Patent Application
20060029634
This invention relates to porous structures.
Alternating layers of oppositely charged polyelectrolytes can be deposited on a surface. A suitable aqueous treatment can convert the deposited polyelectrolytes to a porous structure. The degree of porosity can be controlled by selection of the treatment conditions.
A porous polyelectrolyte multilayer can be loaded with a compound, for example, a drug, a liquid crystal, or ionic liquid. Compounds loaded in the multilayer can alter its properties, such as optical and electrical properties. The compound can also be released from the multilayer. The rate of release can be controlled, for example by controlling the porosity of the multilayer. The multilayer can include porous and non-porous regions.
Porous regions of polyelectrolyte multilayers can have pore sizes ranging from 40 nm to 20 μm. The porous structures can be optically transparent in the visible range, such as when pore size is restricted to values smaller than 150 nm. The pore morphology can be locked in by crosslinking the film using heat or chemistry. These porous films can be loaded with a variety of materials for different applications. The loading technique can be used for any kind of molecule.
The ability to introduce porosity selectively within specific regions of a polymer has further extended the utility of porous polyelectrolyte structures as photonic structures and as optical sensors. The thickness, pore size and level of porosity of spatially distinct regions within a solid polymer matrix can be controlled. This control can be particularly important in the fabrication of heterostructures having a complex arrangement of nanoporous regions. Complex arrangements can be useful in, for example, a Fabry-Perot micro-cavity (see, for example, Yariv, A. An Introduction to Theory and Applications of Quantum Mechanics Wiley: New York, 1982, which is incorporated by reference in its entirety). The layer-by-layer processing schemes developed for the manipulation of polyelectrolytes are ideally suited for this task.
A release device can include a porous polyelectrolyte multilayer. The release device can be a thin polymer film that can be coated onto virtually any surface. This makes it possible to coat implants and deliver therapeutics locally. It also adds the ability to study the release of a drug from the surface onto which a cell is attached. Most drug delivery systems are capsules or gels rather than coatings of surfaces making them incapable for use in this manner.
In general, a porous polyelectrolyte multilayer can be used in, for example, optical structures, optical devices, and drug delivery devices. The optical structures can reflect a desired wavelength of light and transmit other wavelengths. An optical device can alternate between transparent and opaque states, acting as a light shutter. A drug delivery device can change color as the drug is depleted from the device.
In one aspect, a polymer-containing structure includes a layer over a substrate, wherein the layer includes a first polymer region and a second polymer region, where the first polymer region responds to a greater extent than the second polymer region when exposed to a pore-altering medium. The first region can include a first polyelectrolyte and a second polyelectrolyte. The second region can include a third polyelectrolyte and a fourth polyelectrolyte. The first region can be disposed between the substrate and the second region. The second region can be disposed between the substrate and the first region. The second region can remain substantially non-porous when exposed to a pore-altering medium. The first region can be porous and the second region can be substantially non-porous. The first region can include a nanopore. The first region can be substantially free of micropores. The first region can become less porous when exposed to a pore-closing medium. The first region can include a compound. The compound can be a drug, a liquid crystal, or an ionic liquid. The substrate can be glass, plastic or metal.
In another aspect, a polymer-containing structure includes a plurality of alternating fixed and variable regions disposed on a substrate, where the variable regions respond to a greater extent than the fixed regions when exposed to a pore-altering medium. A variable region can include a first polyelectrolyte and a second polyelectrolyte. A fixed region can include a third polyelectrolyte and a fourth polyelectrolyte. The variable regions can each independently have a thickness less than 1000 nm. The fixed regions can each independently have a thickness less than 1000 nm. The alternating fixed and variable regions are arranged as a series of alternating layers over the substrate. The thicknesses and refractive indices of the variable regions and the thicknesses and refractive indices of the fixed regions can be selected such that the structure reflects a predetermined wavelength of light. The structure can be substantially free of pores having a diameter of 150 micrometers or greater. The thickness of a variable region can change upon exposure to a pore-altering medium. The refractive index of a variable region can change upon exposure to a pore-altering medium.
In another aspect, a polymer-containing structure includes a first polymer region and a second polymer region, wherein the first polymer region has a refractive index that can be altered by an aqueous treatment of the structure. The aqueous treatment can alter the porosity of the first region. The aqueous treatment need not substantially alter the porosity of the second region. The aqueous treatment can increase or decrease the porosity of the first region.
In another aspect, a drug delivery device includes a plurality of alternating porous and substantially non-porous regions disposed on a substrate. The device can include a compound distributed in a porous region. A porous region can include a first polyelectrolyte and a second polyelectrolyte. A substantially non-porous region can include a third polyelectrolyte and a fourth polyelectrolyte. The plurality of alternating porous and substantially non-porous regions can be arranged as a series of alternating layers over the substrate. The alternating layers of the series can each independently have a thickness and a refractive index selected such that the device reflects light of a predetermined wavelength. The device can include a delivery medium distributed in a porous region. The delivery medium can alter the refractive index of the porous region, thereby altering the reflection of light of a predetermined wavelength. The delivery medium can include a drug. The device can change color when the delivery medium exits the porous region.
In yet another aspect, an optical device includes a porous polymeric structure arranged on a substrate and a liquid crystal distributed in the pores of the polymeric structure. The porous polymeric structure can form a layer over the substrate. The device can include electrode arranged to apply an electric field across the layer when a voltage is applied to the electrodes. Applying an electric field across the layer can increase transmission of light through the porous polymeric structure.
The details of one or more embodiments are set forth in the accompanying drawings and the description below. Other features, objects, and advantages will be apparent from the description and drawings, and from the claims.
a and 28b are photomicrographs of cells exposed to a porous structure.
Nano- and microporous polymers are useful in applications including separation technologies, catalyst surfaces and supports, and antireflection coatings. See, for example, He, T., et al., J. Appl. Poly. Sci. 2003, 87, 2151; Peterson, D. S., et al. J. Anal. Chem. 2003, 75, 5328; Ling, F. H., et al., J. Org. Chem. 2002, 67, 1993; Lakshmi, B. B. and Martin, C. R. Nature 1997, 388, 758; Gu, W., et al. Chem. Mater. 2001, 13, 1949; Deng, H, et al., J. Am. Chem. Soc. 1998, 120, 3522; Chen, Y., et al. J. Am. Chem. Soc. 2000, 122, 10472; Deleuze, H. et al., Polymer 1998, 39, 6109; Sundell, M. J., et al., Chem. Mater. 1993, 5, 372; Ruckenstein, E. and Hong, L. Chem. Mater. 1992, 4, 122; Walheim, S. et al. Science 1999, 283, 520; and Hiller, J., et al., Nature Materials 2002, 11, 59, each of which is incorporated by reference in its entirety.
