Polymer stabilizers

In the one aspect, this invention relates to novel polymer stabilizers for use in an acidic environment. In another aspect, the invention relates to the composition of a stabilized hydrophilic or water-swellable polymer such as vinyl polymers, copolymers, interpolymers in an acid medium, which may or may not be cross-linked, to guarantee the acidic mucilages of said polymers against viscosity decrease and graining.
Acid solutions have long been employed in a variety of applications including acid pickling, etching, oil well rock fracturing, scale and stain removal solutions, paint strippers, metal preconditioners for painting and rust removal, etc. However, the acid solutions generally require the addition of thickeners to improve their application and sustain their effect on the applied substrate. Polymers have been recommended to provide the increased viscosity desired; however, many excellent polymer thickeners are disqualified for this application because of instability by attack of the acid on their molecular structures or by oxidative or photochemical degradation. When polymer degradation occurs, the polymeric thickener is not retained in solution and the viscosity rapidly declines.
Although polyvinyl pyrrolidone is stable to acid attack, some loss of effectiveness on storage of the acidic solutions is caused by oxidative and/or photochemical degradation. Additionally, aqueous gels of polyvinyl pyrrolidone tend to become grainy on aging so that non-uniform applications of the acid medium result. Most other polymer thickeners are unstable in strong acid solution and rapidly loose thickening effectiveness over a period of several weeks to several months in storage, so that although these polymers form excellent mucilages, gels, emulsifying and suspending agents when freshly prepared, they have the disadvantage of requiring immediate use.
Accordingly it is an object of the present invention to provide stabilizers for the polymeric thickeners which extend their stability for several years.
It is another object of this invention to provide economical stabilizers for combination with the polymer thickeners, which in themselves contribute to the increase in viscosity of the acid solutions.
Another object is to provide a novel composition comprising an aqueous solution having a pH less than 7 and containing acid, polymeric thickener and stabilizer.
Still another object is to provide a stabilized vinyl polymer for use in any acidic environment.
These and other objects will become apparent from the following description and disclosure.
The above objects are accomplished by preparing an acidic solution containing between about 0.5 and about 25 weight % of a polymer thickener and an effective quantity of the stabilizing ingredient, generally in the range of from about 0.005 to about 1 weight %, preferably from about 0.05 to about 0.75 weight %, based on the dry polymer by stirring the composition until a uniform mixture is achieved. The stabilizer, which is a redox indicator having from 6 to 30 carbon atoms, can be added to the mixture of polymer in the acid medium or the stabilizing agent, in the above amount, can be added directly to the dry polymer before introduction of the acidic liquid. The incorporation of ingredients is generally carried out at a temperature above the freezing point of the liquid up to about 100.degree. C. for a period of from about 1 to about 60 hours or until a homogeneous mixture is achieved, under atmospheric pressure. The formulating conditions preferably employed include mixing at ambient temperature and pressure for a period of from about 4 to 50 hours.
The vinyl polymers of the present invention, which may be employed as thickeners in acid media, are water soluble or water swellable polymers and include poly-N-vinyl-2-pyrrolidone; vinyl alkyl ether/maleic anhydride copolymers; vinyl-2-pyrrolidone/vinyl alkyl ether copolymers wherein the alkyl moiety contains from 1 to 3 carbon atoms, the lower alkyl esters of said vinyl ether/maleic anhydride copolymers, and the cross-linked polymers and interpolymers of the above.
Preferably the polymers of the present invention are of relatively high molecular weight. The preferred polymers are homopolymers of N-vinyl-2-pyrrolidone, e.g. K 90 and K 112; and methyl vinyl ether/maleic anhydride copolymer.
Also certain water-soluble or water-swellable co- or ter-polymers and their esters, salts and amides are desirable viscosity stabilizers for the mucilages of the present invention. These polymers may be of the block, alternating or statistical type. The terpolymers may incorporate monomers having a higher molecular weight, e.g., higher alkyl vinyl ethers such as octadecyl vinyl ether, butyl vinyl ether and octyl vinyl ether monomers, provided that the amount incorporated does not destroy the water-solubility or water-swellability of the final polymer. Interpolymers of this group include dicarboxylic acid anhydride and vinyl ether monomers optionally containing a cross-linking agent. Specifically indicated are the dicarboxylic acid anhydrides having the general structure: ##STR1## wherein R and R' are selected from the group consisting of hydrogen, halogen, cyano, alkyl, aryl, alkaryl, aralkyl and cycloaliphatic groups. Illustrative anhydrides include maleic anhydride, chloromaleic anhydride, 2,3-dichloromaleic anhydride, 2,3-dicyano maleic anhydride, 2,3-dimethyl maleic anhydride, 2,3-diphenyl maleic anhydride, 2,3-dibenzyl maleic anhydride, 2,3-di(p-methylphenyl)maleic anhydride, 2,3-dicyclohexyl maleic anhydride, 2-methyl maleic anhydride, 2-ethyl maleic anhydride, 2-cyano maleic anhydride, 2-propyl maleic anhydride, 2-phenyl-, 2-benzyl-, 2(p-methylphenyl-) and 2-cyclohexyl-maleic anhydrides. Maleic anhydride is preferred because of its ready availability and comparatively low cost. The poly-basic acid moieties of the polymers of this invention are those which result from the hydrolysis of the anhydride linkage of the above anhydrides.
The vinyl ether monomers include vinyl methyl ether, vinyl ethyl ether, vinyl propyl ether, vinyl isopropyl ether, vinyl butyl ethers, vinyl hexyl ethers, vinyl 2-ethylhexyl ethers and vinyl octyl ethers. The ethers in which the alkyl group has from 1 to 4 carbon atoms are preferred. Among the most preferred class of vinyl ethers are methyl vinyl ether, ethyl vinyl ether, propyl vinyl ethers, and the butyl vinyl ethers.
