The present disclosure relates to a dosing system for particulate matter for an apparatus for the layer-by-layer formation of three-dimensional (3D) objects, and to the operation of such a dosing system within the apparatus. The dosing system may be particularly suitable for powder bed applications that require reliable control of the amount and consistency of powder within the dosing system.
Applications used to make 3D objects from particulate matter, such as laser sintering or high speed sintering, are receiving increased interest as they are moving towards faster throughput times and become industrially viable. In these processes, the object is formed layer-by-layer from successive layers of particulate matter that are spread across a work surface. The work surface comprises a build bed surface. Each layer of particulate matter is fused, or sintered, over defined regions of the build bed surface to form a ‘slice’ of the 3D object. Ensuring a reliable uniformity of the spread layers plays an important role in determining the quality of the finished object. For example, there should be no gaps or variations in density in the particulate layer that affect the integrity or vary the properties of the ‘slice’ that is being formed. It is therefore necessary to control the density and thickness of the powder layer that is being spread, and ensure that the amount of powder provided for the layer is sufficient to cover the entire build bed surface.
One property that defines the density of the layer of particulate matter is its ‘flowability’. Particulate matter such as polymer powder may easily compact if not handled appropriately. This can be a challenge in a powder handling system that is, for example, required to fit into a compact space of a 3D printer, or that requires holding an amount of powder that self-compacts due to its own weight.
The powder in a 3D printer may also be compacted by active devices, such as by being pushed along by an auger screw, or it may settle by simply being allowed to accumulate in areas of the delivery system that form a ‘dead space’ not under the influence of any forces moving the powder along or keeping it flowable.
One approach to keep a powder flowable is to agitate it, for example by applying a stirring device such as a rotational mechanical device. Another approach may be to force a flow of gas through the powder.
More particularly, it is important to prevent the powder from forming clumps before it is dosed to the work surface. In some 3D apparatus, powder may be dosed from below the work surface to the top of the work surface by a powder dosing system comprising a rotational dosing blade axially mounted to the work surface. Powder supplied to a chamber beneath the blade can be swept up onto the work surface by rotating the blade. For this type of delivery design, powder compaction may occur by overfilling a holding chamber, such as the dosing chamber from which the dosing blade doses powder to the work surface, or by simply building up enough powder height in the dosing chamber so that the weight of the powder pile compacts the lower areas of the pile. Furthermore, powder may ‘settle’ over time the longer it is left non-agitated, for example while the printer is not in use. This can lead to clumps of material being dosed to the work surface which leads to a non uniform layer.
Aspects of the invention are set out in the appended independent claims, while particular embodiments of the invention are set out in the appended dependent claims.
The following disclosure provides, in one aspect, a powder dosing system for an apparatus for manufacturing a three-dimensional object from powder, the powder dosing system comprising: a rotating agitator arranged to agitate a supply of delivered powder by rotating through an agitation volume; a recirculation edge adjacent the agitation volume, arranged to allow excess agitated powder to freely flow over the recirculation edge and out of the dosing system, away from the agitation volume; and a dosing blade arranged to dose a dosed volume of powder to a work surface comprising a build bed surface; wherein the dosing blade is arranged to sweep through a swept volume, which is located, in a vertical sense, above the agitation volume and overlaps, in a vertical sense, the agitation volume, such that the dosing blade doses agitated powder to the work surface.
According to a second aspect of the disclosure there is provided a powder dosing system for an apparatus for manufacturing a three-dimensional object from powder, the powder dosing system comprising: a reciprocating or vibrating agitator arranged to agitate a supply of delivered powder in a region of agitation; and a dosing blade arranged to deliver a portion of powder to a work surface comprising a build bed surface; wherein the dosing blade is arranged to sweep through a swept volume, which is located, in a vertical sense, above and adjacent the agitator, such that the dosing blade doses agitated powder to the work surface; and wherein the powder dosing system further comprises a recirculation edge adjacent to the swept diameter, arranged to allow excess agitated powder to freely flow from the region of agitation over the recirculation edge and out of the dosing system.
According to a third aspect of the disclosure there is provided a method of adjusting the recirculation edge height of a powder dosing system according to the first or second aspects of the disclosure, the method comprising the steps of: (a) setting a recirculation edge height; (b) delivering a supply of powder to the swept volume of the dosing blade, while agitating the delivered powder using the agitator, until excess agitated powder flows over the recirculation edge and out of the dosing system; (c) assessing the volume of powder delivered to the swept volume; and (d) if the assessed volume of powder is not within tolerance of a required volume, adjusting the recirculation edge height, and repeating from step (b); or, (e) if the assessed volume is within tolerance of a required volume, setting the height of the edge to the adjusted recirculation edge height.
