Polypropylene resin prefoamed particles

Abstract

Prefoamed particles consisting essentially of an ethylene/propylene random copolymer, wherein said prefoamed particles are obtained by foaming particles of an ethylene/propylene random copolymer containing 1 to 4% by weight of random-copolymerized ethylene at a temperature in the range of from Tm - 15.degree. C. to Tm - 5.degree. C. (in which Tm is a temperature at which to terminate melting of the copolymer) and within the range of 141.degree. to 151.degree. C., and wherein said prefoamed particles have a crystal structure characterized in that in a DSC curve obtained by heating 1 to 3 mg of the copolymer prefoamed particles to 220.degree. C. at a heating rate of 10.degree. C./min. with a differential scanning calorimeter, there appear a peak (characteristic peak) characteristic of the copolymer and another peak (high temperature peak) at a higher temperature than a temperature at which the characteristic peak appears.

Description

This invention pertains to polypropylene resin prefoamed particles having good in-mold moldability.

So-called bead expanded articles (in-mold expanded articles) obtained by filling prefoamed particles in a mold and heat-expanding them have found wide acceptance in cushioning materials, packages, heat-insulating materials, building materials, etc. because of their excellent cushioning properties, heat-insulating properties, etc., and the demand thereof has been lately much increased.

In-mold expanded articles made of polystyrene prefoamed particles have been so far known as this type of expanded articles. However, said articles have a fatal defect of brittleness and further a defect a inferiority in chemical resistance. The improvement of these defects has been long desired. In-mold expanded articles made from cross-linked polyethylene prefoamed particles have been proposed to remedy such defects. In this instance, it is nevertheless hard to obtain low-density (highly expanded) articles by in-mold expansion. When an attempt is made to prepare low-density molded articles, the resulting articles have a notable shrinkage, great water absorption and poor properties. Molded articles that can be put to practical use have not been obtainable.

The present inventors have therefore focussed their attention on excellent properties of polypropylene resins and made studies for making in-mold expanded articles from polypropylene resin prefoamed particles to remedy the defects associated with the conventional in-mold expanded articles. However, in producing in-mold expanded articles from polypropylene resin prefoamed particles, there have been sometimes obtained expanded articles having a low density (high expansion), low water absorption, low shrinkage and excellent dimensional stability, but at other times only expanded articles having a great shrinkage. Thus, stable good expanded articles could not have been altogether produced.

The present inventors have further made extensive studies to look into the cause thereof, and consequently found that a good in-mold expanded article is obtained when polypropylene resin prefoamed particles used in the in-mold expansion molding are prepared from a specific ethylene/propylene random copolymer and have such a crystal structure that in a DSC curve obtained by the measurement with a differential scanning calorimeter, there appear a peak characteristic of the copolymer and a high temperature peak at a higher temperature than a temperature at which the characteristic peak appears.

Thus, the present invention provides prefoamed particles consisting essentially of an ethylene/propylene random copolymer, wherein said prefoamed particles are obtained by foaming particles of an ethylene/propylene random copolymer containing 1 to 4% by weight of random-copolymerized ethylene at a temperature in the range of from Tm - 15.degree. C. to Tm - 5.degree. C. (in which Tm is a temperature at which to terminate melting of the copolymer) and within the range of 141.degree. to 151.degree. C., and wherein said prefoamed particles have a crystal structure characterized in that in a DSC curve obtained by heating 1 to 3 g of the copolymer prefoamed particles to 220.degree. C. at a heating rate of 10.degree. C./min. with a differential scanning calorimeter, there appear a peak (characteristic peak) characteristic of the copolymer and another peak (high temperature peak) at a higher temperature than a temperature at which the characteristic peak appears.

In the present invention, the DSC curve obtained by measuring the ethylene/propylene random copolymer prefoamed particles with the differential scanning calorimeter means a DSC curve given when 1 to 3 mg of the copolymer prefoamed particles is heated to 220.degree. C. at a heating range of 10.degree. C./min with the differential scanning calorimeter. For instance, a DSC curve given when a sample is heated from room temperature to 220.degree. C. at a heating rate of 10.degree. C./min is designated a first DSC curve, and then a DSC curve given when the sample is cooled from 220.degree. C. to about 40.degree. C. at a cooling rate of 10.degree. C./min and subsequently heated again to 220.degree. C. at a heating rate of 10.degree. C./min is designated a second DSC curve. A characteristic peak and a high temperature peak can be found from these DSC curves.

