Claims
- 1. A process for producing a crystalline aluminosilicate zeolite characterized by having (a) a silica/alumina mole ratio of from 10 to 100, (b) X-ray lattice distances d shown in Table A of the specification, (c) a specific n-hexane adsorption, as measured on a precisely weighed sample of the zeolite which has been calcined at 450.degree. for 8 hours until the pressure reaches 50.+-.1 mm Hg, and maintained at 20.+-.1.degree. C. for 2 hours of at least 0.07 g/g, (d) a (2-methylpentane/cyclohexane) adsorption ratio of from 1.2 to 1.6, and (e) when the intensity (I.sub.o) of the X-ray diffraction peak at d(.ANG.)=3.86 is taken as 100, the relative intensity (I/I.sub.o) of the X-ray diffraction peak at d(.ANG.)=3.83 is at least 70, which comprises maintaining a silica source, an alumina source, and a seed zeolite selected from the group consisting of zeolite ZSM-5 and zeolites having said characteristics (a)-(e) inclusive, specified above, in an aqueous solution containing 1 to 200 millimoles, per gram of said zeolite, of an alkali metal hydroxide, in such proportions that the silica source, the alumina source and the alkali metal hydroxide satisfy the following mole ratios in terms of SiO.sub.2, Al.sub.2 O.sub.3 and OH-:
- SiO.sub.2 /Al.sub.2 O.sub.3 =5-100
- OH-/(SiO.sub.2 +Al.sub.2 O.sub.3 =about 0.5-1 and
- OH-/H.sub.2 O=0.005-0.05,
- and under such temperature, pressure and time conditions as to produce a crystalline aluminosilicate zeolite.
- 2. The process of claim 1 wherein the seed zeolite is zeolite ZSM-5.
- 3. The process of claim 1 or 2 wherein the amount of the alkali metal hydroxide in the aqueous solution is 5 to 100 millimoles per gram of the seed zeolite.
- 4. The process of claim 1 wherein the alkali metal hydroxide is sodium hydroxide, potassium hydroxide, or both.
- 5. The process of claim 1 wherein the proportions of the silica source and the alumina source are such that 0.1 to 200 millimoles of SiO.sub.2 and 0.01 to 20 millimoles of Al.sub.2 O.sub.3 are used per gram of seed zeolite.
- 6. The process of claim 5 wherein the proportions of the silica source and the alumina source are such that 1 to 100 millimoles of SiO.sub.2 and 0.1 to 10 millimoles of Al.sub.2 O.sub.3 are used per gram of the seed zeolite.
- 7. The process of claim 1 wherein the silica source is selected from the group consisting of a silica powder, colloidal silica, water-soluble silicon compounds and silica acid.
- 8. The process of claim 1 wherein the alumina source is selected from the group consisting of alumina, mineral acid salts of aluminum and aluminate salts.
- 9. The process of claim 1 wherein the aluminosilicate is used as a common source of silica and alumina.
- 10. The process of claim 1 wherein the temperature is in the range of 90.degree. to 250.degree. C.
- 11. The process of claim 1 wherein the pressure is at least the autogenous pressure in an autoclave.
- 12. The process of claim 1 wherein the proportions of the silica source, the alumina source and the alkali metal hydroxide are such that the SiO.sub.2 /Al.sub.2 O.sub.3 mole ratio is from 10 to 80, the OH-(SiO.sub.2 +Al.sub.2 O.sub.3) mole ratio is from about 0.5 to 1 and the OH-/H.sub.2 O mole ratio is from 0.01 to 0.04.
- 13. The process of claim 1 wherein the relative intensity (I/I.sub.o) is 73 to 78.
- 14. The process of claim 13 wherein the crystalline aluminosilicate zeolite product has a (2-methylpentane/cyclohexane) adsorption ratio of from 1.25 to 1.45.
Priority Claims (1)
Number |
Date |
Country |
Kind |
57-83240 |
May 1982 |
JPX |
|
Parent Case Info
This is a continuation of application Ser. No. 06/891,063 filed July 31, 1986, whereby in turn is a continuation of application Ser. No. 757,928, filed July 23, 1985, which is in turn a continuation of application Ser. No. 495,825, filed May 18, 1983, which in turn are all now abandoned.
US Referenced Citations (6)
Foreign Referenced Citations (2)
Number |
Date |
Country |
7512644 |
May 1976 |
NLX |
7512645 |
May 1976 |
NLX |
Continuations (3)
|
Number |
Date |
Country |
Parent |
891063 |
Jul 1986 |
|
Parent |
757928 |
Jul 1985 |
|
Parent |
495825 |
May 1983 |
|