing the poly(ethylene terephthalate) to a temperature of ≥170° C. and ≤230° C.
  • 6. The polymer composition according to claim 1, wherein ≥75.0 wt % of the thermoplastic polyester has been subjected to the thermal treatment.
  • 7. The polymer composition according to claim 1, wherein the thermoplastic polyester that has been subjected to a thermal treatment is a thermoplastic polyester that has resulted from a selective sintering process as unsintered material.
  • 8. The polymer composition according to claim 4, wherein the polymer composition comprises the poly(ethylene terephthalate), which is a poly(ethylene terephthalate) homopolymer.
  • 9. The polymer composition according to claim 4, wherein the poly(ethylene terephthalate) has an intrinsic viscosity of ≥0.80 dl/g determined in accordance with ASTM D2857-95 (2007).
  • 10. The polymer composition according to claim 4, wherein the polymer composition comprises ≥90.0 wt % of the poly(ethylene terephthalate) with regard to the total weight of the polymer composition.
  • 11. The polymer composition according to claim 1, wherein the polymer composition is a powder having a mean particle volume size of ≥10 and ≤300 μm as determined in accordance with ISO 9276-2 (2014).
  • 12. The polymer composition according to claim 1, wherein the polymer composition is a powder having a D10 of ≥5 and ≤50 μm, a D50 of ≥60 and ≤150 μm, and a D90 of ≥160 and ≤300 μm as determined in accordance with ISO 9276-2 (2014).
  • 13. The polymer composition according to claim 1, wherein the polymer composition further comprises ≥0.01 wt % and ≤5.00 wt % with regard to the total weight of the polymer composition of a flow agent selected from silica, alumina, phosphate, borate, titania, talc, mica, kaolin, attapulgite, calcium silicate, magnesium silicate or a combination thereof.
  • 14. A process for the production of shaped objects using a polymer composition comprising a thermoplastic polyester selected from poly(ethylene terephthalate), poly(ethylene naphthalate), poly(ethylene furanoate), poly(trimethylene terephthalate), poly(ethylene succinate), or poly(hydroxyl butyrate), wherein ≥10.0 wt % of the thermoplastic polyester has been subjected to a thermal treatment, wherein the process comprises the steps of: (a) providing a quantity of a powder comprising the polymer composition wherein a fraction of the polymer composition has previously been subjected to selective sintering;(b) irradiating a portion of the polymer composition with a radiation source, such as a laser energy beam, such that the particles in that portion of the polymer composition absorb sufficient heat to reach a temperature above the peak melting temperature Tp,m determined via differential scanning calorimetry, first heating run in accordance with ISO 11357-1 (2009);(c) terminating the exposure of the portion of the polymer composition to the irradiation source so that the temperature of the particles of the polymer composition decreases to below Tp,m; and(d) removing the portion of the polymer composition that has not been subjected to irradiation by the energy source;wherein steps (a) through (d) are executed in this sequence.
  • 15. A shaped object produced via the process of claim 14, wherein the shaped object has a porosity of ≤5.0%.
  • 16. The process of claim 14, wherein ≥10.0 wt % of the thermoplastic polyester has been subjected to a thermal treatment for reduction of unsintered waste polymer in a selective sintering moulding process.
  • 17. The process of claim 16, wherein the thermoplastic polyester that has been subjected to a thermal treatment is a thermoplastic polyester that has resulted from a selective sintering process as unsintered material.
Priority Claims (1)
Number Date Country Kind
17207825.5 Dec 2017 EP regional
PCT Information
Filing Document Filing Date Country Kind
PCT/EP2018/084175 12/10/2018 WO 00