Patent Application
20090126601
The present invention relates to a polymer film and a producing method thereof.
A polymer film is used in an optical field. Especially, a cellulose acylate film is widely used as optical film for producing a reasonable and thin liquid crystal device since the cellulose acylate film has merits to be used as protective film for a polarizing filter.
Such a cellulose acylate film is mainly produced by a solution casting method, in which a polymer solution containing polymer (such as cellulose acylate and the like) and solvent is cast onto a running support to form a casting film. Then the casting film is peeled as film, which is dried.
When it is designated to produce the film by the solution casting method, it is contrived to make the casting speed higher so as to increase the productivity. In this case, for example, just after the casing onto the support with use of a drying device, an initial drying is made to a surface of the casting film, namely, a drying air with control of the temperature thereof is fed out through an outlet of a drying device. Thus the evaporation of the solvent from the casting film effectively proceeds, and the above problems are resolved.
However, only the drying air fed out from the outlet doesn't have enough effects of drying, and therefore cannot make the evaporation of the solvent in the casting film well. Further, the drying air fed out from the outlet doesn't flow uniformly. Therefore, the thickness of the casting film becomes uniform to cause the thickness nonuniformity. As the result, the planarity becomes lower.
As developments thereof, an air duct is disposed above the casting film on the support such that a slit-type outlet is directed to the support with inclination. The drying is made by feeding a wind from the outlet (see, Japanese Patent Laid-Open Publication No. 64-55214). Further, a drying air is blown to the casting film on the support in the most upstream side and further a drying device is disposed in a rear side of the support to heat the support. Thus the heating is made from a casting side and the rear side thereof (see, Japanese Patent Laid-Open Publication No. 2003-103544).
In any methods, unevenness on the film surface is reduced such the produced film may be excellent in planarity. However, in the method of the publication No. 64-55214, while the drying air is fed out through the slit-type outlet to make the drying, the drying air doesn't have enough heat quantity, and therefore the drying is sometimes not made enough. In the method of publication No. 2003-103544, since the drying is made from both casting and rear sides of the support, the drying speed can be made larger. However, the temperature of the drying air applied to the casting film on the support is not high, for example, in the range of 20° C. to 80° C. Therefore, the drying is sometimes not made enough.
In recent years, the electric devices are made miniaturized and thinner rapidly. Accordingly, the requirement of the miniaturization and the thinning of the optical film is large. Therefore, the optical film must be more excellent in planarity. However, in the above methods, it is difficult that the produced film has the enough planarity.
An object of the present invention is to provide a production method of producing a polymer film excellent in planarity while a dope is cast on a support to form a casting film in which the generation of unevenness is reduced.
In order to achieve the object and the other object, in a method of producing a film from a casting dope containing solvent and polymer, after the casting dope is cast on a running support to form a casting film, the support is heated with a temperature control almost constant in the range of 40° C. to 80° C. by a heater provided in a rear side of the support, so as to perform a first drying of the casting film. A drying air is fed with a temperature control almost constant in the range of 70° C. to 130° C. out from an outlet of an air duct provided in a casting side of the support, so as to make a second drying of the casting film. The outlet is directed in a running direction of the belt such that the drying air may flow almost in parallel to the belt. The casting film containing the solvent is peeled as the film. Then the drying of the film is made.
Preferably, the casting film has a multi-layer structure including an exposure layer exposed to an atmosphere and an inner layer contacting to the exposure layer. The casting of the casting dope is a co-casting of a first dope of the casting dope for forming the exposure layer and a second dope of the casting dope for forming the inner layer. Especially preferably, a viscosity of the first dope is at most 35 Pa·s.
Preferably, a thickness of the casting film is in the range of 10 μm to 400 μm.
Preferably, the first drying and the second drying are started when a content of the solvent in the casting layer is at least 350 wt. %. Especially preferably, the first drying starts earlier than the second drying, and especially, the second drying starts during performing the first drying.
A polymer film produced by the above method is also the present invention.
According to the present invention, when the dope is cast onto the support to form the casting film, the drying speed increased. Thus the productivity becomes higher and the generation of unevenness on a surface of the casting film is reduced. Therefore the produced film is excellent in planarity.
As polymer in this embodiment, cellulose acylate is used and especially preferably triacetyl cellulose. As for cellulose acylate, it is preferable that the degree of substitution of acyl groups for hydrogen atoms on hydroxyl groups of cellulose preferably satisfies all of following formulae (I)-(III).
2.5≦A+B≦3.0 (I)
0≦A≦3.0 (II)
0≦B≦2.9 (III)
In these formulae (I)-(III), A is the degree of substitution of the acetyl groups for the hydrogen atoms on the hydroxyl groups of cellulose, and B is the degree of substitution of the acyl groups for the hydrogen atoms while each acyl group has carbon atoms whose number is from 3 to 22. Note that at least 90 wt. % of TAC is particles having diameters from 0.1 mm to 4 mm. However, the polymer to be used in the present invention is not restricted in cellulose acylate, but may be the already-known polymers from which the film can be produced by a solution casting method.
As solvents for preparing the dope, there are aromatic hydrocarbons (for example, benzene, toluene and the like), hydrocarbon halides (for example, dichloromethane, chlorobenzene and the like), alcohols (for example, methanol, ethanol, n-propanol, n-butanol, diethyleneglycol and the like), ketones (for example, acetone, methylethyl ketone and the like), esters (for example, methyl acetate, ethyl acetate, propyl acetate and the like), ethers (for example, tetrahydrofuran, methylcellosolve and the like) and the like.
The solvents are preferably hydrocarbon halides having 1 to 7 carbon atoms, and especially dichloromethane. Then in view of the solubility of cellulose acylate, the peelability of a casting film from a support, a mechanical strength of a film, optical properties of the film and the like, it is preferable that one or several sorts of alcohols having 1 to 5 carbon atoms is mixed with dichloromethane. Thereat the content of the alcohols to the entire solvent is preferably in the range of 2 mass % to 25 mass %, and particularly in the range of 5 mass % to 20 mass %. Concretely, there are methanol, ethanol, n-propanol, iso-propanol, n-butanol and the like. The preferable examples for the alcohols are methanol, ethanol, n-butanol, or a mixture thereof.
By the way, recently in order to reduce the effect to the environment to the minimum, the solvent composition when dichloromethane is not used is progressively considered. In order to achieve this object, ethers having 4 to 12 carbon atoms, ketones having 3 to 12 carbon atoms, esters having 3 to 12 esters are preferable (methyl acetate is especially preferable), and a mixture thereof can be used. These ethers, ketones and esters may have the ring structure. Further, the compounds having at least two of functional groups (namely, —O—, —CO— and —COO—) in ethers, ketones and esters can be used for the solvent. Note that the solvent compounds may have other functional groups, such as alcoholic hydroxyl group and the like. If the solvent contains at least two sorts of the solvent compounds, a number of the carbon atoms may be in the described range of each compound having the above functional group.
The detail explanation of cellulose acylate is made from [0140] to [0195] in Japanese Patent Laid-Open Publication No. 2005-104148. The description of this publication is also applied to the present invention. Further, the additives (such as the solvent, plasticizer, deterioration inhibitor, UV absorbing agent, optically anisotropic controller, retardation controller, dyne, matting agent, release agent, releasing accelerator and the like) are described in detail from [0196] to [0516] of Japanese Patent Laid-Open Publication No. 2005-104148.
It is to be noted in a dope production line 10 that the production method of the dope used in the present invention is not restricted in the embodiment shown in
When a valve 31a is opened, the solvent is sent from the solvent tank 11 to the mixing tank 14. Then adequate amount of cellulose acylate is sent from the hopper 13 to the mixing tank 14. Thereafter, a valve 31b is opened such that the additive is sent from the additive tank 12 to the mixing tank 14.