The third monomeric material, which is optional, is a cross-linking agent which contains a plurality of polymerizable CH.sub.2 .dbd.C< groupings and which is copolymerizable with the alpha-beta unsaturated acid anhydride and the vinyl alkyl ether monomers to form cross-linked water-swellable terpolymers. Illustrative cross-linking agents include the polyunsaturated hydrocarbons such as divinyl benzene, divinyl naphthalene, divinyl cyclohexane, low molecular weight polymerized dienes such as polybutadiene and other conjugated diene polymers having substantial unsaturation remaining in the molecule; unsaturated sulfones such as hexaallyl trimethylene trisulfone; unsaturated amides such as trimethylacrylyl triazine; di- and polyunsaturated esters such as ethylene glycol diacrylate, allyl acrylate, allyl cinnamate, diallyl maleate, diallyl phthalate, diallyl malonate, etc.; polyunsaturated acids such as beta-styryl acrylic acid, etc.; polyunsaturated anhydrides such as acrylic anhydride, methacrylic anhydride, etc.; polyunsaturated ethers such as divinyl ether, diallyl ether, diallyl ethylene glycol ether, 1,4,5,8-naphthalene tetrol ethers, the vinyl, allyl, methallyl and crotyl polyethers containing 2 to 7 or more alkenyl ether groups per molecule; polyunsaturated ketones such as divinyl ketone and diallyl ketone; and polyunsaturated compounds containing one or more functional groups such as the half ethers, allyl-beta-allyoxy propionate and allyl methacrylyl sucrose, the half ester monoallyl maleate, the partial ethers of polyhydric alcohols such as diallyl glycerol ether, polyallyl sucrose, polyallyl glycose and other polyallyl derivatives of carbohydrates and polyalcohols, including polyallyl sorbitol, polyallyl mannitol and other polyallyl ethers of sugar-derived alcohols. The carbohydrate polyallyl ethers usually contain 3 or more allyl groups in each molecule.
The preferred class of cross-linking agents are the polyunsaturated hydrocarbons, solvent soluble polymeric open-chain aliphatic conjugated dienes, and the polyalkenyl polyethers of polyalcohols containing at least 4 carbon atoms and at least 3 hydroxyl groups. All of these preferred cross-linking agents must contain a plurality of polymerizable CH.sub.2 .dbd.C< groups, the double bond of which are not in conjugated relationship one with the other. Specific examples of the latter include polyallyl glucose, polyallyl sucrose, polyallyl levulose, polyallyl erythritol, polyallyl pentaerythritol, polyallyl sorbitol, polyallyl mannitol and the polyallyl disaccharides. The amount of cross-linking agent can vary from about 0.1% to about 10% of the combined weight of the remaining monomers.
Maleic acid anhydride and its substituted derivatives tend to form alternating copolymers with most other monomers with which they are copolymerizable. Therefore, substantially molar equivalents of the anhydrides and alkyl vinyl ethers should be used in preparing the cross-linked polymer. If desired, however, up to about 20% of the total monomeric mixture can consist of other monoolefinic monomers such as styrene, acrylonitrile, vinyl chloride, vinylidene chloride, vinyl acetate, vinyl benzoate, diethyl maleate, ethylene, isobutylene or acrylic acid. In preparing cross-linked polymers, it is preferred to use only the essential monomeric materials described heretofore, namely, a maleic anhydride, a vinyl alkyl ether and a cross-linking agent.
Both the cross-linked and non-cross-linked polymers can be converted to partial esters, partial amides or salts by reaction with a primary or secondary alcohol, ammonia or a primary or secondary amine or an inorganic metallic alkaline material. Representative alcohols are preferably aliphatic types having from 1 to about 18 carbon atoms. The amines may be either aliphatic or aromatic and must have at least one replaceable hydrogen on the amine nitrogen. The number of carbon atoms in the amine can vary from 1 to 18. The preferred salt forming groups are those of the alkali metals.
All of the above polymers are well known and most have been added as thickeners to acid solutions for viscosity improvement therein. The viscosity range of these polymers varies widely depending upon the ultimate use of the acid solution. For example, in general the polymer viscosity K-value varies from about 10 to 250 K, more desirably from about 15 to about 150 K.
Other polymers which can be employed in the operation of the present invention include: polyethylene oxide, polypropylene oxide, polyacrylic acid, polymethacrylic acid, sulfated polyvinyl alcohol, polystyrene sulfonate, hydrolyzed polyacrylonitrile, polyacrylamide, copolymers of maleic anhydride with styrene, isobutylene, or ethylene, copolymers of acrylic acid with N-vinylpyrrolidone and methylvinylpyridine, vinylacetate/maleic anhydride copolymers, poly(vinyl alcohol), polymers of caprolactams, e.g. poly(N-vinylcaprolactam) and their copolymers and interpolymers which comprise nylon. The polymer can be in the form of a dry powder or liquid, depending upon its natural physical state.
The acids suitably employed to provide the acidic solutions of the present invention include mineral acids, such as hydrogen halides, phosphoric acid, nitric acid, perchloric acid, chromic acid, hypochloric acid, and sulfuric acid. Of this group, the chlorine containing acids are preferred and hydrogen chloride is most preferred. Polybasic carboxylic acids, such as oxalic, tartaric, citric, adipic, fumaric, maleic and succinic acids can also be used to provide the acid media.
It should be understood that, in the present invention, the composition of the polymer and stabilizer in the absence of an acidic solution, also provides valuable compositions which may be subsequently employed in an acidic environment. Thus, the compositions of the present invention need not include the acidic solution and the stabilizer can be combined with the polymer in a dry or liquid state or both components can be mixed in an inert carrier having a pH below about 7.5. Also certain polymers e.g. methyl vinyl ether/maleic anhydride provide a hydrolyzed, acid moiety which imparts an acid character to aqueous solutions. In these cases, the separate addition of an acid is unnecessary.
