Powder composition, dispersion of this powder composition in oil and cosmetic material containing same

[0001] This application is a continuation-in-part of PCT/JP01/06310 filed on Jul. 19, 2001, entire disclosure is incorporated by reference herein.

FIELD OF THE INVENTION

[0002] This invention relates to a powder composition suitable for cosmetic materials, and in particular to a powder composition having excellent dispersibility comprising alcoholic hydroxyl groups treated by a silicone compound, to a powder composition in oil obtained by dispersing this powder composition in oil, and to a cosmetic material containing these preparations.

BACKGROUND OF THE INVENTION

[0003] Untreated powders tend to stick together due to charges and polarity on the powder surface and minute amounts of impurities, and this interferes with the dispersibility and stability of the powder.

[0004] Various types of surface treatment have been proposed to improve the dispersibility and stability of the powder, and when used in cosmetics, they improve the “feel” of the product.

[0005] The reagents and methods used to treat the powder surface are chosen taking account of properties regarding the nature of the powder surface to be treated and the dispersing medium. For example, there is lipophilic treatment by oils or metal soaps, hydrophilic treatment by surfactants or water-soluble polymers, or water-repellent/oil-repellent treatment by silicone oils.

[0006] Among these, silicone compounds which have excellent feel, water repellent properties and stability are becoming increasingly widely used as oils. In order to improve the miscibility of the powder, a surface treatment using methyl hydrogen siloxane has been proposed in Japanese Patent No. 02719303 (Koho), and a surface improvement by a straight chain, single-terminated alkoxy-modified silicone has been proposed in Japanese Patent Application Public Disclosure (Kokai) Hei 7-196946 (Koho). Further, to improve dispersibility in the silicone oil, Japanese Patent Application Public Disclosure (Kokai) Hei 10-167946 (Koho) discloses a method wherein a polyether-modified silicone with a HLB of 2-7 is used as a dispersant.

[0007] However, although aggregation and sedimentation were improved in these surface-treated powders, further improvements were still desired. Depending on the treatment agent or treatment method, the powder and treatment agent tended to separate from the cosmetic material, or the powder became lumpy with passage of time and was difficult to re-disperse, so product quality and feel were adversely affected. It was therefore desired to develop a powder composition and powder dispersion with little cohesion, excellent dispersibility and time-dependent stability, and a pleasant feel.

[0008] It is therefore a first object of this invention to provide a powder composition having little cohesion and excellent dispersibility.

[0009] It is a second object of this invention to provide an oil-based powder having little cohesion and excellent time-dependent stability.

[0010] It is a third object of this invention to provide a cosmetic material having excellent usability and good time-dependent stability.

SUMMARY OF THE INVENTION

[0011] The above objects of the invention were obtained by a powder composition comprising a silicone represented by the following formula (1) having alcoholic hydroxyl groups and a powder, by an oil-based powder dispersion comprising this powder composition dispersed in an oil, and a cosmetic material comprising these.

R1aR2bR3cSiO(4-a-b-c)/2 (1)

[0012] (1) In the formula, R1 are organic groups which may be the same or different chosen from alkyl, aryl, aralkyl and fluorine-substituted alkyl groups having 1-30 carbon atoms, R2 is a substituent having one or more alcoholic hydroxyl groups, R3 is a group represented by the following general formula (2),

[0013] R4is an oxygen atom or a bifunctional hydrocarbon group, and a, b, c, d are values satisfying the relations 1.0≦a≦2.5, 0.001≦b≦1, 0.001≦c≦1, 1.5≦a+b+c≦2.6, and d is integer of 0≦d≦500.

[0014] As the powder composition of this invention has excellent dispersibility, it is suitable for cosmetic product applications where usability and time-dependent stability are particularly required. The cosmetic material of this invention comprising the powder composition of this invention not only has an excellent cool feel, but also long-lasting make-up properties and time-dependent stability.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Specific examples of R1 in the general formula (1), R1aR2bR3cSiO(4-a-b-c)/2 are alkyl groups such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, cycloalkyl groups such as cyclopentyl and cyclohexyl, aryl groups such as phenyl and tolyl, aralkyl groups such as benzyl and phenetyl, alcohol residues such as oleyloxy and allyloxy, and fluorine-substituted alkyl groups such as trifluoropropyl and heptadecafluorodecyl.

[0016] Specific examples of R2 are groups having one OH group such as —C3H6OH, —C4H8OH, —C8H16OH and —C11H22OH, groups having two primary alcohols such as

[0017] groups having a primary and secondary alcohol such as

C3H6OCH2CH(OH)CH2OH, —C11H22OCH2CH(OH)CH2OH,

[0018] and groups having two primary alcohols and two secondary alcohols such as

—C3H6OCH(CH2OCH2CH(OH)CH2OH)2, —C11H22OCH(CH2OCH2CH(OH)CH2OH)2.

[0019] R3 is a group represented by general formulae (6) and (7).

[0020] a is 1.0-2.5 but preferably 1.2-2.3, while b and c are 0.001-1.5 but preferably 0.005-1.0, respectively.

[0021] R5 in the above formula is identical to R1 or a hydroxyl group.

[0022] n is an integer in the range 1-5, and in particular, n synthesized by the reaction of a vinyl group and —SiH group is 2.

[0023] d is 0-500, but preferably 1-100. When d is larger than 500, there may be problems such as poor reactivity with the main chain.

[0024] The branched silicone which has a group represented by the general formula (6) is synthesized by an addition reaction of an organohydrogen, and a single-terminated vinyl-modified polysiloxane represented by the following general formula (8).

[0025] On the other hand, a branched silicone which has a group represented by the general formula (7) is synthesized by an equilibration reaction using an acid or an alkali catalyst according to conventional methods. A branch silicone unit is introduced by using a trialkoxymethylsilane, trihydroxymethylsilane, tris(trimethylsiloxy) methylsilane, and their straight chain or cyclic oligomers for the equilibration reaction. Alternatively, it is possible to perform a ring-opening polymerization by a living polymerization catalyst using a silanol-modified silicone.

[0026] There is no particular limitation on the weight average molecular weight of the silicone compound of the above-mentioned general formula (1), when using it as a surface treatment agent for powder, but it is preferably 300-100,000. If 100,000 is exceeded, it will have a tacky feel due to the viscosity of silicone, and if it less than 300, the smoothness of silicone is not obtained. In particular, 1,000-10,000 is preferred.

[0027] The silicone compound of the above-mentioned general formula (1) used by this invention is easily synthesized by performing an addition reaction of an organohydrogen polysiloxane and a vinyl group-containing alcohol-modified compound having the following general formula in the presence of a platinum catalyst or a rhodium catalyst.

[0028] It can also be synthesized by adding the following acetal compound, CH2═CHCnH2nOCH(CH2OCH2CH(OH)CH2OH)2, and performing a acetone removal reaction.

[0029] The organohydrogenpolysiloxane used in these cases may be either straight chain or cyclic, but straight chain is preferred from the viewpoint that the addition reaction proceeds more satisfactorily. Also, there is no particular limitation on the bonding site of the —SiH group, which may be either the side chain or the end of the chain.

[0030] It is preferred that the above addition reaction proceeds in the presence of a platinum catalyst or a rhodium catalyst. Specific examples of this catalyst are platinic acid chloride, alcohol-modified platinic acid chloride and platinic acid chloride-vinyl siloxane complex. The amount of catalyst used may be that which is usually employed, but 50 ppm or less and especially 20 ppm or less is preferred in terms of the amount of platinum or rhodium.

[0031] The above-mentioned addition reaction may be performed in an organic solvent if needed. Examples of the organic solvent are aliphatic alcohols, such as methanol, ethanol, 2-propanol and butanol, aromatic hydrocarbons, such as toluene and xylene, aliphatic or cycloaliphatic hydrocarbons, such as n-pentane, n-hexane and cyclohexane, and halogenated hydrocarbons, such as dichloromethane, chloroform and carbon tetrachloride. There is no particular limitation on the addition reaction conditions, but the reaction may conveniently be performed under reflux for 1-10 hours.

