Patent Application
20190048158
The present application relates to polymer films and more particularly to free-standing ultra-thin polymer films.
This section provides background information related to the present disclosure which is not necessarily prior art.
The Prior Art method of preparing ultra-thin polymer films is illustrated in
The Prior Art method of preparing ultra-thin polymer films has several disadvantages. The substrate preparation can introduce roughness, especially in the case of sputtered liftoff layers, which can be on the order of several nanometers, which leads to film non-uniformity and becomes more severe as the film thickness is reduced below 20 nm. Sacrificial liftoff layers can contaminate the film and decrease the strength of the film. At thicknesses lower than 30 nm, the liftoff of the film from the substrate becomes impossible for some preparations. Another drawback is the inability to produce large free-standing films. This inability is related to the shape of the holder, the liftoff technique itself, and the properties of the polymer that is used to produce the thin film. Large films will often tear when lifted out of the water, and in some cases they tear while drying.
Features and advantages of the disclosed apparatus, systems, and methods will become apparent from the following description. Applicant is providing this description, which includes drawings and examples of specific embodiments, to give a broad representation of the apparatus, systems, and methods. Various changes and modifications within the spirit and scope of the application will become apparent to those skilled in the art from this description and by practice of the apparatus, systems, and methods. The scope of the apparatus, systems, and methods is not intended to be limited to the particular forms disclosed and the application covers all modifications, equivalents, and alternatives falling within the spirit and scope of the apparatus, systems, and methods as defined by the claims.
The inventors have developed apparatus, systems, and methods that overcome the limitations of earlier methods. In various embodiments the inventors have developed apparatus, systems, and methods for directly delaminating extraordinarily thin films of polymer material from a substrate without the use of a sacrificial layer. The inventors have also developed a holder for film manipulation, using a marker to locate the film in the water, and unique procedures that include moving the wafer into and/or out of the water at a desired angel and speed. In one embodiment, the inventors have developed apparatus, systems, and methods for preparing large ultrathin free-standing polymer films by providing a polymer material, providing a substrate, processing the substrate with a polyelectrolyte, applying the polymer material to the substrate, and directly delaminating extraordinarily thin films of the polymer material from the substrate without the use of a sacrificial layer.
The inventors have shown the direct delamination of extraordinarily thin (as thin as 8 nm) films of poly(vinyl formal) (PVF), polystyrene, and poly(methyl methacrylate). Large (up to 13 cm diameter) films of PVF could be captured on wire supports to produce free-standing films. By modifying the substrate to lower the interfacial energy resisting film-substrate separation, the conditions for spontaneous delamination are satisfied even for very thin films. The substrate modification is based on the electrostatic adsorption of a cationic polyelectrolyte. Eliminating the use of sacrificial materials and instead relying on naturally self-limiting adsorption makes this method suitable for large areas. Features of the inventor's apparatus, systems, and methods are described below.
Feature 1. The substrate is a silicon wafer cleaned with an oxidizing acid. This substrate is both very flat and wets well, two preconditions for making thin films and removing them from the substrate.
Feature 2. A polyelectrolyte (poly(diallylammonium chloride) (PDAC)) is used as liftoff agent. The agent is not deployed as a sacrificial layer that is dissolved off during the process, but instead is deployed as a monolayer. The expected effect of the monolayer is to maintain a high wettability of the substrate while reducing interaction (such as hydrogen bonding) between substrate and polymer film. The inventors assume that the superior performance of the liftoff agent is a result of introducing a surplus of positive charge that more efficiently screens the negative charge on the substrate.
Feature 3. Very thin films are marked with permanent markers, so that they can be found after liftoff. At thicknesses of 10 nm or less, the films are practically invisible on the water, and the marker outline guides the fabricator to successful liftoff. Using the correct marker is important: some markers reduce the strength of the film, other detach from the film in the water and can contaminate the film.
Feature 4. Custom holders are used to pick up the films from the water surface. The thickness of these holders should not exceed 1.5 mm to avoid creating a large meniscus on the back side of the holder while the film is picked up. Films thinner than 20 nm can be torn apart by a large meniscus.
Feature 5. The angle of the holder to the water during the pickup is important. Early in the pickup, a shallow angle is preferable, to make sure the film attaches properly to the holder. Once the film is attached, the angle should be changed to become steeper, so that the water meniscus can be minimized. The holder should be pulled out of the water at low speed until the meniscus detaches from the back of the holder; afterwards, it can be removed faster.
