Porously coated open-structure substrate and method of manufacture thereof

Abstract
A method for sintering a porous coating on an open-structure substrate, i.e., a substrate with pre-made pores or openings. The open-structure substrate is spread with a coating paste that is prepared with such a viscosity so that the paste will not drip through the pores/openings on the open-structure substrate. The coating paste is then sintered to form a porous layer on the surface of the open-structure substrate. Optionally, the porous coating may be further coated with a catalyst for fuel cell applications.
Description




TECHNICAL FIELD




The technical field relates to a process for the fabrication of a porous coating on top of an open-structure substrate. The porously coated open-structure substrate is preferably used in fuel cell applications.




BACKGROUND




A fuel cell is an electrochemical apparatus wherein chemical energy generated from a combination of a fuel with an oxidant is converted to electrical energy in the presence of a catalyst. The fuel is fed to an anode, which has a negative polarity, and the oxidant is fed to a cathode, which, conversely, has a positive polarity. The two electrodes are connected within the fuel cell by an electrolyte to transmit protons from the anode to the cathode.




One of the essential requirements of typical fuel cells is the easy access to the catalyst and a large surface area for reaction. This requirement can be satisfied by using an electrode made of an electrically conductive porous substrate that renders the electrode permeable to fluid reactants and products in the fuel cell. To increase the surface area for reaction, the catalyst can also be filled into or deposited onto a porous substrate.




However, these modifications result in a fragile porous electrode that needs additional mechanical support. An alternative is to sinter a porous coating on a solid substrate and then fill or re-coat the porous coating with a catalyst. The substrate can be made of conductive materials or patterned with a conductive material. The porous coating can be made of non-conductive materials, such as ceramics or silicon, or conductive materials such as carbon, ceramic-metal mixture or metals. Typically, the coating material, in the form of fine powders, is mixed with a liquid organic “binder” such as glycol to form a coating mixture. The coating mixture is spread on the substrate and is baked in an oven. The binder is burned off and the coating material is sintered on the substrate to form a porous layer. A catalyst is deposited in the porous layer to provide a large catalytic surface. The substrate is then etched from the backside to create openings so that fuel on the cathode side and oxygen on the anode side can reach the active catalytic surfaces through the openings and the porous layer. The etching process, however, is time consuming and requires specially designed machinery.




SUMMARY




A method for sintering an open-structure substrate with a porous coating is disclosed. The open-structure substrate is a substrate with pre-formed openings (i.e., preformed pores, channels, passageways, etc.), which allow liquids and gases to pass from one side of the substrate to the other side of the substrate. The method is based on the fact that a viscous solution can remain a continuous layer after being applied onto open-structure substrates, such as screens or expanded foils, without dripping through the openings of the substrate.




Briefly, for a chosen open-structure substrate, a coating paste is prepared by mixing a solid coating material with a liquid binder. The coating material and the binder is mixed at a ratio such that the viscosity of the paste is high enough to prevent the paste from dripping through the openings on the substrate. The paste is spread on the surface of the open-structure substrate, and is subjected to a heating process to remove the binder and to sinter the coating material on the surface of the open-structure substrate to form a porous coating. Since the openings on the substrate are pre-formed before the coating process, this method eliminates the expensive and time-consuming etching step after the sintering. The method can be used to manufacture electrodes for fuel cells or any other applications which require a porous coating on an open-structure substrate.




In an embodiment, the paste comprises fine metal powders, such as zinc or silver powders, a viscous binder, such as glycol, and, optionally, a flux. A flux is a reducing agent that serves to remove the oxidized surface layer of metal particles.




In another embodiment, the porous coating on the open-structure substrate may be further coated with a catalyst.




In yet another embodiment, the paste may be prepared in the form of a solgel. A solgel is prepared by peptizing a coating material, such as silicon oxide or metal oxide, with water or a water-miscible alcohol, such as methanol, ethanol, isopropanol, ethylene glycol and the like, to form a viscous polymeric sol. The viscous polymeric sol is heated at a relatively low temperature (usually less than 100° C.) to form a heat-set gel. The heat-set gel is then heated in the presence of oxygen at a temperature and for a period of time sufficient to oxidize and volatilize any remaining vapors and organic materials from the gel to form a solid porous product.











