Patent Application
20070095738
The present invention relates to a fluid filter manufactured using powdered metal sintering, and a method of manufacture thereof.
Fluid filters which separate particulates from a fluid are well known in a wide variety of industries. Traditionally, fluid filters include a polymeric substrate including a plurality of openings. When the fluid passes through the fluid filter, particulates larger than the openings are trapped by the substrate, while the fluid and particulates smaller than the openings pass therethrough. In some fluids, there are ferromagnetic particulates which may be smaller than the openings within a given polymeric substrate, and which therefore will not be trapped as the fluid passes through the filter.
The present invention provides a fluid filter comprising a magnetic substrate configured to allow passage of fluid therethrough, with the substrate manufactured from sintered powdered metal. Preferably, the filter has a porosity of at least 10%, and a magnetic flux density of at least 5 gauss. The substrate may include iron, aluminum, barium, cerium, cobalt, chromium, molybdenum, nickel, oxygen, praseodymium, platinum, samarium, and/or strontium.
The present invention also provides a method of manufacturing a fluid filter by sintering powdered metal to form a magnetic substrate configured to allow passage of fluid therethrough. The method may further include shaping the magnetic substrate for use within a desired application.
The above features and advantages and other features and advantages of the present invention are readily apparent from the following detailed description of the best modes for carrying out the invention when taken in connection with the accompanying drawing.
Referring to
When the fluid passes through the magnetic fluid filter 10, non-ferromagnetic particulates larger than the openings in the substrate 12 contained within the fluid are trapped outside the substrate 12, while the fluid and non-ferromagnetic particulates smaller than the openings pass into the substrate 12 through one or more openings 14. Since the substrate 12 has a magnetic flux, as the liquid travels through the substrate 12, ferromagnetic particulates within the fluid will be attracted to the substrate 12, and consequently separated from the liquid. Any ferromagnetic particulates which are attracted by a material having the magnetic flux density of the substrate 12 will thus attach to the substrate 12 within the openings 14. Thus, the openings 14 must be small enough to restrict entry of non-ferromagnetic particulates as desired (i.e. act as a traditional polymeric filter), but also large enough to allow the fluid to pass therethrough without being impeded by the ferromagnetic particulates throughout the required usage life of the magnetic fluid filter 10. The magnetic fluid filter 10 may be reverse flushable for reuse if desired.
One skilled in the art will recognize that powdered metal having magnetic properties can include one or more of the following: iron, aluminum, barium, cerium, cobalt, chromium, molybdenum, nickel, oxygen, praseodymium, platinum, samarium, and strontium. Additionally, it should be recognized that forming the substrate 12 from sintered powder metal imparts improved stability to the substrate 12 as compared to a similarly sized polymeric substrate. Specifically, the substrate 12 according to the present invention has improved structural stability, especially when the substrate 12 is subjected to pressure spikes or fluctuating stresses; improved chemical stability, with the substrate 12 better able to resist degradation from the fluid passing therethrough; and improved thermal stability, with the magnetic fluid filter 10 operative at temperatures at least as high as 400° C.
It should be noted that
The present invention further provides a method of manufacturing a magnetic fluid filter 10 comprising the step of sintering powdered metal to form a magnetic substrate 12 configured to allow passage of fluid therethrough. The method may further include the step of shaping the magnetic substrate 12 for use within a desired application.
While the best mode for carrying out the invention has been described in detail, it is to be understood that the terminology used is intended to be in the nature of words and description rather than of limitation. Those familiar with the art to which this invention relates will recognize that many modifications of the present invention are possible in light of the above teachings. It is, therefore, to be understood that within the scope of the appended claims, the invention may be practiced in a substantially equivalent way other than as specifically described herein.