The method of feeding the additive to the mixing tank is not restricted in the above description. If the additive is in the liquid state in the room temperature, it may be fed in the liquid state to the mixing tank 14 without preparing for the additive solution. Otherwise, if the additive is in the solid state in the room temperature, it may be fed in the solid state to the mixing tank 14 with use of a hopper. If plural sorts of additive compounds are used, the additive containing the plural additive compounds may be accumulated in the additive tank 12 altogether. Otherwise plural additive tanks may be used so as to contain the respective additive compounds, which are sent through independent pipes to the mixing tank 14.
In the above explanation, the solvent (or mixture of solvent compounds), the cellulose acylate, and the additive are sequentially sent to the mixing tank 14. However, the sending order is not restricted in it. For example, after the predetermined amount of cellulose acylate is sent to the mixing tank 14, the feeding of the predetermined amount of the solvent and the additive may be performed to obtain a cellulose acylate solution. Otherwise, it is not necessary to feed the additive to the mixing tank 14 previously, and the additive may be added to a mixture of TAC and solvent in following processes.
The mixing tank 14 is provided with a jacket 32 covering over an outer surface of the mixing tank 14, a first stirrer 34 to be rotated by a motor 33, and a second stirrer 36 to be rotated by a motor 35. The first stirrer 34 preferably has an anchor blade, and the second stirrer 36 is preferably an eccentric stirrer of a dissolver type. The jacket is provided with a temperature controlling device for controlling the temperature of a heat transfer medium flowing in the jacket. Thus the inner temperature in the mixing tank 14 is controlled. The preferable inner temperature is in the range of −10° C. to 55° C. At least one of the first and second stirrers 34, 36 is adequately chosen for performing the rotation. Thus a swelling liquid 37 in which TAC is swollen in the solvent is obtained.
In a downstream from the mixing tank 14, the dope production line 10 further includes a pump 38, a heating device 15, the temperature controlling device 16, a filtration device 17, and the stock tank 22.
The pump 38 is driven such that the swelling liquid 37 in the mixing tank 14 may be sent to the heating device 15 which is preferably a pipe with a jacket. Further, the heating device 15 preferably pressurizes the swelling liquid 37. While the swelling liquid 37 is continuously in only the heating condition or both of the heating and pressurizing condition, the dissolution of TAC proceeds such that the swelling liquid 37 may be a polymer solution. Note that the polymer solution may be a solution in which the polymer is entirely dissolved and a swelling liquid in which the polymer is swollen. Further, the temperature of the swelling liquid 37 is preferably in the range of 0° C. to 97° C. Instead of the heat-dissolution with use of the heating device 15, the swelling liquid 37 may be cooled in the range of −100° C. to −10° C. so as to perform the dissolution, which is already known as the cool-dissolution method. In this embodiment, one of the heat-dissolution and cool-dissolution methods can be chosen in accordance with the properties of the materials, so as to control the solubility. Thus the dissolution of TAC to the solvent can be made enough. The polymer solution is fed to the temperature controlling device 16, so as to control the temperature nearly to the room temperature.
Then the polymer solution is fed to the filtration device 17, such that impurities may be removed from the polymer solution. The filter material of the filtration device 17 preferably has an averaged nominal diameter of at most 100 μm. The flow rate of the filtration in the filtration device 17 is preferably at least 50 liter/hr.
In this embodiment, the polymer solution after the filtration is sent through a valve 40 to the flushing device 31 for concentrating the polymer solution. In the flushing device 31, the solvent of the polymer solution is partially evaporated. The solvent vapor generated in the evaporation is condensed by a condenser (not shown) to a liquid state, and recovered by the recovering device 20. The recovered solvent is recycled by the recycling device 21 and reused. According to this method, the decrease of cost can be designated, since the production efficiency becomes higher and the solvent is reused.
The polymer solution after the concentrating as the above description is extracted from the flushing device 31 through a pump 41 to a filtration device 19 for removing the undissolved materials in the filtration. Note that the temperature of the polymer solution in the filtration device 19 is preferably in the range of 0° C. to 200° C. Further, in order to remove bubbles generated in the polymer solution, it is preferable to perform the bubble removing treatment at the same time. As a method for removing the bubble, there are many methods which are already known, for example, an ultrasonic irradiation method and the like. The polymer solution after the filtration is stored in the stock tank 22, which is provided with a stirrer 43 rotated by a motor 42. The stirrer 43 is rotated so as to continuously stir the polymer solution.
Note that the method of producing the polymer solution is disclosed in detail in [0517] to [0616] in Japanese Patent Laid-Open Publication No. 2005-104148, for example, the dissolution method and the adding methods of the materials, the raw materials and the additives in the solution casting method for forming the TAC film, the filtering method, the bubble removing method, and the like.
[Solution Casting Method]
An embodiment of the solution casting method will be described in reference with
In a film production line 200, a casting dope including plural sorts of dopes is prepared from the polymer solution 39 and cast onto a belt 73 so as to form a casting film 80 having a multi-layer structure. Especially, in following, the casting film 80 has three layers, namely, a base layer and first and second outer layers contacting to the base layer. Therefore, the casting film 80 is peeled from the belt as film 101 having three layer structure. Further, in the preparation, three sorts of dopes are prepared, and three paths 44-46 for preparing the respective dopes are connected to the stock tank 22.
The polymer solution 39 is fed through the path 44 for preparing a dope for base layer (hereinafter, base layer dope). Then an additive 51 is stored in the stock tank 50 is fed by a pump 52 and added to the polymer solution 39. Thereafter, the mixture is mixed and stirred by a static mixer 53 to be uniform. Thus the base layer dope is obtained. The additive 51 is a solution (or a dispersion) previously containing additive compounds, for example, UV absorbing agent, retardation controller and the like.
The polymer solution 39 is fed through the path 45 for preparing a dope for first outer layer (hereinafter, first outer layer dope). Then an additive 56 is stored in the stock tank 55 is fed by a pump 57 and added to the polymer solution 39. Thereafter, the mixture is mixed and stirred by a static mixer 58 to be uniform. Thus the first outer layer dope is obtained. The additive 56 previously contains additive compounds, for example, peeling agent (for example citric acid ester and the like) which makes the peeling of the polymer film from a belt as the support easy, matting agent (silicone dioxide and the like) for reducing the adhesion of film surfaces in the film roll, and the like. Note that the additive 56 may contain the additive compounds, such as plasticizer, UV absorbing agent and the like.
The polymer solution 39 is fed through the path 46 for preparing a dope for second outer layer (hereinafter, second outer layer dope). Then an additive 61 is stored in a stock tank 60 is fed by a pump 62 and added to the polymer solution 39. Thereafter, the mixture is mixed and stirred by a static mixer 63 to be uniform. Thus the first outer layer dope is obtained. The additive 61 contains the additive compounds, such as matting agent (silicone dioxide and the like) for reducing the adhesion of film surfaces in the film roll, and the like. Note that the additive 61 may contain the additive compounds, such as peeling accelerator, plasticizer, UV absorbing agent and the like.
In the casting chamber 70, there are a casting die 72, back-up rollers 74a, 74b, a belt 73 supported by the back-up rollers 74a, 74b, a heat transfer medium circulator 75 and a temperature controlling device 77, and a condenser 78.
The materials of the casting die 72 are preferably precipitation hardening stainless steel. The preferable material has coefficient of thermal expansion of at most 2×10−5(° C.−1). Further, the material to be used has an anti-corrosion property, which is almost the same as SUS316, in the examination of forcible corrosion in the electrolyte solution. Preferably, the materials to be used for the casting die 72 has such resistance of corrosion that the pitting doesn't occur on the gas-liquid interface even if the material is dipped in a mixture of dichloromethane, methanol and water for three months. The casting die 72 is preferably manufactured by performing the polishing after a month from the material casting. Thus the surface condition of the dope flowing in the casting die 72 is kept uniform. The finish precision of a contact face of the casting die to the dopes is at most 1 μm in surface roughness and at most 1 μm/m in straightness. The clearance of a slit of the casting die 72 is automatically adjustable in the range of 0.5 mm to 3.5 mm. According to an edge of the contact portion of a lip end of the casting die 72 to the dope, R(R is chamfered radius) is at most 50 μm in all of a width. Further, the shearing rate in the casting die 72 is controlled in the range of 1 to 5000 per second.
