Patent Application
20230365740
Polyurethanes (PU) were discovered in 1937 by Otta Bayer and his co-workers at I.G. Farbenindustrie in Leverkusen, Germany. Since then numerous commodity PU materials including elastomers, flexible/rigid foams, films, coatings, fibers, and thermoplastics, were developed by controlling the PU chemical structures displaying chain flexibility, crystallinity, interchain interaction, and crosslinking density (Hepburn, C., Polyurethane Elastomers. 2 ed.; Elsevier Science Publishers LTD: New York, NY, USA, 1992). In 2017, approximately 5.8 billion pounds of PU materials were consumed in various end-use markets such as building and construction, furniture, and bedding with an economic output reaching $296.8 billion in the US (The Economic Benefits of the U.S. Polyurethanes Industry 2017; American Chemistry Council: Arlington VA, USA, October 2018).
One growing interest in green chemistry is focused on the utilization of low-cost technical lignins in commodity polymeric materials including PU (Wang, Y.-Y., et al., Polymers 2020, 12, 2277). Lignin has been viewed as the most abundant biogenic aromatic polymer possessing various functional groups such as hydroxyl, methoxy, carboxyl, and carbonyl groups. A representative structural model of native lignin is constituted of three subunits including p-hydroxyphenyl (H), guaiacyl (G), and syringyl (S), and these phenylpropane units are mainly connected via β-O-4′, β-5′, β-β′, 5-5′, and 4-O-5′ interunit linkages (Ralph, J., et al., Phytochem. Rev. 2004, 3, (1), 29-60; and Giummarella, N., et al., Green Chem. 2019, 21, (7), 1573-1595).
Currently, ˜1.1 million tons of commercial lignin is produced annually in four major industrial processes: sulfite, Kraft, soda and organosolv (Upton, B. M., et al., Chem. Rev. 2016, 116, (4), 2275-2306). These technical lignins could be supplied as sustainable replacements for petrochemical polyols in the production of commodity PU materials (Upton, B. M., et al., Chem. Rev. 2016, 116, (4), 2275-2306; Glasser, W. G., About Making Lignin Great Again—Some Lessons From the Past. Front. Chem. 2019, 7, 565; Wang, Y.-Y., et al., Tappi J. 2017, 16, (4), 203-207; and Alinejad, M., et al., Polymers 2019, 11, (7), 1202).
The chemicals used in isolating technical lignins can leave undesirable impurities in the final lignin-based polymers, meanwhile, the heterogeneity of native lignin structure could be detrimentally increased during the pulping or pretreatment process. These factors can potentially limit the amount of lignin that could be incorporated into a polymeric system due to deteriorating material properties as lignin incorporation increases. Therefore, refining technical lignins has been widely investigated to remove impurities and isolate specific lignin cuts with distinct molecular weights, to narrow molecular weight dispersity (D), and more importantly, to enhance solubility in common organic solvents (Duval, A., et al., Holzforschung 2016, 70, (1), 11-20; Sadeghifar, H., et al., ACS Sustainable Chem. Eng. 2017, 5, (1), 580-587; Wang, Y.-Y., et al., ACS Sustainable Chem. Eng. 2018, 6, (5), 6064-6072; Meng, X., et al., Bioresour. Technol. 2019, 272, 202-208; and Jiang, X., et al., ACS Sustainable Chem. Eng. 2017, 5, (1), 835-842). The implementation of lignin refining would support the ideal fabrication of polymer networks with tailored lignin structures. Gioia et al. demonstrated that the material properties of lignin-based epoxies can be improved vastly by increasing the molecular weight of lignin (Gioia, C., et al., J. Am. Chem. Soc. 2018, 140, (11), 4054-4061). Similar trends were observed in our previous study of lignin-based polyurethanes (Wang, Y.-Y., et al., ACS Appl. Polym. Mater. 2019, 1, (7), 1672-1679). Yet, undesirable dispersion and compatibility refrained the utilization of high-molecular-weight lignin cuts in the material matrix.
