Patent Grant
9687818
This invention relates to a production method of a precious metal catalyst. Furthermore, the present invention relates to the catalyst as such and its use as diesel oxidation catalyst.
Exhaust gas emitted from an internal combustion engine such as an automobile engine contains carbon monoxide (CO), hydrocarbons (HC), nitrogen oxides (NOx), and so forth. These detrimental substances are generally purified by an exhaust gas purification catalyst in which a catalyst component mainly consisting of a precious metal such as platinum (Pt), rhodium (Rh), palladium (Pd), iridium (Ir), etc., is supported by an oxide support such as alumina.
To support the precious metal of the catalyst component on the oxide support, a method is generally used which involves the steps of using a solution of a precious metal compound optionally modified, allowing the oxide support to be impregnated with this solution so as to disperse the precious metal compound on the surface of the oxide support, and baking the oxide support. Materials having a high specific surface area such as gamma-alumina are generally employed for the oxide support to give a large contact area with the catalyst component to the exhaust gas.
It is known that the performance of supported metal catalysts depends on the structure and composition of the metal nanoparticles they contain, and the nature of the support.
Though simple, conventional impregnation methods used for the preparation of supported catalysts often provide limited control over the structure of the resulting materials (i.e. average particle size, particle composition and location of the active components).
In order to overcome such disadvantages, published literature describes the use of alternative synthetic routes such as the use of organometallic molecular carbonyl cluster precursors as well as methods involving the use of templating agents (e.g. surfactants and polymers). The potential advantages of using metal carbonyl clusters as precious metal source for catalytic applications lay in the high metal dispersions and homogeneity in particle size composition due to the relatively low temperature of the activation procedure and, when using heterometallic cluster precursors, to the preformed heterometallic bonds. However, the limited stability of such clusters on the surfaces of various supports, as well as difficulties in their synthesis and handling makes the use of cluster-derived catalysts problematic for large-scale applications.
On the other side, synthetic routes based on the use of templating agents offer the possibility to prepare colloidal metal nanoparticles with controlled particle size and composition. The synthetic steps for the preparation of supported metal catalysts through colloidal routes commonly involve the interaction between the metal precursors and the protective agent followed by a reduction treatment leading to the formation of a metal colloidal suspension. Such metal suspension can be then deposited onto the support surface and finally the protective agent removed to expose the nanoparticles to the reactants.
Few examples are reported in the literature describing the use of polymer-stabilized precious metal colloids as precursors for the preparation of supported metal catalysts where improved metal dispersions with respect to conventional methods are achieved.
Liu et al. (Polym. Adv. Technol. 1996, 7, 634) describe the deposition of Poly vinylpyrrolidone—(PVP) and polyvinylalcohol—(PVA) protected Pt and Pd nanoparticles on SiO2 surface. However, such surface needed to be pretreated by pre-adsorption of poly acrylic acid to ensure deposition of the polymer-capped nanoparticles.
Pd colloidal suspensions were prepared by Burton et al. (Top. Catal. 2008, 49, 227-232) by heating up to 300° C. a suitable Pd precursor in a triclyphosphine or in an octylamine solution. The obtained particle were then washed with hexane and deposited onto an oxidic support followed by calcination of support in order to remove the capping agent.
Higher purification performance of the exhaust gas has been further required for such an exhaust gas purification catalyst for the environmental protection. Control of the cluster size of the precious metal to an optimal size is one way. According to the supporting method of the precious metal of the prior art which uses a solution of the precious metal compound, the precious metal is adsorbed on the oxide support at an atomic level in which the precious metal compound is dispersed to the surface of the oxide support, but the atoms of the precious metal move and invite grain growth in the baking process in which the precious metal is firmly supported. It has therefore been extremely difficult to support only the precious metal of a desired cluster size on the oxide support.
Japanese Unexamined Patent Publication (Kokai) No. 2003-181288 proposes a method for supporting a precious metal on an oxide support by introducing the precious metal into pores of a hollow carbon material such as a carbon nano-horn or a carbon nano-tube so that the precious metal forms a cluster having a desired size, instead of directly supporting the precious metal on the oxide support, fixing the precious metal to the carbon material, then baking them together and thereafter burning and removing the carbon material and at the same time, supporting the precious metal on the oxide support.
