Polyurethane protective film

Abstract
A protective film that can be included in multi-layer film laminates for use in marketing, advertising campaigns, particularly outdoor or other environment impacted promotions and safety applications. The film includes at least two different polyurethane polymers and is free or substantially free of polyvinyl chloride based polymer. One polyurethane has an ultimate elongation less than 200%, and another polyurethane has an ultimate elongation more than 400%. The film may be transparent, translucent, clear or have other desirable optical properties.
Description
FIELD

The present subject matter is in the field of non-polyvinyl chloride (PVC) films and non-PVC film laminates for use with small format, and large format graphic films and presentations, advertising media, promotional media, static visual communications, vehicle and product wraps and other commercial applications. The film may be clear, transparent, translucent, or have other desirable optical properties.


BACKGROUND

Polyvinyl chloride films have been used widely in a number of promotional and advertising campaigns, such as outdoor graphics applications in the past. Such applications include signs, banners, fleet marketing graphics, architectural and wall covering, consumer product labeling and other pressure sensitive products. However, there is an increasing awareness on the environmental and health impacts and effects of using PVC based products, which has increased significantly in recent years. Currently, there is a movement to reduce or even eliminate PVC-based products from the consumer marketing, promotional and advertising product streams.


Films for outdoor marketing and graphics applications ideally should have at least some of the following properties: printability, durability, color retention, and scratch resistance. Conformability and proper mechanical properties such as tensile elongation and tensile strength are also important for certain applications. A film with the correct conformability is a film which has sufficient elongation and flexibility to follow the film follow the contour of the subject or surface to which it is applied, preventing the creation of bubbles or gaps between the subject or surface, and the film. A non-conformable film, i.e. a film which does not have sufficient elongation or flexibility may not follow the contour of the subject or surface, creating bubbles or gaps between the surface and the film. Insufficient elongation properties may make the film hard to apply over a surface, e.g. those surfaces that have curves, angles, ridges and other non-planar configurations, but too much elongation may deform the film and potentially causing a distortion of the printed indicia. Sufficient elongation properties make the film easy to apply over those surfaces that have curves, angles, ridges and other non-planar configurations, while sufficiently maintaining the film such as to prevent a distortion of the printed indicia. Films with correct tensile strength prevent easy breakage of the film when being stretched, such as when the film is being applied to a non-planar surface. Films with a low tensile strength may cause the film to break easily when being stretched.


As new PVC replacement films are being developed, some of the films have superior performance in one area, such as printability, but lack adequate functionality with respect to the other properties such as the outdoor durability to make the films acceptable for the demanding advertising and promotional market. One possible way to resolve the foregoing problem is to use a multi-layer film laminate with each layer providing one or more of the desired properties so that the laminate has all the desired properties that are needed.


When used as the outermost protective layer in a film laminate, or simply used as a protective film for a given surface, good outdoor durability and in many cases optical transparency is also required so the indicia on an underneath printable layer can be visible.


Therefore, there is a need for non-PVC-based transparent films and non-PVC film laminates for use with outdoor graphics and other marketing and consumer use applications.


SUMMARY

The embodiments of the present subject matter described below are not intended to be exhaustive or to limit the subject matter to the precise forms disclosed in the following detailed description. Rather, the embodiments are chosen and described so that others skilled in the art may appreciate and understand the principles and practices of the present subject matter.


The subject matter is directed to a non-PVC based film product having similar properties to those of conventional PVC offerings that is suitable for use in connection with marketing promotions, graphics, branding campaigns and other printed or imaged communication based initiatives.


In one exemplary embodiment of the presently described subject matter, a film, which may be clear, transparent, translucent or have other desirable optical properties, is made of at least two different polyurethane polymers, and is substantially free of PVC.


In another exemplary embodiment of the presently described subject matter, an optically transparent protective film comprises at least two different polyurethanes and is substantially free of polyvinyl chloride based polymer. Each of the at least two different polyurethanes comprise at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer.


In another exemplary embodiment of the presently described subject matter, a film laminate includes a top layer, an intermediate layer, and a substrate layer. The top layer is a film comprising at least two different polyurethanes and is substantially free of polyvinyl chloride based polymer. Each of the at least two different polyurethanes comprise at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer. The substrate layer has printed or image indicia thereon.


In another exemplary embodiment of the presently described subject matter, an advertising or informational graphic includes a surface, a film, and an adhesive layer. The surface has promotional indicia provided thereon. The film has front and back faces, the back face being attached to the surface. The adhesive layer is disposed between the back face of the film and the surface and attaches the back face of the film to the surface. The film comprises at least two different polyurethanes and is substantially free of polyvinyl chloride based polymer. Each of the at least two different polyurethanes comprise at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer.


In another exemplary embodiment of the presently described subject matter, an advertising or informational graphic includes a surface, an adhesive layer, a printable substrate, and a transparent film. The printable substrate has front and back faces. The back face of the printable substrate faces the surface and is in contact with the adhesive layer. The front face of the substrate has promotional indicia provided thereon. The transparent film has a top face and a bottom face, wherein the bottom face is facing the front face of the printable substrate. The film comprises at least two different polyurethanes, and is substantially free of polyvinyl chloride based polymer. Each of the at least two different polyurethanes comprise at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer.


In another exemplary embodiment of the presently described subject matter, a roll or sheet of graphic advertising includes a film layer and advertising indicia. The film layer includes a first polyurethane and a second polyurethane and is substantially free of polyvinyl chloride based polymer. The first polyurethane has an ultimate elongation less than 200%. The second polyurethane has an ultimate elongation more than 400%. Each of the first polyurethane and the second polyurethane comprise at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer. The film layer is provided in operative association with advertising indicia.


In another exemplary embodiment of the presently described subject matter, a method of making a protective film includes providing a first polyurethane dispersion that when dried and crosslinked, produces a first polyurethane having an ultimate elongation of less than 200% and is substantially free of polyvinyl chloride based polymer. The method also includes providing a second polyurethane dispersion that when dried and crosslinked, produces a second polyurethane having an ultimate elongation of greater than 400% and is substantially free of polyvinyl chloride based polymer. The method includes mixing the first polyurethane dispersion with the second polyurethane dispersion to form a film composition. The method includes adding one or more additives to the film composition. The additives comprise one or more selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, slip agents, water, isopropyl alcohol, and combinations thereof. The method includes applying the film composition to a surface, and drying the film composition to form the protective film.


In a further exemplary embodiment of the presently described subject matter, a method of protecting an advertising substrate that is subject to degradation from exposure to an outdoor environment includes providing a transparent protective film. The film comprises a first polyurethane having an ultimate elongation of less than 200%, and a second polyurethane having an ultimate elongation of more than 400%. The film is substantially free of polyvinyl chloride based polymer. The method includes covering the advertising substrate with the film to thereby protect the advertising substrate from exposure to the outdoor environment.


Other features and advantages of the present subject matter will become apparent to those skilled in the art from the following detailed description. It is to be understood, however, that the detailed description of the various embodiments and specific examples, while indicating various embodiments of the present subject matter, are given by way of illustration and not limitation. Many changes and modifications within the scope of the present subject matter may be made without departing from the spirit thereof, and the subject matter includes all such modifications.





BRIEF DESCRIPTION OF THE DRAWINGS

These, as well as other objects and advantages of this subject matter, will be more completely understood and appreciated by referring to the following more detailed description of the present exemplary embodiments of the subject matter in conjunction with the accompanying drawings, of which:



FIG. 1 is a sectional illustration of one exemplary embodiment of a film according to the present subject matter;



FIG. 2 is a block diagram illustrating an exemplary manufacturing process for making one embodiment of the film according to the present subject matter;



FIG. 3 is a sectional illustration of one exemplary embodiment of a film according to the present subject matter;



FIG. 4 is a sectional illustration of a further exemplary embodiment of a film laminate according to the present subject matter;



FIG. 5 illustrates the top view of an exemplary embodiment of an advertising graphic applied on a surface according to the present subject matter; and



FIG. 6 illustrates an exemplary embodiment of a roll of an advertising graphic according to the present subject matter.





Unless otherwise indicated, the illustrations in the above figures are not necessarily drawn to scale.


DETAILED DESCRIPTION OF THE EMBODIMENTS

The apparatuses and methods disclosed in this document are described in detail by way of examples and with reference to the figures. Unless otherwise specified, like numbers in the figures indicate references to the same, similar, or corresponding elements throughout the figures. It will be appreciated that modifications to disclosed and described examples, arrangements, configurations, components, elements, apparatuses, methods, materials, etc. can be made and may be desired for a specific application. In this disclosure, any identification of specific shapes, materials, techniques, arrangements, etc. are either related to a specific example presented or are merely a general description of such a shape, material, technique, arrangement, etc. Identifications of specific details or examples are not intended to be, and should not be, construed as mandatory or limiting unless specifically designated as such. Selected examples of apparatuses and methods are hereinafter disclosed and described in detail with reference made to FIGURES.


The present subject matter relates to a film and a film laminate used for outdoor graphics applications, advertising, promotions and other marketing campaigns. More particularly, the present subject matter relates to a non-PVC transparent film and non-PVC film laminate for use in such applications. The film and film laminate provide suitable outdoor durability, scratch resistance, gloss, conformability, tensile elongation and tensile strength. Although many applications of the various films are described as outdoor applications, it will be appreciated that the present subject matter is not limited to outdoor applications. Instead, the films and related aspects of the present subject matter have wide applicability and include indoor applications for example.


In one exemplary embodiment of the subject matter, a transparent film with properties suitable for use in the outdoor graphics applications comprises at least two different polyurethane polymers and is substantially free of PVC based polymer. The term “PVC based polymer” or variations thereof refers to polyvinyl chloride polymers or polymers containing majority weight proportions of PVC.


As used herein the term “graphic” or “graphics” refers to a visually perceptible presentation on some surface that is intended to brand, illustrate, entertain, inform, advertise, announce, and/or market a product, service, event, or the like.