According to a fourth aspect of the disclosure there is provided a control system for adjusting the recirculation edge height of a powder dosing system according to the first or second aspects of the disclosure, the control system comprising a recirculation edge height controller arranged to receive a required powder level; wherein the recirculation edge height controller is arranged to determine, for the required powder level, a corresponding recirculation edge height, and to control a translational mechanism for adjusting the recirculation edge height to the corresponding recirculation edge height.
According to a fifth aspect of the disclosure there is provided a method of forming a three-dimensional object from powder using a powder dosing system according to the first or second aspects of the disclosure.
Reference is now directed to the drawings, in which:
In the figures, like elements are indicated by like reference numerals throughout.
Embodiments of an improved powder dosing system and its use will now be described with respect to
A powder dosing system is provided for an apparatus for manufacturing a three-dimensional object from powder, the powder dosing system comprising a rotating agitator arranged to agitate a supply of delivered powder by rotating over an agitation volume, a recirculation edge adjacent the region of agitation arranged to allow excess agitated powder to freely flow from the region of agitation over the recirculation edge and out of the dosing system, and a dosing blade arranged to deliver a portion of powder to a work surface comprising a build bed surface. The dosing blade is arranged to sweep through a swept volume, which is located, in a vertical sense, above the region of agitation and overlaps, in a vertical sense, the agitation volume, such that the dosing blade doses agitated powder to the work surface. By allowing the powder to freely flow over the recirculation edge and out of the dosing system, for example into an adjacent chamber, the level of powder in the dosing system is self-regulating irrespective of the amount of powder delivered by the delivery mechanism (for example an auger), as long as the delivery mechanism overdelivers powder into the dosing system and the powder is kept in a free-flowing state.
The expression “overlap in a vertical sense”, as used herein, is intended to not only encompass configurations in which the agitation volume and the swept volume directly overlap, one above the other, so as to have a shared overlapping region (e.g. as shown in
Embodiments will now be described by way of example with respect to
The build bed 16 and the formed object 2 are supported inside a build chamber 10, in which the build bed 16 is supported by a piston 18 which is movable in the vertical direction. The piston lowers the build bed 16 by a layer height each time a layer build is completed. Moveable across the build bed surface 12 are modules supporting powder spreading and processing equipment, in this case comprised within two carriages, or sleds. One sled is a printing sled 32 supporting one or more droplet deposition heads and a radiative lamp (e.g. an infrared lamp), and the other sled is a powder distribution sled 34 comprising a powder spreader, for example a roller. Each sled is moveable on a rail 36 across the build bed surface 12. Further shown is a powder dosing system 40, which doses powder to the work surface 13 so that it can be spread by the powder distribution sled 34 across the build bed surface 12. Once a layer of powder has been spread over the build bed surface 12 by the powder distribution sled 34, the printing sled 32 moves across the layer to deposit radiation absorbent material (RAM) in a carrier fluid, and then the radiative lamp (e.g. infrared lamp) mounted on the printing sled 32 is used to irradiate the powder so as to fuse the areas onto which RAM has been deposited. Next, the piston 18 lowers the build bed 16 by a layer thickness, and the process is repeated until the object is fully built.
The build process for forming an object of high quality requires control over the amount and the properties of the powder dosed by the powder dosing system 40, which will now be described in detail.
The dosing blade 416 extends either side of a dosing blade shaft 412. When the shaft 412 rotates about its axis, as indicated by the uppermost dashed line in
The dosing blade 416 shown in
The agitator 426 located in the agitator chamber agitates the powder that is being delivered by the auger screw 452 from the delivery tube outlet 454. The function of the agitator is to keep the powder in a free-flowing state so that it spreads evenly along the length of the powder chamber (along the y-direction) and across the width of the powder chamber (along the x-direction); in this example this can be achieved purely by gravitational force. If the powder is not kept in a free-flowing state, an amount of powder may start to accumulate to form a mound on the surface of the powder above the delivery tube outlet, leading to a non-uniform powder level and uneven dosing by the dosing blade.
The delivery tube outlet 454 may be located in a different position at the bottom of the agitator chamber; for example it may be located in the centre of the agitator chamber. It may alternatively be located in a side wall of the powder chamber, for example at a point along the length of the agitator chamber, or possibly along the length of the dosing chamber.
In
The relation of the agitator 426 to the dosing blade 416 during use is illustrated further in
Regardless of the exact design of the agitator, it will be appreciated that with the dosing blade passing close by the agitator shaft during use, the rotation of the blade needs to be timed to avoid collision with the agitator. For example, the agitator may rotate 90° or close to 90° out of phase with the dosing blade, so that one of the two extends vertically only when the other is in the horizontal “base” position.
The close proximity of the dosing blade and the agitator in
Specifically, the agitator 426 rotates about the agitator shaft 422 which defines an axis of rotation for the agitator. In some implementations, the dosing blade is arranged to extend to within close proximity of the axis of rotation of the agitator when the dosing blade sweeps through the swept volume. In other words, the radius of agitation substantially overlaps the radius of the swept volume. In this respect, the rotation of the agitator is timed (i.e. synchronised) with respect to the rotation of the dosing blade. Such synchronisation could be by mechanical synchronisation, e.g. using gearing or one or more drive belts, or by means of electronic synchronisation.
