POLYMERIC FIBERS AND ARTICLES MADE THEREFROM

Abstract
Fibers described herein comprise a composition including a polymer and graphene sheets. The fibers can be further formed into yarns, cords, and fabrics. The fibers can be in the form of polyamide, polyester, acrylic, acetate, modacrylic, spandex, lyocell fibers, and the like. Such fibers can take on a variety of forms, including, staple fibers, spun fibers, monofilaments, multifilaments, and the like.
Description
FIELD OF THE INVENTION

The present invention relates to fibers made from compositions comprising at least one polymer and graphene sheets.


BACKGROUND

Fibers and structures based on fibers (such as yarns, cords, fabrics, etc.) have been used for a wide variety of applications. The advent of synthetic fibers in the 1930s made available mass produced fibers having a wider range of properties and applications than the previously available natural and modified natural fibers. With numerous desirable properties, such as good tensile properties, toughness, elasticity, thermal stability, dimensional stability, good resistance to adverse environmental conditions (such as water, solvents, light, oxidations, etc.), light weight, etc., many polymeric fibers in particular have found a wide variety of uses.


However, as even lighter weight and stronger materials have become more desirable for many applications (such as reinforcement applications) (including for metal (such as steel) replacement), polymeric fibers having improved properties, such as one or more of strength, tensile properties (including tensile modulus), compression resistance, stiffness, chemical resistance, fatigue resistance, dimensional stability, shrinkage properties, chemical stability, thermal conductivity, electrical conductivity, antistatic properties, etc. are needed. Furthermore, improvements in certain properties can lead to the deterioration of others, and thus it would be in many cases desirable to effect improvements in some properties while minimizing deterioration (or even improving) the other properties. For example, it is often undesirable and/or difficult to form a fiber of a polymer with additives or impurities in the polymer as such additives or impurities can lead to a deterioration of at least one of the properties of the fiber, such as tensile strength. Said another way, polymer fibers are typically formed with a polymer that has as few additives or impurities as possible. It would be desirable, however, to form a fiber from a polymer containing with additives that enhance at least one of the properties of the fiber and do not lead to a deterioration of other properties.


SUMMARY OF THE INVENTION

Disclosed and claimed herein are fibers comprising a composition comprising a polymer and graphene sheets.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 shows a plot of the storage modulus vs. temperature of monofilaments comprising poly(ethylene terephthalate) containing 0.25 wt. % graphene sheets and of commercial PET monofilaments.





DETAILED DESCRIPTION

Fibers described herein comprise a composition including a polymer and graphene sheets. The fibers can be in the form of polyamide, polyesters, acrylics, acetates, modacrylics, spandex, lyocelsl, and the like. Such fibers (also referred to herein as filaments) can take on a variety of forms, including, staple fibers (also referred to as spun fibers), monofilaments, multifilaments, and the like. The fibers can have a number of different average diameters. For example, in some embodiments, the fibers can have a number average diameter of about 1 μm to about 1.5 mm, or of about 15 μm to about 1.5 mm.


The fibers can be of any cross-sectional shape. For example, they can have a circular or substantially circular cross-section, or have cross-sections that are, for example, oval, star-shaped, multilobal (including trilobal), square, rectangular, polygonal, irregular, etc. They can also be hollow in their entirety or in part and can have a foam-like structure. The fibers can be crimped, bent, twisted, woven or the like.


Fibers can be in the form of a multicomponent (such as a bicomponent) composite structure (these are also referred to as conjugate fibers), including, for example, multilayered structures comprising two or more concentric and/or eccentric layers (including inner core and outer sheath layers), a side-by-side structure, or the like. These can be obtained, for example, by extruding two or more polymers from the same spinnerette.


In one embodiment, each of the components of the structures include a form of the composition. In another embodiment, at least one of the components include a form of the composition and another of the components include a material without the composition. For example, other components (such as layers) may comprise other polymeric materials.


Examples of bicomponent structures include fibers comprising a polyester core and a copolyester sheath, a polyester core and a polyethylene sheath, a polyester core and a polyamide sheath, a poly(ethylene naphthalate) core and a sheath of another polyester, a polyamide core and a copolyamide sheath, a polyamide core and a polyester sheath, a polypropylene core and a polyethylene sheath, and the like.