BRIEF DESCRIPTION OF THE DRAWINGS




The detailed description will refer to the following drawings, in which like numerals refer to like elements, and in which:





FIG. 1A

depicts an open-structure substrate.





FIG. 1B

depicts an open-structure substrate covered with a paste.





FIG. 1C

depicts an open-structure substrate with sintered porous coating.





FIG. 1D

depicts a porous coated open-structure substrate with optional catalyst coating.











DETAILED DESCRIPTION





FIG. 1A

shows an open-structure substrate


100


having an upper surface


102


, a lower surface


104


, and a plurality of openings


106


. The number and size of the openings


106


can be variable, so long as they provide enough permeability so that the liquid on one side of the substrate may reach the other side in sufficient quantities. The substrate


100


may be made of conductive materials, such as metal, carbon, metal-ceramic mixture, or non-conductive materials, such as glass, ceramic, flex material such as Kapton (Dupont) or Upilex (Ube), for example. A non-conductive substrate


100


may be patterned with a conductive material (not shown in the figure) for certain electrical applications.





FIG. 1B

shows the open-structure substrate


100


covered with a coating paste


120


. The coating paste


120


comprises a coating material


122


and a binder


124


. The coating material


122


may be in the form of fine particles. The diameters of the particles may vary depending on the desired porosity of the porous coating. In general, smaller particles lead to smaller pores and a larger surface area, while larger particles result in larger pores and a smaller surface area. The coating material may be carbon particles, glass beads, silicon powder, ceramic powder, metal particles, or any other material or a mixture of materials that may form a porous layer after a sintering process. Nonconductive coating materials, such as silicon or ceramic, may be pre-coated with a thin layer of conductive material, such as zinc, before sintering so that the final coating would be conductive.




Metals that are used for the porous coating are not limited to specific kinds. The following substances may be preferably used: Ni, Cu, Al, Fe, Zn, In, Ti, Pb, V, Cr, Co, Sn, Au, Sb, Ca, Mo, Rh, Mn, B, Si, Ge, Se, La, Ga and Ir. Each metal listed above may be used in the form of oxide and sulfide thereof and a simple substance or a mixture, including compounds of these metals. The metals may be used in a powder form to increase the surface area. The peripheral surfaces of the metal powders are desired not to be convex or concave so that they do not intertwine one another. Thus, the metal powders are preferably spherical, dice-shaped, square piller and columner.




The temperature for sintering a metal powder should be high enough to partially melt the metal particles in order to form a sintered porous metal layer. However, overheating may completely melt the metal particles and destroy the porosity of the sintered layer. To prevent the overheating, metal particles (hereafter defined as “core particles”) may be pre-coated with a thin layer of a cover metal with a lower melting temperature. For example, copper core particles may be coated with a cover layer of zinc. The coated core particles are then sintered at the melting temperature of the cover metal. Since the melting temperature of the cover metal is lower than the melting temperature of the core metal, the core particles will not melt and will maintain the porosity of the layer after the sintering process. A similar method may also be used for sintering non-conductive coating materials (hereafter defined as “non-conductive core particles”). In this case, the non-conductive core particles may be pre-coated with a layer of cover material having a melting temperature lower than that of the core particles, and sintered at the melting temperature of the cover material.




The binder


124


may be glycol, wax, a solvent, or any other viscous liquid that is evaporable during the sintering process.




The binder


124


and the coating material


122


are mixed at a ratio that results in a paste


120


with a viscosity high enough to prevent the paste


120


from dripping through the openings


106


on the substrate


100


.




The paste


120


is then applied to the upper surface


102


of the open-structure substrate


100


to form a pre-sintering coating. If the open-structure substrate


100


is patterned with a conductive layer, the paste


120


may be screen printed on the open-structure substrate


100


so that the location and shape of the sintered porous coating can conform to the patterned conductive layer.




If the coating material is metal particles, a reducing agent, called a flux, may be added to the paste to remove oxidized surface layer of the metal particles so that the particles can melt to each other during the sintering process. The choice of flux is dependent on the type of metal that needs the treatment.




