Patent Grant
11298676
The present application claims priority from Czech patent Application No. PV 2017-663 filed on Oct. 17, 2017, the entire contents of which are incorporated herein by reference.
The presented invention applies to the method of production of stable porous coordination polymers (metal-organic framework—MOF) consisting of metal centres linked using organic ligands—linkers based on phosphinic acids that contain two or more phosphinic groups, and their resulting crystalline structure contains pores.
These materials can be used for storing of gases or separation of gases, for preparation of membranes, heterogeneous catalysts, sorbents, lithium batteries, of proton conductors and of drug carriers and they also find application in analytical chemistry as sensors of gases, ions or organic or biologically active substances.
MOFs, thus Metal Organic Frameworks, are hybrid highly porous compounds consisting of inorganic parts (metal ion or cluster) linked with organic linkers which form coordination links to inorganic parts using donor groups while forming crystal structures (D. J. Tranchemontagne, J. L. Mendoza-Cortés, M. O'Keeffea, O. M. Yaghi, Secondary building units, nets and bonding in the chemistry of metal-organic frameworks, Chem. Soc. Rev. 38 (2009) 1257-1283). When compared with other substances, they are exceptional due to their variability. Using suitable inorganic parts and organic linkers, a material with the most different required properties, from size and shape of pores to electric and magnetic properties of the lattice can be designed and composed.
When compared with other porous crystalline materials, e.g. zeolites, MOFs can contain pores in the range of micropores (pore diameter <2 nm) or mesopores (pore diameter in range 2-50 nm) and their surface can be adjusted as hydrophilic or hydrophobic according to the combination of the selected metal and the type of linker. However, the opportunities to set size and share of hydrophobicity/hydrophilicity pores of MOF, for a given metal and length and structure of organic linker, have been very limited up to now. Moreover, most MOFs show low stability in aqueous medium, particularly at higher temperatures (M. Brichtová, P. Doležel, Struktura, vlastnosti a potenciál MOF, Chemagazin, No. 4, volume XX (2010)). Linkers of up to now described MOFs are mostly based on donor groups of acids, particularly of carboxyl, sulphonic or phosphonic ones, and also those based on heterocycles containing nitrogen. However, direct modification of these donor groups: of carboxyl, sulphonic and phosphonic acids with other organic groups, e.g. with alkyls or aryls which would allow to change the character of MOFs, is not possible. Only selection of a suitable spacer among the donor groups can have effect on size of pores of the material.
So called solvothermal techniques are used most frequently for synthesis of MOFs, i.e. they are prepared using synthesis of precursor of metal and organic ligand which are mostly diluted in high-boiling polar solvent and heated in a sealed vessel. The crystallization process is the most important one for the formation of the desired structures. Other options are the wet electrochemical method where the source of metal is an anode submerged in solution of carboxylates. Solvent-free synthesis of MOFs is also highly preferred. This can be carried out mechanically by grinding, where precursors of metal and organic linker are ground together and the rising by-products like water or low-molecular organic products are removed under raised temperature. After the substance is synthesised postsynthetic modification can follow where MOFs are modified without changing their topology, for example adjustments or replacements of organic linkers are carried out.
Recently MOFs have been frequently studied particularly because of their high application potential which involves storing or separation of gases, transport of drugs, heterogeneous catalysis, preparation of membranes, heterogeneous catalysts, parts of lithium batteries and proton conductors and utilisation in analytical chemistry in function of sensors of gases, ions or biologically active substances (B. Li, H.-M. Wen, W. Zhou, B. Chen, Porous Metal-Organic Frameworks for Gas Storage and Separation: What, H-low, and Why? J. Phys. Chem. Lett., 5 (2014) 3468-3479; A. H. Chughtai, N. Ahmad, H. A. Younus, A. Laypkov, F. Verpoort, Metal-organic frameworks: versatile heterogeneous catalysts for efficient catalytic organic transformations, Chem. Soc. Rev. 44 (2015) 6804-6849; M. G. Campbell, M. Dinc{hacek over (a)}, Metal-Organic Frameworks as Active Materials in Electronic Sensor Devices, Sensors 17 (2017) 1108; P. Horcajada, R. Gref, T. Baati, P. K. Allan, G. Maurin, P. Couvreur, G. Férey, R. E. Morris, C. Serre, Metal-organic frameworks in biomedicine Chem. Rev. 112 (2012) 1232-1268). For example, nanocarriers are under development for treatment of cancer which allow efficient and controllable transport of a drug, e.g. of cis-platinum, in body. MOFs can also be used as a contrast agent in magnetic resonance.