It will be seen from the further embodiment illustrated in
With this arrangement of the dosing system 40′ there is no overlap between the swept volume 414 and the agitation volume 424, the height of a non-agitation region S′ of the powder above the agitation volume 424 is higher than the corresponding height of a non-agitation volume S shown in
In addition, significant ‘dead space’ regions 434 of powder are present, which are regions not swept by either the dosing blade 416 or the agitator 426. These regions remain stagnant, and over time the powder in these stagnant regions also settles and densifies. If resulting clumps of powder fall back into the agitator region, they may not be rendered fully flowable again by the agitator. This can lead to clumps of denser powder being delivered to the swept volume 414 and ultimately to the work surface, where the clumps again will cause non-uniform areas in the spread layer over the build bed surface 12, and therefore may cause a faulty object.
Further, the powder profile is affected by the degree of flowability of the powder, which may further compound the non-agitated height S′. This will be explained with respect to
The arrangement of the powder dosing system 40 comprises a powder recirculation edge 428 adjacent the agitator over which powder may fall into a recirculation tube 440. In other words, the powder falling over the recirculation edge 428 leaves the dosing system 40. This avoids the powder chamber 430 becoming overfilled with powder while allowing the delivery mechanism (e.g. the auger screw) to deliver powder at periodic intervals, or continuously, without needing to be actively managed, for example by a powder sensor and feedback system that stops and starts the delivery mechanism in response to the powder level detected. Advantageously, the recirculation edge allows the dosing system to receive an oversupply of powder from the delivery mechanism so that the powder volume in the powder dosing system 40 self-regulates, since excess powder can freely flow over the recirculation edge to leave the dosing system and fall, for example, into an adjacent recirculation chamber. In addition, this means that the delivery mechanism may be run almost continuously and does not have to be stopped for significant periods of time, which can cause stagnation within the delivery mechanism and lead to powder agglomerates being delivered into the powder dosing system from the delivery mechanism. For example, where the delivery mechanism is an auger, the auger may only be stopped during a dosing stroke of the dosing blade 416 during which powder is dosed to the work surface.
The recirculation edge 428 therefore provides for passive regulation of the volume of powder in the powder chamber 430. Reliable regulation of this dosing system arrangement having a recirculation edge 428 may in turn be provided by ensuring that the powder remains in a free-flowing state, so that it can freely flow over the recirculation edge 428 to prevent overfilling the dosing chamber, and to maintain a consistent level of the swept powder volume 414. In this way, the dosing blade 416 may repeatedly dose a consistent volume of powder to the work surface and a repeatable uniform layer of powder may be spread over the build bed surface 12.
With reference to
On the other hand, in
Note that the volume V further depends on the surface profile of the powder. Without agitation, the profile is determined by the avalanche angle of the powder. The avalanche angle is slightly higher than the angle of repose of a powder, which is the slope at which a specific powder naturally rests. Powder slippage occurs if the powder slope is made steeper; this ‘critical’ angle is the avalanche angle. Therefore, when powder falls over the recirculation edge 428, this is due in part to the avalanche angle. The avalanche angle depends on the size and roughness of the powder particles, for example. For a nylon PA12 powder, the avalanche angle may be around 34-38° depending on the temperature and on the powder handling history (such as age, number of recirculation cycles through the printer) of the powder. When the powder is however agitated and becomes freely flowing, the density of the powder also plays an important role. For reduced density, the avalanche angle reduces also, and for a free-flowing material the ‘fluidised’ avalanche angle is near zero. This has been observed near the recirculation edge 428 for the powder dosing system 40. Furthermore, it has been observed that the angle varies non-linearly with distance from the recirculation edge 428, so that above the shaft of the agitator in the vertical direction, the powder forms a small conical pile. It is assumed that this is due to a lower level of flowability of the powder, and slightly increased density, which affects the ‘fluidised’ avalanche angle. For the powder dosing system 40, the range of the degree of fluidisation with distance from the agitation volume is narrow, and the pile formed above the agitator shaft is small.
Meanwhile with regard to the powder dosing system 40′ of
Notably, the height of the recirculation edge 428 of the powder dosing system 40 is comparatively higher than that required for the powder dosing system 40′ due to the high degree of followability that can be achieved near the recirculation edge, leading to a very low fluidised avalanche angle near the recirculation edge.
Note therefore that the vertical overlap between the swept volume 414 and agitation volume 424, in the vertical direction, in combination with a recirculation edge 428 that passively controls the volume of powder along the swept volume, synergistically provide a powder dosing system that may ensure the deposition of a repeatably uniform layer of powder in an apparatus for manufacturing a three-dimensional object from powder.