Other applications include drug delivery systems, tissue engineering, and templates for the growth of nanoscale materials (see, for example, Adiga, S. P. and Brenner, D. W. Nano Lett. 2002, 2, 567; Jang, J.-H.; and Shea, L. D. Journal of Controlled Release 2003, 86, 157; Sohier, J., et al., Journal of Controlled Release 2003, 87, 57; Yang, F., et al., Biomaterials 2004, 25, 1891; Shastri, V. P., et al., Biomaterials 2003, 24, 3133; Lin, A. S. P., et al., Biomaterials 2003, 24, 481; Misner, M. J.; et al., Adv. Mater. 2003, 15, 221; Ulrich, R.; et al., Adv. Mater. 1999, 11, 141; Yi, D. K.; and Kim, D.-Y. Nano Lett. 2003, 3, 207; and Jiang, P.; et al., Science 2001, 291, 453, each of which is incorporated by reference in its entirety).
Porous polymer systems have been prepared by a number of different techniques such as phase separation, the selective dissolution of polymer blends, the degradation of block copolymers, and the polymerization of monomers in sacrificial colloidal or nanoporous silica templates. See, for example, Zhang, G.; et al., Langmuir 2003, 19, 2434; Lin, Z.; et al., Adv. Mater. 2002, 14, 1373; Kiefer, J.; et al., Macromolecules 1996, 29, 4158; Zalusky, A. S.; et al., J. Am. Chem. Soc. 2002, 124, 12761; Urbas, A. M.; et al., Adv. Mater. 2002, 14, 1850; Xu, T.; et al., Polymer 2001, 42, 9091; Takeoka, Y.; and Watanabe, M. Langmuir 2002, 18, 5977; Park, S. H.; and Xia, Y. Adv. Mater. 1998, 10, 1045; Jiang, P.; et al., J. Am. Chem. Soc., 1999, 121, 11630; Holtz, J. H.; and Asher, S. A. Nature, 1997, 389, 829; and Li, Y. Y.; et al., Science, 2003, 229, 2045; each of which is incorporated by reference in its entirety. A polyelectrolyte has a backbone with a plurality of charged functional groups attached to the backbone. A polyelectrolyte can be polycationic or polyanionic. A polycation has a backbone with a plurality of positively charged functional groups attached to the backbone, for example poly(allylamine hydrochloride). A polyanion has a backbone with a plurality of negatively charged functional groups attached to the backbone, such as sulfonated polystyrene (SPS), polyacrylic acid, or a salt thereof. Some polyelectrolytes can lose their charge (i.e., become electrically neutral) depending on conditions such as pH. Some polyelectrolytes, such as copolymers, can include both polycationic segments and polyanionic segments.
Layer-by-layer processing of polyelectrolyte multilayers can be utilized to fabricate conformal thin film coatings with molecular level control over film thickness and chemistry. Charged polyelectrolytes can be assembled in a layer-by-layer fashion. In other words, positively- and negatively-charged polyelectrolytes can be alternately deposited on a substrate. One method of depositing the polyelectrolytes is to contact the substrate with an aqueous solution of polyelectrolyte at an appropriate pH. The pH can be chosen such that the polyelectrolyte is partially or weakly charged. The multilayer can be described by the number of bilayers it includes, a bilayer being the structure formed by the ordered application of oppositely charged polyelectrolytes. For example, a multilayer having the structure PAH-PAA-PAH-PAA-PAH-PAA would be said to be made of three bilayers.
These methods can provide a new level of molecular control over the deposition process by simply adjusting the pH of the processing solutions. The nonporous polyelectrolyte multilayers can form porous thin film structures induced by a simple acidic, aqueous process. Tuning of this porosity process, including the manipulation of such parameters as salt concentration (i.e., ionic strength), temperature, pH, or surfactant chemistry, can lead to the creation of micropores, nanopores, or a combination thereof. A nanopore has a diameter of less than 150 nm, for example, between 1 and 120 nm or between 10 and 100 nm. The nanopores can have diameters of less than 100 nm. A micropore has a diameter of greater than 200 nm. Selection of porosity-inducing conditions can provide control over the porosity of the coating. For example, the coating can be a nanoporous coating, substantially free of micropores. Alternatively, the coating can be a microporous coating, having pores with diameters of greater than 200 nm, such as 250 nm, 500 nm, 1 micron, 2 microns, 5 microns, 10 microns, or larger.
The porosity of polyelectrolyte multilayer can be changed by contacting the polyelectrolyte multilayer with a pore-altering medium. A pore-altering medium can be a pore-forming medium that can induce the formation of pores or increase the size of existing pores in a polyelectrolyte multilayer. Alternatively, a pore-altering medium can be a pore-closing medium that can induce the closing of pores or reduce the size of existing pores in a polyelectrolyte multilayer.
The properties of weakly charged polyelectrolytes can be precisely controlled by changes in pH. See, for example, G. Decher, Science 1997, 277, 1232; Mendelsohn et al., Langmuir 2000, 16, 5017; Fery et al., Langmuir 2001, 17, 3779; Shiratori et al., Macromolecules 2000, 33, 4213; and U.S. patent application Ser. No. 10/393,360, each of which is incorporated by reference in its entirety. A coating of this type can be applied to any surface amenable to the water based layer-by-layer (LbL) adsorption process used to construct these polyelectrolyte multilayers. Because the water based process can deposit polyelectrolytes wherever the aqueous solution contacts a surface, even the inside surfaces of complex objects can be coated.
The fabrication of polyelectrolyte multilayer (PEM) thin films is a simple technique for creating various thin film optoelectronic devices and nanostructured thin film coatings. See, for example, Wu, A., et al., J. Am. Chem. Soc. 1999, 121, 4883; Onitsuka, O., et al., Biosens. Bioelectron. 1994, 9, 677; Decher, G. and Schlenoff, J. B., Multilayer Thin Films: Sequential Assembly of Nanocomposite Materials, Vch Verlagsgesellschaft Mbh, 2003; and Decher, G, Science 1997, 277, 1232, each of which is incorporated by reference in its entirety. The layer by layer (LbL) deposition process provides a means to create multilayer films one molecular layer at a time. Although the polyelectrolytes are sequentially adsorbed during LbL assembly, the internal structure of the assembled multilayer is highly interpenetrated (see, for example, Mendelsohn, J. D., et al., Langmuir 2000, 16, 5017, which is incorporated by reference in its entirety). The multilayer assembly is driven by electrostatic interactions between the oppositely charged polyelectrolytes. LbL systems, for example poly(acrylic acid) (PAA) and poly(allylamine hydrochloride) (PAH), can provide control over the physical and chemical state of the assembled films. Parameters such as charge density, bilayer thickness, molecular conformation and the degree of the interchain ionic bonding can be varied (see, for example, Park, S. Y., et al., Langmuir 2002, 18, 9600, which is incorporated by reference in its entirety).