A width of the casting die 72 is not restricted especially. However, the width is preferably at least 1.1 times and at most 2.0 times as large as a film width. During the film production, it is preferable to provide a temperature controlling device (heater, jacket and the like) for keeping the temperature of the casting die 72 to a predetermined value. Furthermore, the casting die 72 is preferably a coat hanger type die. Further, in order to adjust a film thickness, the casting die 72 is preferably provided with an automatic thickness adjusting device. For example, thickness adjusting bolts (heat bolts) are disposed at a predetermined interval in a widthwise direction of the casting die 72. According to the heat bolts, it is preferable that the profile is set on the basis of a predetermined program, depending on feed rate of pumps (preferably, high accuracy gear pumps) 47-49, while the film production is performed. Further, the film production line 200 may be provided with a thickness meter (not shown), such as infrared ray thickness meter and the like. In this case, the feed back control of the adjustment value of the heat bolts may be made by the adjusting program on the base of the profile of the thickness meter. The thickness difference between any two points in the widthwise direction except the side edge portions in the casting film is controlled preferably to at most 1 μm. The difference between the maximum and the minimum of the thickness in the widthwise direction is at most 3 μm. Further, the accuracy to the designated object value of the thickness is preferably in ±1.5 μm.
Preferably, a hardened layer is preferably formed on a top of a lip end of the casting die 72. A method of forming the hardened layer is not restricted. But it is, for example, ceramics hard coating, hard chrome plating, neutralization processing, and the like. If ceramics is used as the hardened layer, it is preferable that the used ceramics is grindable but not friable, with a lower porosity, high resistance of corrosion, and poor adhesiveness to the casting die 72. Concretely, there are tungsten carbide (WC), Al2O3, TiN, Cr2O3, and the like. Especially preferable ceramics is tungsten carbide. Tungsten carbide coating can be made by a spraying method.
Further, in order to prevent the partial dry-solidifying of the dopes flowing on slit ends of the casting die 72, it is preferable to provide a solvent supplying device (not shown) at the slit ends, on which a gas-liquid interfaces are formed between both edges of the slit and between both bead edges and the outer gas. Preferably, these gas-liquid interfaces are supplied with the solvent which can dissolve the dope, (for example a mixture solvent of dichloromethane 86.5 pts.mass, acetone 13 pts.mass, n-butanol 0.5 pts.mass). The supply rate to each slit end is preferably in the range of 0.02 mL/min to 1.0 mL/min, in order to prevent the foreign materials from mixing into the casting film. Note that the pump for supplying the solvent has a pulse rate (or ripple factor) at most 5%.
A belt 73 is positioned below the casting die 72, and lapped on the back-up rollers 74a, 74b. When the back-up rollers 74a, 74b are rotated by the driving device (not shown), and thus the belt 73 runs endlessly in accordance with the rotation of the back-up rollers 74a, 74b. Then the casting speed is preferably in the range of 10 m/min to 200 m/min. Further, the temperatures of the back-up rollers 74a, 74b are controlled by the heat transfer medium circulator 75 for cycling a heat transfer medium. It is preferable that the surface temperature of the belt 73 is adjusted in the range of −20° C. to 40° C. by heat transmission from the back-up rollers 74a, 74b. In this embodiment, paths (not shown) of the heat transfer mediums are formed in the back-up rollers 74a, 74b, and the heat transfer mediums whose temperatures are controlled by the heat transfer medium circulator 75 pass through the paths. Thus the temperature of the back-up rollers 74a, 74b are kept to the predetermined values.
The width, the length and the material of the belt 73 are not restricted especially. However, it is preferably 1.1 to 2.0 times as large as the casting width. Preferably, the length is from 20 m to 200 m, and the thickness is from 0.5 mm to 2.5 mm. The surface is preferably polished so as to have a surface roughness at most 0.05 μm. The belt 73 is preferably made of stainless steel, and especially of SUS 316 so as to have enough resistance of corrosion and strength. The thickness nonuniformity of the entire belt 73 is preferably at most 0.5%.
In the drive of the back-up rollers 74a, 74b, a tension occurring to the belt 73 is preferably 5×104 kg/m. The difference of the rotating speed between the rollers 74a, 74b is controlled to at most 0.01 m/min. Preferably, the fluctuation of the running speed of the belt is in 0.5%, and the positional fluctuation of the belt 73 in the widthwise direction in one rotation is at most 1.5 mm. In order to control the fluctuation, it is preferable that a detector (not shown) for detecting both side edge portions of the belt 73 and the feed back control is made on the basis of the measured value. Furthermore, just below the casting die 72, the positional variation of the belt 73 in up- and downwards in accordance with the rotation of the rollers 74a and 74b is preferably at most 200 μm.
Note that it is possible to use one of the back-up rollers 74a, 74b as support. In this case, the back-up roller used as support is preferably rotated at high accuracy such that a rotation flutter may be at most 0.2 mm. Therefore the surface roughness is preferably at most 0.01 μm. Further, the chrome plating is preferably performed to the drum such that the drum may have enough hardness and endurance. As described above, it is preferable in the support that the surface defect must be reduced to be minimal. Concretely there are no pin hole of at least 30 μm, at most one pin hole in the range of 10 μm to 30 μm, and at most two pin holes of less than 10 μm per 1 m2.
A temperature controlling device 77 is provided for controlling the inner temperature of a casting chamber 70 in the range of −10° C. to 57° C. Further, a condenser 78 is provided for condensing organic solvent evaporated in the casting chamber 70. Further a recovering device 79 for recovering the condensed organic solvent outside the casting chamber 70.
Further, the cast dope forms a bead between the casting die 72 and the belt 73. In order control the pressure in a rear side of the bead, it is preferable to dispose a decompression chamber 81. Thus the formation of the bead is stabilized, and the wobbling of the bead is reduced. Preferably, the pressure of the bead is from 5 Pa to 1000 Pa lower in the back side than the front side of the bead. Further, in order to control an inner temperature of the decompression chamber 81, there is preferably a jacket (not shown). The inner temperature is not restricted especially, but preferably in the range of 25° C. to 55° C. Furthermore, in order to keep the form of the bead, an aspirating device (not shown) is preferably provided at edge positions of the casting die 72. The aspiration rate of air is preferably in the range of 1 L to 100 L.
An air duct 82 is disposed around and near the belt 73 in the casting chamber 70, so as to dry a casting film 80 formed on the belt 73. Further, a heater 84 is provided in the rear side of the casting belt 73. In a downstream from the belt 73, there is a peeling roller 86 for peeling the casting film 80 as film 101 with support of the casting film 80. Furthermore, near the casting die 72, there are preferably air shielding members (not shown), such as walls for shielding air, and the like, such that the drying air may not be applied to the casting film in the first 5 seconds after the casting. In this case, the static pressure fluctuation near the casting die is preferably in ±1 Pa. The detailed explanation about the drying method of the casting film 80 in the casting chamber 70 will be made later.
In a transfer area 90, there are rollers and an air blower 91. In a tenter device 100, the film 101 is stretched in widthwise direction and relaxed, such that a predetermined optical properties are made. In this case, the stretch ratio as percentage of difference of the film width between after and before the stretch is in the range of 0.5% to 300%. Preferably, the inside of the tenter device 100 are partitioned to a plurality of temperature areas in which inner temperatures are different. In the transfer area 90 or the tenter device 100, it is preferable to draw the film 101 in one of the casting directions, while the draw ratio as percentage of difference of the film length between after and before the drawing is in the range of 0.5% to 300%. Furthermore, the edge slitting device 102 slit off both side edge portions of the film 101 into tips, and the tips of both side edge portions are crushed by a crusher connected to the edge slitting device 102.
