Patent Application
20230098411
This application claims priority to and the benefit of Korean Patent Application No. 10-2021-0129532 filed in the Korean Intellectual Property Office on Sep. 30, 2021, the entire contents of which are hereby incorporated by reference.
Embodiments of the present disclosure relate to a positive electrode active material for a rechargeable lithium battery, a method of preparing the same, and a rechargeable lithium battery including the same are disclosed.
A portable information device such as a cell phone, a laptop, smart phone, and the like or an electric vehicle has used a rechargeable lithium battery having high energy density and easy portability as a driving power source. Recently, research has been actively conducted to use a rechargeable lithium battery having high energy density as a driving power source or power storage power source for hybrid or electric vehicles.
Various positive electrode active materials have been investigated to realize rechargeable lithium batteries for application to various uses. Among them, lithium nickel-based oxide, lithium nickel manganese cobalt composite oxide, lithium nickel cobalt aluminum composite oxide, lithium cobalt oxide, and the like are mainly used as a positive electrode active material. However, these positive electrode active materials have structure collapses or cracks during or as a result of repeated charges and discharges, and thus, problems of deteriorating a long-term cycle-life of a rechargeable lithium battery and increasing resistance and thereby exhibiting unsatisfactory capacity characteristics. Accordingly, development of a novel positive electrode active material securing long-term cycle-life characteristics as well as realizing high capacity and high energy density is required.
A positive electrode active material for a rechargeable lithium battery having improved cycle-life characteristics while implementing a high capacity, a preparing method thereof and a rechargeable lithium battery including the same are provided.
In an embodiment, a positive electrode active material for a rechargeable lithium battery includes a secondary particle in which a plurality of primary particles including a lithium nickel-based composite oxide are aggregated, wherein at least a portion of the primary particles are arranged radially, a boron coating layer on the surface of the secondary particles and containing lithium borate, and a boron-doped layer inside the primary particle exposed to the surface of the secondary particle.
In another embodiment, a method of preparing a positive electrode active material for a rechargeable lithium battery includes mixing together a nickel-based hydroxide, a lithium raw material, and a boron raw material and heat-treating the resultant.
In another embodiment, a rechargeable lithium battery includes a positive electrode including the aforementioned positive electrode active material, a negative electrode, a separator between the positive electrode and the negative electrode, and an electrolyte.
The positive electrode active material for a rechargeable lithium battery according to an embodiment and a rechargeable lithium battery including the same may exhibit excellent cycle-life characteristics while realizing high capacity and high energy density.
The accompanying drawings, together with the specification, illustrate embodiments of the subject matter of the present disclosure, and, together with the description, serve to explain principles of embodiments of the subject matter of the present disclosure.
Hereinafter, example embodiments will be described in more detail so that those of ordinary skill in the art can easily implement them. However, the subject matter of this disclosure may be embodied in many different forms and is not to be construed as being limited to the example embodiments set forth herein.
The terminology used herein is used to describe embodiments only, and is not intended to limit the present disclosure. The singular expression includes the plural expression unless the context clearly dictates otherwise.
As used herein, “a combination thereof” refers to a mixture, a laminate, a composite, a copolymer, an alloy, a blend, a reaction product, and/or the like of constituents.
As used herein, “combination thereof” means a mixture, a laminate, a composite, a copolymer, an alloy, blend, a reaction product, and the like of the constituents.
Herein, it should be understood that terms such as “comprises,” “includes,” or “have” are intended to designate the presence of an embodied feature, number, step, element, or a combination thereof, but it does not preclude the possibility of the presence or addition of one or more other features, number, step, element, or a combination thereof.
In the drawings, the thickness of layers, films, panels, regions, etc., may be exaggerated for clarity and like reference numerals designate like elements throughout the specification. It will be understood that when an element such as a layer, film, region, or substrate is referred to as being “on” another element, it can be directly on the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.
In addition, the term “layer,” as used herein, includes not only a shape formed on the whole surface when viewed from a plan view, but also a shape formed on a partial surface.
In addition, the average particle diameter may be measured by any suitable method generally used in the art, for example, may be measured by a particle size analyzer, or may be measured by a transmission electron micrograph or a scanning electron micrograph. In some embodiments, it is possible to obtain an average particle diameter value by measuring using a dynamic light scattering method, performing data analysis, counting the number of particles for each particle size range, and calculating from the result. Unless otherwise defined, the average particle diameter may mean the diameter (D50) of particles having a cumulative volume of 50 volume % in the particle size distribution.
In an embodiment, a positive electrode active material for a rechargeable lithium battery includes a lithium nickel-based composite oxide, wherein the positive electrode active material includes a secondary particle in which a plurality of primary particles are aggregated together, wherein at least a portion of the primary particles is arranged radially, a boron coating layer on a surface of the secondary particles and containing lithium borate, and a boron-doped layer inside the primary particle exposed at the surface of the secondary particle.
In general, a comparative method of coating boron on a positive electrode active material is conducted by first preparing lithium metal composite oxide and then, mixing it together with a boron raw material in a wet or dry manner and heat-treating the mixture. However, the boron has a problem of acting as resistance on the surface of the positive electrode active material (e.g., the boron increases electrical resistance at the surface of the positive electrode active material), and thus, rather deteriorating capacity and a cycle-life (e.g., reduces capacity and cycle-life of the positive electrode active material). On the contrary, an embodiment of the present disclosure may provide a secondary particle-type positive electrode active material in which at least a portion of primary particles are radially arranged by adding both a lithium raw material and a boron raw material to a set positive electrode active material precursor such as a nickel-based hydroxide and/or the like and then, heat-treating the mixture under set conditions and/or the like, wherein a boron coating layer and a boron doping layer may be concurrently (e.g., simultaneously) formed in the positive electrode active material. When the boron coating layer and the boron doping layer in each suitable or appropriate amount are concurrently (e.g., simultaneously) formed, the boron may no longer act as resistance (e.g., may not act as a resistor that increases electrical resistance of the surface of the positive electrode active material) but improves structural stability of the positive electrode active material, and thus, concurrently (e.g., simultaneously) improves capacity characteristics and high-temperature cycle-life characteristics of a rechargeable lithium battery.
The boron coating layer is formed on the surface of the secondary particles and may be uniformly (e.g., substantially uniformly) coated thereon. The lithium borate of the boron coating layer may be represented as lithium boron oxide and/or lithium borate, for example, LiBO2, Li3B7O12, Li6B4O9, Li3B11O18, Li2B4O7, Li3BO3, Li8B6O13, Li5B3O7, Li4B2O5, Li10B4O11, Li8B2O7, or a combination thereof.