In one embodiment, the film comprises at least two different polyurethane polymers, prepolymers, or co-polymers. In one aspect, the film is made of two polyurethane polymers. One polyurethane has an ultimate elongation of less than 200%. The other polyurethane has an ultimate elongation more than 400%. The two different polyurethanes are combined in amounts or at a weight ratio so that the resulting dried film has an ultimate elongation of greater than 200%. In one aspect, the ultimate elongation of the resulting film is between 200% and 400%. In another aspect, the ultimate elongation of the resulting film is between 250% and 350%. In another aspect, the ultimate elongation of the resulting film is between 200% and 300%.


Using two different polyurethanes allows properties of the film to be specifically tailored for a particular purpose, while not being limited to the properties of a single polyurethane polymer. Using two different polyurethane polymers to produce a film having an ultimate elongation of greater than 200%, allows the characteristics of a film to be tailored in order to provide adequate protection for various intended uses and for substrates of various shapes. Further, properties of films of the present subject matter can be controlled by using specific polyurethane polymers at specific ratios, so as to provide an appropriate balance of different mechanical properties; for example between elasticity and tensile strength.


Typical films having an ultimate elongation between 200% and 400% and formed from a single polyurethane, are too elastic for use as a conformable protective film. In other words, the elasticity of these typical films allows the films to stretch or otherwise change shape when forces are applied thereto. However, these typical films, because they are too elastic, have a tendency to return to their original shape and/or size when the forces are removed. In the case where these typical films are used as protective layer over a substrate in a single or multi-layer film, these typical films tend to peel away from the substrate and/or other layers in a multi-layer film (including where an adhesive layer may be exposed), and fail to offer adequate protection to the substrate. In contrast, the films of the present subject matter can be tailored so that they are not too elastic, and therefore do not tend to pull away from a substrate or other layers in a multi-layer film. In this regard, the present subject matter films, once stretched over a substrate, substantially retain their stretched shape and size so that they offer adequate protection to a substrate.


In one aspect, a film composition is formed by combining a first polyurethane with a different, second polyurethane. The first polyurethane has an ultimate elongation of less than 200% and the second polyurethane has an ultimate elongation of more than 400%. The two polyurethane polymers are combined at a weight ratio from about 20:80 to about 80:20 of the first polyurethane to the second polyurethane. The film composition produces a film having an ultimate elongation of between 200% and 400%.


Various additives as discussed herein, can be added to the film composition. When dried, the film composition forms a transparent film. In one embodiment, the two polyurethanes are included from about 70 weight percent (wt %) to about 99 wt % of the film composition. In another embodiment, the two polyurethanes are included from about 92 wt % to about 97 wt % of the film composition.


In one embodiment, the film composition used to form the film of the present subject matter, has a thickness before drying from about 3.0 mils (76.2 microns) to about 4.5 mils (114.3 microns). In another aspect, the thickness of the film composition before drying is from about 3.3 mils (83.82 microns) to about 4.0 mils (101.6 microns).


After drying, a film is formed having a thickness from about 0.3 mils (7.6 microns) to about 2.0 mils (50.8 microns), in another aspect from about 0.5 mil (12.7 microns) to about 1.5 mils (38.1 microns), and in another aspect from about 0.9 mils (22.9 microns) to about 1.2 mils (30.5 microns). Such film layer can be made from emulsion polymers, solvent polymers, or extruded polymers. When the thickness of the film 100 is too thin, the chemical resistance, scratch resistance and outdoor durability of the film may suffer. When the film is too thick, the thickness of the construction may also impact the conformability of the film.


Reference is now directed to the FIGURES in which FIG. 1 provides a sectional view of an exemplary film prepared in accordance with the presently described subject matter. The film 100 may be a single or multi-layer film. The film may be transparent, translucent, clear or have other desirable optical properties. The film 100 has a top face 102 and a bottom face 104. In one exemplary embodiment, the film 100 comprises a polyurethane polymer including at least two different polyurethane polymers. The film 100 is substantially free of PVC based polymer.


In addition, the film layers may have at least one additive added thereto. If an intermediate layer is included (see FIG. 3), such as an adhesive layer, the additive may also be present in the intermediate layer. The additives are selected from a group including UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, slip agents, co-solvents, water, isopropyl alcohol, or combinations thereof. In one embodiment, the total amount of additives included in the film compositions of the present subject matter is from about 1 wt % to about 30 wt %. In another aspect, the total amount of additives is from about 3 wt % to about 8 wt % of the film composition.


In one embodiment, the polyurethane polymer of the film 100 is a combination of at least two different polyurethane polymers mixed at the molecular level. One polyurethane has ultimate elongation less than 200%, and the other polyurethane has ultimate elongation more than 400%. In one embodiment and in order to be environmentally friendly, the film 100 is created from waterborne dispersions, although other methods for producing the polyurethane polymer may also be used. Typically, there are two methods to make such mixed polymer dispersions. In a first method, a dispersion is formed from the two polyurethanes. In a second method, two polyurethane prepolymers are formed and added together. Polymerization is completed concurrently for the two polyurethane polymers. In one embodiment the two polyurethane dispersions are combined at a weight ratio of about 80:20 to about 20:80 of the first polyurethane dispersion to the second polyurethane dispersion.


The two polyurethane polymer dispersions prepared according to the above described methods have been found to show better mechanical properties when compared to a single polyurethane polymer due to the molecular level mixing which occurs through use of the foregoing processes. In one embodiment, in order to make the formulation even more environmentally friendly, that is to reduce the environmental impact over other preparations, the polyurethane polymer dispersions are further improved to be free of N-methylpyrrolidone (NMP), a component typically used as a processing solvent in other applications. Suitable polyurethane dispersions include but are not limited to Bondthane UD-104, Bondthane UD-255, Bondthane UD-275, and Bondthane UD-312 from Bond Polymers International, Seabrook N.H.; Neorez R-966, Neorez R-2180, Neorez R-2190 from DSM, Heerlen, the Netherlands; and Sancure 2710, Sancure 2715, Sancure 20041, Sancure 20025F from Lubrizol, Wickliffe Ohio.


Suitable polyurethane polymer dispersions for use in the compositions of the present subject matter, are those with aliphatic polyurethane components. As the film products produced can be used in an outdoor environment, the films may be exposed to moisture, such as dew, rain or snow; temperature deviations; light and other conditions which may impact the film performance. For example, moisture may cause components of the film or images thereon to bleach out or fade, and the film itself to whiten. Therefore, the polyurethane polymer structure is designed in order for this film to resist degradation when exposed to such conditions. The polyurethane polymer structures are selected so as to achieve the required tensile properties, block resistance, scratch resistance, transparency, and gloss. For example, the selection and ratio of the two polyurethane polymers controls the tensile properties of the film.


In another embodiment, the polyurethane film dispersions further include a polymer, a copolymer, prepolymers, or polymer blends selected from acrylic, styrene acrylic, vinyl acetate, olefin, and combinations thereof. Suitable polymers included in the polyurethane dispersions comprise, without limitation, acrylic polymers, styrene acrylic polymers, vinyl acetate ethylene copolymers, and polyolefins. Examples of suitable emulsion polymers include, without limitation, JONCRYL 617A JONCRYL 1987, JONCRYL 98, JONCRYL FLX5000, ACRONAL NX4612X and ACRONAL OPTIVE 410 available from BASF, Ludwigshafen, Germany; and VINNAPAS EF 811 from Wacker Chemicals, Munich, Germany or combinations thereof.


In one embodiment, the polyurethane polymer dispersions are crosslinked using a crosslinking agent to form a thermoset elastomer film upon drying. In the present subject matter, the molecular weight of the polyurethane polymer in the films is not particularly critical. In one embodiment, the number average molecular weight of the polyurethane polymer in the protective films upon crosslinking, ranges from about 50,000 to about 100,000.


UV blocking agents and free radical scavengers can be added to the film to improve the outdoor durability. UV blocking agents suitable for this application are typically benzotriazole based compounds, or other compounds capable of absorbing UV energy in the required region. Commercially available UV absorbing agents include, without limitation, TINUVIN 99, TINUVIN 400, TINUVIN 1130 from BASF, Ludwigshafen, Germany; and HOSTAVIN 3310 from Clariant; Muttenz, Switzerland. The amount of UV blocking agents can range from about 0 wt % to about 5 wt %.


Free radical scavengers may also be added to the top layer of the film to improve the weather durability of the top layer. Suitable free radical scavengers include but are not limited to TINUVIN 292, TINUVIN 123 DW from BASF, Ludwigshafen, Germany; and HOSTAVIN 3065 from Clariant, Muttenz, Switzerland. The amount of free radical scavengers can range from about 0 wt % to about 5 wt %.


Other UV blocking systems can also be used for improving weathering durability of this film. These include nano sized zinc oxide, and cerium oxide or combinations thereof which may be used to achieve the UV resistance required for the film. Suitable nano metal oxides include but are not limited to NANOBYK 3840, NANOBYK 3810 from BYK Additives, of Altana, Wesel, Germany. The total amount of UV blocking system additives may range from about 0 wt % to about 10 wt %. UV stabilizers and free radical scavengers can also be added to an intermediate layer, for example an adhesive layer.


Other additives can be used, such as for example, silicon dioxide and/or metal oxide particles to enhance the scratch resistance of the film. The other additives together range from about 0 wt % to about 5 wt % of the total film formulation. Suitable silicon dioxide particles include Minex 12 microparticles from Unimin Corporation and Nanobyk-3620 nanoparticles from BYK. Suitable metal oxides include Nanobyk-3600 aluminum oxide nanoparticles from BYK.


