Patent Grant
11728478
One embodiment of the present invention relates to an object, a method, or a manufacturing method. The present invention relates to a process, a machine, manufacture, or a composition of matter. One embodiment of the present invention relates to a semiconductor device, a display device, a light-emitting device, a power storage device, a lighting device, an electronic device, or a manufacturing method thereof. In particular, one embodiment of the present invention relates to an electronic device and its operating system.
In this specification, the power storage device is a collective term describing units and devices having a power storage function. For example, a storage battery such as a lithium-ion secondary battery (also referred to as secondary battery), a lithium-ion capacitor, and an electric double layer capacitor are included in the category of the power storage device.
Electronic devices in this specification mean all devices including power storage devices, and electro-optical devices including power storage devices, information terminal devices including power storage devices, and the like are all electronic devices.
In recent years, a variety of power storage devices such as lithium-ion secondary batteries, lithium-ion capacitors, and air batteries have been actively developed. In particular, demand for lithium-ion secondary batteries with high output and high capacity has rapidly grown with the development of the semiconductor industry, for portable information terminals such as mobile phones, smartphones, and laptop computers, portable music players, and digital cameras; medical equipment; next-generation clean energy vehicles such as hybrid electric vehicles (HEV), electric vehicles (EV), and plug-in hybrid electric vehicles (PHEV); and the like. The lithium-ion secondary batteries are essential as rechargeable energy supply sources for today's information society.
The performance required for lithium-ion secondary batteries today includes higher capacity, improved cycle performance, safe operation under a variety of environments, and longer-term reliability.
Thus, improvement of a positive electrode active material has been studied to increase the cycle performance and the capacity of the lithium ion secondary battery (Patent Documents 1, 2, and 3).
However, development of lithium ion secondary batteries and positive electrode active materials used therein is susceptible to improvement in terms of cycle characteristics, capacity, charge and discharge characteristics, reliability, safety, cost, and the like.
An object of one embodiment of the present invention is to provide a positive electrode active material which suppresses a reduction in capacity due to charge and discharge cycles when used in a lithium ion secondary battery. Another object of one embodiment of the present invention is to provide a high-capacity secondary battery. Another object of one embodiment of the present invention is to provide a secondary battery with excellent charge and discharge characteristics. Another object of one embodiment of the present invention is to provide a highly safe or reliable secondary battery.
Another object of one embodiment of the present invention is to provide a novel material, active material, or storage device or a manufacturing method thereof.
Note that the descriptions of these objects do not disturb the existence of other objects. In one embodiment of the present invention, there is no need to achieve all the objects. Other objects can be derived from the description of the specification, the drawings, and the claims.
In order to achieve the above object, one embodiment of the present invention is characterized in including a covering layer containing aluminum and a covering layer containing magnesium in a superficial portion of a positive electrode active material.
One embodiment of the present invention is a positive electrode active material comprising a first region, a second region, and a third region. The first region exists in an inner portion of the positive electrode active material. The second region covers at least part of the first region. The third region covers at least part of the second region. The first region includes lithium, a transition metal, and oxygen. The second region includes lithium, aluminum, the transition metal, and oxygen. The third region includes magnesium and oxygen.
In the above embodiment, the third region may contain fluorine.
In the above embodiment, the third region may contain a transition metal.
In the above embodiment, the first region and the second region may each have a layered rock-salt crystal structure. The third region may have a rock-salt crystal structure.
In the above embodiment, the transition metal can be cobalt.
One embodiment of the present invention is a positive electrode active material comprising lithium, aluminum, a transition metal, magnesium, oxygen, and fluorine. A concentration of the aluminum is more than or equal to 0.1 atomic % and less than or equal to 10 atomic %. A concentration of the magnesium is more than or equal to 5 atomic % and less than or equal to 20 atomic %. A concentration of the fluorine is more than or equal to 3.5 atomic % and less than or equal to 14 atomic %. Each of the concentrations is measured with X-ray photoelectron spectroscopy by taking the total amount of the lithium, the aluminum, the transition metal, the magnesium, the oxygen, and the fluorine which are present in the superficial portion of the positive electrode active material as 100 atomic %.
One embodiment of the present invention is a secondary battery comprising a positive electrode including the positive electrode active material described above, a negative electrode, an electrolyte, and an exterior body.
One embodiment of the present invention is a manufacturing method of a positive electrode active material, comprising steps of dissolving an aluminum alkoxide in alcohol, mixing a particle containing lithium, a transition metal, magnesium, oxygen, and fluorine into an alcohol solution of an aluminum alkoxide in which the aluminum alkoxide is dissolved in the alcohol, stirring a mixed solution in which the particle containing the lithium, the transition metal, the magnesium, the oxygen, and the fluorine is mixed into the alcohol solution of the aluminum alkoxide in an atmosphere containing water vapor, collecting a precipitate from the mixed solution, and heating the collected precipitate in an oxygen-containing atmosphere at 500° C. or higher and 1200° C. or lower for a retention time of 50 hours or less.
According to one embodiment of the present invention, a positive electrode active material which suppresses a reduction in capacity due to charge and discharge cycles when used in a lithium ion secondary battery can be provided. A secondary battery with high capacity can be provided. A secondary battery with excellent charge and discharge characteristics can be provided. A highly safe or highly reliable secondary battery can be provided. A novel material, active material, or storage device or a manufacturing method thereof can be provided.
FIGS. 7A1 to 7B2 illustrate an example of a secondary battery.
FIGS. 24A1 to 24B3 are STEM-FET images of a positive electrode active material in Example 2.
FIGS. 25A1 to 25C are an STEM image and EDX element mappings of a positive electrode active material in Example 2.
Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. Note that one embodiment of the present invention is not limited to the description below, and it is easily understood by those skilled in the art that modes and details of the present invention can be modified in various ways. In addition, the present invention should not be construed as being limited to the description in the embodiments given below.
In this specification and the like, crystal planes and orientations are indicated by the Miller index. In the crystallography, a superscript bar is placed over a number in the expression of crystal planes and orientations; however, in this specification and the like, crystal planes and orientations are expressed by placing a minus sign (−) at the front of a number instead of placing the bar over a number because of patent expression limitations. Furthermore, an individual direction which shows an orientation in crystal is denoted by “[ ]”, a set direction which shows all of the equivalent orientations is denoted by “< >”, an individual direction which shows a crystal plane is denoted by “( )”, and a set plane having equivalent symmetry is denoted by “{ }”.
In this specification and the like, segregation refers to a phenomenon in which, in a solid made of a plurality of elements (e.g., A, B, and C), a certain element (for example, B) is non-uniformly distributed.
In this specification and the like, a layered rock-salt crystal structure included in a composite oxide containing lithium and a transition metal refers to a crystal structure in which a rock-salt ion arrangement where cations and anions are alternately arranged is included and the lithium and the transition metal are regularly arranged to form a two-dimensional plane, so that lithium can be two-dimensionally diffused. Note that a defect such as a cation or anion vacancy can exist. In the layered rock-salt crystal structure, strictly, a lattice of a rock-salt crystal is distorted in some cases.
In this specification and the like, a rock-salt crystal structure refers to a structure in which cations and anions are alternately arranged. Note that a cation or anion vacancy may exist.
Anions of a layered rock-salt crystal and anions of a rock-salt crystal each form a cubic closest packed structure (face-centered cubic lattice structure). When a layered rock-salt crystal and a rock-salt crystal are in contact with each other, there is a crystal plane at which orientations of cubic closest packed structures formed of anions are aligned with each other. A space group of the layered rock-salt crystal is R-3m, which is different from a space group Fm-3m of a general rock-salt crystal and a space group Fd-3m of a rock-salt crystal having the simplest symmetry; thus, the Miller index of the crystal plane satisfying the above conditions in the layered rock-salt crystal is different from that in the rock-salt crystal. In this specification, in the layered rock-salt crystal and the rock-salt crystal, a state where the orientations of the cubic closest packed structures formed of anions are aligned with each other is referred to as a state where crystal orientations are substantially aligned with each other.
Whether the crystal orientations in two regions are aligned with each other or not can be judged by a transmission electron microscope (TEM) image, a scanning transmission electron microscope (STEM) image, a high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM) image, an annular bright-field scan transmission electron microscopy (ABF-STEM) image, and the like. X-ray diffraction, electron diffraction, neutron diffraction, and the like can be used for judging. In the TEM image and the like, alignment of cations and anions can be observed as repetition of bright lines and dark lines. When the orientations of cubic closest packed structures of the layered rock-salt crystal and the rock-salt crystal are aligned with each other, a state where an angle between the repetition of bright lines and dark lines in the layered rock-salt crystal and the repetition of bright lines and dark lines in the rock-salt crystal is less than or equal to 5°, preferably less than or equal to 2.5° is observed. Note that, in the TEM image and the like, a light element such as oxygen or fluorine is not clearly observed in some cases; however, in such a case, alignment of orientations can be judged by arrangement of metal elements.
[Structure of Positive Electrode Active Material]
First, a positive electrode active material 100, which is one embodiment of the present invention, is described with reference to
As illustrated in
Although not shown in drawings, the second region 102 may exist in the inner portion of the positive electrode active material 100. For example, in the case where the first region 101 is a polycrystal, the second region 102 may exist in the vicinity of a grain boundary. Furthermore, the second region 102 may exist in a crystal defect portion in the positive electrode active material 100 or in the vicinity of the crystal defect portion.
The second region 102 does not necessarily cover the entire first region 101. Similarly, the third region 103 does not necessarily cover the entire second region 102. In addition, the third region 103 may exist in contact with the first region 101.
In other words, the first region 101 exists in the inner portion of the positive electrode active material 100, and the second region 102 and the third region 103 exist in the superficial portion of the positive electrode active material 100. The second region 102 and the third region 103 in the superficial portion serve as covering layers of the positive electrode active material. Moreover, the third region 103 and the second region 102 may exist in the inner portion of a particle of the positive electrode active material 100.
When the particle size of the positive electrode active material 100 is too large, problems occur such as difficulty in lithium diffusion and surface roughness of the active material layer when the material is applied to a current collector. In contrast, when the particle size is too small, problems occur such as difficulty in applying the material to the current collector and over-reaction with an electrolyte. Thus, D50 (also referred to as a median diameter) is preferably 0.1 μm or more and 100 μm or less, and further preferably 1 μm or more and 40 μm or less.
To increase the density of the positive electrode active material layer, it is effective to mix a large particle (the longest portion is approximately 20 μm or more and 40 μm or less) and a small particle (the longest portion is approximately 1 μm) and embed a space between the large particles with the small particle. Thus, there may be two peaks of particle size distribution.
<First Region 101>
The first region 101 includes lithium, a transition metal, and oxygen. In other words, the first region 101 includes composite oxide containing lithium and a transition metal.
As the transition metal included in the first region 101, a metal that can form layered rock-salt composite oxide together with lithium is preferably used. For example, one or a plurality of manganese, cobalt, and nickel can be used. That is, as the transition metal included in the first region 101, only cobalt may be used, cobalt and manganese may be used, or cobalt, manganese, and nickel may be used. In addition to the transition metal, the first region 101 may include a metal other than the transition metal, such as aluminum.
In other words, the first region 101 can include composite oxide of lithium and the transition metal, such as lithium cobaltate, lithium nickel oxide, lithium cobaltate in which manganese is substituted for part of cobalt, lithium nickel-manganese-cobalt oxide, or lithium nickel-cobalt-aluminum oxide.
The first region 101 is a region which contributes particularly to a charge and discharge reaction in the positive electrode active material 100. To increase capacity of a secondary battery containing the positive electrode active material 100, the volume of the first region 101 is preferably larger than those of the second region 102 and the third region 103.
Note that the first region 101 may be a single crystal or a polycrystal. For example, the first region 101 may be a polycrystal in which an average crystallite size is greater than or equal to 280 nm and less than or equal to 630 nm. In the case of a polycrystal, a grain boundary can be observed from the TEM or the like in some cases. In addition, the average of crystal grain sizes can be calculated from the half width of XRD.
A polycrystal has a clear crystal structure; thus, a two-dimensional diffusion path of lithium ions can be sufficiently ensured. In addition, a polycrystal is easily produced as compared with a single crystal; thus, a polycrystal is preferably used for the first region 101.
A layered rock-salt crystal structure is preferable for the first region 101 because lithium is likely to be diffused two-dimensionally. In addition, in the case where the first region 101 has a layered rock-salt crystal structure, magnesium segregation, which is described later, is likely to occur unexpectedly. Note that the entire first region 101 does not necessarily have a layered rock-salt crystal structure. For example, part of the first region 101 may include crystal defects, may be amorphous, or may have another crystal structure.
<Second Region 102>
The second region 102 includes lithium, aluminum, a transition metal, and oxygen. In other words, aluminum is substituted for part of a transition metal site of a composite oxide of lithium and the transition metal. The transition metal of the second region 102 is preferably the same element as a transition metal of the first region 101. Note that the site in this specification and the like means a position where an element should occupy in the crystal.
The second region 102 may include fluorine.
Since the second region 102 includes aluminum, cycle characteristics of the positive electrode active material 100 can be improved. Note that aluminum in the second region 102 may have a concentration gradient. In addition, the aluminum preferably exists in part of the transition metal site of the composite oxide of lithium and the transition metal, but may exist in other states. For example, the aluminum may exist as aluminum oxide (Al2O3).
In general, as charging and discharging are repeated, a side reaction occurs, for example, a transition metal such as cobalt or manganese, is dissolved in an electrolyte solution, oxygen is released, and a crystal structure becomes unstable, so that the positive electrode active material deteriorates. However, since the positive electrode active material 100, which is one embodiment of the present invention, includes the second region 102 including aluminum in the superficial portion, the crystal structure of the composite oxide of lithium and the transition metal included in the first region 101 can be more stable. As a result, the cycle characteristics of the secondary battery including the positive electrode active material 100 can be significantly improved.
The second region 102 preferably has a layered rock-salt crystal structure. When the second region 102 has a layered rock-salt crystal structure, crystal orientations are likely to be aligned with those of the first region 101 and the third region 103. Orientations of the crystal in the first region 101, the crystal in the second region 102, and the crystal in the third region 103 are substantially aligned with each other, whereby the second region 102 and the third region 103 can serve as a more stable covering layer.
When the thickness of the second region 102 is too small, the function as the covering layer is degraded; however, when the thickness of the second region 102 is too large, the capacity might be decreased. Thus, the second region 102 is preferably provided in a range from the surface of the positive electrode active material 100 to a depth of 30 nm, preferably a depth of 15 nm, in a depth direction.
<Third Region 103>
The third region 103 includes magnesium and oxygen. In other word, the third region 103 includes magnesium oxide.
The third region 103 may include the same transition metal as that in the first region 101 and the second region 102. The third region 103 may include fluorine. In the case where the third region 103 includes fluorine, fluorine may be substituted for part of oxygen of the magnesium oxide.
Since magnesium oxide included in the third region 103 is an electrochemically stable material, degradation hardly occurs even when charging and discharging are repeated, so that it is suitable as a covering layer. That is, the positive electrode active material 100 has the third region 103 in the superficial portion in addition to the second region 102, whereby the crystal structure of the composite oxide containing lithium and the transition metal in the first region 101 can be further stabilized. As a result, the cycle characteristics of the secondary battery including the positive electrode active material 100 can be improved. In addition, when charging and discharging are carried out at a voltage exceeding 4.3 V (vs. Li/Li+), especially 4.5 V (vs. Li/Li+) or more, the constitution of one embodiment of the present invention exerts its significant effect.
When the third region 103 has a rock-salt type crystal structure, orientation of crystals easily is aligned with those of the second region 102, which is preferable because the third region 103 easily serves as a stable covering layer. However, the entire third region 103 does not necessarily have a rock-salt crystal structure. For example, part of the third region 103 may be amorphous or have another crystal structure.
When the thickness of the third region 103 is too small, the function as the covering layer is degraded; however, when the thickness is too large, the capacity is decreased. Therefore, the third region 103 preferably exists from the surface of the positive electrode active material 100 in the range of 0.5 nm or more to 50 nm or less in the depth direction, more preferably 0.5 nm or more and 5 nm or less.
Since it is important for the third region 103 to have an electrochemically stable material, the contained element is not necessarily magnesium. For example, instead of magnesium, or together with magnesium, a typical element such as calcium and beryllium may be contained. Instead of fluorine, or together with fluorine, chlorine may be contained.
<Boundaries Between Regions>
The first region 101, the second region 102, and the third region 103 have different compositions. The element contained in each region has a concentration gradient in some cases. For example, aluminum contained in the second region 102 may have a concentration gradient. The third region 103 may have a concentration gradient of magnesium because the third region 103 is preferably a region where magnesium is segregated as described later. Thus, the boundaries between the regions are not clear in some cases.
The difference of compositions of the first region 101, the second region 102, and the third region 103 can be observed using a TEM image, a STEM image, fast Fourier transform (FFT) analysis, energy dispersive X-ray spectrometry (EDX), analysis in the depth direction by time-of-flight secondary ion mass spectrometry (ToF-SIMS), X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy, thermal desorption spectroscopy (TDS), or the like. Note that in the EDX measurement, measurement while scanning within the region and evaluating the region two-dimensionally may be referred to as EDX surface analysis. From the EDX surface analysis, evaluation while extracting data of a linear region and evaluating the distribution inside the positive electrode active material particle with respect to atomic concentration may be referred to as line analysis.
For example, in the TEM image and the STEM image, difference of constituent elements is observed as difference of brightness; thus, difference of constituent elements of the first region 101, the second region 102, and the third region 103 can be observed. Also in plane analysis of EDX (e.g., element mapping), it can be observed that the first region 101, the second region 102, and the third region 103 contain different elements.
By line analysis of EDX and analysis in the depth direction using ToF-SIMS, a peak of concentration of each element contained in the first region 101, the second region 102, and the third region 103 can be detected.
However, clear boundaries between the first region 101, the second region 102, and the third region 103 are not necessarily observed by the analyses.