Recently, lignin-based epoxies showing tensile strength up to 66 MPa were synthesized from low-molecular-weight (
Novel organosols or co-solvent pretreatments developed for lignocellulosic biorefining enables lignin extraction using biomass-derived organic solvents under acidic conditions at elevated temperatures (Meng, X., et al., Green Chem. 2020, 22, (9), 2862-2872; Shuai, L., et al., Green Chem. 2016, 18, (4), 937-943; Cai, C. M., et al., Green Chem. 2013, 15, (11), 3140-3145; and Li, S.-X. , et al., Bioresour. Technol. 2017, 243, 1105-1111). The Co-solvent Enhanced Lignocellulosic Fractionation (CELF) process employing miscible solutions of tetrahydrofuran (THF) and water with dilute acid can produce technical lignins featuring high lignin yield from biomass and purity. In the previous study, we have demonstrated that CELF lignin's molecular weight, backbone structure, functional groups, and solubility in common organic solvents can be tuned by changing the pretreatment reaction conditions (Wang, Y.-Y. , et al., Front. Energy Res. 2020, 8, (149)).
Certain embodiments of the invention provide a method for the production of biogenic polyurethane coating and adhesives as described herein.
In one embodiment, the invention provides a method comprising, co-polymerizing:
In one embodiment, the invention provides a polyurethane prepared according to a method of the invention.
In one embodiment, the invention provides a polyurethane comprising lignin that is co-polymerized with a monomeric polyol and an isocyanate
The structural complexity and robust intermolecular interactions have challenged the incorporation of technical lignin into value-added polymeric materials for decades. To study the correlation between lignin molecular structure and material properties of lignin-based polyurethanes, we applied Co-solvent Enhanced Lignocellulosic Fractionation (CELF) pretreatment followed by sequential precipitation to produce three distinct lignin preparations with narrowly distributed (<2) and comparatively low molecular weight (<1500 g/mol) from poplar biomass. Structural characterization indicated that these lignin preparations differed in average molecular chain length and stiffness as well as hydroxyl group distribution. Secondary hydroxyl group providers such as aliphatic diols and polyethers were incorporated as building-blocks into the lignin-based polyurethanes to provide additional hydrogen capacity to improve the dispersion of lignin in the PU network. The selected aliphatic diols and polyethers interacted with lignin molecules at different levels of strength depending on their molecular structure, and their impacts were ultimately reflected in the mechanical and thermal properties of the resulting lignin-based polyurethanes. The copolymerization of technical lignin with tailored structure and secondary hydroxyl providers could provide new strategies in formulating lignin-based/containing polyurethanes for various functional applications.
The mechanical performance of CELF-based PUs was determined by the solubility of CELF lignin streams in a casting solvent such as THF. The CELF lignin stream extracted at 160° C. (CL160) was refined by a novel sequential precipitation step employing THF-methanol co-solvent to solubilize the lignin while adding hexane as an antisolvent to promote precipitation. CELF lignin-based PUs (CL-PU) were fabricated from two lignin fractional cuts produced from 160° C. and one CELF lignin stream produced at 180° C. pretreatment temperature. These CELF lignin preparations were readily soluble in THF at room temperature, and differences in their chemical composition, backbone structure, and functional group distribution could potentially affect the mechanical performance of final CL-PUs. Monomeric diols and polyethers were employed as the secondary hydroxyl provider in the synthesis of CL-PUs. Besides serving as a building block and providing additional hydrogen bonding capacity that improves the dispersion of CELF lignin in the PU matrix, tailoring the chemical structure of secondary hydroxyl provider and their molecular interactions with lignin could be applied as a new strategic tool in the development of highly functional lignin-based PUs for commercial applications.
Certain embodiments of the invention provide a method for production of biogenic polyurethane coating and adhesives, comprising: mixing biomass lignin, monomeric polyols, and volatile organic solvent at a temperature ranging from about 20 to about 65° C. to synthesize polyurethanes containing from about 20 to about 60% lignin and from about 10 to about 80% monomeric polyols.
In certain embodiments, the monomeric polyols are selected from the group consisting of 1,3-propanediol, propylene glycol, 1,4-butanediol, 1,3-butanediol, cis-butene-1,4-diol, trans-butene-1,4-diol, 3-hexene-1,6-diol, and glycerol.
In certain embodiments, the biomass lignin is defined as lignin extracted from lignocellulosic biomass using organosolv pretreatment or pulping, ionic liquid pretreatment or pulping, deep eutectic salts pretreatment or pulping, reductive catalytic fractionation extraction of lignin
In certain embodiments, the lignocellulosic biomass is defined as a material containing one or more of corn stover, wheat straw, palm fronds, municipal green waste, forestry residues, agricultural residues, hardwoods, softwoods, miscanthus, sugarcane bagasse, oat hulls, switchgrass, bamboo stalk, hemp stalk, hemp hurd, or hemp bast fiber.
