The invention relates to a method for stabilizing cyclic nitroxide radical compound, as well as a polymerized cyclic nitroxide radical compound and use thereof.
In recent years, electron spin resonance (ESR) imaging by way of reactive oxygen species and radical species for tracing reactions in vitro and the use of stable radicals in the prevention, treatment or the like, of diseases or symptoms in which the reactive oxygen species are involved, have been drawing attention.
The ESR method has been used widely under in and ex vivo environments, using signal analysis and the spin trapping method, for L band ESR imaging, generation and annihilation of reactive oxygen species, and the like. Although the ESR-active electronic spin is known to be an extremely unstable reactive species, for stable cyclic nitroxide radicals such as the 2,2,6,6-tetramethylpiperidino oxy radical (TEMPO), the radical being stabilized, even more various applications are being developed, and in addition, examined (for instance, refer to Non-patent Reference 1 mentioned below). However, the current situation is that such stable cyclic nitroxide radicals are difficult to handle, as the radical or even the stable electronic spin is reduced in a short time in the presence of a reducing species such as ascorbic acid, which is present in vivo.
Note that one of the uses mentioned above, the so-called spin labeling method, is a method whereby stable nitroxide radicals are used as labeling agents for conjugation to proteins, fatty acids or steroids; however this is not intended to stabilize further the stable nitroxide radicals under an external environment, and no improved stabilization can be expected either. In addition, covalently bonding a plurality of stable nitroxide radicals, along with one or a plurality of metal ions/chelaters, to a polymer or an oligomer to try an add a novel function to an MRI contrast medium has also been proposed (for instance, refer to Patent Reference 1 mentioned below).
Meanwhile, it is also known that reactive oxygen species and reactive radical species play important roles in vivo. For instance, a free radical such as the hydroxy radical has been cited as one of the causes involved in the damage of a brain. Typically, it is known that free radicals tend to appear in the penumbra (ischemic penumbra) region, considered as the drug treatment region, during cerebral ischemia or after reperfusion. Therefore, some free radical scavengers have drawn attention as brain protecting agents that eliminate/render harmless a radical causing damages to brain vessels and neuronal cells, and as one among such scavengers, Edaravone (3-methyl-1-phenyl-2-pyrazolin-5-one) is sold commercially under the product name Radicut (refer to Non-patent Reference 2 mentioned below). However, it is also known that the use of Edaravone is accompanied by a risk of the adverse effect of acute kidney failure (kidney function disorder, liver function disorder and heart disease as complications). In addition, it is thought that there is room for improvement from the aspect of the effect and the aspect of safety, since in human, from the aspect of safety, Edaravone is administered multiple times by dividing into smaller amounts than the dose for which remarkable effects are observed in animal experiments.
In addition, it has been discovered that the cyclic nitroxide compounds classified in the above stable cyclic nitroxide radicals, 4-hydroxy-2,2,6,6-tetramethylpiperidine-1-oxyl (Tempol) to begin with, which has unique antioxidant properties, have the ability to decompose a superoxide or a peroxide, thereby functioning as radical scavengers, altering oxidative stress and altering the redox state of a tissue, and thereby interacting with and then altering many metabolic processes (refer to Non-patent Reference 3 mentioned below). Then, in Non-patent Reference 3, it has been suggested that these interactions could be used in therapeutic and research applications including protection against ionizing radiations, probes for functional magnetic resonance imaging, prevention or treatment of cancer, regulation of hypertension and body weight, and defense against damages caused by ischemia and reperfusion. However, once they have entered inside an organism, cyclic nitroxide compounds no longer function as radical scavengers if they are reduced by an endogenous reducing agent such as ascorbic acid.
In prior art, the present inventors have shown that nanoparticles (or polymeric micelles) from the self-assemblage of hydrophylic-phobic type block copolymers in water function as novel materials enabling drug carriers and nano-diagnoses, and have moved various material designs forward. In particular, by introducing a functional group at the water-soluble macromolecular end of the hydrophylic-phobic block copolymer, core-shell type nanoparticles with tens of nanometers in size having a ligand insertion site on the surface layer hold expectations as novel drug carriers enabling active targeting (for instance, refer to Patent Reference 2 and Patent Reference 3 mentioned below).
As described above, stable cyclic nitroxide radicals such as Tempol, while referred to as “stable”, function as radical scavengers; however, under biological reducing environment they become reduced and no longer function as radical scavengers. Concretely, medical uses of the cyclic nitroxide radicals alone as contrast media or therapeutic agents were difficult, since, in vivo, they are reduced in a short time or readily in the presence of reducing species such as, for instance, ascorbic acid. Therefore, it would be meaningful if the provision of means allowing radical species to be introduced and maintained in vivo stably over a long time were possible.
The present inventors introduced this time stable nitroxide radicals (TEMPO or the like) into the hydrophobic segments of specific block copolymers, performed preparations of novel nanoparticles (RNPs) having stable nitroxide radicals mainly in the core regions, examined the disposition thereof, and verified that a significantly high stability in blood in contrast to stable nitroxide radicals could be conferred. (The 18th Symposium of The Materials Society of Japan, Program and Abstracts, 7 Dec. 2007; Issued by: The 18th MRS-J Academic Symposium Organization Committee; Issued from: The Secretariat of MRS-J).
