The present invention relates generally to syringes for use with injectors and to methods of manufacturing syringes and other devices and, particularly, to syringes manufactured by blow molding and to methods of blow molding syringes and other devices.
In many medical procedures, such as drug delivery, it is desirable to inject a fluid into a patient. Likewise, numerous types of contrast media (often referred to simply as contrast) are injected into a patient for many diagnostic and therapeutic procedures for example, gene therapy, cell and biological agent delivery, and delivery of therapeutic agents generally). For example, contrast media are used in diagnostic procedures such as X-ray procedures (including, for example, angiography, venography, urography,), computed tomography (CT) scanning, magnetic resonance imaging (MRI), and ultrasonic imaging. Contrast media are also used during therapeutic procedures, including, for example, angioplasty and other interventional radiological procedures.
A number of injector-actuated syringes and powered injectors for use in medical procedures such as angiography, computed tomography (CT), ultrasound and NMR/MRI have been developed. A front-loading syringe and injector system is, for example, disclosed in U.S. Pat. No. 5,383,858, assigned to the assignee of the present invention, the disclosure of which is incorporated herein by reference. Other front-loading syringes and injectors systems are, for example, disclosed in U.S. Pat. No. 6,652,489, the disclosures of which are incorporated herein by reference.
Historically, it has been difficult to manufacture syringes with desirable transparent optical properties that exhibit sufficient strength for use with front-loading, pressure jacketless injectors. Indeed, depending upon the application, syringe pressures in the range of 300 psi to 1200 psi are commonly experienced in injection procedures using powered injectors. Typically, to achieve suitable strength, the syringe walls must be thickened during manufacture, which increases costs and, depending upon the material, can degrade optical properties. However, in the current injection molding practices for manufacturing syringe, there is a limit to the wall thickness that can be achieved. This limit can result in syringes designed with a lower safety factor than desirable. Moreover, as wall thickness is increased, production costs also increase. For example, increases in wall thickness are associated with longer injection times, longer packing times, higher pressures, longer cooling time, and increased resin costs.
It is desirable to develop new syringes and methods of fabricating or manufacturing syringes that reduce or eliminate the above-identified and other problems associated with current syringes and methods of manufacture.
In one aspect, the present invention provides a syringe for use in a pressurized injection of a fluid. The syringe includes a syringe barrel including a polymeric material having undergone expansion via blow molding. An inner diameter of the syringe barrel can, for example, be sufficiently constant (over at least a portion of the axial length of the syringe) that a plunger slidably positioned within the syringe barrel and in generally sealing contact with an inner wall of the syringe barrel can be used within the syringe barrel to generate a pressure to inject a fluid contained within the syringe barrel. The syringes of the present invention can be used in both low pressure and high pressure application. For example, the constancy of the inner diameter of the syringe barrels of the syringes of the present invention is suitable to generate a pressure of at least 1 psi within the syringe barrel or of, for example, at least 100 psi within the syringe barrel. In several embodiments, the diameters of the inner walls of the syringe barrels of the present invention are suitably constant to generate a pressure of at least 200 psi, at least 300 psi, or even at least 500 psi within the syringe barrel.
The inner diameter of the syringe wall can, for example, vary no more than 0.01 in. The inner diameter of the syringe can also vary by no more than 0.007 in. or even no more than 0.004 in.
The polymeric material can, for example, undergo biaxial orientation via injection stretch blow molding.
The syringe can, for example, include one or more portions, sections or components that are molded to certain predefined acceptable tolerances for a predefined use. Such molded portions, sections or components are sometimes referred to herein as “precision molded” portions, sections or components. For example, the syringe can include one or more attachment mechanisms positioned, for example, to the rear of the syringe barrel. Likewise, one or more attachment mechanism and/or other precision molded portions can be formed on or in the vicinity of the forward end of the syringe, in the vicinity of the syringe outlet.