In certain embodiments, the organosolv pretreatment or pulping is defined as a process that solubilizes and removes lignin from lignocellulosic biomass by treating it under conditions and environment comprising an aqueous co-solvent mixture comprising of methanol, ethanol, tetrahydrofuran, or gamma-valerolactone.
In certain embodiments, the chemically unmodified technical lignins can be directly converted into polyurethane as the primary polyols in the presence of aliphatic diols as the secondary polyols. In certain embodiments the synthesis of lignin-PU starts with fully dissolving a technical lignin in the presence of a diol or a mixture of diols in volatile organic solvents. In certain embodiments, the polyol solution was mixed with isocyanate compounds and catalyst to form PU by solvent casting. In certain embodiments, the dried PU materials were cured at 150° C.
Due to the inherent strong intermolecular forces between lignin macromolecules, miscibility and dispersion of technical lignin is an obstacle for producing high performance lignin-PU. As described herein, diols were introduced to realize faster and complete dissolution of technical lignin in volatile organic solvents, which improve lignin miscibility with other components and its dispersion in the PU materials. The diols were incorporated into the PU materials as chain extenders or crosslinkers to enhance the material performance.
The term “organosolv lignin” includes lignins that have been isolated by co-solvent extraction from biomass. In one embodiment, the organosolv lignin has an average molecular weight of less than about 1500 g/mole. In one embodiment, the organosolv lignin has an average molecular weight of less than about 1200 g/mole. In one embodiment, the organosolv lignin has an average molecular weight of less than about 1000 g/mole. In one embodiment, the organosolv lignin has an average molecular weight of less than about 800 g/mole. In one embodiment, the organosolv lignin has an average molecular weight of greater than about 500 g/mole. In one embodiment, the organosolv lignin has an average molecular weight of greater than about 800 g/mole. In one embodiment, the organosolv lignin can be prepared by co-solvent extraction from biomass with a solvent comprising water and acetone, ethanol, methanol, tetrahydrofuran, or gamma-valerolactone. In one embodiment, the organosolv lignin has a phenolic OH content to 50-70%. In one embodiment, the organosolv lignin has an aliphatic OH content to below 55%.
The term “monomeric polyol” includes any monomeric polyol that can be co-polymerized with lignin to provide a polyurethane according to a method of the invention. In one embodiment, the monomeric polyol is selected from the group consisting of 1,3-propanediol, propylene glycol, 1,4-butanediol, 1,3-butanediol, cis-butene-1,4-diol, trans-butene-1,4-diol, 3-hexene-1,6-diol, and glycerol. In one embodiment, the monomeric polyol comprises cis-butene-1,4-diol.
The term “isocyanate” includes any isocyanate that can be incorporated into a polyurethanes according to a method of the invention. In one embodiment, the isocyanate is a diisocyanate or a polyisocyanate. In one embodiment, the isocyanate comprises poly[(phenyl isocyanate)-co-formaldehyde or Methylene diphenyl diisocyanate. In one embodiment, the poly[(phenyl isocyanate)-co-formaldehyde has an NCO/OH ratio of about 1:1.
In one embodiment, the co-polymerizing is carried out in a solvent that comprises a volatile-organic-solvent. In one embodiment, the volatile-organic-solvent is selected from the group consisting of tetrahydrofuran, methanol, n-hexane, and toluene. In one embodiment, the solvent comprises tetrahydrofuran.
In one embodiment, the co-polymerizing is carried out in the presence of a catalyst. In one embodiment, the co-polymerizing is carried out in the presence of dibutyltin dilaurate catalyst. In one embodiment, the dibutyltin dilaurate catalyst is present at 1.5% by weight of the total mixture.
In one embodiment, the co-polymerizing is carried out at a temperature below about 65° C. In one embodiment, the co-polymerizing is carried out at a temperature ranging from 20-65° C.
In one embodiment, the polyurethane of the invention comprises at least about 20% lignin. In one embodiment, the polyurethane comprises at least about 30% lignin. In one embodiment, the polyurethane comprises at least about 40% lignin. In one embodiment, the polyurethane comprises at least about 50% lignin. In one embodiment, the polyurethane comprises less than about 60% lignin. In one embodiment, the polyurethane comprises less than about 50% lignin. In one embodiment, the polyurethane comprises 20-65% lignin. In one embodiment, the polyurethane comprises 20-60% lignin.