The disclosed apparatus, systems, and methods have use for production of ultrathin films for the assembly of inertial confinement fusion targets. These targets have a fuel capsule that must be supported with minimal mass to avoid perturbations to the implosion. The disclosed apparatus, systems, and method also have use in the fabrication of separation membranes for carbon capture and for desalination. Sample substrates for transmission electron microscopy and other microscopy or x-ray methods also use very thin films to maximize contrast with the sample.
The apparatus, systems, and methods are susceptible to modifications and alternative forms. Specific embodiments are shown by way of example. It is to be understood that the apparatus, systems, and methods are not limited to the particular forms disclosed. The apparatus, systems, and methods cover all modifications, equivalents, and alternatives falling within the spirit and scope of the application as defined by the claims.
The accompanying drawings, which are incorporated into and constitute a part of the specification, illustrate specific embodiments of the apparatus, systems, and methods and, together with the general description given above, and the detailed description of the specific embodiments, serve to explain the principles of the apparatus, systems, and methods.
Referring to the drawings, to the following detailed description, and to incorporated materials, detailed information about the apparatus, systems, and methods is provided including the description of specific embodiments. The detailed description serves to explain the principles of the apparatus, systems, and methods. The apparatus, systems, and methods are susceptible to modifications and alternative forms. The application is not limited to the particular forms disclosed. The application covers all modifications, equivalents, and alternatives falling within the spirit and scope of the apparatus, systems, and methods as defined by the claims.
As used in this application the terms identified below have the following meanings:
Ultra-thin polymer film=A film with a thicknesses below 100 nm.
Thinnest freestanding film=A film with a thicknesses below 20 nm.
Inventor's Thinnest freestanding film=A film with a thickness below 10 nm.
Shallow Angle=An angle of 35° or less.
The disclosed apparatus, systems, and methods produce extraordinarily thin films of polymer material from a substrate without the use of a sacrificial layer. The disclosed apparatus, systems, and methods also include a holder for film manipulation, a marker for locating the film in water, and unique procedures that include moving the wafer into the water at a desired angle and speed.
One embodiment of the inventor's apparatus, systems, and methods of preparing ultra-thin polymer films is illustrated in
Referring now to
By modifying the surface of the silicon wafer 202 to lower the interfacial energy resisting film/substrate separation, the conditions for spontaneous delamination are satisfied even for very thin films. Eliminating the use of sacrificial materials and instead relying on naturally self-limiting adsorption makes this method suitable for large areas. The inventors have observed delamination of films with aspect ratios (ratio of lateral dimension between supports to thickness) of 107 and have captured dry, free-standing films with aspect ratios >106. Films with an aspect ratio of 105 can bear loads up to 106 times the mass of the film itself.
Referring to
Referring now to
The process of separating the film 206 from the substrate 202 was accomplished without the use of the Prior Art sacrificial layer. By eliminating the sacrificial layer altogether and instead directly enhancing the release of the film through a predisposition substrate surface modification the inventors have developed a new and improved apparatus, systems, and methods of producing ultra-thin films. The inventor's substrate surface modification provides a lift-off agent that is part of the surface 204 of the silicon wafer 102. The lift-off agent is a polyelectrolyte. In one embodiment, the inventor's modification is based on the electrostatically mediated adsorption of the polyectrolyte polydiallyldimethylammonium chloride (PDAC). The surface modification has two key characteristics that make it ideally suited for large-area ultrathin films: (1) the chemistry of the modification is chosen based on delamination theory in order to minimize the critical thickness required for spontaneous film release, and (2) the self-limiting nature of the surface modification makes it scalable to large areas without requiring additional process optimization and control. Moreover, the surface modification is entirely water-based, compatible with further aqueous processing, quasi-permanent, and takes only a few minutes.
An embodiment of the inventor's apparatus, systems, and methods of using a marker to locate the ultra-thin film in the water is illustrated in
Referring now to
An embodiment of the inventor's apparatus, systems, and methods of using a holder to remove the ultra-thin film from the water is illustrated in
Referring now to
An embodiment of the inventor's apparatus, systems, and methods of using the ultra-thin film for tents for inertial confinement fusion is illustrated in
Referring now to
The journal article “Enhanced Delamination of Ultrathin Free-Standing Polymer Films via Self-Limiting Surface Modification,” by Salmaan H. Baxamusa, Michael Stadermann, Chantel Aracne-Ruddle, Art J. Nelson, Maverick Chea, Shuali Li, Kelly Youngblood, and Tayyab I. Suratwala published Apr. 22, 2014, Langmuir 2014, 30, 5126-5132 provides additional details of the Inventor's apparatus, systems, and methods. The journal article “Enhanced Delamination of Ultrathin Free-Standing Polymer Films via Self-Limiting Surface Modification,” by Salmaan H. Baxamusa, Michael Stadermann, Chantel Aracne-Ruddle, Art J. Nelson, Maverick Chea, Shuali Li, Kelly Youngblood, and Tayyab I. Suratwala published Apr. 22, 2014, Langmuir 2014, 30, 5126-5132 is incorporated herein in its entirety for all purposes by this reference. Some of the features, procedures, and experimental testing of the inventor's apparatus, systems, and methods are described below.