In several embodiments, the polymeric material of the syringe includes, for example, at least one of polyethyleneterephthalate (PET), cyclic olefin polymer, polypropylene, polystyrene, polyvinylidene chloride, polyethylene naphthalate (PEN) or nylon. The polymeric material can be a coinjected material of one or more of the above identified polymers and/or other polymers. Examples of coinjected materials include, but are not limited to, PET/PEN or PET/nylon. The syringe can include a first layer of a first polymeric material and at least a second layer of a second polymeric material, different from the first polymeric material. At least one of the first polymeric material can, for example, include polyethyleneterephthalate, cyclic olefin polymer, polypropylene, polystyrene, polyvinylidene chloride, polyethylene naphthalate or nylon. The first and/or the second polymeric material can, for example, include a single polymer or blends of two or more polymers. As used herein, the term “polymer” includes homopolymers which are synthesized from a single monomer and copolymers which are synthesized from two or more different monomers. The polymeric materials of the first layer and the second layer can, for example, differ in one or more respects such as composition, molecular weight, crystallinity, barrier properties etc.
The syringe barrels can, for example, withstand relatively high pressures. For example, the syringe barrel can withstand pressures of at least 1 psi, at least 100 psi, at least 150 psi, at least 200 psi, at least 300 psi, at least 500 psi or even at least 1200 psi.
The walls of the syringe barrel can be relatively thin. For example, the wall of the syringe barrel can be less than 0.07 inches in thickness or even less than 0.05 inches in thickness.
The method can further include a heat setting process. For example, a heat setting process can be used to maintain a suitable dimension of internal diameter of a syringe barrel (or, for example, other open ended medical devices and other devices). A heat setting process can also, for example, be used to minimize fluid capacitance of a syringe barrel or other open ended medical device (or, for example, other open ended medical devices and other devices).
In another aspect, the present invention provides a method of forming a syringe including the steps of: injection molding at least one polymeric material to form a preform; placing the preform into a blow mold die; and expanding at least a portion of the preform within the die to form a barrel of the syringe. Those components, elements, portions or sections of the preform to be blow molded/expanded (for example, the barrel portion of the syringe) are typically heated (above the glass transition (Tg) of the polymeric material(s)) prior to placing the preform within the blow mold die. During the preheating process, precision molded components, portions or sections of the preform can be protected from heating (that is, maintained at a lower temperature) to, for example, maintain molded dimensions within acceptable tolerances. Those portions or sections of the preform to be expanded within the blow mold die can also be heated during the blow molding process. The syringes can be formed for use at low pressure or to withstand relatively high pressures as described above. The at least one polymeric material can, for example, be polyethyleneterephthalate, cyclic olefin polymer, polypropylene, polystyrene, polyvinylidene chloride, polyethylene naphthalate or nylon. The method can further include a heat setting process.
Injection molding the preform can, for example, include forming one or more portions molded to dimension of predefined acceptable tolerance such as an attachment mechanism (positioned, for example, adjacent a proximal or rearward end of the syringe), which is adapted to connect the syringe to, for example, a powered injector. The attachment mechanism can, for example, include at least one flange. The tolerances of precision molded portions such as injector attachment mechanisms are maintained during blow molding. For example, the attachment mechanism or other precision molded portion is not altered or substantially altered (for example, such that an attachment mechanism does not suitably retain the syringe upon an injector) during the expansion of the preform. Injection molding the preform can also include forming a connector or other precision molded portion adjacent a distal end of the preform. The connector or other precision molded portion is not altered or substantially altered during expansion of the preform.
Expanding at least a portion of the preform can include forcing of a gas within the preform and axial extension of an extension rod within the preform. Injection molding the preform can also include forming a syringe outlet section at a distal end of the preform, wherein the preform including a passage between a barrel section thereof and the syringe outlet section. The extension rod can, for example, form at least a partial seal with the passage during expansion of the preform. In several embodiments, injection molding the preform can also include forming a connector or attachment mechanism (for example, a Luer connector) during injection molding of the preform as described above, which is positioned adjacent the distal end of the preform. Once again, the connector is not altered or substantially altered during expansion of the preform.
A removable closure can be formed on a distal end of the outlet section during injection molding. The closure can, for example, be removably connected to the outlet section via a wall section of reduced thickness.
In another aspect, the present invention provides a method of forming a syringe for use with an injector including injection molding a polymeric material to form a removable closure integrally with an outlet section or opening of the syringe. The removable closure can, for example, be formed during injection molding of a preform for the syringe which is subsequently blow molded to form the syringe. As described above, the closure can be removably connected to the outlet section via a wall section of reduced thickness.