The polymers can be of any suitable type, including thermoplastics, elastomers, non-melt-processable polymers, thermoset polymers, etc. Examples of polymers include, but are not limited to: polyamides, polyesters, polyolefins (such as polyethylene, ultrahigh molecular weight polyethylene, linear low density polyethylene (LLDPE), low density polyethylene (LDPE), high density polyethylene, polypropylene, and olefin copolymers), cellulosic polymers, rayon, cellulose acetate, acrylics, poly(methyl methacrylate) and other acrylate polymers, poly(phenylene sulfide) (PPS), poly(acrylonitrile) and poly(acrylonitrile) copolymers (such as copolymers with vinyl acetate, methyl acrylate, and/or methyl methacrylate), melamine polymers, polybenzimidazole (PBI), polyurethanes (including thermoplastics and thermosets), poly(p-phenylene-2,6-benzobisoxazole) (PBO), polyphenylene benzobisthiazole, poly{2,6-diimidazo[4,5-b:4′,5′-e]pyridinylene-1,4-(2,5-dihydroxy)phenylene}) (PIPD), liquid crystalline polyesters, aramids (such as those sold by DuPont under the trademarks Kevlar® and Nomex®, including poly(m-phenylene isophtalamide)s and poly(p-phenylene terephthalamide)s, and co-poly-(paraphenylene/3,4′-oxydiphenylene terephthalamide)), and polymers derived from polyurethane and aliphatic polyethers (including polyether polyols such as poly(ethylene glycol), poly(propylene glycol), poly(tetramethylene ether) glycol (PTMEG), and the like)).


Other polymers include, for example, styrene/butadiene rubbers (SBR), styrene/ethylene/butadiene/styrene copolymers (SEBS), butyl rubbers, ethylene/propylene copolymers (EPR), ethylene/propylene/diene monomer copolymers (EPDM), polystyrene (including high impact polystyrene), poly(vinyl acetates), ethylene/vinyl acetate copolymers (EVA), poly(vinyl alcohols), ethylene/vinyl alcohol copolymers (EVOH), poly(vinyl butyral), acrylonitrile/butadiene/styrene (ABS), styrene/acrylonitrile polymers (SAN), styrene/maleic anhydride polymers, poly(ethylene oxide), poly(propylene oxide), poly(acrylonitrile), polycarbonates (PC), polyamides, polyesters, liquid crystalline polymers (LCPs), poly(lactic acid), poly(phenylene oxide) (PPO), PPO-polyamide alloys, polysulf ones (PSU), polyether sulf ones, polyurethanes, polyetherketone (PEK), polyetheretherketone (PEEK), polyimides, polyoxymethylene (POM) homo- and copolymers, polyetherimides, fluoropolymers (such as polytetrafluoroethylene (PTFE), fluorinated ethylene propylene polymers (FEP), poly(vinyl fluoride), and poly(vinylidene fluoride)), poly(vinylidene chloride), poly(vinyl chloride), and epoxy polymers.


The polymers can be elastomers such as, for example, polyurethanes, copolyetheresters, rubbers (including butyl rubbers and natural rubbers), styrene/butadiene copolymers, styrene/ethylene/butadiene/styrene copolymer (SEBS), polyisoprene, ethylene/propylene copolymers (EPR), ethylene/propylene/diene monomer copolymers (EPDM), polysiloxanes, and polyethers (such as poly(ethylene oxide), poly(propylene oxide), and their copolymers).


Preferred polymers include polyamides and polyesters (including, for example, thermoplastic and semicrystalline polyamides and polyesters), aramides, polyolefins, and rayons.