According to such a method, the precious metal exists inside the pores of the carbon material until the carbon material is burnt and removed, and when the carbon material is burnt and removed, the precious metal is quickly supported on the oxide support. Therefore, the precious metal can be substantially supported by the oxide support at a cluster size inside the pores of the carbon material. However, this method is not free from problems in which the precious metal must be introduced into the pores of the hollow carbon material, which results in low productivity.
Torigoe, Esumi et al. proposes in “Chemical Industry”, pp. 276-296 (1998) to produce precious metal particles having particle sizes in the order of nm by reducing a mixed solution of a polymer compound such as polyvinyl pyrrolidone and precious metal ions by using a reducing agent such as H2, NaBH4, C2H5OH, or the like.
However, when a compound is used as the reducing agent in the method described above, there is a problem that an element or elements are contained in the compound mix as impurities in the final precious metal particles. When NaBH4 is used as the reducing agent, for example, Na and B mix. When an alcohol is used as the reducing agent, not only the alcohol, but also ketones, aldehydes, carboxylic acids, etc., formed while the alcohol is oxidised during the reduction of the metal ions, may mix. When hydrogen is used as the reducing agent, problems occur in that the particle diameter of the resulting precious metal particles becomes large and the particles are odd-shaped.
WO 2004/089508 provides a method of preparing an oxidation catalyst for oxidizing volatile organic fraction and a catalyzed wall-flow filter for use in removing soot particulates from diesel engine exhaust, including preparing a PGM salt and a transition/alkali metal salt with a water-soluble polymer compound and a reducing agent, to obtain a first colloidal solution, which is then washcoated to a catalyst-support-coated monolithic ceramic substrate, followed by calcination process at high temperatures, to obtain an oxidation catalyst; and treating a PGM salt and a metal salt mixture including at least one selected from a first group of catalyst metal to increase oxidation activity for nitrogen monoxide (NO) and at least one selected from a second group of catalyst metal to decrease a combustion temperature of soot particulates by oxidizing agents, such as nitrogen dioxide and oxygen, with a water-soluble polymer compound and a reducing agent, to obtain a second colloidal solution, which is then washcoated on a catalyst-support-coated wall-flow filter, followed by calcination process at high temperatures, to obtain a catalyzed wall-flow filter.
WO 95/32790 relates generally to the control of hydrocarbons, carbon monoxide, and nitrogen oxides in the exhaust of internal combustion engines. More particularly, the invention relates to the removal of NO when the exhaust gases include oxygen substantially in excess of that needed for combustion of the fuel. This is for example the case with lean burn engines, diesel engines, and other engines currently under development.
US 2008/0268159 relates to a production method of a precious metal catalyst. More specifically, the present invention relates to a production method of a precious metal catalyst the cluster size of which is controlled. US 2008/0628159 provides a production method of a precious metal catalyst including the steps of uniformly mixing a solution containing a precious metal and an aqueous solution of a polymer compound capable of coordination with the precious metal to form a complex of the precious metal and the polymer compound, adding the drop-wise aqueous solution containing the complex to water containing micro-bubbles containing therein hydrogen, mixing the solutions to reduce the precious metal, supporting the mixed solution on a support and baking the solution.
The processes known from the state of the art have several disadvantages, like for example the use of several steps procedures to obtain the final catalyst, limited control over the colloidal nanoparticles location upon impregnation on a support-coated wall-flow filter, the use of high temperature treatment for the formation of the colloidal suspension or the use of a H2 micro-bubble generator, which have limited life time in solution. These disadvantages limit the applicability of the method and the productivity.
The present invention provides a process for preparing a catalyst avoiding the disadvantages of the processes known from the state of the art.
The present invention is directed to a process for preparing a catalyst. In particular, the present invention is directed to a process for preparing a catalyst, at least comprising the steps:
According to a further aspect, the present invention is directed to a catalyst obtainable by a process according to the present invention.
