Patent Application
20240309159
The present invention relates to a preform structure, a fiber-reinforced plastic, and a production method for a preform structure.
A known example of a fiber-reinforced plastic is one in which a preform structure including reinforcing fibers, such as carbon fibers or glass fibers, is embedded in a resin body. Fiber-reinforced plastics are used in various fields such as sporting goods, leisure goods, materials for automobiles, materials for aircraft, and electronic device components.
As the reinforcing fibers, carbon fibers, which have particularly high strength, are used when high strength is required. However, since carbon fibers are less likely to be processed into freely chosen shapes, a carbon fiber cloth is used in the case of use in a preform structure.
Meanwhile, various forms of preform structures using reinforcing fibers, such as carbon fibers, have been studied. For example, Patent Literature 1 discloses a preform structure in which two or more layers prepared by aligning bundles of reinforcing fibers such that the longitudinal directions thereof are arranged in one direction are stacked such that the longitudinal directions of the bundles of reinforcing fibers are different from each other. In this preform structure, an auxiliary thread is used as means for restraining the positions of the bundles of reinforcing fibers.
In the preform structure disclosed in Patent Literature 1, the layers composed of bundles of reinforcing fibers can be stacked such that the angle of the bundles of reinforcing fibers in the longitudinal direction shifts. However, since designs other than the above cannot be drawn, there is a problem in that design flexibility for improving the strength is low. In view of this, a preform structure having higher design flexibility is desired. In the preform structure disclosed in Patent Literature 1, glass fibers, polyester fibers, nylon fibers, and the like are used as the materials of the auxiliary thread. However, since carbon fibers are not used as the auxiliary thread, there is a problem in that the entire structure cannot be composed of carbon-based materials. There is also a problem in that the compatibility with an impregnating resin may be poor depending on the material of the auxiliary thread.
An object of the invention is to provide a preform structure including a carbon fiber and having high design flexibility, a fiber-reinforced plastic, and a production method for the preform structure.
According to an aspect of the invention, there is provided a preform structure including a carbon fiber, a support layer that serves as a substrate for the carbon fiber, and a carbon-based thread for securing the carbon fiber to the support layer.
In the preform structure according to the above aspect of the invention, the carbon-based thread is preferably at least one selected from the group consisting of a carbon nanotube yarn and a composite yarn of a resin and a carbon nanotube yarn.
In the preform structure according to the above aspect of the invention, the support layer is preferably at least one selected from the group consisting of a glass fiber cloth, a carbon fiber cloth, a resin cloth, and a resin film.
In the preform structure according to the above aspect of the invention, the support layer is preferably at least one selected from the group consisting of a glass fiber cloth and a carbon fiber cloth.
In the preform structure according to the above aspect of the invention, the support layer is preferably at least one selected from the group consisting of a resin cloth and a resin film.
According to another aspect of the invention, there is provided a fiber-reinforced plastic including the preform structure according to the above aspect of the invention; and a resin with which the preform structure is impregnated.
According to still another aspect of the invention, there is provided a fiber-reinforced plastic including the preform structure according to the above aspect of the invention; and a resin with which the preform structure is impregnated, in which a resin that is a material of the resin cloth or the resin film and the resin with which the preform structure is impregnated are the same material.
According to a further aspect of the invention, there is provided a production method for a preform structure, the method being a production method for the preform structure according to the above aspect of the invention, the method including disposing the carbon fiber on the support layer and securing the carbon fiber to the support layer with the carbon-based thread.
In the production method for a preform structure according to the above aspect of the invention, the carbon fiber is preferably secured to the support layer by sewing with the carbon-based thread.
In the production method for a preform structure according to the above aspect of the invention, the carbon fiber is preferably secured to the support layer using an embroidery machine.
In the production method for a preform structure according to the above aspect of the invention, the carbon-based thread preferably has a tensile strength of 500 MPa or more.