Examples of suitable polyamides include, but are not limited to, aliphatic polyamides (such as polyamide 4,6; polyamide 6,6; polyamide 6; polyamide 11; polyamide 12; polyamide 6,9; polyamide 6,10; polyamide 6,12; polyamide 10,10; polyamide 10,12; and polyamide 12,12), alicyclic polyamides, and aromatic polyamides (such as poly(m-xylylene adipamide) (polyamide MXD,6) and polyterephthalamides such as poly(dodecamethylene terephthalamide) (polyamide 12,T), poly(decamethylene terephthalamide) (polyamide 10,T), poly(nonamethylene terephthalamide) (polyamide 9,T), the polyamide of hexamethylene terephthalamide and hexamethylene adipamide, and the polyamide of hexamethyleneterephthalamide, and 2-methylpentamethyleneterephthalamide) and copolymers of the foregoing. Preferred polyamides include polyamide 6,6; polyamide 6; and copolymers of polyamide 6 and polyamide 6,6. The polyamide 6,6 may have a relative viscosity of at least about 65 when measured in 96% formic acid. The polyamide 6 may have a relative viscosity of at least about 85 when measured in 96% formic acid.


Examples of suitable polyesters include, but are not limited to, semiaromatic polyesters, such as poly(butylene terephthalate) (PBT), poly(ethylene terephthalate) (PET), poly(1,3-propylene terephthalate) (PPT), poly(ethylene naphthalate) (PEN), and poly(cyclohexanedimethanol terephthalate) (PCT)), aliphatic polyesters (such as poly(lactic acid), and copolymers thereof. Preferred polyesters are PET, PPT, and PEN. Particularly preferred is PET. Polyesters can include copolyetheresters. Preferred polyesters have an intrinsic viscosity of at least about 0.8 when measured in ortho-chlorophenol.


The graphene sheets are graphite sheets preferably having a surface area of at least about 100 m2/g to about 2630 m2/g. In some embodiments, the graphene sheets primarily, almost completely, or completely comprise fully exfoliated single sheets of graphite (these are approximately 1 nm thick and are often referred to as “graphene”), while in other embodiments, they comprise partially exfoliated graphite sheets, in which two or more sheets of graphite have not been exfoliated from each other. The graphene sheets can comprise mixtures of fully and partially exfoliated graphite sheets.


One method of obtaining graphene sheets is from graphite and/or graphite oxide (also known as graphitic acid or graphene oxide). Graphite can be treated with oxidizing and intercalating agents and exfoliated. Graphite can also be treated with intercalating agents and electrochemically oxidized and exfoliated. Graphene sheets can be formed by ultrasonically exfoliating suspensions of graphite and/or graphite oxide in a liquid. Exfoliated graphite oxide dispersions or suspensions can be subsequently reduced to graphene sheets. Graphene sheets can also be formed by mechanical treatment (such as grinding or milling) to exfoliate graphite or graphite oxide (which would subsequently be reduced to graphene sheets).


Graphite oxide can be reduced to graphene by chemical reduction using hydrogen gas or other reducing agents. Examples of useful chemical reducing agents include, but are not limited to, hydrazines (such as hydrazine, N,N-dimethylhydrazine, etc.), sodium borohydride, hydroquinone, citric acid, etc. For example, a dispersion of exfoliated graphite oxide in a carrier (such as water, organic solvents, or a mixture of solvents) can be made using any suitable method (such as ultrasonication and/or mechanical grinding or milling) and reduced to graphene sheets.


One method of exfoliation includes thermal exfoliation and ultrasonication of suspensions. The graphite can be any suitable type, including natural, Kish, and synthetic/pyrolytic graphites and graphitic materials such as, for example, graphitic carbon fibers (including those derived from polymers), and highly oriented pyrolytic graphite.


In one method of preparing graphene sheets, graphite is first oxidized to graphite oxide, which is then thermally exfoliated to form high surface area graphene sheets in the form of thermally exfoliated graphite oxide. Such a method is generally described in U.S. Patent Pub. No. 2007/0092432, entitled “Thermally Exfoliated Graphite Oxide” by Prud'Homme et al., the disclosure of which is incorporated herein by reference. The thusly formed thermally exfoliated graphite oxide may display little or no signature corresponding to graphite or graphite oxide in its X-ray diffraction pattern.