While the agitator in the above embodiments has been described as a rotating device having protrusions extending in one plane, alternative embodiments, some of which are illustrated in
Alternative arrangements for sweeping the swept volume and the agitation volume may be envisaged; for example, and elliptical rotational motion may be possible to adopt.
A further embodiment shown in
The powder chamber comprises an agitator chamber 420 which is in communication, with respect to the flow of powder, with the dosing chamber 410 via a dosing chamber edge 418. The agitator 426 shown is a rotating agitator of similar design to that of
Therefore, the swept volume 414 and the agitation volume 424 are each arranged adjacent to and at opposing sides of a dosing chamber edge 418, wherein the height of the dosing chamber edge is arranged, in a vertical sense, below the recirculation edge height.
The dosing blade rotation describes a swept volume 414 that determines, based on the powder profile in the dosing chamber, the volume of powder delivered by the dosing blade 416 to the work surface. As with the previous embodiments, the swept volume 414 may be controlled by the height of the recirculation edge 428.
Since, in the embodiment of
As with the previous embodiments, in
In addition to the freedom of design of the agitator that this embodiment allows (potentially enabling a more compact design of the overall apparatus to be achieved), the head of the powder within each chamber is kept small, and therefore prevents the agitated powder from densifying.
According to a further embodiment, a powder dosing system 40 for an apparatus for manufacturing a three-dimensional object from powder comprises a reciprocating or vibrating agitator arranged to agitate a supply of delivered powder in a region of agitation. A dosing blade is arranged to dose a portion of powder to a work surface comprising a build bed surface, and is arranged to sweep through a swept volume. The swept volume is located, in a vertical sense, above and adjacent the reciprocating or vibrating agitator, such that the dosing blade doses agitated powder to the work surface. A recirculation edge adjacent the swept volume is arranged to allow excess agitated powder to freely flow from a region of agitation over the recirculation edge.
This provides for a design in which the rotation of the dosing blade does not have to be timed with respect to the agitator, since the agitator is not a rotating agitator. The region of agitation is the region over which, in the vertical sense, the powder remains in a free-flowing state such that excess agitated powder can fall freely over the recirculation edge and into the recirculation tube. The extent of this region depends on the powder properties and the specific dimensions of the powder chamber, the dosing blade design, and the type and mode of operation of the reciprocating or vibrating agitator.
The use of a reciprocating or vibrating agitator instead of a rotating agitator may be particularly suitable in compact systems where it is not possible to install a powder chamber having an agitation chamber of appreciable depth. Instead, by using a reciprocating or vibrating agitator, the powder chamber depth is primarily defined by the depth of the dosing chamber 430.
In some embodiments, the reciprocating or vibrating agitator may be a mesh agitator. In one implementation,
On other implementations of a reciprocating or vibrating agitator, the mesh may be in the form of parallel wires arranged along the width of the agitator, i.e. along the x-direction. A powder dosing system having a reciprocating or vibrating mesh agitator may be arranged such that powder is delivered to the dosing chamber from below the mesh agitator.
Alternatively, the reciprocating or vibrating agitator may be a predominantly solid plate in cases where powder is delivered to the powder chamber above the agitator. In the case of a reciprocating plate agitator, the plate may comprise parallel raised features along the width (x-direction) of the plate that improve the friction between the plate and the powder.
Similarly to the rotating agitator, the reciprocating or vibrating agitator distributes the powder along the length of the powder chamber and keeps it in a free-flowing state over the region of agitation. Due to the vertical overlap between the region of agitation and the swept volume 414, the recirculation edge maintains a consistent powder volume along the swept volume, since the excess powder overflows over the recirculation edge and out of the dosing system as long as the delivery mechanism overdelivers powder into the dosing system.
In some implementations, the tangent plane of the swept volume of the dosing blade is located in close proximity to the plane of the reciprocating or vibrating agitator. This means that the dosing blade removes substantially all of the agitated volume agitated above the plane surface of the agitator.
Therefore, the vertical overlap between the swept volume 414 and the region of agitation, in the vertical direction, in combination with the recirculation edge 428 that passively controls the volume of powder along the swept volume, synergistically provide a powder dosing system that may ensure the deposition of a repeatably uniform layer of powder in an apparatus for manufacturing a three-dimensional object from powder.
With respect to the above-described embodiments, regardless of the design of the agitator, the dosing blade may be arranged to sweep about a horizontal axis. The rotating agitator may be arranged to rotate about a horizontal axis.
Furthermore, the supply of delivered powder may be continuous or periodic.