In addition, they found that such polymeric micellized cyclic nitroxide radical compounds could prevent or treat damages to brain cells, which are presumed to be caused by free radicals produced in ischemic areas and the like. This being the case, it is presumed that the polymeric micellized cyclic nitroxide radical compounds can translocate within the brain without being affected to translocation limitation within the brain by the blood-brain barrier, and furthermore, exerted within the brain their original actions as radical scavengers. In addition, it was also verified that the compounds, when administered into an artery or a vein at doses enabling the prevention or the treatment of brain cell damages, do not demonstrate marked toxicity or serious adverse effects against test animals. Taking into consideration that the brain damage prevention or treatment describe above is presumed to be due to the free radical scavenging action of the polymeric micellized cyclic nitroxide radical compounds, regardless of which mode of production mechanism of reactive oxygen species or free radicals (or hydroxy radicals) inside the brain may be, in an organism in which reactive oxygen species or free radicals were generated, the compounds are thought to be able to prevent or treat a wide range of diseases or symptoms in which reactive oxygen species or free radicals are involved.
Consequently, the present application discloses an invention with the following modes.
First Mode:
A stabilization method for a cyclic nitroxide radical compound, the method comprising a step of covalently bonding a cyclic nitroxide radical compound to a block copolymer containing a poly(ethylene glycol) chain segment and a hydrophobic chain segment carrying a reactive group through a functional group other than the radical of the compound and the reactive group of the copolymer, the functional group being an amino group, an aminomethyl group, a hydroxy group, a hydroxymethyl group, a carboxyl group or a carboxymethyl group, the reactive group being a halogen atom, a carboxyl group, an isocyanate residue, an isothiocyanate residue, an ester residue, an acid anhydride residue, a boronic acid residue, a maleimide residue or an epoxy group, and the block copolymer being able to form a polymeric micelle in an aqueous solvent in a form in which the cyclic nitroxide radical compound is covalently bonded.
Second Mode:
A polymerized nitroxide radical compound obtainable by such a stabilization method.
The polymerized nitroxide radical compound comprising poly(ethylene glycol) chain segments in which the repeating unit of ethylene oxide is 15 to 10,000 and a polystyrene chain segments in which the repeating unit of styrene is 3 to 3,000, and, at least 10%, preferably 30%, more preferably 50%, even more preferably 80% and particularly preferably 100% of the repeating units of styrene in the polystyrene chain segment, at position 4 of the phenyl group, a residue of cyclic nitroxide radical compound being covalently bonded through a linking group selected from the group consisting of —CH2NH—, —CH2NHCH2—, —CH2O—, —CH2OCH2—, —CH2OCO— and —CH2OCOCH2—, when present, the remainder of the position 4 being a halogen atom, a hydrogen atom or a hydroxyl group and the residue of cyclic nitroxide radical compound being selected from the group consisting of 2,2,6,6-tetramethylpiperidine-1-oxyl -4-yl, 2,2,5,5-tetramethylpyrrolidine-1-oxyl-3-yl, 2,2,5,5-tetramethylpyrroline-1-oxyl-3-yl and 2,4,4-trimethyl-1,3-oxazolidine-3-oxyl-2-yl, 2,4,4-trimethyl-1,3-thiazolidine-3-oxyl-2-yl and 2,4,4-trimethyl-imidazolidine-3-oxyl-2-yl, as a preferred mode.
Third Mode:
A block copolymer represented by the General Formula (III)
where A represents a non-substituted or a substituted C1-C12 alkoxy group, when substituted, the substituent represents a formyl group or a group of formula R1R2CH—, where R1 and R2 are independent and represent a C1-C4 alkoxy or R1 and R2 are combined and represent —OCH2CH2O—, —O(CH2)3O— or —O(CH2)4O—,
L1 represents a linking group selected from the group consisting of a valence bond, —(CH2)cS— and —CO(CH2)cS—, where c represents an integer from 1 to 5,
X represents a chlorine, a bromine or an iodine atom,
m represents an integer from 20 to 5,000 and
n represents an integer from 3 to 1,000.
Fourth Mode:
A pharmaceutical composition for the prevention or the treatment of a disease or a symptom in which a reactive oxygen species or a hydroxy radical is involved, for instance, the group consisting of cerebral infarction, cardiac infarction, cerebral edema, neurological deficit, inflammation, hypertension, hyperlipidemia, obesity, cerebrovascular injury and neuronal cell damage, the composition comprising the polymerized nitroxide radical compound, preferably, a compound represented by the General Formula (II)
where A represents a non-substituted or substituted C1-C12 alkoxy, when substituted, the substituent represents a formyl group or a group of formula R1R2CH—, where R1 and R2 are independent and represent a C1-C4 alkoxy or R1 and R2 are combined and represent —OCH2CH2O—, —O(CH2)3O— or —O(CH2)4O—,
L1 represents a linking group selected from the group consisting of a valence bond, —(CH2)nS—, —CO(CH2)cS—, where c represents an integer from 1 to 5, and preferably 2,
L2 represents a linking group selected from the group consisting of methylimino, methyliminomethyl, methyloxy, methyloxymethyl, methyl ester and methyl ester methyl,
at least 50% of n in the total number of R represents a residue of cyclic nitroxide radical compound selected from the group consisting of 2,2,6,6-tetramethylpiperidine-1-oxyl-4-yl, 2,2,5,5-tetramethylpyrrolidine-1-oxyl-3-yl, 2,2,5,5-tetramethylpyrroline-1-oxyl-3-yl and 2,4,4-trimethyl-1,3-oxazolidine-3-oxyl-2-yl, 2,4,4-trimethyl-1,3-thiazolidine-3-oxyl-2-yl and 2,4,4-trimethyl-imidazolidine-3-oxyl-2-yl, and when present the remaining R represents a hydrogen atom, a halogen atom or a hydroxy group,
m represents an integer from 20 to 5,000 and
n represents an integer from 3 to 1,000, and a pharmaceutically allowed carrier.
Fifth Mode:
A reagent for detecting the presence of a reactive oxygen species or a free radical (or a hydroxy radical) in vivo, comprising the compound represented by the General Formula (II) and a pharmaceutically allowed carrier.