Graphite oxide may be produced by any method known in the art, such as by a process that involves oxidation of graphite using one or more chemical oxidizing agents and, optionally, intercalating agents such as sulfuric acid. Examples of oxidizing agents include nitric acid, sodium and potassium nitrates, perchlorates, hydrogen peroxide, sodium and potassium permanganates, phosphorus pentoxide, bisulfites, and the like. Preferred oxidants include KClO4; HNO3 and KClO3; KMnO4 and/or NaMnO4; KMnO4 and NaNO3; K2S2O8 and P2O5 and KMnO4; KMnO4 and HNO3; and HNO3. A preferred intercalation agent includes sulfuric acid. Graphite can also be treated with intercalating agents and electrochemically oxidized.


The graphene sheets preferably have an average aspect ratio of about 100 to 100,000 (where “aspect ratio” is defined as the ratio of the longest dimension of the sheet to the shortest dimension of the sheet).


The graphene sheets preferably have a surface area of from about 100 m2/g to about 2,630 m2/g, or more preferably of from about 200 m2/g to about 2,630 m2/g, or yet more preferably of from about 300 m2/g to about 2,630 m2/g, or even more preferably from about 350 m2/g to about 2,630 m2/g, or still more preferably of from about 400 m2/g to about 2,630 m2/g, or further more preferably of from about 500 m2/g to about 2,630 m2/g. In another preferred embodiment, the surface area is about 300 m2/g to about 1,100 m2/g. A single graphite sheet has a maximum calculated surface area of 2,630 m2/g. The surface area includes all values and subvalues therebetween, especially including 400, 500, 600, 700, 800, 900, 100, 110, 1,200, 1,300, 1,400, 1,500, 1,600, 1,700, 1,800, 1,900, 2,000, 2,100, 2,200, 2,300, 2,400, 2,500, and 2,630 m2/g.


Surface area can be measured using either the nitrogen adsorption/BET method at 77 K or a methylene blue (MB) dye method in a liquid solution. The dye method is carried out as follows. A known amount of graphene sheets is added to a flask. At least 1.5 g of MB per gram of graphene sheets is then added to the flask. Ethanol is added to the flask and the mixture is ultrasonicated for about fifteen minutes. The ethanol is then evaporated and a known quantity of water is added to the flask to re-dissolve the free MB. The undissolved material is allowed to settle, preferably by centrifuging the sample. The concentration of MB in solution is determined using a UV-vis spectrophotometer by measuring the absorption at λmax=298 nm relative to that of standard concentrations.


The difference between the amount of MB that was initially added and the amount present in solution as determined by UV-vis spectrophotometry is assumed to be the amount of MB that has been adsorbed onto the surface of the graphene sheets. The surface area of the graphene sheets is then calculated using a value of 2.54 m2 of surface covered per milligram of MB adsorbed.


The graphene sheets preferably have a bulk density of from about 0.1 kg/m3 to at least about 200 kg/m3. The bulk density includes all values and subvalues therebetween, especially including 0.5, 1, 5, 10, 15, 20, 25, 30, 35, 50, 75, 100, 125, 150, and 175 kg/m3.


The graphene sheets can be functionalized with, for example, oxygen-containing functional groups (including, for example, hydroxyl, carboxyl, and epoxy groups) and typically have an overall carbon to oxygen molar ratio (C/O ratio), as determined by elemental analysis of at least about 1:1, or more preferably, at least about 3:2. Examples of carbon to oxygen ratios include about 3:2 to about 85:15; about 3:2 to about 20:1; about 3:2 to about 30:1; about 3:2 to about 40:1; about 3:2 to about 60:1; about 3:2 to about 80:1; about 3:2 to about 100:1; about 3:2 to about 200:1; about 3:2 to about 500:1; about 3:2 to about 1000:1; about 3:2 to greater than 1000:1; about 10:1 to about 30:1; about 80:1 to about 100:1; about 20:1 to about 100:1; about 20:1 to about 500:1; about 20:1 to about 1000:1. In some embodiments of the invention, the carbon to oxygen ratio is at least about 10:1, or at least about 20:1, or at least about 35:1, or at least about 50:1, or at least about 75:1, or at least about 100:1, or at least about 200:1, or at least about 300:1, or at least about 400:1, or at least 500:1, or at least about 750:1, or at least about 1000:1; or at least about 1500:1, or at least about 2000:1. The carbon to oxygen ratio also includes all values and subvalues between these ranges.


