Patent Grant
9783649
The present disclosure relates to polymeric materials that can be formed to produce a container, and in particular, polymeric materials that insulate. More particularly, the present disclosure relates to polymer-based formulations that can be formed to produce an insulated non-aromatic polymeric material.
A polymeric material in accordance with the present disclosure includes a polymeric resin and cell-forming agents. In illustrative embodiments, a blend of polymeric resins and cell-forming agents is extruded or otherwise formed to produce an insulated cellular non-aromatic polymeric material.
In illustrative embodiments, an insulative cellular non-aromatic polymeric material produced in accordance with the present disclosure can be formed to produce an insulative cup or other product. Polypropylene resin is used to form the insulative cellular non-aromatic polymeric material in illustrative embodiments.
In illustrative embodiments, an insulative cellular non-aromatic polymeric material comprises a polypropylene base resin having a high melt strength, a polypropylene copolymer or homopolymer (or both), and cell-forming agents including at least one nucleating agent and a blowing agent such as carbon dioxide. In illustrative embodiments, the insulative cellular non-aromatic polymeric material further comprises a slip agent. The polypropylene base resin has a broadly distributed unimodal (not bimodal) molecular weight distribution.
In illustrative embodiments, a polypropylene-based formulation in accordance with the present disclosure is heated and extruded in two stages to produce a tubular extrudate (in an extrusion process) that can be sliced to provide a strip of insulative cellular non-aromatic polymeric material. A blowing agent in the form of an inert gas is introduced into a molten resin in the first extrusion stage in illustrative embodiments.
In illustrative embodiments, an insulative cup is formed using the strip of insulative cellular non-aromatic polymeric material. The insulative cup includes a body having a sleeve-shaped side wall and a floor coupled to the body to cooperate with the side wall to form an interior region for storing food, liquid, or any suitable product. The body also includes a rolled brim coupled to an upper end of the side wall and a floor mount coupled to a lower end of the side wall and to the floor.
The insulative cellular non-aromatic polymeric material is configured in accordance with the present disclosure to provide means for enabling localized plastic deformation in at least one selected region of the body (e.g., the side wall, the rolled brim, the floor mount, and a floor-retaining flange included in the floor mount) to provide (1) a plastically deformed first material segment having a first density in a first portion of the selected region of the body and (2) a second material segment having a relatively lower second density in an adjacent second portion of the selected region of the body. In illustrative embodiments, the first material segment is thinner than the second material segment.
Additional features of the present disclosure will become apparent to those skilled in the art upon consideration of illustrative embodiments exemplifying the best mode of carrying out the disclosure as presently perceived.
The detailed description particularly refers to the accompanying figures in which:
An insulative cellular non-aromatic polymeric material produced in accordance with the present disclosure can be formed to produce an insulative cup 10 as suggested in
A material-forming process 100 uses a polypropylene-based formulation 121 in accordance with the present disclosure to produce a strip 82 of insulative cellular non-aromatic polymeric material as shown in
Insulative cellular non-aromatic polymeric material is used to form insulative cup 10. Insulative cup 10 includes a body 11 having a sleeve-shaped side wall 18 and a floor 20 as shown in
Insulative cellular non-aromatic polymeric material is configured in accordance with the present disclosure to provide means for enabling localized plastic deformation in at least one selected region of body 11 (e.g., side wall 18, rolled brim 16, floor mount 17, and a floor-retaining flange 26 included in floor mount 17) to provide (1) a plastically deformed first material segment having a first density in a first portion of the selected region of body 11 and (2) a second material segment having a relatively lower second density in an adjacent second portion of the selected region of body 11 as suggested, for example, in
One aspect of the present disclosure provides a formulation for manufacturing an insulative cellular non-aromatic polymeric material. As referred to herein, an insulative cellular non-aromatic polymeric material refers to an extruded structure having cells formed therein and has desirable insulative properties at given thicknesses. Another aspect of the present disclosure provides a resin material for manufacturing an extruded structure of insulative cellular non-aromatic polymeric material. Still another aspect of the present disclosure provides an extrudate comprising an insulative cellular non-aromatic polymeric material. Yet another aspect of the present disclosure provides a structure of material formed from an insulative cellular non-aromatic polymeric material. A further aspect of the present disclosure provides a container formed from an insulative cellular non-aromatic polymeric material.
In exemplary embodiments, a formulation includes at least one polymeric material. In one exemplary embodiment a primary or base polymer comprises a high melt strength polypropylene that has long chain branching. Long chain branching occurs by the replacement of a substituent, e.g., a hydrogen atom, on a monomer subunit, by another covalently bonded chain of that polymer, or, in the case of a graft copolymer, by a chain of another type. For example, chain transfer reactions during polymerization could cause branching of the polymer. Long chain branching is branching with side polymer chain lengths longer than the average critical entanglement distance of a linear polymer chain. Long chain branching is generally understood to include polymer chains with at least 20 carbon atoms depending on specific monomer structure used for polymerization. Another example of branching is by crosslinking of the polymer after polymerization is complete. Some long chain branch polymers are formed without crosslinking. Polymer chain branching can have a significant impact on material properties. Final selection of a polypropylene material may take into account the properties of the end material, the additional materials needed during formulation, as well as the conditions during the extrusion process. In exemplary embodiments high melt strength polypropylenes may be materials that can hold a gas (as discussed hereinbelow), produce desirable cell size, have desirable surface smoothness, and have an acceptable odor level (if any).
One illustrative example of a suitable polypropylene base resin is DAPLOY™ WB140 homopolymer (available from Borealis A/S), a high melt strength structural isomeric modified polypropylene homopolymer (melt strength=36, as tested per ISO 16790 which is incorporated by reference herein, melting temperature=325.4° F. (163° C.) using ISO 11357, which is incorporated by reference herein).
Borealis DAPLOY™ WB140 properties (as described in a Borealis product brochure):
Other polypropylene polymers having suitable melt strength, branching, and melting temperature may also be used. Several base resins may be used and mixed together.
In certain exemplary embodiments, a secondary polymer may be used with the base polymer. The secondary polymer may be, for example, a polymer with sufficient crystallinity. In exemplary embodiments the secondary polymer may be at least one crystalline polypropylene homopolymer, an impact copolymer, mixtures thereof or the like. One illustrative example is a high crystalline polypropylene homopolymer, available as F020HC from Braskem. Another illustrative example is a polymer commercially available as PRO-FAX SC204™ (available from LyndellBasell Industries Holdings, B.V.). Another illustrative example include is Homo PP-INSPIRE 222, available from Braskem. In one aspect the polypropylene may have a high degree of crystallinity, i.e., the content of the crystalline phase exceeds 51% (as tested using differential scanning calorimetry) at 10° C./min cooling rate. In exemplary embodiments several different secondary polymers may be used and mixed together.
In exemplary embodiments, the secondary polymer may be or may include polyethylene. In exemplary embodiments, the secondary polymer may include low density polyethylene, linear low density polyethylene, high density polyethylene, ethylene-vinyl acetate copolymers, ethylene-ethylacrylate copolymers, ethylene-acrylic acid copolymers, mixtures of at least two of the foregoing and the like. The use of non-polypropylene materials may affect recyclability, insulation, microwavability, impact resistance, or other properties, as discussed further hereinbelow.
One or more nucleating agents are used to provide and control nucleation sites to promote formation of cells, bubbles, or voids in the molten resin during the extrusion process. Nucleating agent means a chemical or physical material that provides sites for cells to form in a molten resin mixture. Nucleating agents may be physical agents or chemical agents. Suitable physical nucleating agents have desirable particle size, aspect ratio, and top-cut properties. Examples include, but are not limited to, talc, CaCO3, mica, and mixtures of at least two of the foregoing. The nucleating agent may be blended with the polymer resin formulation that is introduced into the hopper. Alternatively, the nucleating agent may be added to the molten resin mixture in the extruder. When the chemical reaction temperature is reached the nucleating agent acts to enable formation of bubbles that create cells in the molten resin. An illustrative example of a chemical blowing agent is citric acid or a citric acid-based material. After decomposition, the chemical blowing agent forms small gas cells which further serve as nucleation sites for larger cell growth from a physical or other types of blowing agents. One representative example is Hydrocerol™ CF-40E™ (available from Clariant Corporation), which contains citric acid and a crystal nucleating agent. In illustrative embodiments one or more catalysts or other reactants may be added to accelerate or facilitate the formation of cells.
In certain exemplary embodiments, one or more blowing agents may be incorporated. Blowing agent means a physical or a chemical material (or combination of materials) that acts to expand nucleation sites. Nucleating agents and blowing agents may work together. The blowing agent acts to reduce density by forming cells in the molten resin. The blowing agent may be added to the molten resin mixture in the extruder. Representative examples of physical blowing agents include, but are not limited to, carbon dioxide, nitrogen, helium, argon, air, pentane, butane, or other alkane mixtures of the foregoing and the like. In certain exemplary embodiments, a processing aid may be employed that enhances the solubility of the physical blowing agent. Alternatively, the physical blowing agent may be a hydrofluorocarbon, such as 1,1,1,2-tetrafluoroethane, also known as R134a, or other haloalkane refrigerant. Selection of the blowing agent may be made to take environmental impact into consideration.
In exemplary embodiments, physical blowing agents are typically gases that are introduced as liquids under pressure into the molten resin via a port in the extruder as suggested in
Chemical blowing agents are materials that degrade or react to produce a gas. Chemical blowing agents may be endothermic or exothermic. Chemical blowing agents typically degrade at a certain temperature to decompose and release gas. In one aspect the chemical blowing agent may be one or more materials selected from the group consisting of azodicarbonamide; azodiisobutyro-nitrile; benzenesulfonhydrazide; 4,4-oxybenzene sulfonylsemicarbazide; p-toluene sulfonyl semi-carbazide; barium azodicarboxylate; N,N′-dimethyl-N,N′-dinitrosoterephthalamide; trihydrazino triazine; methane; ethane; propane; n-butane; isobutane; n-pentane; isopentane; neopentane; methyl fluoride; perfluoromethane; ethyl fluoride; 1,1-difluoroethane; 1,1,1-trifluoroethane; 1,1,1,2-tetrafluoro-ethane; pentafluoroethane; perfluoroethane; 2,2-difluoropropane; 1,1,1-trifluoropropane; perfluoropropane; perfluorobutane; perfluorocyclobutane; methyl chloride; methylene chloride; ethyl chloride; 1,1,1-trichloroethane; 1,1-dichloro-1-fluoroethane; 1-chloro-1,1-difluoroethane; 1,1-dichloro-2,2,2-trifluoroethane; 1-chloro-1,2,2,2-tetrafluoroethane; trichloromonofluoromethane; dichlorodifluoromethane; trichlorotrifluoroethane; dichlorotetrafluoroethane; chloroheptafluoropropane; dichlorohexafluoropropane; methanol; ethanol; n-propanol; isopropanol; sodium bicarbonate; sodium carbonate; ammonium bicarbonate; ammonium carbonate; ammonium nitrite; N,N′-dimethyl-N,N′-dinitrosoterephthalamide; N,N′-dinitrosopentamethylene tetramine; azodicarbonamide; azobisisobutylonitrile; azocyclohexylnitrile; azodiaminobenzene; bariumazodicarboxylate; benzene sulfonyl hydrazide; toluene sulfonyl hydrazide; p,p′-oxybis(benzene sulfonyl hydrazide); diphenyl sulfone-3,3′-disulfonyl hydrazide; calcium azide; 4,4′-diphenyl disulfonyl azide; and p-toluene sulfonyl azide.
In one aspect of the present disclosure, where a chemical blowing agent is used, the chemical blowing agent may be introduced into the resin formulation that is added to the hopper.
In one aspect of the present disclosure, the blowing agent may be a decomposable material that forms a gas upon decomposition. A representative example of such a material is citric acid or a citric-acid based material. In one exemplary aspect of the present disclosure it may be possible to use a mixture of physical and chemical blowing agents.
In one aspect of the present disclosure, at least one slip agent may be incorporated into the resin mixture to aid in increasing production rates. Slip agent (also known as a process aid) is a term used to describe a general class of materials which are added to a resin mixture and provide surface lubrication to the polymer during and after conversion. Slip agents may also reduce or eliminate die drool. Representative examples of slip agent materials include amides of fats or fatty acids, such as, but not limited to, erucamide and oleamide. In one exemplary aspect, amides from oleyl (single unsaturated C-18) through erucyl (C-22 single unsaturated) may be used. Other representative examples of slip agent materials include low molecular weight amides and fluoroelastomers. Combinations of two or more slip agents can be used. Slip agents may be provided in a master batch pellet form and blended with the resin formulation.
One or more additional components and additives optionally may be incorporated, such as, but not limited to, impact modifiers, colorants (such as, but not limited to, titanium dioxide), and compound regrind.
The polymer resins may be blended with any additional desired components and melted to form a resin formulation mixture.