In a further aspect, the present invention provides a syringe including a barrel, an outlet section integrally formed with the barrel at a distal end of the barrel and a removable closure integrally formed with the outlet section at a distal end of the outlet section. The closure can, for example, be removably connected to the outlet section via a wall section of reduced thickness.
In another aspect, method of forming a syringe for use with an injector, including: forming a preform comprising a syringe outlet section on a distal end thereof and a closed section corresponding to a precursor of a barrel section of the syringe on the proximal end thereof by injecting at least one polymeric material into a mold for the preform; placing the preform into an blow mold die; and expanding at least a portion of the preform by passing pressurized gas into the interior of the syringe via an outlet opening in the outlet section to form a barrel of the syringe. As described above, those portions or sections of the preform to be blow molded/expanded (for example, the barrel portion of the syringe) are typically heated (above the glass transition (Tg) of the polymeric material(s)) prior to placing the preform within the blow mold die. During the preheating process, precision molded components, portions or sections of the preform can be protected from heating (that is, maintained at a lower temperature) to, for example, maintain molded dimensions within acceptable tolerances. Once again, those portions or sections of the preform to be expanded within the blow mold die can also be heated during the blow molding process. The syringe can be formed to withstand low pressures and/or relatively high pressures (for example, pressures of at least 100 psi or higher) as described above. The formed syringe can be closed on the proximal end thereof via a removable closure formed integrally or monolithically with the syringe. The removable closure can, for example, form a plunger section upon removal from connection with the syringe.
In a further aspect, the present invention provides a syringe including an outlet section on a distal end thereof. The outlet section includes an outlet opening. A barrel section is integrally or monolithically formed with the outlet section. A disengeagable closure is integrally or monolithically formed at a proximal end of the syringe. In several embodiments, the closure forms at least part of a syringe plunger upon disengagement from the barrel section.
In still a further aspect, the present invention provides a syringe including a syringe wall comprising a first layer of a first polymeric maternal and at least a second layer of a second polymeric material, different from the first polymeric material. One of the first layer and the second layer can, for example, include polyethyleneterephthalate, cyclic olefin polymer, polypropylene, polystyrene, polyvinylidene chloride, polyethylene naphthalate and/or nylon. The first layer can, for example, be radially inward from the second layer and have greater lubricity than the second layer. One of the first layer and the second layer can, for example, have better barrier properties than the other of the first layer and the second layer.
In still a further aspect, the present invention provides a method of forming a device including a first opening, a second opening and a flow path between the first opening and the second opening. The method includes: injection molding at least one polymeric material to form a preform, the preform including a first molded portion in the vicinity of the first opening that is molded to acceptable tolerances; placing the preform into an blow mold die; and expanding an intermediate portion of the preform intermediate between the first opening and the second opening within the die by blowing a gas into the preform and axially extending an extension rod within the preform. The extension rod abuts a section of the preform and forms at least a partially sealing closure between the flow path and the first opening during extension thereof. The intermediate portion of the preform is expanded while maintaining the acceptable tolerances of the first molded portion. The method can further include heating the intermediate portion of the preform before placing the preform into the blow mold die. The method can also include heating the intermediate portion of the preform during expansion within the die. The method can further include a heat setting process.
In several embodiments, the device is a medical device adapted to form a component of a fluid flow system. In a number of embodiments, the device is a syringe.
The preform can, for example, further include a second molded portion in the vicinity of the second opening that is molded to acceptable tolerances. The intermediate portion of the preform is expanded while maintaining the acceptable tolerances of the second molded portion.
The polymeric material can, for example, include polyethyleneterephthalate, cyclic olefin polymer, polypropylene, polystyrene, polyvinylidene chloride, polyethylene naphthalate and/or nylon.
In still another aspect, the present invention provides a system for forming a device including a first opening, a second opening and a flow path between the first opening and the second opening. The system includes a blow mold die adapted to receive an injection molded preform. The preform further includes a first molded portion in the vicinity of the first opening that is molded to acceptable tolerances. The blow mold die includes a forward section shaped to receive the first molded portion. The system further includes an extension rod axially movable within the blow mold die to assist in axially expanding an intermediate portion of the preform intermediate between the first opening and the second opening within the die while gas is blown into the preform. The extension rod is adapted to abut a section of the preform and form at least a partially sealing closure between the flow path and the first opening during extension thereof. In several embodiments, the blow mold die further includes a rearward section shaped to receive a second molded portion in the vicinity of the second opening that is molded to acceptable tolerances. Cooperation between the rearward section and the second molded portion can, for example, operate to retain the preform in the blow mold die during expansion of the intermediate section. The method can further include a heat setting process.
