Patent Grant
8232367
(a) Field of the Invention
The present invention relates to polymer compounds and a preparation method thereof. More specifically, the present invention relates to polymer compounds with well-connected, narrow size distribution free-volume element and a method for preparing the polymer compounds by thermal rearrangement of aromatic polyimides containing ortho-positioned functional groups in the solid state.
(b) Description of the Related Art
Small-molecule and ion diffusion through cavities (i.e., free-volume elements) in soft organic materials is an inherently subnano- or nanoscopic phenomenon. It has important implications for membrane separation processes in chemicals production as well as energy conversion and storage applications [e.g., pharmaceutical separations (B. Jeong et al., Nature 1997, 388, 860), organic batteries (P. Lightfoot et al., Science 1993, 262, 883), fuel cells (M. A. Hickner et al., Chem. Rev. 2004, 104, 4587), and gas separation (H. Lin et al., Science 2006, 311, 639)]. Transport of small gas molecules through polymers occurs by diffusion through transient free-volume elements or cavities formed by random, thermally stimulated motion of the flexible organic chains.
Unlike pore sizes and shapes in rigid microporous inorganic materials such as zeolites (Z. Lai et al., Science 2003, 300, 456) and carbon molecular sieve materials (H. B. Park et al., Adv. Mater. 2005, 17, 477), cavity sizes and shapes are not uniform in amorphous polymers. The cavity radius (r) of the most selective polymers such as polyimides, polysulfones, and polycarbonates, as measured by positron annihilation lifetime spectroscopy (PALS), is 0.3 nm or less with a broad distribution of cavity sizes, and gas permeability is rather low (Y. Yampolskii, I. Pinnau, B. D. Freeman, Materials Science of Membranes for Gas and Vapor Separation (Wiley, London, 2006).
Conversely, the most permeable polymer, poly(1-trimethylsilyl-1-propyne) (PTMSP), exhibits an approximately bimodal cavity size distribution centered at around r=0.3 nm and r=0.6 to 0.7 nm (K. Nagai et al., Polym. Sci. 2001, 26, 721). The high concentration of large cavities and the high connectivity among cavities results in very high permeability for a polymer, but its ability to separate small molecules (kinetic diameter<0.45 nm) is too low to be useful, and the large cavities collapse over time due to physical aging (K. Nagai et al., Polym. Sci. 2001, 26, 721). Thus, among known polymers, free-volume element size and distribution play a key role in determining permeability and separation characteristics. However, the broad size range of free-volume elements in such materials precludes the preparation of polymers having both high permeability and high selectivity.
The inventors of the present invention demonstrate that polymers with an intermediate cavity size, a narrow cavity size distribution, and a shape reminiscent of bottlenecks connecting adjacent chambers, such as those found elegantly in nature in the form of ion channels (D. A. Doyle et al., Science 1998, 280) and aquaporins (D. Kozono et al., Invest. 2002, 109, 1395), yield both high permeability and high selectivity. Central to approach for preparing these intermediate-sized cavities is controlled free-volume element formation through spatial rearrangement of the flat, rigid-rod structure with high-torsional energy barriers to rotation between two rings (V. J. Vasudevan, J. E. McGrath,Macromolecules 1996, 29, 637). The stiff, rigid ring units in such flat topologies pack efficiently, leaving very small penetrant accessible free-volume elements. This tight packing is also promoted by intersegmental interactions such as charge-transfer complexes between heteroatoms containing lone electron pairs (e.g., O, S and N) (W. J. Welsh, D. Bhaumik, J. E. Mark, Macromolecules 1981, 14, 947). The genesis of these materials was the demand for highly thermally and chemically stable polymers. However, their application as gas separation membranes was frustrated by their lack of solubility in common solvents, which effectively prevents them from being prepared as thin membranes by solvent casting, which is the most widely practiced method for membrane preparation.
Consequently, the present inventors suggested that completely aromatic, insoluble, infusible polymers can be prepared from highly soluble precursors by irreversible molecular rearrangement at about 350° C. to 450° C. for aromatic polyimides containing ortho-positioned functional groups (e.g., —OH, —SH and —NH2) [H. B. Park, C. H. Jung, Y. M. Lee et al., Polymers with cavities tuned for fast selective transport of small molecules and ions, Science 2007, 318, 254. 38]. In addition, the present inventors ascertained that aromatic polymers interconnected with heterocyclic rings (e.g., benzoxazole, benzothiazole and benzopyrrolone) showed higher gas permeation performance due to their well-controlled free-volume element formation by thermal rearrangement in the solid state.
Therefore, the present invention has been made in view of the above problems, and it is an object of the present invention to provide polymer compounds with well-connected cavities, an intermediate cavity size and a narrow cavity size distribution.
It is another object of the present invention to provide a method for preparing the polymer compounds by thermally treating aromatic polyimides containing ortho-positioned functional groups (e.g., polyhydroxyimide, polythiolimide, and polyaminoimide).
The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
Hereinafter, the present invention will be illustrated in more detail.
In one aspect, the present invention is directed to polymer compounds containing at least one repeating unit represented by Formulae 1 to 14 below:
In Formulae 1 to 14,
Ar1 is a tetravalent C5-C24 arylene group or a tetravalent C5-C24 heterocyclic ring, which is substituted or unsubstituted with at least one substituent selected from the group consisting of C1-C10 alkyl, C1-C10 alkoxy, C1-C10 haloalkyl and C1-C10 haloalkoxy, or two or more of which are fused together to form a condensation ring or covalently bonded to each other via a functional group selected from the group consisting of O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2 and C(═O)NH;
Ar1′ and Ar2 are identical to or different from each other and are each independently a bivalent C5-C24 arylene group or a bivalent C5-C24 heterocyclic ring, which is substituted or unsubstituted with at least one substituent selected from the group consisting of C1-C10 alkyl, C1-C10 alkoxy, C1-C10 haloalkyl and C1-C10 haloalkoxy, or two or more of which are fused together to form a condensation ring or covalently bonded to each other via a functional group selected from the group consisting of O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CF3)2, C(CF3)2 and C(═O)NH;
Q is O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2, C(═O)NH, C(CH3)(CF3), C1-C6 alkyl-substituted phenyl or C1-C6 haloalkyl-substituted phenyl in which Q is linked to opposite both phenyl rings in the position of m-m, m-p, p-m or p-p;
Y″ is —O or S;
n is an integer from 20 to 200;
m is an integer from 10 to 400; and
l is an integer from 10 to 400.
Ar1 and Ar2 may be the same arylene or heterocyclic ring. Preferably, Ar1 is selected from the following compounds and the linkage position thereof includes all of o-, m- and p-positions.
wherein X is O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2, or C(═O)NH; W is O, S or C(═O); and Z1, Z2 and Z3 are identical to or different from each other and are O, N or S.
More preferably, Ar1 is selected from the following compounds:
Preferably, Ar2 is selected from the following compounds and the linkage position thereof includes all of o-, m- and p-positions.
wherein X is O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2, or C(═O)NH; W is O, S or C(═O); and Z1, Z2 and Z3 are identical to or different from each other and are O, N or S.