The disadvantage of MOFs is their relatively low thermic, chemical and mechanical stability when compared with pure inorganic materials. Due to presence of an organic part, most MOFs are stable at maximum to some 500° C. The above handicap lies in impossibility to modify the known linkers based on coordination groups of carboxyl, sulphonic or phosphonic acids. Linkers based on acids with phosphine groups have been used for preparation of coordination polymer only as monophosphinic acid (V. Moodley, L. Mthethwa, M. N. Pillay, B. Omondi, W. E. van Zyl, The silver(I) coordination polymer [AgO2PPh2]n and unsupported Ag . . . Ag interactions derived from aminophosphonate and phosphinic acid, Polyhedron 99 (2015), 87-95) or diphosphinic acid where phosphine groups have been separated by methylene bridge (F. Cecconi, D. Dakternieks, A. Duthie, C. A. Ghilardi, P. Gili, P. A. Lorenzo-Luis, S. Midollini, A. Orlandini, Inorganic-organic hybrids of the p,p′-diphenylmethylenediphosphinate ligand with bivalent metals: a new 2D-layered phenylphosphinate zinc(II) complex, J. Solid State Chem. 177 (2004) 786-792) or 1,1′ferocendiyl bridge (R. Shekurov, V. Miluykov, O. Kataeva, D. Krivolapov, O. Sinyashin, T. Gerasimova, S. Katsyuba, V. Kovalenko, Y. Krupskaya, V. Kataev, B. Büchner, I. Senkovska, S. Kaskel, Reversible Water-induced Structural and Magnetic Transformations and Selective Water Adsorption Properties of Poly(manganese 1,1′-ferrocenediyl-bis(H-phosphinate)), Cryst. Growth Des. 16 (2016) 5084-5090) but in all cases, the prepared coordinating polymers have not shown porosity accessible to N2 molecules.
The invention concerns the new types of porous coordination polymers (MOF) which have variable prepared pores with porosity up to 1200 m2/g available and the method of their preparation. The inorganic part of MOFs structure consists of trivalent cations of metals, represented above all by iron, aluminium, chromium or yttrium which are linked with organic linkers containing two to four phosphine groups bound to alkyl or aryl frame with general formula:
where R1 is hydrogen, alkyl or aryl and possibly alkyl or aryl carrying a functional group, or it substitutes the second bond of phosphorus to spacer.
Preferably, spacer is formed of aromatic phosphinic acids where two, at least, of phosphinic groups of linker take part in bond to trivalent metal, and therefore they are not a free part of spacer and the remaining, one or two phosphine groups form an indivisible part of spacer, they do not take part in branched polymer bonds to the metal but they intervene in the pore space and this way they modify its space.
Example of Phosphine Acid:
and of its spacer:
It is advantageous to compose spacers of these phosphinic acids:
tetraphenylmethane-4′,4″,4′″,4″″-tetrakis(R phosphinic acid)—TPMTPA(R)
It is advantageous if spacer of TPMTPA(R) contains two free phosphine groups, other two phosphine groups are not a part of spacer but they bond to the trivalent metal.
1,2,3,5,6,7-hexahydrophospholo[3,4-f]isophosphindole-2,6-diol-2,6-dioxide
1,3,5-triphenylbenzene-4′,4″,4′″-tris(R phosphinic acid)—TPBTPA(R)
It is advantageous if spacer of TPBTPA(R) contains no free phosphine groups, that are a part of spacer but all three bond to the trivalent metal.