Sixth Mode:
A method for the prevention or the treatment of a disease or a symptom in which a reactive oxygen species or a free radical (or a hydroxy radical) is involved, for instance, cerebral infarction, cardiac infarction, cerebral edema, neurological deficit, inflammation, hypertension, hyperlipidemia, obesity, cerebral vascular injury and neuronal cell damage, comprising administering to a patient having a disease or a symptom in which a reactive oxygen species or a free radical (or a hydroxy radical) is involved, the compound represented by General Formula (II) at a dose that is effective for preventing or treating the disease or the symptom.
Although not to be limited by a theory, polymerized nitroxide radical compounds such as those described above, by self-assembling in an aqueous medium, form a polymeric micelle having a particle size of tens of nanometers in which it is assumed that nitroxide radical portions are maintained in the core region and the poly(ethylene glycol) strands are present in the shell region (regarding a conceptual drawing of the polymeric micelle, refer to the structure below high pH in
With the stabilization method for cyclic nitroxide radical compound, which is the present invention of the First Mode, a cyclic nitroxide radical compound that can bond covalently with the hydrophobic segment of a block copolymer can stabilize a wide range of compounds without being limited to, for instance, so-called, stable nitroxide radical compounds, such as those advantageously used in spin labeling methods.
A block copolymer that can be used in such a stabilization method comprises, as stipulated above, a poly(ethylene glycol) chain segment (A) and a hydrophobic chain segment (B) carrying a reactive group, and is preferably a di-block copolymer of the AB type, but may also be a tri-block copolymer of the ABA type, or a tetra-block copolymer of the ABBA type. However, among such copolymers, as desirable ones, di-block copolymers may be cited, the block copolymer being represented by General Formula (I)
A-(CH2CH2O)m-L1-(h-phobic)-Z (1)
where A represents a non-substituted or substituted C1-C12 alkoxy, when substituted, the substituent represents a formyl group or a group of formula R1R2CH— (where R1 and R2 are independent and represent a C1-C4 alkoxy or R1 and R2 are combined and represent —OCH2CH2O—, —O(CH2)3O— or —O(CH2)4O—),
L1 represents a linking group selected from the group consisting of a valence bond, —(CH2)cS—, —CO(CH2)nS—, —(CH2)cNH—, —(CH2)cCO— (where each c is an integer from 1 to 5, and preferably 1 or 2), —CO—, —COO— and —CONH—,
(h-phobic) can be selected from those derived from polymers that are well known per se as biocompatible or medical polymers in the relevant technical field. Although not to be limiting, those represented by the following formulae can be given as concrete examples:
a poly amino acid ester chain segment represented by
where p represents 1 or 2, R1 represents a C1-C12 alkyl group optionally substituted at the nonbonding end with one phenyl group or benzhydryl group, and n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly((meta) acrylic acid ester) chain segment represented by
where R1 represents a C1-C12 alkyl group optionally substituted at the nonbonding end with one phenyl group or benzhydryl group, R2 represents a hydrogen atom or a C1-5 alkyl group, preferably a methyl group, and n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a styrene-maleic anhydride copolymer chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly malic acid ester chain segment represented by
where R1 represents a C1-C12 alkyl group optionally substituted at the nonbonding end with one phenyl group or benzhydryl group, and n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly amic acid chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly maleimide chain segment represented by
where R1 represents a C1-C12 alkyl group optionally substituted at the nonbonding end with one phenyl group or benzhydryl group, and n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(halomethylstyrene) chain segment represented by
where L1 represents a chlorine, bromine or iodine atom, and n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(vinyl chloride) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(chloroprene) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(glycidylmethacrylate) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(2-hydroxyethylmetacrylate) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(epichlorohydrin) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(3,3-bischloromethyloxetane) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a poly(oxazoline) chain segment represented by
where R1 represents a C1-C12 alkyl group optionally substituted at the nonbonding end with one phenyl group or benzhydryl group, and n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a polysiloxane chain segment represented by
where a and b independently represent an integer from 3 to 500;
a poly(vinylphenyl boronic acid) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300;
a 1-nylon chain segment represented by
where each n represents an integer from 3 to 1,000, preferably from 5 to 500, and more preferably from 10 to 300; and
a poly(vinyl benzaldehyde) chain segment represented by
where n represents an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 300.
Moreover, in the above Formula (I),
Z represents a hydrogen atom, a hydroxy, a C1-C12 alkyloxy optionally substituted at the nonbonding end with one phenyl group or benzhydryl group or a C1-C12 alkyl carbonyl optionally substituted at the nonbonding end with one phenyl group or benzhydryl group.
However, in particular, a block copolymer in which the hydrophobic chain segment of the block copolymer carrying the reactive group is a poly(halomethylstyrene) chain segment of formula
where L1 represents a chlorine, bromine or iodine atom and n represents an integer from 3 to 1,000, can be used preferably.
A portion of such block copolymers is well known, for instance, those in which the hydrophobic segment represents a poly amino acid ester chain segment are well known through Japanese Patent No. 2690276 (U.S. Pat. No. 5,449,513) or the like, in addition, those representing a poly((meta) acrylic acid ester) chain segment through Patent Reference 3. Other block copolymers can be acquired readily for a person of ordinary skill in the art by referring to the block copolymer preparation method mentioned above or Preparation Example 1 described below in the present specification. Note that when a linking group or a repeating unit of the general formula defining the block copolymer used in the present invention is represented by a formula, it is intended to be integrated in the general formula with the depicted directionality.