The characteristic peak here referred to is a heat atmosphere peak characteristic of a polypropylene resin making up foamed particles, and is considered ascribable to what is called a heat absorption of the polypropylene resin at the point of melting. Said characteristic peak appears in both the first and second DSC curves. The temperatures at the peaks in the first and second DSC curves are at times slightly different, yet the difference is less than 5.degree. C. and usually less than 2.degree. C.

The high temperature peak here referred to is a heat absorption peak appearing at a higher temperature than that of the characteristic peak in the first DSC curve. Polypropylene resin prefoamed particles wherein the high temperature peak does to appear in the DSC curve have a poor in-mold expansion moldability and cannot provide good expanded articles. The above high temperature peak is presumed to be attributable to the presence of a crystal structure different from the structure showing the characteristic peak. Said high temperature peak appears in the first DSC curve, but does not appear in the second DSC curve obtained by heating under the same conditions. Accordingly, the structure showing the high temperature peak is one which the ethylene/propylene random copolymer prefoamed particles of this invention possess. It is not given by heating with the differential scanning calorimeter.

It is desirous that the difference between the temperature of the characteristic peak appearing in the second DSC curve and the temperature of the high temperature peak appearing in the first DSC curve is great. The difference therebetween is 5.degree. C. or above, preferably 10.degree. C. or above.

The ethylene/propylene random copolymer prefoamed particles of this invention can be afforded by charging a sealed vessel with 100 parts by weight of the copolymer particles, 100 to 400 parts by weight of water, 5 to 30 parts by weight of a volatile blowing agent (e.g. dichlorodifluoromethane) and 0.1 to 3 parts by weight of a dispersant (e.g. finely divided aluminum oxide), heating the mixture to a temperature in the range of from Tm - 15.degree. C. to Tm - 5.degree. C. (Tm is a temperature at which to terminate melting of the copolymer) and within the range of 141.degree. to 151.degree. C., then opening one end of the vessel, releasing said resin particles and water from inside the vessel to an atmosphere held at a lower pressure than that of the vessel and expanding the resin particles.

To explain the temperature (Tm) at which to terminate melting, 6 to 8 mg of a sample is heated to 220.degree. C. at a heating rate of 10.degree. C./min with a differential scanning calorimeter, then cooled to about 40.degree. C. at a cooling rate of 10.degree. C./min and heated again to 220.degree. C. at a heating rate of 10.degree. C./min. The temperature (Tm) means a temperature given when the heat absorption in the DSC curve obtained by the second heating is returned to a position of a base line.

There can be obtained, as aforesaid, the prefoamed particles of this invention having a structure that the characteristic peak and the high temperature peak appear in the DSC curve by defining the expansion temperature in the above fixed temperature range which is less than the temperature (Tm) at which to terminate melting. Where the expansion temperature deviates from the above range, the characteristic peak only appears in the DSC curve of the resulting prefoamed particles without the high temperature peak.

Bead expanded articles (in-mold expanded articles) can be produced by pressurizing the above obtained prefoamed particles of this invention with an inorganic gas such as air, filling the pressurized particles into a mold and heat-expanding them with steam of 3 to 4 kg/cm.sup.2 (G). The bead expanded articles are also characterized in that the characteristic peak and the high temperature peak which are approximately the same as those in the prefoamed particles used as the starting material appear in the DSC curve.

The following Examples and Comparative Examples illustrate this invention specifically. Parts in the respective Examples and Comparative Examples are all on the weight basis.