According to the above aspects of the invention, it is possible to provide a preform structure including a carbon fiber and having high design flexibility, a fiber-reinforced plastic, and a production method for the preform structure.
Hereinafter, the invention will be described with reference to an exemplary embodiment on the basis of the drawings. The invention is not limited to the exemplary embodiment. In the drawings, some parts are enlarged or reduced for ease of explanation.
A preform structure 10 according to a first exemplary embodiment of the invention includes a carbon fiber 2, a support layer 1 that serves as a substrate for the carbon fiber 2, and a carbon-based thread 3 for securing the carbon fiber 2 to the support layer 1, as illustrated in
In this manner, the carbon fiber 2 is disposed on the support layer 1 in a flexible design and secured with the carbon-based thread 3. The carbon fiber 2 is usually used as a carbon fiber cloth; however, in the exemplary embodiment, the carbon fiber 2 can be used for the preform structure 10 in a form other than a cloth. Therefore, design flexibility for the carbon fiber 2 can be enhanced. For example, in a case where the support layer 1 is a carbon fiber cloth, when the carbon fiber 2 is stacked on this support layer 1 in a flexible design, preform structures having different designs of carbon fibers can be stacked.
The support layer 1 is a layer that serves as a substrate for the carbon fiber 2. The carbon fiber 2 can be disposed on the support layer 1 in a flexible design.
Examples of the support layer 1 include glass fiber cloths, carbon fiber cloths, resin cloths, and resin films. Of these, glass fiber cloths and carbon fiber cloths are preferred in view of the strength of the preform structure 10. Carbon fiber cloths are particularly preferred from the viewpoint that the whole of the preform structure 10 can be composed of carbon-based materials.
When the support layer 1 is a glass fiber cloth or a carbon fiber cloth, the support layer 1 may be, for example, a cloth woven with warp threads 11 and weft threads 12, as illustrated in
The carbon fiber 2 is a fiber obtained by subjecting a precursor of an organic fiber to heating carbonization treatment, 90% or more of the fiber being composed of carbon by mass ratio. The carbon fiber 2 can be produced by carbonizing, at high temperature, an acrylic fiber or pitch (byproducts of petroleum, coal, coal tar, and the like) serving as a raw material.
Examples of the carbon fiber 2 include PAN-based carbon fibers (carbon fibers using acrylic fibers) and pitch-based carbon fibers (carbon fibers using pitch).
The carbon-based thread 3 is a thread that can penetrate the support layer 1 and that includes fibers composed of a carbon-based material. Note that the carbon fiber 2 described above is not included in the carbon-based thread 3. The carbon fiber 2 is short of flexibility, and unlike threads, the carbon fiber 2 cannot be used for sewing. In contrast, the carbon-based thread 3 can be passed through the weave texture of a carbon fiber cloth or the like, so that the carbon fiber 2 can be secured with the carbon-based thread 3.
With such a carbon-based thread 3, the use of a carbon fiber cloth as the support layer 1 enables all the materials of the preform structure 10 to be carbon-based materials. In addition, the strength of the preform structure 10 can be further improved.
Examples of the carbon-based thread 3 include carbon nanotube yarns and carbon nanotube composite yarns (hereinafter also referred to as “CNT composite yarns”) of a resin and a carbon nanotube yarn.
A carbon nanotube yarn is obtained, for example, in the form of a filamentous linear body, by drawing carbon nanotubes in the form of a sheet from an end portion of a carbon nanotube forest (which is a growth body obtained by growing a plurality of carbon nanotubes on a base plate so as to be oriented in a direction perpendicular to the base plate and which is also referred to as an “array”), bundling the drawn carbon nanotube sheet, and then spinning a bundle of carbon nanotubes. Alternatively, a carbon nanotube yarn can be obtained by, for example, performing spinning from a dispersion liquid of carbon nanotubes. The production of a carbon nanotube linear body by spinning can be performed by, for example, the method disclosed in U.S. Patent Application Publication No. 2013/0251619 (JP 2012-126635 A). From the viewpoint of obtaining a carbon nanotube yarn with high purity, a carbon nanotube yarn is preferably obtained by spinning a carbon nanotube sheet. The carbon nanotube yarn may be a yarn obtained by spinning two or more carbon nanotube yarns together.
