Claims
- 1. A polystyrene resin composition having improved stiffness comprising:
- (a) 100 parts by weight of a composition comprising a polystyrene resin having dispersed therein 2 to 30% by weight of a rubber material, said rubber material being dispersed in said polystyrene resin as particles having an average particle diameter of 0.5 to 5 .mu.m,
- (b) 2 to 50 parts by weight of a fibrous potassium titanate, and
- (c) 0.1 to 5 parts by weight of a higher fatty acid and/or its metal salt.
- 2. The polystyrene resin composition according to claim 1, wherein said fibrous potassium titanate has an average fiber length of from 10 to 60 .mu.m and an average fiber diameter of from 0.1 to 1.5 .mu.m.
- 3. The polystyrene resin composition according to claim 2, wherein the fibrous potassium titanate has an average fiber length of from 10 to 30 .mu.m and an average fiber diameter of from 0.1 to 0.8 .mu.m.
- 4. The polystyrene resin composition according to claim 1, wherein the amount of the fibrous potassium titanate is from 10 to 50 parts by weight.
- 5. The polystyrene resin composition according to claim 4, wherein the amount of the fibrous potassium titanate is from 15 to 50 parts by weight.
- 6. The polystyrene resin composition according to claim 5, including (d) 4 to 35 parts by weight of a fire retardant and (e) 1 to 5 parts by weight of a carbon fiber.
- 7. The polystyrene resin composition according to claim 6, wherein the fibrous potassium titanate has an average fiber length of from 20 to 60 .mu.m and an average fiber diameter of from 0.5 to 1.5 .mu.m.
- 8. The polystyrene resin composition according to claim 1, 2, 3, 4, 5, 6, or 7, wherein said higher fatty acid is a saturated fatty acid having 12 to 22 carbon atoms and said metal is selected from the group consisting of metals of Groups II and III of the periodic table.
- 9. A polystyrene resin composition having improved stiffness consisting of:
- (a) 100 parts by weight of a composition comprising a polystyrene resin having dispersed therein 2 to 30% by weight of a rubber material, said rubber material being dispersed in said polystyrene resin as particles having an average particle diameter of 0.5 to 5 .mu.m,
- (b) 2 to 50 parts by weight of a fibrous potassium titanate,
- (c) 0.1 to 5 parts by weight of at least one of a higher fatty acid and its metal salt,
- (d) 0 to 35 parts by weight of a fire retardant, and
- (e) 0 to 5 pats by weight of a carbon fiber.
- 10. The polystyrene resin composition according to claim 9, wherein the amount of said fire retardant is 4 to 35 parts by weight and the amount of said carbon fiber is 1 to 5 parts by weight.
- 11. The polystyrene resin composition according to claim 9, wherein said fibrous potassium titanate has an average fiber length of from 10 to 60 .mu.m and an average fiber diameter of from 0.1 to 1.5 .mu.m.
- 12. The polystyrene resin composition according to claim 11, wherein the fibrous potassium titanate has an average fiber length of from 10 to 30 .mu.and an average fiber diameter of from 0.1 to 0.8 .mu.m.
- 13. The polystyrene resin composition according to claim 9, wherein the amount of the fibrous potassium titanate is from 10 to 50 parts by weight.
- 14. The polystyrene resin composition according to claim 13, wherein the amount of the fibrous potassium titanate is from 15 to 50 parts by weight.
- 15. The polystyrene resin composition according to claim 13, wherein the fibrous potassium titanate has an average fiber length of from 20 to 60 .mu.m and an average fiber diameter of from 0.5 to 1.5 .mu.m.
- 16. The polystyrene resin composition according to claim 9, wherein said higher fatty acid is a saturated fatty acid having 12 to 22 carbon atoms and said metal is selected form the group consisting of metals of Groups II and III of the periodic table.
- 17. A polystyrene resin composition having improved stiffness consisting of:
- (a) 100 parts by weight of a composition comprising a polystyrene resin having dispersed therein 2 to 30% by weight of a rubber material, said rubber material being dispersed in said polystyrene resin as particles having an average particle diameter of 0.5 to 5 .mu.m,
- (b) 2 to 50 parts by weight of a fibrous potassium titanate having an average fiber length of from 10 to 60 .mu.m and an average fiber diameter of from 0.1 to 1.5 .mu.m,
- (c) 0.1 to 5 parts by weight of at least one of a saturated fatty acid having 12 to 22 carbon atoms and its metal salt, said metal being selected from the group consisting of metals of Groups II and III of the periodic table,
- (d) 4 to 35 parts by weight of a fire retardant, and
- (e) 1 to 5 parts by weight of a carbon fiber.
Priority Claims (1)
Number |
Date |
Country |
Kind |
63-186766 |
Jul 1988 |
JPX |
|
Parent Case Info
This application is a continuation of application Ser. No. 07/673,249 filed Mar. 20, 1992 now abandoned which is a continuation of application Ser. No. 07/294,071 filed Jan. 6, 1989, abandoned.
US Referenced Citations (8)
Non-Patent Literature Citations (4)
Entry |
Kogyo Zairyo (Industrial Materials), vol. 28, No. 8, pp. 85-97 (1980). |
Kogyo Zairyo (Industrial Materials), vol. 29, No. 5, pp. 44-49 (1981). |
Osaka-furitsu Kogyo Gijutsu Kenkyusho Hokoku (Report of Osaka Prefectural Technology Research Laboratories, Japan), No. 77, pp. 49-54 (1980). |
Polymer Engineering and Science, vol. 13, No. 6, pp. 409-414 (1973). |
Continuations (2)
|
Number |
Date |
Country |
Parent |
673249 |
Mar 1992 |
|
Parent |
294071 |
Jan 1989 |
|