Patent Grant
7750112
The present invention relates to novel polymers comprising benzotriazol containing repeating units and to their use in optical devices, such as an optical device comprising an electroluminescent device or a photovoltaic device.
Derivatives of poly(p-phenylenevinylene) have been known for some time as electroluminescence (EL) materials (see, for example, WO90/13148).
WO98/11150 discloses triazine polymers of formula
and their use in electroluminescence (EL) arrangements.
WO00/46321 and U.S. Pat. No. 6,512,083 relate to fluorene-containing polymers and their use in EL arrangements.
WO01/49768 discloses luminescent polymers comprising a triarylene repeat unit which comprises a triarylene of general formula
which is substituted or unsubstituted and an arylene repeat unit —[—Ar—]— that is different from the triarylene repeat unit wherein X″ and Y″ are each independently O, S, CR, SiR or NR and each R is independently alkyl, aryl or H.
WO97/12882 relates to benzotriazole polymers having general formula
which are useful as ultraviolet light stabilizers and metal chelaters. The products of WO97/12882 are derivatives of 4-hydroxyacetophenone benzotriazole and 4-hydroxyphenylmethyl carbinol benzotriazole.
WO02/059121 relates to monomers having general formula
which may be substituted or unsubstituted: where X′ and Y′ are the same or different and are reactive groups capable of undergoing chain extension; X is O, S, NR, RC—CR or RC═CR; Y is O, S, NR, RC—CR or RC═CR; R is H or a substituent group; and Ar is a substituted or unsubstituted aryl or heteroaryl group.
There are a number of challenges faced with the introduction of organic EL displays when their performance is compared with existing technologies. Obtaining the exact color coordinates required by specific guidelines (i.e. NTSC) has been problematic. The operational lifetime of the EL device is relatively lower when contrasted to the existing inorganic technology. In addition, producing a material with a pure blue color and a long lifetime is one of the greatest problems for this industry.
Accordingly, it is the object of the present invention to provide novel materials, which show significant advantages in color purity, device efficiency and/or operational lifetime, when incorporated in optical devices.
Said object is solved by the polymers of the present invention comprising benzotriazole containing repeating units. Optical devices, comprising the polymers of the present invention, can show significant advantages in color purity, device efficiency and/or operational lifetime. In addition, the polymers can have good solubility characteristics and relatively high glass transition temperatures, which facilitates their fabrication into coatings and films that are relatively thin, thermally stable, and relatively tree of defects. If the polymers contain end groups which are capable of being crosslinked, the crosslinking of such groups after the films or coating is formed increases the solvent resistance thereof, which is beneficial in applications wherein one or more solvent-based layers of material are deposited thereon.
Accordingly, the polymers of the present invention should have a glass transition temperature above 100° C., especially a glass transition temperature above 150° C.
The repeating units of the polymers of the present invention comprise a benzotriazole backbone
wherein the phenyl group of the benzotriazole may be substituted in any pattern, including fused ring systems. The benzotriazole monomer (or comonomer) may give rise to a main-chain or a pendant structure of the polymer, both of which may be conjugated or non-conjugated. The present invention is not limited to a benzotriazole structure where one connection to the polymer is through the phenyl ring or a group attached thereto and the other is through the substituent attached to the nitrogen atom. Other structures may exist where both links to the polymer chain are on the phenyl ring or a group attached thereto, and similarly, where both polymer connections are on the substituent attached to the nitrogen atom. In addition, the benzotriazole moiety may be connected to a polymer in a pendant manner.
Examples of the benzotriazole backbones are groups of the following formula
wherein A21, A22, A23, A24, A11, A12, A13, A14′, A15, A16, A17 and A18 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C1-C18perfluoroalkyl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28, wherein E, D, G and R28 are defined as below, or
two groups A11, A12, A13, A14′, A15, A16, A17 and A18, which are neighbouring to each other, are a group
wherein A31, A32, A33, A34, A35, A36 and A37 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C1-C18perfluoroalkyl, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28, and up to 2 substituents A21, A22, A23, A24, A11, A12, A13, A14′, A15′, A16, A17, A18, A31, A32, A33, A34, A35, A36 and A37 can represent the connection to the polymer.
As used herein the term “polymer of the present invention” refers to polymers having repeating units of formula I, including formula Ia to Id, II, including formula IIa to IIg, formula III, and/or formula IV, including formula IVa to IVc.
Accordingly, the present invention relates to polymers comprising a repeating unit of the formula
x and y are 0 or 1,
X1 and X2 are independently of each other a divalent linking group,
Ar1, Ar2, Ar3, Ar4, Ar5, A6, Ar7 and A8 are independently of each other an aryl group, or a heteroaryl group, which can optionally be substituted, especially a C6-C30aryl group, or a C2-C26heteroaryl group, which can optionally be substituted.
In the repeating units of formula IV at least one of x and y is 1. If x and y are both 1, repeating units of formula
results, which could be seen as a “crosslinking structure”, present in 0.01-3%. Preferred are, however, repeating units of formula
Among the repeating units of the formula I, repeating units of formula
are preferred, wherein Ar2 is as defined above,
R1 and R2 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C1-C18perfluoroalkyl, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28,
or two substituents R1 and R2, which are adjacent to each other, are a group
D is —CO—; —COO—; —S—; —SO—; —SO2—; —O—; —NR25—; —SiR30R31—; —POR32—; —CR23═CR24—; or —C≡C—; and
E is —OR29; —SR29; —NR25R26; —COR28; —COOR27; —CONR25R26; —CN; —OCOOR27; or halogen; G is E, or C1-C18alkyl, wherein
R23, R24, R25 and R26 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—; or
R25 and R26 together form a five or six membered ring, in particular
R27 and R28 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R29 is H; C6-C18aryl; C6-C18aryl, which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R30 and R31 are independently of each other C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl, and
R32 is C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl.
Preferably, R1 and R2 are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, or sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
D is preferably —CO—, —COO—, —S—, —SO—, —SO2—, —O—, —NR25—, wherein R25 is C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, or sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
E is preferably —OR29; —SR29; —NR25R25; —COR28; —COOR27; —CONR25R25; or —CN; wherein R25, R27, R28 and R29 are independently of each other C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
Examples of Ar2 are a single bond, —CO—, —COO—; —S—; —SO—; —SO2—; —O—; —CR23═CR24—; or —
n1, n2, n3, n4, n5, n6 and n7 are integers of 1 to 10, in particular 1 to 3,
R6 and R7 are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28, R8 is C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, or C7-C25aralkyl,
R9 and R10 are independently of each other C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, or C7-C25aralkyl, or
R9 and R10 form a ring, especially a five- or six-membered ring,
R14′ and R15′ are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, or C2-C20heteroaryl which is substituted by G,
D is —CO—; —COO—; —S—; —SO—; —SO2—; —O—; —NR25—; —SiR30R31—; —POR32—; —CR23═CR24—; or —C≡C—; and
E is —OR29; —SR29; —NR25R26; —COR28; —COOR27; —CONR25R26; —CN; —OCOOR27; or halogen; G is E, or C1-C18alkyl, wherein
R23, R24, R25 and R26 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—; or
R25 and R26 together form a five or six membered ring, in particular
R27 and R28 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R29 is H; C6-C18aryl; C6-C18aryl, which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R30 and R31 are independently of each other C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl, and
R32 is C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl.
Preferably, R6 and R7 are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl, C1-C18alkyl which is substituted by E and/or interrupted by D, such as —CH2OCH3, —CH2OCH2CH3, —CH2OCH2CH2OCH3, or —CH2OCH2CH2OCH2CH3, C6-C24aryl, such as phenyl, naphthyl, or biphenyl, C6-C24aryl which is substituted by G, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, or —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3)3, or —C6H4tBu.
R8 is preferably H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, n-heptyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
Preferably, R9 and R10 are independently of each other H, C1-C18alkyl, such as n-butyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl, C1-C18alkyl which is substituted by E and/or interrupted by D, such as —CH2(OCH2CH2)wOCH3, w=1, 2, 3, or 4, C6-C24aryl, such as phenyl, naphthyl, or biphenyl, C6-C24aryl which is substituted by G, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3), or —C6H4tBu, or R9 and R10 together form a 4 to 8 membered ring, especially a 5 or 6 membered ring, such as cyclohexyl, or cyclopentyl.
