Polyoxyalkylene alkenyl ether-maleic ester copolymer and use thereof

FIELD OF THE INVENTION
This invention relates to a novel copolymer of a polyoxyalkylene alkenyl ether and a maleic ester and an emulsifier, dispersant or cement additive comprising the same.
BACKGROUND OF THE INVENTION
Copolymers of maleic anhydride and a compound having an unsaturated group have found their application in various fields. For example, a salt of a diisobutylene-maleic anhydride copolymer is used as a dispersant in an aqueous system as described in Cement & Concrete, No. 478, p. 7 (1986), and an ethyl or butyl ester of a methyl vinyl ether-maleic anhydride copolymer is used in cosmetics as described in Nippon Hanyo Keshokin Genryoshu, p. 161, K. K. Yakuji Nipposha (1985). It has been proposed to use a copolymer of a polyoxyalkylene monoalkenyl ether and a maleic ester of a polyalkylene glycol or a monoalkyl ether thereof as a dispersant for cement as disclosed in JP-A-59-162162 (the term "JP-A3[ as used herein means an "unexamined published Japanese patent application").
However, copolymers of an olefin, e.g., diisobutylene, and maleic anhydride, while non-neutralized, are soluble only in limited kinds of solvents such as toluene. When converted to their salts, they are soluble only in water. Further, having an average molecular weight in the thousands, these copolymers are limited in application.
Esters of methyl vinyl ether-maleic anhydride copolymers are poor in lipophilic properties and therefore unsuitable for use as an emulsifier or dispersant.
Copolymers of a polyoxyalkylene monoalkenyl ether and a maleic ester of a polyalkylene glycol or a monoalkyl ether thereof, though effective as additive for cement, exhibit poor lipophilic properties. Further, similarly to the .alpha.-olefinmaleic anhydride copolymers, they are of limited application due to their average molecular weight in the thousands.
SUMMARY OF THE INVENTION
An object of this invention is to provide a novel copolymer which is of wide application as an emulsifier, a dispersant, an additive for cement, and the like.
This invention provides a copolymer of (a) a polyoxyalkylene alkenyl ether represented by formula (I): ##STR3## wherein Z is a residue of a compound having from 2 to 8 hydroxyl groups; AO is an oxyalkylene group having from 2 to 18 carbon atoms; R is an alkenyl group having from 2 to 18 carbon atoms; R.sup.1 is a hydrocarbon group having from 1 to 40 carbon atoms; a.gtoreq.0; c.gtoreq.0; l.gtoreq.1; m.gtoreq.0; n.gtoreq.0; l+m+n=2 top 8; al+bm+cn=1 to 100; and n/(l+m+n).ltoreq.1/3, and (b) a maleic ester of a compund represented by formula (II):
R.sup.2 O(A.sup.1 O).sub.d H (II)
wherein R.sup.2 is a hydrocarbon group having from 1 to 40 carbon atoms; A.sup.1 O is an oxyalkylene group having from 2 to 18 carbon atoms; and d is from 0 to 100; or formula (III): ##STR4## wherein Z.sup.1 is a residue of a compound containing from 2 to 8 hydroxyl groups; A.sup.2 O is an oxyalkylene group having from 2 to 18 carbon atoms; R.sup.3 is a hydrocarbon group having from 1 to 40 carbon atoms; e.gtoreq.0; f.gtoreq.0; p.gtoreq.0; q.gtoreq.1; p+q=2 to 8; and ep+fq=0 to 100.

BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is an infrared absorption spectrum of the copolymer prepared in Example 2.
FIG. 2 is an infrared absorption spectrum of the copolymer prepared in Example 3.

DETAILED DESCRIPTION OF THE INVENTION
A molar ratio of component (a) to component (b) in the copolymer of the present invention is preferably from 3:7 to 7:3, more preferably about 1:1.