The pores can be loaded with drug molecules or electrically responsive molecules. In the former case, changes in the optical properties of the dielectric mirror can be used to monitor the loading and/or release of biomaterials such as DNA or drugs as has been demonstrated in porous silicon based reflectors. See, for example, Chan, S.; et al., Mater. Sci. Eng. C 2001, 15, 277; and Lin, V. S.-Y.; et al., Science 1997, 278, 840, each of which is incorporated by reference in its entirety. Using multilayers, the rate of release of a drug through the heterostructure can be controlled by the choice of barrier layers, their thickness and the sequence in the heterostructure. Liquid crystals loaded into the pores provide a means to vary the refractive index of the porous PAH/PAA blocks with application of an electric field, thereby producing a dynamically tunable Bragg reflector.
Polymer-dispersed liquid crystal (PDLC) films are most often prepared by emulsion or phase separation procedures in which droplet morphology is poorly controlled (see, for example, Kitzerow, H.-S., Liq. Cryst., 1994, 16, 1, which is incorporated by reference in its entirety). Most liquid crystals are organic, rod-like shaped molecules, several nanometers in length and a few angstroms in diameter. Because of this elongated shape and polarizability, the liquid crystal molecule has an anisotropic refractive index. The optical anisotropy of liquid crystal molecules is the basis for LC displays. The macroscopic properties of the liquid crystals can be changed readily by external stimuli. A strong molecular dipole moment can allow the long axis of the molecule to align with an applied field. In the voltage-off state, the refractive index of each liquid crystal domain depends on the domain size (see, for example, Park, N.-H., et al., Colloid Polym Sci., 2001, 279, 1082; and Ren, H-W. and Wu, S-T. Applied Physics Letter, 2002, 81(19), 3537, each of which is incorporated by reference in its entirety). As the voltage increases, the refractive index of each domain decreases and the size dependent profile of the refractive indices is flattened. When the LC molecules are ordered, liquid crystal domains exhibit different refractive indices along the parallel and perpendicular axes (see, for example, Fergason, J. L. Scientific American 1964, 211, 77; Kahn, F. J. Physics Today 1982, 70, 66; and Macrelli, G. Solar Energy Materials and Solar Cells, 1995, 39, 123). Using Mie theory for guidance, the refractive index mismatch, concentration, shape and particle size can all influence the amount of light scattering observed (see Morrison, I. D.; Ross, S. Colloidal Dispersions, Wiley-Interscience, 2002; Chapter 1). An increase in diameter from 50 nm to 2 μm results in a six order of magnitude increase in the scattered-light intensity. Size distribution effects are also observed. PDLC devices with LC droplets of 2-3 μm diameters offer the best electro-optical properties, owing to the balance between transmittance and scattering of incident light by LC droplets of that size (see Decher, G., Science 1997, 277, 1232).
A microporous film can be created simply by immersing multilayer thin films of the weak polyelectrolytes PAA and PAH in an acidic solution (pH 2.4) for 2-24 hrs and rinsing with deionized water (pH=5.5) for about 15 seconds (see, for example, Hiller J., et al., Nature Materials 2002, 1, 59; and Mendelsohn, J. D., et al., Langmuir 2000, 16, 5017, each of which is incorporated by reference in its entirety). These microporous films can be loaded with the liquid crystal mixtures E7 and BL037, resulting in tunable optical materials. A light shutter is one application of the electrically induced transmittance effect exhibited by the LC-loaded microporous films.
Microporosity in polyelectrolyte multilayers can be introduced by a low pH solution treatment. See Mendelsohn, J. D.; et al., Langmuir 2000, 16, 5017, which is incorporated by reference in its entirety. A number of other strategies have been developed for creating both micro- and nanoporous multilayer films (see, for example, Kim, B. Y.; and Bruening, M. L. Langmuir 2003, 19, 94; and Fu, Y.; et al., Macromolecules 2002, 35, 9451; each of which is incorporated by reference in its entirety). Certain multilayer assemblies based on weak polyelectrolytes, such as, e.g., poly(acrylic acid) (PAA) and poly(allylamine hydrochloride) (PAH), can undergo a phase separation process at low pH that produces either micro- or nanoporous material depending on the treatment conditions. In addition, these transitions to the porous state can be completely and repeatedly reversed by treatment at a higher pH. A pH-gated change in the degree of ionization of the PAA chains can drive these transitions.
It is possible to fabricate polyelectrolyte multilayer heterostructures including multiple nanoporous and solid regions. The spatial arrangement and thickness of different regions can be controlled at the molecular level through the layer-by-layer dipping process (see, for example, Wang, T. C.; et al., Adv. Mater. 2002, 14, 1534, which is incorporated by reference in its entirety). The nanopores can be opened and closed by using simple pH treatments. Reversible pH-gated nanoporosity transitions can be induced in polyelectrolyte multilayers. The multilayers can include a non-pore-forming region. The non-pore-forming region can be adjacent a pore-forming region. Multiple non-pore-forming regions can be adjacent to a pore-forming region. Reversible porosity transitions can occur in a pore-forming region when it is sandwiched between non-pore-forming regions. The nanopores of complex thin film heterostructures can be filled with non-ionic small molecules through a simple infiltration process. These structures can be useful in, for example, tunable dielectric mirrors (Bragg reflectors), electro-optical shutters, pH-gated dielectric mirrors, vapor sensors, and drug delivery systems.
Poly(acrylic acid) (PAA) (MW=90,000 g/mol) was obtained from Polysciences as a 25 wt % aqueous solution and poly(allylamine hydrochloride) (PAH) (MW=70,000 g/mol) from Aldrich Chemicals. Polyelectrolyte deposition baths were prepared at 10−2 M (based on the repeat unit molecular weight) using 18 MΩ Millipore water whose pH was adjusted with 1M HCl or NaOH. The liquid crystal materials E7 (no=1.52, ne=1.74), a eutectic mixture of cyanobiphenyls and a cyanoterphenyl, and BL037 (no=1.52, ne=1.81), 4-pentyl-4′-cyanobiphenyl, were purchased from Merck Ltd. All chemicals were used without further purification.
