Claims
- 1. A method of preparing a polymeric composition in which an inorganic substance is firmly consolidated in an organic polymer, comprising: heterogeneously polymerizing methyl methacrylate or a vinyl monomer mixture comprising methyl methacrylate as the major component without initiating the reaction with a radical polymerization initiator in a polymerization system containing said inorganic substance dispersed in an aqueous medium in the presence of at least one carboxylic acid monomer of the formula: ##STR9## wherein R.sub.5 is a hydrogen atom, an alkyl group of 1 to 15 carbon atoms, COOZ, halogen, phenyl or a derivative of a phenyl group, R.sub.6 is hydrogen, alkyl of 1 to 15 carbon atoms, COOZ, hydrogen, phenyl or derivative of a phenyl group, R.sub.7 is a hydrogen, alkyl of 1 to 15 carbon atoms, halogen, phenyl or derivative of a phenyl group, and Z is a hydrogen, ammonium or an alkali metal atom, or at least one monomer of the formula: ##STR10## wherein R.sub.8 and R.sub.9 are each hydrogen, alkyl of 1 to 15 carbon atoms, halogen, phenyl or a derivative of a phenyl group.
- 2. The method of claim 1, wherein the inorganic substance is at least one member selected from the group consisting of calcium sulfite, calcium sulfate, silicone dioxide, titanium oxide, antimony trioxide, talc, clay, aluminum oxide, calcium carbonate, carbon black, carbon fiber, glass fiber, graphite, nickel powder, iron powder, zinc powder, copper powder, iron oxide, zinc oxide and aluminum hydroxide.
- 3. The method of claim 1, wherein said carboxylic acid monomer is acrylic acid, methacrylic acid or crotonic acid.
- 4. The method of claim 1, wherein the weight ratio of monomer mixture to the inorganic substance ranges from 250:1 to 1:5.
- 5. The method of claim 1, wherein said polymerization reaction is conducted under an inert gas atmosphere at a temperature from 10.degree. to 100.degree. C.
- 6. The method of claim 1, wherein the amount of said monomer in the reaction medium ranges from 0.05 to 100% by weight based on the total amount of inorganic substance and monomer in the polymerization medium.
- 7. A method of preparing a polymeric composition in which an inorganic substance is firmly consolidated in an organic polymer, comprising: heterogeneously polymerizing methyl methacrylate or a vinyl monomer mixture comprising methyl methacrylate as the major component without initiating the reaction with a radical polymerization initiator in a polymerization system containing said inorganic substance dispersed in an aqueous medium in the presence of at least one monomer of the formula: ##STR11## wherein R.sub.1 is a hydrogen atom, an alkyl group having 1 to 20 carbon atoms, a phenyl group, a derivative of phenyl group, or halogen atom, X is CONH, ##STR12## COO(CH.sub.2).sub.m or (CH.sub.2).sub.n, wherein R.sub.2 and R.sub.3 are each a hydrogen atom or alkyl group having 1 to 15 carbon atoms, R.sub.4 is an alkylene group having 1 to 15 carbon atoms, m is an integer of 1 to 20, and n is an integer of 0 to 20, and Y is a hydrogen atom, ammonium radical, or an alkali metal atom.
- 8. The method of claim 7, wherein the inorganic substance is at least one member selected from the group consisting of calcium sulfite, calcium sulfate, silicon dioxide, titanium oxide, antimony trioxide, talc, clay, aluminum oxide, calcium carbonate, carbon black, carbon fiber, glass fiber, graphite, nickel powder, iron powder, zinc powder, copper powder, iron oxide, zinc oxide and aluminum hydroxide.
- 9. The method of claim 7, wherein the weight ratio of monomer mixture to the inorganic substance ranges from 250:1 to 1:5.
- 10. The method of claim 7, wherein said polymerization reaction is conducted under an inert gas atmosphere at a temperature up to 100.degree. C.
- 11. The method of claim 7, wherein the amount of said carboxylic acid monomer in the reaction medium ranges from 0.05 to 100% by weight based on the total amount of inorganic substance and monomer in the polymerization medium.
Priority Claims (2)
Number |
Date |
Country |
Kind |
56-937 |
Jan 1981 |
JPX |
|
56-35549 |
Mar 1981 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 530,670, filed Sept. 9, 1983, abandoned, which is a division of application Ser. No. 336,460, filed Dec. 31, 1981, U.S. Pat. No. 4,435,540.
US Referenced Citations (8)
Foreign Referenced Citations (2)
Number |
Date |
Country |
51-46552 |
Apr 1976 |
JPX |
52-31912 |
Mar 1977 |
JPX |
Non-Patent Literature Citations (6)
Entry |
Die Angewandte Makromolekulare Chemie, 53(1976)65-72; Dept. of Applied Chemistry, Faculty of Engineering Tohuku University, Sendai, Japan; Polymerization of Methyl Methacrylate in the Presence of Graphite. |
Chemistry and Industry; Aug. 3, 1974; Polymerisation of Methyl Methacrylate in the Presence of Various Metal Oxides, Sands and Slags. |
Chem. Abs. 99-38853n (1983), Talapatra et al. |
Chem. Abs. 79-151562s (1973), Sugimoto et al. |
Chem. Abst. 77-75590r (1972), Mathis et al. |
Chem. Abs. 81-121141c (1974), Allen et al. |
Divisions (1)
|
Number |
Date |
Country |
Parent |
336460 |
Dec 1981 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
530670 |
Sep 1983 |
|