Additional components, such as thickeners, flow and leveling agents, slip agents, and rheology modifiers can be added to the film formulations to achieve desired coating quality. Examples of suitable thickeners include, without limitation, ACRYSOL RM-2020 NPR, TM8W, and UCAR POLYPHOBE 115 TR from Dow Chemicals, Midland, Mich. Examples of suitable flow and leveling agents include without limitation, Capstone FS-30, Capstone FS-35 from Dupont; Polyfox PF-156A from Omnova Solutions; Surfynol 104 from Air Products, and Masurf from Mason Chemical Company and others with similar chemistry. The percent incorporation for flow and leveling agents can vary from 0 wt % to 10 wt % in the film layer. Additional viscosity modifiers can be included in the formulation to modify the viscosity to a desired level and/or to impart desirable flow characteristics. Products like Rheolate 150, Rheolate 212, Rheolate 288, and Rheolate 350 from Elementis are typical examples that can be used in the formulations. The percent incorporation of viscosity modifiers can vary from between 0 wt % to 10 wt % in the film layer. Slip agents include, without limitation, Dow Corning 52, Dow Corning 54, and BYK 301 and can be added to the film formulation at about 0 wt % to about 10 wt %. Other components, such as water or isopropyl alcohol (IPA) can also be added to the formulation at about 0 wt % to about 10 wt %.


Cross-linking agents can be added to the film formulation to improve/modify the mechanical and chemical resistance properties of that film layer. In one embodiment, the cross-linking agent is included to the formulation at about 0 wt % to about 10 wt %. In another embodiment, the cross-linking agent is included to the formulation at about 1 wt % to about 3 wt %. In one embodiment, crosslinking occurs during the drying of the film composition. Examples of suitable cross-linking agents include, without limitation, polyaziridine based CX-100 from DSM Neo Resins, Waalwijk, The Netherlands; UCARLINK XL-25SE, ERL-4221, ERL-4234 from Dow Chemicals, Midland, Mich.; and COATOSIL 1770, SILQUEST A-187 from Momentive Performance Materials Inc., Waterford, N.Y.


Without limitation, other additives, for example, surfactants, defoamers, dispersants, wetting agents, dyes, pigments and co-solvents known to those skilled in the art can be added to the composition of the film layer.


As described herein, many embodiments of the films are free of PVC or at least substantially free of PVC. The term “substantially free” of PVC as used herein refers to relatively low concentrations of PVC in the film composition such as for example, less than 5%, in other embodiments less than 2%, in other embodiments less than 1%, in other embodiments less than 0.5%, and in still other embodiments less than 0.1%. As noted in certain embodiments, the films are free of PVC, i.e., the film(s) contain 0% PVC.


The film 100 can be generated using any process suitable for such purpose. In one embodiment, the film compositions were first deposited onto a removable support or carrier layer by techniques well known to those skilled in the art. Examples of such techniques include die coating, knife coating, curtain coating and reverse roll coating. The removable support can be separated after the compositions have been dried. An exemplary removable support can be selected from a group including a siliconized belt, a release paper, and a release film such as PET or other suitable materials.


An exemplary method of making a film according to the present subject matter is illustrated in the block diagram 200 of FIG. 2. The process begins at operation 205. Operation 210 is to provide the film components and a removable support. Operation 215 provides that the film components are blended to form a film composition. In one embodiment, the film composition includes at least two different polyurethane polymers as described herein, and at least one of free radical scavenger and UV blocking agent. At operation 220, the removable support is coated with the film composition, such as by reverse roll coating, slot die coating, curtain coating or other acceptable methods. At operation 225, the film composition is dried. Drying may occur by using a heated or ambient air environment, curing or by other suitable methods. Alternatively, the film is further laminated with a pressure sensitive adhesive (PSA) coated release liner. At operation 230, the removable support is removed or separated from the dried film. The separation or removal can be accomplished by using a peel blade or knife which serves to separate the film from the carrier or support layer. Alternatively, the film can be separated by the carrier at a sharp angle so that the film can be easily picked up from the carrier or support. The film is rolled up and ready for use. Alternatively, the film can be cut and separated into sheets or sections of equivalent sizes or of varying lengths. The method ends at operation 235.


In addition to the foregoing, the film can be further overcoated with a varnish or other material to provide a glossy appearance. This operation may occur during the film forming process, after printing, or after collection or rolling up of the material after the production process has been completed.


The film of the present subject matter can be used in operative association with a graphic or other message. As used herein, operative association includes applying the film over the graphic or message, including wherein the graphic or message is part of a substrate, over which the film is applied. As used herein, operative association also includes the graphic or message being an additional layer, such as a printing layer or previously printed layer on the film. As used herein, operative association also includes applying a graphic or message over the film.


In certain versions of the present subject matter, the films exhibit a relatively high degree of transparency. That is, the film(s) may be optically transparent or at least substantially so. The term “transparent” as used herein and with reference to certain transparent films of the present subject matter refers to such films that exhibit a transparency of at least 60%, in other embodiments at least 70%, in still other embodiments at least 80%, in yet other embodiments at least 90%, in still further embodiments at least 95%, in other embodiments at least 98%, and in particular embodiments at least 99% as measured by ASTM D1746.


The film can be used as part of a printable media for outdoor applications, architectural and transportation type advertising campaigns and the like. The film can also be used as a protective film to be laminated over a subject, such as a protective laminate for electronic appliances, architectural, artistic or aesthetic elements, a retro-reflective license plate, a retro-reflective signage film, a name plate, a label, automotive exterior and interior parts, and the like. Additional exemplary uses may include safety signs, a graphic display, governmental mandated displays, military applications, or a surface that needs protection in an outdoor environment.


In one embodiment, the film also includes an adhesive layer. The adhesive can be a pressure sensitive adhesive, glue, and any other type of adhesives that are optically transparent, and when used to contact the printed indicia, would not affect the printed indicia. The adhesive may be pattern coated, and may be selected for particular properties such as permanent, removable or repositionable and the like. The adhesive can be random copolymer adhesives or block copolymer adhesives. Random copolymer adhesives include those based upon acrylic and/or methacrylic copolymers, α-olefin copolymers, silicone copolymers, chloroprene/acrylonitrile copolymers, and the like. Block copolymer adhesives including those based upon linear block copolymers (i.e., A-B and A-B-A type), branched block copolymers, star block copolymers, grafted or radial block copolymers, and the like, and natural and synthetic rubber adhesives. A description of useful pressure sensitive adhesives can be found in Encyclopedia of Polymer Science and Engineering, Vol. 13. Wiley-Interscience Publishers (New York, 1988). Additional descriptions of useful pressure sensitive adhesives can be found in Encyclopedia of Polymer Science and Technology, Vol. 1, Interscience Publishers (New York, 1964).


The film layer and the adhesive layer are substantially coextensive with one another, that is the edges and/or sides are aligned and in juxtaposition. It is of course possible, that the adhesive layer could be applied in a pattern on the film layer so that the layers are not completely juxtaposed on one another.


When pressure sensitive adhesives are used, a release liner can be used to protect the adhesive from inadvertent contact with unintended surfaces. Any release liner suitable for the chosen adhesive can be used. For pressure sensitive adhesives, release liners can be coated papers or films, and super calendared paper, for example. Coating materials suitable for release liners include, for example, silicone-based and fluorine-based materials, or any other material that has the desired releasing properties, for example, waxes and carbamates.



FIG. 3 illustrates one embodiment of the current subject matter. The transparent film 400 has a top face 402, a bottom face 404, an intermediate layer 406 and a release liner 408. Upon application, the release liner can be peeled off to expose a face of the intermediate layer 406, which in one embodiment is an adhesive. The film 400 can be attached to the surface to be protected through the adhesive layer 406. The intermediate layer 406 may include an adhesive layer, a tie coating layer or an adhesion promoting layer.


The film can also be used as part of a larger film laminate. FIG. 4 illustrates a cross-sectional view of one embodiment of a film laminate. The film laminate 514 is comprised of a transparent film 500 having a top face 502 and a bottom face 504, an adhesive layer 506, an ink layer 510, and an underlying substrate layer 512. Though referred to as an ink layer, the ink may not necessarily form a continuous layer. Various printable materials can be used as the underlying substrate layer. A non-PVC based printable material is used in one embodiment to make the whole film laminate non-PVC based. International patent application PCT/US08/84812 describes various films created using non-PVC compositions and is incorporated herein by reference in its entirety. Ink or toner anchor coatings, such as polyvinyl alcohol can be added to increase the anchorage of the printing to the laminate.



FIG. 5 illustrates a top view of an exemplary embodiment of a system 600 including an advertising graphic film laminate 612 applied to a surface 616 according to the present subject matter. The film laminate 612 bearing advertising graphic 614 is posted on a surface 616 through the use of an adhesive.



FIG. 6 illustrates an exemplary embodiment of a roll of the film laminate 700 according to the present subject matter.


Test Methods


Thickness


Film thickness is measured using TMI Model 49-70 Precision Micrometer available from Testing Machines Inc. in Ronkonkoma, N.Y. The specimen is placed between an upper and a lower anvil. The upper anvil rests on top of the specimen and the thickness is measured and displayed on the digital readout.


CIE L*a*b* Color Space


This test is used to describe the color of a sample. This 3-dimensional color space system was developed by the International Commission on Illumination (CIE), and defines L* as representing the lightness of the color, ranging from 0 (black) to 100 (white). In this system, a* represents the color's position along the red (magenta)/green axis, in which negative values represent green and positive values represent red or magenta, and b* represents the color's position along the blue/yellow axis, in which negative values represent blue and positive values represent yellow. The test is conducted using a COLOR I 5 Benchtop Spectrophotometer available from X-Rite, Inc., Grand Rapids, Mich. The test method is TAPPI T524 om-94.


Accelerated Weathering


Accelerated weathering test simulates the damaging effects of long term outdoor exposure of materials by exposing test samples to light, moisture and temperature extremes. A sample is tested and observed for light fastness (fading of colors), and weatherability (cracking, chalking, curling, shrinkage, etc. . . . ). An Atlas C165A Xenon Arc Weather-Ometer from Atlas Material Testing Technology LLC in Chicago, Ill. is used for this test.