The surface of the graphene sheets can be modified by the addition of molecules including hydrocarbons, and those containing neutral or charged functional groups, such as oxygen-, nitrogen-, halogen-, sulfur-, carbon-containing functional groups. Examples of functional groups include hydroxyl groups, amine groups, ammonium groups, sulphates, sulphonates, epoxy groups, carboxylate and carboxylic acid groups, esters, anhydrides, and the like. The modifying molecules may be bound to the surface of the graphene sheets covalently, ionically, via hydrogen bonding, electrostatically, via physical adsorption, and the like.


The graphene sheets can contain atomic scale kinks due to the presence of lattice defects in the honeycomb structure of the graphite basal plane. These kinks can be desirable to prevent the stacking of the single sheets back to graphite oxide and/or other graphite structures under the influence of van der Waals forces. Kinks may also be desirable for adjusting the moduli of the sheets in the composite applications where at low strains the kinks yield at low stress levels and thus provide a gradually increasing modulus (75 to 250 GPa), and at high strains moduli as high as 1 TPa may be attained. The kinks can also be desirable for mechanical interlocking in the composite structures.


The compositions can optionally further include additional polymers and/or additional additives, including stabilizers (such as thermal, oxidative, and/or UV light resistant stabilizers), nucleating agents, colorants (such as pigments, dyes, and the like), other nanofillers (such as nanoclays), other carbon-based fillers (such as carbon nanotubes, carbon black, graphite, and the like), lusterants, delusterants (e.g., titanium dioxide), lubricants, dye-adhesion promoters, and the like.


The compositions preferably include at least about 0.0001 wt % graphene sheets, based on the total weight of the graphene sheets and polymer. The graphene sheets can be present in at least about 0.005 wt %, in at least about 0.001 wt %, in at least about 0.01 wt %, in at least about 0.05 wt %, in at least about 0.1 wt %, in at least about 0.2 wt %, or in at least about 0.25 wt % (where all weight percentages are based on the total weight of the graphene sheets and polymer.


Preferred ranges in which the graphene sheets are present in the compositions include from about 0.0001 wt % to about 3 wt %, from about 0.001 wt % to about 3 wt %, from about 0.005 wt % to about 3 wt %, from about 0.01 wt % to about 3 wt %, from about 0.01 wt % to about 2 wt %, from about 0.025 wt % to about 2 wt %, from about 0.05 wt % to about 2 wt %, from about 0.05 wt % to about 1 wt %, from about 0.05 wt % to about 0.5 wt %, from about 0.1 wt % to about 1 wt %, from about 0.1 wt % to about 0.5 wt %, and from about 0.1 wt % to about 0.3 wt % (where all weight percentages are based on the total weight of the graphene sheets and polymer).


If the polymer is melt processable, the compositions can be made prior to fiber formation using any suitable melt-blending method including using a single or twin-screw extruder, a blender, a kneader, or a Banbury mixer. In one embodiment, the compositions are melt-mixed blends wherein the non-polymeric ingredients are well-dispersed in the polymer matrix, such that the blend forms a unified whole.


The compositions can be formed by preparing a suspension of graphene sheets in a liquid carrier (such as a solvent or water) and combining the suspension with the polymer prior to melt blending. The relative amounts of the suspension and polymer can be chosen such that the graphene sheets coat the surface of the polymer. The polymer can be in a ground or powdered form and the resulting mixture can be in the form of a solid or crumbly material. The carrier can be removed in whole or in part prior to melt blending.


The compositions can also be formed by dry blending polymer and a master batch containing polymer and graphene sheets prior to melt spinning. In such a method, the master batch preferably comprises up to about 50 wt % graphene sheets, or more preferably from about 2 wt % to about 20 wt % graphene, based on the total weight of the master batch.


The compositions can also be made by combining graphene sheets (and optionally, additional components) with monomers that are polymerized to form the polymer.