In a drying device 105, the film 101 is transported with lapping on rollers 104. The solvent vapor evaporated from the film 101 by the drying device 105 is adsorbed by an adsorbing device 106. The film 101 is transported into a cooling chamber 107, and cooled therein to around the room temperature. A humidity control chamber (not shown) may be provided for conditioning the humidity between the drying device 105 and the cooling chamber 107. Thereafter, a compulsory neutralization device (or a neutralization bar) 85 eliminates the charged electrostatic potential of the film 101 to the predetermined value (for example, in the range of −3 kV to +3 kV). The position of the neutralization process is not restricted in this embodiment. For example, the position may be a predetermined position in the drying section or in the downstream side from a knurling roller 109, and otherwise, the neutralization may be made at plural positions. In a winding chamber 110, the film 101 is wound by a winding shaft 111. At this moment, a tension is applied at the predetermined value to a press roller 112.
As shown in
The outlet 82a is directed in the running direction of the belt 73, such that the drying air may be fed out from the outlet 82a to be almost parallel to the running direction of the belt 73. Thus the drying is made with reducing the generation of unevenness on the surface of the casting film 80.
The temperature of the drying air (casting side drying temperature) fed out through the outlet 82a to the surface of the casting film 80 is preferably to a predetermined value in the range of 70° C. to 130° C., and particularly that in the range of 80° C. to 125° C. Thus the drying of the casting film 80 is made enough and the evaporation of the solvent proceeds. If the casting side drying temperature is higher than 130° C., the temperature is too high to dry the casting film adequately. In this case, the foaming occurs in the casting film 80, and therefore the planarity of the film becomes lower, and so on. If the casting side drying temperature is lower than 70° C., the evaporation of the solvent in the casting film 80 is not made enough, and the drying cannot be made enough. Therefore when the casting film 80 is peeled from the belt 73, part of the casing film 80 sometimes remain on the belt 73.
Further, the heater 84 is provided in the rear side of the belt 73. The heater 84 heats the rear side of the belt 73 such that the heating of the casting film 80 may be made from the rear side of the belt 73. Thus the evaporation of the solvent in the casting film 80 is accelerated. Therefore, the drying speed is made higher to dry the casting film 80, which increase the productivity.
The temperature of the heater 84 (rear side drying temperature) is controlled to be preferably a predetermined value in the range of 40° C. to 80° C., and particularly in the range of 50° C. to 70° C., such that the casting film 80 may be dried. Thus, while the casting film 80 is heated from both of the casting side and the rear side, such that the drying may be made from both sides and accelerated. If the rear side drying temperature is higher than 80° C., the temperature is too high to dry the casting film adequately. In this case, the foaming occurs in the casting film 80, and therefore the planarity of the film becomes lower, and so on. If the casting side drying temperature is lower than 40° C., the evaporation of the solvent in the casting film 80 is not made enough, and the drying cannot be made enough. Therefore when the casting film 80 is peeled from the belt 73, part of the casing film 80 sometimes remain on the belt 73.
When it is designated to dry the casting film 80 with using both of the air duct 82 and the heater 84, it is preferable to start drying as soon as possible just after the formation of the casting film 80. Therefore, in this embodiment, the drying with the air duct 82 and the heater 84 starts at the point at which the content of the remaining content is at least 350 wt. %.
Before the content of the remaining solvent becomes 250 wt. %, the drying air is fed out to the casting film 80 with use of the air duct 82. Thus the drying air with rectification thereof is fed out when the content of the remaining solvent is large. In this case, since the drying of the casting film 80 is made only little, the drying layer is not formed. Therefore, even if the drying air is applied to the casting film 80 in this situation, the generation of the unevenness is reduced. However, the content of the remaining solvent is less than 250 wt %, the drying is made such that the drying layer is formed. If the drying air is applied to the casting film 80 in this situation, the unevenness remains on the film surface. Note that the content of the remaining solvent is that on dry basis and measured with use of the samples of the casting film 80 and the produced film which is completely dried. If the sample weight of the casting film 80 was x and the sample weight after the drying was y, the solvent content on the dry basis (%) was calculated in the formula, {(x−y)/y)×100. Note that in the content of the remaining solvent on dry basis, the weight of the solid obtained by completely drying the dope corresponds to 100%.
In the casting film 80, the first and second outer layers are formed respectively, so as to be a lowermost layer contacting to the belt 73 and an uppermost layer, and the base layer is sandwiched by the first and second outer layers. Note that the casting film 80 having the multi-layer structure as above is formed by performing the co-casting of several sorts of dopes which are independently prepared. When the casting film 80 having the multi-layer structure is formed by the co-casting, the production speed can be made higher and the unevenness of the film surface can be reduced. Therefore, the produced film is excellent in the surface condition. Note that the method of the co-casting will be described later.
Each viscosity of the dopes for forming the outer layers is preferably controlled to at most 35 Pa·s. Thus the outer layers are dried faster than the base layer. Thus effects of the protection of the base layer become larger. Thus the foaming caused by evaporating the solvent in the base layer is reduced. If the viscosity of the dope for forming the outer layers larger than 35 Pa·s, the unevenness often occurs on the surface of the casting film 80 easily, or the casting speed becomes lower to elongate the production time.
In following, an embodiment for forming the film in the film production line 200 will be explained. Note that the present invention is not restricted in this embodiment, in reference with
The base layer dope and the first and second outer layer dopes are fed to a feed block 71 at a predetermined flow volume. The dopes are joined and then cast from the casting die 72 to a belt 73.
The dopes is cast from the casting die 72 onto the belt 73, so as to form the casting film 80 while a bead of the cast dopes is formed between the casting die 72 and the belt 73. At the co-casting, the temperature of the dopes is preferably controlled in the range of −10° C. to 57° C. Note that the thickness of the casting film 80 is controlled to a predetermined value preferably in the range of 10 μm to 400 μm, particularly 20 μm to 150 μm, and especially 25 μm to 100 μm. Thus the drying of the casting film 80 is made in a short time, and the produced film is excellent in the optical properties, such as planarity and the like.
The drying air whose temperature is controlled to a predetermined temperature is fed out through the outlet 82a of the air duct 82 to make the drying of the casting film 80. Further, the drying of the casting film 80 is also made from the rear side of the belt 73 (namely the rear side of the casting film 80) with the heater 80 at a predetermined rear side drying temperature.
When the cast dope has self-supporting property, the casting film 80 is continuously peeled as the film 101 with support of the peeling roller 86. Then the film 101 is transported to the transfer area 90. In the transfer area 90, while the film 101 is transported with the support of the rollers, a drying air is fed from the air blower to dry the film 101, such that the drying may proceed. Preferably, the temperature of the drying air is in the range of 20° C. to 250° C. Note in the transfer area 90 that the rotating speed of the roller may be set to be higher in the downstream side, so as to draw the film 101 in the lengthwise direction.
The film 101 is dried until the content of the remaining solvent become the predetermined value, and fed out from the tenter device 100 toward an edge slitting device 102 for slitting off both side edge portions. The slit side edge portions are sent to a crusher 103 by a cutter blower (not shown), and crushed to tips by the crusher 103. The tips are reused for preparing the dope, which is effective in view of the decrease of the production cost. Note that the slitting process of both side edge portions may be omitted. However, it is preferable to perform the slitting between the casting process and the winding process.
The film 101 whose side edge portions are slit off is sent to the drying device 105 and dried furthermore. In the drying device 105, the film 101 is transported with lapping on the rollers 104. The inner temperature of the drying device 105 is not restricted especially. However, it is preferable in the range of 60° C. to 145° C. The solvent vapor evaporated from the film 101 by the drying device 105 is adsorbed by the adsorbing device 106.