As discussed above, the presence of the powder recirculation edge 428 adjacent to the agitator allows powder to flow out of the dosing system and thus prevents the powder chamber from overfilling while allowing the delivery mechanism (e.g. the auger screw) to deliver powder at periodic intervals, or continuously, without needing to be actively managed. The recirculation edge 428 therefore provides for passive regulation of the volume of powder in the powder chamber or the dosing system. In some cases, the powder may be delivered continuously with the auger screw rotating at full duty. In other cases, this may not be necessary, and the auger screw may only be activated periodically, for example only 50% of the time, such as 5 seconds on, 5 seconds off. This may prevent significant heat generation in the powder due to the auger screw. In other systems, the auger may only be stopped during a dosing stroke of the dosing blade to dose powder to the work surface. A near-continuous operation of the auger may reduce or prevent the occurrence of polymer stagnation in the auger, which can lead to powder agglomerates being supplied into the dosing system.
Additionally, the recirculation edge height may be located at a position that lies above the lowest point of the swept volume.
Moreover, as in the embodiment of
In some implementations of the above-described embodiments, the height of the recirculation edge 428 may be adjustable so as to vary the volume of the agitated powder that is dosed to the work surface.
This, for example, provides for an apparatus that can be tuned for the use of different powders. Since different powders are likely to have different flow characteristics, e.g. avalanche angles and ‘fluidised’ avalanche angles, the volume of the powder along the swept volume 414 may have to be adjusted so that a required volume of powder can be delivered to the work surface. Additionally, or instead, the volume of the powder being dosed to the work surface may need to be adjusted.
This may be achieved by making the height of the recirculation edge 428 adjustable. For example, the recirculation edge may be part of a slideable recirculation gate, which is a plate movable with respect to the powder chamber such that the height of the recirculation edge may be altered. This is shown in
In some implementations of the above-described embodiments, the recirculation edge may extend adjacent and parallel to a tangent plane to the swept volume 414. This means that the plane of the recirculation gate 421, or the wall comprising the recirculation edge, is parallel to the tangent plane of the swept volume, and is located as close as possible to the tangent plane of the swept volume, thereby minimising the dead space between the swept volume 414 and the recirculation edge 428 (or the recirculation gate).
The direction of translation of the recirculation edge may extend along a parallel in close proximity to the tangent plane of the swept volume so as to avoid significant regions of dead space of powder.
The slideable recirculation gate 421 may be a metal plate attached to a linear translation motor 429 via a slot in the wall 423, while the motor 429 is attached to wall 423. Such an arrangement would give in-process control of the edge height 428. Alternative implementations of achieving electronic translation of the recirculation gate will be apparent to the skilled person.
Alternatively, a manually adjustable version of a slideable recirculation gate 421 may involve bolting the slideable recirculation gate 421 to the wall 423 of the agitation chamber. The slideable recirculation gate 421 in this case may have vertical slots through which the gate can be bolted to the wall 423. The bolts may be recessed by providing a chamfer on the slot edge so as to avoid the bolts protruding into the agitation chamber. A manually adjustable recirculation edge height may be suitable where the recirculation edge height is only required to be adjusted on build process set-up and not during processing.
Using a motor to electronically adjust the recirculation edge allows for in-process changes of the height of the recirculation edge 428, so as to adjust the dosed powder volume by allowing more powder to accumulate in the swept volume of the dosing blade.
The control over the recirculation edge height may be provided by an edge height controller which may for example be arranged to access conversion values of required powder volume (and/or layer thickness) to a suitable edge height for a specific type of powder. The required powder volume may be provided ad-hoc by the user, or it may be provided as part of a build process sequence for the layer by layer formation of the object. A build process controller may send process information to the edge height controller as necessary to cause the edge height controller to adjust the edge height at specific timings within the build process.
As illustrated, a method for adjusting the recirculation edge height of the powder dosing system comprises the steps of:
At step (c)(ii), the priming process is finished. The build process can then start.
A similar method may be used to find corresponding values for edge height versus layer thickness, and optionally, the powder level of the swept volume. In this way, a look-up table or similar may be provided to the edge height controller to refer to during in-process adjustment of the edge height.
With respect to the step of adjusting the edge height, if the assessed volume of powder is too small, the recirculation edge height is increased, and if the assessed amount of powder is too high, the recirculation edge height is decreased. In practice, a tolerable margin may be defined such that the assessed volume is too small or too large only if it falls outside of the margin of the required volume.
Step (c) for assessing the volume of powder may for example comprise actuating the dosing blade to dose a dosed volume of the agitated powder to the work surface;
In some embodiments, the step of assessing the volume of powder delivered to the swept volume may comprise weighing the delivered volume. Additionally, or alternatively, the step of assessing the volume of powder delivered to the swept volume may comprise sensing the level of powder within the swept volume.
The step of adjusting the recirculation edge height comprises the step of actuating a translational mechanism arranged to adjust the recirculation edge height in response to one of weighing, sensing, or spreading the powder. The translational mechanism may be a linear motor.
Additionally, or alternatively, the powder dosing system of any of the above-described embodiments may comprise a powder level sensor for detecting the powder level within the swept volume, for example so as to monitor the powder level of the swept volume.