In this specification and the like, the third region 103 that is present in a superficial portion of the positive electrode active material 100 refers to a region from the surface of the positive electrode active material 100 to a region where a concentration of a representative element such as magnesium which is detected by analysis in the depth direction is ⅕ of a peak. As the analysis method, the line analysis of EDX, analysis in the depth direction using ToF-SIMS, or the like, which is described above, can be used.
A peak of the magnesium concentration is preferably present in a region from the surface of the positive electrode active material 100 to a depth of 3 nm toward the center, further preferably to a depth of 1 nm, and still further preferably to a depth of 0.5 nm.
Although the depth at which the magnesium concentration becomes ⅕ of the peak is different depending on the manufacturing method, in the case of a manufacturing method described later, the depth is approximately 2 nm to 5 nm from the surface of the positive electrode active material.
The third region 103 that is present inside the first region 101 in the vicinity of a grain boundary, a crystal defect, or the like also refers to a region where a concentration of a representative element which is detected by analysis in the depth direction is higher than or equal to ⅕ of a peak.
A distribution of fluorine in the positive electrode active material 100 preferably overlaps with a magnesium distribution. Thus, fluorine also has a concentration gradient, and a peak of a concentration of fluorine is preferably present in a region from the surface of the positive electrode active material 100 to a depth of 3 nm toward the center, further preferably to a depth of 1 nm, and still further preferably to a depth of 0.5 nm.
In this specification and the like, the second region 102 that is present in a superficial portion of the positive electrode active material 100 refers to a region where the aluminum concentration detected by analysis in the depth direction is higher than or equal to ½ of a peak. The second region 102 that is present inside the first region 101 in the vicinity of a grain boundary, a crystal defect, or the like also refers to a region where the aluminum concentration which is detected by analysis in the depth direction is higher than or equal to ½ of a peak. As the analysis method, the line analysis of EDX, analysis in the depth direction using ToF-SIMS, or the like, which is described above, can be used.
Thus, the third region 103 and the second region 102 overlap with each other in some cases. Note that the third region 103 is preferably present in a region closer to the surface of the positive electrode active material particle than the second region 102 is. The peak of the magnesium concentration is preferably present in a region closer to the surface of the positive electrode active material particle than the peak of the aluminum concentration is.
The peak of the aluminum concentration is preferably present at a depth of 0.5 nm or more and 20 nm or less from the surface of the positive electrode active material 100 toward the center, more preferably at a depth of 1 nm or more and 5 nm or less.
The concentrations of aluminum, magnesium, and fluorine can be analyzed by ToF-SIMS, EDX (planar analysis and line analysis), XPS, Auger electron spectroscopy, TDS, or the like.
Note that the measurement range by the XPS is from the surface of the positive electrode active material 100 to a region at a depth of approximately 5 nm. Thus, the element concentration at a depth of approximately 5 nm from the surface can be analyzed quantitatively. For this reason, when the thickness of the third region 103 is less than 5 nm from the surface, the element concentration of the sum of the third region 103 and part of the second region 102 can be quantitatively analyzed. When the thickness of the third region 103 is 5 nm or more from the surface, the element concentration of the third region 103 can be quantitatively analyzed.
In the XPS measurement from the surface of the positive electrode active material 100, the aluminum concentration is preferably 0.1 atomic % or more and 10 atomic % or less, more preferably 0.1 atomic % or more and 2 atomic % or less when the total amount of lithium, aluminum, the transition metal of the first region 101, magnesium, oxygen, and fluorine is taken as 100 atomic %. The magnesium concentration is preferably 5 atomic % or more and 20 atomic % or less. The fluorine concentration is preferably 3.5 atomic % or more and 14 atomic % or less.
Note that, as described above, elements contained in the first region 101, the second region 102, and the third region 103 may each have a concentration gradient; thus, the first region 101 may contain the element contained in the second region 102 or the third region 103. Similarly, the third region 103 may contain the element contained in the first region 101 or the second region 102. In addition, the first region 101, the second region 102, and the third region 103 may each contain another element, such as carbon, sulfur, silicon, sodium, calcium, chlorine, or zirconium.
[Covering of Second Region]
The second region 102 can be formed by covering a particle of the composite oxide of lithium and the transition metal with a material containing aluminum.
As the covering method with the material containing aluminum, a liquid phase method such as a sol-gel method, a solid phase method, a sputtering method, an evaporation method, a chemical vapor deposition (CVD) method, a pulsed laser deposition (PLD) method, or the like can be used. In this embodiment, the sol-gel method is used, by which uniform coverage is achieved under an atmospheric pressure.
In the case of using the sol-gel method, aluminum alkoxide is first dissolved in alcohol, the particle of the composite oxide containing lithium and a transition metal is mixed in the solution, and the mixture is stirred in an atmosphere containing water vapor. By placing it in an atmosphere containing H2O, hydrolysis and polycondensation reaction of water and aluminum alkoxide occur on the surface of the composite oxide particle containing lithium and a transition metal to form a gel-like layer containing aluminum on the particle surface. Then, the particle is collected and dried. The details of the formation method are described later.
Note that one embodiment of the present invention is not limited to the example shown in this embodiment in which the particle of the composite oxide containing lithium and the transition metal is covered with the material containing aluminum before the particle is applied to a positive electrode current collector. For another example, after the positive electrode active material layer including the particle of the composite oxide of lithium and the transition metal is formed on the positive electrode current collector, the positive electrode current collector and the positive electrode active material layer may be both soaked into an alkoxide solution.
[Segregation of Third Region]
The third region 103 can be formed also by a sputtering method, a solid phase method, a liquid phase method such as a sol-gel method, or the like. However, the present inventors found that when a source of magnesium and a source of fluorine are mixed with a material of the first region 101 and then the mixture is heated, the magnesium is segregated on a superficial portion of the positive electrode active material particle to form the third region 103. In addition, they found that the third region 103 formed in this manner contributes to excellent cycle characteristics of the positive electrode active material 100.
When the third region 103 is formed by segregation of magnesium in the superficial portion of the positive electrode active material particle by heating as described above, the heating is performed preferably after the particle of the composite oxide containing lithium, the transition metal, magnesium, and fluorine is covered with the material containing aluminum. This is because magnesium is surprisingly segregated in the superficial portion of the positive electrode active material particle even after the particle is covered with the material containing aluminum. The details of the formation method are described later.
Note that when the composite oxide containing lithium and the transition metal included in the first region 101 is a polycrystal or has crystal defects, magnesium can be segregated not only in the superficial portion but also in the vicinity of a grain boundary of the composite oxide containing lithium and the transition metal or in the vicinity of crystal defects thereof. The magnesium segregated in the vicinity of a grain boundary or in the vicinity of crystal defects can contribute to further improvement in stability of the crystal structure of the composite oxide containing lithium and the transition metal included in the first region 101.
When the ratio between magnesium and fluorine as raw materials is in the range of Mg:F=1:x (1.5≤x≤4) (atomic ratio), segregation of magnesium occurs effectively, which is preferable. The ratio is further preferably Mg:F=about 1:2 (atomic ratio).
Since the third region 103 formed by segregation is formed by epitaxial growth, orientations of crystals in the second region 102 and the third region 103 are partly and substantially aligned with each other in some cases. That is, the second region 102 and the third region 103 become topotaxy in some cases. When the orientations of crystals in the second region 102 and the third region 103 are substantially aligned with each other, these regions can serve as a more favorable covering layer.
Note that in this specification, a state where three-dimensional structures have similarity or orientations are crystallographically the same is referred to as “topotaxy”. Thus, in the case of topotaxy, when part of a cross section is observed, orientations of crystals in two regions (e.g., a region serving as a base and a region formed through growth) are substantially aligned with each other.
<Fourth Region 104>
It is to be noted that although the example in which the positive electrode active material 100 includes the first region 101, the second region 102, and the third region 103 has been described so far, one embodiment of the present invention is not limited thereto. For example, as illustrated in
[Formation Method]
An example of a formation method of the positive electrode active material 100 including the first region 101, the second region 102, and the third region 103 is described with reference to
First, a starting material is prepared (S11). As the starting material, a particle of composite oxide containing lithium, cobalt, fluorine, and magnesium is used.
First, to form the particle of the composite oxide containing lithium, cobalt, fluorine, and magnesium, a lithium source, a cobalt source, a magnesium source, and a fluorine source are individually weighed. As the lithium source, for example, lithium carbonate, lithium fluoride, or lithium hydroxide can be used. As the cobalt source, for example, cobalt oxide, cobalt hydroxide, cobalt oxyhydroxide, cobalt carbonate, cobalt oxalate, cobalt sulfate, or the like can be used. As a magnesium source, for example, magnesium oxide, magnesium fluoride, or the like can be used. As the fluorine source, for example, lithium fluoride, magnesium fluoride, or the like can be used. That is, lithium fluoride can be used as both a lithium source and a fluorine source. Magnesium fluoride can be used as a magnesium source or as a fluorine source.
The atomic ratio of magnesium to fluorine as raw materials is preferably Mg:F=1:x (1.5≤4), more preferably Mg:F=about 1:2 (atomic ratio). With the atomic ratio, magnesium segregation easily occurs in the heating process performed later.
Next, the weighed starting material is mixed. For example, a ball mill, a bead mill, or the like can be used for the mixing.
Then, the mixed starting material is baked. The baking is preferably performed at higher than or equal to 800° C. and lower than or equal to 1050° C., further preferably at higher than or equal to 900° C. and lower than or equal to 1000° C. The baking time is preferably greater than or equal to 2 hours and less than or equal to 20 hours. The baking is preferably performed in a dried atmosphere such as dry air. In the dried atmosphere, for example, the dew point is preferably lower than or equal to −50° C., further preferably lower than or equal to −100° C. In this embodiment, the heating is performed at 1000° C. for 10 hours, the temperature rising rate is 200° C./h, and dry air whose dew point is −109° C. flows at 10 L/min. After that, the heated materials are cooled to room temperature.
Through the above process, particles of a composite oxide containing lithium, cobalt, fluorine, and magnesium can be synthesized.
As the starting material, a particle of a composite oxide containing lithium and cobalt which are synthesized in advance may be used. For example, a lithium cobaltate particle (C-20F, produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD.) can be used as one of the starting material. The lithium cobaltate particle has a diameter of approximately 20 μm and contains fluorine, magnesium, calcium, sodium, silicon, sulfur, and phosphorus in a region which can be analyzed by XPS from the surface. In this embodiment, a lithium cobaltate particle (product name: C-20F) produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD.) is used as the starting material.
Then, the aluminum alkoxide is dissolved in alcohol, and a particle of the starting material is mixed into the solution (S12).
Examples of the aluminum alkoxide include trimethoxy aluminum, triethoxy aluminum, tri-n-propoxy aluminum, tri-i-propoxy aluminum, tri-n-butoxy aluminum, tri-i-butoxy aluminum, tri-sec-butoxy aluminum, tri-t-butoxy aluminum. As a solvent in which the aluminum alkoxide is dissolved, methanol, ethanol, propanol, 2-propanol, butanol, or 2-butanol is preferably used.
Note that the alkoxide group of the aluminum alkoxide and the alcohol used for the solvent may be of different types, but are particularly preferably of the same type.
Next, the mixed solution is stirred in an atmosphere containing water vapor (S13). By this treatment, H2O and aluminum isopropoxide in the atmosphere undergo hydrolysis and polycondensation reaction. Then, on the surface of a lithium cobaltate particle containing magnesium and fluorine, a gel-like layer containing aluminum is formed.
A magnetic stirrer can be used for the stirring, for example. The stirring time is not limited as long as water and aluminum isopropoxide in the atmosphere cause hydrolysis and polycondensation reaction. For example, the stirring can be performed at 25° C. and a humidity of 90% RH (Relative Humidity) for 4 hours.
By the reaction of aluminum alkoxide with water at room temperature as described above, a covering layer containing aluminum can have higher uniformity and quality than by heating at a temperature higher than the boiling point of alcohol as a solvent (e.g., 100° C. or higher).
After the above process, precipitate is collected from the mixed solution (S14). As the collection method, filtration, centrifugation, evaporation and drying, or the like can be used. In this embodiment, filtration is used. For the filtration, a paper filter is used, and the residue is washed by alcohol which is the same as the solvent in which aluminum alkoxide is dissolved.
Then, the collected residue is dried (S15). In this embodiment, vacuum drying is performed at 70° C. for one hour.
Next, the dried powder is heated (S16). By the heating, magnesium and fluorine contained in the starting material are segregated on the surface to form the third region 103.
In the heating, the retention time within a specified temperature range is preferably shorter than or equal to 50 hours, further preferably longer than or equal to 1 hour and shorter than or equal to 10 hours. The specified temperatures are temperatures for the retention. The specified temperature is preferably higher than or equal to 500° C. and lower than or equal to 1200° C., further preferably higher than or equal to 700° C. and lower than or equal to 1000° C., still further preferably about 800° C. The heating is preferably performed in an oxygen-containing atmosphere. In this embodiment, the specified temperature is 800° C. and kept for 2 hours, the temperature rising rate is 200° C./h, and the flow rate of dry air is 10 L/min. The cooing is performed for the same time as the time of increasing temperature, or longer.
Then, the heated powders are preferably cooled and subjected to crushing treatment (S17). For example, a sieve can be used for the crushing treatment.
Through the above process, the positive electrode active material 100 of one embodiment of the present invention can be formed.
In this embodiment, examples of materials which can be used for a secondary battery containing the positive electrode active material 100 described in the above embodiment are described. In this embodiment, a secondary battery in which a positive electrode, a negative electrode, and an electrolyte solution are wrapped in an exterior body is described as an example.
[Positive Electrode]
The positive electrode includes a positive electrode active material layer and a positive electrode current collector.
<Positive Electrode Active Material Layer>
The positive electrode active material layer contains a positive electrode active material. The positive electrode active material layer may contain a conductive additive and a binder.
As the positive electrode active material, the positive electrode active material 100 described in the above embodiment can be used. When the above-described positive electrode active material 100 is used, a secondary battery with high capacity and excellent cycle characteristics can be obtained.
Examples of the conductive additive include a carbon material, a metal material, and a conductive ceramic material. Alternatively, a fiber material may be used as the conductive additive. The content of the conductive additive with respect to the total amount of the active material layer is preferably greater than or equal to 1 wt % and less than or equal to 10 wt %, more preferably greater than or equal to 1 wt % and less than or equal to 5 wt %.
A network for electric conduction can be formed in the electrode by the conductive additive. The conductive additive also allows maintaining of a path for electric conduction between the positive electrode active material particles. The addition of the conductive additive to the active material layer increases the electric conductivity of the active material layer.
Examples of the conductive additive include natural graphite, artificial graphite such as mesocarbon microbeads, and carbon fiber. Examples of carbon fiber include mesophase pitch-based carbon fiber, isotropic pitch-based carbon fiber, carbon nanofiber, and carbon nanotube. Carbon nanotube can be formed by, for example, a vapor deposition method. Other examples of the conductive additive include carbon materials such as carbon black (e.g., acetylene black (AB)), graphite (black lead) particles, graphene, and fullerene. Alternatively, metal powder or metal fibers of copper, nickel, aluminum, silver, gold, or the like, a conductive ceramic material, or the like can be used.
Alternatively, a graphene compound may be used as the conductive additive.
A graphene compound has excellent electrical characteristics of high conductivity and excellent physical properties of high flexibility and high mechanical strength. Furthermore, a graphene compound has a planar shape. A graphene compound enables low-resistance surface contact. Furthermore, a graphene compound has extremely high conductivity even with a small thickness in some cases and thus allows a conductive path to be formed in an active material layer efficiently even with a small amount. For this reason, it is preferable to use a graphene compound as the conductive additive because the area where the active material and the conductive additive are in contact with each other can be increased. Here, it is particularly preferable to use, for example, graphene, multilayer graphene, or reduced graphene oxide (hereinafter “RGO”) as a graphene compound. Note that RGO refers to a compound obtained by reducing graphene oxide (GO), for example.
In the case where an active material with a small particle diameter (e.g., 1 μm or less) is used, the specific surface area of the active material is large and thus more conductive paths for the active material particles are needed. Thus, the amount of conductive additive tends to increase and the supported amount of active material tends to decrease relatively. When the supported amount of active material decreases, the capacity of the secondary battery also decreases. In such a case, a graphene compound that can efficiently form a conductive path even in a small amount is particularly preferably used as the conductive additive because the supported amount of active material does not decrease.
A cross-sectional structure example of an active material layer 200 containing a graphene compound as a conductive additive is described below.
The longitudinal cross section of the active material layer 200 in
Here, the plurality of graphene compounds are bonded to each other to form a net-like graphene compound sheet (hereinafter referred to as a graphene compound net or a graphene net). The graphene net covering the active material can function as a binder for bonding active materials. The amount of a binder can thus be reduced, or the binder does not have to be used. This can increase the proportion of the active material in the electrode volume or weight. That is to say, the capacity of the storage device can be increased.
Here, it is preferable to perform reduction after a layer to be the active material layer 200 is formed in such a manner that graphene oxide is used as the graphene compound 201 and mixed with an active material. When graphene oxide with extremely high dispersibility in a polar solvent is used for the formation of the graphene compounds 201, the graphene compounds 201 can be substantially uniformly dispersed in the active material layer 200. The solvent is removed by volatilization from a dispersion medium in which graphene oxide is uniformly dispersed, and the graphene oxide is reduced; hence, the graphene compounds 201 remaining in the active material layer 200 partly overlap with each other and are dispersed such that surface contact is made, thereby forming a three-dimensional conduction path. Note that graphene oxide can be reduced either by heat treatment or with the use of a reducing agent, for example.
Unlike a conductive additive in the form of particles, such as acetylene black, which makes point contact with an active material, the graphene compound 201 is capable of making low-resistance surface contact; accordingly, the electrical conduction between the positive electrode active material particles 100 and the graphene compounds 201 can be improved with a smaller amount of the graphene compound 201 than that of a normal conductive additive. This increases the proportion of the positive electrode active material 100 in the active material layer 200, resulting in increased discharge capacity of the storage device.