In the boron coating layer, a content of the lithium borate may be about 0.02 wt % to about 0.5 wt %, for example, about 0.03 wt % to about 0.4 wt %, about 0.04 wt % to about 0.3 wt % or about 0.05 wt % to about 0.2 wt %, and the like based on a total weight of the positive electrode active material. When this content range is satisfied, the boron coating layer may not act as resistance (e.g., may not act as a resistor that increases electrical resistance of the surface of the positive electrode active material) but improve structural stability of the positive electrode active material and thus cycle-life characteristics.
The boron doping layer may be formed inside the secondary particles and, for example, inside the primary particles exposed at the surface of the secondary particles. The primary particles exposed on the surface of the secondary particles may be primary particles in the outermost of the secondary particles. For example, the boron doping layer may be within a depth range of about 10 nm from the outer surface of the primary particles exposed at the surface of the secondary particles. When the outer surface of the primary particles exposed at the surface of the secondary particles is about 0 nm, the doping layer may be present within a depth range of about 0 nm to about 10 nm from the surface. In other words, the boron doping layer also may be said to be within the depth range of about 10 nm from the surface of the secondary particles. When the surface of the secondary particles is about 0 nm, the doping layer may be present within a depth range of about 0 nm to about 10 nm from the surface.
The boron doping layer may be, for example, within a depth range of about 9 nm, within a depth range of about 8 nm, within a depth range of about 7 nm, within a depth range of about 6 nm, within a depth range of about 5 nm, within a depth range of about 4 nm, within a depth range of about 3 nm, or within a depth range of about 2.5 nm from the outer surface of the primary particles exposed at the surface of the secondary particles. This boron doping layer is distinguished from the boron coating layer and also, from a grain boundary boron coating portion further described herein below and contributes to structural stability of the positive electrode active material.
In some embodiments, the positive electrode active material may further include a grain boundary boron coating portion on the surface of the primary particles inside the secondary particles and including lithium borate. Such a grain boundary boron coating portion is present in the inner portion rather than the surface of the secondary particle, and it is coated along the interface of the primary particles in the inner portion of the secondary particle. Here, the inner portion of the secondary particles means the entire interior except for the surface and, for example, may mean the entire interior from a depth of approximately 2 μm from the outer surface. It can also be expressed as an inaccessible part of distilled water when washing the secondary particles of the positive electrode active material with distilled water (e.g., a portion of the secondary particle that is not reached by distilled water when the secondary particle is washed with distilled water).
According to an embodiment, a weight of the boron coating layer may be greater than a weight of the grain boundary boron coating portion. For example, based on a total amount of the boron coating layer and the grain boundary boron coating portion, the grain boundary boron coating portion may be in a range of about 2 wt % to about 30 wt % and, for example, about 3 wt % to about 25 wt %, or about 5 wt % to about 20 wt %, and in addition, the boron coating layer may be included in a range of about 70 wt % to about 98 wt %, about 75 wt % to about 97 wt %, about 80 wt % to about 95 wt %, or the like. For example, the boron coating layer and the grain boundary boron coating portion may have a weight ratio of about 70:30 to about 98:2, for example, about 75:25 to about 97:3, or about 80:20 to about 95:5. When the boron coating layer and the grain boundary boron coating portion are included within these ratios, the boron may not act as resistance (e.g., may not act as a resistor that increases electrical resistance of the surface of the positive electrode active material) in the positive electrode active material but improve performance, improving both capacity characteristics and cycle-life characteristics of the rechargeable lithium battery at the same time.
A content of the boron coating layer, for example, a content of lithium borate of the boron coating layer based on the total weight of the positive electrode active material may be, for example, about 0.02 wt % to about 0.5 wt %, about 0.03 wt % to about 0.4 wt %, about 0.04 wt % to about 0.3 wt %, about 0.05 wt % to about 0.2 wt %, or the like. A content of the grain boundary boron coating portion, for example, a content of lithium borate of the grain boundary boron coating portion based on the total weight of the positive electrode active material may be, for example, about 0.001 wt % to about 0.05 wt %, about 0.001 wt % to about 0.04 wt %, about 0.002 wt % to about 0.03 wt %, or about 0.003 wt % to about 0.02 wt %, but is not limited thereto. When the contents of the boron coating layer and the grain boundary boron coating portion based on the total weight of the positive electrode active material are within the ranges, both the capacity characteristics and the cycle-life characteristics of the rechargeable lithium battery may be improved.
A total amount of the boron coating layer and the grain boundary boron coating portion based on the total amount of the positive electrode active material may be 0.1 mol % to 5 mol %, for example, about 0.1 mol % to about 3 mol %, about 0.1 mol % to about 2.5 mol %, about 0.1 mol % to about 2 mol %, about 0.1 mol % to about 1.5 mol %, or about 0.5 mol % to about 1.3 mol %. When the total amount of the boron coating layer and the grain boundary boron coating portion is out of a set or predetermined content, initial discharge capacity may be reduced, and cycle-life characteristics may be deteriorated. For example, when the content of the boron coating layer on the surface of the secondary particles becomes excessive, boron may work as resistance (e.g., may function as a resistor that increases electrical resistance of the surface of the positive electrode active material), and thus, greatly reduce initial discharge capacity of the rechargeable lithium battery.
In some embodiments, the positive electrode active material includes secondary particles in which at least two or more primary particles are aggregated together, and at least a portion of the primary particles have a radially arranged structure. At least some of the primary particles may have a plate shape. The plate-shaped primary particles may have a thickness smaller than a long axis length. Here, the long axis length means the maximum length with respect to the widest surface of the primary particle. For example, the primary particle may have a structure in which the length (t) in one axial direction (e.g., a thickness direction) is smaller than the long axis length (a) in the other direction (e.g., a plane direction).
In the positive electrode active material, at least a portion of the primary particles may have a radially arranged structure, and for example, long axes of the primary particles may be arranged in a radial direction.
An average length of the primary particles of the secondary particle may be about 0.01 μm to about 5 μm, for example about 0.01 μm to about 2 μm, about 0.01 μm to about 1 μm, about 0.02 μm to about 1 μm, about 0.05 μm to about 0.5 μm, or about 150 nm to about 500 nm. Here, “average length” means the average length of the long axis length (a) in the plane direction when the primary particles are plate-shaped, and when the primary particle is spherical, it means the average particle diameter.