Other aspects of the invention and their advantages will be discerned from the following detailed description when read in connection with the accompanying drawings, in which:
In general, the present invention provides hollow article devices such as syringes and methods of manufacture of such devices using blow molding processes. The present invention is discussed below primarily with reference to representative embodiments of syringes for injection of a fluid into a patient. However, one skilled in the art appreciates that the methods of the present invention can be used to form a number of hollow article devices (including, for example, medical flow path elements or devices).
Blow molding is a method of forming hollow articles from polymeric (thermoplastic) materials. Simplifying, the blow molding process involves forming a heated tube within a mold cavity using a pressurized gas (typically, compressed air). The three most common methods of blow molding are extrusion blow molding, injection blow molding and injection-stretch blow molding. In extrusion blow molding, tubes or parisons are extruded into alternating open mold halves and then blown and cooled prior to removal from the mold. In injection blow molding, a “preform” component is first injection molded. The preform is then blown to the product's final shape. Injection blow molding can provide dimensional precision in certain critical areas. The injection blow molding process can be performed using separate machines or through use of shuttling or rotating molds. In the injection-stretch blow molding process, a preform is, once again, first injection molded. During subsequent blowing, however, the preform/parison is mechanically extended at an optimal temperature, while radially blown to shape within the mold. Injection-stretch blow molding provides a biaxial stretch to enhance material properties. For example, the biaxial orientation can increase tensile strength by an order of five or more. Furthermore, biaxial orientation can enhance other material properties, such as clarity, barrier properties (2× or more), and mechanical properties. For example, crystallinity of certain polymers can be controlled. In several embodiments for syringes of the present invention manufactured from, for example, polyethyleneterephthalate, crystallinity can be increased to as high as approximately 43% (for example, via mechanical and/or thermal processing) to maximize these improvements. One skilled in the art also realizes that further increasing crystallinity can be detrimental and decrease optical properties and cause the material to be too brittle.
The present inventors have discovered that the improved mechanical properties provided by blow molding of, for example, syringes can enable a decrease in the barrel wall thickness of a syringe as compared to an injection molded syringe while maintaining an acceptable safety factor over a range of operating pressures. Moreover, use of a blow molding process in the manufacture of syringes and other devices can substantially increase manufacturing throughput. Indeed, significant reduction in manufacturing cost can result from using a blow molding process to manufacture syringes for use with powered injectors and non-powered or manually powered syringes. Likewise, significant reduction in manufacturing cost can result from using a blow molding process to manufacture other devices including, but not limited to, hollow devices used in flow paths for medical fluids.
As described above, during the stretch blow molding process, stretch rod 320 is extended forward, while compressed air is blown into the interior of preform 10 until preform 10 is expanded to fill the mold cavity, thereby forming syringe 10′ including barrel 12′ in which the thermoplastic is biaxially oriented (that is, oriented axially or in the direction of axis A and radially/tangentially or in a direction normal or around to axis) as described above. In this embodiment, stretch rod 320 pushes against closed end 14′ during the blow stretch molding process. Upon cooling, syringe 10′ is removed from mold 100.
To achieve high pressures, smooth plunger movement within the syringe, limit blow by, and/or provide predictable volume in the syringes of the present invention, it is desirable to have an inner diameter in the syringe barrel having a relatively consistent wall thickness. To ensure a relatively consistent wall thickness and therefore a predictable, relatively consistent interior syringe barrel diameter with adequate strength, the preform design is important. For example, the area in front of the drip flange 30 may undergo a stretch of up to four (4) times its original length and width in preform 10 to meet the final dimensions in syringe 10′. If the material stretches unevenly as a result of design or heating limitations, such stretching variability must be provided for in the preform design. For example, additional material may be required in areas of high stretch. On the other hand, reduced material may be required in areas of low stretch. Alternatively or additionally, the rate or speed of stretch, the preform temperature, and blow pressure can be varied. The inventors of the present invention have discovered that relatively consistent and predictable wall thickness and internal diameter can be readily achieved in blow molded syringes. The process considerations set forth above are known to those skilled in the blow molding arts and can result in a syringe barrel compatible with high-pressure (for example, 50 psi to 1500 psi) use and adequate/predictable fluid performance. An example of an acceptable delivery volume tolerance in an injection system is approximately ±2%+1 mL. In meeting a suitable delivery volume tolerance, the inner diameters of the syringes of the present invention preferably do not vary by greater than 0.01 inches. Variances of no greater than 0.007 inches in inner diameter are also achievable. Indeed, variances of no greater than 0.004 inches in inner diameter are also achievable over the pressurizing zone of the syringe.