Examples of the CNT composite yarns include: (1) yarns obtained by, in the process of obtaining a carbon nanotube yarn, the process including drawing carbon nanotubes in the form of a sheet from an end portion of a carbon nanotube forest, bundling the drawn carbon nanotube sheet, and then spinning a bundle of carbon nanotubes, forming a resin film on a surface of the forest, sheet, bundle, or spun yarn of carbon nanotubes; (2) CNT composite yarns obtained by spinning a bundle of carbon nanotubes together with a yarn composed of another material; and (3) CNT composite yarns obtained by spinning a carbon nanotube yarn or a CNT composite yarn with a yarn composed of another material. The CNT composite yarns (3) are composite yarns obtained by braiding two yarns but may be composite yarns obtained by spinning three or more yarns together as long as at least one carbon nanotube or CNT composite yarn is included.
When a CNT composite yarn is used as the carbon-based thread 3, the resin used in the CNT composite yarn is preferably a resin with which the preform structure 10 is impregnated. Such a resin can be a resin that is the same as a resin of a resin layer 4 described later, and thus the CNT composite yarn is easily impregnated with the resin.
When the carbon-based thread 3 is a spun yarn, the Z-spin (left spin) is preferred. In a case of the Z-spin, unwinding of the thread can be reduced when sewing is performed with the carbon-based thread 3 using an embroidery machine.
The diameter of the carbon-based thread 3 (in a case of a spun yarn, the diameter of the spun yarn) is preferably in a range from 50 μm to 1,000 μm. When the diameter of the carbon-based thread 3 is within the above range, the carbon fiber 2 can be more reliably secured with the carbon-based thread 3.
The carbon-based thread 3 preferably has a tensile strength of 500 MPa or more. When the tensile strength is 500 MPa or more, a problem such as thread breakage during sewing with the carbon-based thread 3 can be prevented.
The tensile strength of the carbon-based thread 3 can be measured by the following method. Specifically, the carbon-based thread 3 is cut with a cutter to have a length of 4 cm, and portions of 1.5 cm from each end of the carbon-based thread 3 are fixed to a paperboard with an adhesive (Aron Alpha EXTRA4020, manufactured by Toagosei Co., Ltd.) such that a measurement length is 1 cm to prepare a specimen. The following tensile test is performed using this specimen to measure the tensile strength.
For each specimen, a tensile strength at which the linear material is broken under the following conditions is measured.
Next, a production method for a preform structure according to the exemplary embodiment will be described.
The production method for a preform structure according to the exemplary embodiment is a production method for the above-described preform structure according to the exemplary embodiment, the method including disposing a carbon fiber 2 on a support layer 1 and securing the carbon fiber 2 to the support layer 1 with a carbon-based thread 3.
In the securing, first, a carbon fiber 2 is disposed on the support layer 1.
Here, the carbon fiber 2 can be arranged in various shapes. The shape of the carbon fiber 2 may be a spiral shape as illustrated in
Examples of the shape of the carbon fiber 2 include circular shapes, elliptical shapes, angular shapes (such as triangular, rectangular, pentagonal, and hexagonal shapes), star shapes, wavy shapes, and linear shapes.
The number of carbon fibers 2 is not particularly limited and is preferably one or more, in view of strength, more preferably two or more.
In the securing, next, the carbon fiber 2 is secured to the support layer 1 with a carbon-based thread 3.
As the method for securing the carbon fiber 2 with the carbon-based thread 3, a publicly known method can be appropriately employed. For example, the method may be a method of securing the carbon fiber 2 to the support layer 1 by sewing with the carbon-based thread 3. The sewing method may be hand sewing or a method using a machine. Examples of the machine used here include sewing machines and embroidery machines. Of these, embroidery machines are preferably used.