Preferably, R14′ and R15′ are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, Iso-propyl, n-butyl, isobutyl, or sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
D is preferably —CO—, —COO—, —S—, —SO—, —SO2—, —O—, —NR25—, wherein R25 is C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, or sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
E is preferably —OR29; —SR29; —NR25R25; —COR28; —COOR27; —CONR25R25; or —CN; wherein R25, R27, R28 and R29 are independently of each other C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl. G is E, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl.
Among the above-mentioned groups Ar2 the following groups are preferred:
wherein R6, R7, R9 and R10 are defined as above and n1 and n2 are 1, 2, or 3.
The polymer of the present invention comprise the repeating unit of the formula I in an amount of from 0.5 mol % to 100 mol %, especially in an amount of from 20 mol % to 60 mol %, wherein the sum of all repeating units (monomers) is 100 mol %. Accordingly, the polymers of the present invention can comprise besides the repeating unit of the formula I additional repeating units in an amount of up to 99.5 mol %, especially in an amount of from 80 mol % to 40 mol %.
Suitable additional repeating units T are selected from the group consisting of
p is an integer from 1 to 10, especially 1, 2 or 3,
q is an integer from 1 to 10, especially 1, 2 or 3,
s is an integer from 1 to 10, especially 1, 2 or 3,
R14 and R15 are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, or C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G,
R16 and R17 are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, or C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28,
R18 is H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl, or C1-C18alkyl which is interrupted by —O—;
R19 and R20 are independently of each other C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, or C7-C25aralkyl,
R19 and R20 together form a group of formula ═CR100R101, wherein
R100 and R101 are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, or C2-C20heteroaryl which is substituted by G, or
R19 and R20 form a ring, especially a five- or six-membered ring, and
D and E are as defined above.
If R19 and R20 together form a group of formula ═CR100R101, T is preferably a group of formula
wherein R102 and R103 are independently of each other C1-C18alkyl, C1-C18alkoxy, C6-C10aryl, C6-C10aryloxy, or di(C1-C18alkyl)amino, wherein the aryl or aryloxy groups optionally can be substituted by C1-C8alkyl (cf. U.S. Pat. No. 6,512,083).
Preferred examples of T are selected from groups of formula
R16 and R17 are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl, C1-C18alkyl which is substituted by E and/or interrupted by D, such as —CH2OCH3, —CH2OCH2CH3, —CH2OCH2CH2OCH3, or —CH2OCH2CH2OCH2CH3, C6-C24aryl, such as phenyl, naphthyl, or biphenyl, C6-C24aryl which is substituted by G, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, or —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3)3, or —C6H4tBu,
R18 is H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, n-heptyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl, and
R19 and R20 are independently H, C1-C18alkyl, such as n-butyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl, C1-C18alkyl which is substituted by E and/or interrupted by D, such as —CH2(OCH2CH2)wOCH3, w=1, 2, 3, or 4, C6-C24aryl, such as phenyl, naphthyl, or biphenyl, C6-C24aryl which is substituted by G, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3)3, or —C6H4tBu, or R9 and R10 together form a 4 to 8 membered ring, especially a 5 or 6 membered ring, such as cyclohexyl, or cyclopentyl.
Particularly preferred are co-monomers T, which are selected from the group consisting of
R16 and R17 are independently of each other C1-C18alkyl, especially C4-C12alkyl, which can be interrupted by one or two oxygen atoms,
R18 is C1-C18alkyl, and
R19 and R20 are independently of each other C1-C18alkyl, especially C4-C12alkyl, which can be interrupted by one or two oxygen atoms, or
R19 and R20 form a five or six membered carbocyclic ring, which optionally can be substituted by C1-C4alkyl.
Especially preferred are polymers, comprising a repeating unit of the formula
and a co-monomer T in an amount of 0 to 99.5 mol %, especially in an amount of 40 to 80 mol %, wherein the sum of the repeating unit(s) and the co-monomer is 100 mol %, wherein
A1 is hydrogen, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A2 is hydrogen, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A3 is hydrogen, or C1-C18alkoxy, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A4 is hydrogen, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A5 is hydrogen, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl, di(C1-C18alkyl)amino, or C1-C18alkoxy, such as methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, isobutoxy, sec-butoxy, t-butoxy, 2-methylbutoxy, n-pentoxy, isopentoxy, n-hexoxy, 2-ethylhexoxy, or n-heptoxy,
A6 is hydrogen, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A7 is hydrogen, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl, or C1-C18alkoxy, such as methoxy, ethoxy, n-propoxy, iso-propoxy, n-butoxy, isobutoxy, sec-butoxy, t-butoxy, 2-methylbutoxy, n-pentoxy, isopentoxy, n-hexoxy, 2-ethylhexoxy, or n-heptoxy, and
T is a group of formula
wherein s is one or two,
R16 and R17 are independently of each other C1-C18alkyl, especially C4-C12alkyl, especially hexyl, heptyl, 2-ethylhexyl, and octyl, which can be interrupted by one or two oxygen atoms, C1-C18alkoxy, especially C4-C12alkoxy, especially hexyloxy, heptyloxy, 2-ethylhexyloxy, and octyloxy, which can be interrupted by one or two oxygen atoms,
and R19 and R20 are independently of each other C1-C18alkyl, especially C4-C12alkyl, especially hexyl, heptyl, 2-ethylhexyl, and octyl, which can be interrupted by one or two oxygen atoms.
In another aspect, the polymers of the present invention comprise repeating units of formula II. Examples of repeating units of the formula II are
wherein Ar4 is as defined above,
R1 and R2 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C1-C18perfluoroalkyl, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28,
or two substituents R1 and R2, which are adjacent to each other, are a group
D is —CO—; —COO—; —S—; —SO—; —SO2—; —O—; —NR25—; —SiR30R31—; —POR32—; —CR23═CR24—; or —C≡C—; and
E is —OR29; —SR29; —NR25R26; —COR28; —COOR27; —CONR25R26; —CN; —OCOOR27; or halogen; G is E, or C1-C18alkyl, wherein
R23, R24, R25 and R26 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—; or
R25 and R26 together form a five or six membered ring, in particular
R27 and R28 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R29 is H; C6-C18aryl; C6-C18aryl, which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R30 and R31 are independently of each other C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl, and
R32 is C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl.
Repeating units of formula (IIe), (IIf), and (IIg) are most preferred.
Preferably, R1 and R2 are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, or sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
D is preferably —CO—, —COO—, —S—, —SO—, —SO2—, —O—, —NR25—, wherein R25 is C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, or sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, or biphenyl.
E is preferably —OR29; —SR29; —NR25R25; —COR28; —COOR27; —CONR25R25; or —CN; wherein R25, R27, R28 and R29 are independently of each other C1-C18 alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl, or C6-C24 aryl, such as phenyl, naphthyl, or biphenyl. G is E, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, or 2-ethyl-hexyl.
Ar4 is preferably a group of formula
p is an integer from 1 to 10, especially 1, 2 or 3,
q is an integer from 1 to 10, especially 1, 2 or 3,
r is an integer of 0 to 10, in particular 0, 1, 2 or 3,
R3 to R8 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —COR28, or
two substituents R3 to R8, which are adjacent to each other, are a group
R14′ and R15′ are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, or C2-C20heteroaryl which is substituted by G,
R16 is C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, which optionally can be substituted, wherein
D is —CO—; —COO—; —S—; —SO—; —SO2—, —O—; —NR25—; —SiR30R31—; —POR32—; —CR23═CR24—; or —C≡C—; and
E is —OR29; —SR29; —NR25R26; —COR28; —COOR27; —CONR25R26; —CN; —OCOOR27; or halogen; G is E, or C1-C18alkyl, wherein
R23, R24, R25 and R26 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—; or
R25 and R26 together form a five or six membered ring, in particular
R27 and R28 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R29 is H; C6-C18aryl; C6-C18aryl, which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R30 and R31 are independently of each other C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl, and
R32 is C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl.
Preferably, R3, R4, R5, R6, R7 and R8 are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl, C1-C18alkyl which is substituted by E and/or interrupted by D, such as —CH2OCH3, —CH2OCH2CH3, —CH2OCH2CH2OCH3, or —CH2OCH2CH2OCH2CH3, C6-C24aryl, such as phenyl, naphthyl, or biphenyl, C6-C24aryl which is substituted by G, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, or —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3)3, or —C6H4tBu.