Although a cyclic nitroxide radical can be used without limitation as long as it is one that can be stabilized by the method of the present invention, a cyclic nitroxide radical compound that is strongly planned for stabilization with the present invention is selected from the group consisting of 4-substituted 2,2,6,6-tetramethylpiperidine-1-oxyl, 3-substituted 2,2,5,5-tetramethylpyrrolidine-1-oxyl, 3-substituted 2,2,5,5-tetramethylpyrroline-1-oxyl, 2-substituted 2,4,4-trimethyl-1,3-oxazolidine-3-oxyl, 2-substituted 2,4,4-trimethyl-1,3-thiazolidine-3-oxyl and 2-substituted 2,4,4-trimethyl-imidazolidine-3-oxyl, the substituents of the 4-substitution, the 3-substitution or the 2-substitution being selected from the group consisting of the amino group, the aminomethyl group and the hydroxyl group, the hydroxymethyl group, the carboxyl group and the carboxymethyl group.
The method for forming a covalent bond through a functional group of the cyclic nitroxide radical compound other than the radical (for instance, an amino group, an aminomethyl group, a hydroxyl group, a hydroxymethyl group, a carboxyl group or a carboxymethyl group) and a reactive group of the block copolymer (a halogen atom, and in particular a chlorine, bromine or iodine atom, a carboxyl group, an isocyanate residue, an isothiocyanate residue, an ester residue, an acid anhydride residue, a boronic acid residue, a maleimide residue or an epoxy group) can be performed by condensation reaction, addition reaction, which are well known per se, or, for instance, regarding an ester residue, aminolysis through the functional group (amino group) of the cyclic nitroxide radical compound, or the like. Such reactions may be performed in an aqueous solvent (water and organic solvents that are miscible in water, for instance, lower alcohols, dioxane, dimethyl formamide, dimethyl sulfoxide, and the like may be included), in the presence of an organic base (trimethylamine, triethanolamine or the like) or an inorganic base (potassium carbonate, sodium carbonate, sodium hydroxide or the like), and other condensation agents well known in the relevant technical field, as necessary. For the block copolymer, although one that is per se capable of forming a polymeric micelle by self-assembling in an aqueous solvent can be used conveniently, if one may form a polymeric micelle in an aqueous solvent in a morphology where the cyclic nitroxide radical compound is covalently bonded, it can be used in the present invention.
In another mode of the present invention, a polymerized compound of cyclic nitroxide radical compound prepared by a cyclic nitroxide radical compound stabilization method using such block copolymers as those described above is provided. Although not to be limiting, as a preferred mode, a polymerized nitroxide radical compound is provided, comprising a poly(ethylene glycol) chain segment in which the repeating unit of ethylene glycol is 15 to 10,000 and a polystyrene chain segment in which the repeating unit of styrene is 3 to 3,000, and, at least 10%, preferably 30%, more preferably 50%, even more preferably 80% and particularly preferably 100% of the repeating units of styrene in the polystyrene chain segment, at position 4 of the phenyl group, a residue of cyclic nitroxide radical compound being covalently bonded through a linking group selected from the group consisting of —CH2NH—, —CH2NHCH2—, —CH2O—, —CH2OCH2—, —CH2OCO— and —CH2OCOCH2—, when present, the remainder of the position 4 being a halogen atom, a hydrogen atom or a hydroxyl group and the cyclic nitroxide radical compound being selected from the group consisting of 2,2,6,6-tetramethylpiperidine-1-oxyl-4-yl, 2,2,5,5-tetramethylpyrrolidine-1-oxyl-3-yl, 2,2,5,5-tetramethylpyrroline-1-oxyl-3-yl and 2,4,4-trimethyl-1,3-oxazolidine-3-oxyl-2-yl, 2,4,4-trimethyl-1,3-thiazolidine-3-oxyl-2-yl and 2,4,4-trimethyl-imidazolidine-3-oxyl-2-yl. More concretely and more preferably, a polymerized nitroxide radical compound of General Formula (II) is provided
where A represents a non-substituted or substituted C1-C12 alkoxy, when substituted, the substituent represents a formyl group or a group of formula R1R2CH— (where R1 and R2 are independent and represent a C1-C4 alkoxy or R1 and R2 are combined and represent —OCH2CH2O—, —O(CH2)3O— or —O(CH2)4O—)
L1 represents a linking group selected from the group consisting of a valence bond, —(CH2)nS—, —CO(CH2)cS—, where c is an integer from 1 to 5, and preferably 2,
L2 represents a linking group selected from the group consisting of methyl imino (—CH2NH—), methyl iminomethyl (—CH2NHCH2—), methyloxy (—CH2O—), methyloxymethyl (—CH2OCH2—), methyl ester (—CH2OCO—) and methyl ester methyl (—CH2OCOCH2—),
at least 50% of n in the total number of R, represents a residue of cyclic nitroxide radical compound selected from the group consisting of 2,2,6,6-tetramethylpiperidine-1-oxyl-4-yl, 2,2,5,5-tetramethylpyrrolidine-1-oxyl-3-yl, 2,2,5,5-tetramethylpyrroline-1-oxyl-3-yl and 2,4,4-trimethyl-1,3-oxazolidine-3-oxyl-2-yl, 2,4,4-trimethyl-1,3-thiazolidine-3-oxyl-2-yl and 2,4,4-trimethyl-imidazolidine-3-oxyl-2-yl, and when present, the remaining R represents a hydrogen atom, a halogen atom or a hydroxy group,
m represents an integer from 20 to 5,000, preferably from 30 to 3,000 and more preferably from 40 to 1,000 and
n representing an integer from 3 to 1,000, preferably from 5 to 500 and more preferably from 10 to 500. In addition, polymerized nitroxide radical compounds for which, in General Formula (II), L1 is a valence bond or —CH2CH2S—, L2 is methyl imino or methyl iminomethyl and
the entirety of R are residues of cyclic nitroxide radical compound represented by any of the following formulae
where R′ is a methyl group,
are provided as a particularly desirable ones from the point of conferring pH responsiveness to the stabilization of the polymeric micelle that can be formed from these compounds.