EXAMPLES 1-5 AND COMPARATIVE EXAMPLES 1-6

A sealed vessel was charged with 300 parts of water, 100 parts of ethylene/propylene random copolymer particles, 0.3 part of ultrafine aluminum oxide as a dispersant and a given amount of a volatile blowing agent indicated in Table 1. The mixture was heated with stirring. After the reaction mixture was maintained for 30 minutes at an expansion temperature indicated in Table 1, one end of the vessel was opened while keeping the pressure in the inside of the vessel at 30 kg/cm.sup.2 with a nitrogen gas, and the resin particles and water were released to an open atmosphere at the same time. The resin particles were expanded to afford prefoamed particles having an apparent expansion ratio (bulk ratio) indicated in Table 1.

With respect to the prefoamed particles, using a differential scanning calorimeter (DT-30 Model, an apparatus manufactured by Schimazu Seisakusho), the first measurement was conducted by heating said particles to 220.degree. C. at a heating rate of 10.degree. C./min, and subsequently the second measurement was conducted by cooling said particles to 40.degree. C. at a cooling rate of 10.degree. C./min and heating them again to 220.degree. C. at a heating rate of 10.degree. C./min.

A DSC curve for the prefoamed particles in Example 1 is represented in FIG. 1, and a DSC curve for the prefoamed particles in Comparative Example 3 in FIG. 2, respectively.

In FIGS. 1 and 2, the full line shows the DSC curve obtained in the first measurement and the dashed line the DSC curve obtained in the second measurement, respectively.

In the individual DSC curves obtained for the prefoamed particles in Examples 1-5, a difference (.DELTA.T) between the temperature of the characteristic peak (a) appearing in the second DSC curve and the temperature of the high temperature peak (b) appearing in the first DSC curve was found, and the results are indicated in Table 1.

Subsequently, the prefoamed particles in Examples 1-5 and Comparative Examples 1-6 were pressurized for 24 hours with air held at 2 kg/cm.sup.2 (G) and then filled in a mold having an internal size of 50 mm.times.300 mm.times.300 mm. Said particles were heat-expanded with steam held at 3.2 kg/cm.sup.2 (G). Each of the resulting expanded articles was dried in an oven kept at 80.degree. C. for 24 hours and slowly cooled to room temperature. Thereafter, an expansion ratio, shrinkage and water absorption were measured for the resulting articles. A melt adhesion was also estimated depending on a water absorption. The results are indicated in Table 1.

TABLE 1__________________________________________________________________________ Polymer Prefoaming conditions Ethylene Maximum contents in Volatile blowing temperature ethylene-propylene agent in the inside Expansion Tm random-copolymers Amount of the vessel temperature (.degree.C.) (wt. %) Type (parts) (.degree.C.) (.degree.C.)__________________________________________________________________________Example1 153 2.0 Dichloro- 18 146 146 difluoro- methane2 153 2.0 Dichloro- 20 143 143 difluoro- methane3 157 1.2 Dichloro- 20 151 151 difluoro- methane4 148 2.8 Dichloro- 18 141 141 difluoro- methane5 146 3.2 Dichloro- 18 143 141 difluoro- methaneComparativeExample1 153 2.0 Dichloro- 8 152 152 difluoro- methane2 153 2.0 Dichloro- 30 125 125 difluoro- methane3 153 2.0 Dichloro- 16 160 125 difluoro- methane4 162 0.8 Dichloro- 16 160 125 difluoro- methane5 140 4.0 Dichloro- 16 140 137 difluoro- methane6 147 3.0 Dichloro- " 145 137 difluoro- methane__________________________________________________________________________ Prefoamed particles Moldability High Melt adhesion Bulk temperature .DELTA.T Expansion Shrin- Water ratio peak .degree.C. ratio kage.sup.*1 absorption.sup.*2 Estimation__________________________________________________________________________Example1 45 Yes 13 43 .circle. less than Melt adhesion 0.003 g/cm.sup.3 is good2 25 Yes 12 24 .circle. less than Melt adhesion 0.003 g/cm.sup.3 is good3 20 Yes 11 19 .circle. less than Melt adhesion 0.003 g/cm.sup.3 is good4 30 Yes 12 28 .circle. less than Melt adhesion 0.003 g/cm.sup.3 is good5 35 Yes 13 33 .circle. less than Melt adhesion 0.003 g/cm.sup.3 is goodComparativeExample1 12 No -- 7 X at least Melt adhesion 0.03 g/cm.sup.3 is poor2 3 No -- Molding impossible (No) Melt adhesion molded article resulted) is poor3 38 No -- 26 X at least Melt adhesion 0.03 g/cm.sup.3 is poor4 30 No -- 25 X at least Melt adhesion 0.03 g/cm.sup.3 is poor5 10 No -- 7 X at least Melt adhesion 0.03 g/cm.sup.3 is poor6 10 No -- 8 X at least Melt adhesion 0.03 g/cm.sup.3 is poor__________________________________________________________________________ .sup.*1 .circle. Indicates that percent decrease of a size in a surface direction of an expanded article relative to a size of a mold (50 mm .times. 300 mm .times. 300 mm) is less than 3%, and X indicates that said percent decrease is 3% or more. .sup.*2 Measured according to JIS K6767 B method.