A printing pattern with white, yellow, magenta, cyan and black stripes is first printed on a printable substrate. The film of the current subject matter, which may be transparent, translucent, clear or have other desirable optical properties, is then laminated over the print layer to make a film laminate through the use of a pressure sensitive adhesive. The sample is first tested for CIE L*a*b* Color Space before being placed in the Weather-Ometer. The sample is allowed to age in the Weather-Ometer for a designated amount of time. The sample is taken out of the Weather-Ometer for CIE L*a*b* Color Space reading and observation for any changes in shrinkage, chalking, cracking, etc. If there is no visible change after 2000 hours, and the changes in L*, a* and b* together, represented by ΔE, is less than 10, the sample is given a pass grade. ΔE value is calculated using the following formula:

ΔE=√{square root over ((ΔL2+Δa2+Δb2))}.

Gloss


Gloss is measured using a BYK Gardner Micro-TRI-Gloss Gloss Meter from BYK Gardner USA in Columbia, Md. The universal measurement angle 60° is used for the measurement. Typically, the acceptable gloss reading is 80 or higher.


Tensile Strength and Tensile Elongation


The tensile elongation and tensile strength of the film is tested using Instron Model 5542 from Instron Co. in Canton, Mass. A modified ASTM D882 was used to determine the tensile strength and percentage elongation of the films of the present subject matter. The procedure is as follows:

    • 1. A 1 inch wide by 4 inch long (25.4 mm×101.6 mm) specimen was cut from the film with the 4 inch length being parallel to the machine direction of the film.
    • 2. The film was gripped across the 1 inch width at both ends, so that the separation between the grips is 2 inches (50.8 mm).
    • 3. The crosshead speed was set at 12 inches per minute (“ipm”) (304.8 mm per minute).
    • 4. The tensile strength was obtained, which is the product of (tensile stress) x (thickness of the film). The tensile strength at break is the product of (maximum stress that occurs at break)×(thickness of the film).
    • 5. The percent elongation is reported by the machine.


The standard for passage requires a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch (“psi”) (6,895 N/m2). The presence or absence of pressure sensitive adhesive (PSA) on the film does not appreciably alter the strength and/or elongation of the film. As such, wherever the film in the examples below includes PSA, the tensile elongation test was performed using the same film but without the layer of PSA.


Rivet Testing


Test samples approximately 2.5 inch (63.5 mm)×2.5 inch (63.5 mm) are applied over painted 4 inch (101.6 mm)×12 inch (304.8 mm) aluminum panels from Frontier Tank Center in Richfield, Ohio. Brazier rivet heads which are 11.4 mm (diameter)×3.3 mm (height)×7.62 mm (shaft diameter) (0.45″ (diameter)×0.13″ (height)×0.3″ (shaft diameter)) are uniformly distributed over the aluminum panel. Application is done so as to minimize forming any wrinkles especially around these rivet heads. Entrapped air is released with the use of pin pricks while a brush with hard bristles and plastic squeegee is used to conform the film around the rivet. The sample is dwelled for 24 hours at ambient conditions. After this time, the diameter of the lifted portion of the film around the rivet is measured and recorded. The sample is then placed in Atlas Ci5000 Xenon Arc Weather-Ometer from Atlas Electric Devices Co. in Chicago, Ill., using a UVB 313 bulb for 1000 hours. The sample is then taken out and the diameter of the film lifted around the rivets is measured again. When the change in diameter is less than 0.0625 inch (1.58 mm), the sample is given a pass grade.


Shrinkage Test


Test sample is coated with a pressure sensitive adhesive under the trade name S8072 from Avery Dennison Corporation in Pasadena, Calif. at about 30 gram per square meter (g/m2) coat weight. The sample is then attached to a clean aluminum panel from 0-Lab Corporation of Cleveland, Ohio. The sample is dwelled at ambient condition for 24 hours. A 5 inch (127 mm) cross hatch in both machine direction (MD) and cross-machine direction (CD) are made on the film. The sample is then aged at 160° F. (71° C.) for 48 hours. The dimension change in the MD and CD are measured. If the shrinkage is less than 0.33% in both directions, the sample is given a pass grade.


EXAMPLES

The materials used in the following examples are listed in Table 1 with information on the function, supplier and location of each.












TABLE 1





Material
Function
Supplier
Location







Bondthane UD-255
Base polymer
Bond Polymer
Seabrook, New




International
Hampshire


Bondthane UD-275
Base polymer
Bond Polymer
Seabrook, New




International
Hampshire


Tinuvin 400
UV absorbant
BASF
Ludwigshafen,





Germany


Tinuvin 99
UV absorbant
BASF
Ludwigshafen,





Germany


Tinuvin 292
Radical scavenger
BASF
Ludwigshafen,





Germany


Byk 024
Defoamer
Byk
Wesel, Germany


Surfynol 104BC
Wetting agent
Air products
Allentown,





Pennsylvania


Byk 301
Slip agent
Byk
Wesel, Germany


Rheolate 350
Rheology modifier
Elementis specialties
East Windsor, New





Jersey


Rheolate 150
Rheology modifier
Elementis specialties
East Windsor, New





Jersey


Neorez cx-100
Crosslinker
DSM
Heerlen, Netherlands









Table 2 lists four examples of formulations used to create the film. All component percentages are by weight.











TABLE 2








Example No.













1
2
3
4



wt %
wt %
wt %
wt %
















Bondthane UD-255
63.78
63.78
53.78
63.58



Bondthane UD-275
27.34
27.34
37.34
27.14



Tinuvin 400
1.14
0
0
0



Tinuvin 99
1.14
1.14
1.14
1.14



Tinuvin 292
1.14
1.14
1.14
1.14



Byk 024
0.01
0.01
0.01
0.01



Surfynol 104BC
0.05
0.05
0.05
0.05



Byk 301
0
1.14
1.14
1.14



Rheolate 350
0.63
0.63
0.63
0.63



Rheolate 150
0.51
0.51
0.51
0.51



Neorez cx-100
0.76
0.76
0.76
1.16



Total wt %
96.5
96.5
96.5
96.5









Examples 1 to 4
Film Compositions

In Examples 1 to 4 the balance 3.5 wt % comprises water, as some components have been diluted before mixing.


Table 3 lists four examples of film thicknesses. Examples 5 to 8 were formed using film compositions, Examples 1 to 4 respectively, to form the film.











TABLE 3








Example No.













5
6
7
8
















Thickness (mils)
1.0
1.2
1.4
1.6









Examples 5 to 8
Films

Film Examples 5 to 8 have been tested for various properties. The thickness of the films has been measured and the films have been tested for gloss at 60 degrees, tensile elongation, scratch resistance, and shrinkage. The films have been subjected to the accelerated weathering and rivet testing. For scratch resistance and shrinkage test, each sample is coated with about 30 g/m2 of a pressure sensitive adhesive under the trade name S8072 from Avery Dennison Corporation in Pasadena, Calif. For accelerated weathering and rivet testing, the adhesive coated sample is further laminated onto a printable film. The printable film is Example No. 29B in the PCT application PCT/US08/84812, which has been incorporated by reference herein in its entirety.


Table 4 lists the properties measured for each of Examples 5 to 8. All examples have passed the accelerated weathering test, have a gloss higher than 90 when measured at 60°, and tensile elongation higher than 200. All of the samples have passed the scratch resistance test, rivet testing, and shrinkage test.











TABLE 4








Example No.













5
6
7
8
















Thickness (mils)
1
1.2
1.4
1.6



Accelerated
Pass
Pass
Pass
Pass



Weathering Test







Gloss @ 60°
>80
>80
>80
>80



Tensile Elongation
>250
>250
>250
>250



Rivet test
Pass
Pass
Pass
Pass



Shrinkage test
pass
pass
pass
pass









All patents, published applications, and articles noted herein are hereby incorporated by reference in their entirety.


All of the features disclosed in the specification, including the claims, abstract, and drawings, and all of the operations in any method or process disclosed, may be combined in any combination, except combinations where at least some of such features and/or operations are mutually exclusive. Each feature disclosed in the specification, including the claims, abstract, and drawings, can be replaced by alternative features serving the same, equivalent, or similar purpose, unless expressly stated otherwise. Thus, unless expressly stated otherwise, each feature disclosed is one example only of a generic series of equivalent or similar features. Publications, patents and patent applications are referred to throughout this disclosure. All references cited herein are hereby incorporated by reference.


The foregoing detailed description of the present subject matter is provided for purposes of illustration, and it is not intended to be exhaustive or to limit the subject matter to the particular embodiments disclosed. The embodiments may provide different capabilities and benefits, depending on the configuration used to implement the key features of the subject matter. Accordingly, the scope of the subject matter is defined only by the following claims.