In several studies of the syringes of
Static high pressure testing was performed at 2 mL/s for 5 samples from each lot using water. In the static high pressure test, each syringe was filled to just below drip flange (approximately 75% full). The plunger was then installed. The syringe was retained in a holding fixture in the Instron universal tensile testing machine while a measurable force was applied to plunger. The Instron universal tensile testing machine, which was calibrated for flow rate, was set at 2 ml/sec and failure mode was recorded. Three PET material types, as described above, were tested. The static high pressure testing resulted in an average pressure of 342 psi with a standard deviation of 40 psi for EN001 PET. Failure modes were barrel burst and blow by. The static high pressure testing resulted in an average pressure of 310 psi with a standard deviation of 171 psi for EN063 PET. Potential failure modes were barrel burst and blow by. The static high pressure testing resulted in an average pressure of 305 psi with a standard deviation of 67 psi for HW CF746 PET. The failure mode was barrel burst.
Dynamic pressure testing was performed at 5 ml/s for 5 samples from each lot using saline. Dynamic pressure and capacitance testing were performed only for EN001 PET as the force to fail was the largest for that material of the three material types tested. In these tests, closed end 14′ of syringes 10′ was drilled out and a metal luer connection was connected. A flow restrictor valve was connected to the luer connection. The Instron was set at 5 ml/sec. The flow restrictor valve was adjusted to generate a pressure of 100 psi. The average dynamic friction force was 50 lbs or 18.7 psi at a syringe pressure of 100 psi.
In tensile strength testing, samples were first cut out using the tensile bar cutting die. Tests were then performed in accordance with the testing procedures set forth in ASTM D638. Samples were cut radially (5 samples of each lot) as well as axially (5 samples of each lot).
In several capacitance testing studies of the syringes of the present invention, a metal luer was installed in syringes 10′ as described above, and syringes 10′ were filled with water. A rubber O-ring plunger was inserted and the plunger was advanced until the front of the plunger was approximately 1 inch past drip flange 30. Syringe 10′ was then mounted onto the Instron. The Instron was set to run at 2 in/min and to stop at a load of 540 lbs. A 3-way stopcock was installed on the end of the syringe, and a scale was placed under the syringe with a beaker to capture the fluid. A piece of connector tubing was attached to the metal luer fitting that was of sufficient length to reach into the beaker. Care was taken so that the tubing did not come in contact with the beaker. The Instron was then run. When the 540 lb limit was reached, the stopcock was turned slowly to dispense the fluid into the beaker. Subsequently, the stopcock was returned to the closed position to dispense the remaining fluid out of the line. The volume of fluid dispensed into the beaker was recorded. The results of several studies are set forth in Table 3.
In general, neither the tested syringes nor the method of manufacture was optimized in the above studies. The failure mode observed during the burst pressure tests, were almost all a result of splitting at the blow mold parting line. The blow mold parting line is the split between the mold halves. A non-optimized parting line can cause undue material stress and malformation, which may weaken this area. Optimizing the parting line (which was not done in the present studies) can, for example, be accomplished by ensuring a minimal mismatch and sharp clean edges on the parting line of the blow molding tool. The friction force and static pressure were found to be relatively consistent in the tested syringe with the highest level of consistency realized with the EN001 material. The data suggested that the blow-up ratio to tensile strength is a linear function, which correlates with published information on injection-stretch blow molding. These results reflect a 2 to 1 ratio on the axial dimension and a 1 to 1+ on radial dimensions. The EN001 material exhibited the highest increase. The friction force was found to consistent along the length of the barrel. Moreover, the barrel wall thickness was consistent, as interpolated from the friction data.
