Preparation of polymer polyols

The present invention relates to novel polyether polyols which can be used in the preparation of polymer/polyols, sometimes termed polymeric polyols or graft polyols. The present invention also relates to processes by which such modified polyether polyols are prepared and to processes which use the polymer/polyols derived from the modified polyether polyols. In particular, the present invention relates to novel modified polyether polyols and their use in the above applications.
The reaction between a polyfunctional isocyante and a polyfunctional alcohol to produce polyurethane foams, elastomers, resins and the like is a well known chemical reaction which is commercially exploited on a large scale. Commercial polyurethane manufacture in general involves the reaction between a polyfunctional isocyanate and a polyfunctional alcohol such as a polyether polyol. Such polyether polyols are made from a polyfunctional low molecular weight alcohol onto which has been added a polyalkylene oxide chain. The polyalkylene oxide chain is typically prepared as a copolymer of ethylene oxide, propylene oxide or a mixture thereof in a random or block form.
In recent years, the use of polyether polyols of the type described above has been in some areas superseded by polyether polyols containing additional polymeric matter. These polyether polyols, known as polymer/polyols have been described in U.S. Pat. No. 3,304,273, U.S. Pat. No. 3,383,351, U.S. Reissue Pat. No. 28,715 and U.S. Reissus Pat. No. 29,118. Typically, these polymer/polyols have been prepared by polymerising one or more olefinically unsaturated monomers dispersed in the polyether polyol in the presence of a free radical catalyst. The polymer/polyols produced by these processes, which are thought to comprise a polymer or copolymer of the monomers at least partially grafted to the polyether polyol, have the important advantage of importing to any polyurethane derived from them improved load-bearing properties as compared with polyether polyols having no additional polymer.
The need to obtain polyurethanes with further improved load-bearing properties has meant that recently attempts have been made to improve polymer/polyols further. In particular developments of polymer/polyols has centred around increasing the polymer content whilst still maintaining the polymer/polyol in the form of a low viscosity fluid having an acceptable resistance to polymer sedimentation and increasing the polystyrene content of the polymer in order to remove problems associated with "scorch".
In order to produce stable low viscosity polymer polyols, it has been proposed to introduce during the polymerisation an extra component often termed a non aqueous dispersant (NAD) stabiliser. The NAD stabiliser comprises a polyol, for example a polyether polyol, containing deliberately added unsaturation which is able to copolymerise with or graft onto the growing polymer chains thereby forming a steric hinderance which prevents the agglomeration of polymer particles.
An example of such an NAD stabiliser is given in U.S. Pat. No. 3,823,201 where there is disclosed an unsaturated polyether polyol obtained by the reaction of a polyether polyol with the anhydride of an unsaturated acid, for example maleic anhydride. In this case, the anhydride of the unsaturated acid reacts with a free hydroxyl group on the polyether polyol to produce a modified polyether polyol having from about 0.10 to 0.70 mole of unsaturation per mole of polyol.
Similar methods of introducing unsaturation into a polyether polyol thereby forming a NAD stabiliser are disclosed in U.S. Pat. No. 4,198,488, GB 1,411,646 and EP 6605.
It has now been found that polymer/polyols having favourable viscosity and resistance to polymer sedimentation at high polymer content can be prepared by polymerising one or more monomers having olefinic unsaturation in a polyether polyol containing a novel NAD stabiliser. The novel NAD stabilisers have the advantage that they are easily prepared in a short time under mild reaction conditions. Such NAD stabilisers also obviate the need for an alkylene oxide capping step as is required when unsaturation is introduced via maleic anhydride.
Accordingly, the present invention provides a modified alcohol suitable for use as an NAD stabiliser characterised in that the modified alochol is the reaction product obtained by reacting an alcohol with a silicon atom containing compound having at least one olefinically unsaturated functional group and at least one functional group attached to the silicon atom which is reactable with the hydroxyl groups on the alcohol.
The alcohols used in the preparation of the NAD stabiliser can be for example polyalkylene polyether monols or polyols, polyhydroxyl containing polyesters, polyhydroxy terminated polyurethane polymers, polyhydric polythioethers, and the like. A preferred class of polyol is the polyalkylene polyether polyols, usually called polyether polyols, of which the following sub-classes are the most preferred
(a) alkylene oxide adducts of non-reducing sugars and their derivatives.
