Claims
- 1. A process for preparing a europium doped BaFCl phosphor comprising: (a) preparing an intimate mixture consisting essentially of particles of BaFCl having a MSED less than 2 microns, a europium source which is selected from the class consisting of EuCl.sub.3, EuCl.sub.2, EuF.sub.2, EuF.sub.3, BaFCl:Eu, and Ba.sub.7 Eu.sub.6 F.sub.32 and about 0.1-25 percent by weight, based on the weight of BaFCl, of a chloride flux of at least one water-soluble chloride selected from the group consisting of alkali metal chlorides and alkaline earth metal chlorides, (b) firing said mixture in an inert atmosphere at a temperature in the range of about 550.degree.-900.degree. C and above the liquid temperature of the flux of a time sufficient to effect reaction of europium with the BaFCl including the reduction of any Eu.sup.3+ to Eu.sup.2+ and diffusion of europium throughout the phosphor, and (c) washing the fired product with water to remove the chloride flux.
- 2. The process of claim 1 wherein the flux is at least one of KCl, NaCl, LiCl, CaCl.sub.2, BaCl.sub.2, SrCl.sub.2, and MgCl.sub.2.
- 3. The process of claim 2 wherein the firing temperature is in the range of about 600.degree.-880.degree. C.
- 4. The process of claim 3 wherein the chloride flux concentration is about 0.1-10 percent by weight.
- 5. The process of claim 3 wherein the flux is a mixture of BaCl.sub.2, CaCl.sub.2 and KCl or a mixture of BaCl.sub.2 and KCl.
- 6. The process of claim 3 wherein the intimate mixture is prepared by slurrying the BaFCl particles and Eusource particles in an aqueous solution of the chloride flux and then removing the water.
- 7. The process of claim 1 wherein the BaFCl is prepared by forming a slurry consisting of an aqueous solution of BaCl.sub.2 and solid BaF.sub.2 with the amount of BaCl.sub.2 being in excess of the stoichiometric amount needed to form BaFCl and agitating the resulting slurry for a time sufficient to allow the solid BaF.sub.2 to be replaced by particles of BaFCl.
- 8. The process of claim 7 wherein an aqueous solution of a water-soluble europium source is added to the precipitated BaFCl to form a slurry.
- 9. The process of claim 8 wherein the water-soluble europium source is EuCl.sub.3.
- 10. The process of claim 8 wherein at least one water-soluble chloride flux selected from the group consisting of KCl, NaCl, LiCl, CaCl.sub.2, BaCl.sub.2, SrCl.sub.2, and MgCl.sub.2 is added to the aqueous slurry containing the particles of BaFCl and the europium source.
- 11. The process of claim 1 wherein the time of firing is in the range of 5 to 60 minutes.
- 12. A process for preparing a europium doped BaFCl phosphor comprising: (a) forming a slurry consisting essentially of an aqueous solution of BaCl.sub.2 and solid BaF.sub.2 with the amount of BaCl.sub.2 being about 0.5-100 mole percent in excess of the stoichiometric amount needed to form BaFCl, agitating the resulting slurry for a time sufficient to allow the BaF.sub.2 to be replaced by particles of BaFCl, said particles having a MSED less than 2 microns, and removing sufficient H.sub.2 O or BaCl.sub.2 solution to entrain excess BaCl.sub.2 with the BaFCl particles, (b) intimately mixing a europium source which is selected from the class consisting of EuCl.sub.3, EuCl.sub.2, EuF.sub.2, EuF.sub.3, BaFCl:Eu and Ba.sub.7 EU.sub.6 F.sub.32 with the BaFCl, (c) drying the mixture, (d) firing the dried mixture in a nitrogen atmosphere at a temperature in the range of about 550.degree.-900.degree. C for a time sufficient to effect reaction of europium with the BaFCl including the reduction of any Eu.sup.3+ to Eu.sup.2+ and diffusion of europium throughout the phosphor, and (e) washing the fired product with water to remove excess BaCl.sub.2.
- 13. The process of claim 12 wherein the europium source is EuCl.sub.3 in aqueous solution.
- 14. The process of claim 12 wherein about 0.1-25 percent by weight, based on the weight of BaFCl, of at least one water-soluble chloride in aqueous solution is added to the europium source-BaFCl mixture, said chloride selected from the group consisting of KCl, NaCl, LiCl, BaCl.sub.2, CaCl.sub.2, SrCl.sub.2 and MgCl.sub.2.
- 15. The process of claim 14 wherein the added chloride is a mixture of CaCl.sub.2, KCl, and BaCl.sub.2, or a mixture of BaCl.sub.2 and KCl.
- 16. The process of claim 13 wherein about 0.1-25 percent by weight, based on the weight of BaFCl, of at least one water-soluble chloride in aqueous solution is added to the mixture of the europium source and BaFCl, said chloride selected from the group consisting of KCl, NaCl, LiCl, BaCl.sub.2, CaCl.sub.2, SrCl and MgCl.sub.2.
- 17. The process of claim 16 wherein the added chloride is a mixture of CaCl.sub.2, KCl and BaCl.sub.2 or a mixture of BaCl.sub.2 and KCl.
- 18. The process of claim 12 wherein the time of firing is in the range of 5 to 60 minutes.
CROSS REFERENCES TO RELATED APPLICATIONS
This application is a continuation-in-part of application Ser. No. 683,396, filed May 5, 1976, and now abandoned.
US Referenced Citations (4)
Foreign Referenced Citations (3)
Number |
Date |
Country |
896,453 |
Mar 1972 |
CA |
2,541,748 |
Apr 1976 |
DT |
1,419,169 |
Dec 1970 |
UK |
Non-Patent Literature Citations (2)
Entry |
Stevels "Philips Research Reports", vol. 30, No. 5, Oct. 1975, pp. 277-290. |
Leverenz "An Introduction to Lumini of Solids", John Wiley & Sons, 1950, pp. 78-79. |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
683396 |
May 1976 |
|