Patent Application
20150011355
The present invention relates to variators of rolling traction type having component parts made using powdered metallurgy. In particular, the invention relates to powder metal variator components with a morphology that resists spalling and related component failure.
A “variator” is a device for transmitting rotary drive at a continuously variable ratio. Variators are used for example in continuously and infinitely variable transmissions for vehicles.
In a rolling traction type variator, drive is transmitted between rotating parts by virtue of traction at a rolling contact between them, and movement of one or more of the rotating parts provides for change in the variator drive ratio. The variator typically includes a first rotating part—a race—upon which runs a second rolling part—a roller.
The rollers and races can take various forms. Some rolling traction variators have conical races, movable along their axial direction to change ratio, with a wheel between them to transmit drive from one to the other. Another example uses spherical rollers rotatably mounted upon respective shafts. An example of this type is provided in U.S. patent application Ser. No. 10/141,652, published under US2002/0170799 and filed in the name of Donald C Miller.
A well known variator is the toroidal race type which comprises at least one pair of semi-toroidally recessed variator races mounted for rotation about a common axis and defining between themselves a generally toroidal cavity. The construction and operation of such variators is described in patents and patent applications held by Torotrak (Development) Ltd and others, including for example Torotrak's International Patent Application PCT/EP2006/)50860, published under no. WO2006/084905, the content of which is incorporated by reference.
In most cases rolling parts must be biased toward one another to provide traction. An important quantity in this regard is the traction coefficient μ, defined in the conventional manner as traction force divided by contact normal force, where the traction force is the force transmitted at the rolling contact and the contact normal force is the force with which the rolling parts are biased together, measured normal to the contact surfaces.
The rollers and races may be in direct mechanical contact, with drive being transmitted from one to the other through friction at the contact. Other rollers and races may be separated by a thin film of fluid (“variator fluid”). The variator fluid is typically jetted onto the rolling parts, and thus drawn into the region between them.
In a toroidal type variator, the contact normal force is typically provided by biasing one of the variator races toward the other. The force applied to the variator race (which determines the contact normal force but is not equal to it, since it is shared over multiple variator rollers and is not in general precisely parallel to the contact normal) is referred to as the “end load”. Some sophisticated variators use a hydraulic actuator to provide an end load which varies with the torque being handled by the variator. Some simple variators use a spring to provide a substantially constant end load. PCT/EP2006/050860, referred to above, provides an example of the latter.
There is a limit to the traction coefficient that can be sustained. If the required traction force becomes excessive in relation to the contact normal force, the result is an unacceptable degree of slippage at the rolling contact, which can result in damage to the variator. The limiting coefficient of traction—at which slippage becomes unacceptable—may depend upon several factors including, for example, the nature of the surfaces of the rolling parts and the elastohydrodynamic properties of the variator fluid, where present. A high value of the limiting coefficient of traction is desirable because it allows for a reduction in the end load. High end loads can reduce the variator's efficiency and reduce the effective life of the component parts especially the races and rollers.
The variator's rollers and races can cyclically suffer high Hertzian contact pressure. Also significant heat can be dissipated, creating potentially high temperatures. There may also be large tangential shear forces at their surface. These factors can lead to failure of the rollers and races, as explained in a paper entitled “Developing the Durability of a Dual-Cavity Full-Toroidal IVT Variator” (Adrian Lee, Jonathan Paul Newall: Torotrak (Development) Ltd, Yoshihiro Ono, Teruo Hoshino Koyo Seiko Co Ltd, SAE 2002 World Congress & Exhibition, March 2002, Detroit: Session: “Transmission and Driveline Systems Symposium (Part A)—IVT/CVT; Document Number 2002-01-0587, Book Number SP-1655). (Referred to as “Durability Paper”).
The Durability Paper describes a prior study of the factors affecting the fatigue life of the variator rollers and races. The rolling parts tested were wrought bearing steel with surfaces that were either ground or lapped. The paper explains that some of these parts underwent rolling contact fatigue, exhibited in two failure modes:
1. surface distress—“failure of rolling elements by the formation of glazed areas, followed by asperity scale microcracks which lead to asperity scale micro-spall craters”; and
2. spalling—“failure by the formation of macroscopic craters in the contact surface as a result of fatigue crack propagation in the Hertzian stress field” (the words in quotation marks are taken directly from the paper).
Both rendered the components unfit. The irregular running surfaces caused by surface distress were observed to lead to unacceptable vibration in the variator. In the trials described in the paper, testing was terminated at that point, but other trials have demonstrated that a bearing steel component which continues to be used after the onset of surface distress will suffer spalling.