(b) alkylene oxide adducts of polyphenols
(c) alkylene oxide adducts of polyhydroxyalkanes.
The polyether polyol used should have a number average molecular weight in excess of 400 and a hydroxyl number in the range 20 to 280. Terms such as number average molecular weight and hydroxyl number will be familiar to those skilled in the art.
Most preferably the polyether polyol is a poly(ethylene oxide and/or propylene oxide) adduct of one of the following polyhydric alcohols; glycerol, trimethylolpropane, diethylene glycol, the isomeric butanetriols, pentanetriols and hexanetriols and pentaerythritol.
The silicon compond which is used to introduce olefinic unsaturation into the alcohol is a silicon containing compound having at least one olefinically unsaturated functional group and at least one functional group, which is reactable with the hydroxyl groups on the alcohol, attached to the silicon atom or one of the silicon atoms present in the compound if more than one silicon atom is present.
A preferred class of such silicon compounds is that having the generic formula R.sub.n Si(X).sub.4-n where;
(a) n is an integer from 1-3,
(b) the R groups are independently saturated or unsaturated hydrocarbyl groups and where at least one R group is an olefinically unsaturated hydrocarbyl group.
(c) the X groups are independently functional groups which are reactable with the hydroxyl groups on the polyol.
As regards the saturated hydrocarbyl groups, these can be alkyl or cycloalkyl groups or even aryl groups since in general any unsaturation present in such groups will be unreactive. Preferably the saturated hydrocarbyl groups are selected from C.sub.1 -C.sub.20 linear or branched alkyl groups, cycloalkyl groups having between 4 and 20 carbon atoms in the ring and substituted or unsubstituted phenyl or benzyl groups.
The unsaturated hydrocarbyl groups are ones having olefinic unsaturation and include C.sub.1 -C.sub.20 alkenyl groups, for example vinyl groups, propenyl groups, butenyl groups, pentenyl groups and the like, as well as cycloalkenyl groups and olefinically substituted aryl groups. Unsaturated hydrocarbyl groups having more than one unit of olefinic unsaturation e.g. butadienyl groups can also be used.
As mentioned earlier, the X groups are functional groups which are reactable with the hydroxyl groups on the alcohol. Any functional group which can be made to react either directly or indirectly with a hydroxyl group can be used providing that the conditions required to engineer such a reaction are not such that either the polyol or the silicon compound is chemically or thermally degraded. Functional groups capable of reacting with the hydroxyl groups on the polyol include alkoxy groups, preferably C.sub.1 -C.sub.10 alkoxyl groups, halide groups, carbamic acid ester groups of formula --NHCO.sub.2 Z where Z is a hydrocarbyl radical and --OY groups where Y is a halogen. Of these X groups, the C.sub.1 -C.sub.10 alkoxy groups are the most preferred.
Suitable examples of the silicon compounds of the class described above therefore include vinyltrialkoxysilanes e.g. vinyltriethoxysilane, vinyltrimethoxysilane and vinyltripropoxysilane, alkyl vinyldialkoxysilanes e.g. methvinyl diethoxysilane, dialkylvinylalkoxysilanes, alkyldivinylalkoxysilanes and the like.
In the Examples given above, the carbon carbon double bond, which is the source of the olefinic unsaturation, is bonded directly to the silicon atom. The carbon carbon double bond can, however, also be bonded to the silicon atom through other atoms as in for example the vinylsilane stabiliser methacryloxypropyl trimethoxysilane.
In addition to the preferred class of silicon atom containing compounds described above, those compounds having the generic formula R.sub.m Si((--OSi(R.sup.1).sub.2).sub.p X).sub.4-n can also be used. In the above formula R,X and n are as described previously, p is an integer greater than zero and R.sup.1 is a hydrocarbyl group. An example of such as stabiliser is CH.sub.2 .dbd.CH.sub.2 Si((--OSi(CH.sub.3).sub.2).sub.p OCH.sub.3).sub.3.
The NAD stabiliser produced from the alcohol and the silicon atoms containing compound has preferably a viscosity in the range 500-4000 cps at 25.degree. C. In addition the NAD stabiliser should have less than 0.8% by weight, preferably 0.3 to 0.7% by weight induced unsaturation.