The film 101 is transported into the cooling chamber 107, and cooled therein to around the room temperature. A humidity control chamber (not shown) may be provided for conditioning the humidity between the drying device 105 and the cooling chamber 107. Preferably, in the humidity control chamber, an air whose temperature and humidity are controlled is applied to the film 101. Thus the curling of the film 101 and the winding defect in the winding process can be reduced.
Thereafter, a compulsory neutralization device (or a neutralization bar) 108 eliminates the charged electrostatic potential of the film 101 to the predetermined value (for example, in the range of −3 kV to +3 kV). The position of the neutralization process is not restricted in this embodiment. For example, the position may be a predetermined position in the drying section or in the downstream side from the knurling roller 109, and otherwise, the neutralization may be made at plural positions. After the neutralization, the embossing of both side portions of the film 101 is made by the embossing rollers to provide the knurling. The emboss height from the bottom to the top of the embossment is in the range of 1 μm to 200 μm.
In the last process, the film 101 is wound by the winding shaft 111 in the winding chamber 110. At this moment, a tension is applied at the predetermined value to a press roller 112. Preferably, the tension is gradually changed from the start to the end of the winding. In the present invention, the length of the film 101 is preferably at least 100 m. The width of the film is preferably at least 600 mm, and particularly in the range of 1400 mm to 1800 mm. Further, even if the width is more than 1800 mm, the present invention is effective. When it is designated to produce the film which is 15 μm to 100 μm in thickness, the present invention is also applied.
In the solution casting method of the present invention, there are casting methods for casting plural dopes, for example, a co-casting method and a sequential casting method. In the co-casting method, a feed block may be attached to the casting die as in this embodiment, or a multi-manifold type casting die (not shown) may be used. In the production of the film having multi-layer structure, the plural dopes are cast onto a support to form a casting film having the base layer and the first and second outer layers. Then in the produced film, at least one of the thickness of the first outer layer and that of the second outer layer is preferably in the range of 0.5% to 30% of the total film thickness. Furthermore, when it is designated to perform the co-casting, a dope of higher viscosity is sandwiched by lower-viscosity dopes. Concretely, it is preferable that the dopes for forming the surface layers have lower viscosity than the dope for forming a layer sandwiched by the surface layers. Further, when the co-casting is designated, it is preferable in the bead between a die slit (or die lip) and the support that the composition of alcohol is higher in the two outer dopes than the inner dope.
As shown in
Japanese Patent Laid-Open Publication No. 2005-104148 describes from [0617] to [0889] in detail about the structures of the casting die, the decompression chamber, the support and the like, and further about the co-casting, the peeling, the stretching, the drying conditions in each process, the handling method, the curling, the winding method after the correction of planarity, the solvent recovering method, the film recovering method. The descriptions thereof can be applied to the present invention.
[Properties & Measuring Method]
(Degree of Curl & Thickness)
Japanese Patent Laid-Open Publication No. 2005-104148 describes from [0112] to [0139] about the properties of the wound cellulose acylate film and the measuring method thereof. The properties and the measuring methods can be applied to the present invention.
[Surface Treatment]
The cellulose acylate film is preferably used in several ways after the surface treatment of at least one surface. The preferable surface treatments are vacuum glow discharge, plasma discharge under the atmospheric pressure, UV-light irradiation, corona discharge, flame treatment, acid treatment and alkali treatment. Further it is preferable to make one of these sorts of the surface treatments.
[Functional Layer]
(Antistatic, Curing, Antireflection, Easily Adhesive & Antiglare Layers)
The cellulose acylate film may be provided with an undercoating layer on at least one of the surfaces, and used in the several ways.
It is preferable to use the cellulose acylate film as a base film to which at least one of functional layers may be provided. The preferable functional layers are an antistatic layer, a cured resin layer, an antireflection layer, an easily adhesive layer, an antiglare layer and an optical compensation layer.
Conditions and Methods for forming the functional layer are described in detail from [0890] to [1087] of Japanese Patent Laid-Open Publication No. 2005-104148, which can be applied to the present invention. Thus, the produced film can have several functions and properties.
These functional layers preferably contain at least one sort of surfactants in the range of 0.1 mg/m2 to 1000 mg/m2. Further, the functional layers preferably contain at least one sort of plasticizers in the range of 0.1 mg/m2 to 1000 mg/m2. The functional layers preferably contain at least one sort of matting agents in the range of 0.1 mg/m2 to 1000 mg/m2. The functional layers preferably contain at least one sort of antistatic agents in the range of 1 mg/m2 to 1000 mg/m2.
(Variety of Use)
The produced cellulose acylate film can be effectively used as a protection film for a polarizing filter. In the polarizing filter, the cellulose acylate film is adhered to a polarizer. Usually, two polarizing filters are adhered to a liquid crystal layer such that the liquid crystal display may be produced. Note that the arrangement of the liquid crystal layer and the polarizing filters are not restricted in it, and several arrangements already known are possible. Japanese Patent Laid-Open Publication No. 2005-104148 discloses the liquid crystal displays of TN type, STN type, VA type, OCB type, reflective type, and other types in detail. The description may be applied to the present invention. Further, in this publication No. 2004-264464 describes a cellulose acylate film provided with an optical anisotropic layer and that having antireflection and antiglare functions. Further, the produced film can be used as an optical compensation film since being double axial cellulose acylate film provided with adequate optical properties. Further, the optical compensation film can be used as a protective film for a polarizing filter. The detail description thereof is made from [1088] to [1265] in the publication No. 2005-104148.
In followings, Experiment of the present invention will be explained. However, the present invention is not restricted in it. The explanation will be made in detail according to Example 1. The experimental conditions and results of Examples 2-3 and Comparisons 1-8 will be shown in Table 1.
In followings, the explanation of Examples the present invention will be made. The composition of the dope (or polymer solution) used for the film production will be shown.
In Example 1, the materials of the following contents are used for producing the dope.
According to cellulose triacetate used in this experiment, the remaining content of acetic acid was at most 0.1 mass %, the Ca content was 58 ppm, the Mg content was 42 ppm, the Fe content was 0.5 ppm, the free acetic acid content was 40 ppm, and the sulfuric ion content was 15 ppm. The degree of acetylation at 6th position was 0.91, and the percentage of acetyl groups at 6th position to the total acetyl groups was 32.5%. The acetone extract was 8 mass %, and a ratio of weight-average molecular weight to number-average molecular weight was 2.5. Further, yellow index was 1.7, haze was 0.08, and transparency was 93.5%. Tg (measured by DSC) was 160° C., and calorific value in crystallization was 6.4 J/g. This cellulose triacetate A (hereinafter TAC-A) is synthesized from cellulose as material obtained from cotton.
The polymer solution was prepared with use of the dope production line 30 in
The swelling liquid 37 was fed from the mixing tank 14 to the heating device 15 by the pump 38. The heating device was a pipe provided with a jacket. The swelling liquid 37 was heated to 50° C. by the heating device 15, and then heated to 90° C. under 2 MPa. Thus the dissolution was completely made, and the heating time was 15 minutes. The swelling liquid was fed out as the polymer solution from the heating device 15, and the filtration of the polymer solution was made by the filtration device 17 in which nominal diameter of a filter was 8 μm. In the filtration, the upstream side filtration pressure was 1.5 MPa, and the downstream side filtration pressure was 1.2 MPa. Note that the filter, a filter housing and the pipes that are used at the high temperature was produced from hasteloy so as to be excellent in corrosion resistance, and had jackets in which heat transfer mediums are fed for heating continuously.
The polymer solution was fed into the flushing device 31 whose pressure was kept to the atmospheric pressure at 80° C., such that the flush evaporation of the polymer solution was made. The solvent vapor was condensed by the condenser to the liquid state, and recovered by the recovering device 20. After the flushing, the content of solid compounds in the polymer solution was 21.8 mass %. Note that the recovered solvent was recycled by the recycling device 21 and reused. The anchor blade is provided at a center shaft of a flush tank of the flushing device 31, and the polymer solution was stirred by the anchor blade at 0.5 m/sec as circumferential velocity. The temperature of the polymer solution in the flush tank was 25° C., the retaining period of the polymer solution in the flush tank was 50 minutes. Part of the polymer solution was sampled, and the measurement of the shearing viscosity was made at 25° C. The shearing viscosity was 450 Pa·s at 10 (1/s) of shearing rate.
