Patent Application
20050008567
The present invention belongs to the field of porous crystalline materials and particularly to zeolitic materials. More particularly, the invention fits in the sector of zeolitic materials useful as catalysts or components of catalysts in processes of conversion of feedstock formed by organic compounds, such as catalytic cracking processes of hydrocarbons, catalytic hydrocracking of hydrocarbons, alkylation of aromatic olefins and in esterification processes, alkylation of aromatics with olefins and in esterification processes, acylation, reaction of aniline with formaldehyde in its acid form and/or exchanged with suitable cations.
Zeolites are porous crystalline aluminosilicates that have found important uses such as catalysts, adsorbing agents and ionic exchangers. Many of these zeolitic materials have well defined structures that form channels and cavities inside of a uniform size and shape that permit adsorption of certain molecules, whereas they prevent from passing inside the crystal other molecules that are too big from spreading through the pores. This characteristic gives these materials properties of molecular sieve. These molecular sieves can include Si and other elements of the group IIIA of the periodic table in the lattice, all of them tetrahedrally coordinated. The tetrahedron are bonded by their vertexes by oxygen atoms forming a three-dimensional lattice. The negative charge generated by the elements of the IIIA group tetrahedrally coordinated in lattice positions is compensated by the presence of cations, such as for example, alkaline or alkaline earth cations, in the crystal. A type of cation may be totally or partially exchanged by another type of cation by means of ionic exchange techniques, being thus possible to vary the properties of a given silicate by selecting the desired cations.
Many zeolites have been synthesized in the presence of an organic molecule that acts as a structure directing agent (SDA). The organic molecules that act as structure directing agents (SDA) generally contain nitrogen in their composition and can give rise to organic cations stable in the reaction medium.
The mobilization of silica can be carried out in the presence of OH− groups and a basic medium, that can be introduced as a hydroxide of the SDA itself, such as for example, tetrapropylammonium hydroxide in the case of zeolite ZSM-5. The fluoride ions can also act as mobilizing agents of silica in the synthesis of zeolites, such as is described, for example, in patent application EP-A-337479 in accordance with which HF is used in H2O at a low pH as a mobilizing agent of the silica for the synthesis of ZSM-5. However, the use of fluoride ions in the synthesis is less desired from an industrial point of view than the use of OH'1, given that the presence of fluoride ions requires the use of special materials in the synthesis equipment, as well as a specific treatment with waste waters and gases.
The present invention refers to a microporous crystalline material (hereinafter also called ITQ-21) and the process for obtaining the same in a basic medium, in the absence of added fluoride. This new material has, in the calcined form as well as in the uncalcined synthesized form, an X-ray diffraction pattern that is different from that of other known zeolitic materials. The most important diffraction lines of the material for its calcined are shown in Table 1.
(a)±0.2
The crystalline material of this invention named ITQ-21 has a molar composition in its calcined and anhydrous state represented by the equation:
x X2O3:y YO2z ZO2
wherein
From the values given, it is clearly inferred that the crystalline material ITQ-21 can be synthesized in the absence of added trivalent elements.
In turn, the most important diffraction lines for the uncalcined form of the material are the ones given in table 2.
(a)±0.2
These diffractograms were obtained with a Philips X'Pert diffractometer equipped with a graphite monochromator and an automatic divergence slot using Kα radiation of copper. The diffraction data were registered by a passing of 2θ of 0.01° wherein θ is the Bragg angle and a count time of 10 seconds per passing. The relative intensity of the lines is calculated as the percentage regarding the most intense peak, and a percentage of 80-100 is considered very strong (vs). a percentage of 60-80 is considered strong (s), a percentage of 40-60 is considered medium, a percentage of 20-40 is considered weak (w) and a percentage of 0-20 is considered very weak (vw).
The compensation cations in the material in its uncalcined form, or after thermal treatment, can be exchanged, in the case of being present, by other metallic ions, H+ and H+ precursors such as for example NH+4. Among the cations that can be introduced by ionic exchange, those that can have a positive role in the activity of the material as a catalyst are preferred, and more specifically, cations such as H+′ rare earth cations and metals of the group VIII, as well as of group IIA. IIIA, IVA, Va, IB, IIB, IIIB, IVB, VB, VIIB of the periodic chart of elements are preferred.
For the purpose of preparing catalysts, the crystalline material of the present invention can be combined closely with hydrogenating-dehydrogenating agents such as platinum, palladium, nickel, rhenium, cobalt, tungsten, molybdenum, vanadium, chrome, manganese, iron. The introduction of these elements can be carried out in the crystallization step, by exchange (if appropriate), and/or by impregnation or by physical mixing. These elements can be introduced in their cationic form and/or as of salts or other compounds which by decomposition produce the metallic component or oxide in its suitable catalytic form.
The material ITQ-21 can be prepared in a basic medium and in the absence of added fluoride ions, from a reaction mixture that contains H2O, optionally an oxide or a source of the trivalent element X, such as for example Al and/or B, an oxide or source of the element or tetravalent elements Y, such as for example Si; a source of Ge, such as for example GeO2 and an organic structure directing agent (R) generally a salt of N(16)-methylsparteinium, preferably the hydroxide.
The composition of the reaction mixture has the following composition in terms of molar ratios of oxides:
Crystallization of the material ITQ-21 can be carried out statically or with stirring, in autoclaves at a temperature between 80 and 200° C., at sufficient times to achieve crystallization, for example, between 12 hours and 30 days.