A “heat setting” process as known in the blow molding arts (effected, for example, via heating the blow mold cavities to elevated temperatures) may be desirable, for example, in the case that ethylene oxide (EtO) sterilization is to be used, as a result of the elevated temperatures used during EtO sterilization. The elevated temperatures of the EtO sterilization process may cause the suitable or acceptable dimension of the syringe barrel internal diameter to relax or change to an unacceptable dimension. The syringe plunger, which is sealingly and slidably positioned within the syringe barrel, exerts an outward force to ensure an adequate seal against the barrel wall to prevent leakage when pressurized during use. The heat setting process prevents the barrel wall from expanding or contracting and changing to an unacceptable dimension. It is not believed that a “heat setting” process will be required to control or improve the fluid capacitance of the syringe barrel. However, the results indicate that syringe fluid capacitance can also be improved with blow molding (for example, via heat setting), as compared to injection molding even with a relatively thin wall. The wall thickness of the syringes studied in the present invention was approximately 0.030 inches (versus, for example, approximately 0.79 for a typical injection molded syringe). The pressure capability of the syringe barrel can, for example, be improved by using a preform which exhibits a higher stretch ratio with the same wall thickness. The preform design can also be improved or optimized to, for example, take advantage of the PET “self-leveling” material characteristics, which will improve dimensional consistency and increase overall material strength. In general, self-leveling is the ability for the polymer to stretch, such that it pulls from a thicker cross section instead of a thinner cross section. If the cross section is properly sized to the total expansion, the final component will exhibit a consistent wall thickness.
Similar to preform 10, preform 210 is placed within the mold, as illustrated in
As described above, during the stretch blow molding process, stretch rod 320 is extended forward, while compressed air is blown into the interior of preform 210 until preform 210 is expanded to fill the mold cavity, thereby manufacturing syringe 210′ including barrel 212′ in which the thermoplastic is biaxially oriented. In this embodiment, stretch rod 320 includes a forward section 330 dimensioned to enter and at least partially seal the rearward portion of syringe tip 214′ (from fluid connection with the portion or preform 210 being expanded), thereby assisting in maintaining pressure within expanding barrel 212′. Stretch rod 320 also pushes against syringe tip 214′ during the blow stretch molding process as described above to, for example, assist in achieving biaxial orientation. Moreover, stretch rod 320 at least partially prevents heated gas from entering syringe tip 214, (which is injection molded during fabrication of preform 210 to predefined acceptable tolerances), thereby assisting in maintaining syringe tip 214 essentially unaltered during the blow molding process.
In general, the process described above in connection with the syringe of
In this embodiment, syringe tip 414 includes an integrally molded syringe tip closure 418 that is molded integrally with syringe tip 414 during the injection molding of the preform. Syringe tip closure 418 can, for example, be connected to syringe outlet 414a via an area of reduced wall thickness 419 so that syringe tip closure 418 can be readily broken off to open syringe outlet 414a. Syringe tip closure 418 can, for example, assist in maintaining sterility in the case of a prefilled syringe. The integrally molded syringe tip closures of the present invention can also be provided on syringes that are not blow molded (for example, injection molded syringes).
With reference to
Although the present invention has been described in detail in connection with the above embodiments and/or examples, it should be understood that such detail is illustrative and not restrictive, and that those skilled in the art can make variations without departing from the invention. The scope of the invention is indicated by the following claims rather than by the foregoing description. All changes and variations that come within the meaning and range of equivalency of the claims are to be embraced within their scope.
This application is a continuation application of co-pending U.S. application Ser. No. 12/794,990, filed Jun. 7, 2010, which is a divisional application to U.S. application Ser. No. 11/833,427, filed Aug. 3, 2007, now U.S. Pat. No. 7,740,792, which claims priority to U.S. Provisional Application Ser. No. 60/821,314, filed Aug. 3, 2006, the disclosures of each of which are incorporated herein by this reference.
Number | Date | Country | |
---|---|---|---|
60821314 | Aug 2006 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 11833427 | Aug 2007 | US |
Child | 12794990 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 12794990 | Jun 2010 | US |
Child | 14605066 | US |