In formula (I), the hydroxyl-containing compound providing a residue represented by Z includes glycols, e.g., ethylene glycol, propylene glycol, butylene glycol, hexylene glycol, styrene glycol, an alkylene glycol having from 8 to 18 carbon atoms, and neopentyl glycol; polyhydric alcohols, e.g., glycerin, diglycerin, polyglycerin, trimethyloletahen, trimethylolpropane, 1,3,5-pentanetriol, erythritol, pentaerythritol, dipentaerythritol, sorbitol, sorbitan, sorbide, a condensation product of sorbitol and glycerin, adonitrol, arabitol, xylitol, and mannitol; partial ethers or esters of the polyhydric alcohol; saccharides, e.g., xylose, arabinose, ribose, rhamnose, glucose, fructose, galactose, mannose, sorbose, cellobiose, maltose, isomaltose, trehalose, sucrose, raffinose, gentianose, and melezitose; and partial ethers or esters of the saccharide.
The oxyalkylene group as represented by AO is derived from ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran, styrene oxide, an .alpha.-olefin oxide having from 6 to 18 carbon atoms, etc. Specific examples are oxyethyelene, oxypropylene, oxybutylene, oxytetramethylene, and oxystyrene groups and an oxyalkylene group having from 6 to 18 carbon atoms. Where the oxyalkylene group comprises two or more kinds of alkylene moieties, they may be linked either in blocks or at random.
The alkenyl group having from 2 to 18 carbon atoms as represented by R preferably includes those having an unsaturated bond at the terminal thereof, e.g., vinyl, allyl, methallyl, isoprenyl, dodecenyl, octadecenyl, and allylphenyl groups.
The hydrocarbon group having from 1 to 40 carbon atoms as represented by R.sup.1 includes methyl, ethyl, propyl, isopropyl, butyl, isobutyl, t-butyl, amyl, isoamyl, hexyl, heptyl, octyl, 2-ethylhexyl, nonyl, decyl, undecyl, dodecyl, isotridecyl, tetradecyl, hexadecyl, isocetyl, octadecyl, isostearyl, oleyl, octyldodecyl, docosyl, decyltetradecyl, benzyl, cresyl, butylphenyl, dibutylphenyl, octylphenyl, nonylphenyl, dodecylphenyl, dioctylphenyl, dinonylphenyl, and styrenated phenyl groups.
In formula (I), l, m, and n are limited for the reasons set forth below. l must be at least 1 for accomplishing copolymerization. If the number of hydroxyl groups, i.e., n, is too large, copolymerization with maleic anhydride would be attended by esterification with maleic anhydride, unfavorably resulting in formation of a three-dimensional structure. Accordingly, a relation of n/(l+m+n).ltoreq.1/3 is preferred.
In formulae (II) and (III), R.sup.2 and R.sup.3 have the same meaning as R.sup.1 ; A.sup.1 O and A.sup.2 O have the same meaning as AO; and Z: has the same meaning as Z.
The copolymer according to the present invention can be prepared as follows. The polyoxyalkylene alkenyl ether of formula (I) and maleic anhydride are copolymerized in the presence of a radical polymerization initiator such as benzoyl peroxide. The resulting copolymer is then esterified with the compound of formula (II) or (III). Alternatively, maleic anhydride and the compound of formula (II) or (III) are subjected to esterification, and the resulting ester is then copolymerized with the polyoxyalkylene alkenyl ether of formula (I) in the presence of a radical polymerization initiator.
The maleic ester unit in the copolymer may be in the form of a monoester or a diester.
The copolymer according to the present invention is a high-molecular weight surface active agent having a weight average molecular weight of more than 1,000, sometimes far up in the ten thousands. The hydrophilic moiety of the copolymer is assigned to the oxyethylene group and hydroxyl group in AO, A.sup.1 O or A.sup.2 O and a carboxyl group formed on ester formation, while the lipophilic moiety is assigned to the hydrocarbon group in R.sup.1, R.sup.2 or R.sup.3 and the oxyalkylene group having 3 or more carbon atoms in AO, A.sup.1 O or A.sup.2 O Thus, it is possible to increase the proportion of the hydrophilic moiety for use as a water-soluble compound, for example, an additive for cement or a dispersant in an aqueous system, or to increase the proportion of the lipophilic moiety for use as an oil-soluble compound, for example, a dispersant for a non-aqueous system. For use as an oil-soluble compound, the copolymer of the present invention may further contain other lipophilic units derived from lipophilic moieties copolymerizable with the polyoxyalkylene alkenyl ether and maleic anhydride, e.g., styrene, .alpha.-olefins, acrylic esters, methacrylic esters, and vinyl acetate.