More preferably, Ar2 is selected from the following compounds:
Preferably, Q is CH2, C(CH3)2, C(CF3)2, O, S, S(═O)2 or C(═O).
More preferably, Ar1 is
Ar2 is
and Q is C(CF3)2.
Preferably, the polymer compounds have a fractional free volume (FFV) of 0.18 to 0.40, a d-spacing of 0.58 to 0.80 nm and a cavity radius difference of 0.1 to 0.4 Å between maximum cavity radius and minimum cavity radius.
The polymer compounds of the present invention may be doped with an acid. By adding small acidic dopants, the cavity size and shape of the polymer compounds can be tuned. For example, after doping, the CO2 permeability decreases but CO2/CH4 selectivity increases.
Suitable acidic dopant for use with the present invention includes sulfuric acid, hydrochloric acid, phosphoric acid, nitric acid, HBrO3, HClO4, HPF6, HBF6, 1-methyl-3-methylimidazolium cation (BMIM+) and mixtures thereof.
Preferably, the polymer compounds of the present invention are organic-inorganic composite polymers via incorporation of inorganic oxides or inorganic fillers into the polymer matrix. Here, the organic-inorganic composite polymers can be prepared by adding an inorganic oxides or inorganic fillers to polyamic acid or polyimide which is subsequently subjected to imidization and thermal-treating or only thermal-treating.
Suitable inorganic oxides for use with the present invention include fumed silica, zirconium oxide, tetraethoxy silane, montmorillonite clay and mixtures thereof. Here, the preferable content of the inorganic oxide is 0.1 to 10% by weight, based on the total weight of the organic-inorganic composite polymer compound. When the amount of inorganic oxide is less 0.1% by weight, the effect of adding the inorganic oxide is too low to expect the improvement of mechanical, thermal, and chemical stabilities. Conversely, when the amount of inorganic oxide exceeds 10% by weight, excessive amount of inorganic oxides cause the composite polymer compounds to rapidly lose the mechanical strength and to be broken.
Suitable inorganic fillers for use with the present invention include phosphotungstic acid (PWA), phosphomolybdenic acid, silicotungstic acid (SiWA), molybdophosphoric acid, silicomolybdic acid, phosphotin acid, zirconium phosphate (ZrP) and mixtures thereof. Here, the preferable content of the inorganic fillers is 0.5 to 60% by weight, based on the total weight of the organic-inorganic composite polymer compound. When the amount of inorganic filler is less 0.5% by weight, the effect of adding the inorganic filler is too low to expect the improvement of mechanical, thermal, and chemical stabilities. Conversely, when the amount of inorganic filler exceeds 60% by weight, excessive amount of inorganic fillers cause the composite polymer compounds to rapidly lose the mechanical strength and to be broken.
The polymer compounds of the present invention have well-connected hourglass shaped cavities, and narrow cavity size distribution. These free-volume elements are appropriate for molecular and ionic transport and molecular separations.
According to Experimental Example 5 of the present invention, the nitrogen absorption/desorption isotherm analysis indicates the presence of substantial amounts of free volume.
With reference to Experimental Example 6 of the present invention, it can be seen from PALS analysis that a precursor polymer[Comparative Example 1, synthesized from 4,4′-(hexafluoroisopropylidene)-diphthalic anhydride (6FDA) and 2,2′-bis(3-amino-4-hydroxylphenyl)hexafluoropropane (bisAPAF) via thermal imidization up to 300° C.] and its corresponding thermally rearranged polymers[Examples 1 to 3] undergoes microstructural change depending on the extent of rearrangement.
In detail, the cavity radius of a precursor polymer (which is centered at about 0.28 nm and is very broad) increases to 0.3 to 0.4 nm, and the distribution of cavity sizes becomes narrow as the thermal rearrangement temperature increases to 450° C. (see
PALS analysis reveals an increase in o-positronium (o-Ps) lifetime as rearrangement temperature increases from 300 to 450° C. (see Table 4). In general, longer o-Ps lifetime indicates larger cavity sizes (B. R. Wilks et al., J. Polym. Sci. Part B: Polym. Phys. 2003, 41, 2185). The o-Ps intensity (%) increases by 700% as thermal rearrangement temperature is increased to 400° C., but decreases above this temperature. Notably, despite increasing o-Ps lifetime, the reduction of o-Ps intensity in the sample treated at 450° C. (Example 3) indicates that an increase in mean cavity size is accompanied by a decrease in the number of cavities, suggesting coalescence of smaller cavities to form larger ones. Hourglass shaped cavities, having narrow neck regions separating much larger adjacent chambers, are consistent with the above results.
To have excellent separation properties, the small neck regions must not be too large relative to the size of the molecules being separated, because large openings enable relatively nonselective flow mechanisms (e.g., Knudsen flow) (Y. Yampolskii, I. Pinnau, B. D. Freeman, Materials Science of Membranes for Gas and Vapor Separation (Wiley, London, 2006)). However, large cavities adjoining the necks will contribute to high rates of molecular transport. The large cavity size of the fully converted sample (Example 3) is smaller than that of PTMSP (0.675 nm) but substantially larger than that of common glassy polymers (e.g., 0.286 nm for polysulfone; 0.289 nm for polycarbonate) (B. R. Wilks et al., J. Polym. Sci. Part B: Polym. Phys. 2003, 41, 2185). Similar behavior is observed in other precursor polymers prepared by a combination of other monomers based on the same methodology.
Referring to Experimental Example 7, it can be confirmed that the polymer compounds of the present invention demonstrate excellent O2/N2 and CO2/CH4 separation performance, surpassing the O2/N2 and CO2/CH4 separation limitation of typical polymer membranes (See
With reference to Experimental Example 8 of the present invention, it can be seen that after the thermal rearrangement through the thermal treatment, the polymer compounds of the present invention undergo morphological change including reduced density, considerably increased fractional free volume due to increased microcavity size and increased d-spacing, as compared to the precursor polymers. As a result, the polymer compounds exhibit considerably high gas permeability, as compared with the precursor polymers.
There are two advantages to the polymer compounds of the present invention. First, the precursor polyimides(i.e., polyhydroxyimide, polythiolimide, polyaminoimide) are soluble in common solvents; that is, they can be prepared in the various forms(e.g., hollow fibers) and then continuously exposed to heat treatment because these polymer compounds produce tough, ductile, robust films rather than brittle, fragile specimens such as zeolite or carbon membranes. This feature markedly enhances their potential utility and ultimate reduction to practice.
Second, it is much easier and simpler to coat these organic polymer compounds without any defects or cracks onto microporous ceramic support membranes for the large scale production of membranes than to coat inorganic materials such as zeolite, silica, and carbon membranes onto such supports. Most of all, the greatest benefit of the polymer compounds according to the present invention is the ability to tune the cavity size and distribution of organic polymers for specific gas applications, vapor separation, water purification, low dielectric constant materials, adsorbents, thermostable fiber, films, and so forth by using various templating molecules and heat treatments, with one starting material.