As the binder, a rubber material such as styrene-butadiene rubber (SBR), styrene-isoprene-styrene rubber, acrylonitrile-butadiene rubber, butadiene rubber, or ethylene-propylene-diene copolymer can be used, for example. Alternatively, fluororubber can be used as the binder.
For the binder, for example, water-soluble polymers are preferably used. As the water-soluble polymers, a polysaccharide and the like can be used. As the polysaccharide, a cellulose derivative such as carboxymethyl cellulose (CMC), methyl cellulose, ethyl cellulose, hydroxypropyl cellulose, diacetyl cellulose, or regenerated cellulose, starch, or the like can be used. It is more preferred that such water-soluble polymers be used in combination with any of the above rubber materials.
Alternatively, as the binder, a material such as polystyrene, poly(methyl acrylate), poly(methyl methacrylate) (PMMA), sodium polyacrylate, polyvinyl alcohol (PVA), polyethylene oxide (PEO), polypropylene oxide, polyimide, polyvinyl chloride, polytetrafluoroethylene, polyethylene, polypropylene, polyisobutylene, polyethylene terephthalate, nylon, polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), ethylene-propylene-diene polymer, polyvinyl acetate, or nitrocellulose is preferably used.
A plurality of the above materials may be used in combination for the binder.
For example, a material having a significant viscosity modifying effect and another material may be used in combination. For example, a rubber material or the like has high adhesion or high elasticity but may have difficulty in viscosity modification when mixed in a solvent. In such a case, a rubber material or the like is preferably mixed with a material having a significant viscosity modifying effect, for example. As a material having a significant viscosity modifying effect, for example, a water-soluble polymer is preferably used. An example of a water-soluble polymer having an especially significant viscosity modifying effect is the above-mentioned polysaccharide; for example, a cellulose derivative such as carboxymethyl cellulose (CMC), methyl cellulose, ethyl cellulose, hydroxypropyl cellulose, diacetyl cellulose, or regenerated cellulose, or starch can be used.
Note that a cellulose derivative such as carboxymethyl cellulose obtains a higher solubility when converted into a salt such as a sodium salt or an ammonium salt of carboxymethyl cellulose, and accordingly, easily exerts an effect as a viscosity modifier. The high solubility can also increase the dispersibility of an active material and other components in the formation of shiny for an electrode. In this specification, cellulose and a cellulose derivative used as a binder of an electrode include salts thereof.
The water-soluble polymers stabilize viscosity by being dissolved in water and allow stable dispersion of the active material and another material combined as a binder such as styrene-butadiene rubber in an aqueous solution. Furthermore, a water-soluble polymer is expected to be easily and stably adsorbed to an active material surface because it has a functional group. Many cellulose derivatives such as carboxymethyl cellulose have functional groups such as a hydroxyl group and a carboxyl group. Because of functional groups, polymers are expected to interact with each other and cover an active material surface in a large area.
In the case where the binder covering or being in contact with the active material surface forms a film, the film is expected to serve as a passivation film to suppress the decomposition of the electrolyte solution. Here, the passivation film refers to a film without electric conductivity or a film with extremely low electric conductivity, and can inhibit the decomposition of an electrolyte solution at a potential at which a battery reaction occurs in the case where the passivation film is formed on the active material surface, for example. It is preferred that the passivation film can conduct lithium ions while suppressing electric conduction.
<Positive Electrode Current Collector>
The positive electrode current collector can be formed using a material that has high conductivity, such as a metal like stainless steel, gold, platinum, aluminum, or titanium, or an alloy thereof. It is preferred that a material used for the positive electrode current collector not dissolve at the potential of the positive electrode. Alternatively, the positive electrode current collector can be formed using an aluminum alloy to which an element that improves heat resistance, such as silicon, titanium, neodymium, scandium, or molybdenum, is added. Still alternatively, a metal element that forms silicide by reacting with silicon can be used. Examples of the metal element that forms silicide by reacting with silicon include zirconium, titanium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten, cobalt, and nickel. The current collector can have any of various shapes including a foil-like shape, a plate-like shape (sheet-like shape), a net-like shape, a punching-metal shape, and an expanded-metal shape. The current collector preferably has a thickness of 5 μm to 30 μm.
[Negative Electrode]
The negative electrode includes a negative electrode active material layer and a negative electrode current collector. The negative electrode active material layer may contain a conductive additive and a binder.
<Negative Electrode Active Material>
As a negative electrode active material, for example, an alloy-based material or a carbon-based material can be used.
For the negative electrode active material, an element which enables charge-discharge reactions by an alloying reaction and a dealloying reaction with lithium can be used. For example, a material containing at least one of silicon, tin, gallium, aluminum, germanium, lead, antimony, bismuth, silver, zinc, cadmium, indium, and the like can be used. Such elements have higher capacity than carbon. In particular, silicon has a significantly high theoretical capacity of 4200 mAh/g. For this reason, silicon is preferably used as the negative electrode active material. Alternatively, a compound containing any of the above elements may be used. Examples of the compound include SiO, Mg2Si, Mg2Ge, SnO, SnO2, Mg2Sn, SnS2, V2Sn3, FeSn2, CoSn2, Ni3Sn2, Cu6Sn5, Ag3Sn, Ag3Sb, Ni2MnSb, CeSb3, LaSn3, La3Co2Sn7, CoSb3, InSb, and SbSn. Here, an element that enables charge-discharge reactions by an alloying reaction and a dealloying reaction with lithium, a compound containing the element, and the like may be referred to as an alloy-based material.
In this specification and the like, SiO refers, for example, to silicon monoxide. SiO can alternatively be expressed as SiOx. Here, x preferably has an approximate value of 1. For example, x is preferably 0.2 or more and 1.5 or less, more preferably 0.3 or more and 1.2 or less.
As the carbon-based material, graphite, graphitizing carbon (soft carbon), non-graphitizing carbon (hard carbon), a carbon nanotube, graphene, carbon black, and the like can be used.
Examples of graphite include artificial graphite and natural graphite. Examples of artificial graphite include meso-carbon microbeads (MCMB), coke-based artificial graphite, and pitch-based artificial graphite. As artificial graphite, spherical graphite having a spherical shape can be used. For example, MCMB is preferably used because it may have a spherical shape. Moreover, MCMB may preferably be used because it can relatively easily have a small surface area. Examples of natural graphite include flake graphite and spherical natural graphite.
Graphite has a low potential substantially equal to that of a lithium metal (higher than or equal to 0.05 V and lower than or equal to 0.3 V vs. Li/Li+) when lithium ions are intercalated into the graphite (while a lithium-graphite intercalation compound is formed). For this reason, a lithium-ion secondary battery can have a high operating voltage. In addition, graphite is preferred because of its advantages such as a relatively high capacity per unit volume, relatively small volume expansion, low cost, and higher level of safety than that of a lithium metal.
Alternatively, for the negative electrode active material, an oxide such as titanium dioxide (TiO2), lithium titanium oxide (Li4Ti5O12), lithium-graphite intercalation compound (LixC6), niobium pentoxide (Nb2O5), tungsten oxide (WO2), or molybdenum oxide (MoO2) can be used.
Still alternatively, for the negative electrode active material, Li3-xMxN=Co, Ni, or Cu) with a Li3N structure, which is a nitride containing lithium and a transition metal, can be used. For example, Li2.6Co0.4N3 is preferable because of high charge and discharge capacity (900 mAh/g and 1890 mAh/cm3).
A nitride containing lithium and a transition metal is preferably used, in which case lithium ions are contained in the negative electrode active material and thus the negative electrode active material can be used in combination with a material for a positive electrode active material which does not contain lithium ions, such as V2O5 or Cr3O8. In the case of using a material containing lithium ions as a positive electrode active material, the nitride containing lithium and a transition metal can be used for the negative electrode active material by extracting the lithium ions contained in the positive electrode active material in advance.
Alternatively, a material which causes a conversion reaction can be used for the negative electrode active material; for example, a transition metal oxide which does not form an alloy with lithium, such as cobalt oxide (CoO), nickel oxide (NiO), and iron oxide (FeO), may be used. Other examples of the material which causes a conversion reaction include oxides such as Fe2O3, CuO, Cu2O, RuO2, and Cr2O3, sulfides such as CoS0.89, NiS, and CuS, nitrides such as Zn3N2, Cu3N, and Ge3N4, phosphides such as NiP2, FeP2, and CoP3, and fluorides such as FeF3 and BiF3.
For the conductive additive and the binder that can be included in the negative electrode active material layer, materials similar to those of the conductive additive and the binder that can be included in the positive electrode active material layer can be used.
<Negative Electrode Current Collector>
For the negative electrode current collector, a material similar to that of the positive electrode current collector can be used. Note that a material which is not alloyed with a carrier ion such as lithium is preferably used for the negative electrode current collector.
[Electrolyte Solution]
The electrolyte solution contains a solvent and an electrolyte. As a solvent of the electrolyte solution, an aprotic organic solvent is preferably used. For example, one of ethylene carbonate (EC), propylene carbonate (PC), butylene carbonate, chloroethylene carbonate, vinylene carbonate, γ-butyrolactone, γ-valerolactone, dimethyl carbonate (DMC), diethyl carbonate (DEC), ethyl methyl carbonate (EMC), methyl formate, methyl acetate, ethyl acetate, methyl propionate, ethyl propionate, propyl propionate, methyl butyrate, 1,3-dioxane, 1,4-dioxane, dimethoxyethane (DME), dim ethyl sulfoxide, diethyl ether, methyl diglyme, acetonitrile, benzonitrile, tetrahydrofuran, sulfolane, and sultone can be used, or two or more of these solvents can be used in an appropriate combination in an appropriate ratio.
When a gelled high-molecular material is used as the solvent of the electrolytic solution, safety against liquid leakage and the like is improved. Furthermore, a secondary battery can be thinner and more lightweight. Typical examples of gelled high-molecular materials include a silicone gel, an acrylic gel, an acrylonitrile gel, a polyethylene oxide-based gel, a polypropylene oxide-based gel, a gel of a fluorine-based polymer, and the like.
Alternatively, when one or more kinds of ionic liquids (room temperature molten salts) which have features of non-flammability and non-volatility is used as a solvent of the electrolyte solution, a secondary battery can be prevented from exploding or catching fire even when the secondary battery internally shorts out or the internal temperature increases owing to overcharging or the like. An ionic liquid contains a cation and an anion. The ionic liquid contains an organic cation and an anion. Examples of the organic cation used for the electrolyte solution include aliphatic onium cations such as a quaternary ammonium cation, a tertiary sulfonium cation, and a quaternary phosphonium cation, and aromatic cations such as an imidazolium cation and a pyridinium cation. Examples of the anion used for the electrolyte solution include a monovalent amide-based anion, a monovalent methide-based anion, a fluorosulfonate anion, a perfluoroalkylsulfonate anion, a tetrafluoroborate anion, a perfluoroalkylborate anion, a hexafluorophosphate anion, and a perfluoroalkylphosphate anion.
As an electrolyte dissolved in the above-described solvent, one of lithium salts such as LiPF6, LiClO4, LiAsF6, LiBF4, LiAlCl4, Li SCN, LiBr, LiI, Li2SO4, Li2B10Cl10, Li2B12Cl12, LiCF3SO3, LiC4F9SO3, LiC(CF3SO2)3, LiC(C2F5SO2)3, LiN(CF3SO2)2, LiN(C4F9SO2) (CF3SO2), and LiN(C2F5SO2)2 can be used, or two or more of these lithium salts can be used in an appropriate combination in an appropriate ratio.
The electrolyte solution used for a storage device is preferably highly purified and contains a small amount of dust particles and elements other than the constituent elements of the electrolyte solution (hereinafter also simply referred to as impurities). Specifically, the weight ratio of impurities to the electrolyte solution is less than or equal to 1%, preferably less than or equal to 0.1%, and further preferably less than or equal to 0.01%.
Furthermore, an additive agent such as vinylene carbonate, propane sultone (PS), tert-butylbenzene (TBB), fluoroethylene carbonate (FEC), LiBOB, or a dinitrile compound such as succinonitrile or adiponitrile may be added to the electrolyte solution. The concentration of a material to be added with respect to the whole solvent is, for example, higher than or equal to 0.1 wt % and lower than or equal to 5 wt %.
Alternatively, a gelled electrolyte obtained in such a manner that a polymer is swelled with an electrolyte solution may be used.
Examples of the polymer include a polymer having a polyalkylene oxide structure, such as polyethylene oxide (PEO); PVDF; polyacrylonitrile; and a copolymer containing any of them. For example, PVDF-HFP, which is a copolymer of PVDF and hexafluoropropylene (HFP) can be used. The formed polymer may be porous.
Instead of the electrolyte solution, a solid electrolyte including an inorganic material such as a sulfide-based inorganic material or an oxide-based inorganic material, or a solid electrolyte including a high-molecular material such as a polyethylene oxide (PEO)-based high-molecular material may alternatively be used. When the solid electrolyte is used, a separator and a spacer are not necessary. Furthermore, since the battery can be entirely solidified, there is no possibility of liquid leakage to increase the safety of the battery dramatically.
[Separator]
The secondary battery preferably includes a separator. As the separator, for example, fiber containing cellulose such as paper; nonwoven fabric; glass fiber; ceramics; or synthetic fiber using nylon (polyamide), vinylon (polyvinyl alcohol-based fiber), polyester, acrylic, polyolefin, or polyurethane can be used. The separator is preferably formed to have an envelope-like shape to wrap one of the positive electrode and the negative electrode.
The separator may have a multilayer structure. For example, an organic material film such as polypropylene or polyethylene can be coated with a ceramic-based material, a fluorine-based material, a polyamide-based material, a mixture thereof, or the like. Examples of the ceramic-based material include aluminum oxide particles and silicon oxide particles. Examples of the fluorine-based material include PVDF and a polytetrafluoroethylene. Examples of the polyamide-based material include nylon and aramid (meta-based aramid and para-based aramid).
Deterioration of the separator in charging and discharging at high voltage can be suppressed and thus the reliability of the secondary battery can be improved because oxidation resistance is improved when the separator is coated with the ceramic-based material. In addition, when the separator is coated with the fluorine-based material, the separator is easily brought into close contact with an electrode, resulting in high output characteristics. When the separator is coated with the polyamide-based material, in particular, aramid, the safety of the secondary battery is improved because heat resistance is improved.
For example, both surfaces of a polypropylene film may be coated with a mixed material of aluminum oxide and aramid. Alternatively, a surface of the polypropylene film in contact with the positive electrode may be coated with the mixed material of aluminum oxide and aramid, and a surface of the polypropylene film in contact with the negative electrode may be coated with the fluorine-based material.
With the use of a separator having a multilayer structure, the capacity of the secondary battery per volume can be increased because the safety of the secondary battery can be maintained even when the total thickness of the separator is small.
In this embodiment, examples of a shape of a secondary battery containing the positive electrode active material 100 described in the above embodiment are described. For the materials used for the secondary battery described in this embodiment, the description of the above embodiment can be referred to.
[Coin-Type Secondary Battery]
First, an example of a coin-type secondary battery is described.
In a coin-type secondary battery 300, a positive electrode can 301 doubling as a positive electrode terminal and a negative electrode can 302 doubling as a negative electrode terminal are insulated from each other and sealed by a gasket 303 made of polypropylene or the like. A positive electrode 304 includes a positive electrode current collector 305 and a positive electrode active material layer 306 provided in contact with the positive electrode current collector 305. A negative electrode 307 includes a negative electrode current collector 308 and a negative electrode active material layer 309 provided in contact with the negative electrode current collector 308.
Note that only one surface of each of the positive electrode 304 and the negative electrode 307 used for the coin-type secondary battery 300 is provided with an active material layer.
For the positive electrode can 301 and the negative electrode can 302, a metal having a corrosion-resistant property to an electrolyte solution, such as nickel, aluminum, or titanium, an alloy of such a metal, or an alloy of such a metal and another metal (e.g., stainless steel) can be used. Alternatively, the positive electrode can 301 and the negative electrode can 302 are preferably covered with nickel, aluminum, or the like in order to prevent corrosion due to the electrolyte solution. The positive electrode can 301 and the negative electrode can 302 are electrically connected to the positive electrode 304 and the negative electrode 307, respectively.
The negative electrode 307, the positive electrode 304, and the separator 310 are immersed in the electrolyte solution. Then, as illustrated in
When the positive electrode active material described in the above embodiment is used in the positive electrode 304, the coin-type secondary battery 300 with high capacity and excellent cycle characteristics can be obtained.
[Cylindrical Secondary Battery]
Next, an example of a cylindrical secondary battery will be described with reference to
Since the positive electrode and the negative electrode of the cylindrical secondary battery are wound, active materials are preferably formed on both sides of the current collectors. A positive electrode terminal (positive electrode current collecting lead) 603 is connected to the positive electrode 604, and a negative electrode terminal (negative electrode current collecting lead) 607 is connected to the negative electrode 606. Both the positive electrode terminal 603 and the negative electrode terminal 607 can be formed using a metal material such as aluminum. The positive electrode terminal 603 and the negative electrode terminal 607 are resistance-welded to a safety valve mechanism 612 and the bottom of the battery can 602, respectively. The safety valve mechanism 612 is electrically connected to the positive electrode cap 601 through a positive temperature coefficient (PTC) element 611. The safety valve mechanism 612 cuts off electrical connection between the positive electrode cap 601 and the positive electrode 604 when the internal pressure of the battery exceeds a predetermined threshold value. The PTC element 611, which serves as a thermally sensitive resistor whose resistance increases as temperature rises, limits the amount of current by increasing the resistance, in order to prevent abnormal heat generation. Barium titanate (BaTiO3)-based semiconductor ceramic can be used for the PTC element.
