Patent Application
20050079419
1. Field of the Invention
The present invention relates to positive electrode active materials and, more particularly, to a surface modified positive electrode active material for use to make a positive electrode for a secondary battery to enhance the wettability between the positive electrode and the electrolytic solution so as to further improve the low temperature characteristics and stability of the secondary battery.
2. Description of the Related Art
Various rechargeable secondary storage batteries are known. The market tendency of these batteries is toward the features of relatively thinner and smaller size, relatively higher energy density, high cost-effectiveness, high safety, well environment protection, and long durability. Li-ion secondary batteries have become the mainstream in the market for the advantages of high working voltage, high energy density, light weight, and meeting 3C (Computer, Consumer and Communication) electronic products' requirements. Nowadays, Li-ion secondary batteries have been developing for use in electrical vehicles and hybrid electrical vehicles to provide a large current output. For this application, high power and broad working temperature range are required. Therefore, there is a heavy demand for secondary batteries that having low-temperature operation feature.
However, conventional Li-ion secondary batteries have a low discharging efficiency when operated at a low temperature. Because the lowering of temperature causes the viscosity of the electrolytic solution to be increased and the volume of the electrolytic solution to be reduced, the contact area between the electrodes and the electrolytic solution will be relatively reduced resulting in a great voltage drop when using a conventional Li-ion secondary battery under a low temperature environment. Current methods of improvement are to increase the low temperature conductivity of ions of the electrolytic solution, or to lower the impedance of the ions of the isolation film. However, the improvement of these methods is not significant.
Further, in addition to a high viscosity solvent such as EC (ethylene carbonates) or PC (propylene carbonates), conventional market available secondary batteries may contain additional low viscosity solvents such as DEC (Diethyl Carbonate), EMC (Ethyl Methyl Carbonate), and DMC (Dimethyl Carbonate) that lower the viscosity of the electrolytic solution to increase Li-ion transmission speed and to reduce the impedance of the secondary batteries. However, low viscosity solvents commonly have a low boiling point and low firing point, and are easy to burn and to explode, affecting the safety of the secondary battery.
In fact, the wettability between the electrodes and the electrolytic solution of the secondary battery is one of the primary factors, which affects the capacity of secondary battery. This factor, i.e. wettability, is very important for secondary battery at low temperature discharging operation. The increasing of the wettability is not only to increase the contact area between the electrodes and the electrolytic solution to improve the operation characters of the secondary battery at low temperature but also to be capable of decreasing the use of low viscosity solvents so as to improve the safety of the secondary battery.
It is the primary objective of the present invention to provide a positive electrode active material that can enhance the wettability between the positive electrode and the electrolytic solution so as to further improve the low temperature working feature of the secondary battery that uses the positive electrode active material.
It is another objective of the present invention to provide a positive electrode active material that can improve the safety of a secondary battery that uses the positive electrode active material.
To achieve these objectives of the present invention, the invention provides a positive electrode active material for use to make a positive electrode for a secondary battery having an electrically conductive electrolytic solution. The positive electrode active material comprises a positive electrode active substance and a modified layer coated on the surface of the positive electrode active substance to enhance the wettability between the positive electrode and the electrolytic solution.
The invention also provides a secondary battery, which comprises a positive electrode made of the aforesaid positive electrode active material, a negative electrode, and an isolation film and an electrolytic solution provided between the positive electrode and the negative electrode.
By means of the positive electrode active material, the wettability between the positive electrode and the electrolytic solution under normal temperature and low temperature is increased, improving the low temperature operation feature of the secondary battery. In addition, the content of solvents of low boiling point, low firing point and low viscosity in the electrolytic solution can be greatly reduced to improve the safety of the secondary battery.
The positive electrode active substance is a lithium transition metal oxide of chemical structure LixMyOz, in which M is one or more transition metals, and 0≦x≦1.15, 0.8≦y≦2.2 and 1.5≦z≦5.