Preferably, R14′ and R15′ are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, and sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, and biphenyl.
R16 is preferably H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, and sec-butyl, or C6-C24aryl, such as phenyl, naphthyl, and biphenyl.
D is preferably —CO—, —COO—, —S—, —SO—, —SO2—, —O—, —NR25—, wherein R25 is C1-C18 alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, hexyl, octyl, and 2-ethyl-hexyl, or C6-C24aryl, such as phenyl, naphthyl, and biphenyl.
E is preferably —OR29, —SR29, —NR25R25, —COR28, —COOR27, —CONR25R25, or —CN, wherein R25, R27, R28 and R29 are independently of each other C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, 2-ethyl-hexyl, or C6-C24aryl, such as phenyl, naphthyl, and biphenyl. G is E, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, hexyl, octyl, 2-ethyl-hexyl.
Another aspect of the present invention, is directed to polymers, comprising repeating units of the formula
wherein
Ar5 and Ar6 are independently of each other an aryl group, or a heteroaryl group, which can optionally be substituted, especially a C6-C30aryl group, or a C2-C28heteroaryl group, which can optionally be substituted.
The repeating unit of formula III is not a repeating unit of formula
especially Ar6 is not a phenyl group substituted by a hydroxy group in ortho position to the bonding to the benzotriazole unit
Examples of
are groups of the following formula
wherein A21, A22, A23, A24, A11, A12, A13, A14′, A15, A16, A17 and A18 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C1-C18perfluoroalkyl, C6-C24aryl, C8-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28, wherein E, D, G and R28 are defined as above, or two groups A11, A12, A13, A14′, A15, A16, A17 and A18, which are neighbouring to each other, are a group
wherein A31, A32, A33, A34, A35, A36 and A37 are independently of each other H, halogen, SO3−, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C1-C18perfluoroalkyl, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, C7-C25aralkyl, or —CO—R28.
Examples of Ar6 are groups of formula
wherein the dotted line represent the bond to the benzotriazole ring;
R56 and R57 are independently of each other H; C1-C18alkyl; C1-C18alkyl which is substituted by E and/or interrupted by D; C6-C24aryl; C6-C24aryl which is substituted by G; C2-C20heteroaryl; C2-C20heteroaryl which is substituted by G; C2-C18alkenyl; C2-C18alkynyl; C1-C18alkoxy; C1-C18alkoxy which is substituted by E and/or interrupted by D; or C7-C25aralkyl;
R58 is H; C1-C18alkyl; C1-C18alkyl which is substituted by E and/or interrupted by D; C6-C24aryl; or C7-C25aralkyl;
R59 and R60 are independently of each other H; C1-C18alkyl; C1-C18alkyl which is substituted by E and/or interrupted by D; C6-C24aryl; C6-C24aryl which is substituted by G; C2-C20heteroaryl; C2-C20heteroaryl which is substituted by G; C2-C18alkenyl; C2-C18alkynyl; C1-C18alkoxy; C1-C18alkoxy which is substituted by E and/or interrupted by D; or C7-C25aralkyl;
R71 is H, C1-C18alkyl, —C≡N, —CONR25R26 or —COOR27,
D is —CO—; —COO—; —OCOO—; —S—; —SO—; —SO2—; —O—; —NR25—; —SiR30R31—; —POR32—; —CR23═CR24—; or —C≡C—; and
E is —OR29; —SR29; —NR25R26; —COR28; —COOR27; —CONR25R26; —CN; —OCOOR27; or halogen; G is E, or C1-C18alkyl, wherein
R23; R24; R25 and R26 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl; C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—; or
R25 and R26 together form a five or six membered ring, in particular
R27 and R28 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—, and
R29is H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R30 and R31 are independently of each other C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl, and
R32 is C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl.
Most preferred, Ar6 is a group of the formula
wherein the dotted line represent the bond to the benzotriazole ring and R71 is H, alkyl, —C≡N, or —COOR27, wherein R27 is H, or C1-C18alkyl, which optionally can be interrupted by one or more oxygen atoms, especially C4-C12alkyl, which can be interrupted by one or two oxygen atoms.
The polymer of the present invention comprise the repeating unit of the formula II and/or III in an amount of from 0.5 mol % to 100 mol %, especially in an amount of from 20 mol % to 80 mol %, wherein the sum of all repeating units (monomers) is 100 mol %. Accordingly, the polymers of the present invention can comprise besides the repeating unit of the formula II and/or III additional repeating units in an amount of up to 99.5 mol %, especially in an amount of from 80 mol % to 40 mol %. Suitable additional repeating units are the repeating units T described for the polymers comprising repeating units of the formula I.
As stated above among the repeating units of the formula IV, repeating units of the formula
against repeating units of the formula
wherein
Ar7, Ar7′, Ar8 and Ar8′ are independently of each other a C6-C30aryl group, or a C2-C26heteroaryl group, which can optionally be substituted,
X1 and X2 are independently of each other a group of the formula
wherein the dotted line represent the bond to the benzotriazole unit,
R56 and R57 are independently of each other H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, or C7-C25aralkyl,
R58 is H, C1-C18alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, or C7-C25aralkyl,
R59 and R60 are independently of each other H, C1-C18 alkyl, C1-C18alkyl which is substituted by E and/or interrupted by D, C6-C24aryl, C6-C24aryl which is substituted by G, C2-C20heteroaryl, C2-C20heteroaryl which is substituted by G, C2-C18alkenyl, C2-C18alkynyl, C1-C18alkoxy, C1-C18alkoxy which is substituted by E and/or interrupted by D, or C7-C25aralkyl, or R59 and R60 form a ring, especially a five- or six-membered ring,
R71 is H, C1-C18alkyl, —C≡N, —CONR25R26 or —COOR27,
D is —CO—; —COO—; —OCOO—; —S—; —SO—; —SO2—; —O—; —NR25—; —SiR30R31—; —POR32—; —CR23═CR24—; or —C≡C—; and
E is —OR29; —SR29; —NR25R26; —COR28; —COOR27; —CONR25R26; —CN; —OCOOR27; or halogen; G is E, or C1-C18alkyl, wherein
R23, R24, R25 and R26are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—; or
R25 and R26 together form a five or six membered ring, in particular
R27 and R28 are independently of each other H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, or C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—, and
R29 is H; C6-C18aryl; C6-C18aryl which is substituted by C1-C18alkyl, C1-C18alkoxy; C1-C18alkyl; or C1-C18alkyl which is interrupted by —O—,
R30 and R31 independently of each other C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl, and
R32 is C1-C18alkyl, C6-C18aryl, or C6-C18aryl, which is substituted by C1-C18alkyl.
Preferably, R56 and R57 are independently of each other H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, and n-heptyl, C1-C18alkyl, which is substituted by E and/or interrupted by D, such as —CH2OCH3, —CH2OCH2CH3, —CH2OCH2CH2OCH3, and —CH2OCH2CH2OCH2CH3, C6-C24aryl, such as phenyl, naphthyl, and biphenyl, or C6-C24aryl, which is substituted by g, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3)3, and —C6H4tBu.
R58 is preferably H, C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, and n-heptyl, or C6-C24aryl, such as phenyl, naphthyl, and biphenyl.
Preferably, R59 and R60 are independently of each other H, C1-C18alkyl, such as n-butyl, sec-butyl, hexyl, octyl, and 2-ethyl-hexyl, C1-C18alkyl which is substituted by E and/or interrupted by D, such as —CH2(OCH2CH2)wOCH3, w=1, 2, 3, or 4, C6-C24aryl, such as phenyl, naphthyl, and biphenyl, C6-C24aryl which is substituted by G, such as —C6H4OCH3, —C6H4OCH2CH3, —C6H3(OCH3)2, —C6H3(OCH2CH3)2, —C6H4CH3, —C6H3(CH3)2, —C6H2(CH3)3, and —C6H4tBu, or R59 and R60 together form a 4 to 8 membered ring, preferably a 5 or 6 membered ring, such as cyclohexyl, and cyclopentyl.
R71 is preferably H, —CONR25R25 or —CN, wherein R25 is H, C1-C18alkyl, or C6-C24aryl, such as phenyl, naphthyl, and biphenyl.