The multilayer thin films were deposited via an automated dipping procedure using an HMS programmable slide stainer from Zeiss, Inc. Clean indium tin oxide coated glass slides (ITO, surface resistivity 20 Ω) were immersed in a polyelectrolyte solution (PAH first, pH 8.5) for 15 minutes followed by rinsing in three successive baths of water (pH=5.5) with light agitation, for 2, 1, and 1 minutes, respectively. The substrates were immersed into the oppositely charged PAA polyelectrolyte solution (pH 3.5) for 15 minutes and subjected to the same rinsing procedure. After the desired number of layers had been deposited on ITO-coated substrates, the substrates were blown dry with air, and placed in an 80° C. oven for 1 hour. The polyelectrolyte multilayer film on the side of the glass not coated with ITO was removed by 1.0 M HCl solution. To make the microporous structure, multilayer substrates were immersed in an acidic solution (pH 2.4) for 2-24 hrs, rinsed with deionized water (pH=5.5) for about 15 seconds, blown dry and then oven dried at 80° C. for 1 hour. Total pore volumes were estimated from measurements of the thickness increase of the film. Thickness measurements were performed on dried films by profilometry. For surface characterization, an atomic force microscope (Digital Instruments Dimension 3000 Scanning Probe Microscope, Santa Barbara, Calif.) was used in tapping mode. Scanning electron microscopy was performed on a JEOL 6320 FESEM with an acceleration voltage 5 kV. For cross section imaging, the microporous multilayer film on the glass slide was scored and fractured at room temperature. The fracture surface of the polymer film was coated with 100 Å Au/Pd by vapor deposition.
The microporous voids were filled with nematic liquid crystal through capillary action. The liquid crystal was allowed to fill the microporous structure for 30 minutes. The LC-loaded devices were heated at 120° C. oven for 2 hours to crosslink the polyelectrolyte multi layer.
UV-visible measurements were performed with an Oriel Model 68806 power supply with a 75 W arc lamp and multispec detector. Instaspec software was used to display the data. The electro-optical properties were investigated at room temperature (25° C.). The relaxation measurements were performed by monitoring transmitted light intensity of a probe light from a diode laser (630 nm). Electro-optical measurements were performed by using a combination of a function generator and an AC high voltage amplifier.
Infrared measurements using a Hewlett-Packard 4284A equipped with a Nicolet spectrometer were performed to examine the electrodynamic responses of the liquid crystalline material devices to perturbations imposed by an electric field. A spectrum of the E7-filled device at 0 V was used as the background and the field response data were computed and presented as the difference spectra. The spectral resolution of the scans was 4 cm−1 and the spectral range was limited to 2200-3500 cm−1 due to the absorbance of indium tin oxide. To apply a voltage across the device, a DC power supply with an output range of 0-100 V was used.
PAH/PAA multilayer films were deposited under the conditions of pH 8.5 for the PAH deposition bath and pH 3.5 for the PAA deposition bath (denoted as 8.5/3.5 PAH/PAA). Under these conditions, 8.5/3.5 PAH/PAA multilayers form with weakly ionized PAA chains depositing onto nearly fully charged PAH surfaces. The molecular organization of these 8.5/3.5 PAH/PAA multilayers can be manipulated to produce a microporous morphology (see Mendelsohn, J. D. et al., Langmuir 2000, 16, 5017). The transition is induced by exposing the film to acidic aqueous solutions at pH 2.4. The low-pH environment of the transformation bath can cleave interchain ionic bonds by the protonation of carboxylate groups, allowing localized reorganization and phase separation of PAH/PAA multilayer films from the acidic water. The films increased in thickness upon exposure to low pH. This thickness change was coupled to the emergence of the highly porous structure. Longer exposure to acidic conditions can lead to greater porosity and larger pores. The thickness continued to increase with acid exposure time up to 24 hours. The dry thicknesses of the porous multilayers were in the range 1.0-6.0 μm, where the corresponding fully dense precursors were 0.3 to 1.8 μm thick. The RMS roughness of the acid-treated films was similarly quite high, reaching up to 350 nm for a 120.5 bilayer film compared to a roughness value of 115 nm in the untreated film.
The stable microporous structure revealed in
Conformal thin coatings thus can be reversibly cycled between fully dense and microporous states. As shown in
The microporous devices were filled with nematic liquid crystal by capillary action (see
Configuration of LC molecules in liquid crystal domains depends on the size and shape of the domains, surface anchoring, and applied fields. Alignment of the LC molecules along an applied electric field decreased the refractive index in that direction to a value close to that of the polymer matrix. This refractive index matching in the on state induced transparency in otherwise opaque films. Strong scattering in the off state can give rise to higher optical contrast. Off state scattering was increased by increases in niso of the LC, the film thickness, the volume fraction of LC domains, and optimizing the domain size relative to the wavelength of incident light. Both AC and DC voltage can operate the devices. AC can be preferable for minimizing electrochemical degradation of the LC.
Measurements of optical transmission through the films as a function of applied electric field were recorded.
An E7-filled 241 bilayer microporous device was sandwiched between two ITO electrodes and studied using FTIR spectroscopy. This measurement was used to examine the electrodynamic responses of liquid crystal domains to perturbations imposed by an electric field. The IR beam was incident in a direction parallel to that of the applied electric field and thus the liquid crystal oriented along the same direction as the propagation of the incident IR beam. A series of difference spectra, measured as a function of the applied potential, is shown in
Optical contrast ratio (CR) is often used for describing the usefulness of optical shutters. The contrast ratio is defined as CR=Ton/Toff, where Ton and Toff stand for the integrated transmittance in the range of 350 nm ˜800 nm with and without external electric field, respectively.
Light scattering from the device can increase with the film thickness because of higher effective concentration of LC and the higher probability of multiple scattering. Light scattering can be highest when the LC domain size approaches the wavelength of the incident light.
PAH (Mw=70,000) and SPS (Mw=70,000) were obtained from Sigma-Aldrich (St. Louis, Mo.). PAA (Mw=90,000) was obtained from Polysciences (Warrington, Pa.). All the chemicals were used as received. Deionized water (>18 M□ cm, Millipore Milli-Q), with an unadjusted pH of approximately 5.5, was exclusively used in all aqueous solutions and rinsing procedures. Liquid crystal E7 was purchased form EM Industries, Inc.
Polyelectrolyte multilayers (PEMs) were assembled on glass microscope slides, 3-aminopropyltriethoxysilane coated microscope slides (LabScientific, Inc.) or polished single-crystal silicon wafers (<1100>) using an automated Zeiss HMS slide stainer as previously described (see Shiratori, S. S.; and Rubner, M. F. Macromolecules 2000, 33, 4213, which is incorporated by reference in its entirety). Silicon wafers and glass substrates were degreased in a detergent solution followed by deionized water rinses prior to multilayer assembly. Silane coated microscope slides were used as received.
