Patent Application
20220219228
The present disclosure belongs to the technical field of preparation of rare earth permanent magnetic materials, and particularly relates to a preparation method of improved sintered neodymium-iron-boron (Nd—Fe—B) casting strips.
Since their invention in 1983, sintered neodymium-iron-boron (Nd—Fe—B) permanent magnetic materials have been greatly developed and applied and have become an important industry. Through research, commercial production of high-magnetic-energy-product magnets is realized, and magnetic properties have been rapidly improved. However, restricted by an Nd—Fe—B powder metallurgy technology, further improvement of the magnetic properties requires improvement of a material microstructure, and mainly depends on the step of producing casting strips in the preparation process of sintered Nd—Fe—B. The microstructure of alloy casting strips obtained in the step will be inherited into final finished products, which directly affects the final microstructure of magnet finished products. However, it is very difficult to improve the microstructure of the Nd—Fe—B alloy casting strips. A current preparation technique of high-temperature alloy materials is not perfect from theory to practice.
A traditional production technology process of sintered neodymium-iron-boron (Nd—Fe—B) finished products includes material compounding, strip casting, powder preparation, forming, sintering, machining, electroplating and the like. During the strip casting, compounded materials are smelted at one time to obtain alloy casting strips.
The present disclosure provides a method for preparing Nd—Fe—B casting strips by adding nucleation assisted alloys to improve the microstructure of Nd—Fe—B alloy casting strips and substantially improve the properties of magnets under the premise of the same formula.
The present disclosure relates to a preparation method of improved sintered Nd—Fe—B casting strips. The method includes the following steps:
1) Nucleation assisted alloy particles (material A) used for sintered Nd—Fe—B casting strips are prepared.
1.1) Nucleation assisted alloy particle elements may be weighted as follows: 26.68-28% of Pr—Nd, 70-72.5% of Fe and 0.90-1% of B, where a Pr element in two elements of the Pr—Nd may account for 0-30 wt %, an Fe element in the nucleation assisted alloy particles can be replaced with part of a Co element, the Co element may account for 0-5 wt % in the material A, and alloy strips with proportion of ingredients close to that of (Pr—Nd)2Fe14B may be obtained through conventional compounding, smelting and pouring, mainly contain tetragonal phases and a few Nd-enriched phases, and have grain size of 5-30 μm.
1.2) The alloy strips may be crushed into particles with diameter of 1-10 mm by a mechanical crushing method or a hydrogen crushing method, to be used as the nucleation assisted alloy particles used for the sintered Nd—Fe—B casting strips. In some embodiments, the mechanical crushing method is preferably selected. If the hydrogen crushing method is adopted, dehydrogenation needs to be as sufficient as possible, and hydrogen content may be smaller than 1000 ppm, preferably smaller than 600 ppm to reduce influence on smelting.
2) Nd—Fe—B alloy casting strips (material C) are prepared.
2.1) Alloy ingredients may be designed according to marks of the casting strips: as the nucleation assisted alloy particles need to be added to materials finally, the addition of the nucleation assisted alloys may influence final alloy ingredients. In order to obtain ingredients of final Nd—Fe—B alloy casting strips, ingredients of materials before addition of the nucleation assisted alloy particles, namely ingredients of intermediate materials, may be designed and calculated. The nucleation assisted alloys may be added with a weight percent of 3-6 wt %. In some embodiments, the nucleation assisted alloys may be added with a weight percent of 5%.
2.2) The intermediate materials may be smelted and melted into molten steel according to a conventional sintered Nd—Fe—B smelting technology, and then may be refined after the intermediate materials are fully melted. The nucleation assisted alloy particles are added, and smelting may be performed for 3-15 minutes under the condition that power is reduced by 150-250 KW. Pouring may be performed, and final Nd—Fe—B alloy casting strips are obtained.
The specific working principle of the present disclosure lies in that:
1) The element ingredients of the nucleation assisted alloys may be weighted as follows: 26.68-28% of Pr—Nd, 70-72.5% of Fe and 0.90-1% of B. The ingredient ratio may determine that the nucleation assisted alloys mainly contain Nd2Fe14B tetragonal phases and basically do not contain Nd-enriched phases and have large grain size of 5-30 μm. After crushing, (Pr—Nd)2Fe14B particles may be obtained. The tetragonal-phase nucleation assisted alloys may be used as a nucleation point, and formation of tetragonal-phase columnar crystals from the Nd—Fe—B casting strips in the pouring process may be better facilitated.