In another aspect, the present invention is directed to a method for preparing the polymer compound comprising:
thermally treating polyimides represented by the following Formulae 15 to 32.
In Formulae 15 to 32,
Ar1 is a tetravalent C5-C24 arylene group or a tetravalent C5-C24 heterocyclic ring, which is substituted or unsubstituted with at least one substituent selected from the group consisting of C1-C10 alkyl, C1-C10 alkoxy, C1-C10 haloalkyl and C1-C10 haloalkoxy, or two or more of which are fused together to form a condensation ring or covalently bonded to each other via a functional group selected from the group consisting of O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2 and C(═O)NH;
Ar2 is a bivalent C5-C24 arylene group or a bivalent C5-C24 heterocyclic ring, which is substituted or unsubstituted with at least one substituent selected from the group consisting of C1-C10 alkyl, C1-C10 alkoxy, C1-C10 haloalkyl and C1-C10 haloalkoxy, or two or more of which are fused together to form a condensation ring or covalently bonded to each other via a functional group selected from the group consisting of O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2 and C(═O)NH;
Q is O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2, C(═O)NH, C(CH3)(CF3), C1-C6 alkyl-substituted phenyl or C1-C6 haloalkyl-substituted phenyl in which Q is linked to opposite both phenyl rings in the position of m-m, m-p, p-m or p-p;
Y is —OH, —SH or —NH2;
Y′ is different from Y and is —OH, —SH or —NH2;
n is an integer from 20 to 200;
m is an integer from 10 to 400; and
l is an integer from 10 to 400.
Ar1 and Ar1 may be the same arylene or heterocyclic ring.
Preferably, Ar1 is selected from the following compounds and the linkage position thereof includes all of o-, m- and p-positions.
wherein X is O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2, or C(═O)NH; W is O, S or C(═O); and Z1, Z2 and Z3 are identical to or different from each other and are O, N or S.
More preferably, Ar1 is selected from the following compounds:
Preferably, Ar2 is selected from the following compounds and the linkage position thereof includes all of o-, m- and p-positions.
wherein X is O, S, C(═O), CH(OH), S(═O)2, Si(CH3)2, (CH2)p (in which 1≦p≦10), (CF2)q (in which 1≦q≦10), C(CH3)2, C(CF3)2, or C(═O)NH; W is O, S or C(═O); and Z1, Z2 and Z3 are identical to or different from each other and are O, N or S.
More preferably, Ar2 is selected from the following compounds:
Preferably, Q is CH2, C(CH3)2, C(CF3)2, O, S, S(═O)2 or C(═O).
More preferably, Ar1 is
Ar2 is
and Q is C(CF3)2.
The method for preparing the polymer compounds comprising irreversible molecular rearrangement at about 350° C. to 500° C. for aromatic polyimides containing ortho-positioned functional groups (e.g., —OH, —SH and —NH2) through intramolecular and intermolecular conversion.
The representative method of these can be explained through polyhydroxyimide containing ortho-positioned hydroxyl group and polythiolimide containing ortho-positioned thiol group as a starting materials.
With reference to
The use of stiff, rigid chain elements (e.g., benzoxazole-phenylene ring, benzothiazole-phenylene ring or benzopyrrolone-phenylene ring) prevents large intrachain, indiscriminant torsional rotation, increases the efficiency of cavity formation, and inhibits rapid collapse of the created cavities. These materials are thermally stable, and the structural rearrangements occurring during this process do not correspond to partial rigid polymer chain segments in the solid state.
The polyimides represented by Formulae 15 to 18 are thermally rearranged through a preparation process which will be mentioned later, to be converted polybenzoxazole, polybenzothiazole and polybenzopyrrolone, each having a high fractional free volume. Here, the polybenzoxazole is prepared from polyhydroxyimide in which Y is —OH, the polybenzothiazole is prepared from polythiolimide in which Y is —SH, and the polybenzopyrrolone is prepared from polyaminoimide in which Y is —NH2.
In addition, the polyimide copolymers represented by Formulae 19 to 22 are thermally rearranged to be converted benzoxazole-imide copolymer, benzothiazole-imide copolymer or benzopyrrolone-imide copolymers which have a high fractional free volume. Here, it is possible to control physical properties of the thermally rearranged polymer compounds by controlling the copolymerization ratio between blocks which will be thermally rearranged into polybenzoxazole, polybenzothiazole and polybenzopyrrolone, and blocks which will be thermally rearranged into polyimides.
In addition, the polyimide copolymers represented by Formulae 23 to 32 are thermally rearranged to be converted copolymers of polybenzoxazole, polybenzothiazole and polybenzopyrrolone, each having a high free volume. Here, it is possible to control the physical properties of thermally rearranged polymer compounds thus prepared can be controlled by controlling the copolymerization ratio between blocks which are thermally rearranged into polybenzoxazole, polybenzothiazole and polybenzopyrrolone.
Preferably, the copolymerization ratio between the blocks, m:1, is from 0.1:9.9 to 9.9:0.1, more preferably 2:8 to 8:2, most preferably 5:5. The copolymerization ratio affects the morphology of the thermally rearranged polymer compounds thus prepared. Since such morphologic change is associated with free volume elements, gas permeability and selectivity, it is considerably important to control the copolymerization ratio.
The thermal treatment is carried out under an inert atmosphere at 350° C. to 500° C., preferably 400 to 450° C., for 1 minute to 12 hours, preferably 10 minutes to 2 hours at a heating rate of 1 to 10° C./min. When the temperature is below this range, the thermal rearrangement is not completed and the polyimide precursor remains unreacted, causing deterioration in purity. On the other hand, when the temperature exceeds this range, polyimide is disadvantageously converted into a carbon substance as an inorganic due to polymer carbonization. Accordingly, it is preferable that the thermal treatment be suitably performed within this temperature range.
The thermal treatment of the present invention will be illustrated in detail with reference to Reaction Schemes 1 and 2 below:
In Reaction Schemes 1 and 2, Ar1, Ar1′, Ar2, Q, Y, Y″, n, m, and l are defined as above.
As can be seen from Reaction Scheme 1, the polyimides represented by the Formulae 15 to 18 are converted through thermal treatment into polybenzoxazole, polybenzothiazole, polybenzopyrrolone represented by the Formulae 1 to 7. The conversion of polyimide into the thermally rearranged polymer compounds is carried out through the removal reaction of CO2 or H2O present in the polymers of Formulae 15 to 18.
At this time, the polyimides of Formulae 15 to 18 in which Y is —OH or —SH (i.e., polyhydroxyimide or polythiolimide) are thermally rearranged into polybenzoxazoles (Y″═O) or polybenzothiazoles (Y″═S) of Formula 1, Formula 3, Formula 5 and Formula 6. In addition, polyimides of Formulae 1 to 4 in which Y is —NH2 (i.e., polyaminoimide) are thermally rearranged into polybenzopyrrolones of Formulae 2, 4 and 7.