Specific material with suitable size of pores adequate to the selected active substance can be created of MOFs, and it is able to contain a large amount of this substance, and therefore much higher portion of the drug to quantity of carriers can be achieved. The change of substituent R1, R2 or R3 itself can have an effect on or control size of pores. The significant benefit of the new MOFs is their environmental, bioapplication potential and high chemical stability.
The MOFs have been prepared through synthesis of salts of trivalent cations of metals M3+, the sources of which are aluminium, chromium, iron or yttrium salts, advantageous if in the form of chlorides, nitrates or sulphates with linkers carrying two to four phosphine groups under presence of solvent. Typical linkers are bivalent phosphine acids, like phenylene-1,4-bis(R phosphinic acid) (PBPA) and biphenylene-4,4′-bis(R phosphinic acid), and also tris- or tetra-phosphine acids. It is advantageous to use linkers carrying alkyl, aryl chain or functional groups on aryl and possibly alkyl chain linking phosphine acid, e.g. 2-methylphenylene-1,4-bis(R phosphinic acid), and the above chains or functional groups can be represented by methyl, ethyl, i-propyl, phenyl, amino or nitro groups, and also by heterocycle (e.g. pyridine), thio, sulphonate or cyano groups, halogens, and the like. It is advantageous if some phosphine groups of tris and tetraphosphinic acids can stay free without binding to the trivalent metal where they are used for further modelling of size and arrangement of pores.
With advantage, linker may be modified by R bonded to phosphor, where R is methyl, ethyl, i-propyl, phenyl, amino or nitro group, furthermore by a heterocycle (e.g. pyridine), thio, sulfonate or cyano group or halogens.
The optimum range of share of M3+ and phosphinic groups is 1:2 to 1:8, and it is advantageous if 1:4, where concentration is advantageous if M3+ being 0.001 mol to 0.02 mol/l. Polymerysation of phosphinic acid and M3 salt runs in solvent during heating. After adding the solvent, the suspension is heated in an autoclave or in glass vials at temperatures from 25° C. to 250° C. for 24 hours, at least, without stirring or with stirring. Water, organic solvents or organic acids, for example N,N-dialkyl formamide, formamide, acetone, hexane, acetonitrile, toluene, dimethylsulphoxide, N-methyl-2-pyrrolidone, tetrahydrofuran, formic acid and benzoic acid can be used as the solvent, and it is advantageous if it is ethanol (EtOH) and N,N-dimethyl formamide, or mixtures of these solvents. Selection of combination of solvent, share of M3+ to phosphine acid, temperature and time for synthesis is very important, if unsuitable conditions and solvent are selected, regular structure need not appear, or can form non-porous coordination polymers.
After cooling, the resulting suspension is centrifuged, and it is advantageous if this is done under 10000 rpm for 5 minutes, at least, and the product deposit is separated through decantation. The product is washed first with water or ethanol, in two repeats, at least, and then the product is washed with acetone, also in two repeats, at least. Finally, the product is dried on air under laboratory temperature.
The general structure of prepared MOFs, for example for coordination polymer of bis-phosphinic acid and trivalent metals with resulting share of metal to phosphinic groups in ratio 1:3
where R1 is hydrogen, alkyl or aryl, and possibly alkyl or aryl carrying a functional group, M is a trivalent metal.
The structure of prepared MOFs was tested using x-ray powder diffraction (XRD) using CoKα radiation. The measured graphs show that the prepared MOFs correspond to the MOF structure containing Fe and phenylene-1,4-bis(R phosphinic acid) or to that with biphenylene-1,4-bis(R phosphine acid). We have compared MOFs with aluminium, chromium, iron and yttrium prepared of phenylene-1,4-bis(methylphosphinic acid) one with another, the diffraction lines of all measurements have been almost equal, thus all the prepared MOFs have shown the analogical structure.