The modified layer is made of one or more inorganic oxides selected from a group consisting of SiO2, SnO2, ITO, TiO2, Al2O3, MgO, TiO2, Fe2O3, B2O3, ZrO2 and Sb2O3. The modified layer is coated on the surface of the positive electrode active substance by means of solid state sintering, PVD/CVD plating, metal organic chemical sintering, chemical sol-gel diffusing, or hot dipping. The modified layer has the thickness of only one or several atomic layers without affecting the transmission speed of conducting ions.
Preferably, the material of the modified layer is comprised of nanometered particles of diameter within 100 nm, or more preferably below 30 nm, and amount below 5 mmole. Because of the advantages of small particles, broad surface area, high reactivity, being easily to be evenly spread over the surface of the positive electrode active substance and to lower the reactive sintering temperature. The heat treating temperature is preferably within 600-900° C.
In actual practice, the invention tests on a Li-ion secondary battery that comprises a positive electrode, a negative electrode, and an isolation film and an electrolytic solution provided between the positive electrode and the negative electrode. The positive electrode comprises a positive electrode active substance, which is selected from LiCoO2, LiCoOxNi1-xO2, LiNiO2, LiMnO2, LiMn2O4, LiCo1-x-yNixMnyO2, LiFePO4, V2O5, MnO2, LiTixOy, and etc.
The electrolytic solution comprises an alkali metal-based electrolyte, a hydrophobic solvent, and additives. The hydrophobic solvent is based on a first solvent of high dielectric coefficient and high viscosity added with a second solvent of low dielectric coefficient and low viscosity. The second solvent may be eliminated from the electrolytic solution.
The present invention will now be explained in more detail in the following examples.
At first, mixed respectively 0.5 mmole, 1 mmole and 5 mmole SnO2 of diameter 18 nm with 1 mole Li CoO2 in 500 mL ethanol thoroughly and then dried the solutions, for enabling SnO2 nanometered particles to be evenly spread on the surface of LiCoO2 as shown in
Thereafter, mixed 93% LiCoO2/SnO2 positive electrode active material with 4% conduction-aidant agent KS-4, 1% VGCF (vapor-grown carbon-fifer), and 4% binder PVdF (Polyvinylene Difloride), and then solved the mixture in a NMP (N-methyl-2-pryyolidone) solution-based paste, and then processed the material thus obtained into a positive electrode, and then measured the average contact angle between the positive electrode and an electrolytic solution (1.1M LiPF6, EC/PC 2/3) to be 8°, which is superior to the contact angle 18° between the surface of LiCoO2 before modification and the electrolytic solution, i.e., the wettability has been greatly improved.
At first, mixed 0.15 mmole Al2O3 of diameter 18 nm with 1 mole LiCoO2 in 500 mL ethanol thoroughly and then dried the solution, for enabling Al2O3 nanometered particles to be evenly spread on the surface of LiCoO2, and then the dried mixture undergo heat treatment at 600°, 700°, 800°, and 900° C. respectively, causing a modified layer of Al2O3 coating to be formed on the surface of LiCoO2. Thus, a LiCoO2/Al2O3 positive electrode active material was obtained.
Thereafter, mixed 85% LiCoO2/Al2O3 positive electrode active material with 10% conduction-aidant agent KS-6 and 5% binder PVdF (Polyvinylene Difloride), and then solved the mixture in a NMP (N-methyl-2-pryyolidone) solution-based paste, and then processed the material thus obtained into a positive electrode, and then measured the average contact angle between the positive electrode and the electrolytic solution (1.1M LiPF6, EC/PC 2/3) to be 14°, which is superior to the contact angle 18° between the surface of LiCoO2 before modification and the electrolytic solution.