[0032] The powders used by this invention may be any of an inorganic powder, organic powder, surfactant metal salt powder (metal soap), colored pigment, pearl pigment, metal powder pigment, tar coloring matter and natural coloring matter. Examples of inorganic powders are titanium dioxide, zirconium oxide, zinc oxide, cerium oxide, magnesium oxide, barium sulfate, calcium sulfate, magnesium sulfate, calcium carbonate, magnesium carbonate, talc, mica, kaolin, sericite, muscovite, synthetic mica, phlogopite, ruby mica, biotite, lithia mica, silicic acid, silicic acid anhydride, aluminium silicate, magnesium silicate, aluminium magnesium silicate, calcium silicate, barium silicate, strontium silicate, metal salt of tungstic acid, hydroxyapatite, vermiculite, haidilite, bentonite montmorillonite, hectorite, zeolite, ceramic powder, calcium secondary phosphate, alumina, aluminium hydroxide, boron nitride and silica. For use in cosmetic materials, fillers such as mica and sericite, or zinc oxide and titanium dioxide, are preferred.

[0033] Examples of organic powders are polyamide powder, polyester powder, polyethylene powder, polypropylene powder, polystyrene powder, polyurethane powder, benzoguanamine powder, polymethyl benzoguanamine powder, poly-tetrafluoroethylene powder, polymethylmethacrylate powder, cellulose powder, silk powder and nylon powder such as 12 nylon powder or 6 nylon powder, styrene acrylic acid copolymer, divinylbenzene-styrene copolymer powder, vinyl resin powder, urea resin powder, phenol resin powder, fluororesin powder, silicon resin powder, acrylate resin powder, melamine resin powder, epoxy resin powder, polycarbonate resin powder, microcrystalline fiber powder, starch and lauroyl lysine powder.

[0034] Examples of metal salt powders (metal soaps) are zinc stearate, aluminum stearate, calcium stearate, magnesium stearate, zinc myrisate, magnesium mynrstate, zinc cetyl phospate, calcium cetyl phosphate and zinc sodium cetyl phosphate.

[0035] Examples of colored pigments include inorganic red pigments, such as iron oxide, iron hydroxide and iron titanate; inorganic brown pigments, such as gamma-iron oxide;

[0036] inorganic yellow pigments, such as iron oxide yellow and loess; inorganic black pigments, such as iron oxide black and carbon black; inorganic violet pigments, such as manganese violet and cobalt violet; inorganic green pigments, such as chromium hydroxide, chromium oxide, cobalt oxide and cobalt titanate; inorganic blue pigments, such as Prussian blue and ultramarine blue; lakes of tar pigments; lakes of natural dyes; and synthetic resin powder complexes of the inorganic pigments as recited above.

[0037] Examples of the pearl pigment include titanium dioxide-coated mica, bismuth oxychloride, titanium dioxide-coated bismuth oxychloride, titanium dioxide-coated talc, fish scale guanine and titanium dioxide-coated colored mica; and examples of the metallic powder pigment include aluminum powder, copper powder and stainless powder.

[0038] Examples of tar pigments are Red No. 3, Red No. 104, Red No. 106, Red No. 201, Red No. 202, Red No. 204, Red No. 205, Red No. 220, Red No. 226, Red No. 227, Red No. 228, Red No. 230, Red No. 401, Red No. 505, Yellow No. 4, Yellow No. 5, Yellow No. 202, Yellow No. 203, Yellow No.204, Yellow No. 4, Yellow No. 5, Yellow No.202, Yellow No. 203, Yellow No. 204, Green No. 3, Green No. 201, Green No. 204, Green No. 205, Orange No. 201, Orange No. 203, Orange No. 204, Orange No. 206 and Orange No. 207.

[0039] The natural pigments described above include powders of carminic acid, laccaic acid, carthamin, bradilin and crocin.

[0040] Furthermore, these powders are not particularly restricted as to their shapes (spherical, acicular or tabular), their sizes (smoke particles, fine particles or pigment particles etc.) or their structures (whether they are porous or nonporous), provided that they have so far been used in traditional cosmetic materials.

[0041] These powders may be complexed or surface-treated with oils, silicones other than the silicone represented by the above-mentioned general formula (1), or fluorine compounds.

[0042] The new silicone powder treatment agent represented by the above-mentioned general formula (1) of this invention can be applied to the powder surface by any known method.

[0043] Although the treatment method can be suitably chosen from well-known methods, the following methods may for example be mentioned.

[0044] 1. The target powder is dispersed in a medium chosen from water or an organic solvent blended with a powder treatment agent.

[0045] 2. After mixing the powder with the powder treatment agent, surface treatment is performed by crushing the mixture in a ball mill or jet mill.

[0046] The oil-based powder of this invention means a dispersion of the powder composition in an oil, or a solution or dispersion of a silicone compound in an oil to which the powder is then added so as to make a mixed dispersion, and it is a liquid dispersion. The oil-based dispersion of this invention may also be suitably modified by known methods such as the methods below.

[0047] 1. The powder composition obtained as described above may be dispersed in an oil such as an ester oil or silicone oil.

[0048] 2. A silicone compound is dissolved or dispersed in the oil described above, then the powder is added and mixed by a dispersion device such as a ball mill, bead mill or sand mill.

[0049] The oil-based dispersion thus obtained may be blended with a cosmetic material as it is.

[0050] When the silicone compound of the general formula (1) in this invention is used as a surface treatment agent for the powder, 0.1-30 weight parts but preferably 0.5-10 weight parts relative to 100 weight parts of the powder is used. Although it depends on the type and form of cosmetic material, the powder composition which has been surface-treated by the above silicone compound is generally blended with the cosmetic materials of this invention so that it is 0.1-99.9 weight parts of the whole cosmetic material.

[0051] To the present cosmetic materials, the agents used in general cosmetic materials, such as water, alcohols, water-soluble polymers, a film-forming agent, a surface active agent, an oil-soluble gelling agent, clay modified with organic compounds, resins, powdered materials, ultraviolet absorbents, a moisture retention agent, antiseptics, an antimicrobial agent, perfume, salts, antioxidants, pH regulators, a chelating agent, refrigerant, an anti-inflammatory agent; skin beautifying s, vitamins, amino acids, nucleic acids, hormones and clathrate compounds, can be added so far as they have no adverse influence on the effects of the present invention.

[0052] Specific examples of these agelits will now be given, although the invention is not limited thereto.

[0053] Examples of alcohols which can be used in this invention are ethanol, propanol, ethylene glycol, ethylene glycol monoalkyl ether, diethylene glycol monoethyl ether, polyethylene glycol, propylene glycol, dipropylene glycol, 1,3-butylene glycol, glycerol, diglycerol, polyglycerol, pentaerythritol, cane sugar, lactose, xylitol, sorbitol, mannitol, maltitol, carrageenan, agar, guar gum, dextrin, tragacanth gum, locust bean gum, polyvinyl alcohol, polyoxyethylene high polymers, polyoxyethylene polyoxypropylene copolymer high polymers, hyaluronic acid, chondroitin sulfate and chitin chitosan, two or more of these being used if necessary. These alcohols are 0.1-99.9% of the weight, but preferably 0.5-50.0% of the weight, of the cosmetic material. At less than 0.1% of the weight, moisture retention properties, antiseptic properties and mildew resistant properties are insufficient, and at more than 99.9% weight, it is impossible to demonstrate the effect of the powder composition of this invention.

[0054] The following are examples of oils which can be used in this invention. POE is polyoxyethylene. Natural animal and vegetable fats and oils, and semi-synthetic fats and oils, include avocado oil, linseed oil, almond oil, Chinese wax, perilla oil, olive oil, cacao butter, kapok wax, kaya oil, carnauba wax, liver oil, candellila wax, beef tallow, beef foot oil, beef bone fat, hydrogenated beef tallow, apricot kernel oil, spermaceti, hydrogenated oil, wheat germ oil, sesame oil, rice germ oil, rice bran oil, sugar cane wax, sasanqua oil, safflower oil, shea butter, Chinese tung oil, cinnamon oil, jojoba wax, shellac wax, turtle oil, soybean oil, tea seed oil, tsubaki oil, evening primrose oil, corn oil, lard, rape seed oil, Japanese tung oil, rice-bran wax, germ oil, horse fat, persic oil, palm oil, palm kernel oil, castor oil, hydrogenated castor oil, methyl caster oil fatty acid, sunflower oil, grape seed oil, bayberry wax, jojoba oil, macadamia nut oil, beeswax, mink oil, cottonseed oil, cotton wax, Japan wax, haze kernel oil, montan wax, coconut oil, hydrogenated coconut oil, tricoconut oil fatty acid glyceride, mutton-tallow, peanut oil, lanolin, liquid lanolin, reduced lanolin, lanolin alcohol, hard lanolin, lanolin acetate, lanolin fatty acid isopropyl, hexyl laurate, POE lanolin alcohol ether, POE lanolin alcohol acetate, polyethylene glycol lanolin fatty acid, POE hydrogenated lanolin alcohol ether and egg yolk oil.