The stabilizers of the present invention comprise a group of redox indicators having from 6 to 30 carbon atoms and containing a nitrogen radical selected from the group consisting of amino, azo and cyano; preferably having from 10 to 26 carbon atoms. These compounds retard oxidation of the polymers in an acid environment and stabilize their structures so as to minimize viscosity loss or, in some cases, increase the viscosity of an acid solution. Compounds representative of this group include methylene blue, pyronine, phenosafranine, malachite green oxalate, the sodium salt of diphenylamine sulfonate, amaranth, tartrazine, methyl orange, methyl green, methyl red, neutral red; gallocyanine; o-tolidine; xylene cyanole; dimethylglyoxine; tionine; N-phenyl-1,2,4-benzenetriamine; N,N-dimethyl-p-phenylenediamine; diphenylamine; N,N-diphenylbenzidine; 3,3-dimethoxybenzidine and the dihydrochloride salt thereof; barium or sodium diphenylamine sulfonate; 1,10-phenanthroline optionally substituted with from 1 to 4 methyl or phenyl groups and the corresponding nitro, iron, sulfate, monochloride or perchlorate derivatives thereof; N-phenanthranilic acid; 4,7-diphenyl-1,10-phenanthroline disulfonic acid disodium salt; bipyridine and its monohydrochloride, ruthenium chloride or iron perchlorate derivatives; terpyridine; picoline and its iron perchlorate derivative; methyl red hydrochloride; the sodium salt of 2,6-dichloroindophenol; 4,4-bis(sulfophenyl)amino]-2,2-biphenyldisulfonic acid tetrasodium salt; and diphenylamine. Of this group, the methylene blue; methyl-red, orange and green; pyronine Y; basic blue; neutral red; phenosafranine; malachite green oxalate; amaranth, tartrazine and sodium diphenylamine sulfonate indicators are most preferred.
The precise amount of stabilizer employed may vary somewhat depending on the conditions under which the polymer containing solution or mucilage is prepared. For example, when a relatively strong acid solution is employed, it is recommended that an amount above 0.05 weight % of the stabilizer based on the polymer be used in the formulation. In weaker acid solutions, containing larger amounts of polymer, as little as 0.005 weight % of the stabilizer can be used effectively.
Many of the present stabilizers impart a color to the acid solution, which does not vary in shade or in hue as long as no polymer degradation occurs. Consequently, these stabilizers provide an additional advantage as visual stabilization indicators for the acidic compositions. This function is particularly useful when the acid solutions are to be stored over an extended period of time and for setting use dates on stored inventories.
Having generally described the invention, reference is now had to the accompanying examples which illustrate preferred embodiments but which are not to be construed as limiting to the scope of the present invention which is more broadly defined in the foregoing disclosure and in the accompanying claims. In the following examples, all amounts are by weight unless otherwise indicated.

EXAMPLES 1 THROUGH 32
Stabilizers for Hydrolyzed Gantrez AN Polymer
The polymer Gantrez AN-119 is a copolymer of methyl vinyl ether and maleic anhydride 50/50 (K approximately 18-43). Gantrez AN-169 is a similar copolymer but of higher viscosity (K approximately 84-92). Both are supplied by GAF Corporation.
In each of the following examples, a total of 100 grams of materials including water, dry polymer solids and stabilizer (previously made up as a 1% aqueous solution) were charged to a 4 ounce widemouth bottle and rotated (3.5 RPM) for 48 hours at ambient temperature, during which time the anhydride portion of the polymer was hydrolyzed and thoroughly mixed with the stabilizer. The pH of the hydrolyzed materials ranged from 0.1 to 1.9. Brookfield viscosities (RVT) were determined directly in the bottle.
Gantrez polymer grades AN-119 and 169 were tested at polymer concentrations of 5, 10 or 20%. It was noted that without benefit of added stabilizers, the percent decrease in viscosity is greater for the higher molecular weight polymer (169). Solutions of Gantrez AN-169, after storage for 130 days were found to retain only from 2.4 to 17.7% of their original viscosity, whereas, Gantrez AN-119 solutions retained from 60 to 69% in the same period.
Comparison of relative effectiveness of the stabilizers tested with the polymer are reported in Table I. Malachite green, in the 130 day test at 0.1% concentration (based on the weight of polymer) resulted in retention of 77% of the original viscosity of a 10% solution of AN-169 and 96% retention for a 10% solution of AN-119. (Examples 1, 2, 23 and 24).
The colors of the various Gantrez AN solutions all remained unchanged for the duration of these tests. The colors formed through use of these stabilizers were as follows: malachite green-bluish green; methylene blue-blue; sodium diphenylamine sulfonate-pale yellow; pyronine Y-red; amaranth-red; tartrazine-red; phenosafranine-violet.
The variations in initial viscosity of unstabilized thickened solutions (Examples 9, 11, 15 and 17 and Examples 21, 23, 28 and 31) is caused by variations in molecular weights of differing lots of polymers employed. In these Examples, the acid moiety of the hydrolyzed methyl vinyl ether/maleic anhydride copolymer was the acid which provided the acidic medium having a pH of 0.1 and 1.9.