In addition to surface topography and morphology, another factor that was found to be beneficial to obtain a high quality insulative cup free of creases was the anisotropy of the insulative cellular non-aromatic polymeric strip. Aspect ratio is the ratio of the major axis to the minor axis of the cell. As confirmed by microscopy, in one exemplary embodiment the average cell dimensions in a machine direction 67 (machine or along the web direction) of an extruded strip 82 of insulative cellular non-aromatic polymeric material was about 0.0362 inches (0.92 mm) in width by about 0.0106 inches (0.27 mm) in height. As a result, a machine direction cell size aspect ratio is about 3.5. The average cell dimensions in a cross direction (cross-web or transverse direction) was about 0.0205 inches (0.52 mm) in width and about 0.0106 inches (0.27 mm) in height. As a result, a cross-direction aspect ratio is 1.94. In one exemplary embodiment, it was found that for the strip to withstand compressive force during cup forming, one desirable average aspect ratio of the cells was between about 1.0 and about 3.0. In one exemplary embodiment one desirable average aspect ratio of the cells was between about 1.0 and about 2.0.
The ratio of machine direction to cross direction cell length is used as a measure of anisotropy of the extruded strip. In exemplary embodiments, a strip of insulative cellular non-aromatic polymeric material may be bi-axially oriented, with a coefficient of anisotropy ranging between about 1.5 and about 3. In one exemplary embodiment, the coefficient of anisotropy was about 1.8.
If the circumference of the cup is aligned with machine direction 67 of extruded strip 82 with a cell aspect ratio exceeding about 3.0, deep creases with depth exceeding about 200 microns are typically formed on inside surface of the cup making it unusable. Unexpectedly, it was found, in one exemplary embodiment, that if the circumference of the cup was aligned in the cross direction of extruded strip 82, which can be characterized by cell aspect ratio below about 2.0, no deep creases were formed inside of the cup, indicating that the cross direction of extruded strip 82 was more resistant to compression forces during cup formation.
One possible reason for greater compressibility of an extruded strip with cells having aspect ratio below about 2.0 in the direction of cup circumference, such as in the cross direction, could be due to lower stress concentration for cells with a larger radius. Another possible reason may be that the higher aspect ratio of cells might mean a higher slenderness ratio of the cell wall, which is inversely proportional to buckling strength. Folding of the strip into wrinkles in the compression mode could be approximated as buckling of cell walls. For cell walls with longer length, the slenderness ratio (length to diameter) may be higher. Yet another possible factor in relieving compression stress might be a more favorable polymer chain packing in cell walls in the cross direction allowing polymer chain re-arrangements under compression force. Polymer chains are expected to be preferably oriented and more tightly packed in machine direction 67.
In exemplary embodiments, the combination of alignment of the formed cup circumference along the direction of the extruded strip where cell aspect ratio is below about 2.0. As a result, the surface of extruded strip with crystal domain size below about 100 angstroms facing inside the cup may provide favorable results of achieving a desirable surface topography with imperfections less than about 5 microns deep.
In one aspect of the present disclosure, the polypropylene resin (either the base or the combined base and secondary resin) may have a density in a range of about 0.01 g/cm3 to about 0.19 g/cm3. In one exemplary embodiment, the density may be in a range of about 0.05 g/cm3 to about 0.19 g/cm3. In one exemplary embodiment, the density may be in a range of about 0.1 g/cm3 to about 0.185 g/cm3.
In an alternative exemplary embodiment, instead of polypropylene as the primary polymer, a polylactic acid material may be used, such as, but not limited to, a polyactic acid material derived from a food-based material, for example, corn starch. In one exemplary embodiment, polyethylene may be used as the primary polymer.
In one exemplary aspect of the present disclosure, one formulation for a material useful in the formation of an insulative cellular non-aromatic polymeric material includes the following: at least one primary resin comprising a high melt strength long chain branched polypropylene, at least one secondary resin comprising a high crystalline polypropylene homopolymer or an impact copolymer, at least one nucleating agent, at least one blowing agent, and at least one slip agent. Optionally, a colorant may be incorporated.
The formulation may be introduced into an extruder via a hopper, such as that shown in
In another exemplary embodiment, the formulation may contain both at least one chemical blowing agent and at least one physical blowing agent.
Cups or other containers or structures may be formed from the sheet according to conventional apparatus and methods.
For the purposes of non-limiting illustration only, formation of a cup from an exemplary embodiment of a material disclosed herein will be described; however, the container may be in any of a variety of possible shapes or structures or for a variety of applications, such as, but not limited to, a conventional beverage cup, storage container, bottle, or the like. For the purpose of nonlimiting illustration only, a liquid beverage will be used as the material which can be contained by the container; however, the container may hold liquids, solids, gels, combinations thereof, or other material.
A material-forming process 100 is shown, for example, in
As shown in
Extrusion resin mixture 103 is conveyed by screw 114 into a second extrusion zone included in second extruder 112 as shown in
Extrudate means the material that exits an extrusion die. The extrudate material may be in a form such as, but not limited to, a sheet, strip, tube, thread, pellet, granule or other structure that is the result of extrusion of a polymer-based formulation as described herein through an extruder die. For the purposes of illustration only, a sheet will be referred to as a representative extrudate structure that may be formed, but is intended to include the structures discussed herein. The extrudate may be further formed into any of a variety of final products, such as, but not limited to, cups, containers, trays, wraps, wound rolls of strips of insulative cellular non-aromatic polymeric material, or the like.
As an example, strip 82 of insulative cellular non-aromatic polymeric material is wound to form a roll of insulative cellular non-aromatic polymeric material and stored for later use either in a cup-forming process. However, it is within the scope of the present disclosure for strip 82 of insulative cellular non-aromatic polymeric material to be used in-line with the cup-forming process. In one illustrative example, strip 82 of insulative cellular non-aromatic polymeric material is laminated with a skin having a film and an ink layer printed on the film to provide high-quality graphics.
An insulative cup 10 is formed using a strip 82 of insulative cellular non-aromatic polymeric material as shown in
Body 11 is formed from a strip 82 of insulative cellular non-aromatic polymeric material as disclosed herein. In accordance with the present disclosure, strip 82 of insulative cellular non-aromatic polymeric material is configured through application of pressure and heat (though in exemplary embodiments configuration may be without application of heat) to provide means for enabling localized plastic deformation in at least one selected region of body 11 to provide a plastically deformed first sheet segment having a first density located in a first portion of the selected region of body 11 and a second sheet segment having a second density lower than the first density located in an adjacent second portion of the selected region of body 11 without fracturing the sheet of insulative cellular non-aromatic polymeric material so that a predetermined insulative characteristic is maintained in body 11.
A first 101 of the selected regions of body 11 in which localized plastic deformation is enabled by the insulative cellular non-aromatic polymeric material is in sleeve-shaped side wall 18 as suggested in
A second 102 of the selected regions of body 11 in which localized plastic deformation is enabled by the sheet of insulative cellular non-aromatic polymeric material is in rolled brim 16 included in body 11 as suggested in
A third 103 of the selected regions of body 11 in which localized plastic deformation is enabled by the sheet of insulative cellular non-aromatic polymeric material is in a floor mount included in body 11 as suggested in
A fourth 104 of the selected regions of body 11 in which localized plastic deformation is enabled by the sheet of insulative cellular non-aromatic polymeric material is in floor-retaining flange of floor mount 17 as suggested in
The compressibility of the insulative cellular non-aromatic polymeric material used to produce insulative cup 10 allows the insulative cellular non-aromatic polymeric material to be prepared for the mechanical assembly of insulative cup 10, without limitations experienced by other non-aromatic polymeric materials. The cellular nature of the material provides insulative characteristics as discussed below, while susceptibility to plastic deformation permits yielding of the material without fracture. The plastic deformation experienced when the insulative cellular non-aromatic polymeric material is subjected to a pressure load is used to form a permanent set in the insulative cellular non-aromatic polymeric material after the pressure load has been removed. In some locations, the locations of permanent set are positioned to provide controlled gathering of the sheet of insulative cellular non-aromatic polymeric material.
The plastic deformation may also be used to create fold lines in the sheet to control deformation of the sheet when being worked during the assembly process. When deformation is present, the absence of material in the voids formed by the deformation provides relief to allow the material to be easily folded at the locations of deformation.
A potential unexpected feature of the sheet of insulative cellular non-aromatic polymeric material formed as described herein is the high insulation value obtained at a given thickness. See, for example, Examples 1 and 2 below.
A potential feature of a cup formed of insulative cellular non-aromatic polymeric material according to exemplary embodiments of the present disclosure is that the cup has low material loss. Furthermore, the material of the present disclosure may have markedly low off-gassing when subjected to heat from a conventional kitchen-type microwave oven for periods of time up to several minutes.
Another potential feature of a cup formed of the insulative cellular non-aromatic polymeric material according to the present disclosure is that the cup can be placed in and go through a conventional residential or commercial dishwasher cleaning cycle (top rack) without noticeable structural or material breakdown or adverse affect on material properties. This is in comparison to beaded expanded polystyrene cups or containers which can break down under similar cleaning processes. Accordingly, a cup made according to one aspect of the present disclosure can be cleaned and reused.
Another potential feature of an article formed of the insulative cellular non-aromatic polymeric material according to various aspects of the present disclosure is that the article can be recycled. Recyclable means that a material can be added (such as regrind) back into an extrusion or other formation process without segregation of components of the material, i.e., an article formed of the material does not have to be manipulated to remove one or more materials or components prior to re-entering the extrusion process. For example, a cup having a printed film layer laminated to the exterior of the cup may be recyclable if one does not need to separate out the film layer prior to the cup being ground into particles. In contrast, a paper-wrapped expanded polystyrene cup may not be recyclable because the polystyrene material could not practicably be used as material in forming an expanded polystyrene cup, even though the cup material may possibly be formed into another product. As a further example, a cup formed from a non-expanded polystyrene material having a layer of non-styrene printed film adhered thereto may be considered non-recyclable because it would require the segregation of the polystyrene cup material from the non-styrene film layer, which would not be desirable to introduce as part of the regrind into the extrusion process.
Recyclability of articles formed from the insulative cellular non-aromatic polymeric material of the present disclosure minimizes the amount of disposable waste created. In comparison, beaded expanded polystyrene cups that break up into beads and thus ordinarily cannot easily be reused in a manufacturing process with the same material from which the article was formed. And, paper cups that typically have an extrusion coated plastic layer or a plastic lamination for liquid resistance ordinarily cannot be recycled because the different materials (paper, adhesive, film, plastic) normally cannot be practicably separated in commercial recycling operations.
A potential feature of a cup or other article formed of material according to one aspect (a non-laminate process) of the present disclosure is that the outside (or inside or both) wall surface of the insulative cellular non-aromatic polypropylene sheet (prior to being formed into a cup, or during cup formation, depending on the manufacturing process employed) can accept printing of high-resolution graphics. Conventional beaded expanded polystyrene cups have a surface which typically is not smooth enough to accept printing other than low-resolution graphics. Similarly, known uncoated paper cups also typically do not have a smooth enough surface for such high-resolution graphics. Paper cups can be coated to have the desired surface finish and can achieve high resolution. Paper has difficulty reaching insulation levels and requires a designed air gap incorporated into or associated with the cup to achieve insulation, such as a sleeve slid onto and over a portion of the cup. Accordingly, solutions have been to use low-resolution printing, laminate to the outside wall a film which has been printed, or to have a printed sleeve (either bonded or removable) inserted over the outside wall or coat the paper to accept high resolution graphics.
A potential feature of a cup formed of the insulative cellular non-aromatic polymeric material according to one aspect of the present disclosure is that it possesses unexpected strength as measured by rigidity. Rigidity is a measurement done at room temperature and at an elevated temperature (e.g., by filling the cup with a hot liquid) and measuring the rigidity of the material. The strength of the cup material is important to reduce the potential for the cup being deformed by a user and the lid popping off or the lid or sidewall seal leaking.
A potential feature of a cup formed of the insulative cellular non-aromatic polymeric material according to the present disclosure is that the sleeve is resistant to puncture, such as by a straw, fork, spoon, finger nail, or the like, as measured by standard impact testing, as described hereinbelow. Test materials demonstrated substantially higher impact resistance when compared to a beaded expanded polystyrene cup. Accordingly, a cup formed one aspect as described herein can reduce the likelihood of puncture and leakage of hot liquid onto a user.
A feature of a cup with a compressed brim and seam formed of the material according to one aspect as described herein is that a greater number of such cups can be nested in a given sleeve length because the seam is thinner and the side wall angle can be minimized (i.e., more approaching 90° with respect to the cup bottom) while providing a sufficient air gap to permit easy de-nesting. Conventionally seam-formed cups having a seam substantially thicker than the side wall requires a greater side wall angle (and air gap) to allow for de-nesting, resulting in fewer cups being able to be nested in a given sleeve length.
A feature of a cup formed of the material according to one aspect of the present disclosure is that the brim may have a cross-section profile of less than about 0.170 inches (4.318 mm) which may be due to localized cell deformation and compression. Such a small profile is more aesthetically pleasing than a larger profile.
A feature of a cup formed of the material according to one aspect of the present disclosure is that the rolled brim diameter can be the same for cups of different volumes, enabling one lid size to be used for different cup sizes, assuming the cup rims outside diameters are the same. As a result, the number of different size lids in inventory and at the point of use may be reduced.
The material formulation may have properties that allow the sheet to be compressed without fracturing.