When the primary particles are plate-shaped, an average thickness of the primary particles may be for example greater than or equal to about 50 nm, greater than or equal to about 100 nm, greater than or equal to about 200 nm, greater than or equal to about 300 nm, greater than or equal to about 400 nm, greater than or equal to about 500 nm, greater than or equal to about 600 nm, greater than or equal to about 700 nm, greater than or equal to about 800 nm, or greater than or equal to about 900 nm, and for example less than or equal to about 5 μm, less than or equal to about 4 μm, less than or equal to about 3 μm, less than or equal to about 2 μm, less than or equal to about 1 μm, less than or equal to about 900 nm, less than or equal to about 800 nm, less than or equal to about 700 nm, less than or equal to about 600 nm, or less than or equal to about 500 nm, for example about 100 nm to about 200 nm. In addition, in the primary particle, a ratio of the average thickness to the average length may be about 1:1 to about 1:10, for example about 1:1 to about 1:8, about 1:1 to about 1:6, or about 1:2 to about 1:5.
As described above, when the average length, the average thickness, and the ratio between the average thickness and the average length of the primary particles satisfy the above ranges and at least a portion of the primary particles are radially arranged, it is possible to have relatively many lithium diffusion pathways between grain boundaries on the surface side, and a large number of crystal planes capable of lithium transfer are exposed to the outside, so that lithium diffusion is improved and high initial efficiency and capacity can be secured. In addition, when the primary particles are arranged radially, the pores exposed on the surface are directed toward the center of the secondary particles, thereby promoting diffusion of lithium. Due to the radially arranged primary particles, uniform (e.g., substantially uniform) contraction and expansion are possible when lithium is deintercalated and/or intercalated, and when lithium is deintercalated, pores exist in the (001) direction (e.g., the (001) crystal plane direction), which is the direction in which the particles expand, so that they act as a buffer. In addition, due to the size and arrangement of the primary particles, the probability of cracks occurring during contraction and expansion of the active material may be lowered (e.g., reduced), and the inner pores further alleviate the volume change to reduce the cracks generated between the primary particles during charging and discharging, resulting in improved cycle-life characteristics of a rechargeable lithium battery and reduced resistance increase phenomenon.
The positive electrode active material may have an irregular porous structure in at least one selected from the inner portion and the outer portion of the secondary particle. The term “irregular porous structure,” as used herein, may refer to a structure in which the pore sizes and shapes are not regular and do not have uniformity. For example, the secondary particle may include an inner portion including an irregular porous structure and an outer portion having a radially arranged structure. In some embodiments, the primary particles in the inner portion may be arranged without regularity, unlike the primary particles in the outer portion. For example, the primary particles at the inner portion may be randomly arranged with respect to one another. The inner portion containing the irregular porous structure includes primary particles like (e.g., the same or substantially the same as) the outer portion.
A ratio of a radius of the inner portion to a radius of the secondary particle (a distance from the center to the surface of the particle) may be about 40 length % to about 60 length %, and such an area may be defined as an inner portion. For example, the inner portion of may have a radius that is 40% to 60% as long as the radius of the secondary particle. The outer portion may refer to an area from the outermost surface to about 40 length % to about 60 length % of a radius of the secondary particle. For example, the outer portion of may have a radius that is 40% to 60% as long as the radius of the secondary particle. In addition, a ratio of a volume of the outer portion to a volume of the secondary particle may be less than or equal to about 90 volume %, less than or equal to about 87 volume %, or less than or equal to about 85 volume %. For example, the outer portion may have a volume that is about 90%, less than or equal to about 87%, or less than or equal to about 85% that of the secondary particle as a whole.
The secondary particle of the positive electrode active material may include a radially-arranged outer portion and an inner portion having an irregular porous structure, wherein the inner portion of the secondary particle may have a larger pore (e.g., larger pore size or larger pore volume) than the outer portion. For example, in the positive electrode active material, the inner portion may have a pore size of about 150 nm to about 1 μm and the outer portion may have a pore size of less than about 150 nm. In this way, when the pore size of the inner portion is larger than that of the outer portion, there may be a feature of shortening a diffusion distance of lithium in the active material, compared with a secondary particle having the same pore sizes at the inner and outer portions, and lithium may be easily inserted from the outside, and in addition, there may be an effect of alleviating volume changes during the charge and discharge. Herein, the pore size means an average diameter when a pore is spherical or circular (e.g., substantially spherical or circular) and a length of a long axis when the pore is oval.
The secondary particle of the positive electrode active material may have open pores on the surface and facing toward the center of the inner portion and a size of the open pore may be less than about 150 nm, for example, about 10 nm to about 148 nm. The open pore is an exposed pore through which a material can enter and exit. The open pores may be formed to a depth of less than or equal to about 150 nm, for example, about 0.001 nm to about 100 nm, for example, about 1 nm to about 50 nm on average from the surface of the secondary particle.
Closed pores may exist in the inner portion of the secondary particle, and closed pores and/or open pores may exist in the outer portion. The closed pores may exclude or mostly exclude an electrolyte, while the open pores may include an electrolyte therein. The closed pores are independent pores that are not connected to other pores because all of the walls of the pores are formed in a closed structure, and the open pores are continuous pores connected to the outside of the particle because at least some of the walls of the pores are formed in an open structure.
In the secondary particle, the inner portion has a porous structure, so that the diffusion distance of lithium ions to the inner portion is reduced, and the outer portion has radial structure, so that lithium ions are easily intercalated into the surface. In addition, because the size of the primary particles is small, it is easy to secure a lithium transfer path between crystal grains. In addition, because the size of the primary particles is small and the pores between the primary particles alleviate the volume change occurring during charging and discharging, the stress caused by the volume change during charging and discharging may be minimized or reduced. Such a positive electrode active material may reduce resistance of a rechargeable lithium battery and improve capacity characteristics and cycle-life characteristics.
In some embodiments of the secondary particles, the plurality of primary particles may have a radial arrangement structure by being arranged toward a single (e.g. sole) center to make surface contact along the thickness direction of the primary particles or, in some embodiments, the secondary particles may have a “multi-center” radial arrangement structure having a plurality of centers. As such, when the secondary particles have a single-center or multi-center radial arrangement structure, lithium is easily deintercalated and/or intercalated to the center (or centers) of the secondary particles.
The secondary particles may include radial primary particles and non-radial primary particles. A content of the non-radial primary particles may be less than or equal to about 30 wt %, for example about 0.01 wt % to about 30 wt %, for example, about 0.1 wt % to about 20 wt %, based on the total weight of the radial primary particles and the non-radial primary particles.