TABLE 1__________________________________________________________________________STABILIZERS FOR HYDROLIZED POLY(METHYL VINYL ETHER/MALEIC ANHYDRIDE)Example Polymer % % Stabilizer Initial Viscosity Final Viscosity Duration of TestNo. Polymer Concentrn. on wt. Polymer Brookfield Brookfield (Days/temp.) Remarks__________________________________________________________________________1 GANTREZ AN 119 10 0 49 CPS 30 CPS 130/ambient Lt. yellow2 GANTREZ AN 119 10 0.1 malachite g. 52 CPS 50 CPS 130/ambient Blue-green3 GANTREZ AN 119 10 0 55 CPS 35 CPS 120/ambient4 GANTREZ AN 119 10 0.1 methylene blue 55 CPS 45 CPS 120/ambient Blue5 GANTREZ AN 119 20 0 375 CPS 225 CPS 130/ambient6 GANTREZ AN 119 20 0.05 malachite g. 375 CPS 325 CPS 130/ambient7 GANTREZ AN 119 20 0 375 CPS 225 CPS 120/ambient8 GANTREZ AN 119 20 0.05 methylene blue 375 CPS 260 CPS 120/ambient9 GANTREZ AN 119 5 0 225 CPS 40 CPS 130/ambient10 GANTREZ AN 169 5 0.2 malachite g. 245 CPS 190 CPS 130/ambient11 GANTREZ AN 169 5 0 210 CPS 25 CPS 120/ambient12 GANTREZ AN 169 5 0.2 methylene blue 210 CPS 140 CPS 120/ambient13 GANTREZ AN 169 5 0 300 CPS 30 CPS 65/ambient14 GANTREZ AN 169 5 0.2 SDPAS* 260 CPS 200 CPS 65/ambient Lt. yellow15 GANTREZ AN 169 5 0 250 CPS 35 CPS 60/ambient16 GANTREZ AN 169 5 0.2 Pyronin Y 240 CPS 150 CPS 60/ambient Red17 GANTREZ AN 169 5 0 280 CPS 36 CPS 5 @ 50.degree. C.18 GANTREZ AN 169 5 0.2 Amaranth 290 CPS 54 CPS 5 @ 50.degree. C. Red19 GANTREZ AN 169 5 0.2 Tartrazine 270 CPS 42 CPS 5 @ 50.degree. C. Yellow20 GANTREZ AN 169 5 0.2 Phenosafranin 276 CPS 150 CPS 5 @ 50.degree. C. Violet21 GANTREZ AN 169 10 0 4500 CPS 110 CPS 130/ambient22 GANTREZ AN 169 10 0.1 methylene blue 4500 CPS 2040 CPS 130/ambient23 GANTREZ AN 169 10 0 2900 CPS 150 CPS 130/ambient Lt. yellow24 GANTREZ AN 169 10 0.1 malachite g. 3600 CPS 2800 CPS 130/ambient Blue-green25 GANTREZ AN 169 10 0 4500 CPS 300 CPS 65/ambient26 GANTREZ AN 169 10 0.1 SDPAS* 4900 CPS 2700 CPS 65/ambient Trace yellow27 GANTREZ AN 169 10 0.2 SDPAS* 4200 CPS 2500 CPS 65/ambient28 GANTREZ AN 169 10 0 4300 CPS 382 CPS 60/ambient29 GANTREZ AN 169 10 0.1 Pyronin Y 3800 CPS 2000 CPS 60/ambient Red30 GANTREZ AN 169 10 0.2 Pyronin Y 3900 CPS 2500 CPS 60/ambient31 GANTREZ AN 169 10 0 4500 CPS 1320 CPS 5 @ 50.degree. C.32 GANTREZ AN 169 10 0.2 Phenosafranin 4240 CPS 1880 CPS 5 @ 50.degree. C.__________________________________________________________________________ *SDPAS = Na salt of diphenylamine sulfonate
EXAMPLES 33 THROUGH 54
Stabilizers for PVP-K90
The polymer PVP-K 90 is poly(N-vinyl-2-pyrrolidone) having a viscosity K value of 90 and is supplied by GAF Corporation.
The test procedure for Examples 33-54 was similar to that described for hydrolyzed Gantrez AN (Table 1) except that in the present examples the initial viscosity was determined after only 24 hours of slow mixing. The mixtures were mixed for another 24 hours and air bubbles rose to the surface while the mixture was allowed to stand. The viscosity was then determined using a Brookfield RVT viscometer with a No. 3 spindle at 10 or 100 RPM.
Stability tests reported in following Table 2 show that aqueous concentrated solutions (10 to 15%) of unstabilized PVP-K90 increase in viscosity on storage, and in the presence or absence of light, form grainy gels within 4 to 5 months. The viscosity of a 10% solution of K90 (pH 6.8) after storage for 130 days, was found to be 221% that of the initial Brookfield value (640 to 1420 cps); additionally, the original smooth mucilage appearance was transformed into a very grainy stringy gel (Example 33). This is probably due to cross-linking by oxidation or U.V. light.
In a related experiment using K 90 at 15% concentration (pH 6.8), the sample bottle was wrapped in heavy aluminum foil and stored in total darkness for 170 days. The viscosity at the end of this time was 140% that of the original viscosity (4000 to 5600 cps) and the consistency of the mucilage had changed to form a grainy stringy gel (Example 35).
Stability tests involving unstabilized PVP-K90 in 10% HCl (pH range 0.1 to 0.15) at polymer concentrations of 10 to 15% showed that, at ambient temperatures, the viscosity decreased to 55 to 60% of the original values within 90 to 95 days (Examples 39, 41 and 47).
The addition of 0.1% malachite green (based on the weight polymer) to a 6.7 pH solution in the 130 days storage test described above, was effective in reducing the viscosity increase to only 125% that of the original (vs 221% for control) and in addition completely eliminated the formation of grainy, stringy gels (Example 34). The use of as little as 0.06% methylene blue, in a 6.7 pH solution in the 170 day darkness trials, prevented any change in viscosity or appearance of the smooth mucilage (Example 36).
Another demonstration of the effectiveness of the present stabilizers was observed in Examples 43-46 conducted at 50.degree. C. After 95 days in a constant temperature oven at 50.degree. C., a 10% solution of unstabilized PVP-K90 in 10% HCl retained only 16% of its original viscosity (810 cps vs 130 cps). However, similar solutions containing 0.1% (based on weight K 90) of either tartrazine, amaranth of phenosafranine, retained from 78 to 92% of their original viscosities. Phenosafranine was the most effective stabilizer. Malachite green was most effective in Gantrez solutions, while pyronine is more effective in acidified PVP.
In a stabilizer concentration of from 0.066 to 0.66% methylene blue (on the weight PVP) in solutions of 15% PVP-K90 in 10% HCl, the viscosity data after 95 days at ambient temperatures showed that the unstabilized control retained only 62% of its original viscosity. The sample containing 0.066% methylene blue retained 86% of its original viscosity, while samples containing 0.13% and 0.33% remained essentially unchanged. Increasing tht levels to 0.46 and 0.66% resulted in final viscosities of 95 and 90% of the original values, respectively (Examples 47-54).
