Polymethacrylate-polymethacrylic acid block copolymers

Abstract

Inventive block copolymers are prepared, and their synthesis is described. These inventive block copolymers act as polymeric surfactants, especially as emulsifiers and surfactants, and as compounds having antistatic properties.

Description

FIELD OF THE INVENTION

The invention relates to new polymethacrylate-polymethacrylic acid block copolymers and their alkali or ammonium salts. The invention further relates to the synthesis of these new block copolymers and to polymeric surfactants, particularly as dispersants and emulsifiers, as well as materials for modifying the antistatic properties comprising the new block copolymers.

Furthermore, the invention relates to polymethacrylate/poly-t-butyl methacrylate block copolymers as new intermediates for the synthesis of the inventive polymers.

BACKGROUND INFORMATION AND PRIOR ART

The German Offenlegungsschrift 21 23 766 relates to copolymers with a hydrophilic surface. They are composed of 75 to 92% methyl methacrylate and 8 to 25% of acrylic acid. The polymerization takes place by a free radical mechanism in the absence of any solvent, so that polymers with a statistical distribution of the monomer units are obtained. The copolymers admittedly are referred to as block copolymers. However, this is a solventless copolymerization of the mixture of monomers and not the blockwise arrangement of the monomer units. The copolymers are recommended particularly for the production of contact lenses, since the surfaces of the shaped copolymers are superficially hydrophilized by reaction with bases.

Polymethyl methacrylate/poly-t-butyl(meth)acrylate block copolymers and their synthesis by anionic polymerization are described in Macromolecules, (1991), 24, 4997-5000. However, this method can hardly be carried out on an industrial scale, since the anionic polymerization requires very pure, anhydrous solvents (particularly tetrahydrofuran) and reactants. The reaction must be carried out at low temperatures of about -78.degree. C. Moreover, it is necessary to use alkali metal initiators.

The EP publication 0 518 225 discloses aqueous, pigmented inks for ink jet printers. These inks contain an AB or ABA block copolymer as stabilizer, the A segment of which is synthesized, for example, by polymerizing n-butyl methacrylate and the B segment initially by polymerizing trimethylsilyl methacrylate. From the latter, a polymethacrylic acid segment can be produced by splitting off the trimethyl group hydrolytically. For the polymerization, the group transfer polymerization (GTP method) described, for example, in U.S. Pat. No. 4,508,880, is employed.

A detailed description of this GTP may be found in Eur. Polym. J. Vol. 29, No. 2/3, 407-414 (1993). Typically, the polymerization is initiated by a O-silyl ketene acetate; 1-methoxy-1-(trimethylsiloxy)-2-methylpropene is customary. A nucleophilic compound, such as tris(dimethylamino)sulfonium bifluoride is used as a catalyst. The GTP method proceeds as follows: ##STR1##

As with the anionic polymerization, this method also requires that the reactants used should be dried very carefully and be free from residues of alcohol. Furthermore, even traces of moisture must be kept from the reaction. Moreover, the compounds used as initiator and as catalyst are expensive, so that this method, as a whole, is costly when used industrially.

The present invention is concerned with the technical problem of synthesizing block copolymers, the segments of which are formed from methacrylate esters and methacrylic acid or its salts. The desired block copolymers are to be synthesized in the simplest way possible, in order to enable these compounds to be made on an industrial scale.

Admittedly, the reaction of polymethacrylate esters with a large excess of diethylaminoethanol at temperatures in excess of 150.degree. C. in the presence of titanates as catalysts is known from Chemical Abstracts 98 (No. 8, 54652f). Polymers are obtained here, for which a portion of the ester groups is transesterified with diethylaminoethanol. However, relatively impure products are obtained at this temperature since it is impossible to avoid obtaining the thermal decomposition products.

Surprisingly, however, it was found that by adhering to certain structural parameters for the polymethacrylate esters that are to be reacted, and by selecting suitable process conditions for the transesterification, it is possible to transesterify one or both terminal ester groups, the terminal tertiary ester group being decisively preferred over the quaternary ester group. This enables the synthesis of novel polymethacrylate esters, the ester groups of which in the .alpha. and optionally in the .omega. positions, differ from those ester groups in the chain.

