Patent Application
20170204225
1. Technical Field
The technical field relates to a method for preparing polyarylene sulfide.
2. Description of the Background Art
Polyarylene sulfide (PAS), specifically polyphenylene sulfide (PPS), is a material with good mechanical properties and excellent thermal and chemical resistance compared to metals of the electronic and automobile industry due to its low density. PAS is also useful in spinning fibers of filters, connectors, coating material, and electronic components. Conventionally, the preparation of PAS is formed by reacting p-dichlorobenzene and sodium sulfide as monomers. A massive byproduct of alkali metal halide resides in the PAS resin, so the PAS resin needs some purification steps. However, purification by removal of the salty waste increases the production cost, degrades the quality, and decreases the efficiency of the production of PAS resin,
JP 07-304872 A discloses the preparation of a polysulfonium intermediate by reacting methyl 4-(phenylthio)phenyl sulfoxide in trifluoromethanesulfonic acid and then demethylating the polysulfonium intermediate with pyridine to obtain a neutral PAS resin with pyridinium salt as a byproduct. This reaction scheme is illustrated below.
However, a salty waste byproduct such as pyridinium salt is disadvantageous. Specifically, a salty waste byproduct results in increased cost due to the additional steps needed to purify the PAS resin. In addition, the salty waste byproduct is not environmentally friendly. Therefore, an industry-wide need exists for a method of preparing a polyarylene sulfide without a salty byproduct.
The disclosed embodiment relates to a method of preparing PAS without salty waste.
One embodiment is directed to a method for preparing a polyarylene sulfide of formula (1), comprising reacting methyl 4-(arylthio)aryl sulfoxide according to the following formula (2) with sulfuric acid, methanesulfonic acid, benzenesulfonic acid, p-toluenesulfonic acid, or trifluoromethanesulfonic acid to obtain a nolvsulfonium intermediate:
wherein Ar1 and Ar2 are aryl groups that may be the same or different and n is an integer of 2 to 1000; and demethylating the polysulfonium intermediate to obtain a polyarylene sulfide, wherein the polysulfonium intermediate is demethylated with aqueous HCl, HBr, or HI.
Further scope of applicability of the disclosed embodiment will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating alternative embodiments of the disclosed embodiment, are given by way of illustration only, since various changes and modifications within the spirit and scope of the disclosed embodiment will become apparent to one of ordinary skill in the art from this detailed description.
The disclosed embodiment will become more fully understood from the detailed description given below and the accompanying drawings that are given by way of illustration only and are thus not limitative of the disclosed embodiment.
In the following detailed description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the disclosed embodiments. It will be apparent, however, that one or more embodiments may be practiced without these specific details. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein.
The disclosed embodiment is directed to a method for preparing a polyarylene sulfide.
The polyarylene sulfide has the following structure according to formula (1):
Ar1—S—Ar2—Sn (1)
wherein Ar1 and Ar2 are aryl groups that may be the same or different and may be a phenyl group, a biphenyl group, a naphthyl group, a thienyl group, a tolyl group, a xylyl group, an indolyl group, a tetrahydronaphthyl group, a phenanthrenyl group, a biphenylenyl group, an indenyl group, an anthracenyl group, or a fluorenyl group. The aryl group may have a single ring, two fused rings, or three fused rings. For example, the aryl group may be a phenyl group. As such, the polyarylene sulfide may be polyphenylene sulfide.
n is an integer ranging from 1 to 1000 or from 2 to 1000.
The first step for preparing the polyarylene sulfide comprises reacting a methyl 4-(arylthio)arylsulfoxide compound with an acid. The methyl 4-(arylthio)aryl sulfoxide compound has the following structure according to formula (2):
wherein Ar1 and Ar2 are aryl groups that may be the same or different and may be a phenyl group, a biphenyl group, a naphthyl group, a thienyl group, a tolyl group, a xylyl group, an indolyl group, a tetrahydronaphthyl group, a phenanthrenyl group, a biphenylenyl group, an indenyl group, an anthracenyl group, or a fluorenyl group. The aryl group may have a single ring, two fused rings, or three fused rings. For example, the aryl group may be a phenyl group. The methyl 4-(arylthio)aryl sulfoxide may be methyl 4-(phenylthio)phenyl sulfoxide.
The acid may be sulfuric acid, methanesulfonic acid, benzenesulfonic acid, p-toluenesulfonic acid, or trifluoromethanesulfonic acid.
Weight moderate methyl-4-(phenylthio)phenyl sulfoxide, and sulfonic acid as solvent may be added inside the reaction between about 0 and 25° C. in about 0.5 atm to 1.5 atm. The reaction may be continuously kept about 0.5 hour to 1.5 hours between about 0° C. and 25° C.; then the temperature may be raised to about 20° C. to 50° C. (for example, about 25° C.) and the reaction may keep proceeding for about 4 hours to 72hours (for example, about 10 hours to 30 hours). After finishing, the white solid may be recrystallized in ethanol. As one embodiment, methyl 4-(arylthio)aryl sulfoxide and the acid may be reacted at about 0° C. for about 1 hour, and then, the temperature of the reaction may be raised to about 25° C. for about 20 hours.