EXAMPLES 6-11 AND COMPARATIVE EXAMPLES 7-11

A sealed vessel was charged with 300 parts of water, 100 parts of ethylene/propylene random copolymer particles, 0.3 part of ultrafine aluminum oxide as a dispersant and a given amount of a volatile blowing agent indicated in Table 2. The mixture was heated with stirring. After the reaction mixture was maintained at an expansion temperature indicated in Table 2 for 30 minutes, one end of the vessel was opened while keeping the pressure in the inside of the vessel at 30 kg/cm.sup.2 (G) with a nitrogen gas. The resin particles and water were released to an open atmosphere at the same time, and the resin particles were expanded to afford prefoamed particles.

A similar DSC curve as shown in FIG. 1 was obtained for the prefoamed particles in Examples 6-11, and a similar DSC curve as shown in FIG. 2 for the prefoamed particles in Comparative Examples 7-11, respectively.

The prefoamed particles were pressurized for 48 hours with air held at 2 kg/cm.sup.2 (G), filled in a mold having an internal size of 50 mm.times.300 mm.times.300 mm and heat-expanded with a steam held at 3.2 kg/cm.sup.2 (G). Each of the thus obtained in-mold expanded articles was dried for 24 hours in an oven kept at 60.degree. C. and slowly cooled to room temperature.

As for the respective expanded articles, using a differential scanning calorimeter (DT-30 Model, an apparatus manufactured by Shimazu Seisakusho), the first measurement was conducted by heating said article to 220.degree. C. at a heating rate of 10.degree. C./min, and the second measurement by cooling said article to 40.degree. C. at a cooling rate of 10.degree. C./min and heating it again to 220.degree. C. at a heating rate of 10.degree. C./min.

A DSC curve for the in-mold expanded article in Example 6 is represented in FIG. 3 and a DSC curve for the in-mold expanded article in Comparative Example 7 in FIG. 4, respectively. In FIGS. 3 and 4, the full line indicates the DSC curve obtained by the first measurement and the dashed line the DSC curve obtained by the second measurement, respectively.

In the individual DSC curves obtained for the in-mold expanded articles in Examples 6-11, a different (.DELTA.T) between the temperature of the characteristic peak (a) appearing in the DSC curve of the second DSC curve and the temperature of the high temperature peak (b) appearing in the first DSC curve was found, and the result are indicated in Table 2.

An expansion ratio, compression hardness, compression set and water absorption were measured for the respective in-mold expanded articles, and the results are indicated in Table 2.