PAH/PAA blocks were built using pH 8.5 (±0.01) PAH (10−2 M by repeat unit) and pH 3.5 (±0.01) PAA (10−2 M) aqueous solutions which were pH adjusted by using either 1 M NaOH or 1 M HCl. Briefly, PEMs on glass slides and silicon wafers were formed by first immersing substrates into the PAH solution for 15 minutes followed by one 2 minute and two 1 minute immersions into water as rinsing steps. Then, the substrates were immersed into the PAA solution for 15 minutes followed by identical rinsing steps. The adsorption and rinsing steps were repeated until desired numbers of bilayers were obtained. One bilayer is defined as a single adsorption of a polycation followed by an adsorption of a polyanion; thus a half-integer number of bilayers of PAH/PAA ends with PAH as the outermost layer.
Thickness was measured using ellipsometry (Gaertner) from films on silicon wafers at wavelengths of 633 nm and from films on silicon wafers and glass by profilometry (Tencor P10). AFM characterization (Digital Instruments Dimension 3000 Scanning Probe Microscope) was performed in tapping mode with Si cantilevers. Near-normal reflectivity (fixed 7° off normal to the plane of the film) from one side of a substrate was measured on a Cary SE ultraviolet/visible/near-infrared spectrophotometer. The film on the other side of the substrate was removed and replaced with a black backing material.
The refractive index of the porous PAH/PAA blocks with air or liquid filled pores was estimated using an effective medium approximation (see, for example, Romanov, S. G.; et al., Physical Review E 1999, 63, 056603; and Sareni, B.; et al., J. Appl. Phys. 1996, 80, 1688, each of which is incorporated by reference in its entirety).
nf=Vp*n1+(1−Vp)*ns Eq. 1
Vp=(H−H0)/H Eq. 2
In Eq. 1, nf is the effective value of refractive index for the air- or liquid-filled, porous PAH/PAA blocks; n1 is the known refractive index of the air or infiltrated liquid, and ns is the refractive index of a fully dense PAH/PAA block. Vp is the pore faction of the porous PAH/PAA block. H0 and H are the block thickness before and after porosity transitions, respectively. This approximation was used to obtain an effective refractive index of the PAH/PAA blocks in Bragg reflectors and vapor sensors. Index values calculated this way compare favorably to those obtained by means of simulation (within 5% or better).
Theoretical reflectivity responses (simulations) were calculated using the transfer matrix method attributed to Abeles (see Abeles, F.; Ann. Phys. 1950, 5, 596, which is incorporated by reference in its entirety). The optical response of an interference filter is dependent upon the refractive index and thickness of each region in the structure. In the simulations, the thicknesses of both the porous and non-porous regions, as well as the refractive index of the non-porous regions were known. Because the experimental reflectance data revealed the location of the maximum Bragg reflectance, the Bragg Equation could be used to solve for the unknown refractive index of the porous regions. In order to produce the theoretical spectral responses in this paper, the matrix method was implemented in MATLAB. As described by Hecht, the thicknesses and refractive index data were used to create a unique 2 by 2 matrix for each region in the structure (see Hecht, E. Optics; 4th ed.; Pearson Addison Wesley: Reading, Mass., 2001, which is incorporated by reference in its entirety). These 2 by 2 matrices were subsequently multiplied together in the order they appeared to create a total transfer matrix for the entire structure. A straightforward equation was then used to derive theoretical reflectance values from the entries of the total transfer matrix. Because the entries of each matrix were dependent upon the wavelength of the incident light, the above procedure was repeated multiple times over a range of wavelengths to give theoretical reflectance vs. wavelength plots.
In the experiments on vapor detection, a cross-linked film was put into a closed quartz spectrophotometer cell with air inside. The transmittance spectrum was obtained on a Cary 5E ultraviolet/visible/near-infrared spectrophotometer. The film was then put into a closed quartz spectrophotometer cell with a saturated analyte vapor. The transmittance of the film was measured at the wavelength of the reflection band until it reached an asymptotic upper limit. Both the film and the spectrophotometer cell were dried in vacuum before use with another analyte.
Polyelectrolyte multilayers constructed from PAH and PAA can exhibit reversible, pH-driven morphological reorganizations leading to the formation of micro- and nanoporous films. For example, multilayers assembled with the PAH dipping solution at a pH of 7.5 and the PAA dipping solution at a pH of 3.5 (7.5/3.5 PAH/PAA) form micropores after a brief exposure to a pH 2.4 aqueous solution, while 8.5/3.5 PAH/PAA multilayers form nanopores after immersion in a pH 1.8 aqueous solution. In both cases, a final brief rinse in water completes the porosity transformation. Multilayer heterostructures having porosity forming regions sandwiched between (or constrained by) non-porosity forming regions can be made. The pore-forming regions can include PAH/PAA bilayers, and the non-pore-forming regions can include PAH/sulfonated polystyrene (SPS) bilayers.
An 8.5 bilayer of 8.5/3.5 PAH/PAA structure was surface capped with 25 bilayers of PAH/SPS (denoted as (PAH/PAA)8.5-(PAH/SPS)25). Ellipsometry measurements revealed that the PAH/PAA and PAH/SPS blocks in the fully dense structure were 86 nm and 47 nm thick respectively, and the average refractive index of the film was 1.55. The film was immersed for 30 seconds in a pH 1.8 acidic solution followed by a 15 second rinse in deionized water (pH 5.5), conditions previously found to create nanopores in 8.5/3.5 PAH/PAA multilayers. After the treatment, multiple macroscopic cracks were observed on the film surface, most likely induced by an uncontrolled swelling of the underlying PAH/PAA block, which in turn generated fractures in the less swellable outermost PAH/SPS block. In contrast, no cracks were observed when a (PAH/PAA)8.5-(PAH/SPS)25 film was treated with a pH 2.2 acidic solution for one minute followed by a one minute rinse in deionized water. In this case, a more controlled swelling of the underlying PAH/PAA block eliminated the formation of cracks in the PAH/SPS surface block. After this treatment, the total dry film thickness increased from 133 to 230 nm while the average refractive index decreased from 1.55 to 1.38. During the fabrication process, the PAH/SPS block was assembled at pH 4.0 with both polymers in their fully ionized form. This bilayer system swells slightly in acidic solution and collapses back to its original thickness and refractive index (1.55) in the dry state (see, for example, Hiller, J. Ph.D. Thesis, Massachusetts Institute of Technology, 2003, which is incorporated by reference in its entirety). Thus, the change in dry thickness observed after treatment is the result of a change in the PAH/PAA block. All of these observations suggest that the film thickness change is due to the formation of pores selectively in the PAH/PAA block.