OBJECT OF THE INVENTION

An object of the present invention is the inventive block copolymers. Another object of the invention is a method of synthesizing the inventive block copolymers. Yet another object of the invention is a polymeric surfactant or a compound having antistatic properties comprising the inventive block copolymers.

New block copolymers have the general formula ##STR2## wherein R.sup.1 are the same or different and represent alkyl groups, except the t-butyl group, with 1 to 22 carbon atoms perfluoroalkyl groups or dialkyl-aminoalkyl groups,

R.sup.2 are --(CH.sub.2).sub.p groups, in which p is a number from 2 to 6, R.sup.3 represents the group of a known chain length regulator, which is free of active hydrogen atoms, X is a cation, and n and m are the same or different and in each case have an average numerical value of not less than 3.

Within the polymeric molecule, R.sup.1 can be the same or different. Preferably, R.sup.1 is an alkyl group with 1 to 8 carbon atoms, particularly the methyl, ethyl, butyl or 2-ethylhexyl group. R.sup.1 shall not be the t-butyl group.

R.sup.1 can also be a perfluoroalkyl group. Examples of perfluoroalkyl groups are the --CH.sub.2 CF.sub.3, --(CH.sub.2).sub.2 C.sub.8 F.sub.17 or --CH.sub.2 --CHF--CHF.sub.2 groups.

R.sup.1 can furthermore represent a dialkylaminoalkyl group. Examples of suitable dialkylaminoalkyl groups are groups having the formula --R.sup.6 --NR.sup.7 R.sup.8, wherein R.sup.6 is an alkyl group with 1 to 4 carbon atoms and R.sup.7 and R.sup.8 are the same or different and represent alkyl groups with 1 to 4 carbon atoms. Examples of such groups are the --CH.sub.2 --CH.sub.2 --N(CH.sub.3).sub.2 and the --CH.sub.2 --CH(CH.sub.3) --N(C.sub.2 H.sub.5).sub.2 groups.

R.sup.2 is a divalent aliphatic group having the formula --(CH.sub.2).sub.p --, wherein p is a number from 2 to 6, preferably a numerical value of 2 or 3 and particularly is 2.

R.sup.3 is the group of a known chain-length regulator, the R.sup.3 group being free of active hydrogen atoms. Examples of chain length-regulators are mercaptans, chloroform and isopropylbenzene. A preferred example of an R.sup.3 group originating from such a chain-length regulator is the --C.sub.12 H.sub.25 S group. Further examples of groups originating from chain-length regulators are the groups derived from t-dodecyl mercaptan and the octadecyl mercaptan and tetradecyl mercaptan groups.

X is a cation, preferably a hydrogen, alkali or ammonium group, which optionally can be alkyl-substituted. Examples of such substituted ammonium groups are the NH(CH.sub.3).sub.3 --, N(C.sub.2 H.sub.5).sub.4 -- and NH(CH.sub.2 --C.sub.6 H.sub.5)(CH.sub.3).sub.2 -- groups. Moreover, the cations, known from the state of the art for poly-methacrylic acid polymers, can also be selected. They are described in detail, for example, in the EP publication 0 518 225 (page 5).

Subscripts n and m are identical or different and have, in each case, an average numerical value of not less than 3. In each case, numerical values of 4 to 20 are particularly preferred for n and m.

Examples of inventive block copolymers are: ##STR3##

Yet another object of invention are the t-butyl esters of polymethacrylate/polymethacrylic acid block copolymers, which are formed as intermediates and correspond to the following general formula ##STR4## in which the groups and subscripts have the meanings already given. These intermediates are responsible for the structure and properties of the end products.