Most preferred are polymers, comprising a repeating unit of the formula
and/or
and a repeating unit T in an amount of 0 to 99.5 mol %, especially in an amount of 40 to 80 mol %, wherein the sum of the repeating unit(s) and the co-monomer is 100 mol %, wherein
wherein the dotted line is the bond to the nitrogen atom of the benzotriazole unit,
wherein the dotted lines are the bonds to the nitrogen atoms of the benzotriazole unit, A41 is hydrogen, C1-C18alkoxy, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A42 is hydrogen, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
A43 is hydrogen, or C1-C18alkoxy, or C1-C18alkyl, such as methyl, ethyl, n-propyl, iso-propyl, n-butyl, isobutyl, sec-butyl, t-butyl, 2-methylbutyl, n-pentyl, isopentyl, n-hexyl, 2-ethylhexyl, or n-heptyl,
X1 and X2 are independently of each other a group of the formula
wherein the dotted line represent the bond to the benzotriazole unit, R71 is H, C1-C18alkyl, —C≡N, or —COOR27, wherein
R27 is H; or C1-C18alkyl, which can be interrupted by one or more oxygen atoms, especially C4-C12alkyl, which can be interrupted by one or two oxygen atoms, and
T is a group of formula
wherein R59 and R60 independently of each other C1-C18alkyl, especially C4-C12alkyl, which can be interrupted by one or two oxygen atoms.
The polymers of this invention preferably have a weight average molecular weight of 50,000 Daltons or greater, more preferably 100,000 Daltons or greater, and most preferably 150,000 Daltons or greater; preferably 1,000,000 Daltons or less, more preferably 500,000 Daltons or less and most preferably 250,000 Daltons or less. Molecular weights are determined according to gel permeation chromatography using polystyrene standards.
A further embodiment of the present invention is represented by the monomers of the formula
x and y are 0 or 1,
Ar1, Ar2, Ar3, Ar4, Ar5 and Ar6 are Independently of each other an aryl group, or a heteroaryl group, which optionally can be substituted, especially a C6-C30aryl group, or a C2-C26heteroaryl group, which can optionally be substituted, and
X11 is independently in each occurrence a halogen atom, or —B(OH)2, —B(OY1)2 or
wherein Y1 is independently in each occurrence a C1-C10alkyl group and Y2 is independently in each occurrence a C2-C10alkylene group, such as —CY3Y4—CY5Y6—, or —CY7Y8—CY9Y10—CY11Y12—, wherein Y3, Y4, Y5, Y6, Y7, Y8, Y9, Y10, Y11 and Y12 are independently of each other hydrogen, or a C1-C10alkyl group, especially —C(CH3)2C(CH3)2—, or —C(CH3)2CH2C(CH3)2—, which are starting materials in the preparation of the polymers of formula I to IV.
Halogen is fluorine, chlorine, bromine and iodine.
C1-C18alkyl is a branched or unbranched radical such as for example methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, 2-ethylbutyl, n-pentyl, isopentyl, 1-methylpentyl, 1,3-dimethylbutyl, n-hexyl, 1-methylhexyl, n-heptyl, isoheptyl, 1,1,3,3-tetramethylbutyl, 1-methylheptyl, 3-methylheptyl, n-octyl, 2-ethylhexyl, 1,1,3-trimethylhexyl, 1,1,3,3-tetramethylpentyl, nonyl, decyl, undecyl, 1-methylundecyl, dodecyl, 1,1,3,3,5,5-hexamethylhexyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, or octadecyl.
C1-C18perfluoroalkyl is a branched or unbranched radical such as for example —CF3, —CF2CF3, —CF2CF2CF3, —CF(CF3)2, —(CF2)3CF3, and —C(CF3)3.
C1-C18alkoxy radicals are straight-chain or branched alkoxy radicals, e.g. methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, tert-butoxy, amyloxy, isoamyloxy or tert-amyloxy, heptyloxy, octyloxy, isooctyloxy, nonyloxy, decyloxy, undecyloxy, dodecyloxy, tetradecyloxy, pentadecyloxy, hexadecyloxy, heptadecyloxy and octadecyloxy.
C2-C18alkenyl radicals are straight-chain or branched alkenyl radicals, such as e.g. vinyl, allyl, methallyl, isopropenyl, 2-butenyl, 3-butenyl, isobutenyl, n-penta-2,4-dienyl, 3-methyl-but-2-enyl, n-oct-2-enyl, n-dodec-2-enyl, isododecenyl, n-dodec-2-enyl or n-octadec enyl.
C2-C24alkynyl is straight-chain or branched and preferably C2-8alkynyl, which may be unsubstituted or substituted, such as, for example, ethynyl, 1-propyn-3-yl, 1-butyn-4-yl, 1-pentyn-5-yl, 2-methyl-3-butyn-2-yl, 1,4-pentadiyn-3-yl, 1,3-pentadiyn-5-yl, 1-hexyn-6-yl, cis-3-methyl-2-penten-4-yn-1-yl, trans-3-methyl-2-penten-4-yn-1-yl, 1,3-hexadiyn-5-yl, 1-octyn-8-yl, 1-nonyn-9-yl, 1-decyn-10-yl, or 1-tetracosyn-24-yl.
C4-C18cycloalkyl is preferably C5-C12cycloalkyl, such as, for example, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl, cyclononyl, cyclodecyl, cyclododecyl. Cyclohexyl and cyclopentyl are most preferred.
C2-C18alkenyl is for example vinyl, allyl, butenyl, pentenyl, hexenyl, heptenyl, or octenyl.
Aryl is usually C6-C30aryl, preferably C6-C24aryl, which optionally can be substituted, such as, for example, phenyl, 4-methylphenyl, 4-methoxyphenyl, naphthyl, biphenylyl, 2-fluorenyl, phenanthryl, anthryl, tetracyl, pentacyl, hexacyl, terphenylyl or quadphenylyl.
C7-C24aralkyl radicals are preferably C7-C15aralkyl radicals, which may be substituted, such as, for example, benzyl, 2-benzyl-2-propyl, β-phenethyl, α,α-dimethylbenzyl, ω-phenyl-butyl, ω-phenyl-octyl, ω-phenyl-dodecyl or 3-methyl-5-(1′,1′,3′,3′-tetramethyl-butyl)-benzyl.
C2-C26heteroaryl is a ring with five to seven ring atoms or a condensed rig system, wherein nitrogen, oxygen or sulfur are the possible hetero atoms, and is typically an unsaturated heterocyclic radical with five to 30 atoms having at least six conjugated π-electrons such as thienyl, benzo[b]thienyl, dibenzo[b,d]thienyl, thianthrenyl, furyl, furfuryl, 2H-pyranyl, benzofuranyl, isobenzofuranyl, dibenzofuranyl, phenoxythienyl, pyrrolyl, imidazolyl, pyrazolyl, pyridyl, bipyridyl, triazinyl, pyrimidinyl, pyrazinyl, pyridazinyl, indolizinyl, isoindolyl, indolyl, indazolyl, purinyl, quinolizinyl, chinolyl, isochinolyl, phthalazinyl, naphthyridinyl, chinoxalinyl, chinazolinyl, cinnolinyl, pteridinyl, carbazolyl, carbolinyl, benzotriazolyl, benzoxazolyl, phenanthridinyl, acridinyl, perimidinyl, phenanthrolinyl, phenazinyl, isothiazolyl, phenothiazinyl, isoxazolyl, furazanyl or phenoxazinyl, which can be unsubstituted or substituted.
Examples of a five or six membered ring formed by R6 and R7 and R56 and R57, respectively are heterocycloalkanes or heterocycloalkenes having from 3 to 5 carbon atoms which can have one additional hetero atom selected from nitrogen, oxygen and sulfur, for example
which can be part of a bicyclic system, for example
Possible substituents of the above-mentioned groups are C1-C8alkyl, a hydroxyl group, a mercapto group, C1-C8alkoxy, C1-C8alkylthio, halogen, halo-C1-C8alkyl, a cyano group, an aldehyde group, a ketone group, a carboxyl group, an ester group, a carbamoyl group, an amino group, a nitro group or a silyl group.