[0055] Examples of hydrocarbon oils include ozokerite, squalane, squalene, ceresine, paraffin, paraffin wax, liquid paraffin, pristane, polyisobutylene, microcrystalline wax and vaseline.

[0056] Examples of higher fatty acids include lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, undecylenic acid, oleic acid, linoleic acid, linolenic acid, arachidoniacicid, eicosapentaenoic acid (EPA), docosahexaenoic acid (DHA), isostearic acid and 12-hydroxystearic acid.

[0057] Examples of higher alcohols which can be added include lauryl alcohol, myristyl alcohol, palmityl alcohol, stearyl alcohol, biphenyl alcohol, hexadecyl alcohol, oleyl alcohol, isostearyl alcohol, hexyldodecanol, octyldodecanol, cetostearyl alcohol, 2-decyltetradecinol, cholesterol, phytosterol, POE cholesterol ether, monostearyl glycerin ether (batyl alcohol) and monooleyl glyceryl ether (cerakyl alcohol).

[0058] Examples of ester oils which can be added include diisobutyl adipate, 2-hexyldecyl adipate, di-2-heptylundecyl adipate, N-alkylglycol monoisostearates, isocetyl isostearate, trimethylolpropane triisostearic acid ester, ethylene glycol di-2-ethylhexanoic acid ester, neopentyl glycol di-2-ethylhexanoic acid ester, cetyl 2-ethylhexanoate, trimethylolpropane tri-2-ethylhexanoic acid ester, pentaerythritol tetra-2-ethylhexanoic acid ester, cetyl octanoate, octyldodecyl gum ester, oleyl oleate, octyldodecyl oleate, decyl oleate, neopentyl glycol dicapric acid ester, triethyl citrate, 2-ethylhexyl cinnamate, amyl acetate, ethyl acetate, butyl acetate, isocetyl stearate, butyl stearate, diisopropyl sebacate, di-2-ethylhexyl sebacate, cetyl lactate, myristyl lactate, isopropyl palmitate, 2-ethylhexyl- palmitate,- -2-hexyldecyl palmitate, 2-heptylundecyl palmitate, cholesteryl 12-hydroxystearate, dipentaerythritol fatty acid esters, isopropyl myristate, 2-octyldodecyl myristate, 2-hexyldecyl myristate, myristyl myristate, hexyldecyl dimethyloctanoate, ethyl laurate, hexyl laurate, N-lauroyl-L-glutaminic acid 2-octyldodecyl ester, diisostearyl malic acid, dextrin palmitic acid ester, dextrin stearic acid ester, dextrin 2-ethylhexanoate palmitic acid ester, cane sugar palmitic acid ester, cane sugar stearic acid ester, monobenzylidene sorbitol and dibenzylidene sorbitol.

[0059] Examples of glyceride oils include acetoglyceride, diisooctanoic acid glyceride, triisostearic acid glyceride, triisopalmitic acid glyceride, tri-2-ethylhexanoic acid glyceride, monostearic acid glyceride, di-2-heptylundecanoic acid glyceride and trimyristic acid glyceride.

[0060] As examples of silicone oils which can be added, mention may be made of dimethylpolysiloxane, methylphenylpolysiloxane, methylhydrogenpolysiloxane, octamethylcyclotetrasiloxane, decamethylcyclopentasiloxane, dodecamethylcyclohexasiloxane, tetramethyltetrahydrogencyclotetrasiloxane, higher alkoxy-modified silicones such as stearoxysilicone, higher fatty acid-modified silicones, fluorine-modified silicones, amino-modified silicones, alkyl-modified silicones, higher fatty acid ester-modified silicones, silicone resins and silicone rubbers.

[0061] As examples of fluorine-containing oils, mention may be made of perfluoropolyether, perfluorodecalin and perfluorooctane.

[0062] One, two or more of these oils may be used as necessary. The proportion of these oils in the cosmetic material of this invention may be within a range of 0-90.0 wt %, but it is particularly preferred that the range is 1-90% of weight. If water is used as a component in the composition of the cosmetic material of this invention, the range is 0-99.0% of the weight.

[0063] Although an excellent cosmetic material according to this invention may be obtained only using the above-mentioned components, the following components i, ii, iii and iv can also be added if needed.

[0064] (i) The Following Powders and/or Colorants

[0065] Examples of inorganic powders are titanium dioxide, zirconium oxide, zinc oxide, cerium oxide, magnesium oxide, barium sulfate, calcium sulfate, magnesium sulfate, calcium carbonate, magnesium carbonate, talc, mica, kaolin, sericite, muscovite, synthetic mica, phlogopite, ruby mica, biotite, lithia mica, silicic acid, silicic acid anhydride, aluminium silicate, magnesium silicate, magnesium aluminium silicate, calcium silicate, baium silicate, strontium silicate, metal salts of tangstic acid, hydroxyapatite, vermiculite, haidilite, bentonite, montmorillonite, hectorite, zeolite, ceramic powder, calcium hydrogen phosphate, alumina, aluminium hydroxide, boron nitride and silica.

[0066] Examples of organic powders are polyamide powder, polyester powder, polyethylene powder, polypropylene powder, polystyrene powder, polyurethane powder, benzoguanamine powder, polymethyl benzoguanamine powder, poly tetrafluoroethylene powder, polymethylmethacrylate powder, cellulose powder, silk powder, and nylon powder such as 12 nylon and 6 nylon.

[0067] Other components that may be added are powders such as styrene acrylic acid copolymer, divinylbenzene, styrene copolymer, vinyl resin, urea resin, phenol resin, fluororesin, silicon resin, acrylate resin, melamine resin, epoxy resin, polycarbonate resin, microcrystalline fiber powder, starch, and lauroyl lysine; surfactant metal salt powders (metal soaps) such as zinc stearate, aluminum stearate, calcium stearate, magnesium stearate, zinc myristate, magnesium myristate, cetyl zinc phosphate, calcium cetyl phosphate, sodium cetyl phosphate; colored pigments including inorganic red pigments such as iron oxide, iron hydroxide iron titanate and □-iron oxide, inorganic yellow pigments such as yellow iron oxide and ocher, inorganic black pigments such as black iron oxide and carbon black, inorganic purple pigments such as manganese violet and cobalt violet, inorganic green pigments such as chromium hydroxide, chromium oxide, cobalt oxide and cobalt titanate, inorganic blue pigments such as Berlin blue and ultramarine blue, lake of tar colorants, lake of natural colorants, and composite powders wherein these powders are complexed; pearl pigments such as titanium dioxide-coated mica, bismuth oxychloride, titanium dioxide-coated bismuth oxychloride, titanium dioxide-coated talc, fish scales foil and titanium dioxide-coated, colored mica; metal powder pigments include aluminium powder, copper powder and stainless steel powder; tar colorants such as Red No. 3, Red No. 104, Red No. 106, Red No. 201, Red No. 202, Red No. 204, Red No. 205, Red No. 220, Red No. 226, Red No. 227, Red No. 228, Red No. 230, Red No. 401, Red No. 505, Yellow No. 4, Yellow No. 5, Yellow No. 202, Yellow No. 203, Yellow No. 204, Yellow No. 401, Blue No. 1, Blue No. 2, Blue No. 201, Blue No. 404, Green No. 3, Green No. 201, Green No. 204, Green No. 205, Orange No. 201, Orange No. 203, Orange No. 204, Orange No. 206 and Orange No. 207; and natural colorants such as carminic acid, laccaic acid, carthamin, bradilin and crocin.

[0068] Any other substances may be added if they are normally used in cosmetics regardless of their shape (spherical, acicular, tabular), particle size (smoke particles, fine particles, pigments particles) or particle structure (porous, non-porous).

[0069] These powders can also be complexed together, surface-treated with an oil or silicone represented by the above-mentioned general formula (1), or surface-treated with a fluorine compound.