Further, the specific surface of MOFs and their porousness have determined, they have been characterised by adsorption isotherm of nitrogen. The adsorption isotherm of nitrogen has been investigated at temperature 77 K. After the equilibrium has set where the pressure of adsorbate (gas) has not changed any more, we have calculated the quantity of adsorbate that had adsorbed from the gas phase from the final pressure, capacity of the vessel with adsorbent (MOF) and size of adsorbate dose. This procedure has been repeated for further doses of adsorbate until, after the adsorption equilibrium had been established, the pressure has been very close to the saturated vapor pressure of the adsorbate at the measurement temperature. Their porousness has been established from rise and shape of the isotherm curve using the NLDFT method or the HK-plot method, and their specific surface using the t-plot or BET methods, it has ranged from 220 m2/g to 1200 m2/g. Porous MOFs that have contained pores with micropores with size less 2 nm or mesopores with size 2-3 nm have been prepared. We have established that change of substituent R1, R2 or R3, change of length of spacer bi-phosphinic acid and change of trivalent metal cation can be used to have effect on porosity of prepared MOF. Generally, we can say that MOFs prepared advantageously of phenylene-1,4-bis(methylphosphinic acid) (PBPA) have contained pores of about 1 nm while MOFs prepared advantageously of biphenylene-4,4′-bis(methylphosphinic acid) (BBPA) (BBPA) have contained pores larger, around 2 nm, and also linking a bigger substituent to the phosphine group makes the pore size lesser.
Further, we have determined stability of the MOFs prepared using thermogravimetric analysis. We have exposed the prepared MOFs to temperature load in oxidizing or inert atmosphere and followed change of weight on microscales. We have raised the temperature gradually with rate 5° C./min. We have found that the prepared MOFs are stable approximately till 450° C. in the air atmosphere and in some cases till 500° C. in the argon atmosphere.
Finally, we have tested application possibilities of the resulting MOFs namely storing of hydrogen and CO2 into their pores. We have found that hydrogen and CO2 adsorbs inside formed pores and it is possible to store it in the pores.
In figures R=alkyl or aryl group, e.g. Me, i-Pr, Ph.
Preparation of Porous Fe-MOF with PBPA(Me)
The initial suspension containing 18.8 mg of phenylene-1,4-bis(methylphosphinic acid)—PBPA(Me) with the amount of substance of 0.08 mmol, 10.8 mg FeCl3.6H2O with the amount of substance of 0.04 mmol and 5 ml of anhydrous EtOH was heated in an autoclave with capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 24 hours without stirring.
After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed first with water (3×30 ml) and acetone (3×30 ml) and it was dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit iron (III) phenylene-1,4-bis(methylphosphinate) with weight of 10 mg was acquired. MOF was characterised using the adsorption isotherm of nitrogen, and from it its specific surface (using t-plot method) and porosity (using HK-plot method) were determined, and the specific surface was 712 m2/g and the diameter of pores was 0.8 nm.
Stability of Fe-MOF with PBPA(Me) was characterised with boiling of 20 mg of Fe-MOF with PBPA(Me) in 10 ml of H2O for 24 hours. Then the specific surface was measured, it was 582 m2/g.
Preparation of Porous Al-MOF with PBPA(Me)
The initial suspension containing 18.8 mg of phenylene-1,4-bis(methylphosphinic acid)—PBPA(Me) with the amount of substance of 0.08 mmol, 9.7 mg AlCl3.6H2O with amount of substance of 0.04 mmol and 5 ml of anhydrous ethanol was heated in an autoclave with capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 24 hours without stirring.
After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed first with water (3×30 ml) and acetone (3×30 ml) and it was dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit aluminium phenylene-1,4-bis(methylphosphinate) with weight of 10 mg was acquired. MOF was characterised using the adsorption isotherm of nitrogen, and from it its specific surface (using t-plot method) and porosity (HK-plot) were determined, and the specific surface was 921 m2/g and the diameter of pores was 0.9 nm. Stability of Al-MOF with PBPA(Me) was characterised with boiling of 20 mg Al-MOF with PBPA(Me) in 10 ml of H2O in water for 24 hours. Then the specific surface was measured, it was 1038 m2/g.