The positive electrode active material includes a lithium nickel-based composite oxide. The nickel content in the lithium nickel-based composite oxide may be greater than or equal to about 30 mol %, for example greater than or equal to about 40 mol %, greater than or equal to about 50 mol %, greater than or equal to about 60 mol %, greater than or equal to about 70 mol %, greater than or equal to about 80 mol %, or greater than or equal to about 90 mol % and less than or equal to about 99.9 mol %, or less than or equal to about 99 mol % based on the total amount of metals other than lithium. For example, the nickel content in the lithium nickel-based composite oxide may be higher than the content of each of other metals of the lithium nickel-based composite oxide such as, for example, cobalt, manganese, and aluminum. When the nickel content satisfies the above range, the positive electrode active material may exhibit excellent battery performance while realizing a high capacity.
The lithium nickel-based composite oxide may be represented by Chemical Formula 1.
Lia1Nix1M1y1M21−x1−y1O2−zXz Chemical Formula 1
In Chemical Formula 1, 0.9≤a1≤1.8, 0.3≤x1≤1, 0≤y1≤0.7, and 0≤z≤0.1, M1 and M2 are each independently Al, B, Ba, Ca, Ce, Co, Cr, Cu, Fe, Mg, Mn, Mo, Nb, Si, Sr, Ti, V, W, Zr, or a combination thereof, and X is F, P, S, or a combination thereof.
In Chemical Formula 1, 0.4≤x1≤1 and 0≤y1≤0.6, 0.5≤x1≤1 and 0≤y1≤0.5, 0.6≤x1≤1 and 0≤y1≤0.4, or 0.7≤x1≤1 and 0≤y1≤0.3, 0.8≤x1≤1 and 0≤y1≤0.2, or 0.9≤x1≤1 and 0≤y1≤0.1.
The lithium nickel-based composite oxide may be, for example, represented by Chemical Formula 2.
Lia2Nix2Coy2M31−x2−y2O2−zXz Chemical Formula 2
In Chemical Formula 2, 0.9≤a2≤1.8, 0.3≤x2<1, 0<y2≤0.7, and 0≤z≤0.1, M3 is Al, B, Ba, Ca, Ce, Cr, Cu, Fe, Mg, Mn, Mo, Nb, Si, Sr, Ti, V, W, Zr, or a combination thereof, and X is F, P, S, or a combination thereof.
In Chemical Formula 2, 0.3≤x2≤0.99 and 0.01≤y2≤0.7, 0.4≤x2≤0.99 and 0.01≤y2≤0.6, 0.5≤x2≤0.99 and 0.01≤y2≤0.5, or 0.6≤x2≤0.99 and 0.01≤y2≤0.4, 0.7≤x2≤0.99 and 0.01≤y2≤0.3, 0.8≤x2≤0.99 and 0.01≤y2≤0.2, or 0.9≤x2≤0.99 and 0.01≤y2≤0.1.
The lithium nickel-based composite oxide may be, for example, represented by Chemical Formula 3.
Lia3Nix3Coy3M4z3M51−x3−y3−z3O2−zXz Chemical Formula 3
In Chemical Formula 3, 0.9≤a3≤1.8, 0.3≤x3≤0.98, 0.01≤y3≤0.69, 0.01≤z3≤0.69, 0≤z≤0.1, M4 is Al, Mn, or a combination thereof, M5 is B, Ba, Ca, Ce, Cr, Cu, Fe, Mg, Mo, Nb, Si, Sr, Ti, V, W, Zr, or a combination thereof, and X is F, P, S, or a combination thereof.
In Chemical Formula 3, 0.4≤x3≤0.98, 0.01≤y3≤0.59, and 0.01≤z3≤0.59, may be 0.5≤x3≤0.98, 0.01≤y3≤0.49, and 0.01≤z3≤0.49, or 0.6≤x3≤0.98, 0.01≤y3≤0.39, and 0.01≤z3≤0.39, or 0.7≤x3≤0.98, 0.01≤y3≤0.29, and 0.01≤z3≤0.29, or 0.8≤x3≤0.98, 0.01≤y3≤0.19, and 0.01≤z3≤0.19, or 0.9≤x3≤0.98, 0.01≤y3≤0.09, and 0.01≤z3≤0.09.
Generally, as the nickel content in the positive electrode active material is increased, because cation mixing, in which Ni2+ ions take lithium sites, also increases, capacity rather decreases, or because diffusion of lithium ions is hindered by impurities such as NiO and/or the like, a battery cycle-life may be deteriorated (e.g., reduced), and in addition, the positive electrode active material has a side reaction with an electrolyte due to the structural collapse and cracks resulting from charges and discharges, which may decrease the battery cycle-life and bring about a safety problem. In order to solve these problems, when boron is coated only on the surface of an active material in a comparative method, the boron acts as resistance (e.g., a resistor) and rather decreases capacity and deteriorates a cycle-life. On the contrary, the positive electrode active material according to an embodiment, even if a high nickel-based material is used, includes the boron coating layer and the boron doping layer suitably or appropriately and accordingly, may improve problems due to the high concentration of nickel and thus realize high capacity and concurrently (e.g., simultaneously), improve cycle-life characteristics without (e.g., substantially without) deteriorating (e.g., reducing) initial discharge capacity.
In an embodiment, a method of preparing a positive electrode active material for a rechargeable lithium battery includes mixing together a nickel-based hydroxide, a lithium raw material, and a boron raw material and heat-treating the resultant.
In comparative methods, when boron is coated on a positive electrode active material, a lithium raw material is mixed together with a nickel-based hydroxide followed by heat-treating the resultant to prepare a lithium nickel-based composite oxide, and a boron source is mixed therewith by a wet or dry method followed by performing heat-treatment again. In this case, only the surface of the positive electrode active material is coated with boron, and thus boron acts as a resistance (e.g., a resistor), thereby reducing capacity and cycle-life. According to the preparing method according to embodiments of the present disclosure, however, a secondary particle in which at least a portion of the primary particles are radially arranged is produced, and at the same time, a boron coating layer and a boron doping layer are appropriately formed, so that boron does not act as a resistance (e.g., a resistor) to obtain a positive electrode active material that is structurally stable and has excellent cycle-life characteristics.
In the preparing method according to embodiments of the present disclosure, the nickel-based hydroxide is a precursor of the positive electrode active material, and may be expressed as a nickel metal composite hydroxide or a nickel transition metal composite hydroxide, and may be prepared by a co-precipitation method and/or the like.
The nickel-based hydroxide may be, for example, represented by Chemical Formula 11.