Where surface distress did not occur (i.e., where the components functioned correctly, without failure) wear rate of the rolling surfaces of the rollers and races was so low as to make its assessment by the conventional method—measurement of weight loss—impractical. This of course is the result of the separation of the surfaces by the fluid film. A related observation (not detailed in the paper but demonstrated in other trials) is that variator rollers and races which have completed their design lifetime and even been tested to the point of destruction have often undergone so little wear as to retain upon their running surfaces the slight machining marks left by turning or grinding during their manufacture.
The study involved components with relatively rough running surfaces (0.13<Ra<0.23) and smoother components (Ra<0.1). The surface distress failure mode was observed only in the relatively rough components, whose lifetime was also shorter than the smoother parts. The Durability Paper implies that running surfaces need to be sufficiently smooth to prevent surface distress.
Variator's rolling parts are typically made as smooth as commercially possible to resist surface distress. The Durability Paper contained proposed alloys and surface treatments intended to provide compressive residual stress at the roller surface, to resist surface initiated cracking.
On the other hand,
Running surface properties, such as roughness, have a bearing on variator performance including the peak or limiting traction coefficient. While factors, such as choice of variator fluid can influence the limiting traction coefficient, it is believed that a suitable degree of roughness can assist in providing traction. However, increased roughness when using the conventional wrought steel parts appears to lead to premature fatigue failure.
International patent application PCT/NL00/00418, published under no. WO 00/77268 in the name of SKF Engineering and Research Centre B.V (“SKF”) discloses high alloy steel variator discs and/or rollers formed using then existing powder metallurgy manufacturing methods.
SKF states that “any method known in the art” may be used and identifies hot isostatic pressing followed by hot forging as a method of making the powdered metal. Hot isostatic pressing was a well known technique for forming high quality steel, involving the application of heat and high pressures to metal particles in a closed capsule, to create a very dense ingot without many internal voids.
The SKF surfaces are to be treated to achieve “a very high hardness”, by austenising and then quenching. The resulting component is said to have a very high surface hardness. For instance, the surface hardness was measured at 67 HRc. Somewhat similar content is found in SKF's International patent application PCT/NL00/00417, published under WO 00/79151.
The present invention involves powder metal variator components including races, rollers and other variator parts that differ from SKF. It is believed that such powder metal components are sufficiently durable for use in variators. Moreover, these parts can be effective when used with ordinary mineral based variator fluids.
By way of example only, embodiments of the present invention are described in the DETAILED DESCRIPTION OF THE DRAWINGS.
The variator described below and the variator components tested and described below serve by way of example only. This application is not limited to toroidal race type variators, but extends to other variators. Nor is this application limited to rollers and races. Other transmission components, such as the epicyclic gearing may be made of powder metal.
The variator 10 has a pair of variator races 12, 14 mounted for rotation about a common axis defined by a shaft 16. Both races are semi-toroidally recessed as seen at 18 and 20 so that together they define a generally toroidal cavity 21 containing a set of rollers 22. Each roller 22 is mounted for rotation about its own axis 24 and each runs upon the recessed faces 18, 20 of both variator races 12, 14 to transfer drive between them.
Variator race 12 is coupled to the shaft 16 through splines, so that it rotates along with the shaft, and is driven by a rotary power source such as an engine E which is itself operatively coupled to the shaft. Variator race 14 is mounted on a bearing 26 co-axial with the shaft 16 and so is able to rotate independently of it, and is coupled to downstream gearing.
In the case of a motor vehicle transmission, this gearing is typically of epicyclic type and leads to the driven vehicle wheels. Suitable epicyclic gear arrangements are well known in the art. PCT/EP2006/050860 provides one example and is incorporated by reference. The splined mounting of variator race 12 allows it to move somewhat along the shaft, and a spring 27, formed in this embodiment as a Belleville washer, urges that race toward its fellow to provide the end load. The mountings of the rollers allow them to undergo a tilting motion to change the angle between the roller axis 24 and the shaft 16, changing the variator ratio in a manner very well known in the art.
Variator rollers and races were produced according to the following process by Hawk Precision Components, which is presented by way of example and not limitation. Powdered metal was placed into compaction tooling generally conforming to the component's shape. The powder in the compaction tooling is then subject to high velocity compaction to create a green compacted component. The Part is then sintered and subject to further processing by High Velocity re-strike. The parts are then heat treated and machined. Textured tooling created the surface used to form the races.