Samples of 15% PVP-K90 in 10% HCl wrapped in aluminum foil and stored in darkness for 170 days with and without methylene blue (0.06% level) demonstrated that unstabilized PVP-K90 forms a grainy gel on storage at pH 0.1. The methylene blue stabilized gel remained smooth. The unstabilized sample retained 78% of its original viscosity while the methylene blue treated sample increased in viscosity 15% (Examples 53 and 54).
Examples 38 and 39 are presented to show viscosities at lower polymer concentrations in the acid solution.
TABLE 2__________________________________________________________________________STABILIZERS FOR PVP - K-90Example K-90 HCl % Stabilizer Initial Final Duration of TestNo. % Conc. % Conc. on Wt. Poly. Viscosity Viscosity (Days/temp.) Remarks__________________________________________________________________________33 10 0 0 640 CPS 1420 CPS 130/ambient Grainy Gel34 10 0 0.1 malachite g. 640 CPS 800 CPS 130/ambient Smooth Gel35 15 0 0 4000 CPS 5600 CPS 170/ambient* Grainy Gel36 15 0 0.066 methylene blue 6000 CPS 6000 CPS 170/ambient* Smooth Gel37 1 9.6 0 10 CPS 5 CPS 30/ambient38 5 9.6 0 50 CPS 35 CPS 30/ambient39 10 10 0 940 CPS 560 CPS 90/ambient Clear Water White40 10 10 0.1 malachite g. 910 CPS 620 CPS 90/ambient Clear Orange41 10 10 0 800 CPS 440 CPS 90/ambient42 10 10 0.1 Pyronin Y 800 CPS 1000 CPS 90/ambient Clear red43 10 10 0 810 CPS 130 CPS 95/50.degree. C.44 10 10 0.1 Amaranth 950 CPS 850 CPS 95/50.degree. C. Clear red45 10 10 0.1 Tartrazine 960 CPS 750 CPS 95/50.degree. C. Clear yellow46 10 10 0.1 Phenosafranin 990 CPS 920 CPS 95/50.degree. C. Violet47 15 10 0 6500 CPS 4000 CPS 95/ambient48 15 10 0.066 methylene blue 7300 CPS 6300 CPS 95/ambient Clear blue49 15 10 0.13 methylene blue 6800 CPS 7000 CPS 95/ambient50 15 10 0.33 methylene blue 6300 CPS 6400 CPS 95/ambient51 15 10 0.46 methylene blue 6900 CPS 6500 CPS 95/ambient52 15 10 0.66 methylene blue 7200 CPS 6500 CPS 95/ambient53 15 10 0 7300 CPS 5700 CPS 170/ambient* Grainy Gel54 15 10 0.066 methylene blue 6500 CPS 7500 CPS 170/ambient* Smooth Gel__________________________________________________________________________ *Stored in dark
EXAMPLES 55 THROUGH 87
The polymer employed in this series is poly-N-vinyl-2-pyrrolidone having a viscosity K value of 112 cross-linked with diallyl polyethylene glycol 600, (0.02 mole % cross-linked).
Methylene blue, malachite green (oxalate) sodium diphenylamine sulfonate and pyronine Y were trested as stabilizers for the polymer and the results after 2-5 months are shown in Table 3. All of these samples were tested in either 5 or 10% HCl at pH range of 0.10 to 0.18. The solution preparation employed for Examples 1-32 was employed for the present examples.
Effectiveness was noted for the present stabilizers in 2 to 5 months tests reported in Table 3. For example, sodium diphenylaminesulfonate was 100% effective; pyronine Y was 90-95% effective; and methylene blue was 100% effective with a tendency to increase viscosity to as much as 147%. Unstabilized controls stored in light from 50 to 130 days ranged from 3% to 62% of their original viscosities while an unstabilized control stored in darkness for 170 days retained 78%.
TABLE 3__________________________________________________________________________STABILIZERS FOR CROSSLINKED PVP (K112) CROSSLINKED VIA DIALLYLPOLYETHYLENE GLYCOL 600Example Polymer HCl % Stabilizer Initial Viscosity Final Viscosity Duration of TestNo. Conc. % Conc. % on Wt. Polymer Brookfield Brookfield (Days/temp.) Remarks__________________________________________________________________________55 3 5 0 55 CPS 15 CPS 50/ambient Water White56 3 5 0.33 methylene blue 70 CPS 80 CPS 155/ambient Blue57 3 10 0.33 methylene blue 80 CPS 88 CPS 155/ambient58 5 5 0 142 CPS 26 CPS 50/ambient59 5 5 0.2 methylene blue 230 CPS 230 CPS 155/ambient60 5 10 0.2 methylene blue 275 CPS 300 CPS 155/ambient61 10 5 0 4000 CPS 135 CPS 50/ambient62 10 5 0.1 methylene blue 4000 CPS 3800 CPS 155/ambient63 10 10 0 3000 CPS 1300 CPS 130/ambient64 10 10 0.1 malachite g. 2700 CPS 1800 CPS 130/ambient Orange yellow65 10 10 0.1 methylene blue 3100 CPS 4000 CPS 155/ambient66 10 10 0.1 methylene blue 3600 CPS 5300 CPS 145/ambient67 10 10 0 5000 CPS 1200 CPS 95/ambient68 10 10 0.01 methylene blue 4700 CPS 4700 CPS 95/ambient69 10 10 0.02 methylene blue 4400 CPS 5700 CPS 95/ambient70 10 10 0.05 methylene blue 5200 CPS 6200 CPS 95/ambient71 10 10 0.07 methylene blue 5000 CPS 5200 CPS 95/ambient72 10 10 0.1 methylene blue 5500 CPS 6000 CPS 95/ambient73 10 10 0.1 malachite g. 5000 CPS 5400 CPS 90/ambient74 10 10 0.2 malachite g. 5600 CPS 5700 CPS 90/ambient75 10 10 0.3 malachite g. 5800 CPS 5600 CPS 90/ambient76 10 10 0 5000 CPS 2600 CPS 95/ambient77 10 10 0.1 SDPAS 4900 CPS 5000 CPS 95/ambient Water white to light blue78 10 10 0.2 SDPAS 4500 CPS 4600 CPS 95/ambient79 10 10 0 4500 CPS 2800 CPS 90/ambient80 10 10 0.1 Pyronin Y 5000 CPS 4500 CPS 90/ambient Red Hazy81 10 10 0.2 Pyronin Y 5700 CPS 5400 CPS 90/ambient82 10 10 0 4500 CPS 3500 CPS 170/ambient* Grainy Gel83 10 10 0.1 methylene blue 4700 CPS 4300 CPS 170/ambient* Smooth Gel84 10 15 0.1 methylene blue 5000 CPS 5600 CPS 145/ambient85 10 20 0.1 methylene blue 5300 CPS 5400 CPS 145/ambient86 10 25 0.1 methylene blue 6500 CPS 7100 CPS 145/ambient87 12 10 0.0075 methylene blue (1) 6000 CPS 3400 CPS 145/ambient Blue__________________________________________________________________________ Hazy *Stored in dark (1) Amount of stabilizer insufficient for polymer:acid concentration. Whe the concentration of either polymer or acid is lowered, this amount of stabilizer should be effective.
