Preparation of electrically conductive soluble heteropolyphenylenes

Abstract

A process for the preparation of electrically conductive heteropolyphenylenes, wherein from 0.5 to 5 per cent by weight of an activating additive is introduced, in the absence of moisture and of oxygen, into a heteropolyphenylene of the general formula ##STR1## where X is O, S, Se, SO or SO.sub.2 and Y has one of the meanings given for X or is NH, CH.sub.2, CO or C.sub.6 H.sub.4, and n is from 2 to 250. The activating additive is preferably one of the compounds AsF.sub.5, SbF.sub.5, UF.sub.6, HClO.sub.4, NO.sup.+ SbF.sub.6.sup.-, NO.sub.2.sup.+ SbF.sub.6.sup.-, NO.sup.+ PF.sub.6.sup.-, SbCl.sub.5, NO.sub.2.sup.+ PF.sub.6.sup.-, NO.sup.+ BF.sub.4.sup.-, NO.sup.+ ClO.sub.4.sup.-, (CF.sub.3).sub.2 SO.sub.4, 2,4,6-trinitrophenol, 2,4,6-trinitrophenylsulfonic acid and 2,4,6-trinitrophenylcarboxylic acid, or is sodium, potassium, rubidium, cesium, calcium or barium or one of their amides, the latter being added, if appropriate, in tetrahydrofuran, dimethoxyglycol, anthracene, naphthalene or 2-methylstyrene. The conductive heteropolyphenylenes may be used in the electrical industry for the production of solar cells, for conversion and fixing of radiation and for the production of electrical and magnetic switches, or may be used for the antistatic treatment of plastics.

Description

The present invention relates to a process for the preparation of electrically conductive soluble heteropolyphenylenes having conductivities greater than 10.sup.-2 S/cm. The symbol S stands for Siemens. The expression S/cm or Siemens/cm is widely used as a unit of electrical conductivity and is equivalent to ohm.sup.-1 cm.sup.-1.

The preparation of polyphenylenes by oxidative coupling is described in Macromolecular Syntheses Collective, 1 (1979), 109-110 (published by John Wiley & Sons), and Naturwissenschaften 56 (1969), 308-313. Further, R. Gehm and W. Kern, Makromol. Chem. 7 (1951), 46-61, have described the preparation of polyphenylenes by stepwise polycondensation, which gives particularly uniform, para-linked methyl-substituted derivatives, which are not contaminated by ortho- or meta-linked polymers.

The work of J. K. Stille, Makromol. Chem. 154 (1972), 49 disclosed the possibility of preparing heteropolyphenylenes by a Diels-Alder condensation.

It is an object of the present invention to provide soluble heteropolyphenylenes and to convert these, by activating additives, into electrically conductive polymers having conductivities greater than 10.sup.-2 S/cm.

We have found that this object is achieved, according to the invention, by a method wherein from 0.5 to 5 percent by weight, based on heteropolyphenylene employed, of an activating additive is introduced, in the absence of moisture and of oxygen, into a heteropolyphenylene of the general formula (I) ##STR2## where X is O, S, Se, SO oder SO.sub.2, Y has one of the meanings given for X or is NH, CH.sub.2, CO oder C.sub.6 H.sub.4 and n is from 2 to 250, preferably from 5 to 50.

Preferably, the activating additive is a strong Lewis acid having a pK.sub.a of from 10 to 14. Particularly preferably, the Lewis acid used is AsF.sub.5, SbF.sub.5, UF.sub.6, HClO.sub.4, NO.sup.+ SbF.sub.6.sup.-, NO.sub.2.sup.+ SbF.sub.6.sup.-, NO.sup.+ AsF.sub.6.sup.-, SbCl.sub.5, NO.sub.2.sup.+ PF.sub.6.sup.-, NO.sub.2.sup.+ AsF.sub.6.sup.-, NO.sup.+ PF.sub.6.sup.-, NO.sup.+ BF.sub.4.sup.-, (CF.sub.3).sub.2 SO.sub.4, NO.sup.+ ClO.sub.4, 2,4,6-trinitrophenol, 2,4,6-trinitrophenylsulfonic acid, or 2,4,6-trinitrobenzoic acid. In another preferred method, the activating additive is sodium, potassium, rubidium, cesium, calcium or barium or an amide thereof. Preferably, when using the alkali metals or alkaline earth metals or their amides, an auxiliary fluid such as tetrahydrofuran, dimethoxyglycol, anthracene, naphthalene or 2-methylstyrene is added, in each case in a molar ratio of the former component to the latter component of from 1:1 to 1:3, preferably from 1:2 to 1:3.

To prepare the heteropolyphenylenes (I), difunctional compounds, for example diaminoisophthalic acid (II), are used as starting materials, and are subjected to a reaction similar to a conventional indigo synthesis. (cf. H. R. Christen, Lehrbuch der organ. Chemie, (1970), 710, Sauerlander Verlag, Aarau) ##STR3##

In the soluble heteropolyphenylenes of the general formula (I), ##STR4## n is from 2 to 250, preferably from 5 to 50, X is O, S, Se, SO or SO.sub.2 and Y is X or is NH, CH.sub.2, CO or C.sub.6 H.sub.4.

The additives are always incorporated in the absence of moisture (water) and of oxygen (air); the process is therefore preferably carried out under an argon atmosphere. The solvents which may be used are stripped off, after the incorporation process, under reduced pressure at below 30.degree. C.