When the methyl 4-(arylthio)aryl sulfoxide is reacted with an acid, a polysulfonium intermediate is obtained. The polysulfonium intermediate may have the following structure according to formula (3):
wherein Ar1 and Ar2 are aryl groups that may be the same or different and may be a phenyl group, a biphenyl group, a naphthyl group, a thienyl group, a tolyl group, a xylyl group, an indolyl group, a tetrahydronaphthyl group, a phenanthrenyl group, a biphenylenyl group, an indenyl group, an anthracenyl group, or a fluorenyl group. The aryl group may have a single ring, two fused rings, or three fused rings. In one embodiment, the aryl group may be a phenyl group.
n is an integer ranging from 1 to 1000 or from 2 to 1000.
Y is represented by anions, such as HSO4−, CH3SO3−, PhSO3−, p-tolSO3−, or CF3SO3−.
In the next step, the polysulfonium intermediate is demethylated to obtain a polyarylene sulfide.
The polysulfonium intermediate may be demethylated with aqueous HCl, HBr, or HI. In this regard, the acidity of the acid used for demethylation may be stronger than the acid used to obtain the polysulfonium intermediate.
The polysulfonium intermediate may be demethylated in an organic solvent. The organic solvent may be at least one selected from the group consisting of ketones, nitriles, sulfones, and amides. In one embodiment, the organic solvent may be a mixed solvent with water. In another embodiment, the organic solvent may be a mixed solvent of water and acetone.
The white polysulfonium solid may be dissolved in a mixed solvent (moderate ratio of water and organic solvent) and may be poured in hydrochloric acid slowly. The reaction keeps proceeding between 8 and 72 hours at room temperature, and a pale brown powdered product is obtained. In one embodiment, the reaction may proceed for 24 hours at room temperature wherein room temperature is defined as being about 18-25° C.
The disclosed embodiment is represented in the following reaction scheme:
One example of a reaction scheme of the disclosed embodiment is shown below wherein a polysulfonium intermediate was obtained by reacting methyl 4-(phenylthio)phenyl sulfoxide with sulfuric acid and then demethylating the polysulfonium intermediate with aqueous hydrochloric acid to obtain a neutral PAS resin without salty waste as a byproduct.
In this reaction scheme, aqueous hydrochloric acid is used as a nucleophile for demethylation of the polysulfonium intermediate to obtain the polyarylene sulfide (PAS) with a high yield and gaseous methyl chloride as byproduct.
As shown in the above reaction scheme, the sulfoxide group of the monomer is protonated to create a cationic hydroxysulfonium group, and π electrons of the aromatic rings are donated to create an electrophilic substitution reaction. Consequently, a soluble polycationic polymer with sulfonium groups is prepared. Aqueous HCl with a high dissociation constant is utilized as a nucleophile to remove the methyl groups on the sulfonium groups of the polycationic polymer, and a gaseous byproduct, CH3Cl, is obtained without salty waste.
As shown in the reaction scheme of JP 07-304872 A, the salty waste may be a pyridinium salt. Other examples of a salty waste include alkali metal halides and alkaline-earth metal halides. The disclosed embodiment does not produce salty waste as a byproduct.
In contrast to conventional methods, the disclosed embodiment generates byproducts that may be at least one selected from the group consisting of sulfuric acid, methanesulfonic acid, trifluoromethanesulfonic acid, CH3Cl, CH3Br, and CH3I. However, unlike conventional methods, the byproducts of the disclosed embodiment, CH3Cl, CH3Br, and CH3I, are gases. As such, the method of the disclosed embodiment may not need further processing or purification steps since the byproducts, CH3Cl, CH3Br, and CH3I, can be simply bubbled off. In this regard, the byproducts may also be collected for reuse. The byproducts, CH3Cl, CH3Br, and CH3I, can be collected by traps in vacuum.
The disclosed embodiment will hereinafter be described with reference to exemplary embodiments, which are written to be understood only as examples and are not intended to limit the scope of the present application.
1 g (4 mmol) methyl-4-(phenylthio)phenyl sulfoxide was added into a 10 ml double-necked round-bottom flask with a stirrer, and 5 ml 97% sulfonic acid was dropped inside the reaction dropwise at 0° C. The reaction continued for about 1 hr at 0° C. Then, the temperature was raised to 25° C., and the reaction proceeded for 20 hr. After 20 hours, the reaction solution was poured in 200 ml ethanol, and a white precipitate (1.31 g, 100%) of a polysulfonium intermediate was obtained.
The white precipitate (1.31 g) was dissolved in a mixed solvent (40 ml water and 20 ml acetone) and dropped in 50 ml 35% aqueous hydrochloric acid slowly. The reaction proceeded for 24 hr at room temperature, and a pale brown powdered product of PPS was obtained (0.8 g, 92%).
According to the DSC spectrum of
It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed embodiments. It is intended that the specification and examples be considered as exemplary only with a true scope of the disclosure being indicated by the following claims and their equivalents.
This non-provisional application claims the benefit under 35 U.S.C. §119(e) to U.S. Provisional Application No. 62/277,091, filed on Jan. 11, 2016, which is hereby expressly incorporated by reference into the present application.