As can be seen from Reaction Scheme 2, through the afore-mentioned thermal treatment, polyimide copolymers of Formulae 19 to 22 are converted through the removal reaction of CO2 present in the polyimides into polymer compounds of Formulae 8 to 14.
At this time, polyimide copolymers of Formulae 19 to 22 in which Y is —OH or —SH are thermally rearranged into benzoxazole(Y″═O)-imide copolymers or benzothiazole(Y″═S)-imide copolymers of Formulae 8, 10, 12 and 13. In addition, polyimide copolymers of Formulae 19 to 22 in which Y is —NH2 are thermally rearranged into benzopyrrolone-imide copolymers of Formulae 9, 11 and 14.
The blocks constituting polyimide copolymers represented by Formulae 23 to 32 are thermally rearranged into polybenzoxazole, polybenzothiazole and polybenzopyrrolone, depending upon the type of Y to be converted into copolymers thereof, i.e., copolymers of polymers represented by Formulae 1 to 7.
The polyimides of Formulae 15 to 18, polyimide copolymers of Formulae 19 to 32 can be prepared in accordance with methods well known in the art. For example, the polyimide and the polyimide copolymer may be prepared by imidizing and cyclizing hydroxyl group (—OH) containing polyamic acid (i.e., polyhydroxyamic acid), thiol group containing polyamic acid (i.e., polythiolamic acid) or amine group (—NH2) containing polyamic acid (i.e., polyaminoamic acid) or copolymers thereof.
According to examples of the present invention, as depicted in Reaction Schemes 3 and 4 below, polyamic acids represented by Formulae 33 to 50 are imidized are then prepared into polyimides represented by Formulae 15 to 18, polyimide copolymers represented by Formulae 19 to 32.
The polyamic acids of Formulae 33 to 50 can be prepared in accordance with methods well known in the art. For example, the polyamic acids may be prepared by reacting tetracarboxylic acid anhydrides as monomers with aromatic diamines containing —OH, —SH or —NH2.
As can be seen from Reaction Scheme 3, polyamic acids (i.e., polyhydroxyamic acid, polythiolamic acid and polyaminoamic acid) represented by the Formula 33, Formula 34, Formula 35 and Formula 36 are converted through imidization i.e., cyclization reaction into polyimides represented by Formula 15, Formula 16, Formula 17 and Formula 18, respectively. In addition, polyamic acid copolymers represented by the Formula 37, Formula 38, Formula 39 and Formula 40 are converted through imidization into polyimide copolymers represented by Formula 19, Formula 20, Formula 21 and Formula 22, respectively.
As can be seen from Reaction Scheme 4, polyamic acid copolymers represented by the Formulae 41 to 50 are converted through imidization into polyimide copolymers represented by Formulae 23 to 32.
The imidization can be conducted in accordance with methods well known in the art. Representative examples of the imidization include chemical imidization, thermal imidization and solution-thermal imidization.
Preferably, the chemical imidization is carried out at 10 to 180° C. for 1 to 48 hours. At this time, acetic anhydride can be added to remove water as a byproduct along with pyridine as a catalyst.
Preferably, the thermal imidization is carried out under an inert atmosphere or vacuum state at 100 to 300° C. for 1 minute to 24 hours after casting the polymeric solution onto a glass plate.
In addition, preferably, the solution-thermal imidization is carried out in solution at 80 to 250° C. for 1 to 48 hours.
When the imidization temperature is below this range, polyamic acid as a precursor is only slightly imidized, and on the other hand, when the imidization temperature exceeds this range, significant effects cannot be obtained and economic efficiency is thus very low. The imidization conditions may be suitably controlled within the range according to the functional groups, Ar1, Ar2, Q and Y.
Hereinafter, preferred examples will be provided for a further understanding of the invention. These examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
A benzoxazole represented by Formula 51 was prepared as follows.
A 250 ml reactor fitted with a teflon stirring system, an inlet for an nitrogen gas and placed in an oil bath to constantly maintain the reaction temperature at room temperature. The reactor was charged with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and N-methylpyrrolidone (NMP) as a solvent. 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride was slowly added into the solution. Then, the solution was allowed to react for about 4 hours to prepare a pale yellow viscous polyhydroxyamic acid solution.
The solution was cast on a glass plate and cured in vacuum oven for 2 hours at 100° C., 1 hour for 150° C., 1 hour for 200° C., and 1 hour for 250° C.
Then, vacuum drying was carried out in a vacuum oven at 60° C. for 24 hours in order to completely remove the residual solvent. Consequently, the transparent brownish polyhydroxyimide film (4 cm×4 cm in size; 20-50 μm in thickness) was obtained. The polyhydroxyimide film was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 350° C. at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 350□ and then cooled down slowly to room temperature.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole was prepared in the same manner as in Example 1, except that the polyhydroxyimide film was thermally treated at 400° C.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole was prepared in the same manner as in Example 1, except that the polyhydroxyimide film was thermally treated at 450° C.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole was prepared in the same manner as in Example 1, except that the polyhydroxyimide film was thermally treated at 500° C.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole represented by Formula 52 was prepared in the same manner as in Example 3, except that 2.94 g (10 mmol) of 3,3′,4,4′-biphenyltetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole represented by Formula 53 was prepared in the same manner as in Example 3, except that 3.10 g (10 mmol) of 4,4′-oxydiphthalic anhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole represented by Formula 54 was prepared in the same manner as in Example 3, except that 2.18 g (10 mmol) of 1,2,4,5-benzenetetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—N) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole represented by Formula 55 was prepared in the same manner as in Example 3, except that 3.22g (10 mmol) of 3,3′,4,4′-benzophenone tetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzothiazole represented by Formula 56 was prepared in the same manner as in Example 3, except that 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 2.08 g (10 mmol) of 2,5-diamino-1,4-benzenedithiol dihydrochloride.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzothiazole at 1,484 cm−1 (C—S) and 1,404 cm−1 (C—S) which were not detected in polythiolimide were confirmed.
A polybenzopyrrolone represented by Formula 57 was prepared in the same manner as in Example 3, except that 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 2.14 g (10 mmol) of 3,3′-diaminobenzidine.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzopyrrolone at 1,758 cm−1 (C═O) and 1,625 cm−1 (C═N) which were not detected in polyaminoimide were confirmed.
A polybenzoxazole represented by Formula 58 was prepared in the same manner as in Example 3, except that 2.68 g (10 mmol) of 1,4,5,8-naphthalenic tetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
Chemical Imidization
A 250 ml reactor fitted with a teflon stirring system, an inlet for an nitrogen gas and placed in an oil bath to constantly maintain the reaction temperature at room temperature. The reactor was charged with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and N-methylpyrrolidone (NMP) as a solvent. 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) was slowly added into the solution. After 4 hours of vigorous stirring, 1.61 ml (20 mmol) of pyridine and 1.89 ml (20 mmol) of acetic anhydride were added to the solution as catalyst for chemical imidization. Subsequently, the oil bath was heated to temperature of 80° C. and allowed to react for about 24 hours to prepare a pale yellow viscous polyhydroxyimide solution.