At first, mixed 0.5 mmole Al2O3 of diameter 40 nm with 0.4 mmole SnO2 of diameter 18 nm and 1 mole Li CoO2 in 500 mL ethanol thoroughly and then dried the solution, for enabling Al2O3—SnO2 nanometered particles to be evenly spread on the surface of LiCoO2, and then the dried mixture undergo a heat treatment at 800° C., causing a uniform layer of Al2O3—SnO2 to be formed on the surface of Li CoO2. Thus, a LiCoO2/Al2O3—SnO2 positive electrode active material was obtained.
Thereafter, mixed 85% LiCoO2/Al2O3—SnO2 positive electrode active material with 10% conduction-aidant agent KS-6 and 5% binder PVdF (Polyvinylene Difloride), and then solved the mixture in a NMP (N-methyl-2-pryyolidone) solution-based paste, and then processed the material thus obtained into a positive electrode, and then measured the average contact angle between the positive electrode and the electrolytic solution (1.1M LiPF6, EC/PC 2/3) to be 13°, which is superior to the contact angle 18° between the surface of LiCoO2 before modification and the electrolytic solution.
At first, mixed 0.05 mmole MgO of diameter 20 nm with 0.045 mmole SnO2 of diameter 18 nm and 1 mole Li CoO2 in 500 mL ethanol thoroughly and then dried the solution, for enabling MgO—SnO2 nanometered particles to be evenly spread on the surface of LiCoO2, and then the dried mixture undergo a heat treatment at 800° C., causing a uniform layer of MgO—SnO2 to be formed on the surface of Li CoO2. Thus, a LiCoO2/MgO—SnO2 positive electrode active material was obtained.
Thereafter, mixed 85% LiCoO2/MgO—SnO2 positive electrode active material with 10% conduction-aidant agent KS-6 and 5% binder PVdF (Polyvinylene Difloride), and then solved the mixture in a NMP (N-methyl-2-pryyolidone) solution-based paste, and then processed the material thus obtained into a positive electrode, and then measured the average contact angle between the positive electrode and the electrolytic solution (1.1M LiPF6, EC/PC 2/3) to be 10°, which is superior to the contact angle 18° between the surface of LiCoO2 before modification and the electrolytic solution.
In addition to the aforesaid inorganic oxides of SnO2, Al2O3 and MgO and their compounds, inorganic oxides SiO2, ITO, TiO2, Fe2O3, B2O3, ZrO2, and Sb2O3, and their compounds may be used.
At first, 0.03 mmole of Sn(OC2H5) was dissolved in 300 g of isopropanol and stirred for 25 hours, and then mixed the solution thus obtained with 1 mole of LiCoO2, and then dried the mixture at 100° C., for enabling organic tin compound to be evenly spread on the surface of LiCoO2, and then heated the dried mixture at 800° C., causing a uniform layer of SnO2 to be formed on the surface of Li CoO2. Thus, a LiCoO2/SnO2 positive electrode active material was obtained.
Thereafter, mixed 85% of LiCoO2/SnO2 positive electrode active material with 10% conduction-aidant agent KS-6 and 5% binder PVdF (Polyvinylene Difloride), and then solved the mixture in a NMP (N-methyl-2-pryyolidone) solution-based paste, and then processed the material thus obtained into a positive electrode, and then measured the average contact angle between the positive electrode and the electrolytic solution (1.1M LiPF6, EC/PC 2/3) to be 10.5°, which is superior to the contact angle 18° between the surface of LiCoO2 before modification and the electrolytic solution.
Further, in addition to metal organic compound chemical sintering, chemical sol-gel diffusing, and hot dipping methods, oxide material solid sintering method or PVD/CVD coating method may be used to coat the modified layer on the surface of the positive electrode active material of a secondary battery.
The followings indicate related tests made on positive electrodes for secondary battery using surface modified positive electrode active materials according to the present invention.