Claims
  • 1. A protective film comprising at least two different polyurethanes; wherein: the film is free or substantially free of polyvinyl chloride based polymer;each of the at least two different polyurethanes comprise at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer;the at least two different polyurethanes are included in the film at an amount of from 70% to 99% by weight of the film;the film further comprises a third polymer, wherein said third polymer is a polymer, co-polymer, prepolymer, or hybrid polymer selected from the group consisting of vinyl acetate, olefin, and combinations thereof;the at least two different polyurethanes and third polymers are mixed together; andthe film passes a rivet test in which (i) the film is applied over a painted aluminum panel having brazier rivet heads uniformly distributed over the aluminum panel such that the film is conformed around each rivet, (ii) the applied film and panel is dwelled for 24 hours at ambient conditions, (iii) a portion of the film around a rivet is then lifted and the diameter measured, (iv) the applied film and panel are then subjected to accelerated weathering including exposure to UV for 1,000 hours, and (v) after the accelerated weathering the portion of the lifted film is measured again and the diameter is compared to the measured diameter prior to accelerated weathering and the change in diameter is less than 0.0625 in (1.58 mm).
  • 2. The film as recited in claim 1, wherein the film comprises: a first polyurethane having an ultimate elongation less than 200%, and a second polyurethane having an ultimate elongation more than 400%.
  • 3. The film as recited in claim 1, wherein the first polyurethane and the second polyurethane are included at a weight ratio from about 80:20 to about 20:80 of the first polyurethane to the second polyurethane.
  • 4. The film as recited in claim 1, further comprising at least one additive in the film selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, slip agents, water, isopropyl alcohol and combinations thereof.
  • 5. The film as recited in claim 1, further comprising an adhesive layer in contact with a surface of the film.
  • 6. The film as recited in claim 1, wherein the film exhibits a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch.
  • 7. The film as recited in claim 1, wherein the film passes a shrinkage test in which (i) the film is adhered to an aluminum panel, (ii) the adhered film and panel are dwelled for 24 hours at ambient conditions, (iii) a 5 inch (127 mm) cross hatch is made on the film in both a machine direction and a cross direction, (iv) the film and panel are then aged at 160° F. (71° C.) for 48 hours, (v) the dimensional change in the machine direction and the cross direction are measured, and (vi) the shrinkage is less than 0.33% in both machine and cross directions.
  • 8. A film laminate comprising a top layer, an intermediate layer, and a substrate layer, wherein: the top layer is a film comprising at least two different polyurethanes and is free or substantially free of polyvinyl chloride based polymer;each of the at least two different polyurethanes comprising at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer;the substrate layer has printed or image indicia thereon;the at least two different polyurethanes are included in the film at an amount of from 70% to 99% by weight of the film;the top layer further comprises a third polymer, wherein said third polymer is a polymer, co-polymer, prepolymer, or hybrid polymer selected from the group consisting of styrene, vinyl acetate, olefin, and combinations thereof;the at least two different polyurethanes and third polymer are mixed together; andthe film passes a rivet test in which (i) the film is applied over a painted aluminum panel having brazier rivet heads uniformly distributed over the aluminum panel such that the film is conformed around each rivet, (ii) the applied film and panel is dwelled for 24 hours at ambient conditions, (iii) a portion of the film around a rivet is then lifted and the diameter measured, (iv) the applied film and panel are then subjected to accelerated weathering including exposure to UV for 1,000 hours, and (v) after the accelerated weathering the portion of the lifted film is measured again and the diameter is compared to the measured diameter prior to accelerated weathering and the change in diameter is less than 0.0625 in (1.58 mm).
  • 9. The film laminate as recited in claim 8, wherein the intermediate layer is selected from a group consisting of an adhesive layer, a tie coating layer, and an adhesive promotion layer.
  • 10. The film laminate as recited in claim 8, further including at least one additive in the top layer, selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, slip agents, water, isopropyl alcohol and combinations thereof.
  • 11. The film laminate as recited in claim 8 wherein the film exhibits a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch.
  • 12. The film laminate as recited in claim 8, wherein the film passes a shrinkage test in which (i) the film is adhered to an aluminum panel, (ii) the adhered film and panel are dwelled for 24 hours at ambient conditions, (iii) a 5 inch (127 mm) cross hatch is made on the film in both a machine direction and a cross direction, (iv) the film and panel are then aged at 160° F. (71° C.) for 48 hours, (v) the dimensional change in the machine direction and the cross direction are measured, and (vi) the shrinkage is less than 0.33% in both machine and cross directions.
  • 13. The film laminate as recited in claim 8, wherein the top layer includes a first polyurethane having an ultimate elongation less than 200%, and a second polyurethane having an ultimate elongation more than 400%.
  • 14. The film laminate as recited in claim 13, wherein the first polyurethane and the second polyurethane are included at a weight ratio from about 80:20 to about 20:80 of the first polyurethane to the second polyurethane.
  • 15. An advertising or informational graphic, comprising a surface having promotional indicia provided thereon, a film having front and back faces, the back face being attached to the surface, and an adhesive layer disposed between the back face and the surface, wherein: the adhesive attaches the back face of the film to the surface;the film comprises at least two different polyurethanes and is free or substantially free of polyvinyl chloride based polymer;each of the at least two different polyurethanes comprising at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer;the at least two different polyurethanes are included in the film at an amount of from 70% to 99% by weight of the film;the film further comprises a third polymer, wherein said third polymer is a polymer, co-polymer, prepolymer, or hybrid polymer selected from the group consisting of styrene, vinyl acetate, olefin, and combinations thereof;the at least two different polyurethanes and third polymer are mixed together; andthe film passes a rivet test in which (i) the film is applied over a painted aluminum panel having brazier rivet heads uniformly distributed over the aluminum panel such that the film is conformed around each rivet, (ii) the applied film and panel is dwelled for 24 hours at ambient conditions, (iii) a portion of the film around a rivet is then lifted and the diameter measured, (iv) the applied film and panel are then subjected to accelerated weathering including exposure to UV for 1,000 hours, and (v) after the accelerated weathering the portion of the lifted film is measured again and the diameter is compared to the measured diameter prior to accelerated weathering and the change in diameter is less than 0.0625 in (1.58 mm).
  • 16. The graphic as recited in claim 15, wherein: the film includes a first polyurethane having an ultimate elongation less than 200%, and a second polyurethane having an ultimate elongation more than 400%; andthe first polyurethane and the second polyurethane are included at a weight ratio from about 80:20 to about 20:80 of the first polyurethane to the second polyurethane.
  • 17. The graphic recited in claim 15, wherein the film exhibits a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch.
  • 18. The graphic as recited in claim 15, wherein the film passes a shrinkage test in which (i) the film is adhered to an aluminum panel, (ii) the adhered film and panel are dwelled for 24 hours at ambient conditions, (iii) a 5 inch (127 mm) cross hatch is made on the film in both a machine direction and a cross direction, (iv) the film and panel are then aged at 160° F. (71° C.) for 48 hours, (v) the dimensional change in the machine direction and the cross direction are measured, and (vi) the shrinkage is less than 0.33% in both machine and cross directions.
  • 19. An advertising or informational graphic, comprising: a surface;an adhesive layer;a printable substrate having front and back faces, the back face facing the surface and in contact with the adhesive layer, and the front face having promotional indicia provided thereon; anda transparent film having a top face and a bottom face, with the bottom face facing the front face of the printable substrate;wherein:the transparent film comprises at least two different polyurethanes, and is free or substantially free of polyvinyl chloride based polymer, each of the at least two different polyurethanes comprising at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer;the at least two different polyurethanes are included in the film at an amount of from 70% to 99% by weight of the film;the film further includes a third polymer, wherein said third polymer is a polymer, co-polymer, prepolymer, or hybrid polymer selected from the group consisting of styrene, vinyl acetate, olefin, and combinations thereof; andthe at least two different polyurethanes and third polymer are mixed together; andthe film passes a rivet test in which (i) the film is applied over a painted aluminum panel having brazier rivet heads uniformly distributed over the aluminum panel such that the film is conformed around each rivet, (ii) the applied film and panel is dwelled for 24 hours at ambient conditions, (iii) a portion of the film around a rivet is then lifted and the diameter measured, (iv) the applied film and panel are then subjected to accelerated weathering including exposure to UV for 1,000 hours, and (v) after the accelerated weathering the portion of the lifted film is measured again and the diameter is compared to the measured diameter prior to accelerated weathering and the change in diameter is less than 0.0625 in (1.58 mm).
  • 20. The advertising graphic as recited in claim 19, wherein: the film includes a first polyurethane having an ultimate elongation less than 200%, and a second polyurethane having an ultimate elongation more than 400%, andthe first and second polyurethane are included at a weight ratio from about 80:20 to about 20:80 of the first polyurethane to the second polyurethane.
  • 21. The advertising graphic as recited in claim 19, wherein the adhesive layer includes an adhesive selected from the group consisting of a permanent adhesive, a removable adhesive, a repositionable adhesive, and combinations thereof.
  • 22. The advertising graphic as recited in claim 19, wherein the substrate includes a print layer.
  • 23. The advertising graphic as recited in claim 19, further including at least one additive in the film, selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross- linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, slip agents, water, isopropyl alcohol and combinations thereof.
  • 24. The advertising graphic as recited in claim 19, wherein the film exhibits a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch.
  • 25. The advertising graphic as recited in claim 19, wherein the film passes a shrinkage test in which (i) the film is adhered to an aluminum panel, (ii) the adhered film and panel are dwelled for 24 hours at ambient conditions, (iii) a 5 inch (127 mm) cross hatch is made on the film in both a machine direction and a cross direction, (iv) the film and panel are then aged at 160° F. (71° C.) for 48 hours, (v) the dimensional change in the machine direction and the cross direction are measured, and (vi) the shrinkage is less than 0.33% in both machine and cross directions.
  • 26. A roll or sheet of graphic advertising comprising a film layer and advertising indicia, wherein: the film layer includes a first polyurethane having an ultimate elongation less than 200%, a second polyurethane having an ultimate elongation more than 400%, and is free or substantially free of polyvinyl chloride based polymer, each of the first polyurethane and the second polyurethane comprising at least one of polyurethane polymer, polyurethane prepolymer, and polyurethane copolymer; andthe film layer is provided in operative association with the advertising indicia;the at least two different polyurethanes are included in the film at an amount of from 70% to 99% by weight of the film;the film further includes a third polymer, wherein said third polymer is a polymer, co-polymer, prepolymer, or hybrid polymer selected from the group consisting of styrene, vinyl acetate, olefin, and combinations thereof;the at least two different polyurethanes and third polymer are mixed together; andthe film passes a rivet test in which (i) the film is applied over a painted aluminum panel having brazier rivet heads uniformly distributed over the aluminum panel such that the film is conformed around each rivet, (ii) the applied film and panel is dwelled for 24 hours at ambient conditions, (iii) a portion of the film around a rivet is then lifted and the diameter measured, (iv) the applied film and panel are then subjected to accelerated weathering including exposure to UV for 1,000 hours, and (v) after the accelerated weathering the portion of the lifted film is measured again and the diameter is compared to the measured diameter prior to accelerated weathering and the change in diameter is less than 0.0625 in (1.58 mm).
  • 27. The roll or sheet of graphic advertising as recited in claim 26, wherein the first polyurethane and the second polyurethane are included at a weight ratio from about 80:20 to about 20:80 of the first polyurethane to the second polyurethane.
  • 28. The roll or sheet of graphic advertising as recited in claim 26, further including a substrate layer provided over the film layer, wherein the substrate layer includes a print layer.
  • 29. The roll or sheet of graphic advertising film as recited in claim 26, further including at least one additive in the film layer selected from the group consisting of UV stabilizing agents, free-radical scavengers, cross-linking agents, thickeners, flow and leveling agents, rheology modifiers, surfactants, defoamers, dispersants, wetting agents, dyes, pigments, co-solvents, slip agents, water, isopropyl alcohol, and combinations thereof.
  • 30. The roll or sheet of graphic advertising as recited in claim 26, wherein the film exhibits a minimum ultimate elongation of 180% and a minimum tensile strength of 0.5 pound per square inch.
  • 31. The roll or sheet of graphic advertising as recited in claim 26, wherein the film passes a shrinkage test in which (i) the film is adhered to an aluminum panel, (ii) the adhered film and panel are dwelled for 24 hours at ambient conditions, (iii) a 5 inch (127 mm) cross hatch is made on the film in both a machine direction and a cross direction, (iv) the film and panel are then aged at 160° F. (71° C.) for 48 hours, (v) the dimensional change in the machine direction and the cross direction are measured, and (vi) the shrinkage is less than 0.33% in both machine and cross directions.
  • 32. The roll or sheet of graphic advertising as recited in claim 26, further including an adhesive layer provided on the film layer.
  • 33. The roll or sheet of graphic advertising as recited in claim 32, further including a release layer provided over the adhesive layer.
CROSS-REFERENCE TO RELATED APPLICATION