In the definition of each group or portion described above, the alkyl portion of C1-C12 alkoxy can be straight or branched alkyl and, for instance, methyl, ethyl, propyl, iso-propyl, butyl, iso-butyl, s-butyl, t-butyl, pentyl, hexyl, heptyl, dodecanyl, and the like, can be cited. In addition, when A represents an alkoxy group substituted by formula R1R2CH—, and, R1 and R2 are independent and represent a C1-C4 alkoxy or R1 and R2 are combined and represent —OCH2CH2O—, —O(CH2)3O— or —O(CH2)4O—, since such a substituent can be readily cleaved under acidic condition and converted into a formyl group, proteins (for instance, antibodies and other ligands) or the like can be covalently bonded readily through an amino acid thereof. When present, it is desirable that such substituents be present at the non-bonded end of the alkoxy group. These substituent can be introduced for instance by referring to the poly(ethylene glycol) chain segment generation methods described in the above Patent References 2 and 3.
In addition, the linking group L1 in the block copolymer described above is not limited, since it may be replaced according to how the poly(ethylene glycol) chain segment and polystyrene are to be bonded. For instance, when a poly(ethylene glycol) chain segment is generated by anionic living polymerization and then living polymerization of halomethylstyrene is continued, L1 is a valence bond. When a poly(ethylene glycol) derivative having a sulphur atom at the ω-end of the poly(ethylene glycol) chain segment is prepared, by carrying out a radical polymerization of halomethylstyrene in the presence of the derivative, the linking group may be —CH2CH2S— or —COCH2CH2S—.
For L2, typically, a linking group selected from the group consisting of methyl imino, methyl iminomethyl, methyloxy and methyloxymethyl, can be cited. While such a linking group varies conveniently depending on the halogen atom of the block copolymer, for instance, a block copolymer represented by General Formula (III)
where A represents a non-substituted or substituted C1-C12 alkoxy, when substituted, the substituent represents a formyl group or a group of formula R1R2CH— (where R1 and R2 are independent and represent a C1-C4 alkoxy or R1 and R2 are combined and represent —OCH2CH2O—, —O(CH2)3O— or —O(CH2)4O—),
L1 represents a linking group selected from the group consisting of a valence bond, —(CH2)nS—, —CO(CH2)cS—, where c is an integer from 1 to 5, and preferably 2,
X represents a chlorine, bromine or iodine atom,
m represents an integer from 20 to 5,000 and
n represents an integer from 3 to 1,000, and the species of the functional group other than the radical of the cyclic nitroxide radical compound, in general, it can be formed by a covalent bond formation reaction that accompanies the elimination of a hydrogen halide.
Note that, to the best of the present inventors' knowledge, the copolymer represented by General Formula (III) has not been described in the literature, and is provided as another mode of the present invention.
In General Formula (II), at least 50%, preferably at least 75%, more preferably at least 90% and particularly preferably 100% of n in the total number R represents a residue of cyclic nitroxide radical compound selected from the group consisting of 2,2,6,6-tetramethylpiperidine-1-oxyl-4-yl, 2,2,4,4-tetramethylpyrrolidine-1-oxyl-3-yl, 2,2,4,4-tetramethylpyrroline-1-oxyl-3-yl and 2,4,4-trimethyl-1,3-oxazolidine-3-oxyl-2-yl, 2,4,4-trimethyl-1,3-thiazolidine-3-oxyl-2-yl and 2,4,4-trimethyl-imidazolidine-3-oxyl-2-yl, and when present, the remaining R represents a hydrogen atom, a halogen atom or a hydroxyl group. The proportion occupied within n, the total number of R, by residues of cyclic nitroxide radical compound can be varied, for instance, by controlling the reaction between the copolymer of General Formula (III) described above and the cyclic nitroxide radical compound, for instance, by controlling the reaction time.
While described above, in addition, m can be an integer from 20 to 5,000, preferably from 35 to 3,000, and more preferably from 60 to 500 and n can also be an integer from 3 to 5000, preferably from 10 to 300, and more preferably from 15 to 100.
Since, as shown concretely in the Test Examples described below, even under reducing conditions, the polymerized nitroxide radical compound of the present invention demonstrates an action that is intrinsic to a cyclic nitroxide radical compound (for instance, refer also to Non-patent Reference 1), it can be used as an antioxidant inside and outside of an organism.
In the present specification, as a more concrete example of use of a compound stabilized by the methods described above, a compound described more concretely, can be used for prevention or treatment of a disease or a symptom in which a reactive oxygen species or a free radical (or a hydroxy radical) involved in vivo.
in vivo referred to in the present invention means inside the body of animals in general, humans to begin with, mammals, fishes and the like, and organs, viscera and body fluid can be cited.
There is no limitation on the diseases or symptoms in which a reactive oxygen species or hydroxy radical is involved, and cerebral infarction, cardiac infarction, cerebral edema, neurological deficit, inflammation, hypertension, hyperlipidemia, obesity, cerebrovascular injury and neuronal cell damage, more concretely, cerebral infarction, cerebral edema, and neurological deficit, cerebral infarction (in particular, atherothrombotic cerebral infarction, lacunar stroke, brain embolism), cerebrovascular spasm (in particular, transient cerebral artery constriction occurring after subarachnoidal bleeding), moyamoya disease (in particular, Willis' ring artery obstruction), brain major artery obstruction/stenosis and mesenteric vascular obstruction can be cited.