The term “haloalkyl” means groups given by partially or wholly substituting the above-mentioned alkyl group with halogen, such as trifluoromethyl etc. The “aldehyde group, ketone group, ester group, carbamoyl group and amino group” include those substituted by an C1-C18alkyl group, a C4-C18cycloalkyl group, an C6-C30aryl group, an C7-C24aralkyl group or a heterocylic group, wherein the alkyl group, the cycloalkyl group, the aryl group, the aralkyl group and the heterocyclic group may be unsubstituted or substituted. The term “silyl group” means a group of formula —SiR105R106R107, wherein R105, R106 and R107 are independently of each other a C1-C8alkyl group, in particular a C1-C4alkyl group, a C8-C24aryl group or a C7-C12aralkylgroup, such as a trimethylsilyl group.
If a substituent, such as, for example R6, R7, R56 and R57, occurs more than one time in a group, it can be different in each occurrence.
As described above, the aforementioned radicals may be substituted by E and/or, if desired, interrupted by D. Interruptions are of course possible only in the case of radicals containing at least 2 carbon atoms connected to one another by single bonds; C6-C18aryl is not interrupted; interrupted arylalkyl or alkylaryl contains the unit D in the alkyl moiety. C1-C18alkyl substituted by one or more E and/or interrupted by one or more units D is, for example, (CH2CH2O)n—Rx, where n is a number from the range 1-9 and Rx is H or C1-C10alkyl or C2-C10alkanoyl (e.g. CO—CH(C2H5)C4H9), CH2—CH(ORy′)—CH2—O—Ry, where Ry is C1-C18alkyl, C5-C12cycloalkyl, phenyl, C7-C15phenylalkyl, and Ry′ embraces the same definitions as Ry or is H; C1-C8alkylene-COO—Rz, e.g. CH2COORz, CH(CH3)COORz, C(CH3)COORz, where Rz is H, C1-C18alkyl, (CH2CH2O)1-9—Rx, and Rx embraces the definitions indicated above; CH2CH2—O—CO—CH═CH2; CH2CH(OH)CH2—O—CO—C(CH3)═CH2.
The polymers containing groups of formulas (I), (II), (III) and (IV) may be prepared by any suitable process, but are preferably prepared by the processes described below. The condensation reaction of an aromatic boronate and a bromide, commonly referred to as the “Suzuki reaction”, is tolerant of the presence of a variety of organic functional groups and as reported by N. Miyaua and A Suzuki in Chemical Reviews, Vol. 95, pp. 457-2483 (1995). This reaction can be applied to preparing high molecular weight polymers and copolymers.
To prepare polymers corresponding to formula (I), (II), (III) or (IV), a dibromide corresponding to formula V, VI, VII, or VIII, or a mixture thereof is reacted with an equimolar amount of diboronic acid or diboronate corresponding to formula V, VI, VII, or VIII, or a mixture thereof, preferably a co-monomer
wherein X11 is independently in each occurrence a halogen atom, or —B(OH)2, —B(OY1)2 or
wherein Y1 is independently in each occurrence a C1-C10alkyl group and Y2 is independently in each occurrence a C2-C10alkylene group, such as —CY3Y4—CY5Y6—, or —CY7Y8—CY9Y10—CY11Y12—, wherein Y3, Y4, Y5, Y6, Y7, Y8, Y9, Y10, Y11 and Y12 are independently of each other hydrogen, or a C1-C10alkyl group, especially —C(CH3)2C(CH3)2—, or —C(CH3)2CH2C(CH3)2—, under the catalytic action of Pd and triphenylphosphine. The reaction is typically conducted at about 70° C. to 120° C. in an aromatic hydrocarbon solvent such as toluene. Other solvents such as dimethylformamide and tetrahydrofuran can also be used alone, or in mixtures with an aromatic hydrocarbon. An aqueous base, preferably sodium carbonate or bicarbonate, is used as the HBr scavenger. Depending on the reactivities of the reactants, a polymerization reaction may take 2 to 100 hours. Organic bases, such as, for example, tetraalkylammonium hydroxide, and phase transfer catalysts, such as, for example TBAB, can promote the activity of the boron (see, for example, Leadbeater & Marco; Angew. Chem. Int. Ed., 2003, 42, 1407 and references cited therein). Other variations of reaction conditions are given by T. I. Wallow and B. M. Novak in Journal of Organic Chemistry, Vol. 59, pp. 5034-5037 (1994); and M. Remmers, M. Schulze, and G. Wegner in Macromolecular Rapid Communications, Vol. 17, pp. 239-252 (1996).
An alternating copolymer results when a dibromide corresponding to formula V, VI, VII, or VIII is reacted with a diboronate corresponding to formula
wherein X11 is independently in each occurrence —B(OH)2, —B(OY1)2 or
wherein Y1 is independently in each occurrence a C1-C10alkyl group and Y2 is independently in each occurrence a C2-C10alkylene group, such as —CY3Y4—CY5Y6—, or —CY7Y8—CY9Y10—CY11Y12—, wherein Y3, Y4, Y5, Y6, Y7, Y8, Y9, Y10, Y11 and Y12 are independently of each other hydrogen, or a C1-C10alkyl group, especially —C(CH3)2C(CH3)2—, or —C(CH3)2CH2C(CH3)2—. If desired, a monofunctional aryl halide or aryl boronate may be used as a chain-terminator in such reactions, which will result in the formation of a terminal aryl group.
Polymerization processes involving only dihalo-functional reactants may be carried out using nickel coupling reactions. One such coupling reaction was described by Colon et al. in Journal of Polymer Science, Part A, Polymer Chemistry Edition, Vol. 28, p. 367 (1990), and by Colon et al. in Journal of Organic Chemistry, Vol. 51, p. 2627 (1986). The reaction is typically conducted in a polar aprotic solvent (e.g., dimethylacetamide) with a catalytic amount of nickel salt, a substantial amount of triphenylphosphine and a large excess of zinc dust. A variant of this process is described by Ioyda et al. in Bulletin of the Chemical Society of Japan, Vol. 63, p. 80 (1990) wherein an organo-soluble iodide was used as an accelerator. Another nickel-coupling reaction was disclosed by Yamamoto in Progress in Polymer Science, Vol. 17, p. 1153 (1992) wherein a mixture of dihaloaromatic compounds were treated with an excess amount of nickel (1,5-cyclooctadiene) complex in an inert solvent. All nickel-coupling reactions when applied to reactant mixtures of two or more aromatic dihalides yield essentially random copolymers. Such polymerization reactions may be terminated by the addition of small amounts of water to the polymerization reaction mixture, which will replace the terminal halogen groups with hydrogen groups. Alternatively, a monofunctional aryl halide may be used as a chain-terminator in such reactions, which will result in the formation of a terminal aryl group.
In one embodiment, the polymers of the invention contain conjugated groups other than the benzotriazole groups described above. “Conjugated groups” refer to moieties containing double bonds, triple bonds and/or aromatic rings. Examples of such groups are the above mentioned co-monomers T. The incorporation of such groups into the polymer may be used to modify the light absorption, ionization potential, and/or electronic properties of the polymer. Such polymers may be prepared using the methods described above incorporating at least one conjugated compound different from the benzotriazole compounds described above. Such conjugated compounds, hereinafter referred to as “comonomers”, have functional groups which permit them to copolymerize with the benzotriazole compounds. For example, dihalo-functional comonomers are preferably used in conjunction with dihalo-functional benzotriazole compounds in nickel-coupling polymerization reactions; dihalo-functional comonomers are preferably used in conjunction with benzotriazole-diboronic acids or benzotriazole-diboronates; and conjugated comonomers bearing diboronic acid or diboronate functionalities are preferably used in conjunction with dihalobenzotriazoles. For the purpose of preparing polymers of the invention, more than one diboronic acid/diboronate and more than one dibromide may be used in a Suzuki polymerization reaction so long as the total molar amount of diboronic acids/diboronates is essentially equivalent to the total amount of dibromides.
Nickel-coupling polymerizations yield essentially random copolymers comprising benzotriazole group-containing units and units derived from other co-monomers, while Suzuki polymerizations yield alternating copolymers.