By means of the additives mentioned it is possible to achieve increases of several orders of magnitude in the electrical conductivity. The initial conductivities of the polyaromatics are about 10.sup.-13 S/cm, but after introducing the additives according to the invention the conductivities are greater than 10.sup.-2 S/cm.

The electrically conductive heteropolyphenylenes prepared according to the invention and having electrical conductivities greater than 10.sup.-2 S/cm may be used for the antistatic treatment of plastics, for the production of solar cells, for conversion and fixing of radiation and for the production of electrical and magnetic switches. The addition of the strong Lewis acid to the polyaromatic produces an n-conductor, whilst the addition of the aklali metal or alkaline earth metal or of amides thereof produces p-conductors.

In the Examples which follow, parts are parts by weight, and the amounts of additives are expressed in mole percent.

EXAMPLES

10 parts of a heteropolyphenylene (I) are mixed with the relevant additive under an argon atmosphere, in the absence of moisture. The electrical conductivity is measured by the method of F. Beck, Ber. Bunsengesellschaft, Phys. Chem. 68 (1964), 558-567.

The heteropolyphenylene used is of the following type (I) ##STR5##

______________________________________ Conductivity inPolyaromatic Doping agent S/cm at 30.degree. C. type and type and amount before afterNo. amount in mole % doping doping______________________________________1 I 1 part AsF.sub.5 0.2 10.sup.-13 0.5 .times. 10.sup.-2 n = about 10 x = O2 I 1 part SbF.sub.5 0.4 " 0.9 .times. 10.sup.-2 n = about 15 x = O3 I 1 part BF.sub.3 0.5 " 1.5 .times. 10.sup.-3 n = about 15 x = S4 I 1 part NO.sub.2.sup.+ SbF.sub.6 0.2 10.sup.-11 7.0 .times. 10.sup.+1 n = about 35 x = S5 I 1 part NO.sup.+ SbF.sub.6 0.2 10.sup.-12 2.6 .times. 10.sup.+1 n = about 15 x = S6 I 1 part CF.sub.3 SO.sub.3 H 0.2 " 0.4 .times. 10.sup.+1 n = about 20 x = Se7 I 1 part Na 0.5 10.sup.-13 0.5 .times. 10.sup.-1 n = about 10 x = O8 I 1 part AsF.sub.5 0.2 about 10.sup.-13 0.5 .times. 10.sup.-1 n = about 20 x = O9 I 1 part AsF.sub.5 0.2 " 1.6 .times. 10.sup.-2 n = about 25 x = O10 I 1 part AsF.sub.5 0.2 " 2.3 .times. 10.sup.-1 n = about 35 x = O11 I 1 part AsF.sub.5 0.2 " 3.5 .times. 10.sup.+1 n = about 50 x = O12 I 1 part AsF.sub.5 0.2 " 4.6 .times. 10.sup.-1 n = about 20 x = S13 I 1 part SbF.sub.5 0.2 about 10.sup.-12 9.4 .times. 10.sup.+1 n = about 80 x = S14 I 1 part AsF.sub.5 0.2 about 10.sup.-11 0.6 .times. 10.sup.+1 n = about 35 x = Se15 I 1 part H.sub.2 SO.sub.4 0.3 about 10.sup.-13 1.5 .times. 10.sup.-2 n = about 20 x = O______________________________________

Claims

1. A process for the preparation of an electrically conductive heteropolyphenylene having a conductivity greater than 10.sup.-2 S/cm, wherein from 0.5 to 5 percent by weight, based on heteropolyphenylene employed, of an activating additive is introduced, in the absence of moisture and of oxygen, into a heteropolyphenylene of the formula ##STR6## where X is O, S or Se, Y has one of the meanings given for X or is SO, SO.sub.2 NH, CH.sub.2, CO or phenylene and n is from 2 to 250.

2. A process as claimed in claim 1, wherein the activating additive is a strong Lewis acid, having a pK.sub.a of from 10 to 14.

3. A process as claimed in claim 1 or 2, wherein the Lewis acid is AsF.sub.5, SbF.sub.5, UF.sub.6, HClO.sub.4, NO.sup.+ SbF.sub.6.sup.-, NO.sup.+ AsF.sub.6.sup.-, NO.sub.2 AsF.sub.6.sup.-, NO.sub.2.sup.+ SbF.sub.6.sup.-, NO.sup.+ PF.sub.6.sup.-, SbCl.sub.5, NO.sub.2.sup.+ PF.sub.6.sup.-, NO.sup.+ BF.sub.4.sup.-, NO.sup.+ ClO.sub.4.sup.-, (CF.sub.3).sub.2 SO.sub.4, 2,4,6-trinitrophenol, 2,4,6-trinitrophenylsulfonic acid or 2,4,6-trinitrobenzoic acid.

4. A process as claimed in claim 1, wherein sodium, potassium, rubidium, cesium, calcium or barium or an amide thereof is introduced, as an activating additive, into the heteropolyphenylene (I).

5. A process as claimed in claim 1 or 4, wherein Na, K, Rb, Cs, Ca or Ba or an amide thereof is added in tetrahydrofuran, dimethoxyglycol, anthracene, naphthalene or 2-methylstyrene, in each case in a molar ratio of the former component to the latter component of from 1:1 to 1:5.

6. A process as claimed in claim 1, wherein n is from 5 to 50.

7. A process as claimed in claim 5, wherein the molar ratio of the former component to the latter component is from 1:2 to 1:3.