The insulative cellular non-aromatic polymeric material of the present disclosure may be formed into a strip which can be wrapped around other structures. For example, a strip of the material according to one aspect of the present disclosure that can be used as a wrapping material may be formed and wrapped around a pipe, conduit, or other structure to provide improved insulation. The sheet or strip may have a layer of adhesive, such as a pressure sensitive adhesive, applied to one or both faces. The strip may be wound onto a roll. Optionally, the strip may have a release liner associated therewith to make unwinding the strip from the roll easier. The polymer formulation may be adapted to provide the requisite flexibility to form a wrap or windable strip, for example, by using one or more polypropylene or other polyolefin materials that have sufficient flexibility to enable the extruded sheet to be flexible enough to be wound onto a roll. The insulative cellular non-aromatic polymeric material may be formed into a sleeve that can be inserted over a cup to provide additional insulation.
In exemplary embodiments sheets formed from the insulative cellular non-aromatic polymeric material of the present disclosure may be cut at the die or be flaked and used as a bulk insulator.
The formulation and insulative cellular non-aromatic polymeric material of the present disclosure satisfies a long-felt need for a material that can be formed into an article, such as a cup, that includes many if not all of the features of insulative performance, ready for recyclability, puncture resistance, frangibility resistance, microwavability and other features as discussed herein. Others have failed to provide a material that achieves combinations of these features as reflected in the appended claims. This failure is a result of the features being associated with competitive design choices. As an example, others have created materials and structures therefrom that based on design choices are insulated but suffer from poor puncture resistance, inability to effectively be recyclable, and lack microwavability. In comparison, the formulations and materials disclosed herein overcome the failures of others by using an insulative cellular non-aromatic polymeric material. Reference is hereby made to U.S. application Ser. No. 13/491,007 filed Jun. 7, 2012 and entitled INSULATED CONTAINER for disclosure relating to articles, such as cups, formed from such insulative cellular non-aromatic polymeric materials, which application is hereby incorporated in its entirety herein.
The following examples are set forth for purposes of illustration only. Parts and percentages appearing in such examples are by weight unless otherwise stipulated. All ASTM, ISO and other standard test method cited or referred to in this disclosure are incorporated by reference in their entirety.
DAPLOY™ WB140 polypropylene homopolymer (available from Borealis A/S) was used as the polypropylene base resin. F020HC, available from Braskem, a polypropylene homopolymer resin, was used as the secondary resin. The two resins were blended with: Hydrocerol™ CF-40E™ as a primary nucleation agent, talc as a secondary nucleation agent, CO2 as a blowing agent, a slip agent, and titanium dioxide as a colorant. Percentages were:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. To this mixture was added
1.1 lbs/hr CO2
0.7 lbs/hr R134a
The carbon dioxide with R134a was injected into the resin blend to expand the resin and reduce density. The mixture thus formed was extruded through a die head into a sheet. The sheet was then cut and formed into a cup.
The test results of the material formed according to Example 1 showed the material had a density of about 0.1902 g/cm3 and a nominal sheet gauge of about 0.089 inches (2.2606 mm).
Microwavability
Containers produced using this material filled with 12 ounces of room temperature water were heated in a FISO Microwave Station (1200 Watts) microwave oven for 2.5 min without burning or scorching or other visible effect on the cup. In comparison, paper cups heated in the same microwave oven scorched or burned in less than 90 seconds.
Rigidity
Test Method
Samples were at 73° F. (22.8° C.) and 50% relative humidity. The Cup Stiffness/Rigidity test was conducted with a horizontal force gauge containing a load cell to measure the resisting force of the cup when exposed to the following test conditions: (a) The test location on the cup was ⅓ down from the rim of the cup; (b) testing travel distance is 0.25 inches (6.35 mm); and (c) testing travel time was 10 seconds.
Test Results
With an average wall thickness of about 0.064 inches (1.6256 mm), average density of about 0.1776 g/cm3, and average cup weight of about 9.86 g, the rigidity of the material are shown below in Tables 1-2.
Insulation
Test Method
A typical industrial cup insulation test method as follows was used:
Material thickness was about 0.089 inches (2.2606 mm). The density was about 0.1902 g/cm3.
Test Results
A cup formed from the formulation noted above was used having a density of about 0.190 g/cm3 and a wall thickness of about 0.089 inches. A hot liquid at 200° F. (93.3° C.) was placed in the cup.
Test Results
The temperature measured on the outside wall of the cup was about 140.5° F. (60.3° C.) resulting in drop of about 59.5° F. (33° C.). The maximum temperature over a five-minute period was observed to peak at about 140.5° F. (60.3° C.). The lower the temperature, the better the insulation property of the cup material as the material reduces the heat transferring from the liquid to the cup material exterior.
Frangibility
Frangibility can be defined as resistance to tear or punctures causing fragmentation.
Test Method
The Elmendorf test method described in ASTM D1922-93 was used. The radius of tear was 1.7 inches (43.18 mm).
Test Results
The test results are shown in Tables 3-4 below. The material as formed in one exemplary embodiment of the present disclosure provides superior resistance to tear forces when compared to EPS.
Note that there was no data obtained for the transverse direction test for expanded polystyrene because expanded polystyrene does not have a material orientation, i.e., a machine or transverse direction, due to the manufacturing process. The range (calculated as: lower range=mean−(3×std dev); upper range=mean+(3×std dev)) for the tested material of the present disclosure was about 213 grams-force to about 351 grams-force in the machine direction and about 143 grams-force to about 281 grams-force in the transverse direction. In comparison, the range of the expanded polystyrene material tested was about 103 grams-force to about 121 grams-force.
Puncture Resistance
Test Method
Determine the force and travel needed to puncture cup sidewall and bottom. An Instron instrument is used in compression mode set to 10 inches (254 mm) per minute travel speed. The cup puncture test fixture on base of Instron is used. This fixture allows the cup to fit over a shape that fits inside the cup with a top surface that is perpendicular to the travel of the Instron tester. The one inch diameter hole of the fixture should be positioned up. The portion of the Instron that moves should be fitted with a 0.300 inch (7.62 mm) diameter punch. The punch with the hole is aligned in the test fixture. The cup is placed over the fixture and the force and travel needed to puncture the cup sidewall is recorded. The sidewall puncture test is repeated in three evenly spaced locations while not puncture testing on the seam of the cup. The bottom of the cup is tested. This should be done in the same manner as the sidewall test except no fixture is used. The cup is just placed upside down on the base of the Instron while bringing the punch down on the center of the cup bottom.
Test Results
Results of the typical sidewall puncture and the bottom puncture are shown in Table 5 below.
Slow Puncture Resistance—Straw
Test Method
The material as formed in one exemplary embodiment of the present disclosure provides superior resistance to punctures when compared to expanded polystyrene using the Slow Puncture Resistance Test Method as described in ASTM D-3763-86. The test results are shown in Tables 6-9 below.
Test Results
The following formulation was used:
The formulation was added to an extruder hopper. The extruder heated the formulation to form a molten resin mixture. To this mixture was added the CO2 to expand the resin and reduce density. The mixture thus formed was extruded through a die head into a strip 82. The strip was then cut and formed into insulative cup 10.
In exemplary embodiments, a tube of extruded insulative cellular non-aromatic polymeric material has two surfaces that are formed under different cooling conditions when the material is extruded. One surface, which will be further referenced as the outside surface of extruded tube, is in contact with air, and does not have physical barriers restricting the expansion. The outside surface of extruded tube surface is cooled by blowing compressed air at cooling rate equal or higher than 12° F. per second. Surface on the opposite side will be referenced as inside of extruded tube. The inside of extruded tube surface is formed when the extruded tube is drawn in the web or machine direction on the metal cooling surface of the torpedo mandrel that is physically restricting the inside of extruded tube and is cooled by combination of water and compressed air at a cooling rate below 10° F. per second. In exemplary embodiments, the cooling water temperature is about 135° F. (57.22° C.). In exemplary embodiments, the cooling air temperature is about 85° F. (29.44° C.). As a result of different cooling mechanisms the outside surface of extruded tube and inside of extruded tube surfaces have different surface characteristics. It is known that the cooling rate and method affects the crystallization process of polypropylene altering its morphology (size of crystal domains) and topography (surface profile and smoothness).
An unexpected feature of exemplary embodiments of an extruded sheet as described herein is in the ability of the sheet to form a noticeably smooth, crease and wrinkle free surface, when curved to form a round article, such as cup. The surface is smooth and wrinkle free even inside the cup, where compression forces typically cause material to crush crease easily, especially for low density material with large cell size. In exemplary embodiments, the smoothness of the surface of an extruded sheet of insulative cellular non-aromatic polymeric material as detected by microscopy is such that the depth of the indentations (creases or wrinkles) naturally occurring in the outside and inside of the cup surface when it is subject to extension and compression forces during cup formation may be less than about 100 microns. In one exemplary embodiment, the smoothness may be less than about 50 microns. In one exemplary embodiment, the smoothness may be about 5 microns or less. At about 10 microns depth and less, the micro-wrinkles on cup surface are ordinarily not visible to the naked eye.
In one exemplary embodiment, an insulative cup formed from a sheet comprising a skin and a strip of insulative cellular non-aromatic polymeric material had typical creases (deep wrinkle) about 200 microns deep extending from the top to bottom of the cup. In one exemplary embodiment, an insulative cup formed from a sheet comprising a strip of insulative cellular non-aromatic polymeric material only (without a skin) had typical creases about 200 microns deep extending from top to bottom of the cup. Such creases with depths from about 100 microns to about 500 microns are typically formed when inside of extruded tube is facing inside of the cup in a compression mode. Creases and deep wrinkles may present a problem of unsatisfactory surface quality making final cups unusable or undesirable. Creases may form in instances where sheets include a skin or exclude a skin.
In exemplary embodiments, the insulative cellular non-aromatic polymeric material may be extruded as strip. However microscopy images show that two distinct layers exist within the extruded strip, namely, dull outside extruded tube layer and shiny inside extruded tube layer. The difference between the two layers is in reflectance of the surface due to the difference in crystal domain size. If a black marker is used to color the surface examined by microscope, reflectance is eliminated and the difference between the two surfaces may be minimal or undetectable.
In one exemplary embodiment, a sample strip was prepared without any skin. Black marker was used to eliminate any difference in reflectance between the layers. Images showed that the cell size and cell distribution was the same throughout the strip thickness. A crease of about 200 microns deep was seen as a fold in the surface where the cell wall collapsed under the compression forces.
Differential scanning calorimetry analysis conducted on a TA Instruments DSC 2910 in nitrogen atmosphere showed that with an increase in cooling rate, the crystallization temperature and crystallinity degree decreased for the polymer matrix material of the strip, as shown below in Table 10.
Differential scanning calorimetry data demonstrates the dependence of crystallization and subsequent 2nd heat melting temperature and percent crystallinity on the rate of cooling during crystallization. Exemplary embodiments of a strip of insulative cellular non-aromatic polymeric material may have the melting temperature between about 160° C. (320° F.) and about 172° C. (341.6° F.), crystallization temperature between about 108° C. (226.4° F.) and about 135° C. (275° F.), and percent crystallinity between about 42% and about 62%.
In exemplary embodiments the extruded sheet as determined by differential scanning calorimetry at 10° C. per minute heating and cooling rate had a melting temperature of about 162° C. (323.6° F.), crystallization temperature of about 131° C. (267.8° F.) and crystallinity degree of about 46%.
It was found unexpectedly that the outside extrusion tube surface works favorably in a compression mode without causing appreciable creasing and therefore a cup (or other structure) may advantageously be made with the outside extrusion tube surface facing inside of the insulative cup. The difference in the resistance of the inside extrusion tube layer and outside extrusion tube layer to compression force may be due to difference in the morphology of the layers because they were crystallized at different cooling rates.
In exemplary embodiments of formation of an extruded sheet, the inside extrusion tube surface may be cooled by combination of water cooling and compressed air. The outside extrusion tube surface may be cooled by compressed air by using torpedo with circulating water and air outlet. Faster cooling rates may result in the formation of smaller size crystals. Typically, the higher cooling rate, the greater the relative amount of smaller crystals that is formed. X-Ray diffraction analysis of an exemplary extruded sheet of insulative cellular non-aromatic polymeric material was conducted on Panalytical X'pert MPD Pro diffractometer using Cu radiation at 45 KV/40 mA. It was confirmed that the outside extrusion tube surface had a crystal domain size of about 99 angstrom, while the inside extrustion tube surface had a crystal domain size of about 114 angstrom. In exemplary embodiments, an extruded strip of insulative cellular non-aromatic polymeric material may have a crystal domain size below about 200 angstroms. In exemplary embodiments, an extruded strip of insulative cellular non-aromatic polymeric material may have a crystal domain size preferably below about 115 angstroms. In exemplary embodiments, an extruded strip of insulative cellular non-aromatic polymeric material may have a crystal domain size below about 100 angstroms.
Rigidity
Test Method
The test method is the same as described for rigidity testing in Example 1.
Test Results
The rigidity test results are shown in Table 11 below.
Insulation
Test Method—Wall Temperature
An insulative cup formed from the formulation noted above was used having a density of about 0.18 g/cm3 and a wall thickness of about 0.074 inches (1.8796 mm). A hot liquid at 200° F. (93.3° C.) was placed in the cup.
Test Results
The temperature measured on the outside wall of the cup was about 151° F. (66.1° C.) with a drop of about 49.0° F. (27.2° C.). The maximum temperature over a five-minute period was observed to peak at about 151° F. (66.1° C.).
