Preparation of electrically conductive polymers

Abstract

A process for the preparation of electrically conductive polymers by polymerizing acenaphthylene, N-vinyl-heterocyclics, eg. N-vinylcarbazole or N-vinylpyridine, or N,N-divinylaniline at from -80.degree. to +100.degree. C. in the presence of a cationtic catalyst, wherein from 1 to 50 percent by weight of an oxidizing Lewis acid, preferably FeCl.sub.3, FeBr.sub.3, SbCl.sub.5, SbF.sub.5, AsF.sub.5 or CF.sub.3 -SO.sub.3 H, or a combination of AlCl.sub.3 or TiCl.sub.4 with the said compounds or with CrO.sub.3 or OsO.sub.4 is used as the catalyst. In a preferred embodiment of the process, thin films of the monomers to be polymerized, applied to glass or to a polymeric base, preferably to a plastic film, are treated with gaseous SbCl.sub.5, SbF.sub.5 or AsF.sub.5. The conductive polymers obtained can be used in the electrical industry for the production of solar cells, for the conversion and fixing of radiation and for the production of electrical and magnetic switches, as well as for the antistatic treatment of plastics.

Description

The present invention relates to a process for the preparation of electrically conductive polymers by polymerizing acenaphthylene, N-vinyl-heterocyclics, eg. N-vinylcarbazole or N-vinylpyridine, or N,N-divinylaniline at from -80.degree. to +100.degree. C. in the presence of a cationic catalyst.

These polymerization processes require from 0.001 to 10% by weight, based on weight of monomers, of the cationic catalysts in order to cause the polymerization to proceed.

The polymerization of vinyl compounds with cationic catalysts has been disclosed (cf. W. R. Soerenson and T. W. Campbell "Preparative Methods of Polymer Chemistry", Interscience Publ., New York 1968, page 265).

It has also been disclosed that electrically conductive polymers may be prepared by oxidative coupling of aromatic compounds by means of Lewis acids (cf. Naturwissenschaften, 56 (1969), 308). However, this process has only been carried out with aromatic and cycloaliphatic systems. The polymers obtained had relatively low molecular weights, with degrees of polymerization of up to about 50, and were accordingly brittle and difficult to process.

It is an object of the present invention to provide high molecular weight, non-brittle polymers possessing good processability and high electrical conductivity.

We have found that this object is achieved by using, as the catalyst for the polymerization of acenaphthylene, N-vinyl-heterocyclics, eg. N-vinylcarbazole or N-vinylpyridine, or N,N-divinylaniline, from 1 to 50, preferably from 10 to 40, % by weight, based on the weight of monomer employed, of an oxidizing Lewis acid.

Preferred Lewis acids are FeCl.sub.3, FeBr.sub.3, SbCl.sub.5, SbF.sub.5, AsF.sub.5 and CF.sub.3 -SO.sub.3 -H, or a combination of AlCl.sub.3 or TiCl.sub.4 with the said compounds or with CrO.sub.3 or OsO.sub.4.

In a particularly preferred embodiment, thin films of the monomers to be polymerized, applied to glass or to a plastic film, are treated with gaseous SbCl.sub.5, SbF.sub.5 or AsF.sub.5.

The polymerization temperature used is from -80.degree. to +100.degree. C., preferably from -30.degree. to +100.degree. C. The polymerization process according to the invention can be carried out in conventional solvents and auxiliary fluids but can also be carried out as a mass polymerization.

A particularly preferred embodiment is an oxidative cationic polymerization wherein thin films of the above monomers, applied to one or both sides of glass or of a polymeric base, preferably a polymer film, are polymerized by means of gaseous initiators, eg. SbCl.sub.5, SbF.sub.5 or AsF.sub.5.

The polymers prepared by the process according to the invention are soluble and have intrinsic viscosities of [.eta.]>0.5, ie. molecular weights greater than 25,000 (according to the conversion formula given in Macromolecular Synthesis, volume I (1974), 83, published by John Wiley, New York). The polymers thus produced have electrical conductivities of about 10.sup.-10 --10.sup.-3 S/cm, depending on the amount of catalyst which has remained in the polymer.