[0070] (ii) The Following Surfactants

[0071] Saturated or unsaturated fatty acid soaps such as sodium stearate or oleic acid triethanolamine, alkylether carboxylic acid and its salts, carboxylates of condensates of amino acid and fatty acids, amide ether carboxylates, □-sulfo fatty acid ester salts, □-acyl sulfonates, alkylsulfonate salts, alkene sulfonates, sulfonates of fatty acid esters, sulfonates of aliphatic acid amide, alkylsulfonate salts and sulfonates of their formalin condensates, sulfates such as alkyl sulfate esters, secondary higher alcohol sulfuric esters, alkyl and allyl ethereal sulfate esters, sulfuric esters of fatty acid esters, sulfuric esters of aliphatic acid alkyloylamide, Turkey red oil, alkylphosphates, alkenyl phosphates, ether phosphates, alkylarylether phosphates, alkylamide phosphates, N-acylamino acid activators;

[0072] cationic surfactants including amines such as alkylamines, polyamines and amino alcohol fatty acid acid derivatives, alkyl quaternary ammonium salts, aromatic quaternary ammonium salts, pyridium salts, imidazolium salts;

[0073] nonionic surfactants including sorbitan fatty acid esters, glycerin fatty acid esters, polyglycerol fatty acid esters, propylene glycol fatty acid esters, polyethylene glycol fatty acid esters, cane sugar fatty acid ester, polyoxyethylene alkylethers, poly oxypropylene alkylethers, polyoxyethylene alkyl phenyl ethers, polyoxyethylene fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxyethylene sorbitol fatty acid esters, polyoxyethylene glycerin fatty acid esters, polyoxyethylene propylene glycol fatty acid esters, polyoxyethylene castor oil, polyoxyethylene hardening castor oil, polyoxyethylene phytostanol ether, polyoxyethylene phytosterol ether, polyoxyethylene cholestanol ether, polyoxyethylene cholesteryl ether, polyoxyalkylene-modified organopolysiloxane, polyoxyalkylene/alkyl comodified organopolysiloxane, polyoxyelkylene/fluoroalkyl comodified organopolysiloxane, polyoxyalkylene/organo poly siloxane block copolymer, alkanolamide, sugar ether, sugar amide; and ampholytic surfactants such as betaine, aminocarboxylate and imidazolines.

[0074] (iii) Crosslinked Organopolysiloxanes

[0075] In the cosmetic material of this invention, one, two or more crosslinked organopolysiloxanes can be used depending on the purpose.

[0076] The cross-linked organopolysiloxanes suitable for addition to the present cosmetic materials are those which cause swelling when they contain a silicone having a low viscosity of from 0.65-10.0 mm2/sec (25° C.) in a quantity larger than the weight of the cross-linked organopolysiloxanes themselves. And it is preferable that the cross-linked structure of those organopolysiloxanes be formed by the reaction between the hydrogen atoms bonded directly to silicon atoms and a cross-linking agent having at least two vinylic reactive moieties per molecule. In the cross-linking reaction, it is appropriate to use the cross-linking agent containing at least one moiety selected from polyoxyalkylene, alkyl, alkenyl, aryl or fluoroalkyl moieties. The suitable proportion of such cross-linked organopolysiloxanes mixed in the present cosmetic material is from 0.1-30.0 wt %, but preferably from 1.0-10.0 wt %, to the total weight of the cosmetic material.

[0077] (iv) Silicone Resins such as Acryl/Silicone Graft or Block Copolymer, and Silicone Compounds Having a Reticular Structure

[0078] The present cosmetic material can further contain one or more of silicone resins such as acryl-silicone graft or block copolymers and silicone compounds having a reticular structure, if needed.

[0079] In particular, acrylsilicone resins are suitable for the present cosmetic materials. Further, it is desirable that at least one moiety selected from the group consisting of pyrrolidone, long-chain alkyl, polyoxyalkylene and fluoroalkyl moieties be present in such an acrylsilicone resin molecule. Further, it is appropriate for those silicone resins to be reticular silicone compounds. When the silicone resins, such as acryl-silicone graft or block copolymer and silicone compounds having a reticular structure, are mixed in the present cosmetic material, the appropriate proportion of silicone resins is from 0.1-20 wt %, but preferably from 1-10 wt %, to the total weight of the cosmetic material.

[0080] There is no particular limitation on the applications of the cosmetic material of this invention, but suitable examples which can be mentioned are skin care products, hair products, antiperspirants, makeup products and ultra-violet light protection products. In addition, there is no particular limitation on the form of the product, but it may be in the form of a liquid, emulsion, cream, solid, paste, gel, powder, laminate, mousse or spray.

[0081] Hereafter, this invention will be described in more detail by means of specific examples, but it is not to be construed as being limited thereby.

[0082] Unless otherwise specified, “part” means “weight part” and “%” means “wt %.” Viscosities are given at 25° C.

Manufacturing Example 1

[0083] 187 weight parts of an organohydrogen siloxane shown by the following average empirical formula (8), 100 weight parts of isopropyl alcohol and 18.3 weight parts of trimethylol propane monoallyl ether shown by the following general formula (9) were introduced into a reactor, 2 parts of an isopropyl alcohol solution containing 0.5 wt % of chloroplatinic acids was added, and a reaction was performed under reflux of the solvent for 6 hours.

[0084] The reactant was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (10) was thus obtained.

[0085] The reaction product was a light brown, transparent liquid, and its viscosity was 200 mm2/second (25° C.)

Manufacturing Example 2

[0086] 186 weight parts of an organohydrogen siloxane shown by the following average empirical formula (8) used in Example 1, 100 weight parts of isopropyl alcohol and 24.3 weight parts of the compound shown by the general formula (11) were introduced into a reactor, 2 parts of an isopropyl alcohol solution containing 0.5 wt % of chloroplatinic acids was added, and a reaction was performed under reflux of the solvent for 6 hours.

[0087] 100 g of 0.025N hydrochloric acid was added, and a acetone removal reaction was performed under reflux of the solvent for 6 hours.

[0088] The reactant was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (12) was thus obtained.

[0089] The reaction product was a light brown, transparent liquid, and its viscosity was 1200 mm2/second (25° C).

Manufacturing Example 3

[0090] 460 weight parts of an organohydrogen siloxane shown by the following average empirical formula (13), 500 weight parts of isopropyl alcohol and 19.6 weight parts of trimethylol propane ether shown by the general formula (9) were introduced into a reactor, 2 parts of an isopropyl alcohol solution containing 0.5 wt % of chloroplatinic acid was added, and a reaction was performed under reflux of the solvent for 6 hours.

[0091] The reactant was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (14) was thus obtained.

[0092] The reaction product was a light brown, transparent liquid, and its viscosity was 120 mm2/second (25° C.).

Manufacturing Example 4

[0093] 460 weight parts of an organohydrogen siloxane shown by the following average empirical formula (13) used in Example 3, 500 weight parts of isopropyl alcohol and 45 weight parts of trimethylol propane monoallyl ether shown by the following general formula (9) used in Example 2 were introduced into a reactor, 2 parts of an isopropyl alcohol solution containing 0.5 wt % of chloroplatinic acid was added, and a reaction was performed under reflux of the solvent for 6 hours. 100 g of 0.025N hydrochloric acid was added, and a acetone removal reaction was performed under reflux of the solvent for 6 hours.

[0094] The reactant was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (15) was thus obtained.

[0095] The reaction product was a light brown, transparent liquid, and its viscosity was 350 mm2/second (25° C.).

Manufacturing Example 5

[0096] 478 weight parts of an organohydrogen siloxane shown by the following average empirical formula (8) used in Example 1, 300 weight parts of isopropyl alcohol, 16.4 weight parts of a trimethylol propane monoallyl compound ether shown by the general formula (9) used in Example 1, and 301 weight parts of the single terminated vinyl-modified silicone having the following average empirical formula (16) were introduced into a reactor, 2 parts of a 0.5% isopropyl alcohol solution of chloroplatinic acid was added, and a reaction performed under reflux for 6 hours.

[0097] The reaction product was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (17) was thereby obtained.

[0098] The product was a light brown, transparent liquid, and its viscosity 1200 cs (25° C.).

Manufacturing Example 6

[0099] 478 weight parts of an organohydrogen siloxane shown by the following average empirical formula (8) used in Example 1, 300 weight parts of isopropyl alcohol, 86.6 weight parts of the compound represented by the aforesaid general formula (11) used in Example 2, and 151 weight parts of the compound having the aforesaid average empirical formula (16) were introduced into a reactor, 2 parts of a 0.5% isopropyl alcohol solution of chloroplatinic acid was added, and a reaction performed under reflux for 6 hours.

[0100] 100 g 0.025N hydrochloric acid was added, and a de-acetone reaction performed under reflux for 6 hours.

[0101] The reaction product was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (18) was thereby obtained.