Next, a fiber-reinforced plastic according to the exemplary embodiment will be described.
A fiber-reinforced plastic 100 (see
Examples of the resin used here include thermosetting resins and thermoplastic resins.
Examples of thermosetting resins include epoxy resins, polyester resins, phenolic resins, and thermosetting polyimide resins. Of these, epoxy resins are preferred in view of, for example, strength.
Examples of thermoplastic resins include polypropylene resins, polyphenylene sulfide resins, polycarbonate resins, and thermoplastic polyurethane resins.
The fiber-reinforced plastic 100 can be produced by, for example, a method including stacking a plurality of prepregs 20 illustrated in
In the stacking, first, a prepreg 20 as illustrated in
The prepreg 20 can be produced by impregnating a preform structure 10 with a resin to form a resin layer 4 so as to cover the preform structure 10. When the resin used here is a thermosetting resin, an uncured thermosetting resin is used.
In the stacking, next, a plurality of prepregs 20 are stacked as illustrated in
When the resin is a thermosetting resin, the method may include curing the thermosetting resin after the stacking.
In this manner, after the stacking, the thermosetting resin can be cured to produce the fiber-reinforced plastic 100.
According to the exemplary embodiment, the following operations and effects can be achieved.
Next, a second exemplary embodiment of the invention will be described.
The configuration of the exemplary embodiment is similar to that of the first exemplary embodiment except that preferred examples of the support layer 1 are different, and thus the point of change will be described, and a description of other features common to those in the previous description will be omitted.
In the preform structure 10 according to the exemplary embodiment, the support layer 1 is preferably a resin cloth or a resin film.
Furthermore, in a fiber-reinforced plastic 100 according to the exemplary embodiment, a resin that is a material of the resin cloth or the resin film and the resin with which the preform structure 10 is impregnated are preferably the same material.
In such a case, the support layer 1 and a resin layer 4 can be integrated with each other. When the resin that is the material of the support layer 1 is a thermoplastic resin, the support layer 1 itself can be utilized as a resin with which the preform structure 10 is impregnated, and it is not always necessary to provide a resin layer 4 separately. Furthermore, a base part that includes a layer composed of a carbon fiber 2 having high design flexibility can be formed.
According to the exemplary embodiment, in addition to the operation and effect (1) in the first exemplary embodiment, the following operation and effect (5) can be achieved.
The invention is not limited to the exemplary embodiments described above, and modifications, improvements, and the like are included in the invention as long as the object of the invention is achieved.
For example, in the exemplary embodiments described above, a layer composed of the carbon fiber 2 is formed only on the upper surface of the support layer 1, but the invention is not limited to this. A layer composed of the carbon fiber 2 may be formed not only on the upper surface of the support layer 1 but also on the lower surface of the support layer 1. In this manner, there is provided a preform structure that includes a layer composed of the carbon fiber 2 having high design flexibility on both surfaces of the support layer 1.
In the exemplary embodiments described above, the fiber-reinforced plastic 100 is produced by stacking a plurality of prepregs 20, but the invention is not limited to this. A plurality of preform structures 10 may be stacked to form a base part, and the base part may then be impregnated with a resin to produce a fiber-reinforced plastic 100.
In the exemplary embodiments described above, in the case of stacking a plurality of prepregs 20, the curing of a thermosetting resin is performed after the stacking, but the invention is not limited to this. For example, the prepregs 20 may be pressure-bonded by hot pressing to cure the thermosetting resin in the stacking, thus producing a fiber-reinforced plastic 100.
1 support layer, 11 warp thread, 12 weft thread, 2 carbon fiber, 3 carbon-based thread, 4 resin layer, 10 preform structure, 20 prepreg, 100 fiber-reinforced plastic.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2021032865 | Mar 2021 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2022/006160 | 2/16/2022 | WO |