When the crystallization step ends, the ITQ-21 crystals are separated from the mother liquors and are recovered. It should be taken into account that the components of the synthesis mixture can come from different sources and depending thereon, crystallization times and conditions can be varied. For the purpose of facilitating synthesis, material ITQ-21 crystals can be added as seeds to the synthesis mixture, in amounts up to 15% by weight with respect to the total oxides. These can be added before or during crystallization of the material ITQ-21.
The organic agent can be eliminated, for example by extraction and/or by thermal treatment heating at a temperature above 250° C. for a period of time between 2 minutes and 25 hours.
The material of the present invention can be made into pellets in accordance with known techniques, and can be used as a component of catalysts of catalytic cracking of hydrocarbons, catalytic hydrocracking of hydrocarbons, alkylation of aromatics with olefins and in processes of esterification, acylation, aniline reaction with formaldehyde in its acid form and/or exchanged with suitable cations.
Several examples that illustrate aspects of ways of carrying out the invention will be described hereinafter.
20.25 g of (−)-sparteine are mixed with 100 ml of acetone. 17.58 g of methyl iodide are added, drop by drop, to this mixture while the mixture is stirred. After 24 hours, a cream color precipitate appears. 200 ml of diethyl ether are added to the reaction mixture, which is filtered and the solid obtained is vacuum dried. The product is N(16)-methylsparteinium iodide with a yield higher than 95%.
The iodide is exchanged by hydroxide using ionic exchange resin, according to the following process: 31.50 g of N(16)-methylsparteinium iodide are dissolved in 92.38 g of water. 85 g of Dowes BR resin are added to the solution and kept with stirring until the next day. Subsequently, it is filtered, washed with distilled water and we obtain 124.36 g of a N(16)-methylsparteinium hydroxide solution with a concentration of 0.65 moles/kg.
2.08 g of GeO2are dissolved in 25.43 g of a N-methylsparteinium hydroxide solution with a concentration of 0.59 moles/1000 g. Once dissolved, 4.16 g of tetraethylorthosilicate are hydrolyzed in said solution, allowing to evaporate with stirring until the ethanol formed evaporates. 0.15 g of ITQ-21 crystals suspended in 1.86 g of water are added. The final composition of the synthesis mixture is:
0.67 SiO2:0.33 GeO2:0.50 C16H29NOH:4 H2O
It is heated at 175° C. in steel autoclaves with an inside Teflon casing for 12 days. The solid obtained after filtering, washing and drying at 100° C. is ITQ-21, and the most important lines of its diffraction pattern are shown in table 3.
(a)±0.2
In this table
When the material is calcined at 540° C. for 3 hours, the most important diffraction lines of the material are the ones that appear in table 4.
(a)±0.2
5.21 g of tetraethylorthosilicate are hydrolyzed in 25.43 g of N-methylsparteinium hydroxide solution with a concentration of 0.59 moles/1000 g, wherein 0.54 g of GeO2 have been previously dissolved. The mixture is allowed to evaporate with stirring until the ethanol formed is eliminated. 0.10 g of ITQ-21 crystals suspended in 2.05 g of water are added. The final composition of the mixture is:
0.83 SiO2:0.17 GeO2:0.50 C16H29NOH:4 H2O
It is heated at 175° C. in steel autoclaves with an inside Teflon casing for 13 days. The solid obtained after filtering, washing and drying at 100° C is ITQ-21 with amorphous material.
0.33 g of GeO2 are dissolved in 27.95 g of a N-methylsparteinium hydroxide solution with a concentration of 0.59 moles/1000 g. A Once dissolved, 6.25 g. of tetraethylorthosilicate are hydrolyzed in said solution, allowing it to evaporate with stirring until the ethanol formed evaporates. 0.15 g of ITQ-21 crystals suspended in 1.86 g of water are added. The final composition is:
0.91 SiO2:0.09 GeO2:0.50 C16H29NOH:4 H2O
The mixture is heated at 175° C. in steel autoclaves with an inside Teflon casing for 24 days. The product obtained is ITQ-21 with amorphous material.
0.245 g of aluminum isopropoxide and 5.213 g of tetraethylorthosilicate are hydrolyzed in 26.576 g of a N-methylsparteinium hydroxide solution with a concentration of 0.564 moles/1000 g, wherein 0.528 g of GeO2 have been previously dissolved. The mixture is allowed to evaporate with stirring until the ethanol is eliminated and the isopropanol formed in the hydrolysis. 0.10 g of ITQ-21 crystals suspended in 2.05 g of water are added. The final composition of the mixture is:
0.83SiO2:0.17 GeO2:0.02 Al2O3:0.50 C16H29NOH:6 H2O
It is heated at 175° C. in steel autoclaves with an inside Teflon casing for 13 days. The product obtained after filtering, washing and drying at 100° C. is Al-ITQ-21 with amorphous material.
| Number | Date | Country | Kind |
|---|---|---|---|
| P200102753 | Nov 2001 | ES | national |
The present application is a Continuation of co-pending PCT Application No. PCT/ES02/00568, filed Nov. 29, 2002, which in turn, claims priority from Spanish Application Serial No. P200102753, filed Nov. 30, 2001. Applicants claim the benefits of 35 U.S.C. §120 as to the PCT application and priority under 35 U.S.C. §119 as to said Spanish application, and the entire disclosures of both applications are incorporated herein by reference in their entireties.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/ES02/00568 | Nov 2002 | US |
| Child | 10855988 | May 2004 | US |