Furthermore, the present invention is directed to the use of a catalyst obtainable by a process according to the present invention or of a catalyst the present invention as diesel oxidation catalyst.
The present invention is directed to a process for preparing a catalyst. In particular, the present invention is directed to a process for preparing a catalyst, at least comprising the steps:
According to the process of the present invention, a catalyst is obtained which contains highly dispersed metal particles on a support material.
The present invention improves the state of the art described above by reducing the number of preparations steps. This results in an improved process and reduced costs.
Furthermore, the process according to the present invention can be carried out without inert atmosphere, thus eliminating the need of purge gasses or inert atmospheres upon dissolution and interaction of the metal salt precursor with the protective agent.
Using the process of the present invention, it is possible to obtain deposition of the metal nanocomposites onto the surface of the support by simplified control over the physico-chemical properties (i.e. pH) of the metal colloidal solutions used as precursor.
The use of additional polymers and or solvents to the aqueous solution to obtain a more homogeneous metal dispersion and metal nanoparticle composition with respect to conventional methods can be avoided.
Finally, the need of multiple metal/protective agent interactions steps and/or reductions steps to form highly dispersed Pt/Pd nanoparticles with homogeneous composition are eliminated according to the present invention. According to the present invention the composition of the resulting Pt/Pd particles is controlled by the relative Pt/Pd amount used in the preparation.
The catalysts obtained by the process according to the present invention show improved catalytic activity of the resulting materials even after hydrothermal treating at 800° C. for 12 h.
The process according to the present invention comprises steps (1) to (5). According to step (1), a protecting agent is added to an aqueous solution of a metal precursor to give a mixture (M1).
As a metal precursor, any suitable compound can be added which is soluble in water, i.e. which is suitable to prepare an aqueous solution of the metal precursor. Suitable compounds are for example metal salts. Preferably, a suitable compound of a metal selected from the group consisting of platinum, palladium, rhodium, gold and silver or mixtures thereof is used. For example metal salts of platinum, palladium, rhodium, gold and silver or mixtures thereof are used in the process of the present invention. In particular, the metal is palladium or platinum.
According to one embodiment, the present invention is therefore directed to a process for preparing a catalyst as disclosed above, wherein the metal precursor is selected from metal salt of platinum, palladium, rhodium, gold and silver or mixtures thereof.
An aqueous solution of the metal precursor is used in step (1). According to the present invention, the concentration of the metal in the aqueous solution of the metal precursor is preferably in the range of from 1*10−6 to 4.6*10−5 mol metal per mol solution, more preferably in the range of from 5*10−6 to 4.3*10−5 mol metal per mol solution, more preferably in the range of from 1*10−5 to 3.9*10−5 mol metal per mol solution, more preferably in the range of from 1.8*10−5 to 3.6*10−5 mol metal per solution.
As a protecting agent, any suitable compound can be used in the context of the present invention. Suitable protecting agents are for example soluble homo- and co-polymers having one or more amino, amido, carboxylic, aldehydic, or hydroxyl groups, and organic molecules having one or more amino, amido, carboxylic, aldehydic, or hydroxyl groups and mixtures thereof.
According to a further embodiment, the present invention is therefore directed to a process for preparing a catalyst as disclosed above, wherein the protecting agent is selected from soluble homo- and co-polymers having one or more amino, amido, carboxylic, aldehydic, or hydroxyl groups, and organic molecules having one or more amino, amido, carboxylic, aldehydic, or hydroxyl groups and mixtures thereof.
Preferred protecting agents are for example selected from poly(vinylalcohol), poly(vinylpyrrolidone), poly(ethyleneimine), poly(acrylic acid), carbohydrates or alkali metal citrates. Therefore, according to a preferred embodiment, the present invention is therefore directed to a process for preparing a catalyst as disclosed above, wherein the protecting agent is selected from poly(vinylalcohol), poly(vinylpyrrolidone), poly(ethyleneimine), poly(acrylic acid), carbohydrates or alkali metal citrates.
According to the present invention, suitable ratios between the metal precursor and the protective agent are in the range of from 1:1 to 1:10 when calculated as ratio between a mol of precious metal and the unit of the protective agent. Preferred ratios between a mol of metal precursor and a unit of protective agent are in the range of from 1:2 to 1:4.