Such a powder level sensor 419 is shown in
Alternatively, or additionally, therefore, step (c) may comprise sensing the powder level, for example to assess whether the swept volume requires adjustment, to monitor the powder level during adjustment of the recirculation edge, and/or to create reference data of the powder properties relevant to the build process, for example a look up table of powder level reading against powder volume/layer thickness and edge height. The look up table may be used during the build process to adjust the recirculation edge height for a required layer thickness. Sensing of the powder level may also be done to test for malfunction once reference data of the powder properties has been created, for example where the set height does not result in a sensed powder level that matches closely with an expected powder level according to the reference data.
Additionally, or instead, the powder dosing system may comprise a recirculation edge sensor. With reference to
In some implementations, the recirculation edge sensor may monitor the height of the recirculation edge, for example such that the actual height may be compared to an expected height by the recirculation edge height controller.
In further arrangements, the functions of the powder level sensor and the recirculation edge sensor may be fulfilled by the same sensor.
During a build process of a three-dimensional object, the recirculation edge height may be adjusted in response to an adjustment of the distributed layer thickness.
Accordingly, a method of forming a three-dimensional object from powder using a powder dosing system 40 is provided, wherein, optionally, the recirculation edge height is adjustable by controlling a translational mechanism.
Several implementations of such a method will now be described. In some processes it may be necessary to alter the dosed powder volume during the build because a different thickness of distributed powder layer is required, or to compensate for the denser sintered area of the previously processed layer, as will be explained below.
At the start of a build process, buffer layers are distributed by the distribution sled without forming any object layers. The buffer layers are pre-warmed and help to ensure an even temperature distribution of the build bed surface. Once the buffer layers have been distributed, the first powder layer for the object build is distributed by the distribution sled and processed by operating the printing sled.
The overall buffer layer thickness is typically several microns thick by distributing 100-500 layers, each of the order of 100 nm thick.
In some cases, some build layers or some buffer layers may require a different thickness than other build layers, or some build layers may require a different dosed powder volume than other layers to achieve the same layer thickness. The buffer layers may have a thickness higher than that of the object layers.
Alternatively, different object layer thicknesses may be required, such as during a temporary “sketch” mode where lower resolution in the z-direction (and therefore a thicker layer) may be acceptable to achieve faster build time.
The layer thickness may be changed by lowering the build bed by a distance equal to the required layer thickness. To ensure enough powder is dosed to the work surface, the required volume plus a small excess is dosed to the work surface. For each layer therefore, excess powder is present at the end of the pass of the powder distribution device, and the excess powder is either disposed of or recycled.
Rather than in response to changing layer thickness, the dosed volume may need to be adjusted during the build in response to the cross section sintered in the previous layer. Typically, the sintered areas are much denser than the unsintered areas, for example the density of unsintered powder volume may be around 0.4-0.6 g/cm3 compared to the density of the sintered powder volume of 0.9-1.1 g/cm3. The sintered areas in the processed powder layer therefore typically present sunken areas with respect to the unsintered powder surface, and present a volume that needs to be infilled with powder when a new layer of powder is distributed over the top. Depending on the cross section of sintered powder within the layer the additional volume of powder required to be dosed may be significant, e.g. 1-10% (possibly more).
While it is possible to set a dosed volume sufficient for all cross sections of the build, such that for some of the layers there will be an oversupply of dosed powder that will be lost at the end of the distribution step, in some cases it may be desirable to avoid wasting powder, and this may be achieved by allowing the amount of powder dosed to the work surface to be controlled during the build process, and in some cases layer-by-layer.
In some instances therefore, it is desirable to adjust the dosed powder volume in response to a different layer thickness or in response to the previous printed cross section causing a volume that requires to be filled within the previous layer. This may be achieved by increasing the recirculation edge height.
The recirculation edge height is adjusted for the required dosed powder volume, the powder chamber is filled by the powder delivery mechanism until agitated powder falls over the recirculation edge and out of the dosing system, and the required swept volume is achieved. Once the swept volume is dosed to the work surface from the dosing blade, it is distributed across the build bed surface by the roller.
In some implementations of the method therefore, two or more layers may be distributed on the build bed surface from powder dosed from the swept volume of the dosing blade such that a first layer is formed from a first swept volume and a second layer is formed from a second swept volume, wherein the swept volume is adjusted from a first volume to a second volume by controlling the translational mechanism.
The thickness of the first layer may be the same as the thickness of the second layer, and the second swept volume may be adjusted based on the area covered by the object in the first layer. This means that sintered, denser areas can be infilled with sufficient powder when the next layer is distributed, to ensure that the next layer is of the required thickness.
The operation of the dosing chamber system having an adjustable recirculation edge height that may be adjusted by a motorised translational mechanism may be controlled by a recirculation edge height controller system. The recirculation edge height controller system may be a distinct controller or it may be part of a build process controller.