TABLE 2__________________________________________________________________________ Polymer Prefoaming conditions Ethylene Maximum contents in Volatile blowing temperature ethylene-propylene agent in the inside Expansion Tm random copolymer Amount of the vessel temperature (.degree.C.) (wt. %) Type (parts) (.degree.C.) (.degree.C.)__________________________________________________________________________Example 157 1.2 Dichloro- 20 145 1456 difluoro- methaneExample 157 1.2 Dichloro- 18 143 1437 difluoro- methaneExample 157 1.2 Dichloro- 7.4 145 1458 difluoro- methane Trichloro- 12.6 fluoro- methaneExample 153 2.0 Dichloro- 18 146 1469 difluoro- methaneExample 148 2.8 Dichloro- 18 141 14110 difluoro- methaneExample 146 3.2 Dichloro- 18 141 14111 difluoro- methaneComparative 157 1.2 Dichloro- 16 160 126Example 7 difluoro- methaneComparative 157 1.2 Dichloro- 5 160 135Example 8 difluoro- methaneComparative 157 1.2 Dichloro- 10 160 135Example 9 difluoro- methane Trichloro- 10 fluoro- methaneComparative 130 8.0 Dichloro- 23 137 137Example 10 difluoro- methaneComparative 138 4.2 Dichloro- 23 137 137Example 11 difluoro- methane__________________________________________________________________________ DSC curve In-mold expanded article High Compression Compression Water temperature .DELTA.T Expansion hardness .sup.*1 set.sup.*2 absorption.sup.*3 peak (.degree.C.) ratio (kg/cm.sup.2) (%) (g/cm.sup.3)__________________________________________________________________________Example Yes 13 45 0.70 6.0 less than6 0.003Example Yes 11 20 1.70 9.0 less than7 0.003Example Yes 17 32 1.10 8.2 less than8 0.003Example Yes 13 43 0.70 5.5 less than9 0.003Example Yes 12 28 1.35 7.9 less than10 0.003Example Yes 13 33 1.20 7.8 less than11 0.003Comparative No -- 31 0.47 52 0.03Example 7 or moreComparative No -- 19 0.74 45 0.03Example 8 or moreComparative No -- 25 0.55 40 0.03Example 9 or moreComparative No -- 40 1.0 40 0.03Example 10 or moreComparative No -- 40 0.9 30 0.03Example 11 or more__________________________________________________________________________ .sup.*1 Measured according to JIS K6767. .sup.*2 Measured according to JIS K6767. .sup.*3 Measured according to JIS K6767 B method.

As has been thus far explained, the prefoamed particles of this invention have excellent in-mold moldability because they are produced from specific ethylene/propylene random copolymer particles under specific temperature conditions and have such crystal structure that the characteristic peak of the polypropylene resin and the high temperature peak at a higher temperature than that of the characteristic peak appear in the DSC curve. That is, when the prefoamed particles are expanded in a mold, a molded article having a low density (high expansion), low water absorption and excellent compression hardness and compression set can be readily obtained without great shrinkage which is observed in an in-mold expanded article made from polypropylene resin prefoamed particles having a crystal structure that the high tempeature peak does not appear in the DSC curve. On top of that, the in-mold expanded article produced from the ethylene/propylene random copolymer prefoamed particles in this invention is not brittle and is excellent in impact strength and chemical resistance compared with an in-mold expanded article obtained from polystyrene resin prefoamed particles. Besides, the in-mold expanded article in this invention is superior to an in-mold expanded article obtained from cross-linked polyethylene prefoamed particles in that even the expanded article having a low density (high expansion) is excellent owing to a low shrinkage and water absorption.

Claims

1. Prefoamed particles consisting essentially of an ethylene/propylene random copolymer, wherein said prefoamed particles are obtained by foaming particles of an ethylene/propylene random copolymer containing 1 to 4% by weight of random-copolymerized ethylene at a temperature in the range of from Tm - 15.degree. C. to Tm - 5.degree. C. (in which Tm is a temperature at which to terminate melting of the copolymer) and within the range of 141.degree. to 151.degree. C., and wherein said prefoamed particles have a crystal structure characterized in that in a DSC curve obtained by heating 1 to 3 mg of the copolymer prefoamed particles to 220.degree. C. at a heating rate of 10.degree. C./min. with a differential scanning calorimeter, there appear a peak (characteristic peak) characteristic of the copolymer and another peak (high temperature peak) at a higher temperature than a temperature at which the characteristic peak appears.

2. The prefoamed particles of claim 1 wherein a difference betwen the temperature at which the characteristic peak appears and the temperature at which the high temperature peak appears is at least 5.degree. C.

3. A bead expanded article prepared by filling the prefoamed particles of claim 1 in a mold and heat-expanding said particles.