Preferably, the reaction is carried out at ambient pressure at a temperature of from 15 to 35° C., more preferably at a temperature of from 20 to 30° C., more preferably at room temperature. It is preferred to carry out the reaction under stirring. According to the present invention, mixtures are obtained by preferably mixing two or more solutions comprising the same or different precious metal components. However, it is also possible that preformed mixtures are used.
In step (1) of the process according to the present invention, mixture (M1) is obtained. According to step (2), a reducing agent is added to mixture (M1) to give a mixture (M2).
In principle, any suitable reducing agent can be used in the process according to the present invention. Preferably, the reducing agent is selected from alkali metal borohydrides, hydrazine, formaldehyde, alkali metal citrates, amino borane complexes, gaseous hydrogen and carbon monoxide.
Therefore, according to a further embodiment, the present invention is therefore directed to a process for preparing a catalyst as disclosed above, wherein the reducing agent is selected from alkali metal borohydrides, hydrazine, formaldehyde, alkali metal citrates, amino borane complexes, gaseous hydrogen and carbon monoxide.
Suitable ratios between the metal precursor and the reducing agent are in the range of from 1:1 to 1:20 when calculated as ratio between a mol of precious metal and a mol of the reducing agent. Preferred ratios between a mol of metal precursor and a mol of reducing agent are in the range of from 1:2 to 1.8. Depending from the reducing agent the reaction can be carried out at room temperature under stirring.
Mixtures thus obtained could be also constituted by mixing two or more (M2) mixtures comprising the same or different precious metal components. Such solutions could be obtained also by mixing two or more (M1) solutions, which are obtained in step (1) by addition of the same or different protective agent, followed by addition of the same or different reducing agent. Additionally, mixture (M2) can be obtained by mixing one or more mixtures (M2) with one ore more mixtures (M1) followed by addition of a reducing agent.
In step (2), the mixture (M2) is obtained. To this mixture, a support material is added to give a mixture (M3).
In principle, any suitable support material can be used in the process according to the present invention. Preferred support materials are for example aluminum oxide, silicon oxide, cerium oxide, zirconium oxide, titanium oxide, magnesium oxide alone or as mixtures and/or solid solutions from these support materials.
According to a further embodiment, the present invention is therefore directed to a process for preparing a catalyst as disclosed above, wherein the support material is selected from aluminum oxide, silicon oxide, cerium oxide, zirconium oxide, titanium oxide, magnesium oxide alone or as mixtures and/or solid solutions from these support materials.
Suitable amounts of the support material are chosen to have a final precious metal concentration on the support in the range of from 0.01% to 10% wt/wt with respect to the resulting material. Preferred concentrations of the precious metal on the support material are in the range of from 0.1% to 5% wt/wt with respect to the support material.
According to the present invention, the support material is added to the mixture at room temperature while the mixture is stirring.
According to step (4) of the process of the present invention, the pH of mixture (M3) obtained in step (3) of the process of the present invention is adjusted. The pH is preferably adjusted to a value in the range from 2 to 7. Thus, according to a further embodiment, the present invention is directed to a process for preparing a catalyst as disclosed above, wherein in step (4) the pH is adjusted to a value in the range from 2 to 7.
According to the present invention, the pH can be adjusted by any suitable method for example by addition of a suitable acid, in particular a mineral acid like HCl or HNO3.
According to the present invention, the pH adjustment is preferably carried out at room temperature while the solution is stirred.
In step (5) of the process of the present invention, the solid and liquid phases of mixture (M3) are separated. Separation can be achieved by any suitable method, for example filtration or centrifugation or evaporation of the solvent. According to a further embodiment, the present invention is therefore directed to a process for preparing a catalyst as disclosed above, wherein in step (5) the solid and liquid phase of mixture (M3) are separated by filtration or evaporation of the solvent.
The process according to the present invention can also comprise additional steps, for example heating or cooling steps or steps for altering the concentration of any of the mixtures obtained in the process of the present invention. The additional steps can be carried out before or after steps (1) to (5) or between any of the steps (1), (2), (3), (4), and/or (5) of the process of the present invention.