[0102] This product was a light brown, transparent liquid, and its viscosity was 11000 cs (25° C.).

Manufactured Example 7

[0103] 272 weight parts of the organohydrogen siloxane represented by the following average empirical formula (19),

[0104] 200 weight parts of isopropyl alcohol, 49 weight parts of the compound having the aforesaid general formula (9) and 301 weight parts of the aforesaid compound having the average empirical formula (16), were introduced into a reactor, 2 parts of a 0.5% isopropyl alcohol solution of chloroplatinic acid was added, and a reaction performed under reflux for 6 hours.

[0105] The reaction product was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (20) was thereby obtained.

[0106] This product was a light brown, transparent liquid, and its viscosity was 750 cs (25° C.).

Manufacturing Example 8

[0107] 272 weight parts of the organohydrogen siloxane represented by the above average empirical formula (20), 500 weight parts of isopropyl alcohol, 17 weight parts of propenyl alcohol and 153 weight parts of a compound having the following empirical formula (21):

[0108] were introduced into a reactor, 2 parts of a 0.5% isopropyl alcohol solution of chloroplatinic acid was added, and a reaction performed under reflux for 6 hours.

[0109] The reaction product was heated under reduced pressure to distil off the solvent, and the organopolysiloxane shown by the following average empirical formula (22) was thereby obtained.

[0110] This product was a light brown, transparent liquid, and its viscosity was 260 cs (25° C.).

EXAMPLES

Example 1

[0111] 10 g of the silicone compound obtained in Manufacturing Example 1 was dissolved in 50 g decamethylcyclopentasiloxane, 40 g of titanium dioxide (TTO—S-2: Ishihara Sangyo Ltd.) was dispersed therein using a bead mill, and a titanium dioxide dispersion (A) was thus obtained.

Example 2

[0112] 8 g of the silicone compound obtained in Manufacturing Example 2 was dissolved in 42 g decamethylcyclopentasiloxane, 50 g of zinc oxide (ZnO350: Osaka Sumitomo Cement Ltd.) was dispersed therein using a bead mill, and a zinc oxide dispersion (B) was thus obtained.

Example 3

[0113] 10 g of the silicone compound obtained in Manufacturing Example 3 was dissolved in 40 g decamethylcyclopentasiloxane, 50 g of zinc oxide (ZnO350: Osaka Sumitomo Cement Ltd.) was dispersed therein using a bead mill, and a zinc oxide dispersion (C) was thus obtained.

Example 4

[0114] 8 g of the silicone compound obtained in Manufacturing Example 4 was dissolved in 52 g decamethylcyclopentasiloxane, 40 g of titanium dioxide (ITO—S-2: Ishihara Sangyo Ltd.) was dispersed therein using a bead mill, and a titanium dioxide dispersion (D) was thus obtained.

Example 5

[0115] 10 g of the silicone compound obtained in Manufacturing Example 5 was dissolved in 50 g decamethylcyclopentasiloxane, 40 g of titanium dioxide (TTO—S-2: Ishihara Sangyo Ltd.) was dispersed therein using a bead mill, and a titanium dioxide dispersion (E) was thus obtained.

Example 6

[0116] 8 g of the silicone compound obtained in Manufacturing Example 6 was dissolved in 42 g decamethylcyclopentasiloxane, 50 g of zinc oxide (ZnO350, Osaka Sumitomo Cement Ltd.) was dispersed therein using a bead mill, and a zinc oxide dispersion (F) was thus obtained.

Example 7

[0117] 10 g of the silicone compound obtained in Manufacturing Example 7 was dissolved in 40 g decamnethylcyclopentasiloxane, 50 g of zinc oxide (ZnO350, Osaka Sumitomo Cement Ltd.) was dispersed therein using a bead mill, and a zinc oxide dispersion (G) was thus obtained.

Example 8

[0118] 8 g of the silicone compound obtained in Manufacturing Example 8 was dissolved in 52 g decamethylcyclopentasiloxane, 40 g of titanium dioxide (TTO—S-2: Ishihara Sangyo Ltd.) was dispersed therein using a bead mill, and a titanium dioxide dispersion (H) was thus obtained.

Comparative Example 1

[0119] 10 g of a polyether-modified silicone compound (KF6017, Shin-Etsu Chemical Industries) was dissolved in 50 g decamethylcyclopentasiloxane, 50 g of zinc oxide (ZnO350: Osaka Sumitomo Cement Ltd.) was dispersed therein using a bead mill, and a zinc oxide dispersion (I) was thus obtained.

Comparative Example 2

[0120] 5 g of methyl hydrogen polysiloxane (KF99, Shin-Etsu Chemical Industries Ltd.) was dissolved in isopropyl alcohol, sprayed into 40 g of titanium dioxide (TTO—S-2: Ishihara Sangyo Ltd.), and then dried at 100° C. The product was added to 60 g of decamethylcyclopentasiloxane, dispersed therein using a bead mill, and a titanium dioxide dispersion (J) was thus obtained.

Example 9

[0121] 5 g of the silicone compound obtained in Manufacturing Example 1 was dissolved in isopropyl alcohol, 40 g of titanium dioxide (TTO—S-1, Ishihara Sangyo Ltd.) was dispersed therein, the solvent was distilled off, and a titanium dioxide composition (K) was thus obtained.

Example 10

[0122] 5 g of the silicone compound obtained in Manufacturing Example 2 was dissolved in isopropyl alcohol, 50 g of zinc oxide (ZnO 350, Osaka Sumitomo Cement Ltd.) was dispersed therein, the solvent was distilled off, and a zinc oxide composition (L) was thus obtained.

Example 11

[0123] 8 g of the silicone compound obtained in Manufacturing Example 3 was dissolved in isopropyl alcohol, 50 g of zinc oxide (ZnO 350, Osaka Sumitomo Cement Ltd.) was dispersed therein, the solvent was distilled off, and a zinc oxide composition (M) was thus obtained.

Example 12

[0124] 10 g of the silicone compound obtained in Manufacturing Example 4 was dissolved in isopropyl alcohol, 40 g of titanium dioxide (TTO—S-1, Ishihara Sangyo Ltd.) was dispersed therein, the solvent was distilled off, and a titanium dioxide composition (N) was thus obtained.

Example 13

[0125] 5 g of the silicone compound obtained in Manufacturing Example 5 was dissolved in isopropyl alcohol, 40 g of titanium dioxide (TTO—S-1, Ishihara Sangyo Ltd.) was dispersed therein, the solvent was distilled off, and a titanium dioxide composition (O) was thus obtained.

Example 14

[0126] 5g of the silicone compound obtained in Manufacturing Example 6 was dissolved in isopropyl alcohol, 50 g of zinc oxide (ZnO350, Osaka Sumitomo Cement Ltd.) was dispersed therein, the solvent was distilled off, and a zinc oxide composition (P) was thus obtained.

Example 15

[0127] 8 g of the silicone compound obtained in Manufacturing Example 7 was dissolved in isopropyl alcohol, 50 g of zinc oxide (ZnO350, Osaka Sumitomo Cement Ltd.) was dispersed therein, the solvent was distilled off, and a zinc oxide composition (Q) was thus obtained.

Example 16

[0128] 10 g of the silicone compound obtained in Manufacturing Example 8 was dissolved in isopropyl alcohol, 40 g of titanium dioxide (TTO—S-1, Ishihara Sangyo Ltd.) was dispersed therein, the solvent was distilled off, and a titanium dioxide composition (R) was thus obtained.

Comparative Example 3

[0129] 10 g of a polyether-modified silicone compound (KF6017, Shin-Etsu Chemical Industries) was dissolved in 50 g isopropyl alcohol, 50 g of titanium dioxide (ZnO350: Osaka Sumitomo Cement Ltd.) was dispersed therein using a bead mill, and the solvent was distilled off to obtain a titanium dioxide dispersion (S).

Comparative Example 4

[0130] 5 g of methyl hydrogen polysiloxane (KF99, Shin-Etsu Chemical Industries Ltd.) was dissolved in isopropyl alcohol, 50 g of titanium dioxide C(TTO—S-2: Ishihara Sangyo Ltd.) was added, and the solvent was distilled off to obtain a titanium dioxide dispersion (T).

[0131] Dispersibility

[0132] The powder compositions and oil-based dispersions in Examples 1 to 16 and Comparative Examples 1 to 4, were mixed with dimethylcyclopentanesiloxane so that the concentration was 5%, the mixed solution was placed in a 50 ml sedimentation tube, and the sedimentation volume was visually observed after two days. The results are shown in the following table.