Examples of these intermediates are ##STR5##

Yet another object of the invention is the synthesis of the inventive block copolymers. This method is characterized in that

a) polymers of the general formula ##STR6## in which the groups and subscripts have the meaning already given, are transesterified with polymers of the general formula ##STR7## in the molar ratio of 1.1:1 to 1.0:1 with the addition of known catalysts, and b) the polymer thus obtained of the general formula ##STR8## is converted at a temperature above 60.degree. C. in the presence of an acid as a catalyst and optionally of a solvent, or at a temperature above 160.degree. C. without a catalyst by splitting off isobutylene into the desired block copolymer having the formula ##STR9## and c) optionally converted in a known manner into the alkali or ammonium salt.

The isobutylene can also be split off photochemically in the presence of so-called Crivello salts (aryl-onium salts), such as triphenylsulfonium hexafluorophosphate, diphenyliodonium hexafluoroantimonate and the like (reference: J. V. Crivello, "UV Curing: Science and Technology", S. P. Pappas, ed., Technology Marketing Corp., Stamford, Conn. 1978).

For the transesterification of step a), the molar ratio of 1.05:1 is preferred.

In step a) of the method, there is thus a selective transesterification of a methacrylate ester, obtained by free radical polymerization, with a t-butyl methacrylate, which was obtained by free radical polymerization and for the synthesis of which a hydroxy-functional alkyl mercaptan was used as initiator. This hydroxy group reacts with the terminal ester group of the first-mentioned methacrylate ester polymer. For this reason, the bridging element ##STR10## is characteristic for the inventive block copolymer. It was particularly surprising that the terminal ester group at the tertiary carbon atom reacts appreciably more rapidly than the remaining ester groups and particularly also more rapidly than the ester group at the other end of the chain.

Preferably, for the transesterification, a known non-basic transesterification catalyst is used. Examples of such a catalyst are alkyl titanates, such as i-propyl, n-butyl, or i-butyl titanate and stannates, such as dialkyl tin acetate halide or tin dialkyl esters, particularly dibutyl tin dilaurate. The catalysts are used in amounts of 0.5 to 2% by weight, based on the polymethacrylate ester.

In the second step (b) of the method

b1) at a temperature in excess of 60.degree. C. in the presence of an acid as a catalyst, particularly of p-toluenesulfonic acid monohydrate, and optionally in the presence of a solvent, such as dioxane, or of solvent mixtures, such as toluene/methanol or toluene/dioxane, or b2) at a temperature above 160.degree. C. without a catalyst, isobutylene is split off and the desired block copolymer is obtained, which can then be converted into the desired alkali or ammonium salt.

In a particularly preferred modification, the acid-catalyzed splitting off of the isobutylene takes place at temperatures of 80.degree. to 100.degree. C. in the presence of a catalyst. If the thermal splitting off is carried out at higher temperatures, anhydric structures are formed, which can be converted once again by known methods into the free acid.

A further object of the invention is the use of the inventive copolymers as polymeric surfactants, particularly as dispersants and emulsifiers and as compounds having antistatic properties.

Preferred areas of application of the inventive polymer are their uses

a) as emulsifiers in the aqueous and inverse emulsion polymerization, b) as dispersants or suspension stabilizers for pigments and fillers, such as metal oxides in ceramic materials, pigments in ink jet dyes and fillers in thermoplastic and duroplastic materials, and c) for hydrophilizing and for providing an antistatic finish as polymer dispersant for alloying plastics.

The inventive method and the properties of the inventive block copolymers are described in greater detail in the following examples, it being understood that these examples are provided by way of illustration and not by way of limitation.

EXAMPLE 1A

Synthesis of a Monohydroxy-Functional Poly-t-Butyl Methacrylate by Controlled Free Radical Polymerization (not of the invention)

A solution of 1.47 g of azodiisobutyronitrile and 78.1 g (approximately 1 mole) of 2-mercaptoethanol in 150 g of xylene and 1136.8 g (approximately 8 moles) of t-butyl methacrylate (TBMA) are added over a period of four hours to a reactor filled with 150 g of xylene; the solvent in the reactor has a temperature of 120.degree. C. and is under an atmosphere of nitrogen.

At the end of the reaction, about 400 ppm of hydroquinone monomethyl ether are added and the solution is cooled to about 40.degree. C. The solvent and the residual monomer are then distilled off at 120.degree. C. and 1 torr. A colorless, viscous liquid remains behind.