The solution was cast on a glass plate and cured in vacuum oven for 6 hours at 180° C. Then, vacuum drying was carried out in a vacuum oven at 60° C. for 24 hours in order to completely remove the residual solvent. Consequently, the transparent brownish polyhydroxyimide film(4 cm×4 cm in size; 20-50 μm in thickness) was obtained. The polyhydroxyimide film was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 450 at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 450° C. and then cooled down slowly to room temperature.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
(Solution-thermal Imidization)
A polybenzoxazole was prepared in the same manner as in Example 12, except that the pale yellow viscous polyhydroxyamic acid solution was prepared without pyridine and acetic anhydride by solution-thermal imidization at 80° C. for 4 hour and 180° C. for 4 hour in solution. As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
A 250 ml reactor fitted with a teflon stirring system, an inlet for an nitrogen gas and placed in an oil bath to constantly maintain the reaction at room temperature. The reactor was charged with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and N-methylpyrrolidone (NMP) as a solvent. 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene) diphthalic anhydride was slowly added into the solution. Then, the solution was allowed to react for about 4 hours to prepare a pale yellow viscous polyhydroxyamic acid solution.
The solution was cast on a glass plate and cured in vacuum oven for 2 hours at 100° C., 1 hour for 150° C., 1 hour for 200° C., and 1 hour for 250° C. Then, vacuum drying was carried out in a vacuum oven at 60° C. for 24 hours in order to completely remove the residual solvent. Consequently, the transparent brownish polyhydroxyimide film (4 cm×4 cm in size; 20-50 μm in thickness) was obtained. The polyhydroxyimide film was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 350° C. at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 350° C. and then cooled down slowly to room temperature.
Then, the polybenzoxazole films were treated in 10M HCl solution at one hour, washed with distilled water, and dried at 150° C.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed, and a characteristic band of chlorine anion at 920 cm−1 was also confirmed.
A polybenzoxazole was prepared in the same manner as in Example 14, except adding a final process in which the thermally rearranged films were treated in 10M NaOH solution until the pH was set to 7.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed, but a characteristic band of chlorine anion at 920 cm−1 was not confirmed.
A polybenzoxazole was prepared in the same manner as in Example 14, except adding two final processes in which the thermally rearranged films were treated in 10M NaOH solution until the pH was set to 7, and treated again in 10M HCl solution at one hour, washed and dried at 150° C.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed, and a characteristic band of chlorine anion at 920 cm−1 was also confirmed.
A polybenzoxazole was prepared in the same manner as in Example 14, except that the 10 M HCl solution was substituted for 10 M H3PO4 solution.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed, and a characteristic band of chlorine anion at 1,020 cm−1 was also confirmed.
Silica-dispersed solution with 5 weight percent was fabricated via dispersion of fumed silica powder (Aerosil 200) with average particle size of 13 nm in N-methylpyrrolidone, and added with content of 1 weight percent into the polyhydroxyamic acid solution in Example 3. The polyhydroxyamic acid solution containing dispersed silica was cast on a glass plate and cured in vacuum oven for 2 hours at 100° C., 1 hour for 150° C., 1 hour for 200° C., and 1 hour for 250° C. Then, vacuum drying was carried out in a vacuum oven at 60° C. for 24 hours in order to completely remove the residual solvent. Consequently, the transparent brownish polyhydroxyimide film (4 cm×4 cm in size; 20-50 μm in thickness) was obtained. The polyhydroxyimide film was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 450° C. at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 450° C. and then cooled down slowly to room temperature.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1(C—O) which were not detected in polyhydroxyimide were confirmed.
Zirconium phosphate-dispersed solution with 5 weight percent was fabricated via dispersion of zirconium phosphate powder as a proton conductor in N-methylpyrrolidone as described in J. Membr. Sci. 2003, 226, 169 and added with content of 20 weight percent into the polyhydroxyamic acid solution in Example 3.
The polyhydroxyamic acid solution containing dispersed zirconium phosphate was cast on a glass plate and cured in vacuum oven for 2 hours at 100° C., 1 hour for 150° C., 1 hour for 200° C., and 1 hour for 250° C. Then, vacuum drying was carried out in a vacuum oven at 60° C. for 24 hours in order to completely remove the residual solvent. Consequently, the transparent brownish polyhydroxyimide film (4 cm×4 cm in size; 20-50 μm in thickness) was obtained. The polyhydroxyimide film was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 450° C. at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 450° C. and then cooled down slowly to room temperature.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm −1(C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzoxazole represented by Formula 59 was prepared in the same manner as in Example 3, except that 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 2.16 g (10 mmol) of 3,3′-dihydroxybenzidine.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,052cm−1 (C—O) which were not detected in polyhydroxyimide were confirmed.
A polybenzopyrrolone represented by Formula 60 was prepared in the same manner as in Example 3, except that 3.10 g (10 mmol) of 4,4′-oxydiphthalic anhydride as starting materials were reacted with 2.84 g (10 mmol) of benzene-1,2,4,5-tetramine tetrahydrochloride.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzopyrrolone at 1,758 cm−1 (C═O) and 1,625 cm−1 (C═N), which were not detected in polyaminoimide were confirmed.
A benzoxazole copolymer (molar ratio of benzoxazole:benzoxazole=5:5) represented by Formula 61 was prepared in the same manner as in Example 3, except that 5.88 g (20 mmol) of 3,3′,4,4′-biphenyltetracarboxylic anhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and 2.16 g (10 mmol) of 3,3′-dihydroxybenzidine.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzoxazole at 1,553, 1,480 cm−1 (C═N) and 1,058 cm −1 (C—O) which were not detected in polyhydroxyimide were confirmed.
A benzoxazole-imide copolymer (molar ratio of benzoxazole:imide=8:2) represented by Formula 62 was prepared in the same manner as in Example 3, except that 6.45 g (20 mmol) of 3,3′,4,4′-benzophenonetetracarboxylic dianhydride as starting materials were reacted with 5.86 g (16 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and 0.8 g (4 mmol) of 4,4′-diaminodiphenylether.
As a result of FT-IR analysis, the resulting benzoxazole-imide copolymer (molar ratio of benzoxazole:imide=8:2) copolymer thus prepared showed characteristic bands of polybenzoxazole block at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1 (C—O), and characteristic bands of polyimide block at 1,720 cm−1 (C═O) and 1,580 cm−1 (C═O).
A benzopyrrolone-imide copolymer (molar ratio of benzopyrrolone:imide=8:2) represented by Formula 63 was prepared in the same manner as in Example 3, except that 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 1.71 g (8 mmol) of 3,3′-diaminobenzidine and 0.4 g (2 mmol) of 4,4′-diaminodiphenylether.