According to the process of the present invention, a catalyst is obtained which has highly dispersed nanoparticles with homogeneous composition.
The catalysts obtained by the process according to the present invention show improved catalytic activity of the resulting materials even after hydrothermal treating at 800° C. for 12 h.
Therefore, according to a further aspect, the present invention is directed to a catalyst obtainable and/or obtained by a process as disclosed above.
The catalyst according to the present invention comprises a support material and highly dispersed metal nanoparticles.
Preferably, the support material is selected from preferred support materials as mentioned above, for example aluminum oxide, silicon oxide, cerium oxide, zirconium oxide, titanium oxide, magnesium oxide alone or as mixtures and/or solid solutions from these support materials.
The metal is preferably selected from platinum, palladium, rhodium, gold and silver or mixtures thereof, more preferred platinum and palladium or mixtures thereof.
The catalysts according to the present invention have improved properties. For example for a catalyst comprising only platinum as metal, after treatment of the catalyst at 450° C. for a desired period of time in an oxidizing atmosphere (air), no less than 65% of the metal particles have an average diameter below 3 nm. Also for a catalyst comprising only platinum as metal, after treatment of the obtained catalyst at 800° C. for 12 h in an oxidizing atmosphere (10% H2O in air), no less than 22% of the metal particles have an average diameter below 22 nm.
For a catalyst comprising platinum and palladium as metals, after treatment of the obtained catalyst at 800° C. for 12 h in an oxidizing atmosphere (10% H2O in air), no less than 36% of the metal particles have an average diameter below 22 nm. Furthermore, for a catalyst comprising platinum and palladium as metals, after treatment of the obtained catalyst at 800° C. for 12 h in an oxidizing atmosphere (10% H2O in air), no less than 90% of the metal particles are constituted by both Pt and Pd.
The catalysts obtained according to the process according to the present invention or the catalysts according to the present invention are in particular suitable as diesel oxidation catalysts, in particular due to the improved thermal resistance and reduced metal particle grain growth during hydrothermal aging conditions simulating the lean aging conditions typically encountered during the operation of a diesel engine. Therefore, according to a further aspect, the present invention is directed to the use of a catalyst obtainable and/or obtained by a process according to the present invention as diesel oxidation catalyst. Also, the present invention relates to a process for oxidizing diesel exhaust wherein the diesel exhaust is brought into contact with a catalyst obtainable and/or obtained by a process according to the present invention.
Such catalyzed soot filter of the present invention can be used in an integrated emission treatment system, in particular in an exhaust conduit comprising one or more additional components for the treatment of diesel exhaust emissions. For example, such exhaust conduit which is most preferably in fluid communication with the diesel engine may comprise a catalyzed soot filter according to the present invention and may further comprise a diesel oxidation catalyst (DOC) article and/or a selective catalytic reduction (SCR) article and/or an NOx storage and reduction (NSR) catalytic article. Most preferably, the DOC article and/or the SCR article and/or the NSR article are in fluid communication with the catalyzed soot filter. The diesel oxidation catalyst can be located upstream or downstream from the catalyzed soot filter and/or selective catalytic reduction component. More preferably, the catalyzed soot filter of the present invention is located downstream from the DOC article. Still more preferably the catalyzed soot filter of the present invention is located either upstream or downstream of the SCR article.
Even more preferably, downstream the inventive catalyzed soot filter, there is no NOx reduction catalytic article comprised in the system, preferably no NOx storage and reduction (NSR) catalytic article.
A suitable SCR article for use in the exhaust conduit is typically able to catalyze the reaction of O2 with any excess NH3 to N2 and H2O, so that NH3 is not emitted to the atmosphere. Useful SCR catalyst compositions used in the exhaust conduit should also have thermal resistance to temperatures greater than 650° C. Such high temperatures may be encountered during regeneration of the upstream catalyzed soot filter. Suitable SCR articles are described, for instance, in U.S. Pat. No. 4,961,917 and U.S. Pat. No. 5,516,497. Suitable SCR articles include one or both of an iron and a copper promoter typically present in a zeolite in an amount of from about 0.1 to 30 percent by weight, preferably from about 1 to 5 percent by weight, of the total weight of promoter plus zeolite. Typical zeoites may exhibit a CHA framework structure.