By increasing the amount of catalyst employed according to the invention, during or after the polymerization, to figures of up to 50% by weight, it is possible to achieve electrical conductivities of up to 10.sup.+2 S/cm. The electrical conductivity is measured by the method of F. Beck, Ber. der Bunsenges. 68 (1964), 559.

The electrically conductive polymers prepared according to the invention and having conductivities greater than 10.sup.-2 S/cm may be used for the antistatic treatment of plastics, for the production of solar cells, for the conversion and fixing of radiation and for the production of electrical and magnetic switches. The addition of the strong Lewis acids to the monomers or polymers results in p-conductors (cf. J. Chem. Educ., 46 (1969), No. 2, 82.

In the Examples which follow, parts are by weight.

EXAMPLE 1

10 parts of acenaphthylene are dissolved in 100 parts of diethyl ether at -50.degree. C. and 1 part of antimony pentafluoride is added at the same temperature. Thereafter, the solution is heated to 25.degree. C. in the course of 5 hours, and the solvent is then stripped off. The polymer obtained is soluble in benzene and has a molecular weight of about 150,000. The electrical conductivity of this product is 2.5.times.10.sup.-2 S/cm.

EXAMPLES 2 to 5

On following the procedure described in Example 1, but varying the amount and nature of the solvent and of the initiator, the following results are obtained.

______________________________________ Temp. Initiator ConductivityNo. Solvent .degree.C. Type Parts S/cm, 30.degree. C.______________________________________2 Benzene 100 parts 10 AsF.sub.5 2 3.8 .times. 10.sup.-13 Toluene 100 parts -50 AsF.sub.5 3 8.5 .times. 10.sup.-14 Methyl- 100 parts -50 SbF.sub.5 3 4.6 .times. 10.sup.-1 ene chloride5 Diethyl 100 parts 0 AlCl.sub.3 2 3.6 .times. 10.sup.-2 ether CrO.sub.3 0.5______________________________________

EXAMPLE 6

The procedure described in Example 1 is followed but varying the monomer; the following results are obtained.

______________________________________No. Monomer Conductivity, S/cm, 30.degree. C.______________________________________6 N--vinylcarbazole 0.6 .times. 10.sup.-27 N--vinylpyridine 1.8 .times. 10.sup.-28 2-Vinylpyridine 3.6 .times. 10.sup.-29 4-Vinylpyridine 0.9 .times. 10.sup.-2______________________________________

EXAMPLES 10 to 15

______________________________________Polymerfrom Ex- Lewis acid Conductivity,No. ample Type Amount S/cm, 30.degree. C.______________________________________10 1 AsF.sub.5 1 2.3 .times. 10.sup.+111 2 AsF.sub.5 2 4.9 .times. 10.sup.+212 3 CF.sub.3 SO.sub.3 H 1 2.8 .times. 10.sup.+1 -13 4 CF.sub.3 SO.sub.3 H 2 4.5 .times. 10.sup.+114 5 CF.sub.3 SO.sub.3 H 3 3.0 .times. 10.sup.+215 6 CF.sub.3 SO.sub.3 H 2 9.2 .times. 10.sup.+1______________________________________

Claims

1. A process for the preparation of electrically conductive compositions which comprises polymerizing acenaphthylene, N-vinylcarbazole, N-vinylpyridene or N,N-divinylaniline at temperatures of from -80.degree. to 100.degree. C. using, as the catalyst, an oxidizing Lewis acid in an amount of from 10 to 50% by weight, based on the weight of the monomer employed.

2. The process of claim 1, wherein N-vinylcarbazole is polymerized.

3. The process of claim 1, wherein N-vinylpyridine is polymerized.

4. The process of claim 1, wherein N,N,-divinylaniline is polymerized.

5. The process of claim 1, wherein the amount of catalyst is from 10 to 40% by weight.