Claims
- 1. A porous polymeric membrane wherein said membrane is elasotomeric, biocompatible and blood compatible and which has a spongy porous cell wall structure with a filamentous outer surface with interfiber spacing ranging from about 30 to 150 microns and a filamentous inner surface with an interfiber spacing ranging from about 30 to about 150 microns said membrane being prepared by a process comprising the steps of,
- a) forming a solution of a polymer in a solvent for the polymer;
- b) adding a nonsolvent to the polymer solution until a thermodynamically unstable polymer solution is obtained;
- c) separately spraying the unstable polymer solution and nonsolvent from separate spray means onto a sliding and rotating mandrel means to form a precipitated material; and
- d) placing the precipitated material into a bath of nonsolvent to cure the precipitated material.
- 2. A porous membrane according to claim 1, wherein the polymer is a polyamino-acid, a polysaccharide, a cellulose derivative, an alginate, a silicone, a polyurethane or mixtures thereof.
- 3. A porous membrane according to claim 1, wherein the solvent is water-miscible and has a low boiling point.
- 4. A porous membrane according to claim 3, wherein the solvent is tetrahydrofuran, an amide solvent, a sulfoxide solvent, a dioxane or mixtures thereof.
- 5. A porous membrane according to claim 1, wherein the nonsolvent is miscible with the solvent and has a solubility parameter different from the polymer.
- 6. A porous membrane according to claim 1, wherein the nonsolvent is water, an alcohol, or water containing a substance which enhances the inducement of solution instability and/or precipitation of polymer from the solution.
- 7. A porous membrane according to claim 6, wherein the solvent is water, a lower alkanol or mixtures thereof.
- 8. A porous membrane according to claim 1, wherein the polymer is polyurethane.
- 9. A porous membrane according to claim 1, wherein the polymer is a polyether urethane-poly(dialkylsiloxane).
- 10. A porous membrane according to claim 9, wherein the solvent is a mixture of tetrahydrofuran and 1, 4-dioxane.
- 11. A porous membrane according to claim 10, wherein the nonsolvent is water.
- 12. A porous membrane according to claim 11, wherein the polymer solution concentration (% w/v) is from about 0.1 to 5.0, the amount of nonsolvent added to the polymer is about 1 to 50 (% v/v), the spray means is driven under gas driving pressure of from about 1 to 45 psi, the polymer solution flow rate from the spray means is about 0.5 to 5.0 ml/min, the nonsolvent flow rate from the spray means is about 0.5 to 5.0 ml/min, the angle between the separate spray means for the nonsolvent and polymer solution and the mandrel means is about 70.degree. to 80.degree., the distance between nozzles of the separate spray means and the mandrel means of about 15 to 100 mm, the mandrel means diameter is from about 0.5 to 1000 mm, the speed of rotation of the mandrel means is about 100 to 2000 rpm and the sliding movement speed of the mandrel means is about 10 to 500 m/min.
- 13. A porous membrane according to claim 1 wherein the filamentous inner surface interfiber spacing ranges from about 50 to 150 .mu.m and the filamentous outer surface interfiber spacing ranges from about 50 to 150 .mu.m.
- 14. A porous membrane according to claim 13, wherein the filamentous inner surface interfiber spacing ranges from about 90 to 150 .mu.m and the filamentous outer surface interfiber spacing ranges from about 90 to 150 .mu.m to 150 .mu.m.
- 15. A porous membrane according to claim 1, wherein the membrane has a hydraulic permeability measured collecting, in the first minute, of from 30 to 60 ml min-1 cm-2 and a high water content.
Parent Case Info
This is a continuation of co-pending application Ser. No. 07/761,508 filed Sep. 18, 1991, now U.S. Pat. No. 5,229,045.