The surface of the pH 2.2 treated (PAH/PAA)8.5-(PAH/SPS)25 film was examined using atomic force microscopy (AFM) (
The pH of the porosity inducing treatment and the thickness of an adjacent non-porosity forming block can influence the properties and microstructure of the final multilayer film. Thus, the treatment needed to create nanopores within confined regions of a multilayer film must be optimized for the particular heterostructure under consideration. It can be preferable to avoid the formation of micropores without destroying or disrupting the heterostructure organization by, for example, uncontrolled swelling. The number and sequence of PAH/PAA and PAH/SPS bilayers, the pH of the acid treatment solution, and the immersion time in the acid and rinse solutions can be important parameters that need to be considered.
A series of films including 1-10 bilayers of PAH/PAA sandwiched between two 50-bilayer PAH/SPS blocks was fabricated. Two different treating solutions (pH 2.3 and pH 2.2) were used to induce porosity in the PAH/PAA regions. The sandwich structures—(PAH/SPS)50-(PAH/PAA)m-(PAH/SPS)50 (m=1, 1.5, 2, 2.5, 3, 3.5, 4, 4.5, 5, 5.5, 6, 7, 8, 9, 10)—were immersed in a pH 2.3 acidic solution for one minute followed by a one minute rinse in deionized water. The (PAH/SPS)50-(PAH/PAA)7-10-(PAH/SPS)50 films turned cloudy after this treatment, suggesting that a high level of micropores was generated in heterostructures with the thickest PAH/PAA blocks (m=7, 8, 9, 10). Heterostructures with fewer than 7 PAH/PAA bilayers, on the other hand, were essentially transparent after treatment indicating that physical constraints caused by the surrounding PAH/SPS blocks can influence the length scale of porosity development in the PAH/PAA layers. Without the PAH/SPS blocks, the PAH/PAA bilayers would form micropores under these conditions.
(PAH/SPS)50-(PAH/PAA)m-(PAH/SPS)50 (m=1, 2, 3, 4, 5, 6, 7, 8, 9, 10) films were also treated with a one minute immersion in a pH 2.2 aqueous solution followed by a one minute water rinse. In this case, all films remained clear after the treatment suggesting that a stronger driving force for phase separation (due to a lower pH) produces a smaller fraction of micropores within the nanoporous structure. The thickness change of the PAH/PAA blocks induced by this treatment is also presented in
The fact that all multilayer heterostructures with 1 to 2.5 bilayers of PAH/PAA did not undergo the porosity transition indicates that interpenetration of the polymer chains nearest to the PAH/SPS blocks is preventing the phase separation process from taking place. The polymer chains in polyelectrolyte multilayers are well interpenetrated. See, for example, Baur, J. W.; et al., Langmuir 1999, 15, 6460; Joly, S.; et al., Langmuir 2000, 16, 1354; and Decher, G. Science 1997, 277, 1232, each of which is incorporated by reference in its entirety. Best estimates for PAH/PAA-PAH/SPS heterostructures are that a single polymer chain penetrates into 1 to 2 surrounding bilayers. To estimate indirectly how much interpenetration occurred at the interface of a PAH/PAA and PAH/SPS block, the thickness change of a film comprised of 1 to 9-bilayers of PAH/PAA assembled onto a PAH/SPS block with 50-bilayers was examined by using profilometry and confirmed by ellipsometry. Thickness measurements were made after a 30 second immersion in a pH 1.8 solution followed by a 15 second water rinse. A pH 1.8 acidic solution was used to ensure that only nanopore formation occurred in the PAH/PAA bilayers. As shown in
The selective introduction of nanoporosity in multilayer heterostructures can lower the refractive index of the pore-forming regions. Reflectivity measurements coupled with suitable modeling can be used to determine the refractive index of both the pore-forming and non-pore-forming regions. A multiblock stack comprised of alternating regions of high and low refractive index is the simplest example of a one-dimensional photonic structure. With suitable block thicknesses, multilayer heterostructures exhibit reflectivity bands in the visible region of the spectrum, i.e., they behave as dielectric mirrors. The optical behavior of the dielectric mirror depends upon the refractive index and thickness of each block in the structure. According to Bragg's law, the first order reflected wavelength of a film with such a periodic index profile is given as:
□1=2(n1d1+n2d2) Eq. 3
where □1 is the first order reflected wavelength and n1 and n2 are the refractive indices of the alternating blocks, and d1 and d2 are the and thicknesses of the alternating blocks (see Alfrey Jr, T.; et al., Polym. Eng. Sci. 1969, 9, 400, which is incorporated by reference in its entirety). The refractive index of the porous blocks can be estimated by putting experimental data, including the first order reflected wavelength of the film, the measured thickness and the known refractive index of the nonporous blocks, and the measured thickness of the porous blocks into Eq. 3. Further, a comparison of simulations of the reflectivity curves with the experimental results can be used to confirm the results of this calculation. Theoretical reflectivity curves were calculated using the transfer matrix method.
Using this approach, the refractive index of the porous PAH/PAA block in (PAH/SPS)50-(PAH/PAA)m-(PAH/SPS)50 heterostructure films with m=3, 4, 5, 6 was calculated to be 1.24, 1.19, 1.16 and 1.15 respectively (pH 2.3 treatment)
As the number of PAH/PAA bilayers increases, the peak of the reflectance band shifts to longer wavelengths and increases in intensity. The band shift is a result of the thickness increase and index change of the PAH/PAA blocks, whereas the intensity increase is due to a decrease in the refractive index of the PAH/PAA block. The apparent refractive index of the PAH/PAA block decreased with increasing number of bilayers because of layer interpenetration that occurs at the PAH/PAA-PAH/SPS interface. The estimated refractive index of the PAH/PAA block is an average of the refractive index of the non-porous, interpenetrated PAH/PAA bilayers and the porous PAH/PAA regions. The contribution of the non-porous bilayers to this average becomes less important as the total thickness of the PAH/PAA block increases.