Three sample secondary batteries and one reference secondary battery were respectively charged at room temperature with 0.2 C electric current, and then respectively discharged at room temperature as well as at −20° C. under working voltage within 2.75˜4.20V, in which the reference secondary battery had LiCoO2 for the positive electrode, Mesocarbon Microbeads (MCMB) for the negative electrode, and 1.1M LiPE6-EC/PC/DEC(=3/2/5) for the electrolytic solution; the sample secondary batteries had 5 mmole, 1 mmole, and 0.5 mmole SnO2 added LiCoO2/SnO2 positive electrode active material for the positive electrode respectively, MCMB for the negative electrode, and 1.1M LiPE6-EC/PC/DEC(=3/2/5) for the electrolytic solution. The test results are indicated in the following Table I and the
The test results show that adding a small mount (0.5-1 mmole) of SnO2 is helpful to improvement on low temperature performance, however greatly increasing the added amount of SnO2 (5 mmole) will reduce the low temperature capacity of the battery.
A sample secondary battery and one reference secondary battery were respectively charged at room temperature with 0.2 C electric current, and then respectively discharged at room temperature as well as at −20° C. under working voltage within 2.75˜4.20V, in which the reference secondary battery had LiCoO2 for the positive electrode, Lithium for the negative electrode, and 1.1M LiPE6-EC/PC/DEC(=3/2/5) for the electrolytic solution; the sample secondary battery had 0.9 mmole Al2O3 added LiCoO2/Al2O3 positive electrode active material for the positive electrode, Lithium for the negative electrode, and 1.1M LiPE6-EC/PC/DEC(=3/2/5) for the electrolytic solution. The test result is indicated in the following Table II and the
The test result shows that adding a small mount (0.5-1 mmole) of Al2O3 is helpful to improvement on low temperature performance.
0.5 mmole nanometered SnO2 particles of diameter 18 nm was mixed with 1 mole LiCoO2 in 500 mL ethanol solution, and then dried the solution, for enabling SnO2 particles to be evenly spread on the surface of LiCoO2, and then heated the compound at 600° C., causing a SnO2 modified layer to be uniformly formed on the surface of LiCoO2, and then mixed LiCoO2/SnO2 positive electrode active material 93% with 5% conduction-aidant agent KS-4 and 1% VGCF and 5% binding agent PVdF 5%, and then solved the mixture in NMP-based paste to form a positive electrode after through coating, drying, and ramming processes, and then the positive electrode thus obtained was used with a negative electrode and a 1.2M LiPF6, EC/PC 2/3 electrolytic solution to form a secondary battery. The secondary battery thus obtained was examined through a large current discharge test. The test result, as shown in
Further, LiCoO2 was mixed with 6% conduction-aidant agent KS-4 and 5% binding agent PVdF, and then solved the mixture in NMP-based paste to form a positive electrode after through coating, drying, and ramming processes, and then the positive electrode thus obtained was used with above-mentioned negative electrode and electrolytic solution to form a secondary battery. The secondary battery thus obtained was examined through a large current discharge test. The test result, as shown in
Therefore, a positive electrode active material-based secondary battery achieves a better performance on large current discharge.
Further, the electrolytic solution used in TEST III does not contain a low viscosity solvent, and can still effectively discharge electric energy at a low temperature. Therefore, the invention can minimize the use of low viscosity solvent to improve the safety of use of the secondary battery without sacrificing the low temperature discharge feature of the secondary battery.
In the aforesaid embodiments, SnO2 and Al2O3 are used for the modified layer for the advantage of high material safety, low material cost, and easy material obtainability. Actually, inorganic oxides of chemical formula fitting MxOy such as oxide of Mg, Ca, B, Al, Ga, In, Tl, Si, Ge, Sn, Pb, P, As, Sb, Bi, or their compound may be used to achieve the same effect.
The proportion of the modified layer of positive electrode active material can be ranged from 0.001 mmole to 5 mmole. According to tests, proportion ranging from 0.001 mmole to 1 mmole is preferable.
Although particular embodiments of the invention have been described in detail for purposes of illustration, various modifications and enhancements may be made without departing from the spirit and scope of the invention. Accordingly, the invention is not to be limited except as by the appended claims.