Nix11M11y11M121−x11−y11(OH)2 Chemical Formula 11
In Chemical Formula 11, 0.3≤x11≤1, 0≤y11≤0.7, and M11 and M12 are each independently Al, B, Ba, Ca, Ce, Co, Cr, Cu, F, Fe, Mg, Mn, Mo, Nb, P, S, Si, Sr, Ti, V, W, Zr, or a combination thereof.
As an example, the nickel-based hydroxide may be represented by Chemical Formula 12 or Chemical Formula 13.
Nix12Coy12M131−x12−y12(OH)2 Chemical Formula 12
In Chemical Formula 12, 0.3≤x12<1, 0<y12≤0.7, M13 is Al, B, Ba, Ca, Ce, Cr, Cu, F, Fe, Mg, Mn, Mo, Nb, P, S, Si, Sr, Ti, V, W, Zr, or a combination thereof.
Nix13Coy13M14z13M151−x13−y13−z13(OH)2 Chemical Formula 13
In Chemical Formula 13, 0.3≤x13≤0.98, 0.01≤y13≤0.69, 0.01≤z13≤0.69, M14 is Al, Mn, or a combination thereof, and M15 is B, Ba, Ca, Ce, Cr, Cu, F, Fe, Mg, Mo, Nb, P, S, Si, Sr, Ti, V, W, Zr, or a combination thereof.
The lithium raw material may be, for example, lithium hydroxide and/or the like, and may be mixed together to a ratio of about 0.8 mole to about 1.8 mole, or about 0.9 mole to about 1.2 mole based on 1 mole of the nickel-based hydroxide.
The boron raw material may be a compound containing boron, for example, H3BO3, HBO2, B2O3, C6H5B(OH)2, (C6H5O)3B, [CH3(CH2)3O]3B, (C3H7O)3B, C3H9B3O6, C13H19BO3, or a combination thereof.
A content of the boron raw material may be about 0.1 parts by mole to about 5 parts by mole, for example about 0.1 parts by mole to about 4 parts by mole, about 0.1 parts by mole to about 3 parts by mole, about 0.1 parts by mole to about 2.9 parts by mole, about 0.1 parts by mole to about 2.5 parts by mole, about 0.1 parts by mole to about 2 parts by mole, about 0.1 parts by mole to about 1.5 parts by mole, or about 0.5 parts by mole to about 1.3 parts by mole based on 100 parts by mole of the nickel-based hydroxide. When the content of boron raw material satisfies the above range, boron does not act as a resistance (e.g., a resistor) in the positive electrode active material and may serve to improve performance of a rechargeable lithium battery, thereby improving capacity and improving cycle-life characteristics. When the content of the boron raw material is excessive, the content of the boron coating layer is excessively increased, and boron acts as a resistance (e.g., a resistor) in the positive electrode active material, thereby reducing the capacity and cycle-life of the battery.
The heat-treating may be performed at a temperature of about 650° C. to about 850° C., or about 690° C. to about 780° C. In this case, a positive electrode active material for a rechargeable lithium battery having a stable structure while including both the boron coating layer and boron doping layer may be prepared.
In addition, the heat-treating may be performed for about 5 hours to about to 25 hours, for example, about 8 hours to about 12 hours. In this case, a positive electrode active material for a rechargeable lithium battery having a stable structure including both the boron coating layer and boron doping layer is prepared.
Another embodiment provides a rechargeable lithium battery including a positive electrode, a negative electrode, a separator between the positive electrode and the negative electrode, and an electrolyte.
The positive electrode for a rechargeable lithium battery according to an embodiment may include a current collector and a positive electrode active material layer on the current collector. The positive electrode active material layer may include a positive electrode active material, and may further include a binder and/or a conductive material (e.g., an electrically conductive material).
The binder improves binding properties of positive electrode active material particles with one another and with a current collector. Examples thereof may include polyvinyl alcohol, carboxylmethyl cellulose, hydroxypropyl cellulose, diacetyl cellulose, polyvinylchloride, carboxylated polyvinylchloride, polyvinylfluoride, an ethylene oxide-containing polymer, polyvinylpyrrolidone, polyurethane, polytetrafluoroethylene, polyvinylidene fluoride, polyethylene, polypropylene, a styrene-butadiene rubber, an acrylated styrene-butadiene rubber, an epoxy resin, nylon, and the like, but are not limited thereto.
A content of the binder in the positive electrode active material layer may be about 1 wt % to about 5 wt % based on the total weight of the positive electrode active material layer.
The conductive material is included to provide electrode conductivity. Any suitable electrically conductive material may be used as a conductive material unless it causes a chemical change (e.g., an unsuitable or undesirable chemical change in the rechargeable lithium battery). Examples of the conductive material may include a carbon-based material such as natural graphite, artificial graphite, carbon black, acetylene black, ketjen black, a carbon fiber, carbon nanotube, and the like; a metal-based material of a metal powder or a metal fiber including copper, nickel, aluminum, silver, and the like; a conductive polymer such as a polyphenylene derivative; or a mixture thereof.
A content of the conductive material in the positive electrode active material layer may be about 1 wt % to about 5 wt % based on the total weight of the positive electrode active material layer.
An aluminum foil may be used as the current collector, but is not limited thereto.
The negative electrode for a rechargeable lithium battery may include, for example, a current collector and a negative electrode active material layer on the current collector. The negative electrode active material layer may include a negative electrode active material, and may further include a binder, and/or a conductive material (e.g., an electrically conductive material).
The negative electrode active material may include a material that reversibly intercalates/deintercalates lithium ions, a lithium metal, a lithium metal alloy, a material capable of doping/dedoping lithium, and/or a transition metal oxide.
The material that reversibly intercalates/deintercalates lithium ions may include, for example crystalline carbon, amorphous carbon, or a combination thereof as a carbon-based negative electrode active material. The crystalline carbon may be non-shaped, or sheet, flake, spherical, and/or fiber shaped natural graphite and/or artificial graphite. The amorphous carbon may be a soft carbon, a hard carbon, a mesophase pitch carbonization product, calcined coke, and/or the like.
The lithium metal alloy includes an alloy of lithium and a metal selected from Na, K, Rb, Cs, Fr, Be, Mg, Ca, Sr, Si, Sb, Pb, In, Zn, Ba, Ra, Ge, Al, and Sn.