1Sedimentationvolume (%)Example 10.5Example 20.7Example 30.5Example 40.4Example 50.6Example 60.7Example 70.5Example 80.6Example 90.2Examnle 100.7Example 110.6Example 120.5Example 130.4Example 140.7Example 150.6Example 160.4Comparative Example 16.5Comparative Example 210.2Comparative Example 39.3Comnarative Examule 415.3

[0133] As can be seen from the above table, in the case of Examples 1-16, the mixture was homogenous without sedimentation, and dispersibility was good. However, in the case of Comparative Examples 1-4, the mixture was not homogeneous and sedimented out.

[0134] A sunscreen having the composition in Table 1 or Table 2 below was prepared, and its quality was evaluated. The unit is “part”.

[0135] Preparation of Sunscreen

[0136] Examples 17 to 24, and Comparative Example 5

[0137] A: 1, 2, 3, 4 were mixed uniformly.

[0138] B: 6, 7, 9 were mixed uniformly.

[0139] C: B was added to A, and emulsified.

[0140] D: 5, 10 and any of 11-19 were added to C to obtain a sunscreen.

[0141] Table 1

2TABLE 1Compar.ExamplesExamples171819202122232451KF96 6cs5.05.05.05.05.05.05.05.05.02KSG-215.05.05.05.05.05.05.05.05.03Triisooctanoic acid glyceryl3.03.03.03.03.03.03.03.03.04kF-60171.01.01.01.01.01.01.01.01.05Octylmethoxycinnamic acid6.06.06.06.06.06.06.06.06.06Sodium chloride0.50.50.50.50.50.50.50.50.571,3 butylene glycol2.02.02.02.02.02.02.02.02.08Decamethylcyclopentasloxane————30253030—9Purified water - remainderResidualResidualResidualResidualResidualResidualResidualResidualResidual amountamountamountamountamountamountamountamountamount10.Perfume - suitable amountSuitableSuitableSuitableSuitableSuitableSuitableSuitableSuitableSuitable amountamountamountamountamountamountamountamountamount11.Titanium oxide dispersion(A) (Example 1)5012.Zinc oxide dispersion (B)(Example 2)5013.Zinc oxide dispersion(C) (Example 3)5014.Titanium dioxide dispersion(D) (Example 4)5015.Titanium dioxide composition(E) (Example 5)5016.Zinc oxide composition50(F) (Example 6)17.Zinc oxide composition50(G) (Example 7)18.Titanium dioxide composition50(H) (Example 8)19.Zinc oxide dispersion (1)50 (Compar, Example 1)Test results1.Dispersion stability⊚⊚⊚⊚⊚⊚⊚⊚◯2.Feel in usage smoothness⊚⊚⊚⊚⊚⊚⊚⊚◯spreadability⊚⊚⊚⊚⊚⊚⊚⊚Δtransparency of cosmetic film⊚⊚⊚⊚◯⊚⊚◯Δabsence of tackiness⊚⊚⊚⊚⊚⊚⊚⊚◯sunscreen effect⊚⊚⊚⊚⊚⊚◯◯◯KF.96: dimethylpolysiloxane KSG-21: silicone gel KF-6017: polyether silicone (Shin-Etsu Chemical Co., Ltd.)

[0142] Examples 25 to 32, and Comparative Example 6

[0143] A: 1, 2, 3, 4 were mixed uniformly, and 8, 10 and any of 20-28 were added to obtain a sunscreen.

[0144] B: 6, 7, 9 were mixed uniformly.

[0145] C: B was added to A, and emulsified.

[0146] D: 5 was added to C to obtain a sunscreen.

[0147] The quality of the sunscreens having the compositions in Table 2 were evaluated as follows.

3TABLE 2Compar.ExamplesExamples252627282930313261.KF96 6cs5.05.05.05.05.05.05.05.05.02.KSG-215.05.05.05.05.05.05.05.05.03.Triisoctanoic acid glyceryl3.03.03.03.03.03.03.03.03.04 KF-60173.04.01.01.01.01.01.01.01.05.Octylmethoxycinnamic acid6.06.06.06.06.06.06.06.06.06.Sodium chloride3.50.50.50.50.50.50.50.50.57.1,3 butylene glycol4.05.02.02.02.02.02.02.02.08.Decamethylcyclo-302530303025303025pentasiloxane9.Purified water - remainderResidualResidualResidualResidualResidualResidualResidualResidualResidual amountamountamountamountamountamountamountamountamount10.Perfume - suitable amountSuitableSuitableSuitableSuitableSuitableSuitableSuitableSuitableSuitable amountamountamountamountamountamountamountamountamount20.Titanium dioxide dispersion50(K) (Example 9)21.Zinc oxide dispersion50(L) (Example 10)22.Zinc oxide dispersion50(M) (Example 11)23.Titanium dioxide dispersion50(N) (Example 12)24.Titanium dioxide composition20(O) (Example 13)25.Zinc oxide composition25(P) (Example 14)26.Zinc oxide composition20(Q) (Example 15)27.Titanium dioxide composition20(R) (Example 16)28.Zinc oxide dispersion25(T) (Compar. Example 4)Test result1.Dispersion stability⊚⊚⊚⊚⊚⊚⊚⊚Δ2.Feel in usage smoothness⊚⊚⊚⊚⊚⊚⊚⊚◯spreadability⊚⊚⊚⊚⊚⊚⊚⊚Δtransparency of cosmetic film⊚⊚⊚⊚◯⊚⊚◯Δabsence of tackiness⊚⊚⊚⊚⊚⊚⊚⊚◯sunscreen effect⊚⊚⊚⊚⊚⊚◯◯◯KF-96: dimethylpolysiloxane KSG-21: silicone gel KF-6017: polyether silicone (Shin-Etsu Chemical Co., Ltd.)

[0148] 1. Dispersion Stability of Powder

[0149] After leaving the sunscreen at room temperature for 1 month, the aggregation of the powder was observed and evaluated according to the following criteria.

[0150] Evaluation Criteria

[0151] {circle over (∘)}: Aggregation of powder is not observed

[0152] ◯: Slight aggregation of powder is observed

[0153] Δ: Tendency of powder to aggregate is observed:

[0154] ×: Aggregation of powder is clearly observed

[0155] 2. Performance Evaluation

[0156] 50 female panelists evaluated the sunscreen obtained with regard to smoothness, extendability, transparency of cosmetic film, stickiness on the skin and sunscreen effect, on a 5 point scale. The average points obtained were classed as {circle over (∘)}, ◯, Δ or × according to the following criteria for each example.

[0157] Evaluation Criteria

[0158] 5 points good

[0159] 4 points fairly good

[0160] 3 points normal

[0161] 2 points rather poor

[0162] 1 poin poor

[0163] Evaluation of Average Points:

[0164] Average points obtained 4.5 or more: {circle over (∘)}

[0165] Average points obtained 3.5 to 4.5: ◯

[0166] Average points obtained 2.5 to 3.5: Δ

[0167] Average points obtained 1.5 to 2.5: ×

[0168] As can be seen from the results of the above table, the sunscreens of Examples 17-32 showed no aggregation of the powder and excellent dispersibility. In addition, they all felt pleasant to use. On the other hand, in Comparative Examples 5 and 6 with added polyether silicone, a small amount of aggregation was observed in the powder, the cosmetic film had poor transparency, and it did not feel good enough to use.

Example 33

[0169] Eyeliner

4(Component)(%)1. Decamethylcyclopentasloxane45.02. Polyether-modified siloxane (Note 1) 3.03. Organosilicon resin15.04. Dioctadecyldimethylammmonium-modified 3.0montmorillonite5. Black iron oxide treated with silicone obtained in10.0Manufacturing Example 36. 1,3-butylene glycol 5.07. Sodium dehydroacetateSuitable amount8. AntisepticSuitable amount9. PerfumeSuitable amount10. Purified waterResidual amount(Note 1) Polyether-modifled silicone; KF-6017 (Shin-Etsu Chemical Co., Ltd.) (Manufacturing Method)

[0170] A: Components 1-4 were mixed, and Component 5 was added to give a uniform dispersion.

[0171] B: Components 6-8 and 10 were mixed.

[0172] C: B was gradually added to A, and Component 9 was added to obtain an eyeliner.