Preparation of Porous Y-MOF with PBPA(Me)
The initial suspension containing 18.8 mg of phenylene-1,4-bis(methylphosphinic acid)—PBPA(Me) with the amount of substance of 0.08 mmol, 7.8 mg YCl3 with the amount of substance of 0.04 mmol and 5 ml of anhydrous ethanol was heated in an autoclave with the capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 96 hours without stirring.
After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed first with water (3×30 ml) and acetone (3×30 ml) and dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit phenylene-1,4-bis(methylphosphinate) with weight of 10 mg was acquired. MOF was characterised using the adsorption isotherm of nitrogen, and from it its specific surface (using t-plot method) and porosity (HK-plot) were determined, and the specific surface was 711 m2/g. MOF had wide distribution of pores and the diameter of pores was over 0.5 nm.
Preparation of Porous Cr-MOF with PBPA(Me)
The initial suspension containing 18.8 mg of phenylene-1,4-bis(methylphosphinic acid)—PBPA(Me) with the amount of substance of 0.08 mmol, 10.6 mg CrCl3.6H2O with the amount of substance of 0.04 mmol and 6 ml of water was heated in an autoclave with capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 48 hours without stirring.
After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed first with water (3×30 ml) and acetone (3×30 ml) and dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit chromium (III) phenylene-1,4-bis(methylphosphinate) with weight of 10 mg was acquired.
MOF was characterised using the adsorption isotherm of nitrogen, and from it its specific surface (using t-plot method) and porosity (using HK-plot method) were determined, and the specific surface was 811 m2/g and the diameter of pores was 0.8 nm.
Preparation of Porous Al-MOF with PBPA(pH)
The initial suspension containing 14.3 mg of phenylene-1,4-bis(phenylphosphinic acid)—PBPA(Ph) with the amount of substance of 0.04 mmol, 4.8 mg AlCl3.6H2O with the amount of substance of 0.02 mmol and 5 ml of anhydrous ethanol was heated in an autoclave with the capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 24 hours without stirring.
After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed first with water (3×30 ml) and acetone (3×30 ml) and it was dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit aluminium phenylene-1,4-bis(phenylphosphinate) with weight of 10 mg was acquired. MOF was characterised using the adsorption isotherm of nitrogen, and from it its specific surface (using t-plot method) and the diameter of pores (using HK-plot method) were determined, and the specific surface was 224 m2/g and the diameter of pores was in range 0.4-0.6 nm.
Preparation of Porous Fe-MOF with BBPA(Me)
The initial suspension containing 24.8 mg of biphenylene-4,4′-bis(methylphosphinic acid) BBPA(Me) with the amount of substance of 0.08 mmol, 10.8 mg FeCl3.6H2O with the amount of substance of 0.04 mmol and 10 ml of N,N-dimethylformamide was heated at 120° C. for 72 hours without stirring.
After the resulting suspension cooled, it was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed with ethanol (3×30 ml) and then acetone (3×30 ml) and dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit iron (III) biphenylene-4,4′-bis(methylphosphinate) with weight of 15 mg was acquired. For the resulting MOF the adsorption isotherm of nitrogen was measured and specific surface (with BET method) and porosity (with NLDFT method for cylindric silicate pores calculated using program Belmaster™) were calculated, and the specific surface was 978 m2/g, the total volume of pores was 1.57 cm3/g and the diameter of pores was 2.4 nm.
Preparation of Porous Fe-MOF with BBPA(pH)
The initial suspension containing 34.8 mg of biphenylene-4,4′-bis(phenylphosphinic acid)—BBPA(Ph) with the amount of substance of 0.08 mmol, 10.8 mg FeCl3.6H2O with the amount of substance of 0.04 mmol and 10 ml of anhydrous ethanol was heated in an autoclave with capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 24 hours without stirring.