When the positive electrode active material described in the above embodiment is used in the positive electrode 604, the cylindrical secondary battery 600 with high capacity and excellent cycle characteristics can be obtained.
[Structural Example of Power Storage Device]
Other structural examples of power storage devices will be described with reference to
The circuit board 900 includes terminals 911 and a circuit 912. The terminals 911 are connected to the terminals 951 and 952, the antennas 914 and 915, and the circuit 912. Note that a plurality of terminals 911 serving as a control signal input terminal, a power supply terminal, and the like may be provided.
The circuit 912 may be provided on the rear surface of the circuit board 900. The shape of each of the antennas 914 and 915 is not limited to a coil shape and may be a linear shape or a plate shape. Further, a planar antenna, an aperture antenna, a traveling-wave antenna, an EH antenna, a magnetic-field antenna, or a dielectric antenna may be used. Alternatively, the antenna 914 or the antenna 915 may be a flat-plate conductor. The flat-plate conductor can serve as one of conductors for electric field coupling. That is, the antenna 914 or the antenna 915 can serve as one of two conductors of a capacitor. Thus, electric power can be transmitted and received not only by an electromagnetic field or a magnetic field but also by an electric field.
The line width of the antenna 914 is preferably larger than that of the antenna 915. This makes it possible to increase the amount of electric power received by the antenna 914.
The power storage device includes a layer 916 between the secondary battery 913 and the antennas 914 and 915. The layer 916 has a function of blocking an electromagnetic field from the secondary battery 913, for example. As the layer 916, for example, a magnetic body can be used.
Note that the structure of the power storage device is not limited to that shown in
For example, as shown in FIGS. 7A1 and 7A2, two opposite surfaces of the secondary battery 913 in
As illustrated in FIG. 7A1, the antenna 914 is provided on one of the opposing surfaces of the secondary battery 913 with the layer 916 provided therebetween. As illustrated in FIG. 7A2, the antenna 915 is provided on the other of the opposing surfaces of the secondary battery 913 with the layer 917 provided therebetween. The layer 917 may have a function of preventing an adverse effect on an electromagnetic field by the secondary battery 913, for example. As the layer 917, for example, a magnetic body can be used.
With the above structure, both of the antennas 914 and 915 can be increased in size.
Alternatively, as illustrated in FIG. 7B2, the secondary battery 913 illustrated in
As illustrated in FIG. 7B1, the antennas 914 and 915 are provided on one of the opposite surfaces of the secondary battery 913 with the layer 916 interposed therebetween. As illustrated in FIG. 7B2, an antenna 918 is provided on the other of the opposite surfaces of the secondary battery 913 with the layer 917 interposed therebetween. The antenna 918 has a function of communicating data with an external device, for example. An antenna with a shape that can be applied to the antennas 914 and 915, for example, can be used as the antenna 918. As a system for communication using the antenna 918 between the power storage device and another device, a response method that can be used between the power storage device and another device, such as NFC, can be employed.
Alternatively, as illustrated in
The display device 920 can display, for example, an image showing whether charging is being carried out, an image showing the amount of stored power, or the like. As the display device 920, electronic paper, a liquid crystal display device, an electroluminescent (EL) display device, or the like can be used. For example, the use of electronic paper can reduce power consumption of the display device 920.
Alternatively, as illustrated in
The sensor 921 has a function of measuring, for example, displacement, position, speed, acceleration, angular velocity, rotational frequency, distance, light, liquid, magnetism, temperature, chemical substance, sound, time, hardness, electric field, electric current, voltage, electric power, radiation, flow rate, humidity, gradient, oscillation, odor, or infrared rays. With the sensor 921, for example, data on an environment (e.g., temperature) where the storage device is placed can be determined and stored in a memory inside the circuit 912.
Furthermore, structural examples of the secondary battery 913 will be described with reference to
The secondary battery 913 illustrated in
Note that as illustrated in
For the housing 930a, an insulating material such as an organic resin can be used. In particular, when a material such as an organic resin is used for the side on which an antenna is formed, blocking of an electric field from the secondary battery 913 can be inhibited. When an electric field is not significantly blocked by the housing 930a, an antenna such as the antennas 914 and 915 may be provided inside the housing 930a. For the housing 930b, a metal material can be used, for example.
The negative electrode 931 is connected to the terminal 911 in
When the positive electrode active material described in the above embodiment is used in the positive electrode 932, the secondary battery 913 with high capacity and excellent cycle characteristics can be obtained.
[Laminated Secondary Battery]
Next, an example of a laminated secondary battery will be described with reference to
A laminated secondary battery 980 is described with reference to
Note that the number of stacks each including the negative electrode 994, the positive electrode 995, and the separator 996 may be determined as appropriate depending on capacity and an element volume which are required. The negative electrode 994 is connected to a negative electrode current collector (not illustrated) via one of a lead electrode 997 and a lead electrode 998. The positive electrode 995 is connected to a positive electrode current collector (not illustrated) via the other of the lead electrode 997 and the lead electrode 998.
As illustrated in
For the film 981 and the film 982 having a depressed portion, a metal material such as aluminum or a resin material can be used, for example. With the use of a resin material for the film 981 and the film 982 having a depressed portion, the film 981 and the film 982 having a depressed portion can be changed in their forms when external force is applied; thus, a flexible secondary battery can be fabricated.
Although
When the positive electrode active material described in the above embodiment is used in the positive electrode 995, the secondary battery 980 with high capacity and excellent cycle characteristics can be obtained.
In
A laminated secondary battery 500 illustrated in
In the laminated secondary battery 500 illustrated in
As the exterior body 509 of the laminated secondary battery 500, for example, a laminate film having a three-layer structure can be employed in which a highly flexible metal thin film of aluminum, stainless steel, copper, nickel, or the like is provided over a film formed of a material such as polyethylene, polypropylene, polycarbonate, ionomer, or polyamide, and an insulating synthetic resin film of a polyamide-based resin, a polyester-based resin, or the like is provided over the metal thin film as the outer surface of the exterior body.
The example in
[Method for Manufacturing Laminated Secondary Battery]
Here, an example of a method for manufacturing the laminated secondary battery whose external view is illustrated in
First, the negative electrode 506, the separator 507, and the positive electrode 503 are stacked.
After that, the negative electrode 506, the separator 507, and the positive electrode 503 are placed over the exterior body 509.
Subsequently, the exterior body 509 is folded along a dashed line as illustrated in
Next, the electrolyte solution 508 is introduced into the exterior body 509 from the inlet of the exterior body 509. The electrolyte solution 508 is preferably introduced in a reduced pressure atmosphere or in an inert gas atmosphere. Lastly, the inlet is bonded. In the above manner, the laminated secondary battery 500 can be manufactured.
When the positive electrode active material described in the above embodiment is used in the positive electrode 503, the secondary battery 500 with high capacity and excellent cycle characteristics can be obtained.
[Bendable Secondary Battery]
Next, an example of a bendable secondary battery is described with reference to
As illustrated in
The positive electrodes 211a and the negative electrodes 211b are stacked so that surfaces of the positive electrodes 211a on each of which the positive electrode active material layer is not formed are in contact with each other and that surfaces of the negative electrodes 211b on each of which the negative electrode active material layer is not formed are in contact with each other.
Furthermore, the separator 214 is provided between the surface of the positive electrode 211a on which the positive electrode active material is formed and the surface of the negative electrode 211b on which the negative electrode active material is formed. In
In addition, as illustrated in
Next, the exterior body 251 is described with reference to FIGS. 16B1, 16B2, 16C, and 16D.
The exterior body 251 has a film-like shape and is folded in half with the positive electrodes 211a and the negative electrodes 211b between facing portions of the exterior body 251. The exterior body 251 includes a folded portion 261, a pair of seal portions 262, and a seal portion 263. The pair of seal portions 262 is provided with the positive electrodes 211a and the negative electrodes 211b positioned therebetween and thus can also be referred to as side seals. The seal portion 263 has portions overlapping with the lead 212a and the lead 212b and can also be referred to as a top seal.
Part of the exterior body 251 that overlaps with the positive electrodes 211a and the negative electrodes 211b preferably has a wave shape in which crest lines 271 and trough lines 272 are alternately arranged. The seal portions 262 and the seal portion 263 of the exterior body 251 are preferably flat.
FIG. 16B1 shows a cross section cut along the part overlapping with the crest line 271. FIG. 16B2 shows a cross section cut along the part overlapping with the trough line 272. FIGS. 16B1 and 16 B2 correspond to cross sections of the battery 250, the positive electrodes 211a, and the negative electrodes 211b in the width direction.
The distance between an end portion of the negative electrode 211b in the width direction and the seal portion 262 is referred to as a distance La. When the battery 250 changes in shape, for example, is bent, the positive electrode 211a and the negative electrode 211b change in shape such that the positions thereof are shifted from each other in the length direction as described later. At the time, if the distance La is too short, the exterior body 251 and the positive electrode 211a and the negative electrode 211b are rubbed hard against each other, so that the exterior body 251 is damaged in some cases. In particular, when a metal film of the exterior body 251 is exposed, there is concern that the metal film is corroded by the electrolyte solution. Thus, the distance La is preferably set as long as possible. However, if the distance La is too long, the volume of the battery 250 is increased.
The distance La between the end portion of the negative electrode 211b and the seal portion 262 is preferably increased as the total thickness of the stacked positive electrodes 211a and negative electrodes 211b is increased.
Specifically, when the total thickness of the stacked positive electrodes 211a and negative electrodes 211b and the separators 214 (not illustrated) is referred to as a thickness t, the distance La is preferably 0.8 times or more and 3.0 times or less, further preferably 0.9 times or more and 2.5 times or less, still further preferably 1.0 times or more and 2.0 times or less as large as the thickness t. When the distance La is in the above-described range, a compact battery which is highly reliable for bending can be obtained.
Furthermore, when a distance between the pair of seal portions 262 is referred to as a distance Lb, it is preferable that the distance Lb be sufficiently longer than a width Wb of the negative electrode 211b. In this case, even when the positive electrode 211a and the negative electrode 211b come into contact with the exterior body 251 by change in the shape of the battery 250 such as repeated bending, the position of part of the positive electrode 211a and the negative electrode 211b can be shifted in the width direction; thus, the positive and negative electrodes 211a and 211b and the exterior body 251 can be effectively prevented from being rubbed against each other.
For example, the difference between the distance Lb (i.e., the distance between the pair of seal portions 262) and the width Wb of the negative electrode 211b is preferably 1.6 times or more and 6.0 times or less, further preferably 1.8 times or more and 5.0 times or less, still further preferably 2.0 times or more and 4.0 times or less as large as the total thickness t of the positive electrode 211a and the negative electrode 211b.
In other words, the distance Lb, the width Wb, and the thickness t preferably satisfy the relation of the following Formula 1.
In the formula, a is 0.8 or more and 3.0 or less, preferably 0.9 or more and 2.5 or less, further preferably 1.0 or more and 2.0 or less.
When the battery 250 is bent, a part of the exterior body 251 positioned on the outer side in bending is unbent and the other part positioned on the inner side changes its shape as it shrinks. More specifically, the part of the exterior body 251 positioned on the outer side in bending changes its shape such that the wave amplitude becomes smaller and the length of the wave period becomes larger. In contrast, the part of the exterior body 251 positioned on the inner side in bending changes its shape such that the wave amplitude becomes larger and the length of the wave period becomes smaller. When the exterior body 251 changes its shape in this manner, stress applied to the exterior body 251 due to bending is relieved, so that a material itself that forms the exterior body 251 does not need to expand and contract. As a result, the battery 250 can be bent with weak force without damage to the exterior body 251.
Furthermore, as illustrated in
Furthermore, the space 273 is provided between the end portions of the positive and negative electrodes 211a and 211b and the exterior body 251, whereby the relative positions of the positive electrode 211a and the negative electrode 211b can be shifted while the end portions of the positive electrode 211a and the negative electrode 211b located on an inner side when the battery 250 is bent do not contact the exterior body 251.
In the battery 250 illustrated in
In this embodiment, examples of electronic devices including the secondary battery of one embodiment of the present invention are described.
First,
In addition, a flexible secondary battery can be incorporated along a curved inside/outside wall surface of a house or a building or a curved interior/exterior surface of an automobile.
The portable information terminal 7200 is capable of executing a variety of applications such as mobile phone calls, e-mailing, viewing and editing texts, music reproduction, Internet communication, and a computer game.
The display surface of the display portion 7202 is curved, and images can be displayed on the curved display surface. In addition, the display portion 7202 includes a touch sensor, and operation can be performed by touching the screen with a finger, a stylus, or the like. For example, by touching an icon 7207 displayed on the display portion 7202, application can be started.
With the operation button 7205, a variety of functions such as time setting, power on/off, on/off of wireless communication, setting and cancellation of a silent mode, and setting and cancellation of a power saving mode can be performed. For example, the functions of the operation button 7205 can be set freely by setting the operation system incorporated in the portable information terminal 7200.
The portable information terminal 7200 can employ near field communication that is a communication method based on an existing communication standard. For example, mutual communication between the portable information terminal 7200 and a headset capable of wireless communication can be performed, and thus hands-free calling is possible.
Moreover, the portable information terminal 7200 includes the input output terminal 7206, and data can be directly transmitted to and received from another information terminal via a connector. In addition, charging via the input output terminal 7206 is possible. Note that the charging operation may be performed by wireless power feeding without using the input output terminal 7206.
The display portion 7202 of the portable information terminal 7200 includes the secondary battery of one embodiment of the present invention. When the secondary battery of one embodiment of the present invention is used, a lightweight portable information terminal with a long lifetime can be provided. For example, the secondary battery 7104 illustrated in
A portable information terminal 7200 preferably includes a sensor. As the sensor, for example a human body sensor such as a fingerprint sensor, a pulse sensor, or a temperature sensor, a touch sensor, a pressure sensitive sensor, an acceleration sensor, or the like is preferably mounted.
The display surface of the display portion 7304 is bent, and images can be displayed on the bent display surface. A display state of the display device 7300 can be changed by, for example, near field communication, which is a communication method based on an existing communication standard.
The display device 7300 includes an input output terminal, and data can be directly transmitted to and received from another information terminal via a connector. In addition, charging via the input output terminal is possible. Note that the charging operation may be performed by wireless power feeding without using the input output terminal.
When the secondary battery of one embodiment of the present invention is used as the secondary battery included in the display device 7300, a lightweight display device with a long lifetime can be provided.
In addition,
When the secondary battery of one embodiment of the present invention is used as a secondary battery of a daily electronic device, a lightweight product with a long lifetime can be provided. As the daily electronic devices, an electric toothbrush, an electric shaver, electric beauty equipment, and the like are given. As secondary batteries of these products, in consideration of handling ease for users, small and lightweight stick type secondary batteries with high capacity are desired.
Next,
The tablet terminal 9600 includes a power storage unit 9635 inside the housings 9630a and 9630b. The power storage unit 9635 is provided across the housings 9630a and 9630b, passing through the movable portion 9640.
Part of the display portion 9631 can be a touch panel region and data can be input when a displayed operation key is touched. A switching button for showing/hiding a keyboard of the touch panel is touched with a finger, a stylus, or the like, so that keyboard buttons can be displayed on the display portion 9631.
The display mode switch 9626 can switch the display between a portrait mode and a landscape mode, and between monochrome display and color display, for example. The power saving mode changing switch 9625 can control display luminance in accordance with the amount of external light in use of the tablet terminal 9600, which is measured with an optical sensor incorporated in the tablet terminal 9600. Another detection device including a sensor for detecting inclination, such as a gyroscope sensor or an acceleration sensor, may be incorporated in the tablet terminal, in addition to the optical sensor.
The tablet terminal is closed in
The tablet terminal 9600 can be folded such that the housings 9630a and 9630b overlap with each other when not in use. Thus, the display portion 9631 can be protected, which increases the durability of the tablet terminal 9600. With the power storage unit 9635 including the secondary battery of one embodiment of the present invention which has high capacity and excellent cycle characteristics, the tablet terminal 9600 which can be used for a long time for a long period can be provided.
The tablet terminal illustrated in
The solar cell 9633, which is attached on the surface of the tablet terminal, supplies electric power to a touch panel, a display portion, an image signal processor, and the like. Note that the solar cell 9633 can be provided on one or both surfaces of the housing 9630 and the power storage unit 9635 can be charged efficiently.
The structure and operation of the charge and discharge control circuit 9634 illustrated in
First, an example of the operation in the case where power is generated by the solar cell 9633 using external light is described. The voltage of electric power generated by the solar cell is raised or lowered by the DCDC converter 9636 to a voltage for charging the power storage unit 9635. When the power from the solar cell 9633 is used for the operation of the display portion 9631, the switch SW1 is turned on and the voltage of the power is raised or lowered by the converter 9637 to a voltage needed for operating the display portion 9631. When display on the display portion 9631 is not performed, the switch SW1 is turned off and the switch SW2 is turned on, so that the power storage unit 9635 can be charged.
Note that the solar cell 9633 is described as an example of a power generation means; however, one embodiment of the present invention is not limited to this example. The power storage unit 9635 may be charged using another power generation means such as a piezoelectric element or a thermoelectric conversion element (Peltier element). For example, the power storage unit 9635 may be charged with a non-contact power transmission module that transmits and receives power wirelessly (without contact) to charge the battery or with a combination of other charging means.
A semiconductor display device such as a liquid crystal display device, a light-emitting device in which a light-emitting element such as an organic EL element is provided in each pixel, an electrophoretic display device, a digital micromirror device (DMD), a plasma display panel (PDP), or a field emission display (FED) can be used for the display portion 8002.
Note that the display device includes, in its category, all of information display devices for personal computers, advertisement displays, and the like other than TV broadcast reception.
In
Note that although the installation lighting device 8100 provided in the ceiling 8104 is illustrated in
As the light source 8102, an artificial light source which emits light artificially by using power can be used. Specifically, an incandescent lamp, a discharge lamp such as a fluorescent lamp, and a light-emitting element such as an LED or an organic EL element are given as examples of the artificial light source.