The fibers can be formed by any suitable method such as, for example, extrusion, melt spinning, solvent (wet) spinning, dry spinning, gel spinning, reaction spinning, electrospinning, and the like. For example, when spinning, suitable nozzles (such as spinnerettes) may be selected to form monofilament or multifilament fibers.


When melt spinning, a quench zone can be used for the solidification of the filaments. Examples of quench zones include cross-flow, radial, horizontal, water bath, and other cooling systems. A quench delay zone that may be heat or unheated can be used. Temperature control may be done using any suitable medium, such as a liquid (e.g. water), a gas (e.g. air), and/or the like.


Filaments and/or yarns can be subjected to one or more drawing and/or relaxation operations during and/or subsequent to the spinning process. Drawing and/or relaxation processes can be combined with the spinning processes (such as by using a spin draw process), or can be done using separate drawing equipment to pre-spun fibers in form of monofilament or multifilament yarns. The drawing process can be done, for example, by using different speed single or duo godets or rolls, with heating (hot drawing), without heating (cold drawing), or both. The draw ratio can be controlled by heating and/or annealing during the quench delay zone. Heating can be achieved using heated godets, one or more hot boxes, etc. Relaxation can be done with heating (hot drawing), without heating (cold drawing), or both.


The spinning speed, spinline tension, spinline temperature, number of drawing stages, draw ratio, relaxation ratio, speed ratios between each relaxation and drawing step, and other parameters can vary. The parameters of the drawing and/or relaxation processes can be selected according to the polymer or polymers used, the polymer structures, processability requirements, and/or desired physical and/or chemical properties of the fibers and/or filaments.


Spinning and/or drawing processes can affect one or more of the degree of crystallization, crystallization rates, crystal structure and size, crystalline orientation, amorphous orientation, and the like. Filament and yarn properties (such as tensile modulus and strength) may vary as a function of spinning and/or drawing processes. In certain cases it is possible that the functionalized graphene sheets increase orientation and crystallization of the polymer structure during the spinning processes.


A spin finish oil may optionally be applied to the filament after quenching, but before any drawing and/or relaxation steps. A finish oil may also be optionally applied to fibers before or during subsequent processes such as twisting, weaving, dipping, and the like.


The fibers can be electrically conductive, meaning that they may have a conductivity of at least about 10−6 S/m. In some embodiments, the fibers preferably have a conductivity of about 10−6 S/m to about 105 S/m, or more preferably of about 10−5 S/m to about 105 S/m. In other embodiments, the fibers have a conductivity of at least about 100 S/m, or at least about 1000 S/m, or at least about 104 S/m, or at least about 105 S/m, or at least about 106 S/m.


The fibers can be formed into fabrics that comprise at least one fiber of the present invention. The fibers can also be formed into yarns that comprise at least one fiber of the present invention. The yarns can be in the form of filament yarns, spun yarns, and the like. The yarns can additionally be formed into cords that comprise at least one yarn of the present invention.


The fibers, yarns, and/or cords can be formed into fabrics having enhanced tensile properties and strengths and tenacities. The fabrics can be woven fabrics, non-woven fabrics (including spunbonded, spunlaid, spun laced, etc. fabrics), knit fabrics, and the like and can include additional components such as, for example, fibers, yarns, and/or cords other than those comprising polymer and graphene. The fibers can also be formed into microfiber fabrics.


Spunbonded (also referred to as spunlaid) non-woven fabrics can be made by depositing spun fibers onto a moving perforated belt. The deposited fibers can subsequently be melt bonded, mechanically interlocked, joined with an adhesive, etc. Examples of uses for non-woven fabrics include, but are not limited to, hygienic fabrics, medical fabrics, cleaning fabrics, filters, cleaning cloths, geotextiles, carpet backings, and the like.


The fibers, yarns, cords, and fabrics can be incorporated into larger articles such as, for example, other polymeric and ceramic articles. The fibers can be fully or partially encapsulated by, or coated with, other materials (such as polymeric materials) or can be wound around, or bonded to other articles. The fibers can be part of multi-layer or multi-ply structures, including, for example, tubular structures such as pipes and tubes, and can be formed such that the composition described herein forms one or more layers including exterior layers, core layers, interior layers, and the like. For example, the fiber can be a multilayered fiber in which the outermost and/or innermost and/or in-between layer comprises the composition described herein.


