4039512
-
Patent Number
4,039,512
-
Date Filed
Monday, September 15, 197549 years ago
-
Date Issued
Tuesday, August 2, 197747 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
-
CPC
-
US Classifications
Field of Search
US
- 260 61
- 260 2 P
- 260 DIG 24
- 260 457 PS
-
International Classifications
-
Abstract
Flame retardant polymers of benzene phosphorus oxydichloride, 4,4'-thiodiphenol and POCl.sub.3 are disclosed which are preferably formed by reacting these monomers in an inert organic solvent at ambient temperature in the presence of an amine acid acceptor.
Description
TECHNICAL DESCRIPTION OF THE INVENTION
The present invention relates to polymers of resinous, branched polymeric phosphonates having improved flame retardant properties.
In U.S. Pat. No. 2,716,101 to H. M. Coover Jr. et al. it was proposed that resinous products be formed by reacting an organophosphonic acid dichloride, such as benzene phosphorus oxydichloride, a dihydroxy aromatic compound, such as a dihydroxydiphenyl sulfone, and a trifunctional phosphorus compound, such as phosphorus oxydichloride. The Coover Jr. et al. patent mentioned that the products produced by such a reaction were useful as materials for the preparation of fibers, films, coating and molding compositions and the like.
It has been unexpectedly found that flame retardant copolymers formed by reacting benzene phosphorus oxydichloride, 4,4'-thiodiphenol and POCL.sub.3 have a flame retardancy which is superior to that exhibited by similar copolymers containing a dihydroxydiphenyl sulfone, e.g., 4,4'-sulfonyl diphenol, as taught by Coover Jr. et al. The flame retardant copolymers of this invention also have utility as an engineering thermoplastic which is suitable for use in conventional injection molding apparatus.
The molor ratio of benzene phosphorus oxydichloride to POCL.sub.3 which are reacted together with 4,4'-thiodiphenol to form the copolymers of the present invention can range anywhere from about 100:1 to about 1:100. It is preferred to use a ratio of from about 50:1 to about 1:50. The molar ratio of 4,4'-thiodiphenol to benzene phosphorus oxydichloride and POCL.sub.3 should be from about 1:1.2 to about 1.8:1, preferably from about 1:1 to about 1.5:1. In general, it is most preferred to use benzene phosphorus oxydichloride, 4,4'-thiodiphenol and POCL.sub.3 in such relative amounts that the molar amount of chlorine in the oxydichloride and POCL.sub.3 is approximately equal to the molar amount of hydroxyl groups in the diphenol. The final product will contain moieties derived from these reactants in the same amounts described above.
A number of processes can be used to make the copolymers of the present invention. For example, any of the above described amounts of the three reactants can be reacted in the absence of either solvent or catalyst at elevated temperatures of from about 120.degree. C. to about 250.degree. C. until a homogeneous melt is produced. This reaction has the disadvantage that it is quite slow, taking several days to complete, and it yields a product which may be of a dark color containing undesired residual hydrochloric acid which can cause chain degradation in the product.
Another procedure which can be used is the same general reaction sequence which is described in U.S. Pat. No. 2,716,101 to H. W. Coover Jr. et al. In this procedure, the monomers, as described above, are reacted in the presence of a catalytically effective amount of a suitable anhydrous alkaline earth halide condensation catalyst, e.g., anhydrous magnesium chloride, at a temperature of from about 90.degree. C. to about 300.degree. C. If desired, this reaction can be carried out in a suitable inert solvent.
The procedure which is preferred for purposes of the present invention is the reaction of the above monomers in the above described amounts at much lower temperatures, e.g., from about 0.degree. C. to about 80.degree. C., in solution and in the presence of an amount of amine acid acceptor which is sufficient to scavenge the hydrochloric acid by-product which is produced by the reaction of the monomers. Generally, a molar amount of amine acid acceptor which ranges from about 2:1 to 3:1, based on the molar amount of the reacting benzene phosphorus oxydichloride or 4,4'-thiodiphenol monomers is sufficient. The solvent which is selected is preferably an inert organic solvent, most preferably a chlorinated hydrocarbon solvent, which will not interfere with the reaction and in which the intermediates and product are soluble. Suitable solvents include methylene chloride, chloroform, dichloroethane and the like.
The amine acid acceptor can be any of the C.sub.1 -C.sub.8 trialkyl or branched dialkyl monoamines or the heterocyclic amines. Preferred acid acceptors are the C.sub.1 -C.sub.8 trialkylamines. Some representative amines are triethylamine, pyridine, diisopropylamine, and the like.
The solubility of the copolymer of this invention in various organic solvents is affected by the amount of POCL.sub.3 which is used. Use of low amounts of POCL.sub.3 will yield a more soluble copolymer whereas higher amounts of POCL.sub.3 will yield a more crosslinked, more insoluble copolymer. It is well within the ability of persons of ordinary skill in the art to vary the molar amount of POCL.sub.3 which is reacted to yield the desired degree of solubility. The copolymers of the present invention can be used as materials for the production of nonflammable fibers, molding compositions and the like.
These and other embodiments of the claimed invention are illustrated by the Examples which follow:
EXAMPLE 1
This Example describes a procedure for forming a copolymer of benzene phosphorus oxydichloride, 4,4'-thiodiphenol and POCL.sub.3 (hereinafter called "BPOD/TDP/POCL.sub.3 " copolymer) in accordance with the present invention.