Gel permeation chromatographic analysis reveals that the polymer obtained has a number average molecular weight M.sub.n (GPC) of 1300 and a weight average molecular weight M.sub.w (GPC) of 2170. From these, the non-uniformity factor is calculated to be 1.67. By comparing the molecular weight, obtained from the hydroxyl number determination (M.sub.n /OH number), and the molecular weight, determined from vapor pressure osmometry (M.sub.n /osmometry), a hydroxy functionality of 1.04 is obtained. The residual monomer content is less than 0.1%.

EXAMPLES 2A TO 8A

Synthesis of Monohydroxy-Functional Poly-t-Butyl Methacrylates of Different Molecular Weights by Controlled, Free-Radical Polymerization (not of the invention)

The method of Example 1A is followed with the exception that the molar ratio of t-butyl methacrylate to 2-mercaptoethanol is varied as shown in Table 1.

TABLE 1______________________________________ Molar Ratio Non-Exam- TBMA/ M.sub.n M.sub.n /GPC uniformityple Regu- OH M.sub.n (PMMA- U =No. lator Number Osmometry Stand.) M.sub.w /M.sub.n______________________________________1A 8/1 1150 1200 1300 1.672A 7/1 950 1000 1250 1.483A 4/1 620 700 700 1.524A 10/1 1350 1300 1600 1.595A 15/1 2050 2100 2200 1.796A 20/1 2600 2850 2950 1.847A 40/1 4900 5150 5200 1.748A 80/1 9900 -- 11250 1.98______________________________________ TBMA: tbutyl methacrylate Controller: 2mercaptoethanol M.sub.n : number average molecular weight M.sub.w : weight average molecular weight

EXAMPLE 1B

Synthesis of a polymethyl Methacrylates by Controlled Free Radical Polymerization (not of the invention)

A solution of 1.4 g of azodiisobutyronitrile, 94 g (approximately 0.47 moles) of dodecyl mercaptan, 76 g of xylene and 376 g (approximately 3.76 moles) of methyl methacrylate is added within a period of 3 to 4 hours to a reactor filled with 40 g of xylene. The solvent in the reactor has a temperature of 100.degree. C. and is under an atmosphere of nitrogen.

Subsequently, a further 0.93 g of azodiisobutyronitrile, dissolved in 9.3 g of methyl ethyl ketone, is added in equal parts over a period of one hour. Finally, the reaction mixture is heated for one hour at a constant temperature of 100.degree. C. At the end of the reaction, the solvent and the residual monomers are distilled at a temperature of 130.degree. C. and a pressure of 1 torr. A colorless, viscous liquid remains behind.

Gel permeation chromatographic analysis reveals that the polymer obtained has a number average molecular weight M.sub.n (GPC) of 1100 and a weight average molecular weight M.sub.w (GPC) of 1710. The non-uniformity factor therefore is 1.55. The residual monomer content is less than 0.1%.

EXAMPLES 2B TO 8B

Synthesis of Polymethacrylates with Different Alkyl Groups and Different Molecular Weights by Controlled Free-Radical Polymerization (not of the invention)

The procedure of Example 1B is followed with the exception that different methacrylates are used as monomers and that the ratio of methacrylate to regulator is varied as stated in Table 2. Likewise, number average and weight average molecular weights and the non-uniformity coefficient from gel permeation chromatographic analysis as well as the molecular weight, determined from vapor pressure osmometry, are given in Table 2. In all cases, the residual monomer content found is less than 0.1%.