In a further aspect of the invention described above there is provided a process for the preparation of the NAD stabiliser by reacting the silicon compound with the polyol. Typically this reaction is carried out by heating the silicon compound and polyol together at temperature in the range 60.degree. to 160.degree. C., preferably 100.degree. to 120.degree. C., optionally in an inert solvent such as cyclohexane or toluene. In the case where the X groups on the silicon compound are alkoxy groups or carbamic acid ester groups, it is preferable to carry out the reaction in the presence of a transesterification or transetherification catalyst for example an acid such as a mixture of trifluoroacetic acid and sodium acetate or a base such as an amidine or guanidine. When an acid catalyst is used it may be necessary to add a neutralising agent, for example sodium bicarbonate, at the end of the reaction.
As mentioned earlier, the NAD stabilisers described above are particularly useful for preparing polymer/polyols containing high levels of polymer. Thus in another aspect of the present invention there is provided a process for the preparation of a fluid polymer/polyol which process comprises polymerising one or more monomers in a liquid polyol under polymerisation conditions and in the presence of a free radical catalyst characterised in that the liquid polyol comprises (1) a base polyol and (2) an NAD stabiliser of the type described above.
The base polyol used in the preparation of the fluid polymer/polyol may be any of the polyols described earlier in relation to the NAD stabiliser or a mixture of such polyols. The base polyols should have viscosities in the range 100-5000 centipoise at ambient temperature, preferably in the range 100-2000 centipoises.
During the preparation of the polymer/polyol, a polymer is produced in the liquid base polyol by polymerisation of the monomer or monomers. The monomers used are suitably vinyl monomers, for example, styrene, acrylonitrile, methacrylonitrile and methyl methacrylate. Preferably a mixture of styrene and acrylonitrile are used to produce a copolymer. The final polymer/polyol is suitably one having more than 20% by weight polymer present and is preferably one having between 30 and 70% by weight polymer. As regards the relative amounts of styrene and acrylonitrile in the copolymer it is desirable for reasons of cost and to reduce scortch to be able to maximise the level of styrene present. Preferably therefore the copolymer should contain between 50 and 100% styrene on a molar basis.
The polymerisation reaction, for example between acrylonitrile and styrene, is initiated by means of a free radical initiator. The free radical initiator can be any of those which are routinely used in vinyl polymerisation processes including peroxides, perborates, persulphates, percarbonates and azo compounds. Typical examples of such free radical initiators include alkyl and aryl hydroperoxides, dialkyl and diaryl peroxides, dialkyl peroxy dicarbonates and azobis(nitriles). Preferred free radical initiators are azobis(isobutyronitrile) and bis(4-tertbutylcyclohexyl) peroxydicarbonate (Perkadox).
The polymer/polyols produced using the NAD stabilisers of the present invention are useful in the preparation of polyurethanes, particularly polyurethane foams. Such polyurethane foams have improved tensile strength and load bearing without impairment of the other physical parameters associated with the product. Accordingly there is also provided a process for the production of a polyurethane foam by reacting a polyfunctional isocyanate with a polymer/polyol of the type described above in the presence of
(a) a catalyst for the urethane forming reaction,
(b) a blowing agent and
(c) a foam stabiliser
Polyfunctional isocyanates which can be used to advantage include diisocyanatoalkanes, e.g. 1,2-diisocyanatoethane, 1,3-diisocyanates, the isomeric benzene, xylene and toluene diisocyanates, MDI and the like.
Catalysts which can be used to accelerate the urethane forming reaction will likewise be familiar to those skilled in the art. These include amines, phosphines, strong inorganic bases, titanate, silicate and stannate esters and organo tin derivatives.
As regards blowing agents and foam stabiliser the range of materials which can be used will be familiar to the skilled man. Thus, suitable blowing agents include water and halogenated hydrocarbons of low molecular weight.
The process may be carried out batchwise or continuously.
The invention is now illustrated by the following examples.

EXAMPLE 1
Vinyltriethoxy Silane Derived NAD Stabiliser
A two liter reactor containing a mechanical stirrer, fitted with a thermometer, and a Dean Stark apparatus topped by a condenser, was charged with trifluoroacetic acid (2.50 g, 21.9 millimoles), potassium acetate (1.30 g, 13 mmoles), toluene (800 ml), a polyether polyol (1000 g, glycerol started, PO: 85%, EO: 15%, MW: 5000, OH Number: 35.5 mg KOH/g, BP Product Polyurax U10-02) and vinyltriethoxy silane (12.0 g, 75 mmoles).