EXAMPLES 88 THROUGH 107
Results of one year shelf life stability tests are reported in Table 4 for either 10 or 15% K 90 solutions in 0 or 10% HCl using methylene blue, malachite green (oxalate), amaranth, tartrazine, phenosafranine, sodium diphenylamine sulfonate, or pyronine Y. In 10% HCl, methylene blue, phenosafranine and pyronine Y completely stabilized the K 90 solutions for the duration of the tests. Amaranth, tartrazine and sodium diphenylamine sulfonate were about 80% effective. Malachite green showed only fair results (36%) but was very effective in K 90 solution without HCl in preventing cross-linking which resulted in a grainy appearance and vast increase in viscosity.
The stabilizers of the present invention demonstrate marked improvement over the prior art as represented by U.S. Pat. No. 2,894,921 which requires 3 to 120% of 8-hydroxyquinoline based on dry polymer to prevent drastic reduction in the viscosity of Gantrez solutions.
TABLE 4__________________________________________________________________________STABILIZERS FOR PVP - K-90RESULTS OF ONE YEAR SHELF LIFE STABILITY TESTSExample K-90 HCl % Stabilizer Initial Final Final Viscosity Duration of FinalNo. % Conc. % Conc. on Wt. Poly. Viscosity Viscosity % of Original (Days/temp.) Color__________________________________________________________________________88 15 10 0.066 methylene blue 7300 CPS 4400 CPS 60 405/ambient Clear Blue89 15 10 0.13 methylene blue 6800 CPS 6200 CPS 91 405/ambient Clear Blue90 15 10 0.33 methylene blue 6300 CPS 6700 CPS 106 405/ambient Clear Blue91 15 10 0.46 methylene blue 6900 CPS 6300 CPS 91 405/ambient Clear Blue92 15 10 0.66 methylene blue 7200 CPS 6700 CPS 93 405/ambient Clear Blue93 15 10 0 6500 CPS 2300 CPS 35 405/ambient Pale Yellow94 10 10 0 810 CPS 90 CPS 11 335/ambient Pale Yellow95 10 10 0.1 Amaranth 950 CPS 820 CPS 86 335/ambient Clear Red96 10 10 0.1 Tartrazine 960 CPS 730 CPS 76 335/ambient Clear Yellow97 10 10 0.1 Phenosafranin 990 CPS 1000 CPS 101 335/ambient Violet98 10 10 0 800 CPS 180 CPS 22 378/ambient Pale Yellow99 10 10 0.1 Pyronin Y 800 CPS 840 CPS 105 378/ambient Clear Red100 10 10 0 840 CPS 180 CPS 21 382/ambient Pale Yellow101 10 10 0.1 Na di-phenyl 1000 CPS 800 CPS 80 382/ambient Pale Blue Aminesulfonate102 10 10 0.1 malachite g. 910 CPS 330 CPS 36 402/ambient Clear Amber103 10 10 0 940 CPS 230 CPS 24 402/ambient Clear Water White104 10 0 0 640 CPS 2000 CPS 312 448/ambient Grainy105 10 0 0.1 malachite g. 640 CPS 740 CPS 115 448/ambient Blue Smooth106 15 0 0 4000 CPS 5000 CPS 125 405/ambient* Pale Yellow107 15 0 0.066 methylene blue 6000 CPS 6800 CPS 113 405/ambient* Blue__________________________________________________________________________ *Stored in dark
EXAMPLES 108 THROUGH 131
The work up for the preparation of acidic polymer solutions which was described for Examples 1-32 were repeated except that samples containing methylene blue, malachite green, sodium diphenylaminesulfonate or pyronine Y were stored for at least one year at room temperatures in light. The results of this one year shelf life stability test reported in Table 5 show that at 0.1% concentration, methylene blue provided retention of 40% of the original viscosity of a 10% solution of Gantrez AN 169; sodium diphenylamine sulfonate 25% of the original viscosity, and malachite green 22% of the original viscosity as compared to 1.5 to 3.0% for the unstabilized controls. In 10% solutions of Gantrez AN 119, 0.1% of malachite green provided retention of 71% of the original viscosity and methylene blue 69% of the original viscosity as compared to 49 to 53% retention for the unstabilized controls.