The inventive catalyzed soot filter can be arranged downstream of the DOC. In such an arrangement, the inventive catalyzed soot filter provides the advantage that HC and CO are reduced during soot combustion which is most preferably achieved by the upstream zone of the inventive filter. Further, the specific design of the rear zone ensures that in the downstream zone of the catalyzed soot filter, as low an amount of NOx as possible is generated. Thus, downstream such DOC, the inventive catalyzed soot filter can be very advantageous in its clean-up function for the treatment of diesel exhaust.
Also, the present invention relates to the catalyzed soot filter as defined above for use in a method of treating a diesel engine exhaust stream, the exhaust stream containing soot particles, said method comprising contacting the exhaust stream with the catalyzed soot filter, preferably after having directed the exhaust stream through a diesel oxidation catalyst (DOC), said DOC preferably comprising a flow through substrate or a wall flow substrate. Similarly, the present invention relates to the use of the catalyzed soot filter as defined above for treating a diesel engine exhaust stream, the exhaust stream containing soot particles, wherein the exhaust stream is contacted with the catalyzed soot filter, preferably after having directed the exhaust stream through a diesel oxidation catalyst (DOC), said DOC preferably comprising a flow through substrate or a wall flow substrate.
Further, the present invention relates to a system for treating for treating a diesel engine exhaust stream, the system comprising an exhaust conduit in fluid communication with the diesel engine via an exhaust manifold;
a catalyzed soot filter as defined above; and
one or more of the following in fluid communication with the catalyzed soot filter: a diesel oxidation catalyst (DOC), a selective catalytic reduction (SCR) article, an NOx storage and reduction (NSR) catalytic article.
Preferably, in this system, the catalyzed soot filter is arranged downstream of the DOC. More preferably, the system does not contain an NOx reduction catalytic article, and more preferably, the system does not contain an NOx storage and reduction (NSR) catalytic article.
Therefore, the present invention also relates to a method of treating a diesel engine exhaust stream, the exhaust stream containing soot particles, said method comprising contacting the exhaust stream with a catalyzed soot filter as defined above, preferably after having directed the exhaust stream through a diesel oxidation catalyst (DOC), said DOC preferably comprising a flow through substrate or a wall flow substrate.
According to an optional embodiment of the present invention, this method further comprises directing the exhaust stream resulting from the DOC or from the catalyzed soot filter through a selective catalytic reduction (SCR) article.
In particular, the present invention is characterized by the following embodiments, including the specific combinations of individual embodiments given by the respective back-references:
The present invention is further illustrated by way of the following examples.
10.2 g of an H2PtCl6 solution containing 5.1*10−2 moles of Pt per liter of solution were diluted in 400 ml of water and an opportune amount of a PVP solution containing 10 mg of PVP per ml of solution was added in order to achieve a Pt/PVP weight ratio equal to 1. After letting the solution stir at room temperature in air for 1 hour, NaBH4 was added to the solution at room temperature. The amount of NaBH4 was chosen in order to have a Pt/NaBH4 weight ratio of ½. Following stirring for 1 hour in air of the obtained mixture, an appropriate amount of alumina powder was added to the solution in order to achieve a total metal loading of 1% wt/wt and the pH adjusted to a value of 2.4 with an HCl solution containing 15% HCl in weight. After 30 minutes of stirring the solution was filtered and the solid powder recovered.
The same process and quantities of reagents were used as in Example 1 with the exception of the PVP addition. Here an opportune amount of PVP solution containing 10 mg of PVP per mg of solution was added in order to achieve a Pt/PVP weight ratio equal to 2.
The same process and quantities of reagents were used as in Example 2 with the exception that 6.6 g of an H2PtCl6 solution containing 5.1*10−2 moles of Pt per liter of solution were diluted in 400 ml of water together with 110 mg of K2PdCl4.