The reaction mixture was then heated at 110.degree. C. during which the transetherification reaction between the polyether polyol and the vinyltriethoxysilane started producing as products the NAD stabiliser and ethanol. At 110.degree. C. a toluene/ethanol azeotrope started to boil and was removed by distillation through the Dean Stark apparatus. By monitoring the levels of ethanol in the distillate using gas chromatography, it was found that the reaction was practically complete after 2 hours. The mixture was then cooled down to 60.degree. C., and neutralized with sodium bicarbonate (2.60 g, 31 mmoles). Toluene was then removed and the product, filtered, had an OH number of 30.6 mg KOH/g. an acid number of 0.78 mg KOH/g,, a viscosity of 6000 cps at 25.degree. C. and an average MW of 12300 used as such without further neutralization. It had an OH number of 40.0 mg KOH/g.
EXAMPLE 2
Solventless Preparation of a NAD Stabiliser
A two liter reactor fitted with a mechanical stirrer, a thermometer, a temperature regulating device, a nitrogen supply and a condensor, was charged with a polyether polyol (1000 G, 0.212 mols, glycerol started, PO: 85% ED: 15%, MW: 5000) and degassed for 30 minutes at 100.degree. C. under 1 mm HG vacuum. The reactor content was cooled to 60.degree. C. and further charged with potassium acetate (0.12 g, 0.0015 mols) and vinyltrimethoxy silane (12.6 g, 0.085 mols).
The mixture temperature was raised to 140.degree. C. under 150 ml/minute nitrogen flow for 8 hours. The entrained gasses being vented to atmosphere.
The reactor content was cooled to room temperature, the product polyether polyol was colourless and had a viscosity of 5720 cps at 25.degree. C., a residual unsaturation of 0.15 M/Q per gram.
EXAMPLE 3
Solventless Catalyst Free Preparation of a NAD Stabiliser
A one-liter autoclave fitted with a mechanical stirrer, a thermometer and heat exchanger means was charged with the same polyether polyol (798.2 g, 0.170 mols) as in Example 2 and degassed at 2 MMHG vacuum at 90.degree. C. for 30 minutes. The autoclave was then purged with a slight nitrogen flow for 10 minutes charged with vinyltrimethoxy silane (16.62 g, 0.112 mols) and closed in without catalyst addition. The charge was heated at 140.degree. C. over 4 hours and then cooled down. The resulting product had the following analysis, viscosity cps at 20.degree. C.: 840. Total unsaturation: (0.186 MEQ/G).
EXAMPLE 4
Production of Modified Silicone Crosslinker (Vinylsiloxane)
A two liter reactor fitted with a mechanical stirrer, a thermometer, a temperature regulating device, and a condensor was charged with vinyltrimethoxysilane (300 g, 2.08 mols), octamethyltetrasiloxane (700 g, 9.46 mols dimethylsiloxane equivalents) and KOH (0.5 g, 0.0086 mols, 500 ppm). The reactor content was heated to 140.degree. C. for 8 hours under slight reflux and cooled without further treatment of the equilibrate. The product had a viscosity at 21.degree. C. of 6.6 cps and had the formula CH.sub.2 .dbd.CH--Si((O(CH.sub.3).sub.2).sub.n OCH.sub.3).sub.3.
EXAMPLE 5
Solventless Preparations of NAD Stabilisers Based on the Modified Silicone Crosslinker of Example 4
Two NAD stabilisers were prepared using the procedure described in Example 2. The charge and analysis were:
______________________________________CompositionProperties ofProducts Sample 1 Sample 2______________________________________Polyether polyol 1000 1000Example 2 (g)Vinylsiloxane from 34.98 41.98Example 4 (g)Potassium acetate (g) 0.125 0.125Viscosity (CKS at 20.degree. C.) 3500 5250______________________________________
EXAMPLE 6
Solventless Preparation of NAD Stabilisers Based on Monols
Two NAD stabilisers were prepared according to the procedure described in Example 2 except that the alcohol was a polyether monol (butanol started, PO: 50%, EO: 50%, MW: 2.800).