The polyoxyalkylene alkenyl ether-maleic ester copolymer having the specific structure as described above is a high-molecular weight surface active agent which can be rendered either water-soluble or oil-soluble and is of very wide application as an emulsifier, a dispersant, or an additive for cement.
The present invention is now illustrated in greater detail by way of Examples, but it should be understood that the present invention is not deemed to be limited thereto. All the percents are by weight unless otherwise indicated.
PREPARATION EXAMPLE 1
Preparation of Compound of Formula (I)
In an autoclave were charged 32 g of methanol and 1.1 g of sodium methylate as a catalyst. After purging the autoclave with nitrogen, 396 g of ethylene oxide was slowly introduced thereinto at 140.degree. C. at a pressure of from about 0.5 to 5 kg/cm.sup.2 G to conduct an addition reaction After completion of the reaction, the reaction mixture was cooled to room temperature, 75 g of sodium hydroxide was added thereto, followed by heating to 110.degree. C., and the mixture was dehydrated in a nitrogen atmosphere under reduced pressure of about 20 mmHg. Nitrogen was then added thereto to raise the pressure to 1 kg/cm.sup.2 G, and . 98 g of allyl chloride was slowly added to the mixture while stirring. The alkalinity of the reaction mixture fell and, after 4 hours from the commencement of reaction, assumed a nearly steady value, at which the reaction was stopped. The reaction mixture was neutralized with hydrochloric acid, and the by-produced salt was separated by filtration to recover an allyl ether.
PREPARATION EXAMPLE 2
Preparation of Compound of Formula (I)
In an autoclave were charged 58 g of allyl alcohol and 5.6 g of potassium hydroxide as a catalyst. After purging the autoclave with nitrogen, 2320 g of propylene oxide was slowly introduced thereinto at 100.degree. C. at a pressure of from about 0.5 to 5 kg/cm.sup.2 G to conduct an addition reaction. After completion of the reaction, the catalyst was neutralized with hydrochloric acid, and the by-produced potassium chloride was removed by filtration. To 1624 g of the recovered product was slowly added 21 g of metallic sodium, the mixture was heated to 110.degree. C., and 186 g of dodecyl chloride was added thereto while stirring. The alkalinity of the reaction mixture fell and, after 4 hours from the commencement of the reaction, assumed an almost steady value, at which the reaction was ceased. The reaction mixture was neutralized with hydrochloric acid, and the by-product salt was removed to obtain an allyl ether.
PREPARATION EXAMPLE 3
Preparation of Compound of Formula (I)
In an autoclave were charged 92 g of glycerin, 5 g of boron trifluoride ethyl etherate as a catalyst, and 432 g of tetrahydrofuran. After purging the autoclave with nitrogen, 264 g of ethylene oxide was slowly introduced thereinto at 70.degree. C. at a pressure of from about 0.5 to 5 kg/cm.sup.2 G to conduct an addition reaction. After completion of the reaction, the catalyst was neutralized with sodium carbonate, and the by-produced salt was removed by filtration. To 630.4 g of the reasulting product was slowly added 50 g of metallic sodium, and 180 g of methallyl chloride was slowly added thereto at 100.degree. C.with stirring. The alkalinity of the reaction mixture fell and, after 4 hours from the start of the reaction, assumed an almost steady value, at which the reaction was stopped. The reaction mixture was neutralized with hydrochloric acid, and the by-produced salt was removed by filtration to recover a methallyl ether.
PREPARATION EXAMPLES 4 TO 12
Various polyoxyalkylene alkenyl ethers of formula (I) shown in Table 1below were prepared in the same manner as in Preparation Examples 1 to 3.