In one embodiment, the polyurethane comprises at least about 2% monomeric polyol. In one embodiment, the polyurethane comprises at least about 5% monomeric polyol. In one embodiment, the polyurethane comprises at least about 10% monomeric polyol. In one embodiment, the polyurethane comprises at least about 20% monomeric polyol. In one embodiment, the polyurethane comprises at least about 30% monomeric polyol. In one embodiment, the polyurethane comprises at least about 40% monomeric polyol. In one embodiment, the polyurethane comprises at least about 50% monomeric polyol. In one embodiment, the polyurethane comprises at least about 60% monomeric polyol. In one embodiment, the polyurethane comprises at least about 70% monomeric polyol. In one embodiment, the polyurethane comprises 10-80% monomeric polyol.
Co-polymerizing organosolv lignin with a monomeric polyol provides a polyurethane that is cross-linked with the monomeric polyol, yielding soft-segments within the polyurethane and producing polyurethanes with unique and beneficial properties. In one embodiment, the polyurethane has an ultimate tensile stress (σmax) of at least about 50 MPa. In one embodiment, the polyurethane has an elongation at break (εb) of at least about 4%. In one embodiment, the polyurethane has an elongation at break (εb) of at least about 5%. In one embodiment, the polyurethane has an elongation at break (εb) of at least about 6%. In one embodiment, the polyurethane has an elongation at break (εb) of at least about 7%. In one embodiment, the polyurethane has an elongation at break (εb) of at least about 8%. In one embodiment, the polyurethane has a glass transition temperatures (Tg) between about 100° C. and about 180° C. In one embodiment, the polyurethane has a glass transition temperatures (Tg) between about 100° C. and about 160° C. In one embodiment, the polyurethane has a glass transition temperatures 30 (Tg) between about 100° C. and about 130° C.
Certain embodiments of the invention will be illustrated in the following non-limiting Examples.
The poplar biomass was sourced from Oak Ridge National Laboratories (ORNL) known as BESC (BioEnergy Science Center) Standard Poplar. This poplar has been used in numerous previous studies supporting CELF pretreatment research (Thomas, V. A. , et al., Biotechnol. Biofuels 2017, 10, (1), 252; Mostofian, B., et al., J. Am. Chem. Soc. 2016, 138, (34), 10869-10878; and Patri, A. S., et al., Biotechnol. Biofuels 2019, 12, (1), 177). The poplar wood chips were first knife-milled by a Thomas-Wiley laboratory mill (model 4) through a 2 mm particle screen before pretreatment. Tetrahydrofuran, methanol, hexane, cis-2-butene-1,4-diol (cBED), 1,4-butanediol (BD), 1,8-octanediol (OD), polyethylene glycol (MW˜400, PEG400), polyethylene glycol (MW˜4000, PEG4k), poly[(phenyl isocyanate)-co-formaldehyde] (average Mn ˜340, ˜2.7 isocyanate groups/molecule, PMDI), dibutyltin dilaurate (DTDL) were purchased from Sigma-Aldrich. All chemicals were used as received.
The preparation of CELF lignin was described in a previous literature (Wang, Y.-Y. , et al., Front. Energy Res. 2020, 8, (149)). n brief, the milled poplar biomass (7.5 wt % solids loading) was treated in THF/water (1:1 w/w) solution containing 0.5 wt % sulfuric acid in a 1 L Hastelloy Parr autoclave reactor (Parr Instruments Co., Moline, IL). The CELF pretreatment was performed at the target temperature for 15 minutes, deemed optimal for lignin extraction without extensive loss of sugars (Thomas, V. A. , et al., Biotechnol. Biofuels 2017, 10, (1), 252). After the reaction, the liquid fraction was collected, and then neutralized by ammonium hydroxide. The remaining THF was removed by open-air boiling at 70° C. in a vapor hood, and the precipitated CELF lignin was collected by filtration, washed extensively with DI water, and air dried at 65° C. in an oven. The resulting CELF lignin powder samples were designated as CL160 and CL180 based upon their corresponding pretreatment temperature (160° C. and 180° C.).