As a result of FT-IR analysis, the resulting benzopyrrolone-imide copolymer (molar ratio of benzopyrrolone:imide=8:2) copolymer showed characteristic bands of polypyrrolone block at 1,758 cm−1 (C═O) and 1,625 cm−1 (C═N) and characteristic bands of polyimide block at 1,720 cm−1 (C═O) and 1,580 cm−1 (C═O).
A benzothiazole-imide copolymer (molar ratio of benzothiazole:imide=8:2) represented by Formula 64 was prepared in the same manner as in Example 3, except that 8.88 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 3.30 g (16 mmol) of 2,5-diamino-1,4-benzenedithiol dihydrochloride and 0.8 g (4 mmol) of 4,4′-diaminodiphenylether.
As a result of FT-IR analysis, the resulting benzothiazole-imide copolymer (molar ratio of benzothiazole:imide=8:2) copolymer showed characteristic bands of polybenzothiazole block at 1,484 cm−1 (C—S) and 1,404 cm−1 (C—S) and characteristic bands of polyimide block at 1,720 cm−1 (C═O) and 1,580 cm−1 (C═O).
A benzoxazole-thiazole copolymer (molar ratio of benzoxazole:thiazole=5:5) represented by Formula 65 was prepared in the same manner as in Example 3, except that 2.94 g (10 mmol) of 3,3′,4,4′-biphenyltetracarboxylic anhydride as starting materials were reacted with 1.08 g (5 mmol) of 3,3′-dihydroxybenzidine and 1.09 g (5 mmol) of 2,5-diamino-1,4-benzenedithiol dihydrochloride.
As a result of FT-IR analysis, the resulting benzoxazole-thiazole copolymer (molar ratio of benzoxazole:thiazole=5:5) copolymer showed characteristic bands of polybenzoxazole block at 1,595, 1,480 cm−1 (C═N) and 1,052 cm−1 (C−O), and characteristic bands of polybenzothiazole block at 1,484 cm−1 (C—S) and 1,404 cm−1 (C—S) which were not detected in polyimide were confirmed.
A benzopyrrolone copolymer (molar ratio of benzopyrrolone:benzopyrrolone=8:2) represented by Formula 66 was prepared in the same manner as in Example 3, except that 8.88 g (20 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 3.42 g (16 mmol) of 3,3′-diaminobenzidine and 1.14 g (4 mmol) of benzene-1,2,4,5-tetramine tetrahydrochloride.
As a result of FT-IR analysis, characteristic bands of the resulting polybenzopyrrolone at 1,758 cm−1 (C═O) and 1,625 cm−1 (C═N), which were not detected in polyaminoimide, were confirmed.
A benzoxazole-imide copolymer (molar ratio of benzoxazole:benzothiazole=5:5) represented by Formula 67 was prepared in the same manner as in Example 3, except that 2.94 g (10 mmol) of 3,3′,4,4′-biphenyltetracarboxylic dianhydride as starting materials were reacted with 1.83 g (5 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and 1.00 g (5 mmol) of 4,4′-diaminodiphenylether.
As a result of FT-IR analysis, the resulting benzoxazole-imide copolymer (molar ratio of benzoxazole:imide=5:5) copolymer thus prepared showed characteristic bands of polybenzoxazole block at 1,553, 1,480 cm−1 (C═N) and 1,058 cm−1 (C—O), and characteristic bands of polyimide block at 1,720 cm−1 (C═O) and 1,580 cm−1 (C═O).
A benzoxazole-imide copolymer (molar ratio of benzoxazole:imide=2:8) was prepared in the same manner as in Example 28, except that copolymerization ratio of benzoxazole to imide was adjusted to 2:8.
A benzoxazole-imide copolymer (molar ratio of benzoxazole:imide=8:2) was prepared in the same manner as in Example 28, except that copolymerization ratio of benzoxazole to imide was adjusted to 8:2.
A 250 ml reactor fitted with a teflon stirring system, an inlet for an nitrogen gas and placed in an oil bath to constantly maintain the reaction temperature at room temperature. The reactor was charged with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane and N-methylpyrrolidone(NMP) as a solvent. 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride was slowly added into the solution. Then, the solution was allowed to react for about 4 hours to prepare a pale yellow viscous polyhydroxyamic acid solution.
The solution was cast on a glass plate and cured in vacuum oven for 2 hours at 100° C., 1 hour for 150° C., 1 hour for 200° C., and 1 hour for 250° C. Then, vacuum drying was carried out in a vacuum oven at 60° C. for 24 hours in order to completely remove the residual solvent. Consequently, the transparent brownish polyhydroxyimide film (4 cm×4 cm in size; 20-50 μm in thickness) was obtained. The polyhydroxyimide film was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 300° C. at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 300° C. and then cooled down slowly to room temperature.
A polythiolimide was prepared in the same manner as in Comparative Example 1, except that 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 2.08 g (10 mmol) of 2,5-diamino-1,4-benzenedithiol dihydrochloride.
A polyaminoimide was prepared in the same manner as in Comparative Example 1, except that 4.44 g (10 mmol) of 4,4′-(hexafluoroisopropylidene)diphthalic anhydride as starting materials were reacted with 2.14 g (10 mmol) of 3,3′-diaminobenzidine.
A polybenzoxazole was prepared in the same manner as in Comparative Example 1, except that 3.10 g (10 mmol) of 4,4′-oxydiphthalic anhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
A polybenzoxazole was prepared in the same manner as in Comparative Example 1, except that 2.18 g (10 mmol) of 1,2,4,5-benzenetetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′ -bis(3 -amino-4-hydroxy-phenyl)hexafluoropropane.
A polybenzoxazole was prepared in the same manner as in Comparative Example 1, except that 3.22 g (10 mmol) of 3,3′,4,4′-benzophenone tetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
A polybenzoxazole was prepared in the same manner as in Example 3, except that 2.94 g (10 mmol) of 3,3′,4,4′-biphenyl tetracarboxylic dianhydride as starting materials were reacted with 3.66 g (10 mmol) of 2,2′-bis(3-amino-4-hydroxy-phenyl)hexafluoropropane.
A carbon molecular sieve film was prepared from carbonizing polyimide (Kapton®, Du Pont) at 600° C.
In detail, a commercial polyimide film prepared from equimolar 1,2,4,5-benzenetetracarboxylic dianhydride and 4,4′-diaminodiphenylether as starting materials was placed in the middle of a quartz tube, and thermally treated in the muffled tubular furnace at 600° C. at a heating rate of 5° C./min under argon flow (100 cm3[STP]/min). Films were held for one hour at 600° C. and then cooled down slowly to room temperature.
A carbon molecular sieve film was prepared in the same manner as in Comparative Example 8, except that polyimide film (Kapton®, Du Pont) was carbonized at 800° C.
A carbon molecular sieve film was prepared from carbonizing polyhydroxyimide of Comparative Example 1, except that the polyhydroxyimide film was carbonized at 600° C.