In
Note that although the split-type air conditioner including the indoor unit and the outdoor unit is illustrated in
In
In addition, in a time period when electronic devices are not used, particularly when the proportion of the amount of power which is actually used to the total amount of power which can be supplied from a commercial power source (such a proportion referred to as a usage rate of power) is low, power can be stored in the secondary battery, whereby the usage rate of power can be reduced in a time period when the electronic devices are used. For example, in the case of the electric refrigerator-freezer 8300, power can be stored in the secondary battery 8304 in night time when the temperature is low and the refrigerator door 8302 and the freezer door 8303 are not often opened and closed. On the other hand, in daytime when the temperature is high and the refrigerator door 8302 and the freezer door 8303 are frequently opened and closed, the secondary battery 8304 is used as an auxiliary power source; thus, the usage rate of power in daytime can be reduced.
The secondary battery of one embodiment of the present invention can be used in any of a variety of electronic devices as well as the above electronic devices. According to one embodiment of the present invention, the secondary battery can have excellent cycle characteristics. Furthermore, in accordance with one embodiment of the present invention, a secondary battery with high capacity can be obtained; thus, the secondary battery itself can be made more compact and lightweight. Thus, the secondary battery of one embodiment of the present invention is used in the electronic device described in this embodiment, whereby a more lightweight electronic device with a longer lifetime can be obtained. This embodiment can be implemented in appropriate combination with any of the other embodiments.
In this embodiment, examples of vehicles including the secondary battery of one embodiment of the present invention are described.
The use of secondary batteries in vehicles enables production of next-generation clean energy vehicles such as hybrid electric vehicles (HEVs), electric vehicles (EVs), and plug-in hybrid electric vehicles (PHEVs).
The secondary battery can also supply electric power to a display device of a speedometer, a tachometer, or the like included in the automobile 8400. Furthermore, the secondary battery can supply electric power to a semiconductor device included in the automobile 8400, such as a navigation system.
Furthermore, although not illustrated, the vehicle may include a power receiving device so that it can be charged by being supplied with electric power from an above-ground power transmitting device in a contactless manner. In the case of the contactless power feeding system, by fitting a power transmitting device in a road or an exterior wall, charging can be performed not only when the electric vehicle is stopped but also when driven. In addition, the contactless power feeding system may be utilized to perform transmission and reception of electric power between vehicles. A solar cell may be provided in the exterior of the automobile to charge the secondary battery when the automobile stops or moves. To supply electric power in such a contactless manner, an electromagnetic induction method or a magnetic resonance method can be used.
Furthermore, in the motor scooter 8600 illustrated in
In accordance with one embodiment of the present invention, the secondary battery can have improved cycle characteristics and the capacity of the secondary battery can be increased. Thus, the secondary battery itself can be made more compact and lightweight. The compact and lightweight secondary battery contributes to a reduction in the weight of a vehicle, and thus increases the driving radius. Furthermore, the secondary battery included in the vehicle can be used as a power source for supplying electric power to products other than the vehicle. In such a case, the use of a commercial power source can be avoided at peak time of electric power demand, for example. If the use of a commercial power source can be avoided at peak time of electric power demand, the avoidance can contribute to energy saving and a reduction in carbon dioxide emissions. Moreover, if the cycle characteristics are excellent, the secondary battery can be used for a long period; thus, the use amount of rare metals such as cobalt can be reduced.
This embodiment can be implemented in appropriate combination with the other embodiments.
This example will show results of comparing characteristics of secondary batteries formed using positive electrode active materials including different covering layers.
<Formation of Positive Electrode Active Material>
Positive electrode active materials of samples 1 to 5 were prepared. The formation method of each sample is as follows.
<<Sample 1>>
To form the sample 1 which is a positive electrode active material containing lithium cobaltate in the inner portion and including a covering layer containing aluminum and magnesium in the superficial portion, a lithium cobaltate particle containing magnesium and fluorine was covered with aluminum-containing layers by a sol-gel method and was heated.
The lithium cobaltate particle containing magnesium and fluorine was produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD. (product name: C-20F).
To 20 ml of 2-propanol, 0.0348 g of tri-i-propoxyaluminum was added and dissolved. To this 2-propanol solution containing tri-i-propoxyaluminum, 5 g of a lithium cobaltate particle containing magnesium and fluorine was added.
This mixed solution was stirred with a magnetic stirrer for four hours, at 25° C., at a humidity of 90% RH. By the process, hydrolysis and polycondensation reaction occurred between H2O and tri-i-propoxyaluminum in the atmosphere, so that a layer containing aluminum was formed on the surface of the lithium cobaltate particle containing magnesium and fluorine.
The mixed solution which had been subjected to the above process was filtered to collect the residue. As a filter for the filtration, Kiriyama filter paper (No. 4) was used.
The collected residue was dried in a vacuum at 70° C. for one hour.
The dried powder was heated. The heating was performed in a dried air atmosphere at 800° C. (the temperature rising rate was 200° C./h) for a retention time of two hours.
The heated powder was cooled and subjected to crushing treatment. In the crushing treatment, the powder was made to pass through a sieve with an aperture width of 53 μm.
The particle subjected to the crushing treatment was used as the positive electrode active material of the sample 1.
<<Sample 2>>
To form the sample 2 (comparative example) which is a positive electrode active material containing lithium cobaltate in the inner portion and including a covering layer containing magnesium in the superficial portion, a lithium cobaltate particle containing magnesium and fluorine was heated.
The lithium cobaltate particle containing magnesium and fluorine was produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD. (product name: C-20F).
The lithium cobaltate particle containing magnesium and fluorine was heated. The heating was performed in an oxygen atmosphere at 800° C. (the temperature rising rate was 200° C./h) for a retention time of two hours.
The heated powder was cooled and made to pass through the sieve with an aperture width of 53 μm, which was used as the positive electrode active material of the sample 2.
<<Sample 3>>
To form the sample 3 (comparative example) which is a positive electrode active material of lithium cobaltate containing magnesium and fluorine in which magnesium is not segregated in the superficial portion, a lithium cobaltate particle containing magnesium and fluorine was used without being heated.
The lithium cobaltate particle containing magnesium and fluorine was produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD. (product name: C-20F).
<<Sample 4>>
To form the sample 4 (comparative example) which is a positive electrode active material containing lithium cobalt oxide in the inner portion and including the aluminum-containing covering layer in the superficial portion, a lithium cobaltate particle containing no magnesium was covered with an aluminum-containing layer by a sol-gel method and then was heated.
The lithium cobaltate particle containing no magnesium was produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD. (product name: C-10N). In the lithium cobaltate particle, magnesium is not detected and fluorine is detected at approximately 1 atomic % by XPS.
As in the sample 1, an aluminum-containing covering layer was formed on the lithium cobaltate particle by a sol-gel method, and the particle was dried, heated, cooled, and made to pass through a sieve. In this manner, a positive electrode active material of the sample 4 was formed.
<<Sample 5>>
As the sample 5 (comparative example) which is a positive electrode active material including no covering layer, a lithium cobaltate particle containing no magnesium was used without being heated.
The lithium cobaltate particle containing no magnesium was produced by NIPPON CHEMICAL INDUSTRIAL CO., LTD. (product name: C-10N).
Table 1 shows the conditions of the samples 1 to 5.
<Cycle Characteristics>
CR2032 coin-type secondary batteries (20 mm in diameter, 3.2 mm in height) were fabricated using the positive electrode active materials of the samples 1 to 5 formed in the above manner. Their cycle characteristics were evaluated.
A positive electrode formed by applying slurry in which the positive electrode active material (LiCoO2) of each of the samples 1 to 5, acetylene black (AB), and polyvinylidene fluoride (PVDF) were mixed at a weight ratio of LiCoO2:AB:PVDF=95:2.5:2.5 to an aluminum foil current collector was used.
A lithium metal was used for a counter electrode.
As an electrolyte contained in an electrolyte solution, 1 mol/L lithium hexafluorophosphate (LiPF6) was used. As the electrolyte solution, a solution in which vinylene carbonate (VC) was added to ethylene carbonate (EC) and diethyl carbonate (DEC) mixed at a volume ratio of EC:DEC=3:7 at a 2 weight % was used.
A positive electrode can and a negative electrode can were formed of stainless steel (SUS).
The measurement temperature in the cycle characteristics test was 25° C. Charging was carried out at a constant current with a current density of 68.5 mA/g per active material weight and an upper limit voltage of 4.6 V, followed by constant voltage charge until a current density was reached to 1.4 mA/g. Discharge was carried out with a lower limit voltage of 2.5 V at a constant current with a current density of 68.5 mA/g per active material weight.
As is clear from
When the sample 2 and the sample 3 which are lithium cobaltate particles containing magnesium and fluorine were compared, the cycle characteristics of the sample 2 being heated was much better than those of the sample 3 not being heated. This is probably due to the effect of magnesium segregation on the superficial portion of the lithium cobaltate particle by heating.
The sample 1, which is the positive electrode active material including the aluminum-containing covering layer on the lithium cobaltate particle containing magnesium and fluorine, showed extremely favorable cycle characteristics, which exceeded those of the sample 2 in which magnesium was segregated on the superficial portion and those of the sample 4 including the aluminum-containing covering layer. It thus became clear that better cycle characteristics can be obtained from a sample including a covering layer containing both aluminum and magnesium than a sample including a covering layer containing only one of aluminum and magnesium.
In this example, features of the lithium cobaltate particle having a covering layer containing aluminum and magnesium were disclosed.
<XPS>
XPS analysis was performed from the surface of the samples 1, 2, and 3 in Example 1. Also, XPS analysis was performed on a sample 6, which corresponds to a particle of the sample 1 in Example 1 which has been subjected to the sol-gel treatment and drying and has not been heated. The calculation results are shown in Table 2. Note that since the analysis results are rounded off to one decimal place, the total is not 100% in some cases.
Table 3 shows atomic ratios calculated by taking the total amount of lithium, aluminum, cobalt, magnesium, oxygen, and fluorine as 100 atomic %, using the results in Table 2.
XPS analysis can quantitatively analyze the positive electrode active material at a depth of about 5 nm from the surface. As shown in Table 2, in the sample 1 and the sample 2 which were heated positive electrode active materials, the atomic proportion of magnesium significantly increased compared with those in the sample 6 and the sample 3 which were not heated. That is, it was revealed that heating made magnesium segregate in the region at a depth of about 5 nm from the surface.
When the sample 1 and the sample 6 in each of which the covering layer containing aluminum was formed by the sol-gel method were compared, the atom proportion of aluminum was smaller in the sample 1 subjected to heating than in the sample 6 not subjected to heating. Therefore, it was inferred that heating made aluminum diffuse from the region at a depth of about 5 nm from the surface.
Therefore, it was inferred that in the sample 1 including a covering layer containing aluminum and magnesium, magnesium exists abundantly on the superficial portion and aluminum exists in a deeper region than magnesium.
<STEM-FFT>
Next, STEM observation results and FFT analysis results of the sample 1 are shown in
FIG. 24A1 is an HAADF-STEM image of the cross section of the vicinity of the surface of the positive electrode active material of the sample 1. FIG. 24A2 is an FFT (Fast Fourier Transform) image of the region indicated by FFT1 in FIG. 24A1. Some luminescent spots in the FFT image of FIG. 24A2 are referred to as A, B, C, and O as shown in FIG. 24A3.
Regarding the luminescent spots in the FFT image in the region indicated by FFT1, the measured values were as follows: d=0.25 nm for OA, d=0.16 nm for OB, d=0.26 nm for OC, ∠AOB=37°, ∠BOC=36°, and ∠AOC=73°.
They are close to the distance and angle obtained from magnesium oxide (MgO) data (ICDD 45-0945) and cobalt oxide (CoO) data (ICDD 48-1719) in the International Centre for Diffraction Data (ICDD) database.
In the magnesium oxide, d=0.24 nm for OA(1-11), d=0.15 nm for OB(0-22), d=0.24 nm for OC(−1-11), ∠AOB=35°, ∠BOC=35°, and ∠AOC=71°.
In the cobalt oxide, d=0.25 nm for OA(1-11), d=0.15 nm for OB(0-22), d=0.25 nm for OC(−1-11), ∠AOB=35°, ∠BOC=35°, and ∠AOC=71°.
Therefore, it became clear that the region of about 2 nm in depth from the surface of the positive electrode active material particle, which was indicated by FFT1, was a region having a rock-salt crystal structure and was an image of [011] incidence. It was also inferred that the region indicated by FFT1 contained either one or both of magnesium oxide and cobalt oxide.
FIG. 24B1 is a HAADF-STEM image of the cross section of the vicinity of the surface of positive electrode active material as the same image as FIG. 24A1. FIG. 24B2 is an FFT image of the region indicated by FFT2 in FIG. 24B1. Some luminescent spots in the FFT image of FIG. 24B2 are referred to as A, B, C, and O as shown in FIG. 24B3.
Regarding the luminescent spots in the region indicated by FFT2 in the FFT image, the measurement values were as follows: d=0.51 nm for OA, d=0.21 nm for OB, and d=0.25 nm for OC, ∠AOB=55°, ∠BOC=24°, and ∠AOC=79°.
They are close to the distance and angle obtained from lithium cobaltate (LiCoO2) data (ICDD 50-0653) and LiAl0.2Co0.8O2 data (ICDD 89-0912) in the ICDD database.
In the lithium cobaltate (LiCoO2), d=0.47 nm for OA(003), d=0.20 nm for OB(104), d=0.24 nm for OC(101), ∠AOB=55°, ∠BOC=25°, and ∠AOC=80°.
In the LiAl0.2Co0.8O2, d=0.47 nm for OA(003), d=0.20 nm for OB(104), d=0.24 nm for OC(101), ∠AOB=55°, ∠BOC=25°, and ∠AOC=80°.
Therefore, it became clear that the region at a depth of more than 3 nm and less than or equal to 6 nm from the surface of the positive electrode active material, which was indicated by FFT2, was a region having the same layered rock-salt crystal structure as the lithium cobaltate and LiAl0.2Co0.8O2 and was an image of [0-10] incidence.
<STEM-EDX (Element Mapping, Line Analysis)>
Next, EDX analysis results of the sample 1 are shown in FIGS. 25A1 to 25C and
FIGS. 25A1 to 25C show STEM-EDX analysis results of the vicinity of the surface of the positive electrode active material of the sample 1. FIG. 25A1 is a HAADF-STEM image. FIG. 25A2 shows a cobalt mapping. FIG. 25B1 shows an aluminum mapping. FIG. 25B2 shows a magnesium mapping.
As shown in FIG. 25B1, it was observed that aluminum distributed in the region at a depth of about 10 nm from the surface of the positive electrode active material. As shown in FIG. 25B2, it was observed that magnesium segregated in the region at a depth of about 3 nm from the surface of the positive electrode active material. As shown in
As shown in
From the above XPS and EDX analysis results, it is found that the sample 1 is a positive electrode active material, which is one embodiment of the present invention, including a first region containing lithium cobaltate, a second region containing lithium, aluminum, cobalt, and oxygen, and a third region containing magnesium and oxygen. It becomes clear that, in the sample 1, part of the second region and part of the third region overlap with each other.
In the graph of
In this example, the average value Oave of the amount of detected oxygen in a distance range from 11 nm to 40 nm was 777. The x axis of the measurement point at which the measurement value closest to 388.5, which is 50% of 777, was obtained indicated a distance of 9.5 nm. Thus, in this example, a distance of 9.5 nm in the graph of
When the outermost surface of the positive electrode active material particle is set at a distance of 9.5 nm, the peak of magnesium agrees with the outermost surface, and the peak of aluminum is present at 2.3 nm in distance from the outermost surface. From the above results of Example 1 and Example 2, it was found that the positive electrode active material of one embodiment of the present invention in which lithium cobaltate is included in the first region 101, lithium, aluminum, cobalt, and oxygen are included in the second region 102, and magnesium and oxygen are included in the third region 103 can obtain extremely favorable cycle characteristics when used for a secondary battery.