CL160 was fractionated by sequential precipitation from THF-methanol (1:1, v/v) cosolvent using hexane as an antisolvent.12 In this work, 50 g of CL160 was dissolved in 500 mL THF-methanol cosolvent a room temperature. The high-molecular-weight CL160 cut precipitated out from the cosolvent after adding 150 mL hexane. The resulting supernatant was mixed with additional 350 mL hexane to generate the medium-molecular-weight CL160 cut (MCL) that accounts for 23.1% of the parent CL160. The low-molecular weight CL160 cut (LCL, 22.2% of the parent CL160) in the liquid phase was collected by removing the solvents by rotary evaporation. The dry solid CL160 cuts were incubated in the oven at 40° C. for 48 hours before characterization and PU synthesis.
The polycondensation reaction between polyols and PMDI was catalyzed by 1.5% DTDL in THF.25 The CELF lignin samples (MCL, LCL, and CL180) and the selected hydroxyl providers such as cBED, BD, OD, PEG400, and PEG4k were employed for fabricating CL-PUs according to the formulations listed in Table 1. The CL-PU samples for tensile testing and dynamic mechanical analysis (DMA) were produced via solution casting from THF in a manner that has been reported previously (Wang, Y.-Y., et al., ACS Appl. Polym. Mater. 2019, 1, (7), 1672-1679).
aThe subscript number expressed the percentage of total polyol and diol applied in the corresponding CL-PU.
The molecular weights of MCL, LCL, and CL180 employed in the CL-PUs preparation were determined by GPC analysis. In this work, ˜1 mg of lignin was dissolved in THF without acetylation and incubated overnight before subjecting to an Agilent GPC SECurity 1200 system equipped with several Waters Styragel columns (Water Corporation, Milford, MA) at a flow rate of 0.3 mL/min at 35° C. The 2D HSQC and 31P NMR spectra were acquired on a Bruker Avance III H 500-MHz spectrometer (Wang, Y.-Y. , et al., Front. Energy Res. 2020, 8, (149)). The 31P NMR analysis of the hydroxyl groups of CELF lignin were performed based on a protocol published previously (Meng, X., et al., Nat. Protoc. 2019, 14, (9), 2627-2647).
The experimental procedures and conditions of tensile testing and DMA of CL-PUs were described in detail in the previous publications (Wang, Y.-Y., et al., ACS Appl. Polym. Mater. 2019, 1, (7), 1672-1679). The error analysis for tensile testing was obtained based on the standard deviation of triplicates. The CL-PU samples were ball-milled to fine powder before subjecting to thermal gravimetric analysis (TGA) that was performed on a TA Q50 thermogravimetric analyzer (TA Instruments) at a heating rate of 20° C./min from 105 to 900° C. in an N2. The samples were preheated to 105° C. and incubated at this temperature for 10 minutes to remove traces of moisture and solvents.
The range of reaction temperatures selected for CELF pretreatment of poplar in this study have been reported to have significant impacts on the molecular structure of the co-product lignin (Wang, Y.-Y. , et al., Front. Energy Res. 2020, 8, (149); and Meng, X., et al., ACS Sustainable Chem. Eng. 2018, 6, (7), 8711-8718). The solvation behavior in THF of CELF lignin depends on the molecular weight and distribution of hydroxyl groups which can be correlated to the pretreatment temperature (Wang, Y.-Y. , et al., Front. Energy Res. 2020, 8, (149)). CL160 was partially soluble in THF and was fractionated via sequential precipitation to produce MCL (medium MW) and LCL (low MW), and CL180 (unrefined) which were readily soluble in THF at the experimental concentration can be subjected to the PU synthesis without any modification. In general, MCL, LCL, and CL180 possess narrow molecular weight distribution and Mw below 1500 g/mol (Table 2).
), hydroxyl (OH)
w, g/mol
aContent expressed as the percentage of the total —OH.