While a compound exerting an effect on such a disease or symptom can have as any of the above compounds as the active ingredient, a polymerized nitroxide radical compound can be cited, which, as a desirable one, is the compound represented by the above General Formula (II), and then, as a more desirable one, is a compound represented by the General Formula (II), where L1 is a valence bond or —CH2CH2S—, L2 is methyl imino or methyl iminomethyl and
The entirety of R are residues of cyclic nitroxide radical compound represented by any of the following formulae
where, R′ is a methyl group. When L2 is methyl imino or methyl iminomethyl, disruption of the polymeric micelle that encapsulates the cyclic nitroxide radicals is promoted under acidic pH conditions and radicals are released under the surrounding environment, such that an action that is intrinsic to the cyclic nitroxide radical (refer to Non-patent Reference 1 above) is performed. Therefore, it can be anticipated that the action of the cyclic nitroxide radical may be exerted selectively at an inflammation site or the like, which in general is known to be in an acidic state.
As pharmaceutically acceptable diluents or excipients that can be included in the pharmaceutical composition, any can be cited as long as they are compounds or substances which are additives used ordinarily in the relevant technical field for preparing an injectable (intravenously and intraarterially injected agent), a locally administered agent (including embedding agent in brain) and the like, and which do not have a detrimental influence on the properties or function of the polymerized cyclic nitro radical. Not to be limiting, for injectables, pure water, deionized water or physiological saline may be cited typically as diluents, and buffering agent can also be included in these liquids. In addition, water miscible organic solvents such as ethanol and dimethylsulfoxide may be included in these liquids as long as they do not exert a detrimental influence on the stability of a polymeric micelle formed by the compound represented by General Formula (I). As excipients, sugars or sugar alcohols such as poly(ethylene glycol) (macrogol) of various molecular weights, glucose, lactose and mannitol, which are usable in drug formulation can be cited. As embedding agents in brain, for instance, those with a morphology where the compound is contained in the envelope matrix layer of a stent placed inside the brain can be cited. Referred herein, diluents or excipients (or carriers) that are acceptable in food can be based on those that are pharmaceutically acceptable described above.
Taking an intravenously administered agent as an example, the optimal dosage is not limited since it varies according to the patient's age, symptom, age, gender and the like; however, the dosage of the composition according to the present invention is, per day, from 0.1 to 900 mg/kg and preferably from 1 to 250 mg/kg based on the cyclic nitroxide radical compound in general with respect to an adult, and administration can be from once to three separate times.
Hereinafter, the present invention will be described in more in detail by giving concrete examples; however, they are not meant to limit the present invention is not intended to these modes.
Acetal-PEG-b-PCMS was synthesized according to the following Synthesis Scheme 1:
A heterobifunctional poly(ethylene glycol) (acetal-PEG-SH) (Mn: 4,600; 0.02 mmol, 92 mg) having an acetal group at the α-end and a thiol group at the ω-end was added to a reaction container. Next, the interior of the reaction container was turned into nitrogen atmosphere by repeating three times the operation of vacuuming the interior of the reaction container and blowing in nitrogen gas. To the reaction container, 1 mL of a solution of azobisisobutyronitrile/benzene (0.01 mmol/mL) and chloromethylstyrene (1 mmol, 0.138 mL), was added, heated to 60° C. and stirred for 24 hours. When the reaction mixture was poured into hexane, a white precipitation was generated. In order to eliminate poly(chloromethylstyrene) homopolymer, the obtained precipitate was put under washing operation three times using diethyl ether, which is a good solvent to poly(chloromethylstyrene) homopolymer, and then benzene freeze-drying was performed to obtain a white powder. The amount produced was 134 mg and the yield was 55.1%. A bimodal distribution was observed from the results of size-exclusion chromatography (SEC) measurements of the obtained acetal-PEG-b-PCMS block copolymer (
As a result, the component ratios for PEG and PCMS in the two fractions were found to be approximately equal. In addition, when the 1H NMR spectra were analyzed based on the molecular weight of acetal-PEG-SH determined by SEC in order to calculate the molecular weights of the PCMS segments within the obtained block copolymers, the molecular weights of the PCMS segments were found to be 3,300 and 6,600 respectively (
Acetal-PEG-b-PCMS (Mn: 7,900; 40 mg, 5.2 μmol) was added to a reaction container. Next, 4-amino-TEMPO (88 mg, 520 mmol) was dissolved in 2 mL of dimethylsulfoxide (DMSO) and added to the reaction container, and stirring was performed at room temperature for 5 hours. After the end of the reaction, the reaction mixture was poured into 2-propanol, which had been cooled to −15° C., next, precipitation was performed three times using 2-propanol and then benzene freeze-drying was performed. The yield was 76.3%.
From the results of 1H NMR measurements, it was observed that 100% chloromethyl group reacted and TEMPO was introduced (
Methoxy-PEG-b-PCMS (Mn: 7,900; 200 mg, 30.6 μmol) was added to a reaction container and dissolved in 1 mL of dimethyl formamide (DMF). Next, 4-hydroxy-TEMPO (260 mg, 1.53 mmol) and NaH (70.3 mg, 3 mmol) were dissolved in 2 mL of DMF and added to the reaction container, and stirring was performed at room temperature for 5 hours. After the end of the reaction, the reaction mixture was poured into 2-propanol, which had been cooled to −15° C., next, precipitation was performed three times using 2-propanol and then benzene freeze-drying was performed to obtain the target methoxy-PEG-b-PCMS-O-TEMPO. The yield was 70.0%.