TABLE 2______________________________________ Molar Non-uni Ratio Meth M.sub.n /GPC formityExam- Meth- acrylate/ M.sub.n (PMMA- U =ple No. acrylate Regulator Osmometry Stand.) M.sub.w /M.sub.n______________________________________1B MMA 8/1 1150 1100 1.552B MMA 28/1 2600 2650 1.863B MMA 46/1 5050 5200 1.784B MMA 95/1 -- 9900 1.945B BMA 5.6/1 950 1000 1.396B BMA 19.7/1 3100 3650 1.787B EHMA 4/1 950 1350 1.348B TFEMA 7/1 1050 1150 1.49______________________________________ MMA: Methyl methacrylate BMA: nButyl methacrylate EHMA: 2Ethylhexyl methacrylate TFEMA: 2,2,2Trifluoroethyl methacrylate Regulator: nDodecyl mercaptan

EXAMPLE 1C

Synthesis of a Polymethyl Methacrylate/Poly-t-Butyl Methacrylate Copolymer (of the Invention)

The controlled polymethyl methacrylate (447 g, approximately 0.40 moles), described in Example 1B, and 490.5 g (approximately 0.42 moles) of the monohydroxy-functional poly-t-butyl methacrylate from Example 1A, dissolved in 438 g of toluene, are heated together with 2 mL of triethylamine under pure nitrogen to about 110.degree. C.

Subsequently, the solvent is distilled off at a pressure of 5 torr, any water present being removed at the same time. After the addition of 470 g of toluene, 4.68 g (0.5% by weight) of isopropyl titanate are added at 115.degree. C. The methanol, formed when the reaction sets in, is separated from the toluene by fractionation and removed. After 4 hours, a further 2.34 g (0.25% by weight) of isopropyl titanate are added, the methanol is removed and the reaction is terminated after another 3 hours.

The hydroxyl number of the product obtained is 1.6 and corresponds to a conversion of 96% (based on the component not used in excess). According to gel permeation chromatographic analysis, the number average molecular weight of the block copolymer M.sub.n (GPC) is 2,350 and the non-uniformity coefficient is 1.48. The molecular weight, determined from vapor pressure osmometry, is 2050.

EXAMPLES 2C TO 15C

Synthesis of Polymethyl Methacrylate/Poly-t-Butyl Methacrylate Copolymers with Different Alky Groups and Different Molecular Weights

In principle, the method of Example 1C is followed, with the exception and as stated in Table 3, that methacrylate segments of different chemical structure and different molecular weights are reacted with monohydroxy-functional poly-t-butyl methacrylates of different molecular weights. Moreover, 1,3-diisopropylbenzene is used instead of toluene as solvent in Examples 9C to 13C. The reaction is carried out at a temperature of 115.degree. C. and a pressure of 40 torr. The total amount of catalysts in Examples 9C to 13C is added in four equal portions. The total reaction time is 16 hours.

TABLE 3__________________________________________________________________________ Polymeth- Conver- Non- PTBMA of acrylate Block sion M.sub.n /GPC uniformityExample Table 1 of Table 2 Copolymer OH M.sub.n (PMMA- U =No. Example No. Example No. Type* Number** Osmometry Stand.) M.sub.w /M.sub.n__________________________________________________________________________1C 1A 1B MV 1111 0.96 2050 2350 1.422C 3A 2B MV 2606 0.91 3200 380 1.633C 2A 1B MV 1110 0.94 2000 2250 1.424C 3A 1B MV 1106 0.87 1500 1800 1.385C 6A 1B MV 1126 0.85 3350 3700 1.666C 7A 1B MV 1150 0.79 5600 6200 1.897C 8A 1B MV 1199 0.75 -- 12500 1.978C 1A 2B MV 2611 0.81 3100 4400 1.569C 3A 5B BV 1006 0.97 1550 1900 1.3110C 1A 5B BV 1011 0.92 1700 2200 1.4411C 1A 6B BV 2611 0.88 3800 4200 1.6412C 3A 7B OV 1006 0.93 1500 1850 1.4213C 1A 7B OV 1011 0.97 2100 2250 1.4714C 3A 8B FV 1106 0.95 1500 1700 1.4415C 1A 8B FV 1111 0.91 2000 2300 1.52__________________________________________________________________________ M: Methyl methacrylate B: nButyl methacrylate O: 2Ethylhexyl methacrylate F: 2,2,2Trifluorethyl methacrylate V: Intermediate = tbutyl methacrylate *The first two numbers in column 4, multiplied by 100, correspond approximately to the molecular weight of the methacrylate block; the last two numbers, multiplied by 100, correspond approximately to the molecular weight of the tbutyl methacrylate block. In the case of the MV 1111 product, this means that each of the two segments has a molecular weight of about 1100. **Moles transesterified, based on the component not used in excess.