Insulation testing in the form of thermal conductivity was done.
Test Method—Thermal Conductivity
This test measures bulk thermal conductivity (W/m-K), measured at ambient temperature and at 93° C. (199.4° F.). A ThermTest TPS 2500 S Thermal Constants Analyzer instrument was used, employing the test method of ISO/DIS 22007-2.2 and using the Low Density/High Insulating option. The TPS sensor #5501 0.2521 inch radius (6.403 mm radius) with Kapton® insulation was used for all measurements. A 20 second test was done, using 0.02 Watts power. Data using points 100-200 were reported.
Test Results
The test results shown in Table 12 below.
Although only a number of exemplary embodiments have been described in detail above, those skilled in the art will readily appreciate that many modifications are possible in the exemplary embodiments without materially departing from the novel teachings and advantages. Accordingly, all such modifications are intended to be included within the scope of this disclosure as defined in the following claims.
As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Ranges may be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another embodiment includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another embodiment. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.
“Optional” or “optionally” means that the subsequently described event or circumstance may or may not occur, and that the description includes instances where said event or circumstance occurs and instances where it does not.
Throughout the description and claims of this specification, the word “comprise” and variations of the word, such as “comprising” and “comprises,” means “including but not limited to,” and is not intended to exclude, for example, other additives, components, integers or steps. “Exemplary” means “an example of” and is not intended to convey an indication of a preferred or ideal embodiment. “Such as” is not used in a restrictive sense, but for explanatory purposes.
Disclosed are components that can be used to perform the disclosed methods, equipment, and systems. These and other components are disclosed herein, and it is understood that when combinations, subsets, interactions, groups, etc. of these components are disclosed that while specific reference of each various individual and collective combinations and permutation of these may not be explicitly disclosed, each is specifically contemplated and described herein, for all methods, equipment and systems. This applies to all aspects of this application including, but not limited to, steps in disclosed methods. Thus, if there are a variety of additional steps that can be performed it is understood that each of these additional steps can be performed with any specific embodiment or combination of embodiments of the disclosed methods.
It will be apparent to those skilled in the art that various modifications and variations can be made without departing from the scope or spirit. Other embodiments will be apparent to those skilled in the art from consideration of the specification and practice disclosed herein. It is intended that the specification and examples be considered as exemplary only.
It should further be noted that any publications and brochures referred to herein are incorporated by reference in their entirety.
This application is a continuation of U.S. application Ser. No. 14/486,618, filed Sep. 15, 2014, which is a continuation of U.S. application Ser. No. 13/491,327, filed Jun. 7, 2012, which claims priority under 35 U.S.C. §119(e) to U.S. Provisional Application Ser. No. 61/529,632, filed Aug. 31, 2011 and Ser. No. 61/618,604, filed Mar. 30, 2012, each of which is expressly incorporated by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1396282 | Penn | Oct 1920 | A |
| 1435120 | Holman | Nov 1922 | A |
| 1920529 | Sidebotham | Jul 1931 | A |
| 1969030 | Page | Dec 1931 | A |
| 2097899 | Smith | Dec 1935 | A |
| 2809776 | Barrington | Mar 1956 | A |
| 3221954 | Lux | Dec 1965 | A |
| 3227784 | Blades | Jan 1966 | A |
| 3252387 | Schur | May 1966 | A |
| 3290198 | Lux | Dec 1966 | A |
| 3312383 | Shapiro | Apr 1967 | A |
| 3327038 | Fox | Jun 1967 | A |
| 3327103 | Bonnet | Jun 1967 | A |
| 3344222 | Shapiro | Sep 1967 | A |
| 3381880 | Lewallen et al. | May 1968 | A |
| 3409204 | Carle | Nov 1968 | A |
| 3431163 | Gilbert | Mar 1969 | A |
| 3468467 | Amberg | Sep 1969 | A |
| 3547012 | Amberg | Dec 1970 | A |
| 3583624 | Peacock | Jun 1971 | A |
| 3658615 | Amberg | Apr 1972 | A |
| 3661282 | Buhayar | May 1972 | A |
| 3733381 | Willette | May 1973 | A |
| 3793283 | Frailey | Feb 1974 | A |
| 3846349 | Harada | Nov 1974 | A |
| 3907193 | Heller | Sep 1975 | A |
| 3919368 | Seto | Nov 1975 | A |
| RE28658 | MacDaniel | Dec 1975 | E |
| 3967991 | Shimano | Jul 1976 | A |
| 3969173 | Amberg | Jul 1976 | A |
| 3971696 | Manfredi | Jul 1976 | A |
| 3973721 | Nakane | Aug 1976 | A |
| 3981412 | Asmus | Sep 1976 | A |
| 4026458 | Morris | May 1977 | A |
| 4049122 | Maxwell | Sep 1977 | A |
| 4070513 | Rhoads | Jan 1978 | A |
| 4106397 | Amberg | Aug 1978 | A |
| 4171085 | Doty | Oct 1979 | A |
| 4197948 | Amberg | Apr 1980 | A |
| 4240568 | Pool | Dec 1980 | A |
| 4284226 | Herbst | Aug 1981 | A |
| 4288026 | Wilhelm | Sep 1981 | A |
| 4298331 | Mueller | Nov 1981 | A |
| 4299349 | Gilden | Nov 1981 | A |
| 4300891 | Bemiss | Nov 1981 | A |
| 4306849 | Cress | Dec 1981 | A |
| 4310369 | Miller | Jan 1982 | A |
| 4349400 | Gilden | Sep 1982 | A |
| 4365460 | Cress | Dec 1982 | A |
| 4391666 | Mueller | Jul 1983 | A |
| 4409045 | Busse | Oct 1983 | A |
| 4490130 | Konzal | Dec 1984 | A |
| 4550046 | Miller | Oct 1985 | A |
| 4579275 | Peelman | Apr 1986 | A |
| 4604324 | Nahmias | Aug 1986 | A |
| 4621763 | Brauner | Nov 1986 | A |
| 4706873 | Schulz | Nov 1987 | A |
| 4720023 | Jeff | Jan 1988 | A |
| 4856989 | Siebert | Aug 1989 | A |
| 4878970 | Schubert | Nov 1989 | A |
| 4918112 | Roox | Apr 1990 | A |
| 4940736 | Alteepping | Jul 1990 | A |
| 5078817 | Takagaki | Jan 1992 | A |
| 5116881 | Park | May 1992 | A |
| 5149579 | Park | Sep 1992 | A |
| 5158986 | Cha | Oct 1992 | A |
| 5160674 | Colton | Nov 1992 | A |
| 5180751 | Park | Jan 1993 | A |
| 5236963 | Jacoby | Aug 1993 | A |
| 5256462 | Callahan | Oct 1993 | A |
| 5286428 | Hayashi | Feb 1994 | A |
| 5308568 | Lipp | May 1994 | A |
| 5348795 | Park | Sep 1994 | A |
| 5366791 | Carr | Nov 1994 | A |
| 5385260 | Gatcomb | Jan 1995 | A |
| 5443769 | Karabedian | Aug 1995 | A |
| 5445315 | Shelby | Aug 1995 | A |
| 5490631 | Iioka | Feb 1996 | A |
| 5507640 | Gilmer | Apr 1996 | A |
| 5547124 | Mueller | Aug 1996 | A |
| 5549864 | Greene | Aug 1996 | A |
| 5605936 | DeNicola, Jr. | Feb 1997 | A |
| 5622308 | Ito | Apr 1997 | A |
| 5628453 | MacLaughlin | May 1997 | A |
| 5629076 | Fukasawa | May 1997 | A |
| 5713512 | Barrett | Feb 1998 | A |
| 5759624 | Neale | Jun 1998 | A |
| 5765710 | Bergerioux | Jun 1998 | A |
| 5766709 | Geddes | Jun 1998 | A |
| 5769311 | Morita | Jun 1998 | A |
| 5819507 | Kaneko | Oct 1998 | A |
| 5840139 | Geddes | Nov 1998 | A |
| 5866053 | Park | Feb 1999 | A |
| 5868309 | Sandstrom | Feb 1999 | A |
| 5895614 | Rivera | Apr 1999 | A |
| 5925450 | Karabedian | Jul 1999 | A |
| 5928741 | Andersen | Jul 1999 | A |
| 5944225 | Kawolics | Aug 1999 | A |
| 5948839 | Chatterjee | Sep 1999 | A |
| 6007437 | Schickert | Dec 1999 | A |
| 6010062 | Shimono | Jan 2000 | A |
| 6030476 | Geddes | Feb 2000 | A |
| 6034144 | Shioya | Mar 2000 | A |
| 6051174 | Park | Apr 2000 | A |
| 6071580 | Bland | Jun 2000 | A |
| 6083611 | Eichbauer | Jul 2000 | A |
| 6103153 | Park | Aug 2000 | A |
| 6109518 | Mueller | Aug 2000 | A |
| 6129653 | Fredricks | Oct 2000 | A |
| 6136396 | Gilmer | Oct 2000 | A |
| 6139665 | Schmelzer | Oct 2000 | A |
| 6142331 | Breining | Nov 2000 | A |
| 6169122 | Blizard | Jan 2001 | B1 |
| 6174930 | Agarwal | Jan 2001 | B1 |
| 6193098 | Mochizuki | Feb 2001 | B1 |
| 6218023 | DeNicola | Apr 2001 | B1 |
| 6231942 | Blizard | May 2001 | B1 |
| 6235380 | Tupil | May 2001 | B1 |
| 6251319 | Tusim | Jun 2001 | B1 |
| 6257485 | Sadlier | Jul 2001 | B1 |
| 6258862 | Matz | Jul 2001 | B1 |
| 6267837 | Mitchell | Jul 2001 | B1 |
| 6284810 | Burnham | Sep 2001 | B1 |
| 6294115 | Blizard | Sep 2001 | B1 |
| 6306973 | Takaoka | Oct 2001 | B1 |
| 6308883 | Schmelzer | Oct 2001 | B1 |
| 6319590 | Geddes | Nov 2001 | B1 |
| 6328916 | Nishikawa | Dec 2001 | B1 |
| 6376059 | Anderson | Apr 2002 | B1 |
| 6378733 | Boonzaier | Apr 2002 | B1 |
| 6379802 | Ito | Apr 2002 | B2 |
| 6383425 | Wu | May 2002 | B1 |
| 6420024 | Perez | Jul 2002 | B1 |
| 6444073 | Reeves | Sep 2002 | B1 |
| 6455150 | Sheppard | Sep 2002 | B1 |
| 6468451 | Perez | Oct 2002 | B1 |
| 6472473 | Ansems | Oct 2002 | B1 |
| RE37932 | Baldwin | Dec 2002 | E |
| 6512019 | Agarwal | Jan 2003 | B1 |
| 6521675 | Wu | Feb 2003 | B1 |
| 6541105 | Park | Apr 2003 | B1 |
| 6562447 | Wu | May 2003 | B2 |
| 6565934 | Fredricks | May 2003 | B1 |
| 6586532 | Gauthy | Jul 2003 | B1 |
| 6593005 | Tau | Jul 2003 | B2 |
| 6593384 | Anderson | Jul 2003 | B2 |
| 6613811 | Pallaver | Sep 2003 | B1 |
| 6616434 | Burnham | Sep 2003 | B1 |
| 6646019 | Perez | Nov 2003 | B2 |
| 6649666 | Read | Nov 2003 | B1 |
| 6713139 | Usui | Mar 2004 | B2 |
| 6720362 | Park | Apr 2004 | B1 |
| 6749913 | Watanabe | Jun 2004 | B2 |
| 6779662 | Dorsey | Aug 2004 | B2 |
| 6811843 | DeBraal | Nov 2004 | B2 |
| 6814253 | Wong | Nov 2004 | B2 |
| 6875826 | Huovinen | Apr 2005 | B1 |
| 6883677 | Goeking | Apr 2005 | B2 |
| 6884377 | Burnham | Apr 2005 | B1 |
| 6884851 | Gauthy | Apr 2005 | B2 |
| 6908651 | Watanabe | Jun 2005 | B2 |
| 6926507 | Cardona | Aug 2005 | B2 |
| 6926512 | Wu | Aug 2005 | B2 |
| 6982107 | Hennen | Jan 2006 | B1 |
| 7056563 | Halabisky | Jun 2006 | B2 |
| 7070852 | Reiners | Jul 2006 | B1 |
| 7074466 | DeBraal | Jul 2006 | B2 |
| 7094463 | Haas | Aug 2006 | B2 |
| 7121991 | Mannlein | Oct 2006 | B2 |
| 7144532 | Kim | Dec 2006 | B2 |
| 7173069 | Swennen | Feb 2007 | B2 |
| 7234629 | Ho | Jun 2007 | B2 |
| 7281650 | Milan | Oct 2007 | B1 |
| 7355089 | Chang | Apr 2008 | B2 |
| 7361720 | Pierini | Apr 2008 | B2 |
| 7365136 | Huovinen | Apr 2008 | B2 |
| 7423071 | Mogami | Sep 2008 | B2 |
| 7458504 | Robertson | Dec 2008 | B2 |