After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed with EtOH (3×30 ml) and then with acetone (3×30 ml) and dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit iron (III) biphenylene-4,4′-bis(phenylphosphinate) with weight of 25 mg was acquired.
For the resulting MOF the adsorption isotherm of nitrogen was measured and specific surface (with BET method) and porosity (with NLDFT method for cylindric silicate pores calculated using program Belmaster™) were calculated, and the specific surface was 1172 m2/g, the total volume of pores was 2.40 cm3/g and the diameter of pores was 2.2 nm.
Preparation of Porous Fe-MOF with PBPA (Me) in the Form of Nanoparticles
The initial suspension containing 4.7 mg of phenylene-1,4-bis(methylphosphinic acid)—PBPA(Me) with the amount of substance of 0.02 mmol, 5.4 mg FeCl3.6H2O with the amount of substance of 0.02 mmol and 10 ml of formamide was heated at 100° C. for 24 hours without stirring.
After the resulting suspension cooled, it was centrifuged at 10000 rpm for 10 minutes and the product deposit was separated through decantation. The product was washed first with water (3×10 ml) and then with anhydrous EtOH (2×10 ml) and the resulting nanoparticles were kept in the form of colloidal solution in anhydrous EtOH. Coordination polymer of porous MOF with monomer unit iron (III) phenylene-1,4-bis(methylphosphinate) with weight of 3 mg was acquired.
Preparation of Porous Fe-MOF with BBPA(CH2═CH2pH)
19.5 mg of biphenylene-4,4′-bis(4-vinylphenylphosphinic acid)—BBPA(CH2═CH2Ph) with the amount of substance of 0.04 mmol and 5.4 mg of FeCl1.6H2O with the amount of substance of 0.02 mmol was suspended in 10 ml of formic acid. The resulting mixture was stirred in a vial at temperature 30° C. for 48 hours.
After stirring was finished, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed with EtOH (3×30 ml) and then acetone (3×30 ml) and dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit iron (III) biphenylene-4,4′-bis(4-vinylphenylphosphinate) with weight of 10 mg was acquired.
For the resulting MOF the adsorption isotherm of nitrogen was measured and specific surface (with BET method) and porosity (with NLDFT method for cylindric silicate pores calculated using program Belmaster™) were calculated, and the specific surface was 569 m2/g, the total volume of pores was 0.88 cm3/g (NLDFT) and the diameter of pores was 1.9 nm.
Preparation of Porous Fe-MOF with TPBTPA(Me)
The initial suspension containing 14.0 mg of 1,3,5-triphenylbenzene-4′,4″,4′″-tris(methylphosphinic acid)—TPBTPA(Me) with the amount of substance of 0.026 mmol, 4.0 mg of FeCl3.6H2O with the amount of substance of 0.015 mmol and 10 ml of anhydrous ethanol was heated in an autoclave with capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 24 hours without stirring. After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed with ethanol (3×30 ml) and then with acetone (3×30 ml) and it was dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit iron (III) 1,3,5-triphenylbenzene-4′,4″,4′″-tris(methylphosphinate) with weight of 7 mg was acquired.
MOF was characterised using the adsorption isotherm of nitrogen, and from it its specific surface (using t-plot method and porosity (HK-plot) were determined, and the specific surface was 869 m2/g and the diameter of pores was 0.9 nm.
Preparation of Porous Fe-MOF with TPMTPA(Me)
The initial suspension containing 11.7 mg of tetraphenylmethane-4′,4″,4′″,4″″-tetrakis(methylphosphinic acid)—TPMTPA(Me) with the amount of substance of 0.02 mmol, 5.4 mg of FeCl3.6H2O with the amount of substance of 0.02 mmol and 10 ml of H2O was heated in an autoclave with capacity of 50 ml with teflon inlet under autogenous pressure at 250° C. for 24 hours without stirring. After the autoclave cooled, the resulting suspension was centrifuged at 10000 rpm for 5 minutes and the product deposit was separated through decantation. The product was washed with ethanol (3×30 ml) and then with acetone (3×30 ml) and it was dried in air at laboratory temperature. Coordination polymer of porous MOF with monomer unit iron (III) tetraphenylmethane-4′,4″,4′″,4″″-tetrakis(methylphosphinic acid) with weight of 5 mg was acquired.