The tested rollers and discs comprised low alloy steel formed using powder metallurgy with one set having 0.3% carbon chromium (C—Cr) steel and another having 0.6% C—Cr steel. The roller contact surfaces were machined to shape while the discs' contact surfaces were not machined. The rollers and discs had a density of between 7.1-7.6 grams (g)/cubic centimeter (cc). The parts had a hardness between 54 and 62 HRc.
The resulting variator component morphology includes internal spaces, voids or cavities. It is believed that this morphology helps render the powdered metal variator components acceptable for use in variators.
These figures disclose random voids within the microstructure. This non-homogeneous random microstructure does not appear to degrade as discovered in similar wrought or forged materials. The randomly distributed voids, asperity peaks and valleys in the powdered metallurgy morphology appear to provide improved traction while still providing a durability not believe obtainable in dense wrought and forged materials.
The powder metal races/discs and rollers were tested for peak traction coefficient, roughness, hardness and durability under the various conditions described below. The races/discs and rollers were tested using prototype variators and a test rig capable of running variator components under adjustable speed and load conditions. The test rig is described in International patent application PCT/GB00/03904, published under W001/27609 by Torotrak, which application is incorporated by reference.
Measurements were made of traction data for the test parts using the test rig. The trials were carried out using (a) conventional wrought steel rollers and races, formed of an alloy referred to as “Ovako 825” and having a high surface finish with roughness Ra of nominally 0.02 micrometres; (b) powder metal rollers and races formed of a steel alloy having 0.3% C—Cr steel, roller roughness Ra=1.02 micrometres and race roughness Ra=0.58 micrometres; and (c) powder metal rollers formed of a steel alloy having 0.6% C—Cr steel, a roller roughness Ra=1.53 micrometres and race roughness 1.12 micrometres. The trial was carried out using both high performance fraction fluid and an automotive automatic transmission fluid (ATF). Results were as follows.
The first chart shows that all the components had an acceptable traction coefficient using the synthetic traction/variator fluid. The powdered metal parts had greater tractions coefficients than the bearing steel parts where the 0.6% C—Cr steel parts performed best overall.
The second chart shows that the bearing steel parts had a lower traction coefficient when used in conjunction with the ATF. The powdered metal test parts had acceptable traction. Some of the 0.3% C—Cr steel parts were found to suffer from deleterious surface distress and consequent failure. Subsequent traction trials have used 0.6% C—Cr steel.
Test parts were also measured for roughness before and after product life tests that were conducted on the test rig using blended traction fluids. All test parts successfully completed a product life test of at least 500 hours.
The following surface properties were measured, using a Form Talysurf with micro-roughness filter with 2.5 micron cut-off and a 2CR-ISO filter with 0.08 mm cut-off:
(1) roughness average (Ra), a conventional measure of surface roughness, defined to be the arithmetic average of the absolute values of the roughness profile ordinates;
(2) root mean square roughness (Rq), obtained numerically from Ra;
(3) skewness (Rsk);
(4) reduced peak height (Rpk), the peak height measured after running in has removed the highest peaks;
(5) kernel roughness depth (Rk);
(6) trough depth (Rvk);
(7) material ratio (MR1) corresponding to the upper limit of the roughness core (Rpk);
(8) material ratio (MR2) corresponding to the lower limit of the roughness core.
The tables set forth below list the various roughness measurements of the tested races/discs and rollers before testing (TABLES 1 and 2) and at the estimated end of product life (500 hours of continuous operation) (TABLES 3 and 4). The tables do not limit the invention. The tables provide only an example of component performance. Other embodiments of the invention may show different properties.
The surface roughness profile of a new variator roller is illustrated in
The tested races/discs and rollers had a roughness higher than conventional bearing steel races/discs and rollers both initially and at the end of the 500 hour life test. The surface roughness of the powder metal components is believed to be partly responsible for the improved traction.
The following factors can affect the surface roughness after use:
a. relative hardness of the disc/races and the rollers
b. density of the materials of these components
c. initial surface texture/roughness
d. porosity of the components.
It appears density should be sufficiently high to provide mechanical strength, thermal conductivity (to allow heat to be dissipated form the rolling contact), and high cycle spalling fatigue. Present results suggest that the rollers should preferably be no harder than those of the disc races. Acceptable test results have been achieved using variator races with hardness in the range of 56 to 61 HRc and rollers with hardness in the range of 54 to 60 HRc. Acceptable test results have also been achieved using roller material density between 7.0 and 7.6 g/cc, and it appears that density of 7.5 g/cc or better is favored.
The effects of a given degree of roughness may depend in some degree upon the thickness of the fluid film separating the rollers form the races. Film thickness is not constant, being dependent upon factors such as fluid temperature, end load, rolling speed, but knowing the expected operating envelope of the variator it is possible to make an estimate of the minimum film thickness expected during normal operation. Also the roughnesses of both components—roller and race—are relevant to performance.