The present application claims the benefit of U.S. Provisional Application No. 61/921,600 filed Dec. 30, 2013, which is incorporated herein by reference in its entirety.

US Referenced Citations (352)
Number Name Date Kind
3351573 Skreckoski Nov 1967 A
3684758 Honig et al. Aug 1972 A
3843478 Zuscik et al. Oct 1974 A
3870521 Mackey et al. Mar 1975 A
4069186 Ramig Jan 1978 A
4108819 Oyamada et al. Aug 1978 A
4198330 Kaizerman et al. Apr 1980 A
4416749 Mahr et al. Nov 1983 A
4436520 Llpko et al. Mar 1984 A
4532189 Mueller Jul 1985 A
4644030 Loewrigkeit et al. Feb 1987 A
4921759 Orain et al. May 1990 A
4935470 Tanuma et al. Jun 1990 A
4978436 Kelly Dec 1990 A
4983461 Daude et al. Jan 1991 A
4983662 Overbeek et al. Jan 1991 A
5030505 Dickinson Jul 1991 A
5041517 Vu et al. Aug 1991 A
5051295 Mori et al. Sep 1991 A
5060981 Fossum et al. Oct 1991 A
5102737 Josephy et al. Apr 1992 A
5104928 Craun et al. Apr 1992 A
5116442 Daude et al. May 1992 A
5120154 Lasch et al. Jun 1992 A
5135797 Sasaki et al. Aug 1992 A
5254394 Bothe et al. Oct 1993 A
5290842 Sasaki et al. Mar 1994 A
5306374 Hambright Apr 1994 A
5314713 Mori et al. May 1994 A
5324467 Anderson, II Jun 1994 A
2364435 Foster et al. Dec 1994 A
5376430 Swenson et al. Dec 1994 A
5420195 Mayer et al. May 1995 A
5422189 Warner et al. Jun 1995 A
5436073 Williams et al. Jul 1995 A
5458935 Alzner Oct 1995 A
5468532 Ho et al. Nov 1995 A
5480705 Tolliver et al. Jan 1996 A
5486426 McGee et al. Jan 1996 A
5494980 Butler et al. Feb 1996 A
5508105 Orensteen et al. Apr 1996 A
5558913 Sasaki et al. Sep 1996 A
5562962 Tung Oct 1996 A
5567761 Song Oct 1996 A
5571861 Klein et al. Nov 1996 A
5578669 Odawa et al. Nov 1996 A
5585193 Josephy et al. Dec 1996 A
5593785 Mayo et al. Jan 1997 A
5594065 Tien et al. Jan 1997 A
5612107 Sangani et al. Mar 1997 A
5623016 Klein et al. Apr 1997 A
5643669 Tsuei Jul 1997 A
5662997 Onishi et al. Sep 1997 A
5672413 Taylor et al. Sep 1997 A
5688573 Goeb et al. Nov 1997 A
5691425 Klein et al. Nov 1997 A
5700582 Sargeant et al. Dec 1997 A
5702790 Be et al. Dec 1997 A
5712044 Fanselow et al. Jan 1998 A
5721086 Emslander et al. Feb 1998 A
5728430 Sartor et al. Mar 1998 A
5755929 Kuroyama et al. May 1998 A
5766744 Fanselow et al. Jun 1998 A
5783303 Tsuei Jul 1998 A
5798123 Cleckner et al. Aug 1998 A
5837375 Brault et al. Nov 1998 A
5849419 Josephy et al. Dec 1998 A
5853899 Anderson et al. Dec 1998 A
5856010 Furuya et al. Jan 1999 A
5866248 Dressier Feb 1999 A
5873607 Waggoner Feb 1999 A
5882388 Adair et al. Mar 1999 A
5888615 Mascarenhas et al. Mar 1999 A
5888635 Yang et al. Mar 1999 A
5902673 Missell et al. May 1999 A
5955512 Numazawa et al. Sep 1999 A
5981045 Kuwabara et al. Nov 1999 A
6001916 Walker et al. Dec 1999 A
6022925 Tomko et al. Feb 2000 A
6025068 Pekala Feb 2000 A
6031041 Chung et al. Feb 2000 A
6033514 Davis et al. Mar 2000 A
6040035 Satoh et al. Mar 2000 A
6045648 Palmgren et al. Apr 2000 A
6045920 Ou-Yang et al. Apr 2000 A
6063858 Daniels et al. May 2000 A
6074747 Scholz et al. Jun 2000 A
6077648 Nair et al. Jun 2000 A
6087001 Jacquemet et al. Jul 2000 A
6093451 Sandlin et al. Jul 2000 A
6096425 Smith Aug 2000 A
6106982 Mientus et al. Aug 2000 A
6110570 Paleari et al. Aug 2000 A
6114021 Pankratz et al. Sep 2000 A
6132858 Kloos Oct 2000 A
6143408 Fujita Nov 2000 A
6146770 Sargeant et al. Nov 2000 A
6150013 Balaji et al. Nov 2000 A
6152115 Busato et al. Nov 2000 A
6153288 Shih et al. Nov 2000 A
6156403 Cochran Dec 2000 A
6159605 Hanada et al. Dec 2000 A
6165593 Brault et al. Dec 2000 A
6171681 Mascarenhas et al. Jan 2001 B1
6177187 Niemoller et al. Jan 2001 B1
6194061 Satoh et al. Feb 2001 B1
6207361 Greener et al. Mar 2001 B1
6218455 Smith et al. Apr 2001 B1
6225381 Sharma et al. May 2001 B1
6228486 Kittel et al. May 2001 B1
6239209 Yang et al. May 2001 B1
6258441 Oguchi et al. Jul 2001 B1
6258918 Ho et al. Jul 2001 B1
6261670 Hakomori et al. Jul 2001 B1
6270912 Peet Aug 2001 B1
6280027 Lawrence et al. Aug 2001 B1
6316120 Emslander Nov 2001 B1
6329060 Barkac et al. Dec 2001 B1
6355345 Furuya et al. Mar 2002 B1
6358660 Agler et al. Mar 2002 B1
6379813 Anderson et al. Apr 2002 B1
6383644 Fuchs May 2002 B2
6391415 McCurry et al. May 2002 B1
6395209 Yoshida et al. May 2002 B2
6403202 Gu et al. Jun 2002 B2
6403223 Albro Jun 2002 B1
6410200 Williams et al. Jun 2002 B1
6428895 Reihs et al. Aug 2002 B1
6436496 Rackovan et al. Aug 2002 B1
6447883 Chen et al. Sep 2002 B1
6451908 Koonce et al. Sep 2002 B1
6461706 Freedman et al. Oct 2002 B1
6461722 Kittel et al. Oct 2002 B1
6495628 Origuchi et al. Dec 2002 B1
6509075 McCurry et al. Jan 2003 B1
6509097 Hatakeyama et al. Jan 2003 B1
6521325 Engle et al. Feb 2003 B1
6531216 Williams et al. Mar 2003 B1
6541101 Cook et al. Apr 2003 B1
6552115 Zecha et al. Apr 2003 B1
6555213 Koneripalli et al. Apr 2003 B1
6555240 Nishikori et al. Apr 2003 B1
6566024 Bourdelais May 2003 B1
6573011 Nair et al. Jun 2003 B1
6589636 Emslander et al. Jul 2003 B2
6592700 Wang et al. Jul 2003 B2
6599593 Niu et al. Jul 2003 B1
6617008 Kono et al. Sep 2003 B1
6623841 Venkatasanthanam et al. Sep 2003 B1
6630049 Hannington et al. Oct 2003 B2
6632485 Tang et al. Oct 2003 B1
6641879 Matsuura et al. Nov 2003 B1
6649260 Kumano et al. Nov 2003 B2
6663947 Freedman et al. Dec 2003 B2
6667093 Yuan et al. Dec 2003 B2
6673453 Beavers et al. Jan 2004 B2
6713166 Yamamoto Mar 2004 B2
6723433 Bacon, Jr. Apr 2004 B2
6723773 Williams et al. Apr 2004 B2
6726969 Balaji et al. Apr 2004 B1
6726981 Steinbeck et al. Apr 2004 B1
6740465 Liang et al. May 2004 B2
6743523 Woo et al. Jun 2004 B1
6755350 Rochford et al. Jun 2004 B2
6759121 Alahapperuma et al. Jul 2004 B2
6761969 Li et al. Jul 2004 B2
6773804 Enlow et al. Aug 2004 B2
6786994 Williams et al. Sep 2004 B2
6790491 Sebastian et al. Sep 2004 B2
6790516 Niepelt Sep 2004 B2
6793859 Emslander et al. Sep 2004 B2
6793860 Xing et al. Sep 2004 B2
6794466 Zecha et al. Sep 2004 B2
6800341 Emslander et al. Oct 2004 B2
6808822 Rajan et al. Oct 2004 B2
6811857 Bravet et al. Nov 2004 B1
6821583 Shouldice et al. Nov 2004 B2
6830803 Vaidya et al. Dec 2004 B2
6841204 Nakamura et al. Jan 2005 B2
6846075 Ylitalo et al. Jan 2005 B2
6846524 Ozawa et al. Jan 2005 B2
6857737 Emslander et al. Feb 2005 B2
6866383 Naik et al. Mar 2005 B2
6866904 Nellis et al. Mar 2005 B2
6875487 Williams et al. Apr 2005 B1
6881458 Ludwig et al. Apr 2005 B2
6881704 Sakamoto et al. Apr 2005 B2
6896944 Ylitalo et al. May 2005 B2
6911239 King et al. Jun 2005 B2
6919113 Therrian et al. Jul 2005 B2
6953624 Bacon, Jr. Oct 2005 B2
6969483 Woo et al. Nov 2005 B1
6986919 Hladik et al. Jan 2006 B2
6989192 Huseman et al. Jan 2006 B2
6989418 Ko et al. Jan 2006 B2
6989715 Yin Jan 2006 B2