As one can see from
6.6 g of an H2PtCl6 solution containing 5.1*10−2 moles of Pt per liter of solution were diluted in 400 ml of water and an opportune amount of a PVP solution containing 10 mg of PVP per ml of solution was added in order to achieve a Pt/PVP weight ratio equal to 1. After letting the solution stir at room temperature in air for 1 hour, NaBH4 was added to the solution at room temperature. The amount of NaBH4 was chosen in order to have a Pt/NaBH4 weight ratio of ½. The resulting solution was stirred for 30 minutes and then 110 mg of K2PdCl4 were added to the solution. After 30 minutes, NaBH4 was added to the solution at room temperature. The amount of NaBH4 was chosen in order to have a Pd/NaBH4 weight ratio of ½. Following stirring for 1 hour in air of the obtained mixture, an appropriate amount of alumina powder was added to the solution in order to achieve a total metal loading of 1% wt/wt and the pH adjusted to a value of 2.4 with an HCl solution containing 15% HCl in weight. After 30 minutes of stirring the solution was filtered and the solid powder recovered.
The same process and quantities of reagents were used as in Example 4 with the exception that the order of addition of H2PtCl6 and of K2PdCl4 has been inverted.
The same process and quantities of reagents were used as in Example 1 with the exception of the PVP addition. Here an opportune amount of PVP solution containing 10 mg of PVP per mg of solution was added in order to achieve a Pt/PVP weight ratio equal to 4.
The same process and quantities of reagents were used as in Example 1 with the exception of the H2PtCl6 and support quantities which were chosen to obtain a catalyst having 2% wt/wt of precious metal with respect to the support.
The same process and quantities of reagents were used as in Example 3 with the exception of the H2PtCl6, K2PdCl4 and alumina quantities which were chosen to obtain a catalyst having 4% wt/wt of precious metal with respect to the support.
Referring to
As one can see, in
Referring to
As one can see, in
At the beginning of the light-off test, the powder sample was equilibrated in the gas mixture for 20 minutes at 50° C. The temperature at which 50% conversion was observed is denoted as T50 and was used as the measure of catalyst activity: the lower the 150, the better the catalyst performance. The activity after thermal aging for 12 h at 800° C. of the samples prepared according to the process of the invention as outlined in Example 2, Example 3, Example 7 and Example 8, was compared to that of samples prepared according to state of the art impregnation incipient wetness methods (IW) from the same precious metal precursors, deposited on the same support material and having the same precious metal content as in Example 2, Example 3, Example 7 and Example 8.
As one can see, the catalytic activity of the samples prepared according to the process of invention is higher than that of the samples prepared according to state of the art impregnation methods as indicated by the lower T50 value of CO in the feed stream used for the evaluation.
This application is a divisional of U.S. application Ser. No. 12/844,287, filed on Jul. 27, 2010, which claims priority to U.S. provisional patent application No. 61/231,427, filed on Aug. 5, 2009, all of which are incorporated herein by reference in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4532228 | Golino et al. | Jul 1985 | A |
| 4536482 | Carcia | Aug 1985 | A |