It is possible to control the sequencing of the monomeric units in the resulting copolymer by controlling the order and composition of monomer feeds in the Suzuki reaction. For instance, a high molecular weight copolymer comprising mainly large blocks of benzotriazole homopolymers connected to short blocks of alternating benzotriazole co-monomer oligomers may be made by first introducing into the reaction reactants in the appropriate ratio to make the alternating benzotriazole-comonomer oligomers followed by the remainder of benzotriazole monomers so long as there is an overall balance of boronic and bromo groups.
Usually the polymers of the present invention comprise end moieties E1, wherein E1 is hydrogen or an aryl moiety which may optionally be substituted with a reactive group capable of undergoing chain extension or crosslinking, or a tri(C1-C18)alkylsiloxy group. As used herein, a reactive group capable of undergoing chain extension or crosslinking refers to any group which is capable of reacting with another of the same group or another group so as to form a link to prepare oligomers or polymers. Preferably, such reactive group is a hydroxy, glycidyl ether, acrylate ester, methacrylate ester, ethenyl, ethynyl, maleimide, nadimide, trifluorovinyl ether moiety or a cyclobutene moiety fused to the aromatic ring of E1.
The polymers of the present invention, where E1 are reactive groups as defined above, are capable of crosslinking to form solvent resistant, heat-resistant films at 100° C. or more, more preferably at 150° C. or more. Preferably, such crosslinking occurs at 350° C. or less, more preferably 300° C. or less and most preferably 250° C. or less. The crosslinkable polymers of the invention are stable at 100° C. or more and more preferably 150° C. or more. “Stable” as used herein means that such polymers do not undergo crosslinking or polymerization reactions at or below the stated temperatures. If a crosslinkable material is desired, E1 is preferably a vinylphenyl, an ethynylphenyl, or 4-(or 3-)benzocyclobutenyl radical. In another embodiment, E1 is selected from a group of phenolic derivatives of the formula —C6H4—O—Y, wherein Y is
If desired, the crosslinkable groups can be present in other parts of the polymer chain. For example, one of the substituents of the co-monomer T may be a crosslinkable group E1.
The end-capping agent E1-X (E1 is as defined above and X is either Cl or Br) is incorporated into the polymers of the present invention under the condition in which the resulting polymers are substantially capped by the reactive group E1. The reactions useful for this purpose are the nickel-coupling and Suzuki reactions described above. The average degree of polymerization is controlled by the mole ratio of monomers to end-capping agent.
Depending on the process of preparation the polymers of the present invention can be block copolymers, random copolymers, or alternating copolymers.
Another aspect of this invention is related to polymer blends containing 1 to 99 percent of at least one benzotriazole containing polymers of this invention. The remainder 1 percent to 99 percent of the blend is composed of one or more polymeric materials selected from among chain growth polymers such as polystyrene, polybutadiene, poly(methyl methacrylate), and poly(ethylene oxide); step-growth polymers such as phenoxy resins, polycarbonates, polyamides, polyesters, polyurethanes, and polyimides; and crosslinked polymers such as crosslinked epoxy resins, crosslinked phenolic resins, crosslinked acrylate resins, and crosslinked urethane resins. Examples of these polymers may be found in Preparative Methods of Polymer Chemistry, W. R. Sorenson and T. W. Campbell, Second Edition, Interscience Publishers (1968). Also may be used in the blends are conjugated polymers such as poly(phenylene vinylene), substituted poly(phenylene vinylene)s, substituted polyphenylenes and polythiophenes. Examples of these conjugated polymers are given by Greenham and Friend in Solid State Physics, Vol. 49, pp. 1-149 (1995).
Another aspect of the invention is the films formed from the polymers of the invention. Such films can be used in polymeric light-emitting diodes. Preferably, such films are used as emitting layers. These polymers may also be used as protective coatings for electronic devices and as fluorescent coatings. The thickness of the coating or film is dependent upon the ultimate use. Generally, such thickness can be from 0.01 to 200 microns. In that embodiment wherein the coating is used as a fluorescent coating, the coating or film thickness is from 50 to 200 microns. In that embodiment where the coatings are used as electronic protective layers, the thickness of the coating can be from 5 to 20 microns. In that embodiment where the coatings are used in a polymeric light-emitting diode, the thickness of the layer formed is 0.01 to 2 microns. The polymers of the invention form good pinhole- and defect-free films. Such films can be prepared by means well known in the art including spin-coating, spray-coating, dip-coating and roller-coating. Such coatings are prepared by a process comprising applying a composition to a substrate and exposing the applied composition to conditions such that a film is formed. The conditions which form a film depend upon the application technique. In a preferred embodiment, the composition applied to the substrate comprises the benzotriazole polymers dissolved in a common organic solvent. Preferably, the solution contains from 0.1 to 10 weight percent of the polymers. This composition is applied to the appropriate substrate by the desired method and the solvent is allowed to evaporate. Residual solvent may be removed by vacuum and/or by heat. After removal of the solvent, the coating is then exposed to the necessary conditions to cure the film, if needed, to prepare a film having high solvent and heat resistance. The films are preferably substantially uniform in thickness and substantially free of pinholes. In another embodiment, the polymers may be partially cured. This is known as B-staging.
A further embodiment of the present invention is directed to an optical device or a component therefore, comprising a substrate and a polymer according to the present invention.
A device according to the present invention may be prepared In accordance with the disclosure of WO99/48160, the contents of which are incorporated by reference. Polymers according to the present invention may be present in the device as the sole light emitting polymer or as a component in a blend further comprising hole and/or electron transporting polymers. Alternatively, the device may comprise distinct layers of a polymer of the present invention, a hole transporting polymer and/or an electron transporting polymer.
In one embodiment the optical device comprises an electroluminescent device, which comprises at least
(a) a reflective or transmissive anode
(b) a reflective or transmissive cathode
(c) an emissive layer comprising a polymer according to the present invention located between the electrodes
and optionally
(d) a charge injecting layer for injecting positive charge carriers, and
(e) a charge injecting layer for injecting negative charge carriers.
The layer (d) may be a positive charge carrier transport layer which is located between the light emissive layer (c) and an anode electrode layer, or may be an anode electrode layer. The layer (e) may be a negative charge carrier transport layer which is located between the light emissive layer (c) and a cathode electrode layer, or may be an cathode electrode layer. Optionally, an organic charge transport layer can be located between the light emissive layer (c) and one of the charge carrier injecting layers (d) and (e).
The EL device emits light below 520 nm, especially between 380 nm and 520 nm, very especially between 400 nm and 490 nm. The EL device emits blue light.
The EL device has a NTSC coordinate of between about (0.10, 0.02) and about (0.25, 0.25), especially a NTSC coordinate of about (0.14, 0.08).
It will be appreciated that the light emissive layer may be formed from a blend or mixture of materials including one or more polymers according to the present invention, and optionally further different polymers. The further different polymers may be so-called hole transport polymers (i.e. to improve the efficiency of hole transport to the light-emissive material) or electron-transport polymers (i.e. to improve the efficiency of electron transport to the light-emissive material). Preferably, the blend or mixture would comprise at least 0.1% by weight of a polymer according to the present invention, preferably from 0.2 to 50%, more preferably from 0.5 to 30% by weight.
The light-emitting layer can be comprised of a single material, but more commonly consists of a host material, i.e. the polymers of the present invention, doped with a guest compound or compounds, where light emission comes primarily from the dopant and can be of any color. The dopant is usually chosen from highly fluorescent dyes, but phosphorescent compounds, e.g., transition metal complexes as described in WO 98/55561, WO 00/18851, WO 00/57676, and WO 00/70655 are also useful. The polymers of the present invention may also be employed as dopants within other host materials. Dopants are typically coated as 0.01 to 10% by weigh into the host material.
Host and emitting molecules known to be of use include, but are not limited to, those disclosed in U.S. Pat. Nos. 4,768,29; 5,141,671; 5,150,006; 5,151,629; 5,294,870; 5,405,709; 5,484,922; 5,593,788; 5,645,948; 5,683,823; 5,755,999; 5,928,802; 5,935,720; 5,935,721; and 6,020,078.