TABLE 1__________________________________________________________________________ Degree of HydroxylPreparation Unsaturation ValueExample No. Compound of Formula (I) (milleq/g) (KOH-mg/g)__________________________________________________________________________1 CH.sub.2CHCH.sub.2 (OC.sub.2 H.sub.4).sub.9 OCH.sub.3 2.13 0.082 CH.sub.2CHCH.sub.2 (OC.sub.3 H.sub.6).sub.40 OC.sub.12 H.sub.25 0.39 0.18 3* ##STR5## 2.14 714 CH.sub.2CHCH.sub.2 (OC.sub.2 H.sub.4).sub.4 OCH.sub.3 3.99 0.045 CH.sub.2CHCH.sub.2 (OC.sub.2 H.sub.4).sub.33 OCH.sub.3 0.62 0.036 CH.sub.2CHCH.sub.2 (OC.sub.2 H.sub.4).sub.2 OC.sub.4 H.sub.9 4.98 0.24 ##STR6## 0.65 0.158 ##STR7## 0.73 0.229 CH.sub.2CHCH.sub.2 (OC.sub.2 H.sub.4).sub.20 OCH.sub.2 CHCH.sub.2 2.16 0.0710 CH.sub.2CHCH.sub.2 (OC.sub.2 H.sub.4).sub.20 OC.sub.18 H.sub.37 0.84 0.1311 ##STR8## 1.15 0.1612 ##STR9## 1.31 0.07__________________________________________________________________________ Note: *Additon mode in the brackets { } is at random, and C.sub.4 H.sub.8 O is an oxytetramethylene group.
PREPARATION EXAMPLE 13
Preparation of Maleic Anhydride Copolymer
______________________________________Preparation of Maleic Anhydride Copolymer______________________________________Allyl ether of Preparation Example 1 468 g (1 mol)Maleic Anhydride 98 g (1 mol)Benzoyl peroxide 6 g (1% based on monomers)Toluene 566 g (the same weight as monomers)______________________________________
The above components were charged in a four-necked flask equipped with a cooling pipe, a pipe for introducing nitrogen, a thermometer, and a stirrer. The mixture was heated to 80.degree. C. in a nitrogen stream and stirred for 4 hours to conduct a copolymerization reaction.
Toluene was removed by distillation at 110.degree. C. under reduced pressure of about 10 mmHg to obtain 510 g of a maleic anhydride copolymer as a clear viscous liquid.
The resulting maleic anhydride copolymer was analyzed to obtain the following results:
Elementary Analysis: Calcd. (%]: C 55.11; H 8.18; Found (%): C 55.07; H 8.1.
Degree of Saponification: 196.3 (calcd.: 198.2)
Weight Average Molecular Weight: 13300 (measured by gel-permeation chromatography, hereinafter the same)
EXAMPLE 1
A copolymerization reaction was carried out in the same manner as in Preparation Example 13, except for using the following components and changing the copolymerization temperature to 70.degree. C.
______________________________________Alkenyl ether of Preparation Example 4 248 g (1 mol)Bis(ethylene glycol) maleate 204 g (1 mol)Azobisisobutyronitrile 5 g (1.1% based on monomers)Toluene 452 g (the same weight as monomers)______________________________________
Toluene was removed by distillation at 110.degree. C. under reduced pressure of about 10 mmHg to obtain 420 g of a copolymer as a clear viscous liquid.
Elementary Analysis: Calcd. (%): C 52.5; H 7.5; Found (%): C 52.0; H 7.0.
Degree of Saponification: 240 (calcd.: 248)
Weight Average Molecular Weight: 2000
EXAMPLE 2
In 600 g of pyridine were dissolved 550 g of the maleic anhydride copolymer as obtained in Preparation Example 13 and 600 g of a polyoxyethylene polyoxypropylene glycol random copolymer having a structural formula of HO{C.sub.3 H.sub.6 O).sub.7 (C.sub.2 H.sub.4 O).sub.4 }H, and the solution was refluxed at 110.degree. to 120.degree. C. for 4 hours. Pyridine was removed by distillation under reduced pressure of 10 mmHg or less at 110.degree. to 120.degree. C. to obtain 1085 g of a copolymer as a clear viscous liquid.