TABLE 5__________________________________________________________________________STABILIZERS FOR GANTREZ ANRESULTS OF ONE YEAR SHELF LIFE STABILITY TESTSExample Gantrez Poly. % Stabilizer Initial Final Final Viscosity Duration of FinalNo. AN Conc. on Wt. Poly. Viscosity Viscosity % of Original (Days/temp.) Color__________________________________________________________________________108 169 5 0 225 CPS 28 CPS 12 425/ambient Clear Trace Yellow109 169 5 0.2 malachite g. 245 CPS 145 CPS 59 425/ambient Clear blue110 169 10 0 2900 CPS 80 CPS 3 425/ambient Clear yellow111 169 10 0.1 malachite g. 3600 CPS 800 CPS 22 425/ambient Clear blue112 119 10 0 49 CPS 26 CPS 53 425/ambient Hazy yellow113 119 10 0.1 malachite g. 52 CPS 37 CPS 71 425/ambient Clear blue114 119 20 0 325 CPS 120 CPS 37 425/ambient Hazy yellow115 119 20 0.05 malachite g. 375 CPS 200 CPS 53 425/ambient Clear Blue-Green116 169 5 0 210 CPS 21 CPS 10 420/ambient Clear yellow117 169 5 0.2 methylene blue 210 CPS 82 CPS 39 420/ambient Clear blue118 169 10 0 2800 CPS 90 CPS 3 420/ambient Yellow119 169 10 0.1 methylene blue 3160 CPS 1260 CPS 40 420/ambient Clear blue120 119 10 0 55 CPS 27 CPS 49 420/ambient Yellow121 119 10 0.1 methylene blue 55 CPS 38 CPS 69 420/ambient Clear blue122 119 20 0 375 CPS 160 CPS 42 420/ambient Hazy yellow123 119 20 0.05 methylene blue 375 CPS 195 CPS 52 420/ambient Clear blue124 169 10 0 4500 CPS 70 CPS 1.5 385/ambient Pale yellow125 169 10 0.1 Na di-phenyl 4900 CPS 1240 CPS 25 385/ambient Straw Aminesulfonate126 169 10 0.2 Na di-phenyl 4200 CPS 1160 CPS 27 385/ambient Clear yellow-green Aminesulfonate127 169 5 0 250 CPS 20 CPS 8 380/ambient Pale yellow128 169 5 0.2 Pyronin Y 240 CPS 25 CPS 10 380/ambient Hazy red129 169 10 0 4300 CPS 70 CPS 1.6 380/ambient Pale yellow130 169 10 0.1 Pyronin Y 3800 CPS 155 CPS 4 380/ambient Hazy red131 169 10 0.2 Pyronin Y 3900 CPS 140 CPS 3.5 380/ambient Hazy__________________________________________________________________________ red
EXAMPLES 132 THROUGH 157
Stabilizers for the cross-linked polymer of Examples 55-87 were tested for one year shelf life stability of the thickened acid solution. The polymer solution was prepared by mixing the stabilizer and polymer in the HCl aqueous solution in the concentration shown in Table 6.
The results of the one year shelf life study show that sodium diphenylaminesulfonate and pyronine Y were 100% effective in maintaining the initial viscosity for over one year. Methylene blue results indicate a slight increase in viscosity. Unstabilized controls stored in light retained only 3 to 7% of their original viscosities but an unstabilized control stored in darkness retained 73%, indicating that light accelerates the deterioration with the system.
TABLE 6__________________________________________________________________________STABILIZERS FOR CROSSLINKED PVP.sup.1 K112RESULTS OF ONE YEAR SHELF LIFE STABILITY TESTSExample Poly HCl % Stabilizer Initial Final Final Viscosity Duration of FinalNo. Conc. Conc. on Wt. Poly. Viscosity Viscosity % of Original (Days/temp.) Color__________________________________________________________________________132 10 10 0.1 malachite g. 2700 CPS 620 CPS 23 445/ambient Orange133 10 10 0 3000 CPS 140 CPS 5 445/ambient Pale Yellow134 10 10 0.01 methylene blue 4700 CPS 2800 CPS 59 420/ambient Pale Blue135 10 10 0.02 methylene blue 4400 CPS 5000 CPS 113 420/ambient Blue136 10 10 0.05 methylene blue 5200 CPS 5800 CPS 111 420/ambient Dark Blue137 10 10 0.07 methylene blue 5000 CPS 6000 CPS 120 420/ambient Dark Blue138 10 10 0.1 methylene blue 5500 CPS 6100 CPS 110 420/ambient Dark Blue139 10 10 0 5000 CPS 260 CPS 5 420/ambient Pale Yellow140 3 5 0.33 methylene blue 70 CPS 75 CPS 107 425/ambient Blue141 5 5 0.2 methylene blue 230 CPS 252 CPS 109 425/ambient Blue142 10 5 0.1 methylene blue 4000 CPS 4500 CPS 112 425/ambient Blue143 3 10 0.33 methylene blue 80 CPS 76 CPS 95 425/ambient Blue144 5 10 0.2 methylene blue 275 CPS 285 CPS 103 425/ambient Blue145 10 10 0.1 methylene blue 4100 CPS 6400 CPS 156 425/ambient Blue146 10 5 0 4000 CPS 135 CPS 3 50/ambient Pale Yellow147 10 10 0.1 malachite g. 5000 CPS 2000 CPS 40 410/ambient Pale Orange148 10 10 0.2 malachite g. 5600 CPS 2500 CPS 44 410/ambient Orange149 10 10 0.3 malachite g. 5800 CPS 3700 CPS 64 410/ambient Orange150 10 10 0 5000 CPS 340 CPS 7 390/ambient Pale Yellow151 10 10 0.1 SDPAS.sup.2 4900 CPS 5100 CPS 104 390/ambient Pale Blue-Green152 10 10 0.2 SDPAS.sup.2 4500 CPS 4900 CPS 109 390/ambient Blue-Green153 10 10 0 4500 CPS 340 CPS 7.5 385/ambient Pale Yellow154 10 10 0.1 Pyronin Y 5000 CPS 5000 CPS 100 385/ambient Red155 10 10 0.2 Pyronin Y 5700 CPS 5400 CPS 95 385/ambient Red156 10 10 0.1 methylene blue 4700 CPS 4200 CPS 89 410/ambient* Blue157 10 10 0 4500 CPS 3300 CPS 73 410/ambient* Pale__________________________________________________________________________ Yellow .sup.1 Vinylpyrrolidone crosslinked with diallyl polyethylene glycol 600 .sup.2 SDPAS = Sodium Diphenylamine sulfonate *Stored in dark
EXAMPLES 158 THROUGH 206
The data presented in Table 7 provides a guide to color changes in the stabilized acid solutions of polymer which may be expected when a decline in viscosity due to oxidation occurs.