The material capable of doping/dedoping lithium may be a Si-based negative electrode active material and/or a Sn-based negative electrode active material. The Si-based negative electrode active material may include silicon, a silicon-carbon composite, SiOx (0<x<2), and/or a Si-Q alloy (wherein Q is an alkali metal, an alkaline-earth metal, a Group 13 element, a Group 14 element, a Group 15 element, a Group 16 element, a transition metal, a rare earth element, and a combination thereof, but not Si) and the Sn-based negative electrode active material may include Sn, SnO2, and/or a Sn—R alloy (wherein R is an alkali metal, an alkaline-earth metal, a Group 13 element, a Group 14 element, a Group 15 element, a Group 16 element, a transition metal, a rare earth element, and a combination thereof, but not Sn). At least one of these materials may be mixed together with SiO2. The elements Q and R may be selected from Mg, Ca, Sr, Ba, Ra, Sc, Y, Ti, Zr, Hf, Rf, V, Nb, Ta, Db, Cr, Mo, W, Sg, Tc, Re, Bh, Fe, Pb, Ru, Os, Hs, Rh, Ir, Pd, Pt, Cu, Ag, Au, Zn, Cd, B, Al, Ga, Sn, In, Tl, Ge, P, As, Sb, Bi, S, Se, Te, Po, and a combination thereof.
The silicon-carbon composite may be, for example, a silicon-carbon composite including a core including crystalline carbon and silicon particles and an amorphous carbon coating layer on the surface of the core. The crystalline carbon may be artificial graphite, natural graphite, or a combination thereof. The amorphous carbon precursor may include a coal-based pitch, mesophase pitch, petroleum-based pitch, coal-based oil, petroleum-based heavy oil, and/or a polymer resin such as a phenol resin, a furan resin, and/or a polyimide resin. In this case, the content of silicon may be about 10 wt % to about 50 wt % based on the total weight of the silicon-carbon composite. In addition, the content of the crystalline carbon may be about 10 wt % to about 70 wt % based on the total weight of the silicon-carbon composite, and the content of the amorphous carbon may be about 20 wt % to about 40 wt % based on the total weight of the silicon-carbon composite. In addition, a thickness of the amorphous carbon coating layer may be about 5 nm to about 100 nm. An average particle diameter (D50) of the silicon particles may be about 10 nm to about 20 μm. The average particle diameter (D50) of the silicon particles may be about 10 nm to about 200 nm. The silicon particles may exist in an oxidized form, and in this case, an atomic content ratio of Si:O in the silicon particles indicating a degree of oxidation may be about 99:1 to about 33:67. The silicon particles may be SiOx particles, and in this case, the range of x in SiOx may be greater than about 0 and less than about 2. As used herein, when a definition is not otherwise provided, an average particle diameter (D50) indicates a particle where an accumulated volume is about 50 volume % in a particle distribution.
The Si-based negative electrode active material or Sn-based negative electrode active material may be mixed together with the carbon-based negative electrode active material. When the Si-based negative electrode active material or Sn-based negative electrode active material and the carbon-based negative electrode active material are mixed together and used, the mixing ratio may be a weight ratio of about 1:99 to about 90:10.
In the negative electrode active material layer, the negative electrode active material may be included in an amount of about 95 wt % to about 99 wt % based on the total weight of the negative electrode active material layer.
In an embodiment, the negative electrode active material layer may further include a binder, and may optionally further include a conductive material (e.g., an electrically conductive material). The content of the binder in the negative electrode active material layer may be about 1 wt % to about 5 wt % based on the total weight of the negative electrode active material layer. In addition, when the conductive material is further included, the negative electrode active material layer may include about 90 wt % to about 98 wt % of the negative electrode active material, about 1 wt % to about 5 wt % of the binder, and about 1 wt % to about 5 wt % of the conductive material.
The binder serves to well adhere the negative electrode active material particles to each other and also to adhere the negative electrode active material to the current collector. The binder may be a water-insoluble binder, a water-soluble binder, or a combination thereof.
Examples of the water-insoluble binder include polyvinyl chloride, carboxylated polyvinyl chloride, polyvinyl fluoride, an ethylene oxide-containing polymer, an ethylene propylene copolymer, polystyrene, polyvinylpyrrolidone, polyurethane, polytetrafluoro ethylene, polyvinylidene fluoride, polyethylene, polypropylene, polyamideimide, polyimide, or a combination thereof.
The water-soluble binder may include a rubber binder and/or a polymer resin binder. The rubber binder may be selected from a styrene-butadiene rubber, an acrylated styrene-butadiene rubber, an acrylonitrile-butadiene rubber, an acrylic rubber, a butyl rubber, a fluororubber, and a combination thereof. The polymer resin binder may be selected from polyethylene oxide, polyvinylpyrrolidone, polyepichlorohydrin, polyphosphazene, polyacrylonitrile, an ethylene propylene diene copolymer, polyvinylpyridine, chlorosulfonated polyethylene, latex, a polyester resin, an acrylic resin, a phenol resin, an epoxy resin, polyvinyl alcohol, and a combination thereof.
When a water-soluble binder is used as the negative electrode binder, a cellulose-based compound capable of imparting viscosity (e.g., capable of increasing viscosity) may be further included. As the cellulose-based compound, one or more of carboxymethyl cellulose, hydroxypropylmethyl cellulose, methyl cellulose, or alkali metal salts thereof may be mixed together and used. As the alkali metal, Na, K or Li may be used. The amount of such a thickener used may be about 0.1 parts by weight to about 3 parts by weight based on 100 parts by weight of the negative electrode active material.
The conductive material is included to provide electrode conductivity (e.g., electrical conductivity). Any suitable electrically conductive material may be used as a conductive material unless it causes a chemical change (e.g., an unsuitable or undesirable change in the rechargeable lithium battery). Examples of the conductive material include a carbon-based material such as natural graphite, artificial graphite, carbon black, acetylene black, ketjen black, a carbon fiber, carbon nanotube, and the like; a metal-based material of a metal powder and/or a metal fiber including copper, nickel, aluminum silver, and the like; a conductive polymer such as a polyphenylene derivative; and/or a mixture thereof.
The current collector may include one selected from a copper foil, a nickel foil, a stainless steel foil, a titanium foil, a nickel foam, a copper foam, a polymer substrate coated with a conductive metal (e.g., an electrically conductive metal), and a combination thereof.
The electrolyte includes a non-aqueous organic solvent and a lithium salt.