The fibers can be used in a variety of applications including, but not limited to: textile fibers and yarns, reinforcing fibers, yarns and materials, geotextiles, carpet fibers and yarns, carpet backings, structural and architectural fibers and yarns (such as those used in roofs and membrane roofs), concrete reinforcing materials, composite reinforcing materials, bristles for brushes (such as paint brushes and tooth brushes), fishing lines, ropes, cables, cordage, marine cables, mooring cables, boat rigging lines, hawsers, bow strings, tow lines, climbing ropes and equipment, space tethers, coated fabrics, hygienic fabrics, medical fabrics, cleaning fabrics, clothing and garment fabrics, protective apparel (such as fire fighter protective equipment, astronaut space suits, ballistic vests, helmets, heat and splash protection equipment, etc.), thermal liners, filters and filtration fabrics, flags, sails, awnings, upholstery (including furniture upholstery), carpets and floor coverings, air bags, seat belts, parachutes and parachute lines, kites and kite lines, air balloons (including weather balloons), fire hoses, air hoses, reinforcing agents for materials transport, water sacks for aerial fire fighting aircraft, tenting, tarpaulins, sleeping bags, tapes, belts, netting (including safety nets and anti-erosion nets), racket strings, strapping materials, strips, sheets, packaging, etc.


The fibers, yarns, cords, and fabrics described herein can be incorporated in spun over-pressure vessels, pipes and tubes, body armor, vehicle armor, automotive body panels and other components, protective cockpits for automobile and airplane operators, boat hulls, umbilical cables (such as those used in oil and gas exploration and extraction), skis and snowboards, safety glass, etc.


EXAMPLES
Example 1

Graphene sheets are added to poly(ethylene terephthalate) (PET) by melt compounding in an extruder to yield a PET composition comprising about 0.25 weight percent graphene sheets. The PET composition is then solid phase polymerized at 215° C. to an IV of about 1 dL/g. The composition is spun into monofilaments that are then post drawn to a draw ratio of about 4 to 5. After drawing, the filaments have a diameter of about 120 microns. The storage modulus of the monofilaments is then measured as a function of temperature using a dynamic mechanical analyzer (DMA). The results are given in Table 1 and in FIG. 1.


Comparative Example 1

The storage modulus of commercial PET monofilaments having an IV of about 0.6 to 0.8 dL/g and a diameter of about 250 microns is measured using a DMA. The commercial PET and the PET of Example 1 have similar tenacities The results are given in Table 1 and FIG. 1.