______________________________________Composition Sample No. 1 Sample No. 2______________________________________Polyether monol 1,000 1,000(2800 MW) (G)Vinyltrimethoxysilane (G) 12.6 14.5Potassium acecate (G) 0.120 0.120Product AnalysisViscosity (CPS at 25.degree. C.) 1.570 3,000Total unsaturation (MEQ/G) 0.09 0.06______________________________________
EXAMPLE 7
Solventless Preparation of NAD Stabilisers Based on an Unsaturated Monol
Two NAD stabilisers were prepared using the procedure described in Example 2 except that the alcohol was an unsaturated polyether monol (allylalcohol started, PO: 60%, EO: 40%, MW: 4,000).
______________________________________Composition Sample No. 1 Sample No. 2______________________________________Unsaturated monol 1,000 1,000polyether (G)Vinyltrimethoxysilane (G) 12.3 18.5Potassium acetate (G) 0.12 0.12AnalysisViscosity (CPS at 25.degree. C 0.20 0.26______________________________________
EXAMPLE 8
Solventless Preparation of a NAD Stabiliser Based on Vinylmethyldimethoxysilane
Two NAD stabilisers were prepared using the procedure described in Example 2 except that the silicon atom containing compound was vinylmethyldimethoxysilane.
______________________________________Composition Sample No. 1 Sample No. 2______________________________________Polymer polyol of 1,000 1,0005,000 MW (G)Vinylmethyldimethoxy 13.7 19.6silane (G)Potassium acetate 0.12 0.12AnalysisViscosity (CPS at 25.degree. C.) 2,900 3,000Total unsaturation (MEQ/G) 0.14 0.16______________________________________
EXAMPLE 9
Preparation of Polymer/Polyol
A one liter reactor equipped with a thermometer, stirrer, graduated dropping funnel and heat exchange means, was charged with a blend of a base polyether (210 g, glycerol started, PO: 86%, EO: 14%, MW: 3500, OH Number: 46.0 mg KOH/g. BP Product: Polyurax U10-01) and the NAD stabiliser of Example 1 (26.5 g, 5%). With stirring and under a slight nitrogen flow, the charge was heated to 125.degree. C., and a stream of styrene (141.2 g, 26.6%), acrylonitrile (60.5 g, 12%), and a polymerization initiator (Perkadox P-16 a product sold by Akzo Chimie, 2.65% g, 0.5%), dispersed in the above described base polyether (90.0 g), was continuously added to the charge during a period of two hours. Upon completion of addition, the reaction mixture was maintained at 125.degree. C. for 1 hour. The reaction mixture was then stripped of volatiles for two hours at 110.degree. C., under less than 10 mm of mercury. The stripped reaction product, a white opaque stable dispersion, had a viscosity of 9000 cps at 25.degree. C.
COMPARATIVE EXPERIMENT A
Preparation of Polymer/Polyol
In a one liter reactor equipped as described above, was charged a base polyether polyol (210 g of the polyether polyol in above example, without any added stabiliser). With stirring and under a slight nitrogen flow, the charge was heated to 125.degree. C., and a stream of styrene (90.65 g, 21%), acrylonitrile (38.85 g, 9%) and a polymerisation initiator (Perkadox P-16, 2.65 g, 0.5%) dispersed in the above described polyether (90.0 g) was continuously added to the charge during two hours period. Before completion of the addition, a completely coagulated mass of polymer was obtained, blocking the stirrer.
EXAMPLE 10
Batch Preparation of a Polymer Polyol Dispersion, Polymer Content 23%, Styrene
Acrylonitrile=70:30
A two liter reactor equipped with a stirrer, thermometer and heat exchanger, and a graduated dropping funnel, was charged with a base polyether (597 g, 47.78 weight percent, MW: 5000).
While stirring under a slight nitrogen flow, the chrage was heated to 125.degree. C., and a stream of:
(a) NAD stabiliser (62.5 g, S.O w/w percent, product from Example No. 2);
(b) Azo-bis-isobutyronitrile (4.4 g, 0.35 w/w percent, e.g. AZDN-LMC from FBC Limited);
(c) Styrene (201.3 g), 16.11 w/w percent) and acrylonitrile (86.3 g, 6.9 w/w percent), dispersed in the above described base polyether (298 g, 23.85 w/w percent) was continuously added to the charge during a period of 30 minutes.