However, their physical forms, as well as molecular structure and distribution of hydroxyl groups, are quite different. The HSQC spectrum of MCL shows the typical cross-peaks of substructures (β-O-4′ ether, β-β′ resinol and β-5′ phenylcoumaran) and subunits (p-hydroxybenzoate, guaiacyl, syringyl, and their condensed and oxidized derivatives) which were observed for CELF lignin extracted from poplar biomass. MCL represents a relatively flexible molecular structure with the highest frequencies in both β-O-4′ interunit linkage and aliphatic —OH groups among the three CELF lignin samples. LCL is composed of oligomers of 3˜4 phenylpropane C9 units with high S/G=3.9 and approximately equal amounts of β-O-4′ ether and β-β′ resinol substructures. Besides the lignin cross-peaks, the HSQC spectrum of LCL contains a substantial amount of non-lignin structures in the aliphatic region. These non-lignin components including traces of 5-hydroxymethylfurfural were concentrated down in LCL via sequential precipitation, and they might contribute to the flow behavior of LCL at elevated temperatures (>40° C.). Unrefined CL180 is a darker brown powder and forms a dark liquid solution when dissolved in THF. It was confirmed when CELF pretreatment temperature increased to 180° C., lignin underwent complex acid-catalyzed depolymerization by cleavage of aryl-ether linkages and repolymerization, and consequently, its molecular structure became more rigid and highly condensed (Wang, Y.-Y. , et al., Front. Energy Res. 2020, 8, (149)).
One challenge that impedes the application of technical lignins in commercial polymer products is their poor solubility in organic solvents. In this work, MCL, LCL, and CL180 can all fully dissolve in THF at high concentration, and no precipitation was observed during PU formation when up to 63% of the CELF lignins were incorporated into the CL-PU (Table 1). In MCL100 and LCL100, lignin served as the only —OH provider in the resulting CL-PUs. Although their Young's moduli (E) were close and around 0.9 GPa (
CL180100 produced from CL180 as the only hydroxyl provider demonstrated promising mechanical properties considering the molecular weight and total OH content of CL180 were close to MCL (
CL180 extracted at 180° C. with aqueous THF and two CL160 cuts, MCL and LCL, produced by sequential precipitation from THF-methanol-hexane co-solvent system were converted into CL-PUs with aliphatic diols and polyethers as the secondary hydroxyl provider. These low-molecular-weight CELF lignin samples exhibited distinct molecular structures including backbone composition and hydroxyl group distribution. MCL contains a moderate amount of flexible aryl ether interunit linkages along with other typical substructure and subunits commonly found in poplar lignin. LCL showing thermal flow behavior is a mixture of oligomers, in which the C—C bonded substructures constitute >50% of the predominate lignin interunit linkages. For MCL-PUs, the mechanical properties were vastly improved by the addition of monomeric diols or polyethers. LCL by itself can form PUs with σmax exceeding 50 MPa and Tg around 130° C.
CL180 obtained directly via CELF process possessed high frequencies of phenolic -OH functional groups and the most rigid molecular structure among the three CELF lignin samples. The unsaturated aliphatic diol, cBED, exhibited biphasic behavior with CELF lignin, and thus toughened the resulting CL-PUs. Polyether, PEG that can form robust hydrogen bonds with lignin were ineffective in softening the CL-PU network. The strategic combination of cBED and PEG demonstrated enhancement in both toughness and ductility without scarifying the incorporation level of lignin in the CL-PU. Therefore, understanding the molecular interactions within the polymer system and deploying them in designing lignin-based/containing materials could benefit the cost-effective utilization of technical lignin in value-added products.
Representative polyurethanes were prepared using the following method, which illustrates a method of the invention.
Organosolv lignin samples were dissolved in THF with monomeric polyols. The mixture was incubated in a thermal shaker (Alkali Scientific Inc.) at 140 rpm, 60° C. for 1 hour, and then it was combined with a THF solution containing poly[(phenyl isocyanate)-co-formaldehyde] (PMDI, Mn˜340) with NCO/OH ratio at 1:1 and 1.5% dibutyltin dilaurate (DTDL). After 3-day curing at room temperature, the CL-PU samples were kept at 150° C. for 3 hours.
All publications, patents, and patent documents (including Yun-Yan Wang, et al., “Polyurethanes Based on Unmodified and Refined Technical Lignins: Correlation between Molecular Structure and Material Properties”, Biomacromolecules 2021 22 (5), 2129-2136) are incorporated by reference herein, as though individually incorporated by reference. The invention has been described with reference to various specific and preferred embodiments and techniques. However, it should be understood that many variations and modifications may be made while remaining within the spirit and scope of the invention.
This application claims priority to U.S. Provisional Application No. 63/335,166, filed on Apr. 26, 2022. The entire content of this application is hereby incorporated by reference herein.
This invention was made with government support under 2016-10008-25321 awarded by National Institute of Food and Agriculture, USDA. The government has certain rights in the invention.
| Number | Date | Country | |
|---|---|---|---|
| 63335166 | Apr 2022 | US |