We define the “composite roughness” of the parts as follows:
√{square root over (Rq(race)2+Rq(roller)2)}{square root over (Rq(race)2+Rq(roller)2)}
where Rq(race) is the root mean square roughness of the race and Rq(roller) is the corresponding value for the roller. Then we define the specific film thickness as the minimum film thickness divided by the composite roughness. Specific film thickness gives an indication of whether the components make physical contact with each other. Conventional wrought steel variator components are typically run at a specific film thickness of 1.5 or more, so that little or no contact takes place between surface asperities on the rolling parts. However, performing the same calculation for the test parts shows that specific film thickness is 1.0 or less, implying that surface asperities do make physical contact.
Rates of wear for various powder metal variator rollers, measured at intervals during testing, are shown in the
One group of test results seen in this graph showed excessively rapid wear, resulting from inadequate powder metal density. The other group, representative of suitable powder metal components, showed a wear rate which was acceptable in terms of the design life of the parts. However, the wear rate was greater than conventional wrought steel parts.
Volume of material removed by wear can be calculated using V=κWx where x is the sliding distance, W is the load on the contact, measured normal to it and κ is the dimensional wear coefficient. For smooth wrought steel variator parts which do not suffer surface distress, κ is approximately 2×10−11 mm3(Nm)−1. For powder metal parts used in the trials, κ was approximately 1.5×10−8 mm3(Nm)−4.
The test parts wore more than the bearing steel parts which are intended to undergo minimal wear. However, the wear did not render the poweder metal test parts unacceptable. In some rough bearing steel components wear resulting from surface distress creates an irregular surface which produced vibration in the variator and can lead to surface initiated spalling causing the component to fail. The poweder metal test parts have been found to wear in a manner which does not impair their function. Instead, wear of the test parts resulted in a surface which remained—on a sufficiently large measurement scale—regular, and which retained—on a smaller scale—a desirable degree of roughness. The surface is believed to be renewing itself as it wears, without being ruined by surface distress or being polished smooth. It is believed that wear takes place by the removal from the surface of microscopic particles which has been and will be referred “micropitting”.
Surface roughness of the test parts was such that, had they been formed of wrought bearing steel, and in line with the prior test results mentioned above, spalling would have been expected. Surface distress and spalling have been observed in some powder metal parts. However in the majority of trials this did not occur and the longevity of the parts was acceptable. An assumption in the past has been that wear of the variator rollers and races is deleterious and is to be avoided. However, the powdered metal parts that wear in use appear to renew their running surfaces.
Traction properties of the test parts was acceptable and the 0.6% C-CR parts appeared to out perform bearing steel parts under certain traction fluid conditions.
With respect to the traction/variator film thickness discussion, conventional variator parts are made sufficiently smooth that they do not make physical contact in normal operation (except of course at start up, before the fluid film is established), while the test parts are sufficiently rough that contact between their asperities is to be expected.
Explanations of the reasons for the powdered metal component performance is not intended to limit the scope of the invention by reference to any particular theory in this regard. However it is believed that the powder metal components experienced micro-pitting instead of spalling and, as a result, the parts did not fail. It is also believed that propagation of surface initiated cracks which would have led to spalling was limited or eliminated resulting from the powder metal morphology. Small particles were lost from the component surface, but the larger cracks which would cause spalling did not develop. It is also believed that micro-pitting renews the running surfaces of the components to a certain extent to help sustain a level of surface roughness to improve the traction coefficient. See
It is also believed that the powder metal components morphology may enhance lubrication. See the explanation of
The traction tests described above suggest that specialized synthetic traction fluids are not necessary to maintain acceptable performance with powder metal components. Consequently the use of suitable powder metal components may enable use of less expense/more economical traction fluid. It may also provide for reduction in end load and consequent improvement in energy efficiency.
Component testing is still ongoing so it is difficult at this time to determine yet the actual cause of the improved performance of the powdered metal parts. Moreover, the discussion of the results is not intended to limit the scope of the invention by reference to any particular theory as to the reasons for the performance of the tested components.
This is a divisional of co-pending U.S. application Ser. No. 13/443,642, filed Apr. 10, 2012, which is a continuation of U.S. application Ser. No. 11/626,809, now U.S. Pat. No. 8,152,687, filed Jan. 24, 2007, which is incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13443642 | Apr 2012 | US |
| Child | 14323953 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11626809 | Jan 2007 | US |
| Child | 13443642 | US |