Additionally the Redox Potential of methylene blue, phenosafranine and sodium diphenylamine sulfonate is provided, as a guide for color change in the oxidized form.
The normal redox potential for methylene blue at various pH's is given as +0.101 (pH 5.0), +0.011 (pH 7.0) and -0.050 (pH 9.0) (Chemical Indicators-Tomicek).
TABLE 7__________________________________________________________________________ Color of Initial Color Initial Color inExample Redox Potential Oxidized Color of Reduced in Solution Hydrolyzed GantrezNo. Indicator at pH O.sup.a Form in H.sub.2 O Form in H.sub.2 O PVP + HCl AN Solution with__________________________________________________________________________ HCl158 Phenosafranine 0.28 volts Red Colorless Violet Violet159 Methylene Blue 0.53 volts Blue Colorless Blue Blue160 Sodium Diphenylamine sulfonate 0.84 volts Violet-Red Colorless Pale Pink Pale Yellow161 Amaranth -- Colorless Red Red Red162 Tartrazine -- Colorless Yellow Yellow Yellow163 Malachite Green -- Blue-Green Colorless Blue-Green Blue-Green164 Pyronin Y -- -- -- Red Red165 Neutral Red 0.20.sup.b volts Red-Violet Colorless166 Gallocyanine 0.02 volts Violet-Blue Colorless167 Safranine T 0.24 volts Blue-Violet Colorless168 Dimethylglyoxime.sup.c 0.25.sup.d volts Colorless Red169 5,5'-Indigodisulfonic Acid, 0.29 volts Blue Colorless Disodium Salt170 Nile Blue A (Sulfate) 0.41 volts Blue Colorless172 Thionin(e) 0.56 volts Violet Colorless173 Brilliant Cresyl Blue 0.58 volts Blue Colorless174 2,6-Dichloroindophenol, 0.67 volts Red Colorless Sodium Derivative175 N.sup.1 --Phenyl-1,2,4-benzene- 0.70 volts Red Colorless triamine176 Variamine Blue B Hydrochloride 0.71 volts Blue Colorless177 2,2-Bipyridine.sup.c 0.97 volts Blue Red178 2',2'-Bipyridine 0.97 volts Blue Red Monohydrochloride.sup.c179 2,2'-Bipyridine, Iron (II) 0.97 volts Blue Red Derivative, Perchlorate180 5,6-Dimethyl-1,10-phenan- 0.97 volts Pale Blue Red throline181 Erioglaucine (A) 1.00 volts Pink Green182 Xylene Cyanole FF 1.00 volts Pink Yellow-Green183 Setoglaucine O 1.01 volts Yellow-Red Yellow-Green184 5-Methyl-1,10-phenan- 1.06 volts Pale Blue Red throline.sup.c185 5-Methyl-1,10-phenanthro- 1.06 volts Pale Blue Red line, Iron (II) Derivative, Perchlorate186 N--Phenylanthranilic Acid 1.08 volts Violet-Red Colorless187 Setopaline 1.10 volts Orange Yellow188 1,10-Phenanthroline.sup.c 1.14 volts Pale Blue Dark Red189 1,10-Phenanthroline 1.14 volts Pale Blue Dark Red Monohydrochloride.sup.c190 2,2'-Bipyridine, Ruthenium- 1.25 volts Colorless Yellow (II) Derivative, Chloride191 N,N--Dimethyl-p-phenylene- 0.76 volts Red Colorless diamine192 Diphenylamine 0.76 volts Violet Colorless193 N,N--Diphenylbenzidine 0.76 volts Violet Colorless194 3,3'-Dimethoxybenzidine 0.76 volts Red Colorless195 3,3'-Dimethoxybenzidine 0.76 volts Red Colorless Dihydrochloride196 Barium Diphenylamine- 0.84 volts Violet-Red Colorless sulfonate197 3,4,7,8-Tetramethyl-1,10- 0.85 volts Pale Blue Red phenanthroline.sup.c198 3,4,7,8-Tetramethyl-1,10- 0.85 volts Pale Blue Red phenanthroline, Iron (II) Derivative, Sulfate199 4,7-Dimethyl-1,10-phenan- 0.87 volts Pale Blue Red throline.sup.c200 o-Tolidine 0.87 volts Blue Colorless201 Benzidine Dihydrochloride 0.92 volts Blue Colorless202 5-Nitro-1,10-phenanthroline.sup.c 1.25 volts Pale Blue Red203 2,2':6',2"-Terpyridine.sup.c 1.25 volts Pale Blue Red204 Brucine -- Red Colorless205 Cacotheline -- Yellow Red-Violet206 Methyl Red Hydrochloride.sup.g -- Orange Violet or Yellow__________________________________________________________________________ .sup.a Vs. normal hydrogen electrode .sup.b At pH 5 .sup.c Fe (II) present .sup.d At pH 9.4 .sup.g Irreversible
The Redox indicators of the present invention have been found to aid in stabilizing acidic solutions of PVP or Gantrez AN. They retard oxidation of these polymers which results in chain scission with a decrease in viscosity or cross-linking with increased viscosity, both of which were observed in the tests conducted.
It is to be understood that any of the aforereferenced polymers can be substituted in the above examples employing the present Redox indicators for improved stability over extended periods.

Number	Name	Date
3906513	Siegelman	Sep 1975
4066595	Bunge	Jan 1978
4163001	Carumpalos	Jul 1979
4197087	Ami	Apr 1980
4205998	Becker	Jun 1980
4225475	Carumpalos	Sep 1980
4248636	Sasaki	Feb 1981

Polymer stabilizers

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

US Referenced Citations (7)