| 5208207 | Stonehart | May 1993 | A |
| 5439865 | Abe | Aug 1995 | A |
| 5897846 | Kharas et al. | Apr 1999 | A |
| 6030921 | Ziemer | Feb 2000 | A |
| 6440378 | Hirata et al. | Aug 2002 | B1 |
| 7166555 | Shustack et al. | Jan 2007 | B2 |
| 7229597 | Patchett et al. | Jun 2007 | B2 |
| 7381683 | Wang | Jun 2008 | B1 |
| 7390770 | Nochi et al. | Jun 2008 | B2 |
| 7431749 | Kim et al. | Oct 2008 | B2 |
| 7550117 | Alward et al. | Jun 2009 | B2 |
| 7572416 | Alward et al. | Aug 2009 | B2 |
| 7601662 | Bull et al. | Oct 2009 | B2 |
| 7601670 | Yasuda et al. | Oct 2009 | B2 |
| 7605109 | Jia | Oct 2009 | B1 |
| 7611680 | Jia | Nov 2009 | B2 |
| 7673448 | Voss et al. | Mar 2010 | B2 |
| 7709407 | Hao | May 2010 | B1 |
| 7709414 | Fujdala | May 2010 | B2 |
| 7722829 | Punke et al. | May 2010 | B2 |
| 7745367 | Fujdala | Jun 2010 | B2 |
| 20050031514 | Patchett et al. | Feb 2005 | A1 |
| 20050042151 | Alward et al. | Feb 2005 | A1 |
| 20050121044 | Banerjee | Jun 2005 | A1 |
| 20060165910 | Kodas | Jul 2006 | A1 |
| 20060188416 | Alward et al. | Aug 2006 | A1 |
| 20070014710 | Gerlach | Jan 2007 | A1 |
| 20070041881 | Voss et al. | Feb 2007 | A1 |
| 20070104623 | Dettling et al. | May 2007 | A1 |
| 20070160899 | Atanassova | Jul 2007 | A1 |
| 20080045405 | Beutel et al. | Feb 2008 | A1 |
| 20080127638 | Vaarkamp et al. | Jun 2008 | A1 |
| 20080132405 | Patchett et al. | Jun 2008 | A1 |
| 20080141661 | Voss et al. | Jun 2008 | A1 |
| 20080171650 | Alward et al. | Jul 2008 | A1 |
| 20080187477 | Nochi et al. | Aug 2008 | A1 |
| 20080268159 | Hirata | Oct 2008 | A1 |
| 20090011177 | Kubo et al. | Jan 2009 | A1 |
| 20090155134 | Li | Jun 2009 | A1 |
| 20090255241 | Patchett et al. | Oct 2009 | A1 |
| 20090257933 | Chen et al. | Oct 2009 | A1 |
| 20090274602 | Alward et al. | Nov 2009 | A1 |
| 20100124523 | Chen et al. | May 2010 | A1 |
| 20100263358 | Chen et al. | Oct 2010 | A1 |
| 20110034331 | Kikuchi | Feb 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 101069850 | Nov 2007 | CN |
| 0 457 480 | Nov 1991 | EP |
| 1 611 952 | Jan 2006 | EP |
| 1 886 726 | Feb 2008 | EP |
| 2 452 750 | May 2012 | EP |
| H02-141508 | May 1990 | JP |
| H07-100380 | Apr 1995 | JP |
| 2003-181288 | Jul 2003 | JP |
| 2003-299957 | Oct 2003 | JP |
| 2005-052718 | Mar 2005 | JP |
| 2005-262162 | Sep 2005 | JP |
| 2008-049336 | Mar 2008 | JP |
| 2008-529775 | Aug 2008 | JP |
| 10-2004-00894 68 | Oct 2004 | KR |
| WO-9532790 | Dec 1995 | WO |
| WO 9832956 | Jul 1998 | WO |
| WO-2004089508 | Oct 2004 | WO |
| WO 2005063390 | Jul 2005 | WO |
| WO-2009020957 | Feb 2009 | WO |
| WO-2009079557 | Jun 2009 | WO |
| WO-2010083313 | Jul 2010 | WO |
| WO-2010083315 | Jul 2010 | WO |
| WO-2010083357 | Jul 2010 | WO |
| WO-2010114873 | Oct 2010 | WO |
| Entry |
|---|
| Partial translation of CN-101069850. |
| Burton, Patrick D. et al., “Synthesis and Activity of Heterogeneous Pd/A12O3 and Pd/ZnO Catalysts Prepared from Colloidal Palladium Nanoparticles”, Top. Catal. 49 2008, 227-232 pgs. |
| Torigoe, Esumi et al., “Chemical Industry”, 1996, 269-277 pgs. |
| Wang, Yuan et al., “Immobilization of Polymer-protected Metal Colloid Catalysts by the Formation of Polymer Hydrogen Bond Complexes”, Polymers for Advanced Technologies, vol. 7 1996, 634-638 pgs. |
| Number | Date | Country | |
|---|---|---|---|
| 20140044627 A1 | Feb 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61231427 | Aug 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12844287 | Jul 2010 | US |
| Child | 14058559 | US |