A control system for adjusting the recirculation edge height of the powder dosing system of the above-described embodiments comprises a recirculation edge height controller arranged to receive an input of a required powder level. The recirculation edge height controller is arranged to determine, for the required powder level, a corresponding recirculation edge height, and to control a translational mechanism for adjusting the recirculation edge height to the corresponding recirculation edge height.
The required powder level may be provided in the form of one of required layer thickness, required powder volume within the swept volume (required swept powder volume), or the actual required swept powder level within the dosing chamber, for example, or a request to increase/decrease the swept powder level by a percentile. In some embodiments, the edge height controller may receive the value for the required recirculation edge height. In other embodiments, the controller may be adapted to calculate, based on data of the sintered cross sections of a previous layer, the powder volume required to be dosed for the next layer. The powder level may be a qualitative or quantitative property—for example it may be a specific quantitative value, or it may be provided as a qualitative “low”, “medium” or “high” level.
An embodiment of a recirculation edge height controller system is illustrated in
Once the recirculation edge height has been adjusted to the corresponding recirculation edge height, the recirculation edge height controller 56 may send a signal to the build process controller 60 that the edge height has been adjusted.
The build process controller may then send a signal to the dosing blade controller 58 to actuate the dosing blade, whereupon the dosing blade doses the powder volume within the swept volume to the work surface, and the dosed volume of powder can be assessed. Assessment of the dosed powder volume may be done for example by the build process controller sending a signal to the sled system controller controlling the motion and functions of the sleds, whereupon the sled system controller causes the distribution sled to pass over the build bed surface to distribute the dosed powder over the build bed surface, and the thickness and uniformity of the distributed layer may be assessed.
The recirculation edge height controller may determine the required edge height from data, for example data in the form or a look up table or graph, correlating values of required layer thickness and/or required swept powder volume against corresponding edge height. This data may for example be provided by the method described for
The data may be in the form of a graph of layer thickness (or swept volume) versus edge height, extrapolating between measured values.
Additionally, the required thickness may be provided with a tolerance margin, such that the actual thickness to be achieved falls within an acceptable range of thicknesses.
The edge height controller system 54 may comprise one or more sensors. Specifically, the control system may comprise a powder level sensor arranged to detect a powder level of the swept volume. The edge height controller is arranged to receive the detected swept powder volume level, to determine a required swept powder volume level corresponding to the required powder level, and to determine whether the detected swept powder volume level is different from the required swept powder volume level. If the detected swept powder volume level is different from the required swept powder volume level, the edge height controller is further arranged to determine an adjustment to be made to the recirculation edge height to achieve the required swept powder volume level, and to control the translational mechanism to perform said adjustment.
Powder level sensor 419 may be located in the dosing chamber 410 so as to detect the swept powder volume level.
Alternatively, the controller may receive a required layer thickness instead of a required swept powder volume level, wherein the edge height controller is further arranged to determine a corresponding swept powder volume level in order to compare it to the detected swept powder volume level.
The amount of excess powder delivered in the overflow can also be detected, as a way of verifying that the apparatus is working normally and the dosing system is not being deprived of powder. Implementations of the powder dosing system may comprise a recirculation edge sensor arranged to detect excess agitated powder falling over the recirculation edge, and/or to detect the height of the recirculation edge.
During a priming process, the edge height controller may interrogate sensor 419 to assess the swept powder volume level in the dosing chamber, and compare it to the required swept powder volume level. In this case, the edge height controller determines from the required layer thickness the corresponding required swept powder volume level to compare against the detected swept powder volume level. If the required swept powder volume level is not the same as the detected swept powder volume level, within a margin of tolerance, the priming process of the powder chamber is not complete. Once the required swept powder volume level is the same as the detected swept powder volume level, within a margin of tolerance, the priming process of the powder chamber is complete and the edge height controller may send to the build process controller 60 a signal that the required swept powder volume level has been reached, and the build process controller can begin, or resume, a test or build procedure.
In some implementations, the control system may further comprise a recirculation edge sensor arranged to detect excess agitated powder falling over the recirculation edge, and/or to detect the height of the recirculation edge.
In the implementation of
During a priming process, the priming of the powder chamber may be complete once the edge height controller determines from the recirculation edge sensor 436 that powder is falling over the recirculation edge and out of the dosing system. The output of powder level sensor 419 may be used in addition to determine by the edge height controller 56 that the priming process is complete, or it may be used by the edge height controller 56 to test, once the recirculation edge sensor 436 senses powder falling over the edge, whether the detected swept powder volume level corresponds to an expected swept powder volume level based on data available to the edge height controller. If the detected swept powder volume level does not correspond to the swept powder volume level expected based on the recirculation edge height, despite the recirculation edge sensor signalling that priming is complete, the edge height controller may signal malfunction to the build process controller 60.
Alternatively, if a test procedure is used for determining a corresponding edge height corresponding to a required layer thickness, according to the steps illustrated in
The recirculation edge sensor 436 may further be used to detect the height of the recirculation edge, so that the edge height controller 56 may compare the set edge height value against the detected height value to assess whether a malfunction of the recirculation edge, for example of the translational mechanism, has occurred.