7014910 Rochford et al. Mar 2006 B2
7022385 Nasser Apr 2006 B1
7025453 Ylitalo et al. Apr 2006 B2
7045199 Yamamoto et al. May 2006 B2
7097298 Sondergeld et al. Aug 2006 B2
7147923 Roberts et al. Dec 2006 B2
7157133 Moran Jan 2007 B2
7166156 Parrinello et al. Jan 2007 B2
7166649 Day et al. Jan 2007 B2
7179521 Arthurs et al. Feb 2007 B2
7205029 Ohrbom et al. Apr 2007 B2
7223468 Yamamoto et al. May 2007 B2
7291372 Otsuki et al. Nov 2007 B2
7326462 Ishiguro et al. Feb 2008 B2
7332205 Hannington et al. Feb 2008 B2
7344618 Hannington et al. Mar 2008 B2
7358295 Miller et al. Apr 2008 B2
7371465 Peilingra et al. May 2008 B2
7384672 Chang et al. Jun 2008 B2
7402341 Halahmi Jul 2008 B2
7410692 Koda et al. Aug 2008 B2
7476705 Pajerski Jan 2009 B2
7534479 Utz May 2009 B2
7569272 Ohrul et al. Aug 2009 B2
7582698 Lubnin et al. Sep 2009 B2
7588812 Patel et al. Sep 2009 B1
7641947 Chen et al. Jan 2010 B2
7655296 Haas et al. Feb 2010 B2
7678959 Okada et al. Mar 2010 B2
7691784 Yuki et al. Apr 2010 B2
7691948 Takamatsu et al. Apr 2010 B2
7700188 Balaji et al. Apr 2010 B2
7799851 Hladik et al. Sep 2010 B2
7872069 Xia et al. Jan 2011 B2
7906218 Steichen et al. Mar 2011 B2
7910519 Majumdar et al. Mar 2011 B2
7935398 Park et al. May 2011 B2
7951457 Casteren Van et al. May 2011 B2
7968183 Takada et al. Jun 2011 B2
7972681 Roys et al. Jul 2011 B2
8002938 Elwakil et al. Aug 2011 B2
8003176 Ylitalo et al. Aug 2011 B2
8088847 Numrich et al. Jan 2012 B2
8114485 Schwendimann et al. Feb 2012 B1
8796351 Koch Aug 2014 B2
9240131 Onderisin et al. Jan 2016 B2
9636938 Owusu et al. May 2017 B2
20010051265 Williams et al. Dec 2001 A1
20020009576 Fu et al. Jan 2002 A1
20020011306 Mannington et al. Jan 2002 A1
20020039642 Inoue et al. Apr 2002 A1
20020098327 Ohta et al. Jul 2002 A1
20020146544 Kronzer Oct 2002 A1
20020164455 Nishikawa et al. Nov 2002 A1
20020177669 Jenny et al. Nov 2002 A1
20030031820 Nagamoto et al. Feb 2003 A1
20030049415 Pedginski et al. Mar 2003 A1
20030050379 Shih et al. Mar 2003 A1
20030060574 Muller et al. Mar 2003 A1
20030096087 Benanati et al. May 2003 A1
20030099827 Shih et al. May 2003 A1
20030121600 Loncar, Jr. et al. Jul 2003 A1
20030157276 Romano, Jr. Aug 2003 A1
20030170405 Parrinello et al. Sep 2003 A1
20030180541 Naik et al. Sep 2003 A1
20030207051 Kozumi Nov 2003 A1
20040001135 Soga Jan 2004 A1
20040048073 Bacon, Jr. Mar 2004 A1
20040058133 Bilodeau Mar 2004 A1
20040063826 Sobieski et al. Apr 2004 A1
20040076804 Kijima et al. Apr 2004 A1
20040091645 Heederik et al. May 2004 A1
20040105940 Parrinello et al. Jun 2004 A1
20040105971 Parrinello et al. Jun 2004 A1
20040105994 Lu et al. Jun 2004 A1
20040197572 Bell Oct 2004 A1
20040202840 Do et al. Oct 2004 A1
20040241352 Shih et al. Dec 2004 A1
20050003112 Chen Jan 2005 A1
20050008794 Graczyk et al. Jan 2005 A1
20050019508 Engel et al. Jan 2005 A1
20050048303 Henderson et al. Mar 2005 A1
20050074601 Onishi Apr 2005 A1
20050084788 Yau et al. Apr 2005 A1
20050100687 Dutton et al. May 2005 A1
20050136263 Roberts et al. Jun 2005 A1
20050147807 Haas et al. Jul 2005 A1
20050196607 Shih et al. Sep 2005 A1
20050234175 Ko et al. Oct 2005 A1
20050244657 Kawamura et al. Nov 2005 A1
20060001725 Nagata et al. Jan 2006 A1
20060014022 Kendig et al. Jan 2006 A1
20060019073 Kinley et al. Jan 2006 A1
20060160949 Styranec et al. Jul 2006 A1
20060204689 Tsukamoto et al. Sep 2006 A1
20060234075 Watanabe Oct 2006 A1
20060263564 Steyaert Nov 2006 A1
20060292317 Parrinello et al. Dec 2006 A1
20070048466 Huynh Mar 2007 A1
20070077421 Grefenstein et al. Apr 2007 A1
20070125490 Elwakil et al. Jun 2007 A1
20070136973 Patel et al. Jun 2007 A1
20070148444 Kamiya et al. Jun 2007 A1
20070172608 Tojo et al. Jul 2007 A1
20070172609 Williams Jul 2007 A1
20070172636 Smith et al. Jul 2007 A1
20070196647 Yokohama et al. Aug 2007 A1
20080026182 Abe et al. Jan 2008 A1
20080057251 Griswold et al. Mar 2008 A1
20080085385 Ylitalo et al. Apr 2008 A1
20080166507 Park et al. Jul 2008 A1
20080199704 Ho et al. Aug 2008 A1
20080280111 Blackwell et al. Nov 2008 A1
20080286576 McGuire, Jr. et al. Nov 2008 A1
20080302470 Sumita et al. Dec 2008 A1
20090017299 Shimbo et al. Jan 2009 A1
20090047449 Snow Feb 2009 A1
20090214837 Aibenice et al. Aug 2009 A1
20090233067 Doornheim et al. Sep 2009 A1
20090269568 Kuhlmann et al. Oct 2009 A1
20090286033 Taghavi et al. Nov 2009 A1
20090297820 Kovalchuk et al. Dec 2009 A1
20090317572 Abe et al. Dec 2009 A1
20100009108 Shih Jan 2010 A1
20100048077 Ko et al. Feb 2010 A1
20100051200 Mueller et al. Mar 2010 A1
20100058656 Chevalier et al. Mar 2010 A1
20100065212 Husemann et al. Mar 2010 A1
20100104872 Lu Apr 2010 A1
20100112263 Lorence et al. May 2010 A1
20100143615 Hsu Jun 2010 A1
20100215880 Chu Aug 2010 A1
20100243151 Stokes Sep 2010 A1
20110009561 Pajerski et al. Jan 2011 A1
20110012974 Niu Jan 2011 A1
20110027505 Majumdar et al. Feb 2011 A1
20110033698 Woods et al. Feb 2011 A1
20110033700 Caylus Feb 2011 A1
20110045290 Maeda et al. Feb 2011 A1
20110052843 Dontula et al. Mar 2011 A1
20110064900 Uesugi et al. Mar 2011 A1
20110064953 O'Rourke et al. Mar 2011 A1
20110064956 Casteren Van et al. Mar 2011 A1
20110077345 Erdem et al. Mar 2011 A1
20110104488 Mussig et al. May 2011 A1
20110111146 Williams May 2011 A1
20110117296 Jang et al. May 2011 A1
20110117299 Kung et al. May 2011 A1
20110152439 Wu et al. Jun 2011 A1
20110200830 Tennebroek et al. Aug 2011 A1
20110250368 Shih et al. Oct 2011 A1
20120000591 Mussig et al. Jan 2012 A1
20120088054 Shih et al. Apr 2012 A1
20140242316 Shih et al. Aug 2014 A1
20150184037 Owusu et al. Jul 2015 A1
20170203598 Owusu et al. Jul 2017 A1
Foreign Referenced Citations (165)
Number Date Country
1090032 Sep 2002 CN
1537142 Oct 2004 CN
1553853 Dec 2004 CN
100381530 Apr 2008 CN
101368073 Feb 2009 CN
100493670 Apr 2009 CN
100569884 Dec 2009 CN
101619200 Jan 2010 CN
100592110 Feb 2010 CN
101812277 Aug 2010 CN
101864258 Oct 2010 CN
101434819 Nov 2010 CN
101544725 Dec 2010 CN
101497680 Feb 2011 CN
102190988 Sep 2011 CN
102190990 Sep 2011 CN
102190992 Sep 2011 CN
102250566 Nov 2011 CN
102268233 Dec 2011 CN
101717468 Jan 2012 CN
101362815 Feb 2012 CN
102382605 Mar 2012 CN
101717612 May 2012 CN
101974299 Jul 2012 CN
102226068 Jul 2012 CN
102020956 Sep 2012 CN
102070741 Jan 2013 CN
102206476 Mar 2013 CN
102344522 Jul 2013 CN
101591511 Aug 2015 CN
102869501 May 2016 CN
4114085 Nov 1992 DE
102005029722 Dec 2006 DE
102005041134 Mar 2007 DE
102009005517 Jul 2010 DE
0355982 Feb 1990 EP
0359532 Mar 1990 EP
0275755 Nov 1990 EP
0538173 Apr 1993 EP
0547834 Jun 1993 EP
0696516 Feb 1996 EP
0899130 Mar 1999 EP
0929602 Jul 1999 EP
0976580 Feb 2000 EP
1026215 Aug 2000 EP
1125169 Aug 2001 EP
1180436 Feb 2002 EP
