Claims
- 1. A polymeric resinous material comprising(a) from 15 to 39 weight percent units derived from limonene; (b) from 15 to 39 weight percent units derived from dicyclopentadiene; and (c) from 46 to 70 weight percent units derived from tertiary-butyl styrene; wherein the sum of the weight percent units derived from limonene and dicyclopentadiene range from 30 to 54 weight percent units of the resin.
- 2. The polymeric resinous material according to claim 1 having a capillary tube melting point of from about 100° C. to about 200° C.
- 3. The polymeric resinous material according to claim 1 comprising(1) from 22 to 27 weight percent units derived from limonene; (2) from 22 to 27 weight percent units derived from dicyclopentadiene; and (3) from 46 to 56 weight percent units derived from tertiary-butyl styrene.
- 4. The polymeric resinous material according to claim 3 wherein the weight ratio of limonene:dicyclopentadiene:tertiary-butyl styrene is 1:1:2.
- 5. The polymeric resinous material according to claim 1 wherein the polymeric resinous material is modified by containing up to about 25 weight percent units derived from other unsaturated hydrocarbons containing from 9 to 10 carbon atoms.
- 6. The polymeric resinous material according to claim 1 wherein said polymeric resinous material is prepared by the method which comprises polymerizing a mixture of limonene, dicyclopentadiene and tertiary-butyl styrene in the presence of an anhydrous halide catalyst selected from the fluorides, chlorides and bromides of aluminum, tin and boron and from alkyl aluminum dihalides selected from methyl aluminum dichloride, ethyl aluminum dichloride and isopropyl aluminum dichloride.
- 7. The polymeric resinous material according to claim 6 wherein the halide catalysts are selected from aluminum chloride, stannic chloride, boron trifluoride, methyl aluminum dichloride, ethyl aluminum dichloride and isopropyl aluminum dichloride.
- 8. A rubber composition comprising (a) a diene-based elastomer containing olefinic unsaturation and (b) 1 to 80 phr of a polymeric resinous material comprising(1) from 15 to 39 weight percent units derived from limonene; (2) from 15 to 39 weight percent units derived from dicyclopentadiene; and (3) from 46 to 70 weight percent units derived from tertiary-butyl styrene; wherein the sum of the weight percent units derived from limonene and dicyclopentadiene-range from 30 to 54 weight percent units of the resin.
- 9. The rubber composition according to claim 8 characterized by the polymeric resinous material having a capillary tube melting point of from about 100° C. to about 200° C.
- 10. The rubber composition according to claim 8 wherein from 20 to 40 phr of a polymeric resinous material is present.
- 11. The rubber composition according to claim 8 wherein said polymeric resinous material comprises(1) from 22 to 27 weight percent units derived from limonene; (2) from 22 to 27 weight percent units derived from dicyclopentadiene; and (3) from 46 to 56 weight percent units derived from tertiary-butyl styrene.
- 12. The rubber composition according to claim 11 wherein the weight ratio of limonene:dicyclopentadiene:tertiary-butyl styrene is 1:1:2.
- 13. The rubber composition according to claim 8 wherein the polymeric resinous material is modified by containing up to about 25 weight percent units derived from other unsaturated hydrocarbons containing from 9 to 10 carbon atoms.
- 14. The rubber composition according to claim 8 wherein said polymeric resinous material is prepared by the method which comprises polymerizing a mixture of limonene, dicyclopentadiene and tertiary-butyl styrene in the presence of an anhydrous halide catalyst selected from the fluorides, chlorides and bromides of aluminum, tin and boron and from alkyl aluminum dihalides selected from methyl aluminum dichloride, ethyl aluminum dichloride and isopropyl aluminum dichloride.
- 15. The rubber composition according to claim 14 wherein the halide catalysts are selected from aluminum chloride, stannic chloride, boron trifluoride, methyl aluminum dichloride, ethyl aluminum dichloride and isopropyl aluminum dichloride.
- 16. The rubber composition according to claim 8 wherein said elastomer containing olefinic unsaturation is selected from the group consisting of natural rubber, neoprene, polyisoprene, polybutadiene, styrene-butadiene copolymer, styrene/isoprene/butadiene rubber, methyl methacrylate-butadiene copolymer, isoprene-styrene copolymer, methyl methacrylate-isoprene copolymer, acrylonitrile-isoprene copolymer, acrylonitrile-butadiene copolymer, EPDM and mixtures thereof.
- 17. The rubber composition according to claim 16 wherein said elastomer is styrene-butadiene copolymer.
- 18. The rubber composition according to claim 17 wherein said styrene-butadiene copolymer has a bound styrene content of from 20 to 45 percent.
- 19. The rubber composition according to claim 8 wherein a filler is present in said elastomer in an amount ranging from 10 to 250 phr.
Parent Case Info
This is a Divisional of application Ser. No. 09/251,282, filed on Feb. 16, 1999, presently U.S. Pat. No. 6,221,990.
US Referenced Citations (16)
Foreign Referenced Citations (4)
Number |
Date |
Country |
0063092 |
Oct 1982 |
EP |
0074273 |
Mar 1983 |
EP |
0249904 |
Dec 1987 |
EP |
0990669 |
Sep 1999 |
EP |
Non-Patent Literature Citations (3)
Entry |
Chemical Abstract, Secion Ch., Week 198608, Abstract No. XP-002136626. |
Chemical Abstracts, 56115s, vol. 90, 1979. |
European Search Report. |