In some implementations of the control system, the edge height controller may be arranged to
In some implementations, the recirculation edge height controller is arranged to determine the corresponding recirculation edge height corresponding to the required swept powder volume level from stored data.
Alternatively, or additionally, the corresponding swept powder volume level may be determined based on the surface profile of the swept powder volume.
The data may be stored in the form of a look-up table or graph in memory comprised within the edge height controller, within the edge height controller system, or within the build process controller.
In the above examples it is clear that the swept powder volume is intended to be the same as, or closely corresponding to, the dosed powder volume. The swept powder volume becomes the dosed powder volume once it is delivered to the work surface. Depending on the design, it is possible that a small portion of the swept powder volume is not delivered to the work surface, i.e. the dosed volume is slightly smaller than the swept volume.
References to powder level are intended to refer to the height of the swept powder volume within the dosing chamber. The sensor therefore detects the height of the powder volume within the chamber.
When referring to a swept volume or to an agitation volume, these are intended to represent the three-dimensional spaces directly occupied by rotational devices such as the dosing blade and the rotational agitator during their operation. The volumes may be cylindrical, or they may take different shapes depending on the mode of rotation, eccentricity of axis, and the design of the protrusions of the agitator and the dosing blade.
The profile of the powder in the powder chamber may correspond to the profile shown in the Figures more strongly near and/or above the powder delivery outlet, and be less pronounced further away along the powder chamber from the powder delivery outlet. Nonetheless, even a reduced region that spans a portion of the length of the powder chamber but that is subject to powder settling and densifying will compromise the quality of the layer spread on the work surface, and therefore the quality of the object. While the specific powder profile is dependent on the type of powder, environmental conditions, and the design of the powder dosing system, the above embodiments apply similarly to different powder profiles.
It should be noted that, in a conventional dosing system in which the amount of powder on the dosing blade is regulated by allowing excess powder to flow down the dosing blade according to the avalanche angle and back into the dosing chamber, the powder volume in the dosing chamber is required to be adjusted by stop-starting the auger to regulate the amount of powder in the dosing system. If the auger runs a little lean, the powder volume in the dosing chamber recedes and the dosing blade starts to deliver a reduced amount of powder. This can eventually lead to non-uniform and/or incomplete distribution of one or more powder layers, which in turn leads to failure of the manufactured object.
Advantageously, though, the presence of the recirculation edge in the above embodiments and their various implementations allows the dosing systems 40 to receive a continuous oversupply of powder from the delivery mechanism so that the powder volume in the dosing system self-regulates, since excess powder can freely flow over the recirculation edge and out of the dosing system, to fall for example into an adjacent recirculation chamber. Thus, without any change in process parameters, in-process measuring and adjusting of powder level in the dosing system is not necessary to prevent powder starvation or overfilling of the dosing system, for example due to running the auger only intermittently or at an incorrect speed.
The self-regulating powder volume of the dosing system 40 may have additional effects depending on the powder handling system of the apparatus 1. This will now be described with reference to
(a) In a system where the recirculation edge 428 is adjacent a recirculation tube 440, the powder falling into the recirculation tube 440 may be directly fed back into the auger tube 450 by connecting the recirculation tube at a recirculation tube entry location 490. The virgin powder enters the recirculation pipe 440 at a location 540 upstream from location 490 with respect from a virgin tank 500, via pipe 510. The recirculated powder thus enters the auger with priority over the virgin powder, keeping the recirculated powder in a free flowing state and continuously mixing it with virgin powder from the auger. Such as system reuses the recirculated powder, thus reducing waste powder and the costs of manufacturing the object.
(b) In an apparatus that additionally also returns excess powder at the end of a powder distribution stroke across the build bed surface 12 into a return slot 610 at the far side of the build bed surface, the returned powder may enter the delivery pipe 450 at a location 630 upstream from recirculation entry location 490, via pipe 620. The powder is thus prioritised to enter the delivery pipe 450 with prioritisation over powder from the recirculation pipe 440. By ensuring that the volume of powder in the recirculation loop is significantly higher than the volume supplied to the auger from the return loop, for example ten times higher, a high quality of powder uniformity can be ensured by mixing small amounts of return powder with large amounts of recirculated powder. The returned powder will have experienced a temperature cycle higher than the recirculated powder by being passed over the hot build bed surface 12. The recirculated powder will only have experienced moderate temperatures in the auger tube 450 and dosing system 40 (eg for PA11 powder this may be around 140° C.), and thus it may be preferable to mix a significantly larger amount of recirculated high quality powder with a comparatively smaller amount of compromised quality return powder.
Number | Date | Country | Kind |
---|---|---|---|
1819681.6 | Dec 2018 | GB | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/GB2019/053413 | 12/3/2019 | WO | 00 |