Then the defoaming was further made by irradiating very weak ultrasonic waves. Thereafter, the polymer solution was fed to the filtration device 19 by the pump 41. In the filtration device 19, the polymer solution was fed at first through a sintered metal filter whose nominal diameter was 10 μm, and then through the same filter of 10 μm nominal diameter. At the forward and latter filters, the upstream side pressures were respectively 1.5 MPa and 1.2 MPa, and the downstream side pressures were respectively 1.0 MPa and 0.8 MPa. The temperature of the polymer solution after the filtration was controlled to 36° C., and the polymer solution stored as the polymer solution 39 in the stainless stock tank 22 whose volume was 2000 L. The anchor blade is provided to a center shaft of the stock tank 22, and the polymer solution 39 was always stirred by the anchor blade at 0.3 m/sec as circumferential velocity. Note that when the concentrating of the polymer solution is made, corrosions of parts or portions contacting to the polymer solution in the devices and devices didn't occur at all. Further, a mixture solvent MS of dichloromethane 86.5 pts.mass, acetone 13 pts.mass and n-butanol 0.5 pts.mass was prepared.
The film was formed in a film production line 200 shown in
The casting die 72 has the feed block 71 which is 1.8 m in width and adequate for the co-casting, such that not only the base layer dope but also the first and second outer layer dopes on both surfaces of the main dope can be cast simultaneously. Thus the produced film has three-layer structure. The polymer solution 39 was fed through the paths 44-46.
The additive 51 for the base layer was prepared by mixing UV agent A (2(2′-hydroxy-3′,5′-di-tert-butylphenyl)benzo-triazol; 0.7 pts.mass), UV agent B (2(2′-hydroxy-3′,5′-di-tert-amylphenyl)-5-chlorobenzotriazol; 0.3 pts.mass), retardation controller (N,N′-di(m-tolyl)-N″-p-methoxyphenyl-1,3,5-triazine-2,4,6-triamine; 4 pts.mass), the mixture solvent MS and the polymer solution 39. The prepared additive 51 was contained in the stock tank 22. Then the additive 51 was fed from the stock tank 22 to the path 44 by the pump 52, and thus added to the polymer solution 39. Thereafter, the mixing was made by the static mixer 53, such that the base layer dope was obtained. The content control was made such that the total solid content might be 21.8 mass %, the content of UV absorbing agents A & B in the produced film might be 1 mass %, and the retardation controller content in the film might be 4 mass %.
Silicone dioxide 0.05 pts.mass (particle diameter, 15 nm; Mohs Hardness, about 7) as matting agent, citric acid ethylester 0.006 pts.mass (citric acid, citric acid monoester, citric acid diester, citric acid triester) as peeling agent and the polymer solution 39 were dissolved to or dispersed in the and the mixture solvent. Thus the additive 56 for the first outer layer was obtained in liquid state. The additive 56 was stored in the stock tank 55, and fed out by the pump 57 at the predetermined flow volume to the polymer solution 39 which is flowing in the path 45. Then the additive 56 and the polymer solution 39 was mixed by the static mixer 58 such that the first outer layer dope was obtained. The content control was made such that the total solid content might be 20.5 mass %, the matting agent content might be 0.05 mass %, and the peeling accelerator content might be 0.03 mass %.
Silicone dioxide 0.1 pts.mass as matting agent was dispersed in the mixture solvent, such that the additive 61 for the second outer layer was obtained in the liquid state. The additive 61 was stored in the stock tank 60, and fed out by the pump 62 to the polymer solution 39 which is flowing in the third path 66. Then the mixture of the additive 56 and the polymer solution 39 is mixed by the static mixer 63 such that the dope for forming the second outer layer was obtained. The content control was made such that the total solid content might be 20.5 mass %, and the matting agent content might be 0.1 mass %.
The thickness of each of the base layer and the first and second outer layers in the TAC film was respectively 4 μm, 73 μm, and 3 μm, and the film thickness was 80 μm. The casting width was 1700 mm, and the flow rate of each cellulose triacetate dope at die lips was adjusted during the casting. The casting die 72 was provided with a jacket in which heat transfer medium was supplied. The casting die 72 was provided with a jacket (not shown) in which a heat transfer medium was supplied. The temperature of the heat transfer medium at an entrance of the jacket was 36° C., such that the temperature of the dope might be 36° C.
The casting die 72 was the coat hunger type, in which heat bolts for adjusting the film thickness were disposed at the pitch of 20 mm. Thus the film thickness (or the thickness of the dopes) are automatically controlled by the heat bolt. A profile of the heat volt can be set corresponding to the flow rate of the high accuracy gear pump, on the basis of the preset program. Thus the feed back control can be made by the control program on the basis of the profile of an infrared ray thickness meter (not shown) disposed in the film production line 200. The control was made such that, with exception of both side edge portions (20 mm each in the widthwise direction of the produced film), the difference of the film thickness between two positions which were 50 mm far from each other might be at most 1 μm, and the largest difference between the minimal values of the film thickness in the widthwise direction might be at most 3 μm/m. Further, the control was made such that the averaged thickness accuracy of each of the first and second outer layers might be ±2%, that of the base layer might be at most 1%, and the average film thickness might be at most ±1.5%.
In the upstream side of the casting die 72, the decompression chamber 81 was provided for decompressing the pressure in the upstream side from the casting die 72. Further, there were labyrinth packings (not shown) in the upstream and downstream sides of the beads. Further, an opening was provided in both edges. Further, an edge suctioning device (not shown) for reducing the disturbance of the bead was provided.
The material of the casting die was the double layer stainless alloy, whose coefficient of thermal expansion was at most 2×10−5 (° C.−1). In the compulsory corrosion experiment in an electrolyte solution, the corrosion resistance was almost the same as that of SUS316. Further, the material to be used for the casting die had enough corrosion resistance, such that the pitting (or pitting corrosion) might not occur on the gas-liquid interface even if this material were dipped in a mixture liquid of dichloromethane, methanol and water for three months. The finish accuracy of the contact surface of each casting die 72 and feed block 71 was at most 1 μm in surface roughness, the straightness was at most 1 μm in any directions, and the slit clearance was adjusted to 1.5 mm in straightness. According to an edge of the contact portion of a lip end of the casting die 72, R is at most 50 μm in all of a width. Further, the shearing rate in the casting die is controlled in the range of one to 5000 per second. Further, the WC coating was made on the lip end from the casting die 72 by a melt extrusion method, so as to provide the hardened layer.
In order to prevent the dry and solidification on part of the slit end of the casting die 72, the mixture solvent dissolvable of the solidified dope was supplied to each edge portion of the gas-liquid interface of the slit at 0.5 ml/min. Thus the mixture solvent is supplied to each bead edge. The pulse rate of a pump for supplying the mixture solvent was at most 5%. Further, the decompression chamber 81 was provided for decreasing the pressure in the rear side by 150 Pa. In order to control the temperature of the decompression chamber 81, a jacket (not shown) was provided, and a heat transfer medium whose temperature was controlled at 35° C. was supplied into the jacket. The edge suction rate could be controlled in the range of 1 L/min to 100 L/min, and was adequately controlled in this experiment so as to be in the range of 30 L/min to 40 L/min.