The combination of experimental data and theoretical simulations of the sandwich structures of
Bragg Reflectors
Dielectric mirrors can be made by introducing nanoporosity controllably in select regions of a multilayer heterostructure. The dielectric mirror can have any desired optical profile over a wide range of the electromagnetic spectrum. Porosity-inducing treatment pH and time can be design factors in the fabrication of multilayer heterostructures containing multiple alternating porous and nonporous regions. For example, a multilayer heterostructure having five alternating heterostructure regions in the following sequence: (PAH/SPS)50-[(PAH/PAA)6-(PAH/SPS)50]5 was made. In this film, the thicknesses of the PAH/SPS and PAH/PAA blocks before porosity treatment were 112 nm and 61 nm, respectively. The porosity forming treatment involved immersing the film in a pH 2.3 solution for 3 minutes followed by a 3-minute water rinse and air dying. The two-step porosity formation treatment cycle was repeated three times. The final thickness of the treated film was 1257 nm. Assuming a complete and uniform transformation of the PAH/PAA regions to the nanoporous state, the thickness of each of these regions was estimated to be to 117 nm using Eq. 4:
d1=(dt−N2*d2)/N1 Eq. 4
where dt, d1 and d2 are the total thickness of the film, the porous PAH/PAA blocks, and the PAH/SPS blocks, respectively. N1 and N2 are the number of porous PAH/PAA and PAH/SPS blocks.
b shows the experimental reflectance spectrum (thick lines) of this dielectric mirror as well as the theoretical reflectance spectrum (thin lines) calculated by using the measured thickness (112 nm) and refractive index of PAH/SPS blocks (1.55) and calculated index of the porous PAH/PAA blocks (1.22, calculated using Eq. 3) and the above indicated thickness value (117 nm) for the porous PAH/PAA blocks. The simulation predicts the existence of a reflection peak at 633 nm and a maximum reflectivity of 79%. Both are in excellent agreement with the experimental results, demonstrating that with suitable treatment, dielectric mirrors with predictable optical properties can be designed and fabricated. The good agreement between the experimental data and the theoretically predicted reflectivity also suggests that each PAH/PAA region is uniformly converted into a similar state of nanoporosity (i.e., same refractive index and thickness).
The layer-by-layer processing technique allows the thickness and sequence of the various blocks present in a dielectric mirror to be easily controlled by selecting the number and types of layers deposited during assembly. See, e.g., Wang, T. C., et al., Adv. Mater. 2002, 14, 1534, which is incorporated by reference in its entirety. The position and intensity of the reflectance band (or bands) of the dielectric mirror are readily tunable by selecting the appropriate design.
a shows the reflectance curve of a dielectric stack fabricated with five PAH/PAA blocks: (PAH/SPS)50-[(PAH/PAA)4-(PAH/SPS)50]5. In this case, the as-assembled thicknesses of the PAH/SPS and PAH/PAA blocks were 112 nm and 38 nm, respectively. Using the porosity treatment outlined above, the thickness of the PAH/PAA blocks increased to 80 nm and the refractive index was calculated to be 1.24 using Eq. 3. The simulation (thin line) of this dielectric mirror is again in good agreement with the experimental results (thick line). Both show the expected shift of the reflectance peak to lower wavelength (545 nm versus 633 nm). The effective medium approximation (Eq. 1 and Eq. 2,) was also used to calculate the refractive index of the porous PAH/PAA blocks in the above dielectric mirrors and predicted similar index values within 5% (results: n=1.28 for the 6-bilayer PAH/PAA block and n=1.26 for the 4-bilayer PAH/PAA block).
A more complex dielectric mirror having a multilayer heterostructure with a Fabry-Perot optical cavity was created (see, for example, Dirr, S., et al., Adv. Mater. 1998, 10, 167, which is incorporated by reference in its entirety). The presence of such a cavity opens up a transmission window in the reflectivity band. The cavity was created by producing a thicker PAH/SPS block in the center of the film. The structure of this film is shown in
Reversible pH-Gated Nanoporosity Transitions
The nanoporosity transitions in 8.5/3.5 PAH/PAA multilayers are reversible. pH-Gated reversible nanoporosity transitions are also possible within confined PAH/PAA mutlilayers. A multilayer heterostructure was fabricated with 5 PAH/PAA blocks: [(PAH/PAA)6-(PAH/SPS)50]5. As shown in the inset of
The PAH/PAA regions of these multilayer heterostructures can be cycled repeatedly between the open and closed pore state by these pH treatments. The nanopores of a nanoporous film immersed in deionized water overnight, however, were eliminated due to a further reorganization of the polymer chains. Similar behavior is observed with both microporous and nanoporous multilayers of PAH/PAA. It is possible to regenerate the nanoporous regions by treatment in a low pH solution. For example,
Applications of Multilayer Heterostructures Containing Nanoporous Domains
The optical properties of dielectric mirrors that utilize nanoporosity transitions to create the low index blocks of a Bragg stack are highly sensitive to changes in the level of porosity. A substance that penetrates into the pores can modify the refractive index of these regions and hence the optical properties. This strong coupling between optical properties and the physical or chemical state of the nanoporous regions opens up numerous possibilities in applications such as vapor sensors, monitorable drug delivery systems, or switchable Bragg gratings (see, for example, Crawford, G. P. Optics & Photonics News 2003 54; and Pikas, D. J., et al., Appl. Phys. A 2002, 74, 767, each of which is incorporated by reference in its entirety). Various kinds of Bragg stacks have been investigated for vapor sensing. Bragg stacks based on polymer replicas of nanoporous silicon films, for example, exhibit a significant reflectance-band shift upon exposure to various solvent vapors. The shift is caused by the condensation of analyte vapors within pores and the concomitant change in the refractive index of the porous regions. See, for example, Gao, J., et al., Langmuir 2002, 18, 2229, which is incorporated by reference in its entirety.
To demonstrate this effect with polyelectrolyte multilayer Bragg reflectors, a [(PAH/PAA)8-(PAH/SPS)50]9 film was converted to the nanoporous state by alternating immersion for two minutes in a pH 2.2 and pH 9.5 solution. A higher pH rinsing solution can enhance nanopore formation in the thick PAH/PAA blocks. The film was then cross-linked by heating at 140° C. for 5 hours. The transmittance spectrum of this film is presented in
Table 1 presents the refractive index of each liquid analyte, and the transmission level and wavelength of minimum transmission resulting from exposure to each solvent. The transmittance was higher when the film is exposed to the vapor of a liquid with a higher refractive index. The better refractive index match between the pores filled with analyte liquid and the polymer matrix resulted in a lower film reflectance, leading to a higher transmittance. The distinct optical changes observed with different vapors can be used to distinguish analytes. Using the data generated from the toluene-exposed film, it was possible to confirm that the solvent vapor was in fact condensing into the pores. The refractive index of PAH/PAA regions with toluene filled nanopores was calculated to be 1.50 using the effective medium approximation (Eq. 1 and Eq. 2). Using this value in a reflectance simulation predicts a minimum transmission (76%) at 663 nm, which is in good agreement with the experimental result (77% at 658 nm). The more dramatic shift to the red observed with water (and somewhat with ethanol) can be due to a swelling of the multilayer by these more polar solvents.