A three necked flask with a mechanical stirrer, addition funnel and condenser were used. The following reagents were charged into the flask:
______________________________________Reagent Amount______________________________________4,4'-thiodiphenol 89.8 g. (0.412 mole)Triethylamine 88.8 g. (0.88 mole)Methylene chloride 600 ml.______________________________________
The following reagents were placed in the addition funnel:
______________________________________Reagent Amount______________________________________Benzene phosphorus 78.0 g. (0.40 mole)oxydichloride -POCl.sub.3 1.22 g. (0.008 mole)Methylene chloride 250 ml.______________________________________
The benzene phosphorus oxydichloride was slowly added to the flask over a period of 20-30 minutes with rapid stirring at room temperature. The stirring was continued for one hour after the addition had been completed, and the resulting solution was washed with an equal volume of 1N hydrochloric acid and an equal volume of distilled water. The solution was added to methanol to yield the desired product as a precipitate. The precipitate was removed from solution and was vacuum dried.
The relative viscosity of the product was 1.92 when measured as a 1% by weight solution in a 60/40 phenol/tetrachloroethane mixture. The yield of product was 90%. It had an intrinsic viscosity of 0.65 and a melting point of 180.degree. C.
EXAMPLE 2
The same procedure used in Example 1 was again used to form a copolymer of benzene phosphorus oxydichloride, 4,4'-sulfonyldiphenol and POCL.sub.3, as described in U.S. Pat. No. 2,716,101 to H. W. Coover Jr. et al. This polymer is hereinafter abbreviated "BPOD/SDP/POCL.sub.3 " copolymer. The reagents in the flask are:
______________________________________Reagent Amount______________________________________4,4'-sulfonyl diphenol 65.38 g. (0.2575 mole)Triethylamine 55.5 g. (0.55 mole)Methylene chloride 400 ml.______________________________________
The reagents in the addition funnel are:
______________________________________Reagent Amount______________________________________Benzene phosphorus 48.75 g. (0.25 mole)oxydichloridePOCl.sub.3 0.77 g. (0.005 mole)Methylene chloride 100 ml.______________________________________
The yield of product was 94%, it had an intrinsic viscosity of 0.42 and a melting point of 185.degree.-190.degree. C.
EXAMPLE 3
Examples 1 and 2 were repeated using a higher amount of POCL.sub.3 so as to yield copolymers having a 2 mole% content of POCL.sub.3 based on the molar sum of benzene phosphorus oxydichloride, the diphenol and POCL.sub.3. The amount in Examples 1 and 2 was 1%.
The copolymer products in this Example were tested for flammability using the Limiting Oxygen Index (LOI) ASTM D-2863 test which is described by Fenimore and Martin in the November, 1966 issue of Modern Plastics. This method directly relates to the minimum percentage concentration of oxygen in an oxygen-nitrogen mixture which permits a sample to burn. A high LOI is indicative of a higher degree of flame retardancy. The following LOI values were observed and demonstrate the greater flame retardancy for the product of the present invention.
______________________________________Sample LOI MP(.degree. C) T.sub.g (.degree. C)______________________________________BPOD/TDP/POCl.sub.3 copolymer 60 180 88BPOD/SDP/POCl.sub.3 copolymer 50 190 151______________________________________
The polymers of the present invention have an intrinsic viscosity of from about 0.30 to about 1.1 when measured in a 60/40 mixture (by weight) of phenol and tetrachloroethane at 30.degree. C. A preferred intrinsic viscosity is greater than about 0.35 and less than about 0.7.
These Examples illustrate certain preferred embodiments of the claimed invention. The scope of protection which is sought is set forth in the claims which follow.
Claims
- 1. A resinous polymer of benzene phosphorus oxydichloride, 4,4'-thiodiphenol and POCL.sub.3.
- 2. A polymer as claimed in claim 1 which has an intrinsic viscosity of from about 0.30 to about 1.1 when measured in a 60/40, weight ratio, phenol/tetrachloroethane mixture at 30.degree. C.
- 3. A polymer as claimed in claim 1 which has an intrinsic viscosity of greater than about 0.35 and less than about 0.7 when measured in a 60/40, weight ratio, phenol/tetrachloroethane mixture at 30.degree. C.
- 4. A polymer as claimed in claim 1 wherein the molar ratio of benzene phosphorus oxydichloride to POCL.sub.3 ranges from about 100:1 to about 1:100.
- 5. A polymer as claimed in claim 4 wherein the molar ratio ranges from about 50:1 to about 1:50.
- 6. A polymer as claimed in claim 1 wherein the molar ratio of 4,4'-thiodiphenol to benzene phosphorus oxydichloride and POCL.sub.3 ranges from about 1:1.2 to about 1.8:1.
- 7. A polymer as claimed in claim 6 wherein the ratio of 4,4'-thiodiphenol to benzene phosphorus oxydichloride and POCl.sub.3 ranges from about 1:1 to about 1.5:1.
- 8. A polymer as claimed in claim 1 formed by a reaction such that the molar amount of chlorine in the oxydichloride and POCl.sub.3 is about equal to the molar amount of hydroxyl groups in the diphenol.