Dissolved in 2 mL of DMF was 20 mg of acetal-PEG-b-PCMS-N-TEMPO, and the polymer solution was added inside of a dialysis membrane (Spectra/Por; molecular weight cut-off size: 3,500; Spectrum Medical Industries Inc., Houston, Tex.) to perform dialysis against 2 L of distilled water. The distilled water was exchanged three times after 2, 4 and 8 hours. After the dialysis, when the average particle size of the obtained RNP was measured by DLS measurements, it was verified to be a monomodal particle with an average particle size of 40 nm (
Except that acetal-PEG-b-PCMS-N-TEMPO in Preparation Example 4 was changed to methoxy-PEG-b-PCMS-O-TEMPO, the operation procedure of Preparation Example 4 was repeated using similar amounts of reactants, solvents, and the like. When DLS measurements were performed in order to confirm the average particle size of O-TEMPO-RNP obtained in this way, it was verified to be monomodal with an average particle size of 40 nm, similarly to N-TEMPO-RNP of Preparation Example 4. Next, a measurement of ESR spectrum of the obtained O-TEMPO-RNP was performed. While in general the small molecule TEMPO in a dilute solution demonstrates a spectrum with three lines due to the interaction between the nitrogen nucleus and the unpaired electrons (refer to
Test 1: pH-Responsiveness of N-TEMPO-RNP and O-TEMPO-RNP
The average particle size and ESR spectra versus pH change for N-TEMPO-RNP obtained in Preparation Example 4 were measured by dynamic light scattering (DLS) and ESR. It was revealed that while in the region from neutral pH to basic pH the particles were monomodal with an average particle size of 40 nm and there was no change in the scattered intensity, in the acidic region, the scattered intensity decreased and the particle size increased. In addition, it was revealed by ESR measurements that, while at neutral pH and at basic pH the ESR spectrum of RNP was one broad line, under acidic conditions, the shape of the spectrum changed from one line to three lines (top of
In contrast, O-TEMPO-RNP demonstrates similar ESR signals at all pH regions (bottom of
Test 2: Reduction-Resistance of N-TEMPO-RNP Radical against glutathione
It is known that, in general, while the interior of a cell is a reductive environment with high concentrations (0.5 mM to 10 mM) of glutathione present, on the order of only one over 100 to 1000 of that in the cell is present in blood. Thus, the small molecule TEMPO, which possesses a stable radical, is readily reduced upon entering inside a cell, rapidly loosing the ESR signal intensity. Then, in order to evaluate the glutathione reduction-resistance of the polymerized cyclic nitroxide radical, a solution of 64 μM of micelle comprising acetal-PEG-b-PCMS-N-TEMPO(N-TEMPO-RNP) was prepared (pH7.2) using a 900 mM Britton-Robinson buffer solution, and the change in the ESR spectrum was observed in the presence of 10 mM of glutathione. One hour after colocalization with GSH, a decrease of 50% was observed in the intensity of the ESR signal for the small molecule TEMPO (gray bar); in contrast, no change in the ESR signal intensity was observed for the prepared RNP (
Test 3: Reduction-Resistance of N-TEMPO-RNP Radical against ascorbic acid (AsA)
AsA, also referred to as vitamin C, is present in general at high concentrations in blood. The small molecule TEMPO, which possesses a stable radical, is known to be reduced readily in blood after intravital administration and decrease ESR signal intensity rapidly. Thus, in order to evaluate the reduction-resistance of N-TEMPO-RNP against AsA, the change in ESR spectrum of 90 μM of acetal-PEG-b-PCMS-N-TEMPO-prepared N-TEMPO-RNP was observed in the presence of 3.6 mM AsA, in a PBS buffer solution (10 mM, 150 mM NaCl, pH 7.4). The results are shown in
Test 4: In-Blood Retention of N-TEMPO-RNP and O-TEMPO-RNP
Each of N-TEMPO-RNP and O-TEMPO-RNP prepared as described above was independently injected in the vein of a different mouse, and after a given time period, laparotomy was performed to carry out blood collection from the heart. After blood collection, centrifugal separation was performed at 6,200 rpm (2000×g) for 10 minutes to obtain blood plasma. When the ESR spectrum of the obtained blood plasma was measured, an ESR signal of each RNP was observed from within the blood. In addition, when the disposition thereof was examined, the half-life was approximately 20 minutes for the former (
Test 5: Treatment of Cerebral Ischemia Model Rat
(1) Instead of acetal-PEG-SH used in the preparation of acetal-PEG-b-PCMS of Preparation Example 2, methoxy-PEG-SH was used to prepare methoxy-PEG-b-PCMS similarly, which served as raw materials for operating according to Preparation Examples 3 and 4 to obtain a polymer solution of methoxy-PEG-b-PCMS-N-TEMPO in dimethyl formamide, which was dialyzed and then, when the average particle size of the obtained RNP(N-TEMPO-RNP) was measured by DLS measurement, monomodal particles with an average particle size of 60 nm were observed. Physiological saline was added to the N-TEMPO-RNP aqueous solution obtained in this way, which was concentrated with a centrifugal evaporator so as to have a concentration of 100% physiological saline and adjusted to 20 mg/mL.
Cerebral ischemia model rats were prepared as follows:
SD strain male rats (3 weeks-old) were acclimatized for one week, and then inhalation anesthesia by isoflurane was performed. The common carotid artery was constricted with an occluding string and recirculated two hours after. Immediately after reperfusion, N-TEMPO-RNP (20 mg/mL) was injected from the femoral vein (or common carotid artery) at a concentration of 120 mg/mL and a rate of 1 mL/min. After 24 hours, they were sacrificed by Nembutal injection anesthesia. The brain was removed, the surface was hardened with liquid oxygen or dry ice, then, sliced to 2 mm thickness, and both sides were stained with a 2,3,5-triphenyl tetrazolium chloride (TTC) solution at 37 degrees, 30 minutes each. As controls, tests were also performed in parallel for a group in which no administration was performed after reperfusion and a group administered with Tempol at the same molar concentration as TEMPO in the polymerized TEMPO micelle (also called N-TEMPO-RNP). Each trial number was N=3.