Elementary Analysis: Calcd. (%): C 57.1; H 8.4; Found (%): C 56.4; H 8.4.
Degree of Saponification: 93.2 (calcd.: 92.3)
Weight Average Molecular Weight: 13,500
The infrared absorption spectrum of the copolymer is shown in FIG. 1.
EXAMPLE 3
The same procedure of Example 2 was repeated, except for replacing the compound as used in Example 2 with 46 g of ethanol and changing the reaction temperature to 70.degree. to 80.degree. C., to obtain 590 g of a copolymer as a clear viscous liquid.
Elementary Analysis: Calcd. (%): C 54.9; H 8.5; Found (%): C 54.6; H 8.2.
Degree of Saponification: 188 (calcd.: 183)
Weight Average Molecular Weight: 13,300
EXAMPLES 4 TO 12
Copolymers shown in Table 2 below were prepared in the same manner as in the foregoing Examples.
TABLE 2 Compound of Formula (1) OH-Containing Com- Solubility in Preparation Maleic Other pound (inclusive of Polymerization Average Acetone Example Example Amount Anhydride Monomer Maleic Acid Ester) Initiator Molecular Methanol No. No. (mol %) (mol %) (mol %) (mol %) (mol %) Weight Description*.sup.4 Water Ethanol 1 4 50 -- -- bis(ethylene glycol) 50 AIBN*.sup.1 1.1 2,000 liquid soluble soluble maleate 2 1 50 50 -- HO{(C.sub.3 H.sub.6 O).sub.7 (C.sub.2 H.sub.4 O).sub.4 }H 50 BPO*.sup.2 1.0 13,500 " " " (random copolymer) 3 1 50 50 -- ethanol 50 BPO*.sup.2 1.0 13,300 " " " 4 2 50 50 -- HO(C.sub.2 H.sub.4 O).sub.23 H 50 BPEH*.sup.3 1.0 20,000 " insoluble " 5 5 50 50 -- C.sub.18 H.sub.37 O(C.sub.2 H.sub.4 O).sub.20 H 50 BPO*.sup.2 1.0 18,500 solid soluble " 6 6 50 -- -- diisopropyl 50 BPO*.sup.2 1.0 3,500 liquid " " maleate 7 7 50 50 -- ##STR10## 50 BPEH*.sup.3 0.7 130,000 solid " " 8 8 50 50 -- C.sub.9 H.sub.19C.sub.6 H.sub.4O(C.sub.2 H.sub.4 O).sub.10 H 50 AIBN*.sup.1 0.9 16,300 liquid " " 9 10 40 50 styrene 50 C.sub.4 H.sub.9 O(C.sub.3 H.sub.6 O).sub.5 H 50 BPO*.sup. 2 1.2 7,400 solid " " 10 11 44 50 vinyl 2 C.sub.12 H.sub.25 OH 50 BPO*.sup.2 0.9 unmeasurable " insoluble insoluble 3 4 acetate 11 2 46 50 -- HO(C.sub.2 H.sub.4 O).sub.7 H 50 BPEH*.sup.3 1.0 unmeasurable solid insoluble insoluble 9 4 12 1 40 50 ethyl 4 HO(C.sub.3 H.sub.6 O).sub.5 H 50 BPO*.sup.2 1.0 " " " " 3 6 methacrylate 13 1 50 50 -- C.sub.4 H.sub.9 O{(C.sub.2 H.sub.4 O).sub.6 (C.sub.3 H.sub.6 O).sub.2 }H 50 BPEH*.sup.3 1.0 14,400 liquid soluble soluble (random copolymer) 14 5 50 50 -- CH.sub.3 O(C.sub.2 H.sub.4 O).sub.12 Notes: *.sup.1 Azobisisobutyronitrile *.sup.2 Benzoyl peroxide *.sup.3 tButyl peroxy2-ethylhexanoate *.sup.4 at 20.degree. C.