2) In the process of preparing the Nd—Fe—B casting strips, compared with a pouring time, the time for adding the nucleation assisted alloy particles, namely material A, cannot be too early, otherwise the temperature may be too high and the material A and the intermediate materials may be melted together. In this instance, the meaning of adding the material A and the intermediate materials separately is lost, and the time for adding the nucleation assisted alloy particles, namely the material A, cannot be too late. Otherwise, the nucleation assisted alloys remain solid small grains and a nucleation effect cannot be achieved. In some embodiments, the nucleation assisted alloys may be close to a softened state and atomic clusters may be in a short-range order. Although all atoms may still be in a highly-active state, the atoms may also be limited by a crystal lattice. Thus, in the pouring process, the atoms in intermediate material molten steel may achieve nucleation growth by relying on an inherent crystal structure of the nucleation assisted alloys to obtain a desired microstructure.
3) The nucleation assisted alloys may be added after the intermediate materials are melted and smelted for 10-20 minutes. After the nucleation assisted alloys are added, smelting may be performed for 3-15 minutes under the condition that power may need to be reduced by 150-250 KW. Pouring may then be performed so that the nucleation assisted alloys in the molten steel are softened, but may not be in a free atom state completely.
The preparation method has the following technical effects that after the technology and the technique are adopted, the metallographic phase quality of the casting strips is improved, and the intrinsic coercivity Hcj of magnet finished products prepared from the casting strips is improved.
To enable those skilled in the art to better understand the technical solution of the present disclosure, the present disclosure will be described in detail below with reference to the accompanying drawings. The description in this section is merely exemplary and explanatory and should not have any limitation on the scope of protection of the present disclosure.
1) A formula of nucleation assisted alloys (A material) in the example was designed as: Pr—Nd28Fe69.5Co1.5B1, with an added weight percent of 5%, where the ingredients of the alloys were calculated before addition of the nucleation assisted alloys according to the design, and ingredients of the intermediate materials were obtained as follows:
Pr—Nd25.9Dy4.42FebalCo1.5B0.98M0.96 (M=Al, Cu, Nb, Ga), where M was an impurity element, and bal represented balance; and
the intermediate materials accounted for 95% in the final Nd—Fe—B casting strips (C materials). The final formula of the Nd—Fe—B casting strips (C materials) was designed as (in a weight percent): Pr—Nd26Dy4.2FebalCo1.58B0.98M0.90 (M=Al, Cu, Nb, Ga).
2) The nucleation assisted alloys (A materials) were smelted. The compounded A materials were added into a smelting crucible, vacuumizing was performed until the intensity of pressure was smaller than or equal to 0.5 Pa, and the materials were heated and baked at a low power for 20 minutes. The materials were heated and baked at the largest power of 580 KW until furnace materials were melted through visual observation. Smelting was performed for 12 minutes under the condition that the power was reduced by 100 KW. The molten steel was poured out when the temperature of the molten steel was in the range of 1430-1450° C. During pouring, the rotating speed of a copper roller wheel of a smelting furnace was about 30-35 r/min. The linear speed of a corresponding molten steel swinging position was 0.96-1.12 m/s, and casting strips with thickness of 0.25-1 millimeter were obtained.
The casting strips were crushed into particles with particle size diameter of about 1-10 mm by a mechanical crushing method as the nucleation assisted alloy particles.
3) The Nd—Fe—B casting strips (C material) were smelted. 570 Kg of the compounded intermediate materials were added into the smelting crucible, vacuumizing was performed until the intensity of pressure was smaller than or equal to 0.5 Pa, and the materials were heated and baked at a low power for 20 minutes. The materials were heated and baked at the largest power of 580 KW until the furnace materials were melted. Smelting was performed for 20 minutes after the smelting power was slightly regulated down to 480 KW. The nucleation assisted alloys, namely the materials A, were added through a special tool for later-added materials, arranged at a top end, and after the materials A were added, smelting was performed for 15 minutes after the power was regulated down to 300 KW, so that the nucleation assisted alloys, namely the materials A, in the molten steel were softened but not in a free atom state completely. The molten steel was poured out when the temperature was in the range of 1390-1400° C. During pouring, the rotating speed of the copper roller wheel of the smelting furnace was about 40-45 r/min, the linear speed of the corresponding molten steel swinging position was 1.28-1.44 m/s, and casting strips with thicknesses of 0.15-0.35 millimeter were obtained.