An organic EL device typically consists of an organic film sandwiched between an anode and a cathode such that when a forward bias is applied to the device, holes are injected into the organic film from the anode, and electrons are injected into the organic film from the cathode. The combination of a hole and an electron may give rise to an exciton, which may undergo radiative decay to the ground state by liberating a photon. In practice the anode is commonly a mixed oxide of tin and indium for its conductivity and transparency. The mixed oxide (ITO) is deposited on a transparent substrate such as glass or plastic so that the light emitted by the organic film may be observed. The organic film may be the composite of several individual layers each designed for a distinct function. Since holes are injected from the anode, the layer next to the anode needs to have the functionality of transporting holes. Similarly, the layer next to the cathode needs to have the functionality of transporting electrons. In many instances, the electron-(hole) transporting layer also acts as the emitting layer. In some instances one layer can perform the combined functions of hole and electron transport and light emission. The individual layers of the organic film may be all polymeric in nature or combinations of films of polymers and films of small molecules deposited by thermal evaporation. It is preferred that the total thickness of the organic film be less than 1000 nanometers (nm). It is more preferred that the total thickness be less than 500 nm. It is most preferred that the total thickness be less than 300 nm. It is preferred that the thickness of the active (light emitting) layer be less than 400 nanometers (nm). It is more preferred that the thickness is in the range of from 40 to 160 nm.
The ITO-glass which serves as the substrate and the anode may be used for coating after the usual cleaning with detergent, organic solvents and UV-ozone treatment. It may also be first coated with a thin layer of a conducting substance to facilitate hole injection. Such substances include copper phthalocyanine, polyaniline and poly(3,4-ethylenedioxy-thiophene) (PEDOT); the last two in their conductive forms by doping with a strong organic acid, e.g., poly(styrenesulfonic acid). It is preferred that the thickness of this layer be 200 nm or less; it is more preferred that the thickness be 100 nm or less.
In the cases where a hole-transporting layer is used, the polymeric arylamines described in U.S. Pat. No. 5,728,801, may be used. Other known hole-conducting polymers, such as polyvinylcarbazole, may also be used. The resistance of this layer to erosion by the solution of the polymer film which is to be applied next is obviously critical to the successful fabrication of multi-layer devices. The thickness of this layer may be 500 nm or less, preferably 300 nm or less, most preferably 150 nm or less.
In the case where an electron-transporting layer is used, it may be applied either by thermal evaporation of low molecular weight materials or by solution coating of a polymer with a solvent that would not cause significant damage to the underlying film.
Examples of low molecular weight materials include the metal complexes of 8-hydroxyquinoline (as described by Burrows et al. in Applied Physics Letters, Vol. 64, pp. 2718-2720 (1994)), metallic complexes of 10-hydroxybenzo(h)quinoline (as described by Hamada et al. in Chemistry Letters, pp. 906-906 (1993)), 1,3,4-oxadiazoles (as described by Hamada et al. in Optoelectronics-Devices and Technologies, Vol. 7, pp. 83-93 (1992)), 1,3,4-triazoles (as described by Kido et al. in Chemistry Letters, pp. 47-48 (1996)), and dicarboximides of perylene (as described by Yoshida et al. in Applied Physics Letters, Vol. 69, pp. 734-736 (1996)). Further examples of low molecular weight materials are disclosed in the European patent application no. 03100972.3, the content of which is incorporated herein by reference.
Polymeric electron-transporting materials are exemplified by 1,3,4-oxadiazole-containing polymers (as described by Li et al. in Journal of Chemical Society, pp. 2211-2212 (1995), by Yang and Pei in Journal of Applied Physics, Vol 77, pp. 4807-4809 (1995)), 1,3,4-triazole-containing polymers (as described by Strukelj et al. in Science, Vol. 267, pp. 1969-1972 (1995)), quinoxaline-containing polymers (as described by Yamamoto et al. in Japan Journal of Applied Physics, Vol. 33, pp. L250-L253 (1994), O'Brien et al. in Synthetic Metals, Vol. 76, pp. 105-108 (1996)), and cyano-PPV (as described by Weaver et al. in Thin Solid Films, Vol. 273, pp. 39-47 (1996)). The thickness of this layer may be 500 nm or less, preferably 300 nm or less, most preferably 150 nm or less.
The cathode may be deposited either by thermal evaporation or by sputtering and may consist of a number of layers. The thickness of the cathode material may be from 100 nm to 10,000 nm. The preferred metals are calcium, barium, magnesium, indium, lithium fluoride (LiF), Caesiumfluoride (Csf), Ca(acac) and aluminum. Mixtures or alloys of these materials may also be used.
In a preferred embodiment, the electroluminescent device comprises at least one hole-transporting polymer film and a light-emitting polymer film comprised of the polymer of the invention, arranged between an anode material and a cathode material such that under an applied voltage, holes are injected from the anode material into the hole-transporting polymer film and electrons are injected from the cathode material into the light-emitting polymer films when the device is forward biased, resulting in light emission from the light-emitting layer.
In another preferred embodiment, layers of hole-transporting polymers are arranged so that the layer closest to the anode has the lower oxidation potential, with the adjacent layers having progressively higher oxidation potentials. By these methods, electroluminescent devices having relatively high light output per unit voltage may be prepared.
The term “hole-transporting polymer film” as used herein refers to a layer of a film of a polymer which when disposed between two electrodes to which a field is applied and holes are injected from the anode, permits adequate transport of holes into the emitting polymer. Hole-transporting polymers are typically poly(3,4-ethylenedioxy-thiophene) (PEDOT), PEDOT-PSS(PSS=poly(styrenesulfonic acid), polyaniline (PANI) and polythiophenes. The term “light-emitting polymer film” as used herein refers to a layer of a film of a polymer whose excited states can relax to the ground state by emitting photons, preferably corresponding to wavelengths in the visible range. The term “anode material” as used herein refers to a semi transparent, or transparent, conducting film with a work function between 4.5 electron volts (eV) and 5.5 eV. Examples are gold, silver, copper, aluminum, indium, iron, zinc, fin, chromium, titanium, vanadium, cobalt, nickel, lead, manganese, tungsten and the like, metallic alloys such as magnesium/copper, magnesium/silver, magnesium/aluminum, aluminum/indium and the like, semiconductors such as Si, Ge, GaAs and the like, metallic oxides such as indium-tin-oxide (“ITO”), ZnO and the like, metallic compounds, and furthermore, electroconducting polymers such polyacetylene, polypyrrole, polyparaphenylene and the like. Oxides and mixed oxides of indium and tin, and gold are preferred. Most preferred is ITO, especially ITO on glass or plastic as substrate. The term “cathode material” as used herein refers to a conducting film with a work function between 2.5 eV and 4.5 eV. Examples are alkali metals, alkaline earth metals, group 13 elements, silver, and copper as well as alloys or mixtures thereof such as sodium, lithium, potassium, calcium, barium, lithium fluoride (LiF), caesium fluoride (CsF), sodium-potassium alloy, magnesium, magnesium-silver alloy, magnesium-copper alloy, magnesium-aluminum alloy, magnesium-indium alloy, aluminum, aluminum-aluminum oxide alloy, aluminum-lithium alloy, Indium, calcium, and materials exemplified in EP-A 499,011, such as electroconducting polymers e.g. polypyrrole, polythiophene, polyaniline, polyacetylene etc. Preferably lithium, calcium, barium, CsF, LiF, magnesium, indium, silver, aluminum, or blends and alloys of the above are used. In the case of using a metal or a metallic alloy as a material for an electrode, the electrode can be formed also by the vacuum deposition method. In the case of using a metal or a metallic alloy as a material forming an electrode, the electrode can be formed, furthermore, by the chemical plating method (see for example, Handbook of Electrochemistry, pp 383-387, Mazuren, 1985).
As methods for forming said thin films, there are, for example, the vacuum deposition method, the spin-coating method, the casting method, the Langmuir-Blodgett (“LB”) method, the ink jet printing method and the like. Among these methods, the vacuum deposition method, the spin-mating method, the ink jet printing method and the casting method are particularly preferred In view of ease of operation and cost.
In the case of forming the layers by using the spin-coating method, the casting method and ink jet printing method, the coating can be carried out using a solution prepared by dissolving the composition in a concentration of from 0.0001 to 90% by weight in an appropriate organic solvent such as benzene, toluene, xylene, chlorobenzene, tetrahydrofurane, methyltetrahydrofurane, N,N-dimethylformamide, chloroform, dichloromethane, dimethylsulfoxide and the like. The polymers should be completely soluble in the employed solvents.