The bottom portion of a thermally crosslinked multilayer heterostructure with nanoporous PAH/PAA blocks ([(PAH/PAA)8-(PAH/SPS)50]3) was immersed into E7 liquid crystal. After a short period of time, the liquid crystal infiltrated the pores by a wicking effect. This process could be easily monitored by observing the film under a UV lamp. As the fluorescent liquid crystal diffused through the multilayer film, the film became fluorescent. The reflectivity of the film also changed dramatically as the liquid crystal filled the pores and modified the refractive index of the PAH/PAA regions.
The average/isotropic refractive index of the liquid crystal is 1.62. The average refractive index of the PAH/PAA regions therefore increases when the pores are filled, thereby reducing the index contrast between the PAH/PAA and PAH/SPS regions. The refractive index of E7-filled PAH/PAA blocks was calculated to be 1.57 using the effective medium approximation (Eq. 1 and Eq. 2) and a theoretical simulation of the reflectivity curve of the E7 loaded film (see
To demonstrate that non-ionic small molecules can be loaded into the porous regions of multilayer films, we utilized the well-known liquid crystal E7 (a eutectic mixture of 4-cyano-4′-n-alkylbiphenyls). To accomplish this, the bottom portion of a thermally crosslinked multilayer heterostructure ([(PAH/PAA)8-(PAH/SPS)50]3) deposited onto a glass slide was simply immersed into the liquid crystal. After a short period of time, the liquid crystal was observed to infiltrate into the film by a wicking effect as shown in
Another application of loaded porous multilayer films is controlled drug delivery. Crosslinked heterostructure-films were constructed and immersed into an organic solution containing a drug. The drug wicked up the porous layers in the film as could be monitored by the change in reflectance of the film. The controlled release of the drug in a buffer solution was observed by monitoring the absorbance change of the buffer solution. An example of these experiments is shown in
Loading and Releasing of Cytochalasin D
Cytochalasin D was loaded into porous multilayer films by wicking it up in a solution of dimethyl sulfoxide (DMSO). The films consisted of alternating blocks of nonporous (poly(allyl amine hydrochloride) (PAH)/poly(sodium 4-styrene-sulfonate) (SPS)) multilayers and porous (PAH/polyacrylic acid (PAA)) multilayers. A PAH/SPS block consisting of 101 layers was built first on the substrate (PAH as the first layer). The substrate consisted of either a glass microscope slide or silicon wafer. For deposition, the pH of both the PAH and the SPS solutions was adjusted to 4.0, and both solutions contained 0.1 M NaCl. After the first PAH/SPS block, the PAH/PAA block, which consisted of either 10 or 16 layers, was constructed on top (PAA as the first layer). For this block, the PAA solution was adjusted to pH 3.5 and the PAH solution was adjusted to pH 8.5. Afterwards alternating blocks of PAH/SPS (100 layers) and PAH/PAA (10 or 16 layers) were constructed so that the film contained 3, 7, or 11 total blocks. The PAH/PAA blocks were made porous by treatment in a pH 2.3 or pH 2.4 aqueous bath and then subsequent treatment in pH 5.5 water. Heating the films to 180° C. for 2 hours locked in the structure. The cytochalasin D was wicked into the films in either a 0.2 mg/mL or 1.0 mg/mL DMSO solution.
The release of this compound was studied by monitoring the release into a buffer solution using UV-Vis spectroscopy to observe the change of absorbance of the solution with time. The loaded films showed a linear release profile over a span of one month. The effects of cytochalasin D on murine wild type (WT) NR6 fibroblasts was studied by growing the cells on top of the loaded films. The WT NR6 fibroblasts were cultured in pH 7.4 modified Eagles medium-α (MEM-α) with 7.5% (v/v) fetal bovine serum (FBS), 1% (v/v) sodium pyruvate (100 mM), 1% (v/v) nonessential amino acids (10 mM), 1% (v/v) Geneticin (G418) antibiotic (350 μg/10 mL PBS), 1% (v/v) L-glutamine (200 mM), 1% (v/v) penicillin (10,000 U/mL), and 1% streptomycin (10 mg/mL). Cells were kept in a humid incubator at 37.5° C. and 5% CO2. Cytochalasin D inhibits cells from dividing during mitosis, which results in multinucleated cells with different morphology from normal ones. The cells were affected by the cytochalasin D, meaning it was successfully delivered to them, as confirmed by optical microscopy.
Loading and Releasing of Ketoprofen
Ketoprofen was loaded into porous multilayer films by wicking it up in a DMSO solution. The films were constructed in the same manner as described in the cytochalasin D example above. The ketoprofen was wicked into the films in either a 0.2 mg/mL or 10 mg/mL DMSO solution. The release of this compound was followed by using UV-Vis spectroscopy to observe the change of absorbance of the solution with time. Like cytochalasin D, a linear release was observed.
Loading and Releasing of Other Compounds
A variety of other compounds, including hormones, antibiotics, anti-inflammatory and anti-tumor compounds, were loaded in porous multilayer films. Beta-estradiol, progesterone, camptothecin, indomethacin, ampicillin, and a mixture of penicillin, neomycin and streptomycin were each wicked into the films in either a 0.2 mg/mL or 10 mg/mL DMSO solution. The compounds are released from the films. Films that release antibiotics kill bacteria, such as E. coli or S. epidermis.
Ionic Liquids
Other applications of loaded porous multilayer films are solar cells and batteries made by loading ionic liquids into the pores. The conductive properties of ionic liquids make them a very attractive research topic, but their physical properties make them difficult to work with since they often leak out of devices. After wicking the ionic liquid, 1-ethyl-3-methyl imidazolium trifluromethane sulfonate, into the porous multilayer film, the multilayers acted as a container for the ionic liquid and did not allow it to escape. The conductivity of the device was about 10−5 S/cm, which is within an order of magnitude of the original liquid ionic conductivity of 10−4 S/cm. We can control this conductivity by changing the pore density with different pH conditions as explained by percolation theory. This technique could have an immense impact on electro-optical as well as energy storage devices.
Other embodiments are within the scope of the following claims.
The U.S. Government may have certain rights in this invention pursuant to Grant No. 94-00224 awarded by MIT MRSEC and Grant No. 972-02-1-0016 awarded by DARPA.