EXAMPLE 1D

Synthesis of a Polymethyl Methacrylate/Polymethacrylic Copolymer (of the Invention)

The block copolymer (173 g), described in Example 1C, is heated with 115 g of dioxane and 4.3 g (2.5% by weight) of p-toluenesulfonic acid monohydrate to a temperature of 95.degree. to 100.degree. C. and kept for a period of 5 hours at the same temperature.

The incipient splitting off of the isobutene can be recognized by a distinct evolution of gas. The acid number of the product in the solution obtained is 118 and corresponds to a conversion of 90%.

According to NMR spectroscopy, (.sup.1 H--, .sup.13 C-NMR: comparison of the signal intensities of the characteristic t-butyl group), the conversion is 97%.

EXAMPLES 2D TO 15D

Synthesis of Polymethacrylate/Polymethacrylic acid Copolymers (of the Invention)

The method of Example 1D is followed with the exception that, when the viscosity becomes too high as the isobutene is being split off, the solids concentration is adjusted by dilution with dioxane, so that homogeneous reaction conditions are ensured throughout the reaction.

No solvents were used for Examples 12D and 13D.

A solvent mixture, consisting of one part dioxane and one part toluene, was used for Examples 8D and 11D.

The conversions, determined from the acid number and.sup.13 C NMR spectroscopy, are given in Table 4.

______________________________________ Block Conversion Copolymer of Block in % ConversionExample Table 3 Copolymer (Acid in %No. Example No. Type Number).sup.1 (.sup.13 C-NMR)______________________________________1D 1C MA 1111 90 972D 2C MA 2606 87 983D 3C MA 1110 96 974D 4C MA 1106 92 985D 5C MA 1126 87 976D 6C MA 1150 90 957D 7C MA 1199 92 968D 8C MA 2611 100 989D 9C BA 1006 89 9710D 10C BA 1011 90 9811D 11C BA 2611 94 9612D 12C OA 1006 95 9613D 13C OA 1011 97 9514D 14C FA 1106 95 9915D 15C FA 1111 94 97______________________________________ M: Methyl methacrylate B: nButyl methacrylate O: 2Ethylhexyl methacrylate F: 2,2,2Trifluoroethyl methacrylate A: Acid (= Methacrylic acid) .sup.1 taking into consideration the weighed out amount of ptoluenesulfonic acid monohydrate.

EXAMPLE E

Synthesis of a Polymethyl Methacrylate/Polysodium Methacrylate Copolymer by Neutralization with an Aqueous Sodium Hydroxide Solution (of the invention)

The polymethyl methacrylate/polymethacrylic acid copolymer (2 g), synthesized in Example 1D, is suspended in 31 mL of water, mixed with a few drops of phenolphthalein solution and titrated with 7.7 mL of 1N sodium hydroxide to the end point. A waterwhite solution with a solids content of about 5% is obtained, the pH of which is determined to be 8.7.

Claims

1. A block copolymer of a formula ##STR11## wherein R.sup.1 represents alkyl groups except t-butyl group with 1 to 22 carbon atoms, perfluoroalkyl groups or dialkylaminoalkyl groups,

R.sup.2 is the --(CH.sub.2).sub.p group, in which p is a number from 2 to 6,

R.sup.3 represents a chain length regulator which is free of active hydrogen atoms,

X is a cation, and

n and m are same or different and in each case have an average numerical value of not less than 3.

2. The block copolymer of claim 1, wherein

R.sup.1 is an alkyl group with 1 to 8 carbon atoms except the t-butyl group,

R.sup.2 is --(CH.sub.2).sub.2 --,

R.sup.3 is --C.sub.12 H.sub.25 S--,

X is a hydrogen ion, an alkali ion, an ammonium ion or a substituted ammonium ion, and

n and m are same or different and in each case have an average numerical value of 4 to 20.