| 7504347 | Poon | Mar 2009 | B2 |
| 7510098 | Hartjes | Mar 2009 | B2 |
| 7513386 | Hartjes | Apr 2009 | B2 |
| 7514517 | Hoenig | Apr 2009 | B2 |
| 7524911 | Karjala | Apr 2009 | B2 |
| 7557147 | Martinez | Jul 2009 | B2 |
| 7579408 | Walton | Aug 2009 | B2 |
| 7582716 | Liang | Sep 2009 | B2 |
| 7585557 | Aylward | Sep 2009 | B2 |
| 7592397 | Markovich | Sep 2009 | B2 |
| 7608668 | Shan | Oct 2009 | B2 |
| 7622179 | Patel | Nov 2009 | B2 |
| 7622529 | Walton | Nov 2009 | B2 |
| 7629416 | Li | Dec 2009 | B2 |
| 7655296 | Haas | Feb 2010 | B2 |
| 7662881 | Walton | Feb 2010 | B2 |
| 7666918 | Prieto | Feb 2010 | B2 |
| 7671106 | Markovich | Mar 2010 | B2 |
| 7671131 | Hughes | Mar 2010 | B2 |
| 7673564 | Wolf | Mar 2010 | B2 |
| 7687442 | Walton | Mar 2010 | B2 |
| 7695812 | Peng | Apr 2010 | B2 |
| 7714071 | Hoenig | May 2010 | B2 |
| 7732052 | Chang | Jun 2010 | B2 |
| 7737061 | Chang | Jun 2010 | B2 |
| 7737215 | Chang | Jun 2010 | B2 |
| 7741397 | Liang | Jun 2010 | B2 |
| 7754814 | Barcus | Jul 2010 | B2 |
| 7759404 | Burgun | Jul 2010 | B2 |
| 7786216 | Soediono | Aug 2010 | B2 |
| 7795321 | Cheung | Sep 2010 | B2 |
| 7803728 | Poon | Sep 2010 | B2 |
| 7811644 | DeBraal | Oct 2010 | B2 |
| 7818866 | Hollis | Oct 2010 | B2 |
| 7820282 | Haas | Oct 2010 | B2 |
| 7825166 | Sasaki | Nov 2010 | B2 |
| 7841974 | Hartjes | Nov 2010 | B2 |
| 7842770 | Liang | Nov 2010 | B2 |
| 7858706 | Arriola | Dec 2010 | B2 |
| 7863379 | Kapur | Jan 2011 | B2 |
| 7883769 | Seth | Feb 2011 | B2 |
| 7893166 | Shan | Feb 2011 | B2 |
| 7897689 | Harris | Mar 2011 | B2 |
| 7906587 | Poon | Mar 2011 | B2 |
| 7910658 | Chang | Mar 2011 | B2 |
| 7915192 | Arriola | Mar 2011 | B2 |
| 7918005 | Hollis | Apr 2011 | B2 |
| 7918016 | Hollis | Apr 2011 | B2 |
| 7922071 | Robertson | Apr 2011 | B2 |
| 7928162 | Kiss | Apr 2011 | B2 |
| 7935740 | Dang | May 2011 | B2 |
| 7947367 | Poon | May 2011 | B2 |
| 7951882 | Arriola | May 2011 | B2 |
| 7977397 | Cheung | Jul 2011 | B2 |
| 7989543 | Karjala | Aug 2011 | B2 |
| 7993254 | Robertson | Aug 2011 | B2 |
| 7998579 | Lin | Aug 2011 | B2 |
| 7998728 | Rhoads | Aug 2011 | B2 |
| 8003176 | Ylitalo | Aug 2011 | B2 |
| 8003744 | Okamoto | Aug 2011 | B2 |
| 8012550 | Ylitalo | Sep 2011 | B2 |
| 8026291 | Handa | Sep 2011 | B2 |
| 8043695 | Ballard | Oct 2011 | B2 |
| 8067319 | Poon | Nov 2011 | B2 |
| 8076381 | Miyagawa | Dec 2011 | B2 |
| 8076416 | Ellul | Dec 2011 | B2 |
| 8084537 | Walton | Dec 2011 | B2 |
| 8087147 | Hollis | Jan 2012 | B2 |
| 8105459 | Alvarez | Jan 2012 | B2 |
| 8119237 | Peng | Feb 2012 | B2 |
| 8124234 | Weaver | Feb 2012 | B2 |
| 8173233 | Rogers | May 2012 | B2 |
| 8198374 | Arriola | Jun 2012 | B2 |
| 8211982 | Harris | Jul 2012 | B2 |
| 8227075 | Matsushita | Jul 2012 | B2 |
| 8273068 | Chang | Sep 2012 | B2 |
| 8273826 | Walton | Sep 2012 | B2 |
| 8273838 | Shan | Sep 2012 | B2 |
| 8288470 | Ansems | Oct 2012 | B2 |
| 8304496 | Weaver | Nov 2012 | B2 |
| 8404780 | Weaver | Mar 2013 | B2 |
| 8435615 | Tsuchida | May 2013 | B2 |
| 8679620 | Matsushita | Mar 2014 | B2 |
| 8715449 | Leser | May 2014 | B2 |
| 8721823 | Vaideeswaran | May 2014 | B2 |
| 8883280 | Leser | Nov 2014 | B2 |
| 9067705 | Leser | Jun 2015 | B2 |
| 9180995 | Iyori | Nov 2015 | B2 |
| 9358772 | Leser | Jun 2016 | B2 |
| 20010010848 | Usui | Aug 2001 | A1 |
| 20010010849 | Blizard | Aug 2001 | A1 |
| 20010038893 | Mohan | Nov 2001 | A1 |
| 20010041236 | Usui | Nov 2001 | A1 |
| 20020030296 | Geddes | Mar 2002 | A1 |
| 20020041046 | Hartjes | Apr 2002 | A1 |
| 20020058126 | Kannankeril | May 2002 | A1 |
| 20020135088 | Harfmann | Sep 2002 | A1 |
| 20020137851 | Kim | Sep 2002 | A1 |
| 20020144769 | Debraal | Oct 2002 | A1 |
| 20020172818 | DeBraal | Nov 2002 | A1 |
| 20030003251 | DeBraal | Jan 2003 | A1 |
| 20030017284 | Watanabe | Jan 2003 | A1 |
| 20030021921 | DeBraal | Jan 2003 | A1 |
| 20030029876 | Giraud | Feb 2003 | A1 |
| 20030108695 | Freek | Jun 2003 | A1 |
| 20030138515 | Harfmann | Jul 2003 | A1 |
| 20030211310 | Haas | Nov 2003 | A1 |
| 20030228336 | Gervasio | Dec 2003 | A1 |
| 20030232210 | Haas | Dec 2003 | A1 |
| 20040013830 | Nonomura | Jan 2004 | A1 |
| 20040031714 | Hanson | Feb 2004 | A1 |
| 20040038018 | Anderson | Feb 2004 | A1 |
| 20040062885 | Imanari | Apr 2004 | A1 |
| 20040115418 | Anderson | Jun 2004 | A1 |
| 20040170814 | VanHandel | Sep 2004 | A1 |
| 20050003122 | Debraal | Jan 2005 | A1 |
| 20050006449 | DAmato | Jan 2005 | A1 |
| 20050101926 | Ausen | May 2005 | A1 |
| 20050104365 | Haas | May 2005 | A1 |
| 20050115975 | Smith | Jun 2005 | A1 |
| 20050121457 | Wilson | Jun 2005 | A1 |
| 20050124709 | Krueger | Jun 2005 | A1 |
| 20050145317 | Yamamoto | Jul 2005 | A1 |
| 20050147807 | Haas | Jul 2005 | A1 |
| 20050159496 | Bambara | Jul 2005 | A1 |
| 20050165165 | Zwynenburg | Jul 2005 | A1 |
| 20050184136 | Baynum | Aug 2005 | A1 |
| 20050236294 | Herbert | Oct 2005 | A1 |
| 20050256215 | Burnham | Nov 2005 | A1 |
| 20050272858 | Pierini | Dec 2005 | A1 |
| 20050288383 | Haas | Dec 2005 | A1 |
| 20060000882 | Darzinskas | Jan 2006 | A1 |
| 20060094577 | Mannlein | May 2006 | A1 |
| 20060095151 | Mannlein | May 2006 | A1 |
| 20060108409 | Pyper | May 2006 | A1 |
| 20060135699 | Li | Jun 2006 | A1 |
| 20060148920 | Musgrave | Jul 2006 | A1 |
| 20060151584 | Wonnacott | Jul 2006 | A1 |
| 20060178478 | Ellul | Aug 2006 | A1 |
| 20060198983 | Patel | Sep 2006 | A1 |
| 20060199006 | Poon | Sep 2006 | A1 |
| 20060199030 | Liang | Sep 2006 | A1 |
| 20060199744 | Walton | Sep 2006 | A1 |
| 20060199872 | Prieto | Sep 2006 | A1 |
| 20060199884 | Hoenig | Sep 2006 | A1 |
| 20060199887 | Liang | Sep 2006 | A1 |
| 20060199896 | Walton | Sep 2006 | A1 |
| 20060199897 | Karjala | Sep 2006 | A1 |
| 20060199905 | Hughes | Sep 2006 | A1 |
| 20060199906 | Walton | Sep 2006 | A1 |
| 20060199907 | Chang | Sep 2006 | A1 |
| 20060199908 | Cheung | Sep 2006 | A1 |
| 20060199910 | Walton | Sep 2006 | A1 |
| 20060199911 | Markovich | Sep 2006 | A1 |
| 20060199912 | Fuchs | Sep 2006 | A1 |
| 20060199914 | Harris | Sep 2006 | A1 |
| 20060199930 | Shan | Sep 2006 | A1 |
| 20060199931 | Poon | Sep 2006 | A1 |
| 20060199933 | Okamoto | Sep 2006 | A1 |
| 20060205833 | Martinez | Sep 2006 | A1 |
| 20060211819 | Hoenig | Sep 2006 | A1 |
| 20060234033 | Nishikawa | Oct 2006 | A1 |
| 20060289609 | Fritz | Dec 2006 | A1 |
| 20060289610 | Kling | Dec 2006 | A1 |
| 20070000983 | Spurrell | Jan 2007 | A1 |
| 20070010616 | Kapur | Jan 2007 | A1 |
| 20070032600 | Mogami | Feb 2007 | A1 |
| 20070056964 | Holcomb | Mar 2007 | A1 |
| 20070065615 | Odle | Mar 2007 | A1 |
| 20070066756 | Poon | Mar 2007 | A1 |
| 20070078222 | Chang | Apr 2007 | A1 |
| 20070095837 | Meier | May 2007 | A1 |
| 20070112127 | Soediono | May 2007 | A1 |
| 20070141188 | Kim | Jun 2007 | A1 |
| 20070155900 | Chang | Jul 2007 | A1 |
| 20070167315 | Arriola | Jul 2007 | A1 |
| 20070167575 | Weaver | Jul 2007 | A1 |
| 20070167578 | Arriola | Jul 2007 | A1 |
| 20070202330 | Peng | Aug 2007 | A1 |
| 20070219334 | LiPiShan | Sep 2007 | A1 |
| 20080020162 | Fackler | Jan 2008 | A1 |
| 20080045638 | Chapman | Feb 2008 | A1 |
| 20080118738 | Boyer | May 2008 | A1 |
| 20080121681 | Wiedmeyer | May 2008 | A1 |
| 20080138593 | Martinez | Jun 2008 | A1 |
| 20080156857 | Johnston | Jul 2008 | A1 |
| 20080177242 | Chang | Jul 2008 | A1 |
| 20080227877 | Stadlbauer | Sep 2008 | A1 |
| 20080234435 | Chang | Sep 2008 | A1 |
| 20080260996 | Heilman | Oct 2008 | A1 |
| 20080269388 | Markovich | Oct 2008 | A1 |
| 20080280517 | Chang | Nov 2008 | A1 |
| 20080281037 | Karjala | Nov 2008 | A1 |
| 20080311812 | Arriola | Dec 2008 | A1 |
| 20090042472 | Poon | Feb 2009 | A1 |
| 20090068402 | Yoshida | Mar 2009 | A1 |
| 20090069523 | Itakura | Mar 2009 | A1 |
| 20090076216 | Kiss | Mar 2009 | A1 |
| 20090105417 | Walton | Apr 2009 | A1 |
| 20090110855 | McCarthy | Apr 2009 | A1 |
| 20090110944 | Aguirre | Apr 2009 | A1 |
| 20090170679 | Hartjes | Jul 2009 | A1 |
| 20090220711 | Chang | Sep 2009 | A1 |
| 20090247033 | Peng | Oct 2009 | A1 |
| 20090263645 | Barger | Oct 2009 | A1 |
| 20090275690 | Weaver | Nov 2009 | A1 |
| 20090324914 | Lieng | Dec 2009 | A1 |
| 20100025073 | Fagrell | Feb 2010 | A1 |
| 20100028568 | Weaver | Feb 2010 | A1 |
| 20100029827 | Ansems | Feb 2010 | A1 |
| 20100040818 | Farha | Feb 2010 | A1 |
| 20100055358 | Weaver | Mar 2010 | A1 |
| 20100069574 | Shan | Mar 2010 | A1 |
| 20100093942 | Silvis | Apr 2010 | A1 |
| 20100116422 | Vaideeswaran | May 2010 | A1 |
| 20100137118 | Chang | Jun 2010 | A1 |
| 20100168267 | Dang | Jul 2010 | A1 |
| 20100181328 | Cook | Jul 2010 | A1 |
| 20100181370 | Berbert | Jul 2010 | A1 |
| 20100196610 | Chang | Aug 2010 | A1 |
| 20100240818 | Walton | Sep 2010 | A1 |
| 20100279571 | Poon | Nov 2010 | A1 |
| 20100324202 | Bafna | Dec 2010 | A1 |
| 20110003929 | Soediono | Jan 2011 | A1 |
| 20110008570 | Seth | Jan 2011 | A1 |
| 20110009513 | Chaudhary | Jan 2011 | A1 |
| 20110014835 | Sieradzki | Jan 2011 | A1 |
| 20110091688 | Maurer | Apr 2011 | A1 |
| 20110104414 | Onodera | May 2011 | A1 |
| 20110111150 | Matsuzaki | May 2011 | A1 |
| 20110118370 | Jiang | May 2011 | A1 |
| 20110118416 | Arriola | May 2011 | A1 |
| 20110124818 | Arriola | May 2011 | A1 |
| 20110136959 | Brandstetter | Jun 2011 | A1 |
| 20110144240 | Harris | Jun 2011 | A1 |
| 20110217492 | Stamatiou | Sep 2011 | A1 |
| 20110229693 | Maurer | Sep 2011 | A1 |
| 20110230108 | Arriola | Sep 2011 | A1 |
| 20110318560 | Yun | Dec 2011 | A1 |
| 20120004087 | Tharayil | Jan 2012 | A1 |
| 20120024873 | Roseblade | Feb 2012 | A1 |
| 20120028065 | Bafna | Feb 2012 | A1 |
| 20120041148 | Bafna | Feb 2012 | A1 |
| 20120043374 | Lemon | Feb 2012 | A1 |
| 20120045603 | Zerafati | Feb 2012 | A1 |
| 20120108714 | Wittner | May 2012 | A1 |
| 20120108741 | Wu | May 2012 | A1 |
| 20120108743 | Krishnaswamy | May 2012 | A1 |
| 20120125926 | Iyori | May 2012 | A1 |
| 20120132699 | Mann | May 2012 | A1 |
| 20120178896 | Bastioli | Jul 2012 | A1 |
| 20120184657 | Lake | Jul 2012 | A1 |
| 20120193365 | Humphries | Aug 2012 | A1 |
| 20120199278 | Lee | Aug 2012 | A1 |
| 20120199279 | Lee | Aug 2012 | A1 |
| 20120199641 | Hsieh | Aug 2012 | A1 |
| 20120214890 | Senda | Aug 2012 | A1 |
| 20120220730 | Li | Aug 2012 | A1 |
| 20120225961 | VanHorn | Sep 2012 | A1 |
| 20120237734 | Maurer | Sep 2012 | A1 |