Examples of TTC-stained brain photographs are shown in
Meanwhile, with arterial administration, more cell death-protection effect at a given level or greater was obtained than with intravenous administration, also with Tempol. This is thought to be due to the fact that with arterial administration, Tempol reaches the diseased site before being reduced by a blood circulating component. In addition, it is thought to be due to the fact that, in the case of venous administration, by being carried by the bloodstream and dispersed inside the body, the amount reaching the affected area is fewer than with administration from the common carotid artery.
In addition, the surface area of the infarcted portion (infract volume) was quantified in the results of TTC staining and shown in
(2) Tests were performed on cerebral ischemia model rats such as those described above, with additional trial numbers and controls or comparative examples.
The agents or controls the tests were performed with were as follows: performed with the above-mentioned N-TEMPO-RNP, a group with nothing administered after reperfusion as control, a group administered with Tempol at the same molar concentration as TEMPO in N-TEMPO-RNP, a group administered with 100% physiological saline and a group of micelle of methoxy-PEG-b-PCMS with no TEMPO added (hereinafter also referred to as Blank-NP; prepared according to Preparation Example 4) also in parallel. The respective test number N was N=20 for N-TEMPO-RNP and Tempol, and N=8 for physiological saline and Blank-NP. Analyses of body temperature, blood pressure and blood gas of the rat during operation were performed. The change in body weight between prior to model preparation and prior to sacrifice was also examined.
No large differences were observed in the body weight change in each group before and after the test. In addition, difference was observed in the results of body weight and blood gas analyses, confirming that model preparation for each group was performed under a given condition. Average blood pressure at the time of agent administration decreased significantly for Tempol (refer to
Regarding the cerebral infarction surface area (infract volume), N-TEMPO-RNP decreased the cerebral infarction surface area significantly compared to physiological saline, Blank-NP and Tempol (
Also with the neurological symptom score (0: when the tail is held and raised, both anterior limbs are extended, no defects; 1: when the tail is held and raised, left anterior limb is on the chest and the right anterior limb is extended; 2: in addition to score 1, resistance to lateral push is decreased; 3: in addition to score 2, upper half body is twisted; the larger these values, the more severe the symptoms), N-TEMPO-RNP decreased neurological symptoms more significantly than Tempol (refer to
Test 6: Preparation of ESR Probe for the Purpose of Visualizing Reactive Oxygen Species (ROS) in a Cancerous/Inflammatory Tissue
It has become apparent that oxidative stress induced by reactive oxygen species (ROS) is causes of various disorders and diseases. For instance, it is known that ROS is produced in cancerous tissues and inflammatory tissues. Visualization of ROS in vivo is extremely important for elucidating the relation ship between ROS and a disease. ESR imaging has been drawing attention in recent years as a tool for visualizing oxidation-reduction reaction in vivo. While various probes for ESR imaging have been developed so far, small molecule ESR probes have a short half-life in blood, in addition have no function for accumulating specifically a the target site, such that observation at a specific tissue is difficult. In addition, it is known that the pH is decreased in inflammation sites and cancerous tissues where oxidative stress are thought to be involved. Thus, exploiting the fact that N-TEMPO-RNP is disrupted under acidic conditions, the possibility of developing a ROS visualizable novel ESR probe was examined.
(1) Development of ROS Visualizable ESR Probe (N-TEMPO-RNP-H)
To a DMF solution of 5 mg/mL methoxy-PEG-b-PCMS-N-TEMPO, 1500-fold in amounts of anhydrous hydrazine was added, the polymer solution was added inside a dialysis membrane (Spectra/Por; molecular weight cut-off size: 3,500; Spectrum Medical Industries Inc., Houston, Tex.) and a dialysis was performed against 2 L of distilled water. The distilled water was exchanged three times after 2, 4 and 8 hours. After the dialysis, when the average particle size of the obtained RNP was measured by DLS, it was verified to be a monomodal particle with an average particle size of 40 nm (similarly to the preparation of the nanoparticle (N-TEMPO-RNP) from acetal-PEG-b-PCMS-N-TEMPO according to Preparation Example 4). measurements of ESR spectra were performed for the RNP obtained in this way. While RNP demonstrated a spectrum with one broad line when no anhydrous hydrazine was added (
(2) Model Experiment of Visualization of In Vivo Oxidation Reaction
To N-TEMPO-RNP-H (46 mM, 60 μL), an aqueous solution of H2O2 (500 mM, 60 μL) and Horseradish peroxidase (HRP)/100 mM Britton Robinson (375 U/mL, 480 μL) were added, oxidation reaction of N-TEMPO-RNP-H was performed at acidic pH (pH 5.6) and neutral pH (pH 7.4) to observe the change in ESR spectra. While the rate of oxidation reaction is known to decrease with the pH becoming acidic in general for small molecule TEMPOL, when polymerized micellized N-TEMPO-RNP-H was used, the ESR signal intensity was found to be enhanced remarkably only under the condition of pH 5.6. From this result, it is inferred that N-TEMPO-RNP-H can be used as a probe enabling visualization of ROS under acidic conditions around cancer and inflammatory tissue (
As described above, the cyclic nitroxide radical stabilization method provided by the present invention, and the polymerized compound provided by the method, can be used in the fields of medicine and diagnostic, particularly since in vitro stabilization of a stable radical is achieved.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2008-120626 | May 2008 | JP | national |
| 2008-178150 | Jul 2008 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|