[0173] The eyeliner obtained above spread lightly, was easy to draw with, and had a cool, cool freshness without any tackiness. It did not change with temperature or time, was extremely easy to use and very stable, had excellent water resistance and perspiration resistance, and lasted a very long time.

5(Component)(%)1. Decamethyl cyclopentasioxane8.32. Dimethylpolysiloxane (6 mm2/second)5.03. Polyether-modified silicone (Note 1)2.04. Dioctadecyldimethylammmonium-modified4.0montmorillonite5. Powder dispersion (Note 2)61.36. Dipropylene glycol5.07. Para-oxybenzoic acid methyl ester0.38. 2-amino-2-methyl-1,3-propanediol0.29. Hydrochloric acid0.110. PerfumeSuitable amount11. WateResidual amount(Note 1)Polyether-modified silicone: KF-6017 (Shin-Etsu Chemical Co., Ltd.)(Note 2) Titanium dioxide 15%Talc 9%Mica 9%Red ocher2.4%Yellow iron oxide1.0%Black iron oxide0.3%Silicone compound obtained in Manufacturing Example 2 10%Powder dispersion obtained by dispersing53.3% decamethylpentasiloxane by a ball mill.

[0174] (Manufacturing Method)

[0175] A: Components 1-4 were heated and mixed, Component 5 was added and the mixture made homogeneous.

[0176] B: Components 6-9 and 11 were added and dissolved (pH of aqueous system was 9.0)

[0177] C: B was gradually added to A with stirring to make an emulsion, cooled, and Component 10 was added to obtain an emulsion.

[0178] The foundation obtained above had a fine texture, spread lightly, was non-tacky and non-oily, moist, fresh and clean. It lasted well, did not change with temperature or time, and was extremely stable.

Example 35

[0179] Eye Shadow

6(Components)(%)1. Decamethyl cyclopentasiloxane15.02. Dimethylpolysiloxane (6 mm2/second)10.03. Polyether modified silicone (Note 1)2.04. PEG (10) lauryl ether (Note 2)0.55. Chromium oxide treated by silicone compound6.2obtained in Manufacturing Example 36. Permanent blue treated by silicone compound4.0obtained in Manufacturing Example 37. Titanium-coated mica treated by silicone compound6.0obtained in Manufacturing Example 38. Sodium chloride2.09. Propylene glycol8.010. AntisepticSuitable amount11. PerfumeSuitable amount12. Purified waterResidual amount(Note 1) Polyoxyalkylene/alkyl co-modified organopoly sioxane: KF6026 (Shin-Etsu Chemical Co.,Ltd.) (Note 2) PEG (10) means that ten polyethylene glycol units are joined together.

[0180] (Manufacturing Method)

[0181] A: Components 1-4 were mixed, and Components 5-7 were added and uniformly dispersed.

[0182] B: Components 8-10 and 12 were dissolved uniformly.

[0183] C: B was gradually added to A with stirring to form an emulsion, and Component 11 was added to obtain an eye shadow.

[0184] The eye shadow obtained above spread lightly, was not oily or powdery, and had a fresh, non-tackiness. It had excellent water resistance, water repellence and perspiration resistance, lasted well, did not disintegrate when used in cosmetics, did not change with temperature or time and was very stable.

Example 36

[0185] Liquid Emulsion Foundation

7(Components)(%)1. Dimethylpolysiloxane (6 mm2/second)5.02. Mulberry orchid4.03. Dioctanoic acid neopentyl glycol3.04. Myristic acid isosteairic acid diglycerate2.05. α-mono isostearyl glyceryl ether1.06. Polyether-modified silicone (Note 1)1.07. Aluminium distearate0.28. Powder dispersion (Note 2)26.29. Magnesium sulfate0.710. Glycerin3.011. AntisepticSuitable amount12. PerfumeSuitable amount13. Purified waterResidual amount(Note 1)Polyoxyalkylene/alkyl co-modified organopoly siloxane:KF6026 (Shin-Etsu Chemical Co., Ltd.):(Note 2)Powder dispersion obtained by dispersing the followingcomponents in a bead mill(Components)(%)Titanium dioxide20Sericite8Talc12Red ocher1.6Black iron oxide0.4Silicone compound that was obtained in Manufacturing10Example 4Decamethylcyclopentasiloxane48.0

[0186] (Manufacturing Example)

[0187] A: Components 1-7, 10 were heated with mixing, Component 8 was added and blended uniformly.

[0188] B: Components 9 to 11 and 13 were heated and dissolved.

[0189] C: B was gradually added to A with stirring to make an emulsion, cooled, and Component 12 was added to obtain a liquid emulsion foundation.

[0190] The liquid emulsion foundation obtained above had a low viscosity and fine texture, spread lightly, was non-tacky and non-oily, moist, fresh and had a cool freshness. It lasted a long time, did not change with temperature or time, and was extremely stable.

Example 37

[0191] Cream

8(Components)(%)1. Dimethylpolysiloxane (6 mm2/second)6.02. Methylphenylpolyslioxane4.03. Mulberry orchid5.04. Dioctanoic acid neopentyl glycol3.05. Polyether..modified silicone (Note 1)3.06. Hydrophobically-treated fine titanium dioxide2.0(Note 2)7. Magnesium sulfate0.78. Glycerin10.0 9. Antiseptic agentSuitable amount10. PerfumeSuitable amount11. Purified waterResidual amount(Note 1) Polyether-modified silicone: KF6012 (Shin-Etsu Chemical Co., Ltd.) (Note 2) Hydrophobically-treated fine titanium dioxide: Fine titanium dioxide of average particle diameter 0.05 um was dispersed in water to 10%, 10% sodium silicate solution (SiO2/NaO2) mole ratio: 0.5) equivalent to 2% relative to titanium dioxide in terms of SiO2 was added, and the mixture thoroughly stirred. 10% aluminum sulfate solution equivalent to 7.5% relative to titanium dioxide in terms of Al2O3 was gradually added, and # hydrates of silicic acid and alumina were thereby deposited on the surface of the titanium dioxide.

[0192] After the reaction, the mixture was filtered, rinsed and dried, and crushed in a jet mill. This was transferred to a Henschel mixer, 1% of the silicone compound obtained in Manufacturing Example 3 was added with vigorous stirring, and the mixture blended with stirring. Heat treatment was then performed at 120° C.

[0193] (Manufacturing Method)

[0194] A: Components 1-5 were heated and mixed, Component 6 was added and the mixture made homogeneous.

[0195] B: Components 7-9 and 11 were heated and dissolved.

[0196] C: B was gradually added to A with stirring to make an emulsion, cooled, and Component 10 was added to obtain a cream.

[0197] The cream obtained above had a fine texture, spread lightly, was non-tacky and non-oily, moist, fresh and had a cool freshness. It lasted well, did not change with temperature or time, and was extremely stable.

Example 38

[0198] Sunscreen Emulsion

9(Components)(%)1. Decamethylcyclopentasiloxane 20.02. Methylphenylpolysiloxane3.05. Monoisostearic acid sorbitan1.03. Polyether-modified silicone (Note 1)0.55. Trimethylsiloxy silicic acid1.06. Octyl p-methoxycinnamate4.07. Titanium dioxide (J) obtained in Example 88.08. Sorbitol2.09. Sodium chloride2.010. AntisepticSuitable amount11. PerfumeSuitable amount12. Purified waterResidual amount(Note 1) Polyether-modified silicone: KF6015 (Shin-Etsu Chemical Co.,Ltd.)

[0199] (Manufacturing Method)

[0200] A: Components 1-6 were heated and mixed, Component 7 was added and the mixture made homogeneous.

[0201] B: Components 8-10 and 12 were dissolved uniformly.

[0202] C: B was gradually added to A with stirring to make an emulsion, cooled, and Component 11 was added to obtain an emulsion.

[0203] The sunscreen emulsion obtained above had a fine texture, spread lightly, was non-tacky and non-oily, moist and fresh. It lasted well, did not change with temperature or time, and was extremely stable.