| 20120267368 | Wu | Oct 2012 | A1 |
| 20120270039 | Tynys | Oct 2012 | A1 |
| 20120295994 | Bernreitner | Nov 2012 | A1 |
| 20120318805 | Leser | Dec 2012 | A1 |
| 20120318807 | Leser | Dec 2012 | A1 |
| 20120318859 | Leser | Dec 2012 | A1 |
| 20130023598 | Song | Jan 2013 | A1 |
| 20130032963 | Tokiwa | Feb 2013 | A1 |
| 20130052385 | Leser | Feb 2013 | A1 |
| 20130140320 | Nadella | Jun 2013 | A1 |
| 20130216744 | Liao | Aug 2013 | A1 |
| 20130280517 | Buehring | Oct 2013 | A1 |
| 20130303645 | Dix | Nov 2013 | A1 |
| 20140131430 | Leser | May 2014 | A1 |
| 20140263367 | Robertson | Sep 2014 | A1 |
| 20150250342 | Euler | Sep 2015 | A1 |
| 20150258771 | Leser | Sep 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 2291607 | Jun 2000 | CA |
| 2765489 | Dec 2010 | CA |
| 1288427 | Mar 2001 | CN |
| 1495100 | May 2004 | CN |
| 1942370 | Apr 2007 | CN |
| 101370873 | Feb 2009 | CN |
| 101429309 | May 2009 | CN |
| 101531260 | Sep 2009 | CN |
| 101538387 | Sep 2009 | CN |
| 102089370 | Jun 2011 | CN |
| 102115561 | Jul 2011 | CN |
| 102245368 | Nov 2011 | CN |
| 102391570 | Mar 2012 | CN |
| 102762350 | Oct 2012 | CN |
| 2831240 | Jan 1980 | DE |
| 2831240 | Mar 1988 | DE |
| 102006025612 | Nov 2007 | DE |
| 102006025612 | Nov 2007 | DE |
| 0001791 | May 1979 | EP |
| 0086869 | Aug 1983 | EP |
| 0161597 | Nov 1985 | EP |
| 0318167 | May 1989 | EP |
| 9113933 | Sep 1991 | EP |
| 0520028 | Dec 1992 | EP |
| 0570221 | Nov 1993 | EP |
| 0570221 | Nov 1993 | EP |
| 0588321 | Mar 1994 | EP |
| 0659647 | Jun 1995 | EP |
| 0879844 | Nov 1998 | EP |
| 0972727 | Jan 2000 | EP |
| 0796199 | Feb 2001 | EP |
| 0940240 | Oct 2002 | EP |
| 1308263 | May 2003 | EP |
| 1323779 | Jul 2003 | EP |
| 1479716 | Nov 2004 | EP |
| 1666530 | Jun 2006 | EP |
| 1754744 | Feb 2007 | EP |
| 1921023 | May 2008 | EP |
| 1939099 | Jul 2008 | EP |
| 2266894 | Dec 2010 | EP |
| 2386584 | Nov 2011 | EP |
| 2386601 | Nov 2011 | EP |
| 2720954 | Apr 2014 | EP |
| 1078326 | Aug 1967 | GB |
| 2485077 | May 2012 | GB |
| 52123043 | Oct 1977 | JP |
| 52123043 | Oct 1977 | JP |
| S5641146 | Apr 1981 | JP |
| 58029618 | Feb 1983 | JP |
| H02129040 | May 1990 | JP |
| H02269683 | Nov 1990 | JP |
| H0543967 | Jun 1993 | JP |
| 0615751 | Jan 1994 | JP |
| 3140847 | Jan 1994 | JP |
| 06192460 | Jul 1994 | JP |
| H08067758 | Mar 1996 | JP |
| 2000128255 | May 2000 | JP |
| P310847 | Dec 2000 | JP |
| 2001310429 | Nov 2001 | JP |
| 2001315277 | Nov 2001 | JP |
| 2003292663 | Oct 2003 | JP |
| 2003321566 | Nov 2003 | JP |
| 2004018101 | Jan 2004 | JP |
| 2004168421 | Jun 2004 | JP |
| 2004168421 | Jun 2004 | JP |
| 2004330464 | Nov 2004 | JP |
| 2005272542 | Oct 2005 | JP |
| 2006096390 | Apr 2006 | JP |
| 2006130814 | May 2006 | JP |
| 2006142008 | Jun 2006 | JP |
| 2007154172 | Jun 2007 | JP |
| 2008162700 | Jul 2008 | JP |
| 2009504858 | Feb 2009 | JP |
| 2009066856 | Apr 2009 | JP |
| 2009126922 | Jun 2009 | JP |
| 2009138029 | Jun 2009 | JP |
| 2009190756 | Aug 2009 | JP |
| 2010173258 | Aug 2010 | JP |
| 2011104890 | Jun 2011 | JP |
| 100306320 | Oct 2001 | KR |
| 2003036558 | May 2003 | KR |
| 2004017234 | Feb 2004 | KR |
| 101196666 | Nov 2012 | KR |
| 393427 | Jun 2000 | TW |
| M362648 | Aug 2009 | TW |
| 201021747 | Jun 2010 | TW |
| 9413460 | Jun 1994 | WO |
| 9729150 | Aug 1997 | WO |
| 9816575 | Apr 1998 | WO |
| 0002800 | Jan 2000 | WO |
| 0119733 | Mar 2001 | WO |
| 0132758 | May 2001 | WO |
| 0153079 | Jul 2001 | WO |
| 0234824 | May 2002 | WO |
| 03076497 | Sep 2003 | WO |
| 03099913 | Dec 2003 | WO |
| 2004104075 | Dec 2004 | WO |
| 2006042908 | Apr 2006 | WO |
| 2006124369 | Nov 2006 | WO |
| 2007003523 | Jan 2007 | WO |
| 2007020074 | Feb 2007 | WO |
| 2007068766 | Jun 2007 | WO |
| 2007090845 | Aug 2007 | WO |
| 2008030953 | Mar 2008 | WO |
| 2008038750 | Apr 2008 | WO |
| 2008045944 | Apr 2008 | WO |
| 2008057878 | May 2008 | WO |
| 2008080111 | Jul 2008 | WO |
| 2008145267 | Dec 2008 | WO |
| 2009035580 | Mar 2009 | WO |
| 2010006272 | Jan 2010 | WO |
| 2010019146 | Feb 2010 | WO |
| 2010076701 | Jul 2010 | WO |
| 2010111869 | Oct 2010 | WO |
| 2011005856 | Jan 2011 | WO |
| 2011036272 | Mar 2011 | WO |
| 2011036272 | Mar 2011 | WO |
| 2011038081 | Mar 2011 | WO |
| 2011076637 | Jun 2011 | WO |
| 2011141044 | Nov 2011 | WO |
| 2012020106 | Feb 2012 | WO |
| 2012025584 | Mar 2012 | WO |
| 2012044730 | Apr 2012 | WO |
| 2012055797 | May 2012 | WO |
| 2012099682 | Jul 2012 | WO |
| 2012173873 | Dec 2012 | WO |
| 2012174422 | Dec 2012 | WO |
| 2012174567 | Dec 2012 | WO |
| 2012174568 | Dec 2012 | WO |
| 2013032552 | Mar 2013 | WO |
| 2013101301 | Jul 2013 | WO |
| Entry |
|---|
| Office Action for Chinese Patent Application No. 201380065116.7, dated Jun. 28, 2016, including English language summary, 12 pages. |
| Australian First Patent Examination Report for Application No. 2013334155, dated May 23, 2016, 4 pages. |
| Extended European Search Report for European Application No. 13862331.9-1708 / 2931627 PCT/US2013/074923, dated Jul. 7, 2016. |
| English translation of Russian Office Action for Application Serial No. 2014101298, dated Jul. 22, 2016, 7 pages. |
| Third Party Observations filed with respect to European Patent Application No. 12727994.1, Aug. 17, 2015 (22 pages). |
| U.S. Appl. No. 61/498,455, filed Jun. 17, 2011, related to PCT Application No. PCT/US2012/041395, 46 pages. |
| “Slip Agents”, Polypropylene Handbook, 2nd edition, 2005, pp. 285-286. |
| English translation of Russian Office Action for Application Serial No. 2015127677, dated Sep. 16, 2015. |
| Office Action dated Oct. 8, 2015 for U.S. Appl. No. 14/188,504. |
| Second Chinese Office Action dated Sep. 6, 2015 for Chinese Application Serial No. 201280034350.9. |
| Office Action dated Oct. 27, 2015 for U.S. Appl. No. 14/462,073. |
| Office Action dated Dec. 31, 2015 for U.S. Appl. No. 14/755,546. |
| Notice of Allowance dated Jan. 29, 2016 for U.S. Appl. No. 14/755,546. |
| English translation of First Office Action for Taiwanese Application No. 101121656, dated Nov. 13, 2015. |
| Singapore Notice of Eligibility for Grant, Search Report, and Examination Report dated Dec. 10, 2015 for Singapore Application No. 11201503336V. |
| Office Action dated Jan. 11, 2016 for U.S. Appl. No. 14/161,328. |
| English Summary of Russian Office Action for Application Serial No. 2014111340, dated Feb. 25, 2016, 8 pages. |
| United Kingdom Examination Report for Patent Application No. GB1400762.9 dated Feb. 11, 2016. |
| Office Action dated Feb. 16, 2016 for U.S. Appl. No. 14/108,142. |
| Extended European Search Report for European Application No. 13849152.7-1303 / 2912142 PCT/US2013/066811, dated Feb. 12, 2016. |
| English summary of Spanish Office Action for Application Serial No. P201490025, dated Feb. 9, 2016, 8 pages. |
| Supplemental European Search Report for European Application No. 12727994.1-1302, dated Feb. 17, 2016. |
| International Search Report and Written Opinion dated Oct. 18, 2013, relating to International Application No. PCT/US2013/053935. |
| International Preliminary Report on Patentability dated Feb. 16, 2016, relating to International Application No. PCT/US2014/051508. |
| English Summary of Chinese Office Action for Application Serial No. 201380041896.1, dated Mar. 21, 7 pages. |
| Extended European Search Report for European Application No. 13827981.5-1708 / 2888092 PCT/US2013/053935, dated Feb. 19, 2016. |
| Australian First Patent Examination Report for Application No. 2012271047, dated Feb. 29, 2016. |
| N.N. Najib, N.M. Manan, A.A. Bakar, and C.S. Sipaut, Effect of Blowing Agent Concentration on Cell Morphology and Impact Properties of Natural Rubber Foam, Journal of Physical Science, vol. 20(1), 13-25, 2009 (13 pages). |
| Nigel Mills, Polymer Foams Handbook, Fig. 2.2, 1st ed. 2007 (2 pages). |
| University of Massachusetts , Advanced Plastics Processing Lecture, Lecture 11: Foam Processes, Slide 4 (Nov. 11, 2012) (2 pages). |
| Australian Second Patent Examination Report for Application No. 2012302251, dated Feb. 26, 2016. |
| English summary of Chinese Office Action for Chinese Application Serial No. 201380065781.6, dated Apr. 19, 2016, 14 pages. |
| Affidavit of Christopher Butler of Internet Archive, Borealis webpage dated Jan. 20, 2010 (https://web.archive.org/web/20100120102738/http://www.borealisgroup.com/industry-solutions/advancedpackaging/rigid-packaging/polyolefin-foam/daploy-hmspp-extruded-foam/). |
| Reichelt et al., “PP-Blends with Tailored Foamability and Mechanical Properties”, Cellular Polymers, vol. 22, No. 5, 2003, 14 pages. |
| Ratzsch et al., “Radical reactions on polypropylene in the solid state”, Prog. Polym. Sci. 27 (2002) 1195-1282, 88 pages. |
| Excerpts from Encyclopedia of Polymer Science and Technology: Plastics, Resins, Rubbers, and Fibers, “Blowing Agents”, vol. 2, John Wiley & Sons, Inc. (1965), 37 pages. |
| Excerpts from Polymer Foams: Science and Technology, Lee et al., “Introduction to Polymeric Foams”, CRC Press (2007) 51 pages. |
| “Daploy(TM) HMS Polypropylene for Foam Extrusion”, obtained from Borealis webpage obtained from the Internet Archive\s “Wayback Machine” as of Nov. 16, 2008 https://web.archive.org/web/20081116085125/http://www.borealisgroup.com/pdf/literature/borealisborouge/brochure/K—IN0020—GB—FF—2007—10—BB.pdf). |
| Excerpts from Gibson and Ashby, Cellular solids: Structure and properties—Second edition, Cambridge University Press, 1997, 66 pages. |
| Excerpts from Maier and Calafut, Polypropylene: the Definitive User's Guild and Databook, Plastics Design Library, William Andrew Inc. (1998), 35 pages. |
| ASTM D3763-86, an American Society for Testing of Materials (ASTM), “Standard Method for High-Speed Puncture Properties of Plastics Using Load and Displacement Sensors” (1986 Edition), 5 pages. |
| ASTM D1922-93, an American Society for Testing of Materials (ASTM), “Standard Method for Propagation Tear Resistance of Plastic Film and Thin Sheeting by Pendulum Method” (1993 Edition), 5 pages. |
| Naguib et al., “Effect of Supercritical Gas on Crystallization of Linear and Branched Polypropylene Resins with Foaming Additives”, Ind. Eng. Chem. Res., 44 (2005), 6685-6691. |
| Tabatabaei et al., “Rheological and thermal properties of blends of a long-chain branched polypropylene and different linear polypropylenes”, Chemical Engineering Science, 64 (2009), 4719-4731. |