EXAMPLE 15
Each of the copolymers prepared in Examples 4 to 9 was tested for performance as an emulsifier in the following composition.
______________________________________Polydimethylsiloxane (100,000 cst) 35%Emulsifier 5%Water 60%______________________________________
A mixture of polydimethylsiloxane and the copolymer was heated to 70.degree. C., and water at 70.degree. C. was slowly added thereto to emulsify the mixture. The resulting emulsion was allowed to stand in a thermostat at 40.degree. C. for 1 month to examine emulsion stability.
For comparison, the same test was conducted but using the same amount of a nonionic surface active agent in place of the copolymer of the present invention.
The results of examination are shown in Table 3 below.
TABLE 3______________________________________ State of EmulsionEmulsifier of Example After Standing Remarks______________________________________Example 4 Milky white liquid InventionExample 5 " "Example 6 " "Example 7 " "Example 8 " "Example 9 " "C.sub.18 H.sub.37 O(C.sub.2 H.sub.4 O).sub.6 H separated in Comparison two layers1:1 (by weight) separated in "mixture of sorbitan two layersmonostearate andpolyoxyethylene (20mol) sorbitan monosterate______________________________________
It can be seen from Table 3 that the emulsions using the copolymer of the present invention keeps to be stable milky white liquid, proving that the copolymer is an excellent emulsifier.
EXAMPLE 16
Each the copolymers prepared in Example 1 to 9 was tested for performance as a dispersant in the following composition.
______________________________________Calcium stearate 50%Dispersant 5%Water 45%______________________________________
The dispersant was dissolved in water, and calcium stearate was slowly added and dispersed in the solution at 50.degree. C. while stirring by means of a homogenizer to obtain a white viscous slurry. The slurry was allowed to stand in a thermostat at 40.degree. C. for 1 month was carried out using the same amount of a nonionic surface active agent in place of the copolymer of the present invention. The results of the test are shown in Table 4 below.
TABLE 4______________________________________ State of DispersionDispersant of Example After Standing Remarks______________________________________Example 1 Fluidity was Invention maintainedExample 2 Fluidity was " maintainedExample 3 Fluidity was " maintainedExample 4 Fluidity was " maintainedExample 5 Fluidity was " maintainedExample 6 Fluidity was " maintainedExample 7 Fluidity was " maintainedExample 8 Fluidity was " maintainedExample 9 Fluidity was " maintainedC.sub.8 H.sub.17 --C.sub.6 H.sub.4 --O(C.sub.2 H.sub.4 O).sub.15 H Solidified ComparisonC.sub.18 H.sub.37 O(C.sub.2 H.sub.4 O).sub.30 H " "Polyoxyethylene " "(20 mol) sorbitanmonostearate______________________________________
It can be seen from Table 4 that the slurries using the copolymer of the present invention as a dispersant maintained a slurry state of stable fluidity, whereas those using a comparative dispersant solidified and lost fluidity.
EXAMPLE 17
Each of the copolymers prepared in Examples 1 to 14 was tested for performance as an additive for cement in the following composition.
______________________________________Water 165 kg/m.sup.3Cement 300 kg/m.sup.3Sand 758 kg/m.sup.3Gravel (max. size: 25 mm) 1067 kg/m.sup.3Air entrainng and water 0.75 kg/m.sup.3reducing agent ("PozzolithNo. 5L" produced by NissoMaster Builders Co., Ltd.)Additive 3 kg/cm.sup.3 (1% based on cement)Water/cement ratio 55.0%Sand percentage 42.0%______________________________________
In accordance with JIS R 5201, the above components were kneaded in a mortar mixer, and the slump was measured every minutes. After 60 minutes in Run Nos. 15, 16 and 17 or after 90 minutes in other runs, the mixture was cast in a mold (10.times.10.times.40 cm), released from the mold after one day, cured in water at 20.degree. C. for 7 days from the release, and then allowed to stand at 20.degree. C. and 65% RH (relative humidity]. The dry shrinkage of each sample was measured using a comparator method. For reference, compressive strength of each sample was measured after being allowed to stand under the above-described conditions to the age of 35 days. The results of these measurements are shown in Table 5 below.