The organic EL device of the present invention has significant industrial values since it can be adapted for a flat panel display of an on-wall television set, a flat light-emitting device, a light source for a copying machine or a printer, a light source for a liquid crystal display or counter, a display signboard and a signal light. The polymers and compositions of the present invention can be used in the fields of an organic EL device, a photovoltaic device, an electrophotographic photoreceptor, a photoelectric converter, a solar cell, an image sensor, and the like.
The following examples are included for illustrative purposes only and do not limit the scope of the claims. Unless otherwise stated, all parts and percentages are by weight.
Bis(1,5-cyclooctadiene)nickel(0) (2.0 g, 7.27 mmol) and 2,2′-bipyridyl (1.14 g, 7.27 mmol) are dissolved in anhydrous toluene (7.0 ml) and stirred at 80° C. for 1 hour under an argon atmosphere in the dark. Monomer 1 (0.23 g, 0.60 mmol) and 2,7-dibromo-9,9-dihexylfluorene (Monomer 2) (1.50 g, 3.05 mmol) are dissolved in anhydrous toluene (7.0 ml) and purged thoroughly with argon, then added to the solution of Ni complex and stirred at 80° C. for 17 hours under argon in the dark. Anhydrous toluene (7.0 ml) is added and the reaction allowed to progress a further 5 hours. Bromobenzene (1 ml, 9.5 mmol) is added and the reaction stirred for a further 2 hours. The reaction mixture is poured into stirred methanol/c.HCl(aq) (10:1, 600 ml) and the resulting precipitate is stirred for 30 minutes and collected by filtration. The precipitate is redissolved in toluene (80 ml) and the precipitation repeated in acidic methanol. The precipitate is redissolved in chloroform (80 ml) and passed through a plug of silica, then washed through with chloroform (5×100 ml). The combined chloroform phases are concentrated to ca. 80 ml and precipitated in stirred methanol (600 ml) and stirred for 30 minutes. The polymer is collected by filtration and dried. 0.674 g; 58% recovery of material: MW=650,000, PD=2.21 (GPC, PS standards).
The polymerisation protocol in Example 1 may be used to produce either high MW homopolymers or high MW statistical (random) co-polymers from the following monomer families:
Monomer 1:
Monomer 3 (1.0 g, 2.31 mmol) and monomer 4 (2.38 g, 2.31 mmol) are suspended in toluene (15 ml) and purged by bubbling argon through for 10 minutes. Palladium catalyst (1 mol %) is added and the toluene phase purged for a further 10 minutes. Tetraethylammonium hydroxide (20% aq. solution; 8 ml) is added and the whole heated to reflux for 20 hours. Bromobenzene (0.2 ml) is added and the reaction allowed to proceed for a further hour, then phenylboronic acid is added and the reaction stirred for another hour. On cooling the reaction mixture is diluted with toluene (20 ml) and poured into acidic methanol (10 ml 32% HCl(aq) in 500 ml methanol) and filtered. The pale solid is redissolved in toluene (100 ml) and stirred vigorously with an aqueous solution of disodium EDTA (5%, 200 ml) for 1 hour. The toluene phase is separated, concentrated to ca. 50 ml and precipitated in methanol (400 ml), filtered and dried.
The polymerisation in Example 2 may be used to produce either homopolymers or alternating copolymers from the following monomer families:
Monomer 3:
The ITO-glass used for device fabrication is 1 square inch with a nominal sheet resistance of 12 ohm/square. The ITO is patterned by photolithography and etching, then cleaned with water, solvents and finally by exposure to RF-plasma. The PEDOT-PSS (PEDOT=poly(3,4-ethylenedioxy-thiophene), PSS=poly(styrenesulfonic acid)) layer is spin-coated from aqueous dispersion as acquired from Bayer Corporation and baked at 200° C. for 30 minutes, such that the final layer thickness was 40 nm. Polymer 67 is spin-coated from toluene solution such that the layer thickness is 80 nm. Calcium (20 nm) and aluminium (70 nm) are thermally deposited in a vacuum chamber. The patterning of ITO and cathode creates 8 active devices of area 4 mm2.
The devices exhibit a turn-on voltage (luminance >1 cd/m2) of 7.4 V, reaching a peak efficiency of 0.012 cd/A.
Monomer 5 (1.58 g, 3.18 mmol) and monomer 6 (1.57 g, 3.18 mmol) are dissolved in toluene (22 ml) and purged by bubbling argon through for 10 minutes. Palladium catalyst (1 mol %) is added and the toluene phase purged for a further 10 minutes. Tetraethylammonium hydroxide (20% aq. solution; 12 ml) is added and the whole heated to reflux for 20 hours. Bromobenzene (0.2 ml) is added and the reaction allowed to proceed for a further hour, then phenylboronic acid is added and the reaction stirred for another hour. On cooling the reaction mixture is diluted with toluene (20 ml) and poured into methanol (10 ml 32% HCl(aq) in 500 ml methanol) and filtered. The pale solid is redissolved in toluene (100 ml) and stirred vigorously with an aqueous solution of disodium EDTA (5%, 200 ml) for 1 hour. The toluene phase is separated, concentrated to ca. 50 ml and precipitated in methanol (400 ml), filtered and dried to yield 1.6 g polymer (85% recovery).
The polymerisation in Example 3 may be used to produce either homopolymers or alternating copolymers from the following monomer families:
The ITO-glass used for device fabrication is 1 square inch with a nominal sheet resistance of 12 ohm/square. The ITO is patterned by photolithography and etching, then cleaned with water, solvents and finally by exposure to RF-plasma. The PEDOT-PSS layer is spin-coated from aqueous dispersion as acquired from Bayer Corporation and baked at 200° C. for 30 minutes, such that the final layer thickness is 100 nm. Polymer 67 is spin-coated from toluene solution such that the layer thickness is 80 nm. Barium (5 nm) and aluminium (100 nm) are thermally deposited in a vacuum chamber. The patterning of ITO and cathode creates 8 active devices of area 4 mm2.
The devices exhibit a turn-on voltage (luminance >1 cd/m2) of 3.6 V, reaching a peak efficiency of 0.61 cd/A.
The ITO-glass used for device fabrication is 1 square inch with a nominal sheet resistance of 12 ohm/square. The ITO is patterned by photolithography and etching, then cleaned with water, solvents and finally by exposure to RF-plasma. The PEDOT-PSS layer is spin-coated from aqueous dispersion as acquired from Bayer Corporation and baked at 200° C. for 30 minutes, such that the final layer thickness is 100 nm. Polymer 67 is spin-coated from toluene solution such that the layer thickness is 80 nm. Lithium fluoride (5 nm), calcium (10 nm) and aluminium (200 nm) are thermally deposited in a vacuum chamber. The patterning of ITO and cathode creates 8 active devices of area 4 mm2.
The devices exhibit a turn-on voltage (luminance >1 cd/m2) of 3.7 V, reaching a peak efficiency of 1.41 cd/A.
The ITO-glass used for device fabrication is 1 square inch with a nominal sheet resistance of 12 ohm/square. The ITO is patterned by photolithography and etching, then cleaned with water, solvents and finally by exposure to RF-plasma. The polyaniline (PANI) layer is spin-coated such that the final layer thickness is 100 nm. Polymer 67 is spin-coated from toluene solution such that the layer thickness is 80 nm. Lithium fluoride (5 nm), calcium (10 nm) and aluminium (200 nm) are thermally deposited in a vacuum chamber. The patterning of ITO and cathode creates 8 active devices of area 4 mm2.
The devices exhibit a turn-on voltage (luminance >1 cd/m2) of 3.8 V, reaching a peak efficiency of 1.39 cd/A.
| Number | Date | Country | Kind |
|---|---|---|---|
| 03405317 | May 2003 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2004/050606 | 4/26/2004 | WO | 00 | 11/6/2006 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2004/099285 | 11/18/2004 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6392056 | Wood et al. | May 2002 | B1 |
| 6451887 | Wood et al. | Sep 2002 | B1 |
| 6512083 | Woo et al. | Jan 2003 | B1 |
| Number | Date | Country |
|---|---|---|
| 26 20 970 | Nov 1976 | DE |
| 08311193 | Nov 1996 | JP |
| 9712882 | Apr 1997 | WO |
| 0149768 | Jul 2001 | WO |
| 0212204 | Feb 2002 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070043204 A1 | Feb 2007 | US |