The next step is to bake the paste


120


in an oven to dry out the binder


124


. As shown in

FIG. 1C

, the coating material


122


is sintered and forms a porous coating


130


on the surface of the open-structure substrate


100


after the baking process.




The baking conditions, i.e., baking time and temperature, may vary depending on the coating material


122


and the binder


124


. For metallic coating materials, the paste


120


is preferably baked under a condition that partially melts the metal particles in order to form a layer of porous metal.





FIG. 1D

shows an optional step of further depositing a layer of catalytic coating


140


on the porous coating


130


. Referring to the composition of catalytic coating for fuel cells using methanol, catalytic materials such as Pt—Ru and Pt—Ru—Os, are found to be effective in converting methanol to protons without poisoning other fuel cell constituents. If the porous coating


130


is made of conductive materials, the catalyst may be deposited onto the porous coating


130


by electroplating, electroless plating, atomic layer deposition, or any other process that is capable of coating the surface of a conductive porous layer. In this case, the porous coating


130


may function as a current collector. If the porous coating


130


is made of non-conductive materials, a conductive material may be deposited onto the surface of the non-conductive porous coating


130


by electroless plating, atomic layer deposition, or any other process that is capable of coating the surface of a non-conductive porous layer. The catalyst


140


is then deposited onto the conductive material by electroplating, electroless plating, atomic layer deposition, or any other process that is capable of coating the surface of a conductive porous layer. Alternatively, the non-conductive porous coating


130


may be directly coated with the catalyst


140


by atomic layer deposition, or any other process that is capable of coating the surface of a non-conductive porous layer.




Although preferred embodiments and their advantages have been described in detail, various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the sintering process as defined by the appended claims and their equivalents.



Claims
  • 1. A method for sintering a porous coating on an open-structure substrate comprising the steps of:selecting an open-structure substrate with openings of desired sizes, said open-structure substrate having a first side and a second side; admixing a coating material with a binder to form a paste having a viscosity high enough to prevent said paste from dripping through the openings on the open-structure substrate, wherein the coating material is non-conductive; applying the paste to the first side of said open-structure substrate to form a paste layer of a desired thickness; heating the paste layer at a sintering temperature for a period of time to form a porous coating on the open-structure substrate; pre-coating the non-conductive coating material with a conductive material by electroless plating or atomic layer deposition; and depositing a catalyst on the pre-coated non-conductive coating material by electroplating, electroless plating, or atomic layer deposition.
  • 2. A method for sintering a porous coating on an open-structure substrate comprising the steps of:selecting an open-structure substrate with openings of desired sizes, said open-structure substrate having a first side and a second side; admixing a coating material with a binder to form a paste having a viscosity high enough to prevent said paste from dripping through the openings on the open-structure substrate, wherein the coating material comprises a core particle coated with a cover layer, wherein the core particle and the cover layer each has a melting temperature, and wherein the melting temperature of the cover layer is lower than the melting temperature of the core particle; applying the paste to the first side of said open-structure substrate to form a paste layer of a desired thickness; and heating the paste layer at a sintering temperature for a period of time to form a porous coating on the open-structure substrate, wherein the sintering temperature is higher than the melting temperature of the cover layer but lower than the melting temperature of the core particle.
US Referenced Citations (10)
Number Name Date Kind
2267918 Hildabolt Dec 1941 A
3359622 Pierre Potet et al. Dec 1967 A
3607433 Isenberg et al. Sep 1971 A
3650839 Lang et al. Mar 1972 A
4043933 Breault et al. Aug 1977 A
4446210 Okada et al. May 1984 A
4847173 Mitsunaga et al. Jul 1989 A
5266177 Watanabe et al. Nov 1993 A
5521020 Dhar May 1996 A
5876867 Itoh et al. Mar 1999 A
Foreign Referenced Citations (1)
Number Date Country
0583773 Feb 1994 EP
Non-Patent Literature Citations (1)
Entry
Oguri, “Japanese Patent abstract of JP 5-155636 A”, Jun. 1993.