This application is based on Japanese Patent Application serial no. 2016-225046 filed with Japan Patent Office on Nov. 18, 2016, the entire contents of which are hereby incorporated by reference.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-225046 | Nov 2016 | JP | national |
This application is a continuation of U.S. application Ser. No. 16/900,108, filed Jun. 12, 2020, now pending, which is a continuation of U.S. application Ser. No. 15/800,184, filed Nov. 1, 2017, now pending, which claims the benefit of a foreign priority application filed in Japan as Serial No. 2016-225046 on Nov. 18, 2016, all of which are incorporated by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4302518 | Goodenough et al. | Nov 1981 | A |
| 4668595 | Yoshino et al. | May 1987 | A |
| 5240794 | Thackeray et al. | Aug 1993 | A |
| 5443929 | Yamamoto et al. | Aug 1995 | A |
| 5576608 | Nagai et al. | Nov 1996 | A |
| 5604396 | Watanabe et al. | Feb 1997 | A |
| 5637981 | Nagai et al. | Jun 1997 | A |
| 5705291 | Amatucci et al. | Jan 1998 | A |
| 5783333 | Mayer | Jul 1998 | A |
| 5824278 | Yao | Oct 1998 | A |
| 5834139 | Shodai et al. | Nov 1998 | A |
| 5871866 | Barker et al. | Feb 1999 | A |
| 5910382 | Goodenough et al. | Jun 1999 | A |
| 6085015 | Armand et al. | Jul 2000 | A |
| 6127065 | Yamamoto et al. | Oct 2000 | A |
| 6218050 | Yoon et al. | Apr 2001 | B1 |
| 6277521 | Gao et al. | Aug 2001 | B1 |
| 6346348 | Nakajima et al. | Feb 2002 | B1 |
| 6458487 | Takeuchi et al. | Oct 2002 | B1 |
| 6514640 | Armand et al. | Feb 2003 | B1 |
| 6582814 | Swiler et al. | Jun 2003 | B2 |
| 6589499 | Gao et al. | Jul 2003 | B2 |
| 6680143 | Thackeray et al. | Jan 2004 | B2 |
| 6737195 | Kweon et al. | May 2004 | B2 |
| 6753111 | Kweon et al. | Jun 2004 | B2 |
| 6846592 | Kweon et al. | Jan 2005 | B2 |
| 6878490 | Gao et al. | Apr 2005 | B2 |
| 6919144 | Miyazaki et al. | Jul 2005 | B2 |
| 6974601 | Kweon et al. | Dec 2005 | B2 |
| 6984469 | Kweon et al. | Jan 2006 | B2 |
| 7018741 | Suhara et al. | Mar 2006 | B2 |
| 7138209 | Kweon et al. | Nov 2006 | B2 |
| 7294435 | Miyamoto et al. | Nov 2007 | B2 |
| 7303840 | Thackeray et al. | Dec 2007 | B2 |
| 7309546 | Kweon et al. | Dec 2007 | B2 |
| 7368071 | Dahn et al. | May 2008 | B2 |
| 7393476 | Shiozaki et al. | Jul 2008 | B2 |
| 7481991 | Kawasato et al. | Jan 2009 | B2 |
| 7504180 | Tatsumi et al. | Mar 2009 | B2 |
| 7635536 | Johnson et al. | Dec 2009 | B2 |
| 7709148 | Kawasato et al. | May 2010 | B2 |
| 7709151 | Inoue et al. | May 2010 | B2 |
| 7727673 | Ooyama et al. | Jun 2010 | B2 |
| 7736807 | Hasegawa et al. | Jun 2010 | B2 |
| 7790308 | Johnson et al. | Sep 2010 | B2 |
| 7892679 | Shimizu et al. | Feb 2011 | B2 |
| 7927506 | Park | Apr 2011 | B2 |
| 7935270 | Park | May 2011 | B2 |
| 8003256 | Ohishi | Aug 2011 | B2 |
| 8007941 | Kweon et al. | Aug 2011 | B2 |
| 8034486 | Kweon et al. | Oct 2011 | B2 |
| 8080340 | Thackeray et al. | Dec 2011 | B2 |
| RE43276 | Kweon et al. | Mar 2012 | E |
| 8236449 | Nakura | Aug 2012 | B2 |
| 8394534 | Lopez et al. | Mar 2013 | B2 |
| 8470477 | Miwa et al. | Jun 2013 | B2 |
| 8475959 | Venkatachalam et al. | Jul 2013 | B2 |
| 8476510 | Swager et al. | Jul 2013 | B2 |
| 8535832 | Karthikeyan et al. | Sep 2013 | B2 |
| 8540902 | Xing et al. | Sep 2013 | B2 |
| 8557440 | Yu et al. | Oct 2013 | B2 |
| 8652687 | Zhamu et al. | Feb 2014 | B2 |
| 8685569 | Oguni et al. | Apr 2014 | B2 |
| 8685570 | Miwa et al. | Apr 2014 | B2 |
| 8709654 | Takeuchi et al. | Apr 2014 | B2 |
| 8741485 | Lopez et al. | Jun 2014 | B2 |
| 8753532 | Levasseur et al. | Jun 2014 | B2 |
| 8808918 | Jung et al. | Aug 2014 | B2 |
| 8877377 | Hosoya | Nov 2014 | B2 |
| 8877381 | Yasuda et al. | Nov 2014 | B2 |
| 8883351 | Todoriki et al. | Nov 2014 | B2 |
| 8906547 | Taniguchi et al. | Dec 2014 | B2 |
| 8927148 | Kawakami | Jan 2015 | B2 |
| 8945770 | Koo et al. | Feb 2015 | B2 |
| 8945772 | Kawakami et al. | Feb 2015 | B2 |
| 8951448 | Toyama et al. | Feb 2015 | B2 |
| 8993167 | Chang et al. | Mar 2015 | B2 |
| 9087626 | Xing et al. | Jul 2015 | B2 |
| 9105926 | Fujiki et al. | Aug 2015 | B2 |
| 9126845 | Nagai | Sep 2015 | B2 |
| 9225003 | Yukawa | Dec 2015 | B2 |
| 9227850 | Ooishi | Jan 2016 | B2 |
| 9293236 | Kawakami et al. | Mar 2016 | B2 |
| 9362557 | Watanabe et al. | Jun 2016 | B2 |
| 9385366 | Yamakaji et al. | Jul 2016 | B2 |
| 9391322 | Liu et al. | Jul 2016 | B2 |
| 9478796 | Li et al. | Oct 2016 | B2 |
| 9505631 | Masukuni et al. | Nov 2016 | B2 |
| 9515313 | Umeyama et al. | Dec 2016 | B2 |
| 9614225 | Park | Apr 2017 | B2 |
| 9666326 | Kawakami et al. | May 2017 | B2 |
| 9698420 | Ishizaki et al. | Jul 2017 | B2 |
| 9774034 | Kawakami et al. | Sep 2017 | B2 |
| 9786903 | Ryu et al. | Oct 2017 | B2 |
| 9812702 | Ikeuchi et al. | Nov 2017 | B2 |
| 9812709 | Endoh et al. | Nov 2017 | B2 |
| 9825283 | Kim et al. | Nov 2017 | B2 |
| 9871246 | Kim et al. | Jan 2018 | B2 |
| 9899664 | Yamaki et al. | Feb 2018 | B2 |
| 9923244 | Takanashi et al. | Mar 2018 | B2 |
| 9929402 | Kawakami | Mar 2018 | B2 |
| 9972834 | Kong et al. | May 2018 | B2 |
| 10026960 | Lee et al. | Jul 2018 | B2 |
| 10128495 | Satow et al. | Nov 2018 | B2 |
| 10141567 | Choi et al. | Nov 2018 | B2 |
| 10177377 | Yu et al. | Jan 2019 | B2 |
| 10243215 | Shitaba et al. | Mar 2019 | B2 |
| 10340513 | Sugiura | Jul 2019 | B2 |
| 10347916 | Sun et al. | Jul 2019 | B2 |
| 10361432 | Takaichi et al. | Jul 2019 | B2 |
| 10559810 | Yanagihara et al. | Feb 2020 | B2 |
| 10741828 | Ochiai | Aug 2020 | B2 |
| 10777815 | Kanada et al. | Sep 2020 | B2 |
| 20010010807 | Matsubara | Aug 2001 | A1 |
| 20020055042 | Kweon et al. | May 2002 | A1 |
| 20020071990 | Kweon et al. | Jun 2002 | A1 |
| 20020071991 | Kweon et al. | Jun 2002 | A1 |
| 20020102459 | Hosoya et al. | Aug 2002 | A1 |
| 20020110736 | Kweon et al. | Aug 2002 | A1 |
| 20020164156 | Bilbrey | Nov 2002 | A1 |
| 20020195591 | Ravet et al. | Dec 2002 | A1 |
| 20030104279 | Miyazaki et al. | Jun 2003 | A1 |
| 20030134186 | Shizuki | Jul 2003 | A1 |
| 20030138697 | Leising | Jul 2003 | A1 |
| 20040142241 | Nagayama | Jul 2004 | A1 |
| 20040229123 | Takahashi et al. | Nov 2004 | A1 |
| 20040229124 | Miyamoto et al. | Nov 2004 | A1 |
| 20040234857 | Shiozaki et al. | Nov 2004 | A1 |
| 20050019662 | Suhara et al. | Jan 2005 | A1 |
| 20060051671 | Thackeray et al. | Mar 2006 | A1 |
| 20060051673 | Johnson et al. | Mar 2006 | A1 |
| 20060068289 | Paulsen | Mar 2006 | A1 |
| 20060121352 | Kejha et al. | Jun 2006 | A1 |
| 20060188780 | Fujii et al. | Aug 2006 | A1 |
| 20060210879 | Kawasato et al. | Sep 2006 | A1 |
| 20060263690 | Suhara et al. | Nov 2006 | A1 |
| 20060275664 | Ohzuku et al. | Dec 2006 | A1 |
| 20060286459 | Zhao et al. | Dec 2006 | A1 |
| 20070026315 | Lampe-Onnerud et al. | Feb 2007 | A1 |
| 20070099086 | Kang et al. | May 2007 | A1 |
| 20070117014 | Saito et al. | May 2007 | A1 |
| 20070122712 | Kang et al. | May 2007 | A1 |
| 20070148546 | Shimizu et al. | Jun 2007 | A1 |
| 20070160906 | Tooyama et al. | Jul 2007 | A1 |
| 20070212609 | Iwami | Sep 2007 | A1 |
| 20070224506 | Ooyama et al. | Sep 2007 | A1 |
| 20080131780 | Kawasato et al. | Jun 2008 | A1 |
| 20080166637 | Inagaki et al. | Jul 2008 | A1 |
| 20080241693 | Fukuchi et al. | Oct 2008 | A1 |
| 20090011335 | Takeda et al. | Jan 2009 | A1 |
| 20090017383 | Suhara et al. | Jan 2009 | A1 |
| 20090081547 | Nakura | Mar 2009 | A1 |
| 20090087731 | Fukui et al. | Apr 2009 | A1 |
| 20090104530 | Shizuka | Apr 2009 | A1 |
| 20090104532 | Hosoya | Apr 2009 | A1 |
| 20090123813 | Chiang et al. | May 2009 | A1 |
| 20090123842 | Thackeray et al. | May 2009 | A1 |
| 20090220862 | Toyama et al. | Sep 2009 | A1 |
| 20100019194 | Fujiwara et al. | Jan 2010 | A1 |
| 20100035147 | Kotato et al. | Feb 2010 | A1 |
| 20100086854 | Kumar et al. | Apr 2010 | A1 |
| 20100129714 | Toyama et al. | May 2010 | A1 |
| 20100129715 | Saito et al. | May 2010 | A1 |
| 20100143784 | Johnson et al. | Jun 2010 | A1 |
| 20100143799 | Park | Jun 2010 | A1 |
| 20100159330 | Sugiura et al. | Jun 2010 | A1 |
| 20100178464 | Choi et al. | Jul 2010 | A1 |
| 20100216024 | Kanno et al. | Aug 2010 | A1 |
| 20100233542 | Endo et al. | Sep 2010 | A1 |
| 20100247986 | Toyama et al. | Sep 2010 | A1 |
| 20100248033 | Kumar et al. | Sep 2010 | A1 |
| 20100294985 | Suhara et al. | Nov 2010 | A1 |
| 20110020708 | Fujiki et al. | Jan 2011 | A1 |
| 20110033749 | Uchida et al. | Feb 2011 | A1 |
| 20110059367 | Morita et al. | Mar 2011 | A1 |
| 20110076564 | Yu et al. | Mar 2011 | A1 |
| 20110171371 | Li et al. | Jul 2011 | A1 |
| 20110200879 | Saito et al. | Aug 2011 | A1 |
| 20110229757 | Kawakami et al. | Sep 2011 | A1 |
| 20110244331 | Karthikeyan et al. | Oct 2011 | A1 |
| 20110256437 | Katsuki et al. | Oct 2011 | A1 |
| 20110269023 | Kawakami et al. | Nov 2011 | A1 |
| 20110297876 | Masukuni et al. | Dec 2011 | A1 |
| 20110300441 | Kawakami | Dec 2011 | A1 |
| 20120034516 | Koo et al. | Feb 2012 | A1 |
| 20120045692 | Takemura et al. | Feb 2012 | A1 |
| 20120058397 | Zhamu et al. | Mar 2012 | A1 |
| 20120064406 | Sato et al. | Mar 2012 | A1 |
| 20120064409 | Zhamu et al. | Mar 2012 | A1 |
| 20120088151 | Yamazaki et al. | Apr 2012 | A1 |
| 20120088156 | Nomoto et al. | Apr 2012 | A1 |
| 20120118149 | Dabrowski et al. | May 2012 | A1 |
| 20120244430 | Yamazaki et al. | Sep 2012 | A1 |
| 20120256337 | Yokoyama et al. | Oct 2012 | A1 |
| 20120258358 | Yura et al. | Oct 2012 | A1 |
| 20120258365 | Yokoyama et al. | Oct 2012 | A1 |
| 20120258369 | Yokoyama et al. | Oct 2012 | A1 |
| 20120261622 | Honma | Oct 2012 | A1 |
| 20120295163 | Yanagita et al. | Nov 2012 | A1 |
| 20120308891 | Todoriki et al. | Dec 2012 | A1 |
| 20120315544 | Yasuda et al. | Dec 2012 | A1 |
| 20120328951 | Hirohashi et al. | Dec 2012 | A1 |
| 20120328956 | Oguni et al. | Dec 2012 | A1 |
| 20120330044 | Hou | Dec 2012 | A1 |
| 20130004657 | Xu et al. | Jan 2013 | A1 |
| 20130017435 | Sato et al. | Jan 2013 | A1 |
| 20130040193 | Tsuchida et al. | Feb 2013 | A1 |
| 20130045418 | Oguni et al. | Feb 2013 | A1 |
| 20130052534 | Fujiki et al. | Feb 2013 | A1 |
| 20130052547 | Ogino et al. | Feb 2013 | A1 |
| 20130065120 | Miwa et al. | Mar 2013 | A1 |
| 20130078516 | Taniguchi et al. | Mar 2013 | A1 |
| 20130084384 | Yamakaji | Apr 2013 | A1 |
| 20130089786 | Jeong et al. | Apr 2013 | A1 |
| 20130130103 | Kim et al. | May 2013 | A1 |
| 20130134051 | Takahashi et al. | May 2013 | A1 |
| 20130156683 | Holzapfel et al. | Jun 2013 | A1 |
| 20130156942 | Yamakaji et al. | Jun 2013 | A1 |
| 20130157034 | Choi et al. | Jun 2013 | A1 |
| 20130164619 | Yamakaji et al. | Jun 2013 | A1 |
| 20130177806 | Caldwell et al. | Jul 2013 | A1 |
| 20130183579 | Kim et al. | Jul 2013 | A1 |
| 20130189585 | Kang et al. | Jul 2013 | A1 |
| 20130190449 | Kinloch et al. | Jul 2013 | A1 |
| 20130202953 | Sharma et al. | Aug 2013 | A1 |
| 20130212879 | Ogino | Aug 2013 | A1 |
| 20130230770 | Oya et al. | Sep 2013 | A1 |
| 20130266858 | Inoue et al. | Oct 2013 | A1 |
| 20130266859 | Todoriki et al. | Oct 2013 | A1 |
| 20130313471 | Endo et al. | Nov 2013 | A1 |
| 20130316237 | Miki | Nov 2013 | A1 |
| 20130337320 | Yukawa | Dec 2013 | A1 |
| 20140004412 | Ogino | Jan 2014 | A1 |
| 20140023920 | Yamazaki et al. | Jan 2014 | A1 |
| 20140079995 | Wakada | Mar 2014 | A1 |
| 20140099554 | Inoue et al. | Apr 2014 | A1 |
| 20140113194 | Tsunozaki et al. | Apr 2014 | A1 |
| 20140127567 | Kuriki et al. | May 2014 | A1 |
| 20140127568 | Kawakami et al. | May 2014 | A1 |
| 20140131633 | Ito et al. | May 2014 | A1 |
| 20140147740 | Kokubu et al. | May 2014 | A1 |
| 20140162132 | Ishii et al. | Jun 2014 | A1 |
| 20140166946 | Miwa et al. | Jun 2014 | A1 |
| 20140184172 | Momo et al. | Jul 2014 | A1 |
| 20140186663 | Hiroki et al. | Jul 2014 | A1 |
| 20140212759 | Blangero et al. | Jul 2014 | A1 |
| 20140234700 | Moriwaka et al. | Aug 2014 | A1 |
| 20140234716 | Lopez et al. | Aug 2014 | A1 |
| 20140242463 | Song et al. | Aug 2014 | A1 |
| 20140295068 | Nanba et al. | Oct 2014 | A1 |
| 20140332715 | Kawakami et al. | Nov 2014 | A1 |
| 20140332731 | Ma et al. | Nov 2014 | A1 |
| 20140370184 | Takemura et al. | Dec 2014 | A1 |
| 20150014581 | Kawakami et al. | Jan 2015 | A1 |
| 20150014605 | Kawakami et al. | Jan 2015 | A1 |
| 20150064565 | Todoriki et al. | Mar 2015 | A1 |
| 20150093648 | Son et al. | Apr 2015 | A1 |
| 20150099178 | Kawakami et al. | Apr 2015 | A1 |
| 20150099179 | Ikenuma et al. | Apr 2015 | A1 |
| 20150123050 | Yamazaki et al. | May 2015 | A1 |
| 20150155556 | Kawakami et al. | Jun 2015 | A1 |
| 20150162598 | Kim et al. | Jun 2015 | A1 |
| 20150166348 | Ikenuma et al. | Jun 2015 | A1 |
| 20150262762 | Ikenuma et al. | Sep 2015 | A1 |
| 20150325855 | Kawakami et al. | Nov 2015 | A1 |
| 20150333320 | Tamaki et al. | Nov 2015 | A1 |
| 20150333324 | Umeyama et al. | Nov 2015 | A1 |
| 20150357641 | Sugie et al. | Dec 2015 | A1 |
| 20150380722 | Blangero | Dec 2015 | A1 |
| 20150380737 | Kawasato et al. | Dec 2015 | A1 |
| 20160006032 | Paulsen | Jan 2016 | A1 |
| 20160028080 | Sugiura | Jan 2016 | A1 |
| 20160049644 | Lee. et al. | Feb 2016 | A1 |
| 20160056469 | Kawakita et al. | Feb 2016 | A1 |
| 20160064726 | Ikenuma et al. | Mar 2016 | A1 |
| 20160087315 | Oyama | Mar 2016 | A1 |
| 20160099469 | Paulsen. et al. | Apr 2016 | A1 |
| 20160104880 | Gao et al. | Apr 2016 | A1 |
| 20160118646 | Ikenuma | Apr 2016 | A1 |
| 20160118649 | Yamamoto et al. | Apr 2016 | A1 |
| 20160118658 | Kawakami et al. | Apr 2016 | A1 |
| 20160156030 | Sun et al. | Jun 2016 | A1 |
| 20160164089 | Kawakami et al. | Jun 2016 | A1 |
| 20160181611 | Cho et al. | Jun 2016 | A1 |
| 20160218360 | Nakahara et al. | Jul 2016 | A1 |
| 20160268601 | Paulsen. et al. | Sep 2016 | A1 |
