Claims
- 1. A catalyst which forms on mixing:
- A. a catalyst component A formed by milling
- (1) a magnesium halide or manganous halide with
- (2) at least one carbonic acid ester of the formula ##STR3## wherein R is an aryl group having from 6 to about 20 carbon atoms and R' is the same as R or hydrogen,
- (3) treating the composite thus obtained from (1) and (2) with a tetravalent titanium halide for a period of time sufficient to incorporate titanium tetrahalide on at least a portion of the surface of said milled composite; and
- B. a cocatalyst component B comprising an organoaluminum compound wherein the molar ratio of component B to titanium compound ranges from 0.5:1 to 2,000:1 and the amount of titanium present in the finished catalyst ranges from about 0.1 to about 10 weight percent based on the dry composite.
- 2. A catalyst according to claim 1 which additionally contains an aromatic ester as part of cocatalyst component B and wherein the molar ratio of B to aromatic ester is about 1:1 to 8:1.
- 3. A catalyst according to claim 1 wherein (2) is diphenyl carbonate.
- 4. A catalyst according to claim 1 wherein (1) is MgCl.sub.2 and (3) is TiCl.sub.4.
- 5. A catalyst according to claim 4 wherein B comprises triethylaluminum and the catalyst additionally contains ethyl anisate and diethylaluminum chloride.
- 6. A catalyst according to claim 5 wherein (2) is diphenyl carbonate.
- 7. A catalyst according to claim 1 further including a solid particulate material which is inert to the catalyst components.
- 8. A catalyst according to claim 7 wherein the solid particulate material is selected from silica, alumina, calcium carbonate and solid organic material selected from polyvinyltoluene, polycarbonate, polyethylene, polypropylene, polystyrene, polymethylmethacrylate and mixtures thereof.
- 9. A catalyst according to claim 8 wherein said solid particulate materials are milled in the presence of (1) and (2).
- 10. A catalyst according to claim 1 wherein the catalyst composite obtained after treating the product of (1) and (2) with (3) is washed with an inert solvent to remove excess titanium tetrahalide and the resulting composite is dried prior to combining with cocatalyst component.
- 11. A method for preparing a catalyst comprising:
- milling together a manganese halide or manganous halide with a carbonic acid ester of the formula ##STR4## wherein R is an aryl group having from 6 to about 20 carbon atoms and R' is the same as R or hydrogen under conditions and for a period of time sufficient to form a finely divided milled composite;
- reacting the milled composite with a titanium tetrahalide under conditions and for a period of time sufficient to incorporate titanium tetrahalide on at least a portion of the surface of the milled composite; and
- washing the solid catalyst thus formed and recovering catalyst component A which is effective for olefin polymerization.
- 12. A method according to claim 11 wherein the catalyst composite obtained after reacting with a titanium tetrahalide is washed with an inert solvent to remove excess titanium tetrahalide.
- 13. A method according to claim 12 wherein said milled composite is reacted with titanium tetrahalide at a temperature ranging from about 0.degree. to about 200.degree. C. and the product treated with titanium tetrahalide is cooled under ambient conditions prior to washing.
- 14. A method according to claim 11 wherein said milled composite reacted with titanium tetrahalide is combined with a cocatalyst component B comprising an organoaluminum compound.
Parent Case Info
This is a continuation-in-part application of copending application having Ser. No. 968,156, filed Dec. 11, 1978, now U.S. Pat. No. 4,243,552.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3758621 |
Morikawa et al. |
Sep 1973 |
|
4013823 |
Longi et al. |
Mar 1977 |
|
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
968156 |
Dec 1978 |
|