| Almanza et al., “Applicability of the Transient Plane Source Method to Measure the Thermal Conductivity of Low-Density Polyethylene Foams”, Journal of Polymer Science: Part B: Polymer Physics, vol. 42 (2004), 1226-1234. |
| The Burn Foundation, “Scald Burns”, available at https://web.archive.org/web/20080926114057/http:/wwwvii.burnfoundation.org/programs/resource.cfm?c=1&a=3, dated Sep. 26, 2008, accessed on Feb. 5, 2016. |
| AntiScald Inc. available at https://web.archive.org/web/20080517041952/http:/www.antiscald.com/prevention/general—info/table.php, dated May 17, 2008, accessed on Feb. 5, 2016. |
| “Fire Dynamics”, available at http://www.nist.gov/fire/fire—behavior.cfm, accessed on Feb. 5, 2016. |
| “Power of a Microwave Oven”, available at https://web.archive.org/web/20071010183358/http://hypertextbook.com/facts/2007/TatyanaNektalova.shtml, dated Oct. 10, 2007, accessed on Feb. 5, 2016. |
| Health Physics Society, “Microwave Oven Q & A”, available at https://web.archive.org/web/20090302090144/http://www.hps.org/publicinformation/ate/faqs/microwaveovenq&a.html, dated Mar. 2, 2009, accessed on Feb. 5, 2016. |
| Cook's Info, “Microwave Ovens”, available at http://www.cooksinfo.com/microwave-ovens, accessed on Feb. 5, 2016. |
| Antunes et al., “Heat Transfer in Polypropylene-Based Foams ProducedUsing Different Foaming Processes”, Advanced Engineering Materials, 11, No. 10 (2009), 811-817. |
| Excerpts from Frank Kreith, Principles of Heat Transfer, 3rd ed., Intext Educational Publishers (1973). |
| Excerpts from James M. Gere, Mechanics of Materials, 5th ed., Brooks/Cole (2001). |
| Technical data sheet of HIFAX CA 60 A, obtained from https://www.lyondellbasell.com/en/polymers/p/Hifax-CA-60-A/d372c484-8f5a-4b2c-8674-8b7b781a1796, accessed on Feb. 4, 2016, 2 pages. |
| Michel Biron, “Chapter 4—Detailed Accounts of Thermoplastic Resins,” Thermoplastics and Thermoplastic Composites, Technical Information for Plastics Users, Elsevier Ltd. (2007), 217-714. |
| Excerpts from Cornelia Vasile, “Mechanical Properties and Parameters of Polyolefins”, Handbook of Polyolefins, 2nd ed., Marcel Dekker, Inc. (2000). |
| Williams et al., “Thermal Connectivity of Plastic Foams”, Polymer Engineering and Science, Apr. 1983, vol. 23, No. 6., 293-298. |
| Excerpts from M.C. McCrum et al., Principles of Polymer Engineering, 2nd ed., Oxford Science Publications (1997). |
| Excerpts from Robert H. Perry, Perry\s Chemical Engineers Handbook, 7th ed., The McGraw-Hill Companies, Inc. (1997). |
| Martinez-Diez et al., “The Thermal Conductivity of a Polyethylene Foam Block Produced by a Compression Molding Process”, Journal of Cellular Plastics, vol. 37 (2001), 21-42. |
| Borealis Product Brochure, Daploy HMS Polypropylene for Foam Extrusion (2010), 20 pages. |
| R. Coquard and D. Baillis, Journal of Heat Transfer, 2006, 128(6): 538-549. |
| A. R. Katritzky et al., “Correlation and Prediction of the Refractive Indices of Polymers by QSPR,” J. Chem. Inf. Comput. Sci., 38 (1998), 1171-1176. |
| M. Antunes et al., “Heat Transfer in Polyolefin Foams,” Heat Transfer in Multi-Phase Materials, A. Öchsner and G. E. Murch, Eds. Springer-Verlag Berlin Heidelberg, 2011, 131-161. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 1]. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 2]. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 3]. |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (2101 pages) [Submitted in multiple parts—section 4]. |
| English summary of Mexican Office Action for Application Serial No. MX/a/2013/014993, dated Apr. 27, 2016, 5 pages. |
| Japanese Office Action for Japanese Patent Application No. 2014-528384, dated Mar. 1, 2016. |
| English Summary of Chinese Office Action for Application Serial No. 201380041896.1, dated Mar. 18, 2016, 7 pages. |
| Doerpinghaus et al., “Separating the effects of sparse long-chain branching on rheology from those due to molecular weight in polyethylenes”, Journal of Rheology, 47, 717 (2003). |
| English Summary of Chinese Office Action for Application Serial No. 201280051426.9, dated Apr. 29, 2016, 5 pages. |
| Office Action dated Jun. 30, 2016 for U.S. Appl. No. 14/106,276. |
| Australian First Patent Examination Report for Application No. 2012363114, dated Jun. 15, 2016, 4 pages. |
| Office Action for Chinese Patent Application No. 201380064860.5, dated Jun. 2, 2016 including English language summary, 13 pages. |
| Singapore Office Action and Written Opinion dated May 26, 2016 for Singapore Application No. 11201504333Y. |
| Singapore Office Action and Written Opinion dated May 27, 2016 for Singapore Application No. 11201504330U. |
| Singapore Office Action and Written Opinion dated May 27, 2016 for Singapore Application No. 11201504327V. |
| Office Action dated Jun. 10, 2016 for U.S. Appl. No. 14/188,504. |
| Office Action dated Mar. 10, 2016 for U.S. Appl. No. 14/620,073. |
| Notice of Acceptance dated Jun. 10, 2016 for Australian Application No. 2012302251. |
| English translation of Japanese Office Action for Japanese Application No. 2014-516089, dated May 10, 2016. |
| Third Party Submission Under 37 CFR 1.290 filed on May 12, 2016 in U.S. Appl. No. 14/739,510. |
| Daploy HMS Polypropylene for Foam Extrusion, 20 pages, Borealis Borouge Shaping the Future with Plastics, Published 2010, www.borealisgroup.com, www.borouge.com, Vienna, Austria. |
| Lugao, A.B. et al., HMSPP—New Developments, Chemical and Environmental Technology Center, IPEN—Progress Report, 2002-2004 (1 page). |
| Davesh Tripathi, Practical Guide to Polypropylene, 2002 (5 pages). |
| Jinghua Tian et al., The Preparation and Rheology Characterization of Long Chain Branching Polypropylene, Polymer, 2006 (9 pages). |
| Bc. Lukas Kovar, High Pressure Crystallization of Long Chain Branched Polypropylene, Master Thesis, Thomas Bata University in Zlin, 2010 (83 pages). |
| Inter Partes Review Petition for U.S. Pat. No. 8,883,280 (712 pages), [Reference submitted in three parts]. |
| Borealis webpage dated Jan. 20, 2010 from Internet Archive (6 pages). |
| Gibson and Ashby, Cellular solids: structure and properties, 2nd ed., Cambridge University Press (1997) (7 pages). |
| C. Maier and T. Calafut, Polypropylene: the Definitive User\s Guide and Databook, Plastics Design Library, William Andrew Inc. (1998) (19 pages). |
| Reichelt et al., Cellular Polymers, vol. 22, No. 5 (2003) (14 pages). |
| Ratzsch et al., Prog. Polym. Sci., 27 (2002), 1195-1282 (88 pages). |
| Encyclopedia of Polymer Science and Technology: Plastics, Resins, Rubbers, and Fibers, vol. 2, John Wiley & Sons, Inc. (1965) (37 pages). |
| Shau-Tarng Lee, Chul B. Park, and N.S. Ramesh, Polymer Foams: Science and Technology, CRC Press (2007) (51 pages). |
| Grant & Hackh\s Chemical Dictionary, 5th ed., McGraw-Hill, Inc. (1987) (3 pages). |
| Merriam-Webster\s Collegiate Dictionary, 11th ed. (2003), p. 70 (3 pages). |
| Merriam-Webster\s Collegiate Dictionary, 11th ed. (2003), p. 1237 (3 pages). |
| Hawley\s Condensed Chemical Dictionary, 14th Ed. (2001) (5 pages). |
| Reichelt et al., Abstract of PP-Blends with Tailored Foamability and Mechanical Properties, Cellular Polymers, (2003) available from http://www.polymerjournals.com/journals.asp?Page=111&JournalType=cp&JournalIssue=cp22-5&JIP=, listing (4 pages). |
| Ratzsch et al., Abstract of Radical Reactions on Polypropylene in the Solid State, Progress in Polymer Science, vol. 27, Issue 7, (Sep. 2002), available from http://www.sciencedirect.com/science/article/pii/S0079670002000060 (3 pages). |
| “Borealis Dapoly HMS Polypropylene for Foam Extrusion” obtained from Borealis webpage obtained from the Internet Archive\s “Wayback Machine” as of Nov. 16, 2008 (https://web.archive.org/web/20081116085125/http://www.borealisgroup.com/pdf/literature/borealis-borouge/brochure/K—IN0020—GB—FF—2007—10—BB.pdf) (“Brochure \08”) (20 pages). |
| Borealis AG, DAPLOY(TM) HMS Polypropylene for Foam Extrusion, 2010, 20 pages. |
| European Search Report of Application No. 12861450.0, dated Nov. 21, 2014. |
| International Search Report and Written Opinion dated Apr. 16, 2014, relating to International Application No. PCT/US2013/075013. |
| International Search Report and Written Opinion dated Apr. 21, 2014, relating to International Application No. PCT/US2013/074923. |
| International Search Report and Written Opinion dated Apr. 22, 2014, relating to PCT/US2013/074965. |
| International Search Report and Written Opinion dated Apr. 25, 2014, relating to PCT/US2013/075052. |
| International Search Report and Written Opinion dated Jul. 3, 2014, relating to International Application No. PCT/US2014/025697. |
| International Search Report and Written Opinion dated Sep. 17, 2013, relating to International Application No. PCT/US2012/041395. |
| International Search Report dated Feb. 26, 2013, relating to International Application No. PCT/US2012/043018. |
| International Search Report dated Jan. 29, 2013, relating to International Application No. PCT/US2012/043017. |
| International Search Report dated Jan. 30, 2013, relating to International Application No. PCT/US2012/042737. |
| International Search Report dated Jul. 29, 2013, relating to International Application No. PCT/US2012/043016, 25 pages. |
| International Search Report dated Jul. 30, 2012, relating to International Application No. PCT/US2012/041397. |
| International Search Report dated Mar. 11, 2014, relating to International Application No. PCT/US2013/66811. |
| International Search Report dated Nov. 19, 2012, relating to International Application No. PCT/US2012/041395. |
| International Search Report dated Nov. 7, 2014, relating to International Application No. PCT/US2014/51508. |
| Jaakko I. Raukola, A New Technology to Manufacture Polypropylene Foam Sheet and Biaxially Oriented Foam Film, VTT Publications 361, Technical Research Centre of Finland, Apr. 1998, 100 pages. |
| Machine English translation of JP 2006-130814. |
| New Zealand First Examination Report for Application No. 619616 dated Oct. 10, 2014. |
| New Zealand First Examination Report for Application No. 621219 dated Nov. 17, 2014. |
| Office action dated Apr. 11, 2014 for U.S. Appl. No. 13/526,417. |
| Office Action dated Aug. 19, 2014 for Chinese Application No. 201280035667.4. |