As described in J. Polym. Sci.,: Part B: Polym. Phys. 30, 1215, 2,2′-bis(trimethylsilylamino-4-trimethylsiloxy-phenyl)-1,1,1,3,3,3-hexafluoropropane and hexafluoroisopropylidenebiphenyl-4,4-dicarboxylic acid chloride with the same equivalent was dissolved in dimethylacetamide at 0° C., and reacted to obtain poly(o-hydroxyamide). The solution was cast on a glass plate and thermal-treated at 300° C. under an inert atmosphere. Consequently, polybenzoxazole film was obtained.
FT-IR Analysis
In order to characterize precursor and polymer compounds, ATR-FTIR spectra were obtained using an Infrared Microspectrometer (IlluminatIR, SensIR Technologies, Danbury, Conn., USA).
As can be seen from
In addition, Examples 1, 2, 5 to 8, 11 to 20 and 22 which contain the similar structure and same functional groups to Example 3, and Comparative Examples 4 to 7 to Comparative Example 1 showed the same spectra with Example 3 and Comparative Example 1, respectively.
As shown in
As can be seen from
In addition, Examples 21 and 27 which contain the similar structure and same functional groups to Example 10 showed the same infrared spectra with Example 10.
Thermogravimetric Analysis/Mass Spectroscopy (TGA-MS)
The polyimides of Comparative Example 1, 2, and 3, the polybenzoxazoles of Examples 1, 3 and 4, the polybenzothiazole of Example 9, and the polybenzopyrrolone of Example 10 were subjected to thermogravimetric analysis/mass spectroscopy (TGA-MS) to confirm the weight loss occurred from the thermal rearrangement. The TGA-MS was carried out using TG 209 F1 Iris and QMS 403C Aeolos (NETZSCH, Germany), while injecting Ar into each precursor membrane. At this time, heating rate was 10° C./min and Ar purge flow was 90 cm3 (STP)/min. The results thus obtained are shown in
As can be seen from
In addition, Examples 2, 5 to 8, 11 to 20 and 22 which contain the similar structure and same functional groups to Example 3, and Comparative Examples 4 to 7 to Comparative Example 1 showed the similar thermal decomposition curves to Example 3 and Comparative Example 1, respectively.
As can be seen from
As can be seen from
In addition, Examples 21 and 27 which contain the similar structure and same functional groups to Example 10 showed the similar thermal decomposition curves to Example 10.
From these data, we can see that thermal resistance of the present invention thermally treated at high temperature is very good.
Elemental Analysis
To observe structure change of the polymer compounds of Examples 1 to 4 and Comparative Example 1, elemental analyzer (Carlo Erba/Fison Inc., ThermoFinnigan EA1108) was engaged, WO3/Cu was engaged as a catalyst, BBOT (2,5-bis(5-tert-butyl-benzoxazole-2-yl) thiophene) was engaged as Standard material. Table 1 shows the test result of examples at 1000° C.
Referring table 1, polyhydroxyimide of Comparative Example 1 must be comprised of 52.7% C, 1.82% H, 3.62% N, 11.3% O, 29.4% F in the abstract. The constituents of polyhydroxyimide of Comparative Example 1 (53.2±0.08% C, 1.87±0.06% H, 3.62±0.01% N, 11.3±0.22% O, 30.0±0.08% F) was consistent with the above theoretic polyhydroxyimide constituents.
In addition, polybenzoxazole of Example 3 must be comprised of 55.9% C, 2.06% H, 4.08% N, 4.66% 0, 33.2% F in the abstract. The constituents of polybenzoxazole of Example 3 (56.7±0.01% C, 1.93±0.02% H, 4.21±0.01% N, 4.89±0.12% O, 32.3±0.12% F) was consistent with the above theoretic polybenzoxazole constituents.
From these data, we can confirm that the formula of the thermally rearranged polymer compounds of the present invention is consistent with the supposed chemical formula.
Mechanical Properties
The mechanical properties of the precursor and polymer films shown were measured at 25° C. using AGS-J 500N (shimadzu). Five specimens of each sample were tested. Standard deviation from the mean was within ±5%. The results thus obtained are shown in Table 2.
As can be seen from Table 2, the polymer compounds of the present invention showed better tensile strength and elongation percent than that of Comparative Example, because the polyimide main chain structure was changed into stiff and rigid aromatic-connected polybenzoxazole structure through thermal rearrangement. Therefore, it is advantageous that the polymer compounds of the present invention can endure harsh conditions such as long operation temperature, acidic conditions and high humidity due to the rigid polymer backbone present in the polymer compounds.
Adsorption and Desorption Isotherm Analysis
This experiment was performed to determine N2 adsorption/desorption characteristics of the polymer compounds according to the present invention. N2 adsorption isotherms of the polymer compounds were measured by a BET method. The results thus obtained are shown in
As shown in
In order to realize more precise characterization, the pore volume of polymer compounds according to the present invention was measured using a specific surface area and pore analyzer (ASAP2020, Micromeritics, GA, USA). At this time, the polymer compounds were transferred to pre-weighed analytic tubes which were capped with Transeal™ to prevent permeation of oxygen and atmospheric moisture during transfers and weighing. The polymer compounds were evacuated under dynamic vacuum up to 300□ until an outgas rate was less than 2 mTorr/min. The results are shown in Table 3 below.
Specific surface area and total pore volume were calculated by measuring nitrogen adsorption degree until saturated pressure (P/Po=1) by the cm3/g unit and using liquefied nitrogen at 77K through Equations 1 to 2 well-known as Brunauer-Emmett-Teller (BET) within 0.05<P/Po<0.3.
In the Equation 1, P is balance pressure of gas, P0 is saturated pressure of gas, v is quantity of gas adsorbed, vm is quantity of gas adsorbed at single phase at adsorption temperature, and c is BET constant of Equation 2.
In the Equation 2, E1 is adsorption heat at first phase, and EL is adsorption heat beyond second phase, R is a gas constant, and T is measuring temperature.
As can be seen from Table 3, the BET surfaces area of Example 3 are markedly large for polymers, 661.5 m2g−1, total pore volume at a single point are 0.335 cm3g−1. It indicates the presence of substantial amount of free volume.
Positron Annihilation Lifetime spectroscopy (PALS) Measurements
The PALS measurements were performed in nitrogen at ambient temperature using an automated EG&G Ortec fast-fast coincidence spectrometer. The timing resolution of the system was 240 ps. The polymer films were stacked to a thickness of 1 mm on either side of a 22Na—Ti foil source. There was no source correction needed for the Ti foil (thickness 2.5 μm). Each spectrum consisted of approximately 10 million integrated counts. The spectra were modeled as the sum of three decaying exponentials or as a continuous distribution. The shortest lifetime, τ1, was fixed at 0.125 ns, which is characteristic of para-positronium self-annihilation. The second lifetime, τ2, was approximately 0.35-0.45 ns for all samples, characteristic of free and trapped positrons. The longer lifetime, τ3, was >1 ns and attributed to annihilations of o-Ps in the free volume elements of the polymer.