The belt 73 was an endless stainless belt which was 2.1 m in width and 70 m in length. The thickness of the belt 73 was 1.5 mm, and the surface of the belt 73 was polished, such that the surface roughness might be at most 0.05 μm. The material was SUS316, which had enough corrosion resistance and strength. The thickness nonuniformity of the entire belt 73 was at most 0.5% of the predetermined value. The belt 73 was moved by rotating the back-up rollers 74a, 74b. At this moment, the tension of the belt 73 was controlled to 1.5×104 kg/m. Further, the relative speed to each roller to the belt 73 changed. However, in this experiment, the control was made such that the difference of the relative speed between the back-up rollers 74a, 74b was at most 0.01 m/min. Further the control was made such that the variation of the speed of the belt 73 was at most 0.5% to the predetermined value. The position of the belt in the widthwise direction was controlled with detection of the position of the side end, such that meandering in one circle of the moving belt 73 was reduced in 1.5 mm. Further, below the casting die 72, the variation of the position in the vertical direction between the lip end of the casting die and the belt 73 was in 200 μm. The three dopes (for forming the base layer and the first and second outer layers) were cast onto the belt 73 from the casting die 72.
In this experiment, the back-up rollers 74a, 74b were supplied therein with a heat transfer medium, such that the temperature of the belt 73 might be controlled. The back-up roller 74a disposed in a side of the casting die 72 was supplied with the heat transfer medium at 5° C., and the back-up roller 74b was supplied with the heat transfer medium at 40° C. The surface temperature of the middle portion of the belt 73 at a position just before the casting was 15° C., and the temperature difference between both sides of the belt was at most 6° C. Note that a number of pinhole (diameter, at most 30 μm) was zero, a number of pinhole (diameter, at least 10 μm and less than 30 μm) was at most one in square meter, and a number of pinhole (diameter, less than 10 μm) was at most two in square meter.
The temperature of the casting chamber 70 controlled to 35° C. by the temperature controlling device 77. The air duct 82 was positioned just after the casting dope was cast from the casting die 72, and the outlet 82a of the air duct 82 was directed in the running direction of the belt 73, such that the drying air may be fed out toward the surface side from the belt 73. Further the heater 84 was disposed in the rear side (downwards) of the belt 73.
The drying air was fed out almost in parallel to the belt 73 from the outlet 82a such that the casting side drying temperature might be 120° C. Further, the heater 84 heats the rear side of the casting film 80 such that the rear side drying temperature might be 50° C.
The overall heat transfer coefficient from the drying air to the belt 73 was 24 kcal/(m2·hr·° C.). The oxygen concentration in the drying atmosphere on the belt 73 was kept at 5 vol. %. In order to keep the oxygen concentration at 5 vol. %, the air was substituted by the nitrogen gas. Further, in order to condense and recover the solvent in the casting chamber 70, the condenser 78 was provided, and the temperature of the exit was set to −10° C.
When the solvent ratio in the casting film became 150 mass % of dry weight standard, the casting film 80 was peeled as the film 101 from the belt 73 with support of the peeling roller 86. At the peeling, the peeling tension was 10 kgf/m. Further, in order to reduce the peeling defect, the peeling speed was adequately controlled such that the percentage thereof to the speed of the belt 73 might be in the range of 100.1% to 110%. The surface temperature of the film 101 was 15° C.
According to the drying speed, 60 mass % of the solvent in dry weight standard was evaporated per minute in average. The solvent vapor generated in the drying was condensed at −10° C. by the condenser 78, and recovered by the recovering device 79. The recovered solvent was reused after the conditioning thereof. At this moment, the water content in the solvent was at most 0.5%. The air from which the solvent was removed was heated again and reused as the drying air. The film 101 was transported toward the tenter device 100 by the rollers in the transfer area 90. At this moment, the air blower 91 fed the drying air at 40° C. to the film 101.
In the tenter device 100, both side edge portions of the film 101 was held by clips, and then transported in a drying zone for performing the drying. The clip was supplied with a heat transfer medium at 20° C. The drive of the tenter device 100 was made with use of chain, and the speed variation of sprockets of the chain was at most 0.5%. Further, the inside of the tenter device 100 was partitioned into three zones, in which the temperatures of the drying airs were 90° C., 100° C. and 110° C. sequentially from the upstream side. The drying air had composition so as to be saturated at −10° C. According to the drying speed in the tenter device 100, the 120 mass % of the solvent of dry weight standard was evaporated per minute in average. The conditions of the drying zones were adjusted such that the remaining content of the solvent in the film might be 7 mass % at an exit of the tenter device 100.
Further, in the tenter device 100, the stretching in the widthwise direction was made as the transportation was made. If the percentage of the film width of the film 101 before the tenter device 100 was determined to 100%, the stretching ratio of the film width after the tenter device 100 was 103%. Further, the film was drawn in the lengthwise direction between the peeling roller 86 and the tenter device 100. The drawing ratio in percentage was 102%. According to the stretching ration in the tenter device 100, the difference of the actual stretching ratio was at most 10% between parts which were at least 10 mm apart from the holding positions of the clips, and at most 5% between parts which were 20 mm apart from the holding portions. In the side edge portions in the tenter device 100, the ratio of the length in which the fixation was made was 90%. The solvent vapor generated in the tenter device 100 was condensed at −10° C. to a liquid state and recovered. For the condensation, a condenser (not shown) was provided, and a temperature at an exit thereof was −8° C. The water content in the recovered solvent was regulated to at most 0.5 mass %, and then the recovered solvent was reused. The film 101 was fed out as the film 101 from the tenter device 100.
In 30 seconds from exit of the tenter device 100, both side edge portions were slit off in the edge slitting device 102. In this experiment, each side portion of 50 mm in the widthwise direction of the film 101 was determined as the side edge portion, which were slit off by an NT type slitter of the edge slitting device 102. The slit side edge portions were sent to the crusher 103 by applying air blow from a blower (not shown), and crushed to tips about 80 mm2. The tips were stored into edge silos for reusing as raw material with the TAC flakes for the dope production. The oxygen concentration in the drying atmosphere in the tenter device 100 was kept to 5 vol. %. Note that the air was substituted by nitrogen gas in order to keep the oxygen concentration at 5 vol. %. Before the drying at the high temperature in the drying chamber 105, the pre-heating of the film 101 was made in a pre-heating chamber (not shown) in which the air blow at 100° C. was supplied.
The film 101 was dried at high temperature in the drying chamber 105, which was partitioned into four partitions. Air blows whose temperatures were 120° C., 130° C., 130° C. and 130° C. from the upstream side were fed from air blowers (not shown) to the partitions. The transporting tension of each roller 104 to the film 101 was 100 N/width. The drying was made for ten minutes such that the content of the remaining solvent might be 0.3 mass %. The lapping angle of some of the rollers 104 was 900 and that of the others was 180°. The rollers 104 were made of aluminum or carbon steel. On the surface, the hard chrome coating was made. The surfaces of the rollers 104 were flat or processed by blast of matting process. The swing of the roller in the rotation was in 50 μm. Further, the bending of each roller 104 at the tension of 100 N/width was reduced to at most 0.5 mm.
The solvent vapor contained in the drying air is removed with use of the adsorbing device 106 in which an adsorbing agent was used. The adsorbing agent was active carbon, and the desorption was performed with use of dried nitrogen. The recovered solvent was reuse as the solvent for the dope preparation after the water content might be at most 0.3 mass %. The drying air contains not only the solvent vapor but also gasses of the plasticizer, UV-absorbing agent, and materials of high boiling points. Therefore, a cooler for removing by cooling and a preadsorber were used to remove them. Thus the drying air was reused. The ad- and desorption condition was set such that a content of VOC (volatile organic compound) in exhaust gas might be at most 10 ppm. Furthermore, in the entire solvent vapor, the solvent content to be recovered by condensation method was 90 mass %, and almost of the remaining solvent vapor was recovered by the adsorption recovering.
The dried film 101 was transported into a first humidity control chamber (not shown). Between the drying chamber 105 and the first humidity control chamber, there was the transfer area 90 into which a drying air at 110° C. was fed. In the first humidity control chamber, an air whose temperature and dewing point were respectively 50° C. and 20° C. was fed. Further, the film 101 was transported into a second humidity control chamber (not shown) for preventing the curling of the film 101. In the second humidity control chamber, an air whose temperature and humidity were respectively 90° C. and 70% was directly applied.