MOF was characterised using the powder x-ray diffraction and its structure was found using electron diffraction tomography.
Comparison of Porosity of Prepared MOFs
Fe-MOF with BBPA(Me) produced according to Example 5 was compared with Fe-MOF with BBPA(Ph) that was prepared according to Example 6. The size of pores of Fe-MOF with BBPA(Ph) was 0.2 nm less when compared with Fe-MOF with BBPA(Me). This shows that if the substituent at the R1 position is phenyl, this will shrink size of pores when compared with substitution with methyl.
Fe-MOF with PBPA(Me) produced according to Example 1 was compared with Al-MOF with PBPA(Me) that was prepared according to Example 2, with Y-MOF with PBPA(Me) produced according to Example 3 and with Cr-MOF with PBPA(Me) produced according to Example 4. The applied method of measurement could not determine porousness of Y-MOF with PBPA(Me), according to the resulting graph the porousness was over 0.5 nm. Fe-MOF with PBPA(Me), Al-MOF with PBPA(Me) and Cr-MOF with PBPA(Me) had pores of comparable size 0.8-0.9 nm which falls within the experimental error of the applied method and it indicates independence of size of pores on used metal.
Last but not least, Al-MOF with PBPA(Ph) prepared according to Example 4 was compared with Al-MOF with PBPA(Me) prepared according to Example 2. The size of pores of Al-MOF with PBPA(Ph) was 1 nm less than the size of pores in the structure of Al-MOF with PBPA(Me). Likely the size of pores of Al-MOF with PBPA(Ph) was almost equal to size of nitrogen atoms and thus the measurement was at the limits of the applied method. However, we can expect that the size of pores of Al-MOF with PBPA(Ph) is less than in MOF with a lesser substituent and this is methyl in the structure of Al-MOF with PBPA(Me).
Analysis of Absorption of N2, H2 and CO2 in MOFs Samples
MOF—adsorbent
N2, H2 and CO2—adsorbate
We weighted a cuvette, poured a sample of prepared MOF inside, then the sample was evacuated at least 24 hours by 80° C. to remove residua of solvents and of air moisture. We weighted the cuvette again after the evacuation had finished, to determine the weight of the MOF specimen—adsorbent. Subsequently we filled it with known amount of adsorbate N2, H2 or CO2, we measured the pressure in the cuvette corresponding to the amount of adsorbed adsorbate after the pressure in the cuvette was in equilibrium and we added more adsorbate up to pressure 0.95 bar. In case of sorption of N2 we also measured desorption i.e. small quantity of gas-adsorbate was pumped out and we waited till the pressure stabilised down to 0.3 bar where we finished the experiment. We did the measurement with a device Belsorp max II (company MicrotracBel). Before the measurement we evacuated the samples at temperature 80° C. for 24 hours, at least, in order to remove residua of solvents and of air moisture. Then we evacuated the samples and gradually added adsorbate while monitoring pressure increase so that each point in the graph would correspond to the equilibrium conditions for that pressure. We measured up to 0.95 bar. Then we measured gas desorption for N2 in a similar way, only the pressure was decreased down to 0.3 bar.
We measured adsorbate H2 and N2 at 77K (fluid nitrogen) and CO2 at 25° C.
MOFs with the above properties can be used for applications oriented particularly on storing of gases, separation of gases, as drug carriers, for preparation of membranes, of heterogeneous catalysts, sorbents, lithium batteries, of proton conductors and they can be used in analytical chemistry as sensors, above all, of gases, ions or biologically active substances.
| Number | Date | Country | Kind |
|---|---|---|---|
| CZ2017-663 | Oct 2017 | CZ | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20190134602 | Yoon | May 2019 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20190210002 A1 | Jul 2019 | US |