1260566 Nov 2002 EP
0997314 Dec 2002 EP
1135815 Jul 2003 EP
0963857 Feb 2004 EP
0933226 Mar 2004 EP
1520690 Apr 2005 EP
1059379 Feb 2006 EP
1705219 Sep 2006 EP
1364800 Mar 2007 EP
1767341 Mar 2007 EP
1777243 May 2011 EP
1114734 Jul 2011 EP
1908798 Aug 2013 EP
60-253544 Dec 1985 JP
4-285650 Oct 1992 JP
52-14181 Aug 1993 JP
7179831 Jul 1995 JP
08-99458 Apr 1996 JP
9-503168 Mar 1997 JP
10006654 Jan 1998 JP
10-110032 Apr 1998 JP
10235815 Sep 1998 JP
10-264500 Oct 1998 JP
10305533 Nov 1998 JP
10305534 Nov 1998 JP
11198555 Jul 1999 JP
11202536 Jul 1999 JP
11315257 Nov 1999 JP
2000-071607 Mar 2000 JP
2000168018 Jun 2000 JP
2000-185459 Jul 2000 JP
2000-309160 Nov 2000 JP
2000-326622 Nov 2000 JP
2000-336327 Dec 2000 JP
2001-071631 Mar 2001 JP
2002-322359 Nov 2002 JP
2003-002923 Jan 2003 JP
2003-096140 Apr 2003 JP
2003-154612 May 2003 JP
2003-154748 May 2003 JP
2003-220670 Aug 2003 JP
2003-231226 Aug 2003 JP
2003-276133 Sep 2003 JP
2004-010661 Jan 2004 JP
2004-010662 Jan 2004 JP
2004-083787 Mar 2004 JP
2004-090380 Mar 2004 JP
2004-223811 Aug 2004 JP
2004-331899 Nov 2004 JP
2005-070686 Mar 2005 JP
2005-131930 May 2005 JP
2005-132032 May 2005 JP
2005-238694 Sep 2005 JP
2006-021354 Jan 2006 JP
2006-052298 Feb 2006 JP
2006-088349 Apr 2006 JP
2006-150653 Jun 2006 JP
2006-274220 Oct 2006 JP
2006-346885 Dec 2006 JP
2007-037900 Feb 2007 JP
2007-038677 Feb 2007 JP
2007-050620 Mar 2007 JP
2007-111867 May 2007 JP
2007-118584 May 2007 JP
2007-160746 Jun 2007 JP
2007-237438 Sep 2007 JP
2007-296827 Nov 2007 JP
2007-297569 Nov 2007 JP
2008-012716 Jan 2008 JP
2008-062611 Mar 2008 JP
2008-073871 Apr 2008 JP
2008087173 Apr 2008 JP
2008-105356 May 2008 JP
2008-221689 Sep 2008 JP
2008-238481 Oct 2008 JP
2009-120663 Jun 2009 JP
2009-172888 Aug 2009 JP
2010-069687 Apr 2010 JP
2010-076183 Apr 2010 JP
2010-094813 Apr 2010 JP
2010-094974 Apr 2010 JP
2010-229291 Oct 2010 JP
2010-253704 Nov 2010 JP
2010-253759 Nov 2010 JP
2010-253892 Nov 2010 JP
2010-269583 Dec 2010 JP
2011-021134 Feb 2011 JP
2011-032355 Feb 2011 JP
2011-051303 Mar 2011 JP
9214768 Sep 1992 WO
9504655 Feb 1995 WO
9804418 Feb 1998 WO
9928791 Jun 1999 WO
0013887 Mar 2000 WO
0013888 May 2001 WO
0231016 Apr 2002 WO
0236353 May 2002 WO
0248260 Jun 2002 WO
02062894 Aug 2002 WO
03016045 Feb 2003 WO
03037614 May 2003 WO
03080356 Oct 2003 WO
2003093357 Nov 2003 WO
2004003060 Jan 2004 WO
2004003093 Jan 2004 WO
2004060641 Jul 2004 WO
2004060686 Jul 2004 WO
2004060687 Jul 2004 WO
2005068195 Jul 2005 WO
2010005452 Jan 2010 WO
2010062438 Jun 2010 WO
2010091346 Aug 2010 WO
2010129299 Nov 2010 WO
2011037732 Mar 2011 WO
2011109692 Sep 2011 WO
2011146188 Nov 2011 WO
2011091132 Dec 2011 WO
2013033067 Mar 2013 WO
Non-Patent Literature Citations (29)
Entry
Griffin, G.J.L, “Biodegradation of ethylene/vinylacetate copolymers,” Proceedings of 3rd International Biodegradation Symposium, pp. 807-813, 1975.
Derwent Abstract for JP H10-110032 dated Apr. 28, 1998.
International Search Report and Written Opinion dated Oct. 24, 2012 issued in corresponding international Application No. PCT/US2012/052616.
International Preliminary Report on Patentability dated Mar. 13, 2014 issued in corresponding International Application No. PCT/US2012/052616.
Invitation to Pay Additional Fees and Partial international Search Report issued in PCT/US08/069706 dated Oct. 30, 2008.
SAE Technical Standard J1960 (Rev. Oct. 2004).
Griffin, G.J.L, “Biodegradation of ethylene/vinylacetate copolymers,” Proceedings of 3rd international Blodegredation Symposium, pp. 807-813, 1975.
International Search Report and the Written Opinion of the International Searching Authority issued in PCT/US08/069706 dated Feb. 19, 2009.
Invitation to Pay Additional Fees and Partial International Search Report issued in PCT/US2008/084812 dated Mar. 20, 2009.
International Search Report and Written Opinion issued in corresponding PCT/US2008/084812 dated May 19, 2009.
International Search Report and Written Opinion dated Jul. 21, 2011 issued in corresponding International Application No. PCT/US2011/027154 filed Mar. 4, 2011.
International Preliminary Report on Patentability dated Nov. 4, 2012 issued in corresponding International Application No. PCT/US2011/027154 filed Mar. 4, 2011.
“Evaluation of the Residual Stability of Polyurethane Automotive Coatings by DSC,” P. Simon et al., Journal of Thermal Analysis an Calorimety, vol. 84 (2006) 3, 679-692.
International Search Report dated Apr. 16, 2015 issued in corresponding International Application No. PCT/US2014/070259.
Written Opinion dated Apr. 16, 2015 issued in corresponding International Application No. PCT/US2014/070259.
International Preliminary Report on Patentability dated Jul. 14, 2016 issued in corresponding International Application No. PCT/US2014/070259.
International Search Report and Written Opinion dated Apr. 17, 2013 issued in corresponding International Application No. PCT/US2013/021 205 filed Jan. 11, 2013.
International Preliminary Report on Patentability dated Jul. 24, 2014 issued in corresponding International Application No. PCT/US2013/021205 filed Jan. 11, 2013.
“ASTM D1238 Standard Test Method for Melt Flow Rates of Thermoplastics by Extrusion Plastometer,” ASTM D1238, Jan. 1, 2013, pp. 284-299, XP009195312.
National Application 3688-2006 (ROEHM GMBH) Dec. 22, 2006 as cited in an Office Action dated Apr. 20, 2018 for Chilean App. No. 201601603.
Press release “Air Products Introduces Hybrid Waterborne Resins at ICE,” published on Nov. 14, 2003, downloaded from https://coatings.specialchem.com.
Notice of Opposition filed by Eun-Suk Choi in corresponding EP2542409, dated Sep. 24, 2019, 29 pages.
“Hybridur(R) 870 and 878 Polymer Binders are New Cost-Effective Waterborne Resin Technologies with Chemical Resistance of a PUT—and are NMP-free,” Press Release from Air Products and Chemicals, Inc., Nov. 12, 2003, 1 page.
“JONCRYL(R) 617, an acrylic polymer emulsion for use i water-based inks and oerprint varnishes,” BASF Resins BV, Jan. 1, 2007, 4 pages.
“Hybridur(R) 870 Polymer Dispersion,” Evonik Corporation, Jun. 2017, 6 pages.
Standard Test Method for Tensile Properties of Thin Plastic Sheeting, D882-10, Aug. 6, 2020, 10 pages.
“Industrial Coatings, raw material selection guide,” BASF Corporation, 2014, 56 pages.
“Printing and Packaging, resins, performance and formulation additives selection guide for packaging solutions,” BASF Corporation, 2017, 36 pages.
“Benefits, built on eachother—The BASF resins and additives portfolio for printing and packaging,” BASF SE, date unknown, 32 pages.
Related Publications (1)
Number Date Country
20150184038 A1 Jul 2015 US
Provisional Applications (1)
Number Date Country
61921600 Dec 2013 US