Finally, with the same ingredients, comparison of metallographic phases of casting strips obtained by a technique disclosed by the present disclosure and those by a traditional technology was obtained.
The Nd—Fe—B casting strips were then subjected to conventional crushing and powdering, pressing and forming, and sintering so that the Nd—Fe—B finished products were obtained. A comparison table of properties of Nd—Fe—B finished products obtained by different technologies with the same ingredients is shown in the following Table 1. 1-1 # to 1-3 # show the properties of Nd—Fe—B magnets obtained by adopting the technique disclosed by the present disclosure, and 1-4 # to 1-6 # show the properties of Nd—Fe—B magnets obtained by adopting the traditional technology.
It can be seen from
A formula of the nucleation assisted alloys (A materials) in the example was designed as Pr—Nd28Fe69.09Co2B0.91, with an added weight percent of 5%, where the ingredients of the alloys were calculated before addition of the nucleation assisted alloys according to the design, and ingredients of the intermediate materials were obtained as follows:
Pr—Nd29.47Tb1.05FebalCo2.0B0.93M0.59 (M=Al, Cu, Zr, Ga), and the intermediate materials accounted for 95 wt % in final (C materials).
The final formula of the C materials was designed as (in a weight percent): Pr—Nd29.4Tb1FebalCo2.0B0.93M0.55 (M=Al, Cu, Nb, Ga).
2) The nucleation assisted alloys (A materials) were smelted. The compounded A materials were added into the smelting crucible, vacuumizing was performed until the intensity of pressure was smaller than or equal to 0.5 Pa, and the materials were heated and baked at a low power for 20 minutes. The materials were heated and baked at the largest power of 580 KW until furnace materials were melted through visual observation. Smelting was performed for 5-10 minutes under the condition that the power was reduced by 20 -50 KW. The molten steel was poured out when the temperature of the molten steel was in the range of 1450-1480° C. During pouring, the rotating speed of a copper roller wheel of a smelting furnace was about 30-35 r/min, the linear speed of a corresponding molten steel swinging position was 0.96-1.12 m/s, and casting strips with thicknesses of 0.25-1 mm were obtained.
The casting strips were crushed into particles with particle size of about 1-10 mm by the mechanical crushing method, to be used as the nucleation assisted alloys.
3) The Nd—Fe—B casting strips (C materials) were smelted. 570 Kg of the compounded intermediate materials were added into the smelting crucible, vacuumizing was performed until the intensity of pressure was smaller than or equal to 0.5 Pa, and the materials were heated and baked at a low power for 20 minutes. The materials were heated at the largest power of 580 KW until the furnace materials were melted. Smelting was performed for 10-12 minutes after the smelting power was slightly regulated down to 450 KW. The nucleation assisted alloys, namely the A materials, were added through a special tool for later-added materials, arranged at a top end, and after the A materials were added, smelting was performed for 3-5 minutes after the power was regulated down to 300 KW so that the nucleation assisted alloys, namely the A materials, in the molten steel were softened but not in a free atom state completely. The molten steel was poured out when the temperature was in the range of 1410-1420° C. During pouring, the rotating speed of the copper roller wheel of the smelting furnace was about 40-45 r/min, the linear speed of the corresponding molten steel swinging position was 1.28-1.44 m/s, and casting strips with thicknesses of 0.15-0.35 mm were obtained.
It can be seen from
The Nd—Fe—B casting strips were then subjected to conventional crushing and powdering, pressing and forming, and sintering, so that the Nd—Fe—B finished products were obtained. A comparison table of properties of Nd—Fe—B finished products obtained by different technologies with the same ingredients is shown in the following Table 2. 2-1 # to 2-3 # shows the properties of the Nd—Fe—B magnets obtained by adopting the technique disclosed by the present disclosure, and 2-4 # to 2-6 # shows the properties of the Nd—Fe—B magnets obtained by adopting the traditional technology.
It can be seen from
| Number | Date | Country | Kind |
|---|---|---|---|
| 202110036074.0 | Jan 2021 | CN | national |
This patent application claims the benefit and priority of Chinese Patent Application No. 202110036074.0, filed on Jan. 12, 2021, the disclosure of which is incorporated by reference herein in its entirety as part of the present application.