Feature 1. The substrate is a silicon wafer cleaned with an oxidizing acid. This substrate is both very flat and wets well, two preconditions for making thin films and removing them from the substrate.
Feature 2. A polyelectrolyte (poly(diallylammonium chloride) (PDAC)) is used as liftoff agent. The agent is not deployed as a sacrificial layer that is dissolved off during the process, but instead is deployed as a monolayer. The expected effect of the monolayer is to maintain a high wettability of the substrate while reducing interaction (such as hydrogen bonding) between substrate and polymer film. The inventors assume that the superior performance of the liftoff agent is a result of introducing a surplus of positive charge that more efficiently screens the negative charge on the substrate.
Feature 3. Very thin films are marked with permanent markers, so that they can be found after liftoff. At thicknesses of 10 nm or less, the films are practically invisible on the water, and the marker outline guides the fabricator to successful liftoff. Using the correct marker is important: some markers reduce the strength of the film, other detach from the film in the water and can contaminate the film.
Feature 4. Custom holders are used to pick up the films from the water surface. The thickness of these holders should not exceed 1.5 mm to avoid creating a large meniscus on the back side of the holder while the film is picked up. Films thinner than 20 nm can be torn apart by a large meniscus.
Feature 5. The angle of the holder to the water during the pickup is important. Early in the pickup, a shallow angle is preferable, to make sure the film attaches properly to the holder. Once the film is attached, the angle should be changed to become steeper, so that the water meniscus can be minimized. The holder should be pulled out of the water at low speed until the meniscus detaches from the back of the holder; afterwards, it can be removed faster.
All silicon wafers were cleaned in a 100° C. piranha solution (3 parts H2SO4 to 1 part 30 wt % H2O2 by volume) and rinsed thoroughly with distilled water prior to use.
PDAC (Sigma-Aldrich, Mw˜1×105-2×105 g/mol) was diluted from the as-received 20 wt % aqueous suspension to 0.5 wt % using distilled water. PDAC was allowed to adsorb on the silicon wafer by spin-casting 1-2 mL of solution onto a silicon wafer at 4000 rpm for 15 s (WS-400 spin coater, Laurell Technologies). The wafer was dried for 10 s on a 100° C. hot plate, and the presence of PDAC was verified by the characteristic dark gray color of a very thin (˜10-15 nm) transparent film. Loosely bound PDAC was then removed via thorough rinsing with distilled water; the wafer was then air-dried. Strongly bound PDAC remained on the surface as a submonolayer, as shown by X-ray photoelectron spectroscopy (XPS) results. PDAC used as a sacrificial underlayer was prepared in the same manner, but the rinsing step was omitted.
For samples prepared using the commercial surfactant (Windex Foaming Glass Cleaner, SC Johnson), the surfactant was applied to the wafer using the supplied aerosol container, allowed to sit for 1 min, rinsed thoroughly with distilled water, and air-dried.
Wettability Measurements
Because of the hydrophilicity of the surfaces, we could not measure the contact angle using a traditional side-view camera. Instead, the extent to which a sessile water droplet wetted the surface was measured by first depositing a known volume of water (0.1 μL) with a microsyringe and then immediately collecting an image using a digital optical microscope (Keyence VHX2000). The droplet diameter was measured by fitting a circle to the image of the droplet. The contact angle was estimated assuming a spherical cap for the droplet. Any error introduced by this assumption will affect only the absolute contact angle, not the relative measurement between the two surfaces.
Polymer Deposition
Poly(vinyl formal) (Vinylec E, SPI Supplies) resin was dissolved to 0.5-2 wt % in ethyl lactate (Sigma-Aldrich, >98%). The solution (1-2 mL) was dropped onto a rotating substrate (˜300 rpm) and then spun for 3 s at 500-3000 rpm. Polystyrene (PS, Sigma-Aldrich, Mw˜2.8×105 g/mol) and poly(methyl methacrylate) (PMMA, Sigma-Aldrich, Mw˜1.2×105 g/mol) were dissolved to 0.3 wt % in toluene (reagent grade, JT Baker) and cast by spinning for 60 s between 2000 and 3000 rpm. The weight fraction of polymer in solution and spin speed were varied depending on the desired film thickness. All films were allowed to dry in place. Any remaining solvent was evaporated by drying on a hot plate at 50° C. for 60 s. Film thickness was measured by spectral reflectometry between 400 and 1050 nm (F20, FilmMetrics).