Example 39

[0204] Liquid Foundation

10(Components)(%)1. Decamethyl cyclopentasiloxane16.0 2. Dimethylpolysiloxane (6 mm2/second)8.03. Octyl p-methoxycinnamate3.04. 12-hydroxystearic acid1.05. Fluorine-modified silicone (Note 1)15.0 6. Polyether-modified silicone (Note 2)5.07. Spherical silicone resin powder (Note 3)3.08. Fine titanium dioxide treated by silicone compound8.0obtained in Manufacturing Example 19. Mica titanium treated by silicone compound1.0obtained in Manufacturing Example 110. titanium dioxide treated by silicone compound5.0obtained in Manufacturing Example 111. Red ocher treated by silicone compound obtained0.9in Manufacturing Example 112. Yellow iron oxide treated by silicone compound2.0obtained in Manufacturing Example 113. Black iron oxide treated with silicone obtained1.0in Manufacturing Example 114. Ethanol15.0 15. Glycerin3.016. Magnesium sulfate1.017. AntisepticSuitable amount18. PerfumeSuitable amount19. Purified waterResidual amount(Note 1) Fluorine-modified silicone: FL-100 (Shin-Etsu Chemical Co., Ltd.) (Note 2) Polyoxyethylene/trifluoropropyl co-modified silicone (Note 3) Spherical silicone resin powder: KMLP590 (Shin-Etsu Chemical Co., Ltd.)

[0205] (Manufacturing method)

[0206] A: Components 7-13 were mixed uniformly

[0207] B: Components 1-6 were heated to 70° C. with mixing, and A was added and uniformly dispersed.

[0208] C: Components 14-17 and 19 were heated to 40° C., B was gradually added to make an emulsion, cooled, and Component 18 was added to obtain a liquid foundation.

[0209] The foundation obtained above had a fine texture, spread lightly, was non-tacky and non-oily, clean and cool. It did not change with temperature or time, and was extremely stable.

Example 40

[0210] Eyeliner

11(Components)(%)1. Decamethylcyclopentasiloxane22.0 2. Dimethylpolysiloxane (6 mm2/second)5.03. Black iron oxide treated with silicone obtained in20.0Manufacturing Example 44. Vitamin E acetate0.25. Jojoba oil2.06. Bentonite3.07. Polyether-modified silicone (Note 1)2.08. Ethanol10.0 9. 1,3-butylene glycol10.0 10. AntisepticSuitable amount11. PerfumeSuitable amount12. Purified waterResidual amount(Note 1) Polyether-modified silicone: KF6017 (Shin-Etsu Chemical Co., Ltd.)

[0211] (Manufacturing Method)

[0212] A: Components 1-2, 4-7 were mixed, and Component 3 was added to give a uniform dispersion.

[0213] B: Components 8-10 and 12 were mixed.

[0214] C: B was gradually added to A, and Component 11 was added to obtain an eyeliner.

[0215] The eyeliner obtained above spread lightly, was easy to draw with, had a cool feel and was not tacky. It did not change with temperature or time, was extremely easy to use and very stable, had excellent water resistance and perspiration resistance, and lasted a very long time.

Example 41

[0216] Cream

12(Components)(%)1. Decamethyl cyclopentasiloxane16.0 2. Dimethylpolysioxane (6 mm2/second)4.03. Polyether-modified silicone (Note 1)5.04. POE (5) octyldodecyl ether (Note 2)1.05. Monostearic acid polyoxyethylene sorbitan0.5(20E.O.) (Note 3)6. Anhydrous silicic acid-treated zinc oxide (Note 4)2.07. titanium dioxide composition (G) obtained in10.0 Example 58. Liquid paraffin2.09. Macadamia nut oil1.010. Ogon extract (Note 5)1.011. Gentiana extract (Note 6)0.512. EthanolSuitable amount13. 1,3-butylene glycol2.014. AntisepticSuitable amount15. PerfumeSuitable amount16. Purified waterResidual amount(Note 1) Polyether-modified silicone: KF6017 (Shin-Etsu Chemical Co., Ltd.) (Note 2) POE (5) means that five polyoxyethylene units are joined together. (Note 3) 20.E.O. means that twenty ethylene oxides are joined together. (Note 4) Anhydrous silicic acid-treated zinc oxide: silica of particle size 0.01-10 micrometers including 50% zinc oxide (Sansufer SZ-5, Asahi Glass) (Note 5) Ogon extract: extract with 50% 1,3-butylene glycol water (Note 6) Gentiana extract: extract with 20% ethanol water

[0217] (Manufacturing Method)

[0218] A: Components 1, 2, 3, 4 were mixed uniformly.

[0219] B: Components 1-5 were mixed, and A was added.

[0220] C: Components 10-14 and 16 were mixed, and B was added to form an emulsion.

[0221] D: C was cooled, and Component 15 was added to obtain a cream.

[0222] The cream obtained above was not tacky, spread lightly, had excellent skin contact with good cohesion, gave a lustrous finish and lasted very well. It did not change with temperature or time and was very stable.

Example 42

[0223] Foundation

13(Components)(%) 1. Decamethylcyclopentasioxane27.0 2. Methyiphenylpolysioxane3.0 3. Tri-isooctanoic acid glycerol10.0 4. Polyether-modified silicone (Note 1)1.0 5. Monoisostearic acid polyglyceryl3.0 6. Hydrophobically-treated mixed powder (Note 2)18.0 7. Red ocher1.2 8. Yellow iron oxide2.6 9. Black iron oxide0.210. 1,3-butylene glycol7.011. Sodium chloride0.512. AntisepticSuitable amount13. PerfumeSuitable amount14. Purified waterResidual amount(Note 1) Polyoxyalkylene/alkyl co-modified organopoly sioxane: KF6026 (Shin-Etsu Chemical Co.,Ltd.): (Note 2) Hydrophobically-treated mixed powder a. Fine titanium dioxide8.0 (parts)b. Fine zinc oxide4.0c. Talc3.0d. Mica3.0

[0224] (Manufacturing Method)

[0225] A: Components a . . . d were mixed, the silicone compound produced in Manufacturing Example 1 was added to the mixed powder to 1%, and the result was heat-treated.

[0226] B: Components 1-5 were mixed, heated and dissolved, and Components 6-9 were uniformly dispersed.

[0227] C: Components 10-12 and 14 were mixed, and B was added to form an emulsion.

[0228] D: C was cooled, and Component 13 was added to obtain a foundation.

[0229] The cream obtained above was not tacky, spread lightly, had excellent skin contact with good cohesion, gave a lustrous finish and lasted very well. It did not change with temperature or time and was very stable.

Example 43

[0230] Suncut Cream

14(Components)(%) 1. Decamethyl cyclopentasioxane15.0 2. KP545 (Note 1)12.0 3. Triisooctanoic acid glyceryl5.0 4. Octyl p-methoxycinnamate6.0 5. KSG21 (Note 2)5.0 6. Polyether-modifled silicone (Note 3)1.0 7. Zinc oxide composition (I) obtained in Example 720.0 8. Sodium chloride0.5 9. 1,3-butylene glycol2.010. AntisepticSuitable amount11. PerfumeSuitable amount12. Purified waterResidual amount(Note 1) KF-545: (Shin-Etsu Chemical Co.,Ltd.) (Note 2) KSG21: (Shin-Etsu Chemical Co.,Ltd.) (Note 3) Polyoxyalkylene/alkyl co-modified organopolysiloxane: KF6026 (Shin-Etsu Chemical Co.,Ltd.):

[0231] (Manufacturing Method)

[0232] A: Component 2 was added to part of Component 1 and uniformly blended, and Component 7 was added and dispersed by a bead mill.

[0233] B: 3-6 were mixed with the remainder of Component 1, and uniformly blended.

[0234] C: Components 8-10 and 12 were mixed and dissolved.

[0235] D: C was added to B to form an emulsion, and Component 11 was added to obtain a suncut cream.

[0236] The suncut cream obtained above was not tacky, spread lightly, had excellent skin contact with good cohesion, gave a lustrous finish, and lasted very well. It did not change with temperature or time and was very stable.

[0237] Industrial Field of Application

[0238] The powder composition of thee present invention has excellent dispersibility, and is suitable for cosmetics. The cosmetic material of this invention with which the powder composition and oil-based composition of this invention was blended, spread lightly, was not oily but moist and fresh, had a cool feel and lasted well. It did not change with temperature or time, was very stable and was an excellent cosmetic material.

[0239] The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples.

[0240] The entire disclosures of all applications, patents and publications, cited herein and of corresponding Japanese Patent Application No. 2000-220892, filed Jul. 21, 2000, and International Application Serial No. PCT/JP01/06310, filed Jul. 19, 2001 are incorporated by reference herein.

[0241] From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention and, without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.

	Number	Date	Country
Parent	PCT/JP01/06310	Jul 2001	US
Child	10346176	Jan 2003	US

Powder composition, dispersion of this powder composition in oil and cosmetic material containing same

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (1)

Continuation in Parts (1)