| 20160276658 | Choi et al. | Sep 2016 | A1 |
| 20160276659 | Choi et al. | Sep 2016 | A1 |
| 20160285102 | Shitaba et al. | Sep 2016 | A1 |
| 20160308200 | Yamakaji et al. | Oct 2016 | A1 |
| 20160329533 | Tajima | Nov 2016 | A1 |
| 20160336595 | Choi et al. | Nov 2016 | A1 |
| 20160349905 | Momma et al. | Dec 2016 | A1 |
| 20160380263 | Nakayama et al. | Dec 2016 | A1 |
| 20160380271 | Ochiai et al. | Dec 2016 | A1 |
| 20170005364 | Yamazaki et al. | Jan 2017 | A1 |
| 20170018768 | Yushin | Jan 2017 | A1 |
| 20170018772 | Satow et al. | Jan 2017 | A1 |
| 20170040594 | Yamaki et al. | Feb 2017 | A1 |
| 20170062819 | Ikenuma | Mar 2017 | A1 |
| 20170069907 | Zhu et al. | Mar 2017 | A1 |
| 20170117589 | Tajima et al. | Apr 2017 | A1 |
| 20170149100 | Ishii | May 2017 | A1 |
| 20170187035 | Yanagihara et al. | Jun 2017 | A1 |
| 20170207444 | Yanagihara et al. | Jul 2017 | A1 |
| 20170229742 | Aykol | Aug 2017 | A1 |
| 20170256817 | Kadoma et al. | Sep 2017 | A1 |
| 20170309910 | Jo et al. | Oct 2017 | A1 |
| 20170338471 | Zheng | Nov 2017 | A1 |
| 20180013130 | Ochiai et al. | Jan 2018 | A1 |
| 20180019462 | Kadoma et al. | Jan 2018 | A1 |
| 20180019464 | Xia et al. | Jan 2018 | A1 |
| 20180034045 | Xia et al. | Feb 2018 | A1 |
| 20180040888 | Park et al. | Feb 2018 | A1 |
| 20180040897 | Park et al. | Feb 2018 | A1 |
| 20180048015 | Lee | Feb 2018 | A1 |
| 20180076489 | Mikami et al. | Mar 2018 | A1 |
| 20180102536 | Kawakami et al. | Apr 2018 | A1 |
| 20180108944 | Yamakaji | Apr 2018 | A1 |
| 20180145317 | Momma et al. | May 2018 | A1 |
| 20180145368 | Ochiai et al. | May 2018 | A1 |
| 20180190976 | Blangero et al. | Jul 2018 | A1 |
| 20180254477 | Horikawa et al. | Sep 2018 | A1 |
| 20180366729 | Yanagita et al. | Dec 2018 | A1 |
| 20190140276 | Pullen | May 2019 | A1 |
| 20200028162 | Yamamoto et al. | Jan 2020 | A1 |
| 20200144601 | Takahashi et al. | May 2020 | A1 |
| 20200152961 | Momma et al. | May 2020 | A1 |
| 20200168908 | Kim | May 2020 | A1 |
| 20200176770 | Takahashi et al. | Jun 2020 | A1 |
| Number | Date | Country |
|---|---|---|
| 001346160 | Apr 2002 | CN |
| 001434527 | Aug 2003 | CN |
| 001685543 | Oct 2005 | CN |
| 001715193 | Jan 2006 | CN |
| 001773753 | May 2006 | CN |
| 001820385 | Aug 2006 | CN |
| 001981396 | Jun 2007 | CN |
| 101148263 | Mar 2008 | CN |
| 100426570 | Oct 2008 | CN |
| 101414680 | Apr 2009 | CN |
| 101950803 | Jan 2011 | CN |
| 102195027 | Sep 2011 | CN |
| 102210045 | Oct 2011 | CN |
| 102272985 | Dec 2011 | CN |
| 102339998 | Feb 2012 | CN |
| 102447107 | May 2012 | CN |
| 102569775 | Jul 2012 | CN |
| 102569877 | Jul 2012 | CN |
| 102610806 | Jul 2012 | CN |
| 102637866 | Aug 2012 | CN |
| 102694201 | Sep 2012 | CN |
| 102779976 | Nov 2012 | CN |
| 102918686 | Feb 2013 | CN |
| 103022502 | Apr 2013 | CN |
| 103456946 | Dec 2013 | CN |
| 103490060 | Jan 2014 | CN |
| 103563139 | Feb 2014 | CN |
| 103606674 | Feb 2014 | CN |
| 103633312 | Mar 2014 | CN |
| 103650219 | Mar 2014 | CN |
| 103733392 | Apr 2014 | CN |
| 103794776 | May 2014 | CN |
| 104134779 | Nov 2014 | CN |
| 104332627 | Feb 2015 | CN |
| 104471759 | Mar 2015 | CN |
| 104505500 | Apr 2015 | CN |
| 104701534 | Jun 2015 | CN |
| 104781964 | Jul 2015 | CN |
| 105024047 | Nov 2015 | CN |
| 105051946 | Nov 2015 | CN |
| 105070907 | Nov 2015 | CN |
| 105229829 | Jan 2016 | CN |
| 105280911 | Jan 2016 | CN |
| 105304936 | Feb 2016 | CN |
| 105917500 | Aug 2016 | CN |
| 106025212 | Oct 2016 | CN |
| 106030872 | Oct 2016 | CN |
| 106099098 | Nov 2016 | CN |
| 106104869 | Nov 2016 | CN |
| 102569775 | Jan 2017 | CN |
| 2352190 | Aug 2011 | EP |
| 2879210 | Jun 2015 | EP |
| 2882014 | Jun 2015 | EP |
| 2897201 | Jul 2015 | EP |
| 2999036 | Mar 2016 | EP |
| 3101716 | Dec 2016 | EP |
| 3203553 | Aug 2017 | EP |
| 3203556 | Aug 2017 | EP |
| 05-314965 | Nov 1993 | JP |
| 05-314995 | Nov 1993 | JP |
| 06-325795 | Nov 1994 | JP |
| 07-014582 | Jan 1995 | JP |
| 07-022009 | Jan 1995 | JP |
| 08-037007 | Feb 1996 | JP |
| 08-100107 | Apr 1996 | JP |
| 08-236114 | Sep 1996 | JP |
| 10-117443 | May 1998 | JP |
| 11-025983 | Jan 1999 | JP |
| 11-096993 | Apr 1999 | JP |
| 3031546 | Apr 2000 | JP |
| 2000-203842 | Jul 2000 | JP |
| 3172388 | Jun 2001 | JP |
| 2001-291518 | Oct 2001 | JP |
| 2001-319692 | Nov 2001 | JP |
| 2002-124262 | Apr 2002 | JP |
| 2002-216760 | Aug 2002 | JP |
| 2002-352802 | Dec 2002 | JP |
| 2002-358953 | Dec 2002 | JP |
| 2003-068306 | Mar 2003 | JP |
| 2003-217572 | Jul 2003 | JP |
| 2003-221235 | Aug 2003 | JP |
| 2003-331824 | Nov 2003 | JP |
| 2004-014381 | Jan 2004 | JP |
| 2004-103566 | Apr 2004 | JP |
| 2004-196604 | Jul 2004 | JP |
| 2004-288579 | Oct 2004 | JP |
| 2004-342554 | Dec 2004 | JP |
| 2005-158612 | Jun 2005 | JP |
| 2005-225734 | Aug 2005 | JP |
| 2005-302510 | Oct 2005 | JP |
| 2005-332629 | Dec 2005 | JP |
| 2006-164758 | Jun 2006 | JP |
| 2006-261132 | Sep 2006 | JP |
| 2006-318928 | Nov 2006 | JP |
| 2006-318929 | Nov 2006 | JP |
| 2007-128714 | May 2007 | JP |
| 2007-213866 | Aug 2007 | JP |
| 3959333 | Aug 2007 | JP |
| 2007-258095 | Oct 2007 | JP |
| 2008-060033 | Mar 2008 | JP |
| 2008-166156 | Jul 2008 | JP |
| 2009-104805 | May 2009 | JP |
| 2009-179501 | Aug 2009 | JP |
| 2010-080407 | Apr 2010 | JP |
| 2010-102895 | May 2010 | JP |
| 2010-244847 | Oct 2010 | JP |
| 2010-272239 | Dec 2010 | JP |
| 2011-028976 | Feb 2011 | JP |
| 2011-082133 | Apr 2011 | JP |
| 2011-138718 | Jul 2011 | JP |
| 4739780 | Aug 2011 | JP |
| 2011-210694 | Oct 2011 | JP |
| 2012-043794 | Mar 2012 | JP |
| 2012-066944 | Apr 2012 | JP |
| 2012-074366 | Apr 2012 | JP |
| 2012-084257 | Apr 2012 | JP |
| 2012-169217 | Sep 2012 | JP |
| 2012-209077 | Oct 2012 | JP |
| 2013-012410 | Jan 2013 | JP |
| 2013-503449 | Jan 2013 | JP |
| 2013-062082 | Apr 2013 | JP |
| 2013-087040 | May 2013 | JP |
| 2013-091581 | May 2013 | JP |
| 2013-100197 | May 2013 | JP |
| 2013-516037 | May 2013 | JP |
| 2013-246936 | Dec 2013 | JP |
| 2014-049239 | Mar 2014 | JP |
| 2014-063707 | Apr 2014 | JP |
| 2014-063708 | Apr 2014 | JP |
| 2014-063724 | Apr 2014 | JP |
| 2014-116111 | Jun 2014 | JP |
| 2014-241193 | Dec 2014 | JP |
| 5643996 | Dec 2014 | JP |
| 2015-069958 | Apr 2015 | JP |
| 2015-082374 | Apr 2015 | JP |
| 2015-088450 | May 2015 | JP |
| 2015-099722 | May 2015 | JP |
| 2015-520109 | Jul 2015 | JP |
| 2015-156363 | Aug 2015 | JP |
| 2015-191853 | Nov 2015 | JP |
| 2015-201432 | Nov 2015 | JP |
| 2016-025077 | Feb 2016 | JP |
| 2016-033902 | Mar 2016 | JP |
| 2016-072071 | May 2016 | JP |
| 2016-076454 | May 2016 | JP |
| 2016-143490 | Aug 2016 | JP |
| 2017-021942 | Jan 2017 | JP |
| 2014156116 | Feb 2017 | JP |
| 2017-033817 | Feb 2017 | JP |
| 2017-091777 | May 2017 | JP |
| 2017-213417 | Dec 2017 | JP |
| 2018-088400 | Jun 2018 | JP |
| 2018-092934 | Jun 2018 | JP |
| 2018-147726 | Sep 2018 | JP |
| 2020-202184 | Dec 2020 | JP |
| 10-0696619 | Mar 2007 | KR |
| 2009-0111130 | Oct 2009 | KR |
| 2012-0099375 | Sep 2012 | KR |
| 2012-0114955 | Oct 2012 | KR |
| 2015-0063955 | Jun 2015 | KR |
| 2016-0092946 | Aug 2016 | KR |
| 2016-0128978 | Nov 2016 | KR |
| WO-2011031544 | Mar 2011 | WO |
| WO-2011031546 | Mar 2011 | WO |
| WO-2011079238 | Jun 2011 | WO |
| WO-2011141486 | Nov 2011 | WO |
| WO-2011152183 | Dec 2011 | WO |
| WO-2011155781 | Dec 2011 | WO |
| WO-2012005180 | Jan 2012 | WO |
| WO-201 2029729 | Mar 2012 | WO |
| WO-2012124242 | Sep 2012 | WO |
| WO-2012132387 | Oct 2012 | WO |
| WO-2013066593 | May 2013 | WO |
| WO-2013181994 | Dec 2013 | WO |
| WO-2014061653 | Apr 2014 | WO |
| WO-2014098238 | Jun 2014 | WO |
| WO-2014156116 | Oct 2014 | WO |
| WO-201 5047024 | Apr 2015 | WO |
| WO-2015079372 | Jun 2015 | WO |
| WO-2015111710 | Jul 2015 | WO |
| WO-2015136881 | Sep 2015 | WO |
| WO-2015145235 | Oct 2015 | WO |
| WO-2015163356 | Oct 2015 | WO |
| WO-2016017077 | Feb 2016 | WO |
| WO-2016017079 | Feb 2016 | WO |
| WO-2016053051 | Apr 2016 | WO |
| WO-2016053053 | Apr 2016 | WO |
| WO-2016116862 | Jul 2016 | WO |
| WO-2016155314 | Oct 2016 | WO |
| WO-2018211375 | Nov 2018 | WO |
| Entry |
|---|
| Noboru Taguchi, Tomoki Akita, Kuniaki Tatsumi, Hikari Sakaebe, Characterization of MgO-coated-LiCoO2 particles by analytical transmission electron microscopy, Journal of Power Sources, vol. 328, 2016 p. 161-66. (Year: 2016). |
| Antolini.E, “LiCoO2: formation, structure, lithium and oxygen nonstoichiometry, electrochemical behaviour and transport properties”, Solid State Ionics, 2004, vol. 170, No. 3-4, pp. 159-171. |
| Ding.Y et al., “Preparation of nano-structured LiFePO4/graphene composites by co-precipitation method”, Electrochemistry Communications, 2010, vol. 12, No. 1, pp. 10-13, Elsevier. |
| Ceder.G et al., “Identification of cathode materials for lithium batteries guided by first-principles calculations”, Nature, Apr. 16, 1998, vol. 392, pp. 694-696. |
| Gopukumar.S et al., “Synthesis and electrochemical performance of tetravalent doped LICoO2 in lithium rechargeable cells”, Solid State Ionics, 2003, vol. 159, pp. 223-232, Elsevier. |
| Katsuno.H et al., “Growth modes in two-dimensional heteroepitaxy on an elasticsubstrate”, J. Cryst. Growth (Journal of Crystal Growth), Feb. 15, 2005, vol. 275, No. 1-2, pp. e283-e288, Elsevier. |
| Taguchi.N et al., “Characterization of MgO-coated-LiCoO2 particles by analytical transmission electron microscopy”, Journal of Power Sources, 2016, vol. 328, pp. 161-166, Elsevier. |
| Thackeray.M et al., “Li2MnO3-stabilized LiMO2(M=Mn, Ni, Co) electrodes for lithium-ion batteries”, J. Mater. Chem. (Journal of Materials Chemistry), 2007, vol. 17, pp. 3112-3125. |
| Berbenni.V et al., “Thermogravimetry and X-Ray Diffraction Study of the Thermal Decomposition Processes in LI2CO3—MNCO3 Mixtures”, Journal of Analytical and Applied Pyrolysis, 2002, vol. 62, pp. 45-62. |
| Johnson.C et al., “Lithium-manganese oxide electrodes with layered-spinel composite structures xLi2MnO3 ⋅ (1-x)Li1+yMn2-yO4(0>x>1,0≤y≤0.33) for lithium batteries”, Electrochemistry Communications, May 1, 2005, vol. 7 , No. 5, pp. 528-536, Elsevier. |
| Khedr.A et al., “Synthesis, Structure, and Electrochemistry of Sm-Modified LiMn2O4 Cathode Materials for Lithium-Ion Batteries”, J. Electron. Mater.(Journal of Electronic Materials), Apr. 23, 2013, vol. 42, No. 6, pp. 1275-1281. |
| Lee.S et al., “Antiferromagnetic ordering in Li2MnO3 single crystals with a two-dimensional honeycomb lattice”, Journal of Physics: Condensed Matter, Nov. 14, 2012, vol. 24, No. 45, pp. 456004-1-456004-9. |
| Mukai.K et al., “Magnetic properties of the chemically delithiated LixMn2O4 with 0.07≤x≤1”, Journal of Solid State Chemistry, May 1, 2011, vol. 184, No. 5, pp. 1096-1104. |
| Wang.Z et al., “EELS analysis of cation valence states and oxygen vacancies in magnetic oxides”, MICRON, Oct. 1, 2000, vol. 31, No. 5, pp. 571-580, Elsevier. |
| Tan.H et al., “Oxidation state and chemical shift investigation in transition metal oxides by EELS”, Ultramicroscopy, May 1, 2012, vol. 116, pp. 24-33, Elsevier. |
| McCalla.E et al., “The spinel and cubic rocksalt solid-solutions in the Li—Mn—Ni oxide pseudo-ternary system”, Solid State Ionics, May 2, 2013, vol. 242, pp. 1-9, Elsevier. |
| Dreyer.D et al., “The Chemistry of Graphene Oxide”, Chemical Society Reviews, Nov. 3, 2009, vol. 39, No. 1, pp. 228-240. |
| Zou.M et al., “Synthesis and Electrochemical Performance of High Voltage Cycling LiM0.05Co0.95O2 as Cathode Material for Lithium Rechargeable Cells”, Electrochemical and Solid-State Letters, 2004, vol. 7, No. 7, pp. A176-A179. |
| Tukamoto.H et al., “Electronic Conductivity of LiCoO2 and its Enhancement by Magnesium Doping”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Sep. 1, 1997, vol. 144, No. 9, pp. 3164-3168. |
| Cho.Y et al., “High Performance LiCoO2 Cathode Materials at 60° C. for Lithium Secondary Batteries Prepared by the Facile Nanoscale Dry-Coating Method”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2010, vol. 157, No. 5, pp. A617-A624. |
| Yano.A et al., “LiCoO2 Degradation Behavior in the High-Voltage Phase Transition Region and Improved Reversibility with Surface Coating”, J. Electrochem. SOC. (Journal of the Electrochemical Society), 2017, vol. 164, No. 1, pp. A6116-A6122. |
| Liu.L et al., “Electrochemical and In Situ Synchrotron XRD Studies on Al2O3-Coated LiCoO2 Cathode Material”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2004, vol. 151, No. 9, pp. A1344-A1351. |
| Cho.J et al., “Comparison of Al2O3- and AlPO4-coated LiCoO2 cathode materials for a Li-ion cell”, Journal of Power Sources, 2005, vol. 146, pp. 58-64, Elsevier. cited by applicant |
| Jin.Y et al., “Electrochemical Characterizations of Commercial LICoO2 Powders with Surface Modified by Li3PO4 Nanoparticles”, Electrochemical and Solid-State Letters, Apr. 3, 2006, vol. 9, No. 6, pp. A273-A276. |
| Hong.W et al., “Modification of LiCoO2 by Surface Coating with MgO/TiO2/SiO2 for High-Performance Lithium-Ion Battery”, Electrochemical and Solid-State Letters, Dec. 20, 2005, vol. 9, No. 2, pp. A82-A85. |
| Eom.J et al., “M3(PO4)2-Nanoparticie-Coated LiCoO2 vs LiCo0.96M0.04O2(M=Mg and Zn) on Electrochemical and Storage Characteristics”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Jan. 8, 2008, vol. 155, No. 3, pp. A201-A205. |
| Kim.Y et al., “Suppression of Cobalt Dissolution from the LiCoO2 Cathodes with Various Metal-Oxide Coatings”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2003, vol. 150, No. 12, pp. A1723-A1725. |
| Chung.K et al., “Structural Studies on the Effects of ZrO2 Coating on LiCoO2 during Cycling Using In Situ X-Ray Diffraction Technique”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2006, vol. 153, No. 11, pp. A2152-A2157. |