Positron annihilation lifetime spectroscopy (PALS) is an instrument measuring 0.511 MeV of 2-γ signals regarding β+ positron disappearance by combining with electron in the pore. β+ positron is emitted during radioisotope decay of 22Na to 22Ne. The size of pore can be calculated through Equation 3 using disappearance time of 0.511 MeV of 2γ signals.
In the Equation 3, τ0-Ps is disappearance time of positron (ns), R is pore size, and ΔR is empirical parameter of the supposition that the pore is sphere.
The results thus obtained are shown in
Micropore size and uniformity can be seen from
Gas Permeability Measurements
In order to ascertain gas permeability and selectivity of Examples 1 to 11, 14 to 18, 20 to 30 and Comparative Examples 1 to 10, the following processes were performed using a high-vacuum time-lag apparatus (the calibrated downstream volume was 30 cm3, the upstream and the downstream pressures were measured using a Baratron transducer with a full scale of 33 and 0.002 atm, respectively). The results are shown in Table 5 and
All pure gas permeation tests were performed at 35° C. more than five times, and the standard deviation from the mean values of the permeabilities was within ±2%. The sample-to-sample reproducibility was very good, within ±5%. The effective area of the membranes was 4.00 cm2.
For theses pure gases, it is possible to measure either the volume of permeate at fixed pressure or the rate of rise of permeate pressure in a fixed receiver volume. The pressure at permeate, p2, has very small value (<2 Torr) while the pressure at inlet, p1 is atmospheric pressure or more. While the pressure at permeate side was measured by recording of p2 versus time(sec), it is capable of approximating the permeabilities of gas molecules through the thin films. The permeability coefficient of A molecules, PA, can be calculated from the rate at which the downstream pressure increases in the fixed permeate volume at the steady state as follows;
where V is the volume of fixed downstream receiver, 1 is the film thickness, A is the film area, p1 and p2 are the pressures in the upstream and downstream, respectively, R, T and t are the gas constant, temperature and time, respectively.
In the two plots, these microporous materials of the present invent showed superior gas permeabilities with proper selectivities due to the well-organized free volumes of these polymers, and most of them exceeded the conventional polymeric upperbounds well-known to an imaginary limitation for certain gas mixtures [L. M. Robeson, Correlation of separation factor versus permeability for polymeric membrane, J. Membr. Sci., 1991, 62, 165, L. M. Robeson, The upper bound revisited, J. Membr. Sci., 2008, 320, 390].
Fractional Free Volume
The fractional free volume of the precursor and polymer compounds was measured. Density of polymer is related with degree of free-volume, has an influence on transmittance. First, density of the membranes was measured by a buoyancy method using a Sartorius LA 310 S analytical balance in accordance with Equation 5.
In the Equation 5, ρp is density of polymer, ρω is density of deionized water, ωα is weight of polymer measured in the air, ωω is weight of polymer measures in the deionized water.
The fractional free volume (FFV, Vf) was calculated from the data in accordance with Equation 6 below [W. M. Lee. Selection of barrier materials from molecular structure. Polym Eng Sci. 1980;20:65-9].
wherein V is the polymer specific volume and Vw is the specific Van der Waals volume. The Van der Waals volume was estimated by a Cerius 4.2 program using a synthia module based on the work of J. Bicerano [J. Bicerano. Prediction of polymer properties, Third Edition. Marcel Dekker Inc. 2002].
The d-spacing was calculated in accordance with Bragg's equation from X-ray diffraction pattern results.
As can be seen from Table 6, porosity in the polymer matrix of the present invention greatly increased from the result that Vf of Example 3, 5 to 8, 10 compared with Comparative Examples 1, 3 to 7 increased 28% to 102% due to the decrease in density of Example 3, 5 to 8, 10 after thermal treatment.
This application is a continuation of U.S. patent application Ser. No. 12/249,159 filed Oct. 10, 2008 and entitled “POLYMER COMPOUNDS AND A PREPARATION METHOD THEREOF,” the contents of which are incorporated in this application by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3461096 | Gaudemaris et al. | Aug 1969 | A |
| 3532673 | Pezdirtz et al. | Oct 1970 | A |
| 3598786 | Yoda et al. | Aug 1971 | A |
| 4087409 | Preston | May 1978 | A |
| 4820793 | Imai et al. | Apr 1989 | A |
| 4978733 | Khanna | Dec 1990 | A |
| 4980447 | Khanna | Dec 1990 | A |
| 5030706 | Harris et al. | Jul 1991 | A |
| 5071948 | Khanna | Dec 1991 | A |
| 5120825 | Vora et al. | Jun 1992 | A |
| 5173561 | Gupta | Dec 1992 | A |
| 5262056 | Koros et al. | Nov 1993 | A |
| 5494991 | Kaneko et al. | Feb 1996 | A |
| 5525436 | Savinell et al. | Jun 1996 | A |
| 5716727 | Savinell et al. | Feb 1998 | A |
| 5723086 | Ledjeff et al. | Mar 1998 | A |
| 5919892 | Hwang et al. | Jul 1999 | A |
| 5985969 | Harris et al. | Nov 1999 | A |
| 6099988 | Savinell et al. | Aug 2000 | A |
| 6204356 | Saito et al. | Mar 2001 | B1 |
| 6291635 | Maeda et al. | Sep 2001 | B1 |
| 6548621 | Tsai et al. | Apr 2003 | B1 |
| 6602415 | Koros et al. | Aug 2003 | B2 |
| 7745516 | Dueber et al. | Jun 2010 | B2 |
| 20020153315 | Koros et al. | Oct 2002 | A1 |
| 20040229160 | Naiini et al. | Nov 2004 | A1 |
| 20040229166 | Rushkin et al. | Nov 2004 | A1 |
| 20040229167 | Naiini et al. | Nov 2004 | A1 |
| 20040249110 | Naiini et al. | Dec 2004 | A1 |
| 20040253537 | Rushkin et al. | Dec 2004 | A1 |
| 20040253542 | Rushkin et al. | Dec 2004 | A1 |
| 20050181297 | Naiini et al. | Aug 2005 | A1 |
| 20060216641 | Naiini et al. | Sep 2006 | A1 |
| 20060275699 | Naiini et al. | Dec 2006 | A1 |
| 20070099111 | Naiini et al. | May 2007 | A1 |
| 20090111050 | Naiini et al. | Apr 2009 | A1 |
| 20090197067 | Naiini et al. | Aug 2009 | A1 |
| 20090282982 | Jung et al. | Nov 2009 | A1 |
| 20090286078 | Lee et al. | Nov 2009 | A1 |
| 20090286904 | Lee et al. | Nov 2009 | A1 |
| 20090297850 | Jung et al. | Dec 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 2001-348428 | Dec 2001 | JP |
| 10-20060085845 | Jul 2006 | KR |
| 10-0782959 | Dec 2007 | KR |
| WO2006080766 | Aug 2006 | WO |
| WO2009107889 | Sep 2009 | WO |
| WO2009113747 | Sep 2009 | WO |
| WO2009142434 | Nov 2009 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20110230605 A1 | Sep 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12249159 | Oct 2008 | US |
| Child | 13112426 | US |