Claims
- 1. A process for the preparation of an alkenyl aromatic-butadiene polymer, the steps of the method comprising providing a solution comprising 80 to 30 parts by weight of alkenyl aromatic monomer 20 to 70 parts by weight of butadiene, and up to 50 weight percent based on the total weight of the solution of a solvent which is generally inert under conditions of polymerization, initiating polymerization with a lithium based polymerization initiator at a temperature of from about 10.degree. to 70.degree. centigrade until about 5 to about 30 weight percent of the combined weight of alkenyl aromatic monomer and butadiene has been converted to form a rubbery alkenyl aromatic monomer-butadiene polymer containing from about 2 to 25 weight percent alkenyl aromatic monomer, terminating the polymerization and separating unreacted butadiene therefrom and initiating free radical polymerization of the alkenyl aromatic monomer present.
- 2. The process of claim 1 wherein the lithium based polymerization initiator is a butyllithium.
- 3. The method of claim 1 wherein polymerization of butadiene is initiated at a temperature of from about 30.degree. C. to about 50.degree. C.
- 4. The method of claim 1 wherein at least a portion of heat generated by polymerization of the butadiene is removed by refluxing butadiene.
- 5. The process of claim 1 wherein the alkenyl aromatic monomer is styrene.
- 6. The process of claim 4 including the step of adding styrene to the reaction mixture after the polymerization has been terminated.
- 7. The method of claim 6 including adding styrene prior to initiating free radical polymerization of the styrene.
- 8. A process for the preparation of a styrene-butadiene polymer, the steps of the method comprising providing a solution comprising 80 to 30 parts by weight of styrene, 20 to 70 parts by weight of butadiene and up to 50 weight percent based on the total weight of the solution of a solvent which is generally inert under conditions of polymerization initiating polymerization with a lithium based polymerization initiator until about 5 to about 30 weight percent of the combined weight of styrene and butadiene has been converted to from a rubbery styrene-butadiene polymer, terminating the polymerization and separating unreacted butadiene therefrom, subsequently initiating polymerization to induce polymerization of styrene until a desired quantity of styrene has been converted to styrene polymer and subsequently isolating from the reaction mixture styrene polymer reinforced with a rubbery styrene-butadiene polymer.
Parent Case Info
This application is a continuation-in-part of the copending application Ser. No. 058,704, filed July 18, 1979, now abandoned.
US Referenced Citations (9)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
58704 |
Jul 1979 |
|