| Fang.T et al., “Effect of calcination temperature on the electrochemical behavior of ZnO-coated LiCoO2 cathode”, Surface & Coatings Technology , Apr. 19, 2006, vol. 201, No. 3-4. pp. 1886-1893, Elsevier. |
| International Search Report (Application No. PCT/IB2017/053896) dated Oct. 3, 2017. |
| Written Opinion (Application No. PCT/IB2017/053896) dated Oct. 3, 2017. |
| Yamamoto.K et al., “in situ Total-Reflection Fluorescence X-Ray Absorption Spectroscopic Study on Stability at LiFePO4 / Elecrtrolyte Interface”, 224th ECS Meeting Abstract, Oct. 27, 2013, p. 923. |
| Yamamoto.K et al., “Stabilization of the Electronic Structure at the Cathode/Electrolyte Interface via MgO Ultra-thin Layer during Lithium-ions Insertion/Extraction”, Electrochemistry, Oct. 5, 2014, vol. 82, No. 10, pp. 891-896. |
| Wang.Z et al., “Electrochemical Evaluation and Structural Characterization of Commercial LiCoO2 Surfaces Modified with MgO for Lithium-ion Batteries”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Mar. 4, 2002, vol. 149, No. 4, pp. A466-A471. |
| Lee.Y et al., “Phase Transitions of Bare and Coated LixCoO2 (x=0.4 and 0.24) at 300° C.”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Jul. 28, 2005, vol. 152, No. 9, pp. A1824-A1827. |
| Gabrisch.H et al., “Hexagonal to Cubic Spinel Transformation in Lithiated Cobalt Oxide TEM Investigation”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2004, vol. 151, No. 6, pp. A891-A897. |
| Geder.J et al., “Impact of active material surface area on thermal stability of LiCoO2 cathode”, Journal of Power Sources, Jul. 1, 2014, vol. 257, pp. 286-292, |
| Shi.S et al., “Enhanced cycling stability of Li[Li 0.2Mn0.54Ni0.13Co0.13]O2 by surface modification of MgO with melting impregnation method”, Electrochimica Acta, Nov. 1, 2012, vol. 88, pp. 671-679. |
| Bensalah.N et al., “Review on Synthesis, Characterizations, and Electrochemical Properties of Cathode Materials for Lithium Ion Batteries”, Journal of Material Science & Engineering, 2016, vol. 5, No. 4, pp. 1000258-1-1000258-21. |
| Lu.Y et al., “Recent progress on lithium-ion batteries with high electrochemical performance”, Science China Chemistry, Feb. 25, 2019, vol. 62, No. 5, pp. 533-548. |
| Xiao.B, “Surface Modifification of Electrode Materials for Lithium-Ion Batteries”, Graduate Program in Mechanical and Materials Engineering, 2006, pp. 1-235. |
| Ohnishi.M et al., “Investigation of the surface degradation of LiCoO2 particles in the cathode materials of Li-ion batteries using FIB-TOF-SIMS”, Journal of Surface Analysis, 2013, vol. 20, No. 2, pp. 99-110. |
| Koyama.Y et al., “Co K-edge XANES of LiCoO2 and CoO2 with a variety of structures by supercell density functional calculations with a core hole”, Phys. Rev. B (Physical Review. B), Feb. 27, 2012, vol. 85, No. 7, pp. 075129-1-075129-7. |
| Iwaya.K et al., “Impact of Lithium-Ion Ordering on Surface Electronic States of LixCoO2”, Phys. Rev. Lett. (Physical Review Letters), Sep. 20, 2013, vol. 111, No. 12, pp. 126104-1-126104-5. |
| Zou.M et al., “Synthesis of High-Voltage (4.5 V) Cycling Doped LiCoO2 for Use in Lithium Rechargeable Cells”, Chem. Mater. (Chemistry of Materials), Dec. 16, 2003, vol. 15, No. 25, pp. 4699-4702. |
| Park.S et al., “Novel Surface Modification Technique to Improve Electrochemical Performance of LiCoO2 at High Voltage”, Electrochemical and Solid-State Letters, Apr. 21, 2005, vol. 8, No. 6, pp. A299-A302. |
| Mladenov.M et al., “Effect of Mg doping and MgO-surface modification on the cycling stability of LiCoO2 electrodes.”, Electrochemistry Communications, Aug. 1, 2001, vol. 3, No. 8, pp. 410-416. |
| Liu.A et al., “Synthesis of Mg and Mn Doped LiCoO2 and Effects on High Voltage Cycling”, J. Electrochem. SOC. (Journal of the Electrochemical Society), Jun. 2, 2017, vol. 164, No. 7, pp. A1655-A1664. |
| Quinlan.R et al., “XPS Investigation of the Electrolyte Induced Stabilization of LiCoO2 and “AlPO4”-Coated LiCoO2 Composite Electrodes”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Dec. 3, 2015, vol. 163, No. 2, pp. A300-A308. |
| Jo.C et al., “An effective method to reduce residual lithium compounds on Ni-rich Li[Ni0.6Co0.2Mn0.2]O2 active material using a phosphoric acid derived Li3PO4 nanolayer”, Nano Research, Dec. 4, 2014, vol. 8, No. 5, pp. 1464-1479, Springer. |
| Tebbe.J et al., “Mechanisms of LiCoO2 Cathode Degradation by Reaction with HF and Protection by Thin Oxide Coatings”, ACS Applied Materials & Interfaces, Oct. 12, 2015, vol. 7, No. 43, pp. 24265-24278. |
| Sun.Y et al., “High-energy cathode material for long-life and safe lithium batteries”, Nature Materials, Mar. 22, 2009, vol. 8, pp. 320-324. |
| Joshi.T et al., “Effects of Dissolved Transition Metals on the Electrochemical Performance and SEI Growth in Lithium-Ion Batteries”, J. Electrochem. SOC. (Journal of the Electrochemical Society), 2014, vol. 161, No. 12, pp. A1915-A1921. |
| Chen.Z et al., “Staging Phase Transitions in LixCoO2”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2002, vol. 149, No. 12, pp. A1604-A1609. |
| Shim.J et al., “Characterization of Spinel LixCo204-Coated LiCo02 Prepared with Post-Thermal Treatment as a Cathode Material for Lithium Ion Batteries”, Chem. Mater. (Chemistry of Materials), Apr. 10, 2015, vol. 27, No. 9, pp. 3273-3279. |
| Okumura.T et al., “Correlation of lithium ion distribution and X-ray absorption near-edge structure in O3- and O2-lithium cobalt oxides from first-principle calculation”, Journal of Materials Chemistry, 2012, vol. 22, pp. 17340-17348. |
| Motohashi.T et al., “Electronic phase diagram of the layered cobalt oxide system LixCoO2 (0.0≤x≤1.0)”, Phys. Rev. B (Physical Review. B), Oct. 9, 2009, vol. 80, No. 16, pp. 165114-1-155114-9. |
| Counts.W et al., “Fluoride Model Systems: II, The Binary Systems CaF2—BeF2, MgF2—BeF2, and LiF—MgF2”, J. Am. Ceram. Soc. (Journal of the American Ceramic Society), 1953, vol. 36, No. 1, pp. 12-17. |
| Ohzuku.T et al., “Solid-State Redox Reactions of LiCoO2 (R-3m) for 4 Volt Secondary Lithium Cells”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Nov. 1, 1994, vol. 141, No. 11, pp. 2972-2977. |
| Amatucci.G et al., “CoO2, The End Member of the LixCoO2 Solid Solution”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Mar. 1, 1996, vol. 143, No. 3, pp. 1114-1123. |
| Wang.Z et al., “Structural and electrochemical characterizations of surface-modified LiCoO2 cathode materials for Li-ion batteries”, Solid State Ionics, Jun. 2, 2002, vol. 148, No. 3-4, pp. 335-342, Elsevier. |
| Wang.Z et al., “Improving the cycling stability of LiCoO2 at 4.5 V through co-modification by Mg doping and zirconium oxyfluoride coating”, Ceramics Internationa, 2015, vol. 41, No. 1, pp. 469-474. |
| Wang.Z et al., “Mg doping and zirconium oxyfluoride coating co-modification to enhance the high-voltage performance of LiCoO2 for lithium ion battery”, Journal of Alloys and Compounds, Feb. 5, 2015, vol. 621, pp. 212-219. |
| Kweon.H et al., “Effects of metal oxide coatings on the thermal stability and electrical performance of LiCoCO2 in a Li-ion cell”, Journal of Power Sources, Feb. 16, 2004, vol. 126, pp. 156-162, Elsevier. |
| Shim.J et al., “Effects of MgO Coating on the Structural and Electrochemical Characteristics of LiCoO2 as Cathode Materials for Lithium Ion Battery”, Chem. Mater. (Chemistry of Materials), Mar. 24, 2014, vol. 26, No. 8, pp. 2537-2543. |
| Zhao.H et al., “Improvement of electrochemical stability of LiCoO2 cathode by a nano-crystalline coating”, Journal of Power Sources, May 20, 2004, vol. 132, pp. 195-200, Elsevier. |
| Iriyama.Y et al., “Effects of surface modification by MgO on interfacial reaction of lithium cobalt oxide thin film electrode”, Journal of Power Sources, Oct. 5, 2004, vol. 137, pp. 111-116, Elsevier. |
| Shim.J et al., “Effects of MgO Coating on the Structural and Electrochemical Characteristics of LiCoO2 as Cathode Materials for Lithium Ion Battery”, Chem. Mater. (Chemistry of Materials), [e.g. ), Suppor] Supporting Information, Mar. 24, 2014, vol. 26, No. 8, pp. 31-33. |
| Orikasa.Y et al., “Origin of Surface Coating Effect for MgO on LiCoO2 to Improve the Interfacial Reaction between Electrode and Electrolyte”, Adv. Mater.Interfaces (Advanced Materials Interfaces), Aug. 28, 2014, vol. 1, No. 9, pp. 1400195-1-1400195-8. |
| Shim. J et al., “Synergistic effects of coating and doping for lithium ion battery cathode materials: synthesis and characterization of lithium titanate-coated LiCoO2 with Mg doping”, Electrochimica Acta, Dec. 20, 2015, vol. 186, pp. 201-208, Elesevier. |
| Benecke.M et al., “Effect of LiF on Hot-Pressing of MgO”, J. Am. Ceram. Soc. (Journal of the American Ceramic Society), Jul. 1, 1967, vol. 50, No. 7, pp. 365-368. |
| Hart.P et al., “Densification Mechanisms in Hot-Pressing of Magnesia with a Fugitive Liquid”, J. Am. Ceram. Soc. (Journal of the American Ceramic Society), Feb. 1, 1970, vol. 53, No. 2, pp. 83-86. |
| Belsky.A et al., “New developments in the Inorganic Crystal Structure Database (ICSD): Accessibility in support of materials research and design.”, Acta. Cryst.(Acta Crystallographica Section B), Jun. 1, 2002, vol. B58, No. 3, pp. 364-369. |
| Alcantara.R et al., “SPES, 6Li MAS NMR, and Ni3+ EPR evidence for the formation of Co2+-containing spinel phases in LiCoO2 cycled electrode materials”, Journal of Electroanalytical Chemistry, Aug. 28, 1998, vol. 454, No. 1-2, pp. 173-181. |
| Antaya.M et al., “Preparation and Characterization of LiCoO2 Thin Films by Laser Ablation Deposition”, J. Electrochem. Soc. (Journal of the Electrochemical Society), Mar. 1, 1993, vol. 140, No. 3, pp. 575-578. |
| Schipper.F et al., “Study of Cathode Materials for Lithium-Ion Batteries: Recent Progress and New Challenges”, Inorganics, Apr. 28, 2017, vol. 5, No. 2, pp. 1-29. |
| Xia.H et al., “Phase Transitions and High-Voltage Electrochemical Behavior of LiCoO2 Thin Films Grown by Pulsed Laser Deposition”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2007, vol. 154, No. 4, pp. A337-A342. |
| Sun.Y et al., “Role of AlF3 Coating on LiCoO2 Particles during Cycling to Cutoff Voltage above 4.5 V”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2009, vol. 156, No. 12, pp. A1005-A1010. |
| Araki.K et al., “Electrochemical properties of LiNi1/3Co1/3Mn1/3O2 cathode material modified by coating with Al2O3 nanoparticles”, Journal of Power Sources, 2014, vol. 269, pp. 236-243. |
| Kim.H et al., “Capacity fading behavior of Ni-rich layered cathode materials in Li-ion full cells”, Journal of Electroanalytical Chemistry, 2016, vol. 782, pp. 168-173. |
| Lin.F et al., “Surface reconstruction and chemical evolution of stoichiometric layered cathode materials for lithium-ion batteries”, Nature Communications, Mar. 27, 2014, vol. 5, pp. 3529-1-3529-9. |
| Yano.A et al., “Surface Structure and High-Voltage Charge/Discharge Characteristics of Al-Oxide Coated LiNi1/3Co1/3Mn1/3O2 Cathodes”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2015, vol. 162, No. 2, pp. A3137-A3144. |
| Yano.A et al., “Surface Structure and High-Voltage Charging/Discharging Performance of Low-Content Zr-Oxide-Coated LiNi1/3Co1/3Mn1/3O2”, J. Electrochem. Soc. (Journal of the Electrochemical Society), 2016, vol. 163, No. 2, pp. A75-A82. |
| Chen et al., “Role of surface coating on cathode materials for lithium-ion batteries”, Journal of Materials Chemistry, 2010, vol. 20, pp. 7606-7612. |
| Chinese Office Action (Application No. 201911351437.9) dated Sep. 15, 2020. |
| Chinese Office Action (Application No. 201911351432.6) dated Nov. 5, 2020. |
| Chinese Office Action (Application No. 202010628027.0) dated Dec. 2, 2020. |
| Lee.H et al., “Atomic structure and defect energetics of LiCoO2 grain boundary”, Materials Research Bulletin, May 6, 2016, vol. 82, pp. 81-86. |
| Notice of Reasons for Revocation (Patent No. Japanese Patent No. 6736240) dated May 18, 2021. |
| Notice of Reasons for Revocation (Patent No. Japanese Patent No. 6736242) dated May 25, 2021. |
| Written Opposition to Grant of Patent (Patent number. Japanese Patent No. 6916262) dated Mar. 2, 2022. |
| Notice of Reasons for Revocation (Patent number. Japanese Patent No. 6916262) dated May 25, 2022. |
| Hashimoto et al., “Lateral Resolution of EDX Analysis with Low Acceleration Voltage SEM,” Journal of Surface Analysis, Jan. 6, 2008, vol. 14, No. 4, pp. 428-432. |
| Chinese Office Action (Application No. 201711141051.6) dated Dec. 2, 2021. |
| Written Opposition to Grant of Patent (Patent number. Japanese Patent No. 6857272) dated Nov. 16, 2021. |
| Notice of Reasons for Revocation (Patent number. Japanese Patent No. 6857272) dated Jan. 25, 2022. |
| Chemical Power Source Battery Principle and Manufacturing Technology, Jun. 30, 2000, pp. 325-326. |
| Chinese Office Action (Application No. 201711141051.6) dated Jul. 6, 2022. |
| Some Frontier Research Topics in Materials Chemistry, 2013, pp. 120-129. |
| Chinese Office Action (Application No. 201911351436.4) dated Jul. 7, 2022. |
| Chinese Office Action (Application No. 202010788736.5) dated Apr. 6, 2021. |
| Chinese Office Action (Application No. 201911351437.9) dated Apr. 22, 2021. |
| Written Opposition to Grant of Patent (Patent Number. Japanese Patent No. 6736240) dated Feb. 4, 2021. |
| Written Opposition to Grant of Patent (Patent number. Japanese Patent No. 6736242) dated Feb. 4, 2021. |
| Typical element, https://ko.wikipedia.org/wiki/%EC%A0%84%ED%98%95_%EC%9B%90%EC%86%8C. |
| Petition for Patent Cancellation for KR10-2319774-0000. |
| Number | Date | Country | |
|---|---|---|---|
| 20200373567 A1 | Nov 2020 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16900108 | Jun 2020 | US |
| Child | 16917190 | US | |
| Parent | 15800184 | Nov 2017 | US |
| Child | 16900108 | US |