| Office Action dated Aug. 21, 2014 for U.S. Appl. No. 13/526,454. |
| Office Action dated Jul. 25, 2014 for U.S. Appl. No. 13/525,640. |
| Office Action dated Oct. 10, 2014 for U.S. Appl. No. 14/106,358. |
| Office Action dated Oct. 16, 2014 for U.S. Appl. No. 14/106,212. |
| Office Action dated Sep. 25, 2014 for U.S. Appl. No. 13/526,417. |
| Notice of Allowance dated Apr. 6, 2015 for U.S. Appl. No. 13/526,417. |
| International Search Report and Written Opinion dated Jan. 19, 2015, relating to International Application No. PCT/US2014/059312. |
| International Search Report dated Jan. 19, 2015, relating to International Application No. PCT/US2014/059216. |
| Office Action dated Feb. 2, 2015 for U.S. Appl. No. 14/106,114. |
| Office Action dated Jan. 6, 2015 for Chinese Application No. 201280034350.9 (11 pages). |
| Office Action dated Jan. 9, 2015 for Chinese Application No. 201280035667.4 (22 pages). |
| Spanish Search Report of Application No. 201390099, dated Feb. 9, 2015. |
| Third-Party Submission Under 37 CFR 1.290 filed on Dec. 9, 2014 in U.S. Appl. No. 14/063,252. |
| Machine English translation of EP0086869. |
| Third-Party Submission Under 37 CFR 1.290 filed on Feb. 26, 2015 in U.S. Appl. No. 13/491,007. |
| Certified English translation of EP0086869. |
| Singapore Office Action dated Dec. 18, 2014 for Singapore Application No. 2014002273. |
| Office Action dated Apr. 30, 2015 for U.S. Appl. No. 14/462,073. |
| Office Action dated Apr. 14, 2015 for U.S. Appl. No. 14/106,212. |
| Office Action dated Apr. 10, 2015 for U.S. Appl. No. 14/106,358. |
| English translation of Spanish Search Report of Application No. 201490025, dated Apr. 20, 2015. |
| Spanish Search Report for Application No. 201490025, dated Apr. 20, 2015. |
| Office Action dated Jun. 23, 2015 for U.S. Appl. No. 13/525,640. |
| Third Party Submission Under 37 CFR 1.290 in U.S. Appl. No. 14/188,504 submitted May 11, 2015 and May 27, 2015 (43 pages). |
| Naguib et al., “Fundamental Foaming Mechanisms Governing the Volume Expansion of Extruded Polypropylene Foams,” Journal of Applied Polymer Science, vol. 91, pp. 2661-2668, 2004 (10 pages). |
| Wang et al., “Extending PP\s Foamability Through Tailored Melt Strength and Crystallization Kinetics,” paper 19 from the Conference Proceedings of the 8th International Conferences of Blowing Agents and Foaming Processes, May 16-17, 2006 in Munich, Germany Smithers Rapra Ltd, 2006 (14 pages). |
| Australian First Patent Examination Report for Application No. 2012302251 dated Jul. 9, 2015. |
| Office Action dated May 19, 2015 for Chinese Application No. 201280035667.4. |
| Office Action Chinese Patent Application No. 201280051426.9 dated Jul. 23, 2015. |
| Office Action dated Aug. 27, 2015 for U.S. Appl. No. 14/106,358. |
| Office Action dated Aug. 18, 2015 for U.S. Appl. No. 14/106,212. |
| Certified English translation of JP2003292663. |
| Notice of Allowance dated Jun. 23, 2014 for U.S. Appl. No. 13/491,327. |
| Notice of Allowance dated Oct. 6, 2014 for U.S. Appl. No. 13/491,327. |
| Taiwan Office Action for Taiwan Pat. App. No. 102146299, 7 pages. |
| Third Party Observation filed in European Patent App. No. 12727994.1, 11 pages. |
| International Standard ISO 16790:2005(E), 20 pages. |
| S. Muke et al., The Melt Extensibility of Polypropylene, Polym. Int. 2001,515-523, 9 pages. |
| P. Spitael and C.W. Macosko, Strain Hardening in Polypropylenes and its Role in Extrusion Foaming, Polym. Eng. Sci. 2004, 2090-2100. |
| Combined Search and Examination Report for Great Britain App. No. GB1616321.4, 4 pages. |
| British Examination Report for GB App. No. 1400762.9, 2 pages. |
| Chinese Office Action for Chinese Applicaiton 201380065781.6, 33 pages. |
| Research Progress of Polypropylene Foamed Material, Baiquan Chen et al., Plastics Manufacture, No. 12, pp. 55-58. |
| Modification and Formulation of Polypropylene, Mingshan Yang edits, Chemical Industry Press, p. 43, the second paragraph from the bottom, Jan. 31, 2009. |
| Extended European Search Report for European App. No. 13863649.3, 9 pages. |
| Office Action dated Nov. 4, 2016 for U.S. Appl. No. 13/961,411. |
| Chinese Office Action for Chinese Application No. 201280051426.9, 9 pages. |
| English Summary of Chinese Office Action for Application Serial No. 201380041896.1, dated Nov. 11, 2016, 11 pages. |
| Extended European Search Report for European App. No. 14775300.8 sent Oct. 24, 2016, 9 pages. |
| Office Action dated Nov. 18, 2016 for U.S. Appl. No. 14/718,836. |
| Office Action dated Sep. 1, 2016 for U.S. Appl. No. 14/106,212. |
| Australian First Patent Examination Report for Application No. 2013359097 dated Aug. 26, 2016, 3 pages. |
| British Examamination Report for GB Application No. GB1400762.9, dated Aug. 8, 2016, 2 pages. |
| Extended European Search Report for European Application No. 13863546.1 dated Jul. 12, 2016, 7 pages. |
| Office Action dated Aug. 9, 2016 for U.S. Appl. No. 14/108,142. |
| Jacoby, Philip, “Recent Insights on the Use of Beta Nucleation to Improve the Thermoforming Characteristics of Polypropylene,” Society of Plastics Engineers, Annual Technical Conference Proceedings, ANTEC 2012, Apr. 2012, pp. 2292-2296. |
| Singapore Written Opinion for Singapore Patent Application No. 11201504756T dated Jul. 19, 2016, 7 pages. |
| Office Action dated Sep. 27, 2016 for U.S. Appl. No. 14/725,319. |
| Office Action dated Jan. 4, 2017 for U.S. Appl. No. 14/108,110. |
| Japanese Office Action for Japanese Patent App. 2014-516089 dated Dec. 20, 2016, 6 pages. |
| Typical Engineering Properties of Polypropylene information sheet, Ineos Olefins and Polymers USA, archived at https://web.archive.org/web/20160501000000*/http://www.ineos.com/globalassets/ineos-group/businesses/ineos-olefins-and-polymers-usa/products/technical-information-patents/ineos-engineering-properties-of-pp.pdf, Mar. 2016, p. 1. |
| Office Action dated Dec. 14, 2016 for U.S. Appl. No. 14/211,553. |
| Office Action dated Dec. 22, 2016 for U.S. Appl. No. 14/858,158. |
| Gulf Cooperation Council Examination Report for GCC Patent App. No. GC2012-21529, 6 pages. |
| Office Action dated Dec. 28, 2016 for U.S. Appl. No. 14/106,276. |
| European Examination Report for European App. No. 12727994.1, 4 pages. |
| Spanish Search Report for Spanish App. No. 201490025, 5 pages. |
| Singapore Office Action and Written Opinion dated Feb. 14, 2014 for Singapore Application No. 11201504327V, 6 pages. |
| Singapore Office Action and Written Opinion for Singapore Application No. 11201504330U, 6 pages. |
| Office Action dated Feb. 7, 2017 for U.S. Appl. No. 13/491,007. |
| Office Action for Chinese Patent Application No. 201380064860.5, dated Jan. 25, 2017, 12 pages. |
| European Examination Report for European App. No. 13849152.7 dated Jan. 30, 2017, 3 pages. |
| Office Action dated Feb. 15, 2017 for U.S. Appl. No. 14/858,193. |
| Japanese Office Action for Japanese App. No. 2014-528384, 15 pages. |
| Office Action dated Feb. 24, 2017 for U.S. Appl. No. 14/188,504. |
| Office Action dated Feb. 28, 2017 for U.S. Appl. No. 15/004,263. |
| Office Action dated Mar. 6, 2017 for U.S. Appl. No. 14/108,142. |
| Chinese Office Action for Chinese App. No. 201480052411.3 dated Feb. 28, 2017, 16 pages. |
| New Zealand First Examination Report for New Zealand Application 708546, 2 pages. |
| Singapore Office Action and Written Opinion dated Dec. 13, 2016 and Singapore Application No. 11201504333Y, 6 pages. |
| Office Action for Chinese Patent Application No. 201380065116.7, dated Mar. 1, 2017, 9 pages. |
| Office Action dated Mar. 15, 2017 for U.S. Appl. No. 14/106,212. |
| Office Action dated Mar. 17, 2017 for U.S. Appl. No. 14/106,276. |
| Office Action dated Mar. 20, 2017 for U.S. Appl. No. 14/188,504. |
| Chinese Office Action dated Mar. 10, 2017 for Chinese Patent Application 201480007369.3, 11 pages. |
| New Zealand Examination Report for New Zealanc Application No. 708463, 3 pages. |
| Office Action dated Mar. 24, 2017 for U.S. Appl. No. 14/506,906. |
| Office Action dated Mar. 30, 2017 for U.S. Appl. No. 15/137,657. |
| Supplemental European Search Report for European App. No. 14836418 dated Feb. 23, 2017, 6 pages. |
| Office Action dated Apr. 7, 2017 for U.S. Appl. No. 14/063,252. |
| Chinese Office Action for Chinese Application No. 201380065127.5 dated Apr. 1, 2017, 14 pages. |
| Japanese Office Action for Japanese Application No. 2014-515882, dated Apr. 4, 2017, 6 pages. |
| New Zealand Examination Report for New Zealand Application No. 708552 dated Mar. 29, 2017, 2 pages. |
| Australian Search Report for Australian App. No. 2013359028, dated Apr. 10, 2017, 5 pages. |
| Australian Search Report for Australian App. No. 20133358988 dated Apr. 11, 2017, 4 pages. |
| Chinse Office Action for Chinese Patent App. No. 201511030247.9 dated Apr. 5, 2017, 12 pages. |
| Chinese Office Action for Chinese App. No. 201380065089.3 dated Apr. 21, 2017, 10 pages. |
| Applied Plastics Engineering Handbook, 1st edition, edited by Myer Kutz, published Jul. 20, 2011, 2 pages. |
| Chinese Office Action for Chinese App. No. 201380065781.6 dated May 10, 2017, 11 pages. |
| Office Action dated Jun. 7, 2017 for U.S. Appl. No. 15/388,319; (pp. 1-21). |
| Chinese Office Action for Chinese Application No. 201280051426.9 dated May 15, 2017, 12 pages. |
| Japanese Office Action for Japanese Patent App. No. 2015-539838 dated Jun. 6, 2017, 19 pages. |
| Taiwan Office Action for Taiwan App. No. 101121655 dated Jun. 14, 2017, 29 pages. |
| Australian Examiner's Report for Australian App. No. 2014244210 dated Jun. 16, 2017, 4 pages. |
| European Examination Report for European App. No. 13863308.6 dated May 17, 2017, 3 pages. |
| Extended European Search Report for European App. No. 14836418.5 dated Jun. 6, 2017, 14 pages. |
| Office Action dated Jun. 13, 2017 for U.S. Appl. No. 14/858,193; (pp. 1-21). |
| Chinese Office Action for Chinese App. No. 201380041896.1 dated May 22, 2017, 9 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20150274916 A1 | Oct 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61529632 | Aug 2011 | US | |
| 61618604 | Mar 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14486618 | Sep 2014 | US |
| Child | 14739510 | US | |
| Parent | 13491327 | Jun 2012 | US |
| Child | 14486618 | US |