This invention relates to a method for purifying and optionally reusing (or recycling) polymer-containing solutions, such as those used in the production of flexographic printing plates. More specifically, this method relates to purifying such solutions using microfiltration as the primary purification means.
Organic solutions are used in various industries for washing, developing, or cleaning various substrates or materials and as a result, the organic solutions generally become contaminated with various polymeric materials that are dissolved in the organic solvents of which the organic solutions are composed.
For example, washout or developing processes are known for the preparation of flexographic printing plates, and the developing solutions become contaminated with various polymeric and non-polymeric materials from the non-imaged portions of the flexographic printing plate precursors. Such developing processes are described for example in U.S. Pat. No. 5,240,815 (Telser et al.), U.S. Pat. No. 7,226,709 (Kidnie et al.), and U.S. Pat. No. 7,279,254 (Zwadlo) and in U.S. Patent Application Publication 2005/0227182 (Ali et al.). Generally, the flexographic printing plate precursors are imaged and then developed to remove non-polymerized material while leaving the polymerized (cured) material intact to form a relief image in the resulting flexographic printing plates. Various organic solvents are generally contained in such developing solution including but not limited to, chlorinated hydrocarbons, saturated cyclic or acyclic hydrocarbons, aromatic hydrocarbons, lower aliphatic ketones, and terpene hydrocarbons.
Because flexographic printing plate precursors can be prepared from a variety of polymeric materials, it is usually necessary to match the imaged precursors with specific developing solutions so the non-polymerized materials can be quickly and completely removed to provide the relief images. Mechanical means such as brushing with rubbing means may be used to facilitate polymer removal.
The need for different developing solutions is a major inconvenience in the industry of flexography, particularly if all types of flexographic printing plate precursors are being imaged and processed in the same facility. The industry has been trying to develop effective and environmentally-friendly developing solutions to overcome these problems. For example, U.S. Pat. No. 6,248,502 (Eklund) describes the use of terpene esters in developing solutions to overcome some of these problems.
In addition, U.S. Pat. No. 7,326,353 (Hendrickson et al.) describes a useful process for purifying or recycling developing solutions containing specific organic solvents. This process requires the use of centrifuging the polymer-containing solvents with optional organic membrane filtration steps before or after centrifugation.
The present invention provides an improved method for purification, reclaiming, or recycling organic solvents from various industrial processes but particularly from the development of imaged flexographic printing plate precursors.
Thus, this invention provides a method for purifying a polymer-containing solution consisting essentially of subjecting the polymer-containing solution to microfiltration using a tubular filter having an average pore diameter of less than 1 μm and a filtration pressure of at least 0.35 MPa to provide a purified solution.
More specifically, the present invention provides a method for purifying a polymer-containing flexographic developing solution comprising:
subjecting the developing solution to microfiltration using a metal tubular filter having an average pore diameter of from about 0.02 to about 0.5 μm and a filtration pressure from about 1 to about 2 MPa and a flow rate of from about 15 to about 1,000 liters/min to provide a purified developing solution,
the developing solution containing one or more block copolymers of styrene and butadiene, block copolymers of styrene and isoprene, copolymers of butadiene and acrylonitrile, or copolymers of butadiene, acrylonitrile and acrylic acid.
We have found that the method of this invention is an environmentally freed, simple, and inexpensive means for reclaiming or recycling organic solvents such as flexographic developing solvents. While known reclamation methods are suitable for removing particulates and relatively large materials, the present invention can be used to remove smaller materials because of the use of microfiltration tubes having average pore size below 1 μm. Distillation and other power consuming and expensive methods can be avoided. The reclaimed solvents can be reused if desired or discarded in an environmentally appropriate manner.
The method can be carried out in a self-contained apparatus or by using separate equipment in different places. Most advantageously, the method is carried out in a self-contained manner so that the purified solvent can be readily recycled for reuse, for example, in a continuous manner. One system useful for this purpose is known as the Cold Reclamation System (CRS) that includes a continuous, tubular microfiltration process utilizing for example, stainless steel tubular filters. The method can also be carried out in a batch manner.
The method of this invention can be illustrated by reference to
The various parts of the purification system illustrated in
The polymer-containing solution can be pumped through the tubular filters at a pressure of at least 0.35 megapascals (MPa) (or 50 psi) and generally at from about 1 to about 2 MPa as a flow rate of from about 15 to about 1,000 liters/min (for example, about 15 to 50 liters/min going into the microfiltration tubes and up to 1,000 liters/min inside the microfiltration tubes). The permeate is pushed through the microfilter tubular membranes for recirculation or storage for future use. Recycling allows for continuous processing, for example, of imaged flexographic printing plate precursors. Concentrate that may build up within the microfiltration tubes, and containing polymers and other undesired materials, can be disposed of in any suitable manner. The microfiltration process generally recirculates the polymer-containing solution as many times as needed to reduce the solid content to 3% or less and preferably to 1% or less.
The method of this invention can be carried out at a temperature of from about 15 to about 50° C.
The polymer-containing solution is a polymer-containing organic solution such as a flexographic printing plate developing solution. The solution may contains one or more block copolymers of styrene and butadiene, block copolymers of styrene and isoprene, copolymers of butadiene and acrylonitrile, and copolymers of butadiene, acrylonitrile, and acrylic acid.
Moreover, the polymer-containing solution generally contains one or more of the following organic compounds: dialkylene glycol dialkyl ethers, acetic acid esters, carboxylic acid esters, alcohols, terpenes, terpene esters, lower aliphatic ketones, aromatic hydrocarbons, saturated or alicyclic hydrocarbons, and chlorinated hydrocarbons, that can serve as solvents or solvent mixtures.
While the microfiltration technique described herein is the only essential purification technique for this invention, the present invention may optionally include prefiltering the flexographic developing solution to remove solids before the microfiltration. Alternatively, or in addition to prefiltration, the method may also include, after microfiltration, subjecting the purified developing solution to ultrafiltration to remove non-polymeric molecules such as photoinitiators, crosslinking agents (or thermal curing agents), colorants, and any other additives that may be present in flexographic imaging compositions.
To aid in the separation and filtration of polymers from solvents in the polymer-containing solution (such as flexographic developers or washout solutions), the contaminated solution may be pre-treated before the microfiltration step in a crosslinking step to crosslink polymers and photopolymerizable monomers and oligomers. The crosslinking may be achieved using any suitable process such as UV or visible irradiation with thermal curing agents, such as peroxides, or the use of a flocculation step using a flocculating agent that is appropriate for the given polymer(s) in the solution. The crosslinking and flocculation steps can be used simultaneously or in sequence if desired.
The following example is meant to be representative of how the present invention is carried out and is not meant to be limiting in any manner.
Samples of commercially available Cyrel® flexographic printing plate precursors (DuPont) were imagewise exposed and then processed (developed) in a commercially available flexographic plate processor unit using a washout solution (developer) like that described in Example 4 of U.S. Pat. No. 6,162,593 (Wyatt et al.) that contained diisopropylbenzene, benzyl alcohol, a petroleum distillate, and a terpene alcohol. The resulting contaminated flexographic developing solution, which contained dissolved polymer from the flexographic printing plate, was then pumped through a SCEPTER stainless steel membrane module (containing TiO2 coatings permanently sintered to the inside of stainless steel support tubes). When the polymer level in the permeate (purified solvent solution) reached about 3 weight % solids (typically 1% solids or less), the purified solvent solution was ready for reuse in the plate processor unit and supplied to that unit as needed to process additional imaged plate samples.
The invention has been described in detail with particular reference to certain preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.