Delamination and Mechanical Testing
The deposited films were scored in a grid-pattern with a razor blade and slowly immersed in a bath of distilled water at a 40° angle. Individual squares delaminated and floated to the top of the bath where they were captured on a stainless steel hoop-shaped support. For mechanical testing, PVF films were glued onto a 5 mm diameter cylinder, and excess film was cut away with a hot soldering iron tip. The mechanical testing apparatus has been previously described in detail. Briefly, the sample was mounted on a balance and films were indented with a 2 mm diameter ruby or stainless steel ball moving at 0.1 mm/min. Large-area films were delaminated by making a small, single score at the edge of the wafer.
XPS Characterization
Quantitative compositional analysis of the surface chemistry was performed with XPS using a monochromatic Al Kα source (1486.7 eV). The 200 μm X-ray beam was incident normal to the sample, and the detector was 45° from normal. Core-level spectra were collected with pass energy of 23.5 eV with a resolvable XPS peak width of 1.2 eV. Deconvolution of nonresolved peaks was accomplished using Multipak 9.2 (PHI) curve fitting routines with Gaussian-Lorentzian line shapes and a Shirley background. The collected data were referenced to an energy scale with binding energies for Cu 2p3/2 at 932.72±0.05 eV and Au 4f7/2 at 84.01±0.05 eV.
Although the description above contains many details and specifics, these should not be construed as limiting the scope of the application but as merely providing illustrations of some of the presently preferred embodiments of the apparatus, systems, and methods. Other implementations, enhancements and variations can be made based on what is described and illustrated in this patent document. The features of the embodiments described herein may be combined in all possible combinations of methods, apparatus, modules, systems, and computer program products. Certain features that are described in this patent document in the context of separate embodiments can also be implemented in combination in a single embodiment. Conversely, various features that are described in the context of a single embodiment can also be implemented in multiple embodiments separately or in any suitable subcombination. Moreover, although features may be described above as acting in certain combinations and even initially claimed as such, one or more features from a claimed combination can in some cases be excised from the combination, and the claimed combination may be directed to a subcombination or variation of a subcombination. Similarly, while operations are depicted in the drawings in a particular order, this should not be understood as requiring that such operations be performed in the particular order shown or in sequential order, or that all illustrated operations be performed, to achieve desirable results. Moreover, the separation of various system components in the embodiments described above should not be understood as requiring such separation in all embodiments.
Therefore, it will be appreciated that the scope of the present application fully encompasses other embodiments which may become obvious to those skilled in the art. In the claims, reference to an element in the singular is not intended to mean “one and only one” unless explicitly so stated, but rather “one or more.” All structural and functional equivalents to the elements of the above-described preferred embodiment that are known to those of ordinary skill in the art are expressly incorporated herein by reference and are intended to be encompassed by the present claims. Moreover, it is not necessary for a device to address each and every problem sought to be solved by the present apparatus, systems, and methods, for it to be encompassed by the present claims. Furthermore, no element or component in the present disclosure is intended to be dedicated to the public regardless of whether the element or component is explicitly recited in the claims. No claim element herein is to be construed under the provisions of 35 U.S.C. 112, sixth paragraph, unless the element is expressly recited using the phrase “means for.”
While the apparatus, systems, and methods may be susceptible to various modifications and alternative forms, specific embodiments have been shown by way of example in the drawings and have been described in detail herein. However, it should be understood that the application is not intended to be limited to the particular forms disclosed. Rather, the application is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the application as defined by the following appended claims.
The present application is a Division of application Ser. No. 15/130,524 filed Apr. 15, 2016, which claims benefit under 35 U.S.C. § 119(e) of U.S. Provisional Patent Application No. 62/150,392 filed Apr. 21, 2015 entitled “preparation of large ultrathin free-standing polymer film,” the content of which is hereby incorporated by reference in its entirety for all purposes.
The United States Government has rights in this application pursuant to Contract No. DE-AC52-07NA27344 between the United States Department of Energy and Lawrence Livermore National Security, LLC for the operation of Lawrence Livermore National Laboratory.
| Number | Date | Country | |
|---|---|---|---|
| 62150392 | Apr 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15130524 | Apr 2016 | US |
| Child | 16163220 | US |