TABLE 1








Comparative



Example 1
Ex. 1





















Storage
 32° C.
17.7
8.83



modulus
 52° C.
22.9
8.99



(GPa)
 70° C.
21.8
9.13




 90° C.
20.7
9.00




110° C.
19.0
7.85




130° C.
16.3
5.21




150° C.
14.0
3.34




170° C.
11.2
2.56




190° C.
9.82
2.49




210° C.
8.89
2.45









Claims
  • 1. A fiber comprising: a composition including a polymer and graphene sheets.
  • 2. The fiber of claim 1, wherein the fiber is a staple fiber.
  • 3. The fiber of claim 1, wherein the fiber is a monofilament fiber.
  • 4. The fiber of claim 1, wherein the fiber is a multifilament fiber.
  • 5. The fiber of claim 1, wherein the polymer is one or more polymers selected from the group consisting of cellulosic polymers, polyamides, polyesters, polyolefins, aramids, and rayon.
  • 6. The fiber of claim 5, wherein the polymer is a polyamide.
  • 7. The fiber of claim 6, wherein the polyamide is one or more of polyamide 6,6; polyamide 6; and polyamide 6,6/polyamide 6 copolymers.
  • 8. The fiber of claim 5, wherein the polymer is a polyester.
  • 9. The fiber of claim 8, wherein the polyester is one or more of poly(ethylene terephthalate); poly(ethylene naphthalate); and poly(ethylene terephthalate)/poly(ethylene naphthalate) copolymers.
  • 10. The fiber of claim 5, wherein the polymer is an aramid.
  • 11. The fiber of claim 5, wherein the polymer is rayon.
  • 12. The fiber of claim 1, wherein the composition comprises at least about 0.0001 wt % graphene sheets, based on the total weight of graphene sheets and polymer.
  • 13. The fiber of claim 1, wherein the composition comprises about 0.001 wt % to about 3 wt % graphene sheets, based on the total weight of graphene sheets and polymer.
  • 14. The fiber of claim 1, wherein the composition comprises about 0.05 wt % to about 2 wt % graphene sheets, based on the total weight of graphene sheets and polymer.
  • 15. The fiber of claim 1, wherein the graphene sheets have a surface area of about 100 m2/g to about 2,630 m2/g.
  • 16. The fiber of claim 1, wherein the graphene sheets have a surface area of about 300 m2/g to about 2,630 m2/g.
  • 17. The fiber of claim 1, wherein the graphene sheets have a carbon to oxygen molar ratio of at least about 10 to 1.
  • 18. The fiber of claim 1, wherein the graphene sheets have a carbon to oxygen molar ratio of at least about 20 to 1.
  • 19. The fiber of claim 1, wherein the graphene sheets have a carbon to oxygen molar ratio of at least about 50 to 1.
  • 20. The fiber of claim 1, wherein the graphene sheets have a carbon to oxygen molar ratio of at least about 100 to 1.
  • 21. A yarn comprising the fiber of claim 1.
  • 22. A cord comprising the yarn of claim 21.
  • 23. A fabric comprising the fiber of claim 1.
  • 24. A fabric comprising the yarn of claim 21.
  • 25. A fabric comprising the cord of claim 22.
  • 26. The fiber of claim 1, in the form of a textile fiber, reinforcing fiber, carpet fiber, structural or architectural fiber, bush bristle, fishing line, a boat rigging line, or a rope.
  • 27. The yarn of claim 21, in the form of a textile yarn, reinforcing yarn, carpet yarn, boat rigging line, or rope.
  • 28. The fabric of claim 23, in the form of a clothing or garment fabric, a flag, a sail, an awning, an air bag, a seat belt, a parachute, a tarpaulin, a tape, a belt, or a strapping material.
  • 29. The fiber of claim 1, having an average diameter of about 1 μm to about 1.5 mm.
  • 30. The fiber of claim 1, having an average diameter of about 15 μm to about 1.5 mm.
  • 31. A method of forming a fiber, comprising the steps of: forming a composition of graphene sheets and polymer, and spinning the composition into a fiber.
  • 32. The method of claim 31, wherein the spinning is melt spinning.
  • 33. The method of claim 31, further comprising: drawing and relaxing the spun fiber.
  • 34. The method of claim 31, wherein the composition is formed by melt blending the polymer and graphene sheets.
  • 35. The method of claim 31, wherein the spinning is solvent spinning, dry spinning, gel spinning, reaction spinning, or electrospinning.
  • 36. A method of forming a fiber, comprising the steps of: forming a composition of graphene sheets and polymer, andextruding the composition into a fiber.
CROSS REFERENCE TO RELATED APPLICATIONS

This application claims priority to and is a continuation of international application number PCT/US10/27439, filed Mar. 16, 2010, which claims priority to, and the benefit of U.S. Provisional Patent Application Ser. No. 61/160,585, filed on Mar. 16, 2009, entitled “Polymeric Fibers and Articles Made Therefrom”. International application number PCT/US10/27439 was published as International Publication Number WO 2010/107762 A1 on Sep. 23, 2010. The entirety of each of these patent applications is incorporated herein by reference. This application is also related to co-filed applications having Attorney Docket No. VORB-002/01 US (310917-000), entitled “Tire Cords,” and Attorney Docket No. VORB-003/01 US (310917-000), entitled “Reinforced Polymeric Articles,” the entire disclosures of which are incorporated herein by reference.

Provisional Applications (1)
Number Date Country
61160585 Mar 2009 US
Continuations (1)
Number Date Country
Parent PCT/US10/27439 Mar 2010 US
Child 13234602 US