After the humidity control, the film 101 was cooled in the cooling chamber 107 such that the temperature of the film might be at most 30° C. Then the edge slitting of both film edge portions were made. Further, the compulsory neutralization device (or a neutralization bar) 108 eliminated the charged electrostatic potential of the film 101 in the range of −3 kV to +3 kV. After the neutralization, the embossing of both side portions of the film 101 was made by the knurling rollers 109 to provide the knurling. The knurling width was 10 mm, and the knurling pressure was determined such that the maximal emboss height might be 12 μm in average larger than the averaged thickness.
The film 101 was transported to the winding chamber 110, whose inside temperature and humidity were respectively kept to 28° C. and 70%. Further, a compulsory neutralization device (not shown) was provided, such that the charged electrostatic potential of the film might be in the range of −1.5 kV to +1.5 kV. The obtained film 101 was 1475 mm in width. The diameter of the winding shaft 111 was 169 mm. The tension pattern was set such that the winding tension was 360 N/width at first, and 250 N/width at last. The film 101 was entirely 3940 m in length. The winding cycle was 400 m, and the oscillation width was in ±5 mm. Further, the pressure of the press roller 112 to the winding shaft 111 was set to 50 N/width. The temperature of the film at the winding was 25° C., the water content was 1.4 mass %, and the content of the remaining solvent was 0.3 mass %. Through all processes, the film production speed was 40 m/min.
The film 101 was produced from the same dope by the same method as Example 1. However, when the casting film 80 was dried, the casting side drying temperature was 120° C. in drying by the air duct 82, and the rear side drying temperature was 50° C. in drying by the heater 84. Further, the viscosity of the second outer layer as uppermost layer of the casting film 80 was 25 Pa·s.
The film 101 was produced from the same dope by the same method as Example 1. However, when the casting film 80 was dried, the casting side drying temperature was 120° C. in drying by the air duct 82, and the rear side drying temperature was 50° C. in drying by the heater 84. Further, the viscosity of the second outer layer as uppermost layer of the casting film 80 was 40 Pa·s.
(Comparison 1)
In Comparison 1, the polymer solution 39 was produced by mixing the following materials in the dope production line 10 of
The materials of the following contents are used for producing the dope.
(Comparison 2)
In Comparison 2, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, the casting speed was 40 m/min in all processes. Other conditions were the same as Comparison 1.
(Comparison 3)
In Comparison 3, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, the heater 84 was not used but only the air duct 82 of Example 1 was used. The drying air was fed out from the outlet while the casting side drying temperature was 160° C. The casting speed was 40 m/min in all processes.
(Comparison 4)
In Comparison 4, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, the heater 84 was not used but only the air duct 82 of Example 1 was used. The drying air was fed out from the outlet while the casting side drying temperature was 140° C. The casting speed was 40 m/min in all processes.
(Comparison 5)
In Comparison 5, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, the heater 84 was not used but only the air duct 82 of Example 1 was used. The drying air was fed out from the outlet while the casting side drying temperature was 120° C. The casting speed was 40 m/min in all processes.
(Comparison 6)
In Comparison 6, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, both of the heater 84 and the air duct 82 were used as Example 1. The drying air was fed out from the outlet while the casting side drying temperature was 120° C. and the rear side drying temperature was 30° C. The casting speed was 40 m/min in all processes.
(Comparison 7)
In Comparison 7, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, both of the heater 84 and the air duct 82 were used as Example 1. The drying air was fed out from the outlet while the casting side drying temperature was 120° C. and the ear side drying temperature was 50° C. The casting speed was 40 m/min in all processes.
(Comparison 8)
In Comparison 8, the polymer solution 39 was produced by the same method as Comparison 1. However, in the production of the film 101, both of the heater 84 and the air duct 82 were used as Example 1. The drying air was fed out from the outlet while the casting side drying temperature was 120° C. and the ear side drying temperature was 80° C. The casting speed was 40 m/min in all processes.
(Estimation of Film)
The estimation of the film 101 was made in three points, namely planarity, peelability, and foaming.
(Planarity)
The surface of the film 101 was observed with eyes, and the estimation of planarity was made depending on how much unevenness was observed. If little unevenness observed, the estimation was A. If unevenness was observed not so much, the estimation was B. If unevenness was observed much, the estimation was N.
(Peelability)
How much part of the casting film 80 remains on the belt 73 after the peeling was observed with eyes for estimation of peelability. If there were no remaining part of the casting film 80, the estimation was A. If there were some remaining parts, the estimation was B. If the remaining parts are so much, the estimation was N.
(Foaming)
The surface of the film 101 was observed with eyes, and the estimation of foaming was made. If the foaming didn't occur, the estimation was A. If the foaming occurred little, the estimation was B. If the foaming occurred so much, the estimation was N.
The results of the above estimations about planarity, peelability and foaming, and the production conditions will be shown in Table 1.
As Table 1 teaches, the results of the estimations of the films 101 in Examples 1-3 were excellent in the planarity, peelability and reduction of foaming. Therefore, if the film 101 is produced by drying from both casting and rear sides of the casting film 80 in the co-casting method, the produced film is excellent in planarity.
However, in Example 3, unevenness was observed a little more on the surface of the film 101 than Examples 1&2. In comparison among Examples 1-3, the drying conditions of the air duct and the heater are the same, but the viscosities of the outer layer dope were different. Thus if the viscosity of the outer layer dope is at most 35 Pa·s, the produced film is excellent in planarity.
In Comparisons 1&2, the air duct has the slit-type outlet confronting to the belt 73, through which the drying air was fed out to dry the casting film 80. As the result, if the production speed was increased, the planarity and the peelability of the film became lower. The considerable reason therefor was the drying of the casting film 80 was not made enough since the drying air which is almost perpendicularly fed out from the slit-type outlet cannot supply enough heat quantity for the casting film 80 in the transportation at higher production speed. Consequently it is hard to increase the production speed, because of lack of calories supplied for the casting film 80 from the drying air fed out from the slit-type outlet.
In Comparisons 3-5, the heater 84 was not used, and only the air duct 82 was used with variation of the casting side drying temperature so as to dry the casting film 80. As the result, if the casting side drying temperature is high, the foaming occurs. The considerable reason therefor was that the evaporation of the solvent was made rapidly, and therefore, it is difficult to reduce the foaming. If the casting side drying temperature is low, the peelability becomes worse. The considerable reason therefor was that the drying was not made enough and therefore the peelability becomes worse. Consequently, it is difficult to make the drying and the reduction of foaming, only in the surface drying by the drying air.
In Comparisons 6-8, both of the air duct 82 and the heater 84 were used with variation of the rear side drying temperature so as to dry the casting film 80. As the result, if the rear side drying temperature is high, the foaming occurs. The considerable reason therefor was that the evaporation of the solvent was made rapidly, and therefore, it is difficult to reduce the foaming. If the rear side drying temperature is low, the peelability becomes worse. The considerable reason therefor was that the drying was not made enough and therefore the peelability becomes worse. Consequently, it is difficult to make the drying and the reduction of foaming, only in the surface drying by the drying air.
As described above, in order to produce the film excellent in planarity, peelability and reduction of foaming, the drying can be effectively made if the drying air having a predetermined temperature is fed out in parallel to the casting film over the film surface and the casting film is heated to a predetermined temperature of the rear side of the casting film by the heater. In this case, the present invention becomes more effective when it is designated to make the co-casting to form the casting film having multi-layer structure in which there are a base layer and at least one of outer layer. Further, as the drying conditions, the casting side drying temperature is in the range of 70° C. to 130° C., and the rear side drying temperature is in the range of 40° C. to 80° C. Furthermore, the present invention becomes extremely effective when the viscosity of the outer layer dope is at most 35 Pa·s.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2006/306395 | 3/22/2006 | WO | 00 | 11/15/2007 |