The non-aqueous organic solvent serves as a medium for transmitting ions taking part in the electrochemical reaction of a battery. The non-aqueous organic solvent may be a carbonate-based, ester-based, ether-based, ketone-based, and/or alcohol-based solvent, and/or aprotic solvent. The carbonate-based solvent may be dimethyl carbonate (DMC), diethyl carbonate (DEC), dipropyl carbonate (DPC), methylpropyl carbonate (MPC), ethylpropyl carbonate (EPC), methylethyl carbonate (MEC), ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate (BC), and/or the like. The ester-based solvent may be methyl acetate, ethyl acetate, n-propyl acetate, dimethyl acetate, methyl propionate, ethyl propionate, γ-butyrolactone, decanolide, valerolactone, mevalonolactone, caprolactone, and/or the like. The ether-based solvent may be dibutyl ether, tetraglyme, diglyme, dimethoxyethane, 2-methyltetrahydrofuran, tetrahydrofuran, and/or the like and the ketone-based solvent may be cyclohexanone, and/or the like. In addition, the alcohol-based solvent may be ethyl alcohol, isopropyl alcohol, etc. and the aprotic solvent may be nitriles such as R—CN (where R is a C2 to C20 linear, branched, or cyclic hydrocarbon group and may include a double bond, an aromatic ring, and/or an ether bond), amides such as dimethylformamide, dioxolanes such as 1,3-dioxolane, sulfolanes, and/or the like.
The non-aqueous organic solvent may be used singularly or in a mixture. When the organic solvent is used in a mixture, the mixture ratio may be controlled in accordance with a suitable or desirable battery performance.
In addition, in the case of the carbonate-based solvent, a mixture of a cyclic carbonate and a chain carbonate may be used. In this case, when the cyclic carbonate and the chain carbonate are mixed together to a volume ratio of about 1:1 to about 1:9, the electrolyte may exhibit excellent performance.
The non-aqueous organic solvent may further include an aromatic hydrocarbon-based organic solvent in addition to the carbonate-based solvent. In this case, the carbonate-based solvent and the aromatic hydrocarbon-based organic solvent may be mixed together to a volume ratio of about 1:1 to about 30:1.
As the aromatic hydrocarbon-based solvent, an aromatic hydrocarbon-based compound represented by Chemical Formula I may be used.
In Chemical Formula I, R4 to R9 are the same or different and are selected from hydrogen, a halogen, a C1 to C10 alkyl group, a C1 to C10 haloalkyl group, and a combination thereof.
Examples of the aromatic hydrocarbon-based solvent may be benzene, fluorobenzene, 1,2-difluorobenzene, 1,3-difluorobenzene, 1,4-difluorobenzene, 1,2,3-trifluorobenzene, 1,2,4-trifluorobenzene, chlorobenzene, 1,2-dichlorobenzene, 1,3-dichlorobenzene, 1,4-dichlorobenzene, 1,2,3-trichlorobenzene, 1,2,4-trichlorobenzene, iodobenzene, 1,2-diiodobenzene, 1,3-diiodobenzene, 1,4-diiodobenzene, 1,2,3-triiodobenzene, 1,2,4-triiodobenzene, toluene, fluorotoluene, 2,3-difluorotoluene, 2,4-difluorotoluene, 2,5-difluorotoluene, 2,3,4-trifluorotoluene, 2,3,5-trifluorotoluene, chlorotoluene, 2,3-dichlorotoluene, 2,4-dichlorotoluene, 2,5-dichlorotoluene, 2,3,4-trichlorotoluene, 2,3,5-trichlorotoluene, iodotoluene, 2,3-diiodotoluene, 2,4-diiodotoluene, 2,5-diiodotoluene, 2,3,4-triiodotoluene, 2,3,5-triiodotoluene, xylene, or a combination thereof.
The electrolyte may further include vinylene carbonate and/or an ethylene carbonate-based compound of Chemical Formula II in order to improve cycle-life of a battery.
In Chemical Formula II, R10 and R11 are the same or different, and are selected from hydrogen, a halogen, a cyano group, a nitro group, and fluorinated C1 to C5 alkyl group, provided that at least one of R10 and R11 is selected from a halogen, a cyano group, a nitro group, and fluorinated C1 to C5 alkyl group, but both of R10 and R11 are not hydrogen.
Examples of the ethylene carbonate-based compound may be difluoro ethylenecarbonate, chloroethylene carbonate, dichloroethylene carbonate, bromoethylene carbonate, dibromoethylene carbonate, nitroethylene carbonate, cyanoethylene carbonate, and/or fluoroethylene carbonate. The amount of the additive for improving cycle-life may be used within a suitable or appropriate range.
The lithium salt dissolved in the non-organic solvent supplies lithium ions in a battery, enables a basic operation of a rechargeable lithium battery, and improves transportation of the lithium ions between positive and negative electrodes.
Examples of the lithium salt include at least one supporting salt selected from LiPF6, LiBF4, LiSbF6, LiAsF6, LiN(SO2C2F5)2, Li(CF3SO2)2N, LiN(SO3C2F5)2, Li(FSO2)2N (lithium bis(fluorosulfonyl)imide; LiFSI), LiC4F9SO3, LiClO4, LiAlO2, LiAlCl4, LiPO2F2, LiN(CxF2x+1SO2)(CyF2y+1SO2), (wherein x and y are natural numbers, for example, an integer ranging from 1 to 20), lithium difluoro(bisoxolato) phosphate, LiCl, LiI, LiB(C2O4)2 (lithium bis(oxalato) borate; LiBOB), and lithium difluoro(oxalato)borate (LiDFOB).
The lithium salt may be used in a concentration in a range from about 0.1 M to about 2.0 M. When the lithium salt is included at the above concentration range, an electrolyte may have excellent performance and lithium ion mobility due to suitable or optimal electrolyte conductivity and viscosity.
The separator 113 separates a positive electrode 114 and a negative electrode 112 and provides a transporting passage for lithium ions and may be any suitable, generally-used separator in a lithium ion battery. In other words, it may have low resistance to ion transport and excellent impregnation for an electrolyte. For example, the separator may be selected from a glass fiber, polyester, polyethylene, polypropylene, polytetrafluoroethylene, or a combination thereof. It may have a form of a non-woven fabric or a woven fabric. For example, in a lithium ion battery, a polyolefin-based polymer separator such as polyethylene and polypropylene may be mainly used. In order to ensure the heat resistance or mechanical strength, a coated separator including a ceramic component or a polymer material may be used. Optionally, it may have a mono-layered or multi-layered structure.
Rechargeable lithium batteries may be classified into lithium ion batteries, lithium ion polymer batteries, or lithium polymer batteries according to a type (e.g., kind) of separator and a type of electrolyte used in the batteries, into cylindrical type, prismatic type, coin-type, pouch-type, or the like according to a shape, and into a bulk type or a thin film type according to a size. Because structures of these batteries and manufacturing methods thereof are readily apparent to those of ordinary skill in the art upon reviewing this disclosure, further detailed descriptions thereof will not be provided here.