TABLE 5__________________________________________________________________________ Slump (cm) Immediately After After After Dry Shrinkage Compressive After 30 60 90 After After After StrengthRun No. Additive Kneading Min. Min. Min. 7 Days 14 Days 28 Days (kg/cm.sup.3)__________________________________________________________________________ 1 (Invention) Copolymer of 17.2 16.9 16.5 15.6 0.020 0.035 0.044 397 Example 1 2 (Invention) Copolymer of 18.0 17.4 17.3 17.2 0.010 0.026 0.027 423 Example 2 3 (Invention) Copolymer of 17.4 17.0 16.6 16.2 0.020 0.030 0.042 398 Example 3 4 (Invention) Copolymer of 18.0 17.7 17.5 17.0 0.020 0.028 0.039 407 Example 4 5 (Invention) Copolymer of 18.0 17.8 17.4 17.1 0.018 0.021 0.029 405 Example 5 6 (Invention) Copolymer of 17.5 17.0 16.4 15.9 0.019 0.029 0.037 396 Example 6 7 (Invention) Copolymer of 17.7 17.5 17.3 17.0 0.013 0.026 0.028 411 Example 7 8 (Invention) Copolymer of 17.8 17.4 17.2 17.0 0.016 0.025 0.031 408 Example 8 9 (Invention) Copolymer of 17.6 17.0 16.5 15.8 0.014 0.022 0.033 412 Example 910 (Invention) Copolymer of 17.4 16.8 16.2 15.7 0.017 0.022 0.033 406 Example 1011 (Invention) Copolymer of 17.3 16.9 16.4 16.0 0.018 0.025 0.034 405 Example 1112 (Invention) Copolymer of 17.5 17.0 16.3 16.0 0.020 0.027 0.036 403 Example 1213 (Invention) Copolymer of 18.0 18.0 17.9 17.8 0.013 0.028 0.032 410 Example 1314 (Invention) Copolymer of 17.7 17.9 18.0 17.9 0.019 0.030 0.038 405 Example 1415 (Comparison) HO{(C.sub.3 H.sub.6 O).sub.7 (C.sub.2 H.sub.4 O).sub.3 }H*.sup.1 16.0 12.2 9.0 unmea- 0.013 0.029 0.030 420 sured16 (Comparison) sodium naphthanene- 17.3 12.5 8.8 unmea- 0.024 0.046 0.060 400 sulfonate formaldehyde sured condensate (mol. wt.: 4,000)17 (Comparison) sodium diiso- 17.4 15.8 13.8 12.9 0.025 0.044 0.060 393 butylenemaleic anhydride copolymer (mol. wt.: 5,000)18 (Comparison) none 14.0 11.2 8.3 unmea- 0.026 0.046 0.060 395 sured__________________________________________________________________________ Note: *.sup.1 The bracket { } means a random copolymer
As is shown in Table 5, the copolymers according to the present invention are excellent in prevention of slump loss and dry shrinkage without adversely affecting compressive strength.
While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Number	Name	Date
4471100	Tsubakimoto et al.	Sep 1984
4946904	Akimoto et al.	Aug 1990
4946918	Akiyama et al.	Aug 1990

Number	Date	Country
0056627	Jul 1982	EPX
0315167	May 1989	EPX

Polyoxyalkylene alkenyl ether-maleic ester copolymer and use thereof

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

US Referenced Citations (3)

Foreign Referenced Citations (2)

Non-Patent Literature Citations (3)

Entry
Derwent Abstract of JP-A-59-162162.
Database WPIL, No. 84-266252, Derwent Publications Ltd., London, GB; & JP-A-59 162 162 (Sanyo Chem. Ind. Ltd) (Cat. D).
Database WPIL, No 90-232609, Derwent Publications Ltd., London, GB; & JP-A-379 676 (Nippon Oil and Fats Co.).