The rechargeable lithium battery according to an embodiment may be used in an electric vehicle (EV), and/or a hybrid vehicle such as a plug-in hybrid electric vehicle (PHEV) and/or the like due to a high capacity, improved storage stability at a high temperature and cycle-life characteristics, and high rate capability.
Hereinafter, examples of the present disclosure and comparative examples are described. It is to be understood, however, that the examples are for the purpose of illustration and are not to be construed as limiting the present disclosure.
A positive electrode active material precursor was prepared through the following co-precipitation method. Nickel sulfate, cobalt sulfate, and aluminum nitrate were used as metal raw materials.
[First step: 1.5 kW/m3, NH4OH 0.35 M, pH 11.5 to 11.7, and reaction time of 6 hours]
First, ammonia water having a concentration of 0.35 M was put in a reactor. While a metal raw material and a complex agent were added thereto respectively at 85 ml/min and 9 ml/min at 50° C. under a stirring power of 1.5 kW/m3, a reaction was started. While NaOH was added thereto to maintain pH, the reaction was performed for 6 hours. As a result of the reaction, it was confirmed that the average size of the obtained core particles was in the range of about 6.5 μm to 7.5 μm, and the second step was performed as follows.
[Second step: 1.0 kW/m3, NH4OH 0.40 M, pH 11.5 to 11.7, and reaction time of 16 hours]
The metal raw material and the complex agent were added thereto respectively at 107 ml/min and 13 ml/min, while the reaction temperature was maintained at 50° C., so that the complex agent maintained a concentration of 0.40 M. While adding NaOH thereto in order to maintain pH, the reaction was performed for 16 hours. At this time, the stirring power was lowered to 1.0 kW/m3, which was lower than the first step, and the reaction proceeds. By carrying out this reaction, it was confirmed that the average size of the product particles containing the core and the intermediate layer was 10.5 μm to 11.5 μm, and the third step was performed as follows.
[Third step: 0.5 kW/m3, NH4OH 0.40 M, pH 11.5 to 11.7, and reaction time of 5 hours]
While maintaining the reaction temperature of 50° C., the metal raw material and the complex agent were added at the rates of 142 ml/min and 17 ml/min, respectively, so that the concentration of the complex agent was maintained the same as in the second step. While adding NaOH to maintain the pH, the reaction was carried out for 5 hours so that the average particle size reached 14 μm. At this time, the stirring power was lowered to 0.5 kW/m3, which was lower than in the second step, and the reaction proceeded.
After washing the resultant, the washed resultant was dried with hot air at about 150° C. for 24 hours to obtain nickel-based hydroxide (Ni0.945Co0.04Al0.015(OH)2), which was a precursor of the positive electrode active material.
The obtained nickel-based hydroxide and LiOH were mixed together to a mole ratio of 1:1, and 1.0 part by mole of boric acid based on that of the nickel-based hydroxide was added thereto and then, heat-treated 725° C. under an oxygen atmosphere for 10 hours, obtaining a positive electrode active material.
96 wt % of the obtained positive electrode active material, 2 wt % of polyvinylidene fluoride, 2 wt % of carbon nanotube, and N-methylpyrrolidone as a solvent were mixed together in a mixer to prepare a slurry for a positive electrode active material layer. The slurry for a positive electrode active material layer was coated on an aluminum foil onto an electrode plate and then, dried at 135° C. for at least 3 hours, roll-pressed, and vacuum-dried, manufacturing a positive electrode.
The positive electrode and a lithium metal counter electrode were used to manufacture a coin half-cell. Between the positive electrode and the lithium metal counter electrode, a separator formed of a porous polyethylene film (thickness: about 16 μm) was interposed, and an electrolyte solution was injected thereinto. The electrolyte solution was prepared by mixing together ethylenecarbonate (EC) and ethylmethylcarbonate (EMC) to a volume ratio of 3:5 and dissolving 1.1 M LiPF6 in the mixed solvent.
A positive electrode and a battery cell were manufactured in substantially the same manner as in Example 1 except that LiNi0.945Co0.04Al0.015O2 composed of general secondary particles and having a particle diameter of about 14 μm were used as a positive electrode active material of Comparative Example 1.
A positive electrode active material coated with a boron compound was prepared in a comparative method by mixing together the positive electrode active material (LiNi0.945Co0.04Al0.015O2) of Comparative Example 1 together with 1.0 mol % of boric acid and then, heat-treating the mixture at 350° C. for 8 hours under an oxygen atmosphere. Subsequently, a positive electrode and a battery cell were manufactured in substantially the same manner as in Example 1 except that this positive electrode active material of Comparative Example 2 was used.
The positive electrode active material (LiNi0.945Co0.04Al0.015O2) of Comparative Example 1 was heat-treated at 350° C. for 8 hours under an oxygen atmosphere without adding the boric acid. Subsequently, a positive electrode and a battery cell were manufactured in substantially the same manner as in Example 1 except that this positive electrode active material of Comparative Example 3 was used.
ICP (inductively coupled plasma) emission spectroscopic analysis was performed on the positive electrode active material prepared in Example 1 to measure the content of boron. Then, 10 g of each positive electrode active material was added to 100 g of distilled water and then, stirred for 30 minutes and filtered with a filter to obtain the positive electrode active material. Through this washing process, boron on the surface of the positive electrode active material was all removed. The recovered positive electrode active material was dried at 130° C. for 24 hours and then a content of boron remaining in the positive electrode active material was measured through an ICP emission spectroscopic analysis again. This boron content is expressed as a boron content of the ‘inner portion.’
This means the content of the grain boundary boron coating portion. In addition, a difference obtained by subtracting the boron content after the washing from the boron content before the washing, that is, a boron content removed through the washing is expressed as a boron content of the ‘outer portion.’
This means the content of the boron coating layer.
Positive electrode active materials were prepared in substantially the same method as in Example 1 except for changing the content of boric acid (1.0 part by mole in Example 1) into 0 part by mole, 0.5 parts by mole, 1.5 parts by mole, 3.0 parts by mole, and 5.0 parts by mole and then, analyzed with respect to inner and outer boron contents in substantially the same method as the above, and the results are shown in
Referring to
The battery cells according to the examples and the comparative examples were charged to an upper limit voltage of 4.25 V at a constant current of 0.2 C and discharged to a discharge cut-off voltage of 3.0 V at 0.2 C at 25° C. and then, measured with respect to initial charge and discharge capacity, and the results are shown in
Referring to
While the subject matter of this disclosure has been described in connection with what is presently considered to be practical example embodiments, it is to be understood that the present disclosure is not limited to the disclosed embodiments. On the contrary, it is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims, and equivalents thereof.