Upon completion of addition, the reaction mixture was maintained at 125.degree. C. for 30 minutes.
The resulting polymer/polyol dispersion had the following analysis:
Viscosity CPS at 25.degree. C. (unstripped): 2,800, (stripped at 135.degree. C.): 3,000.
Filtration hindrance: 150 mesh: 100% pass in 15 seconds, 700 mesh: 98% pass in 300 seconds.
EXAMPLE 11
Preparation of Polymer/Polyol Dispersion
A polymer dispersion was prepared using as base polyether a Polyurax Polyol U10-02 (glycerol starter, PO: 65%, EO: 15%, MW: 5000, OH Number: 35.5 mg KOH/g) and as stabiliser the polyol of Example 1 (13.1% on base polyether). The polymer polyol dispersion was prepared by a continuous process in which a premix of total weight (50 kg) comprising polyether polyol/styrene/acrylonitrile/catalyst was prepared in a stirred container and then fed by means of a metering pump, to a jacketted continuous stirred tank reactor (CSTR) of capacity (approximately 2 liters) maintained at a reaction temperature of 125.degree. C..+-.5.degree. C., over a period of approximately 8 hours. The reactor fitted with an external cooling loop with heat exchanger and pumped recirculation (capacity approximately 2 liters) to assist in controlling reaction temperature.
The contents from the reactor then passed to a secondary reactor in the form of a jacketted tube (unstirred), capacity approximately 4 liters, the system being maintained at the same temperature and a positive pressure of 5 psig by means of a back pressure valve, before being collected in a receiving vessel at atmospheric pressure. Prior to commencing the premixed feed to the stirred reactor, the system was filled with polymer/polyol dispersion containing 20% of total polymer, and already heated to, and maintained at, 125.degree. C.
The resulting polymer dispersion had the following analysis:
______________________________________Polystyrene (PS) (%) : 29.6Polyacrylonitrile (PAN) (%) : 10.8Total Polymer (%) : 40.4Filtration hindrance: 7 10150 mesh 100% Pass (s) 13 14 14700 mesh (%) Pass 17 06 11RT: Residence time numberViscosity (cps, 25.degree. C.) : 4870______________________________________
EXAMPLE 12
All Polystyrene Polymer Dispersion
A one liter reactor equipped as described in Example 2, was charged with a blend of a base polyether (of Example 2, 190 g), and the stabiliser of Example 1 (24.0 g, 5%). With stirring and under a slight nitrogen flow, the charge was heated to 125.degree. C., and a stream of styrene (202 g, 42%), and a polymerization initiator (Perkadox P-16, 4.80 g, 1%) dispersed in the above described base polyether (60 g) was continuously added to the charge during two hours period. Upon completion of addition, the reaction mixture was maintained at 125.degree. C. for 1 hour. The reaction mixture was then stripped of volatiles for two hours at 110.degree. C., under less than 10 mm of mercury. The stripped reaction product, a white opaque stable dispersion, had a polymer content of 41% (analysed by centrifugable solids) and a viscosity of 3500 cps at 25.degree. C.
EXAMPLE 13
Continuous Preparation of a Polymer Polyol Dispersion S/AN:70/30, Polymer Content 23%
A polymer dispersion was made using the same composition as for Example 10, but was polymerised according to a continuous process as described below.
A premix of 5.1 kg comprising a polyether polyol (3,678 g, 71.95%, MW: 5000), a NAD stabiliser (255 g, 4.99%, e.g. product from Example 2), acrylonitrile (360 g, 7.04%), styrene (800 g, 15.65% and AIBN (19.25 g, 0.37%) was prepared in a stirred container and then fed by means of a metering pump to a jacketted continuous stirred tank reactor (CSTR) of 0.2 liter capacity, maintained at 125.+-.5.degree. C., over a period of approximately 8 hours. The CSTR was fitted with an external heat exchanger. The contents from the reactor were then passed to a secondary reactor formed by an unstirred jacketted tube of 0.4 liter capacity, maintained at 125.+-..degree.C., and at a positive pressure of 5 psig before being collected in a receiving vessel at atmospheric pressure. Prior to commencing the premix feed to the stirred reactor, the system was filled with polymer polyol dispersion containing 13% of total polymer which had been previously heated to 125.degree. C.
The resulting polymer polyol dispersion was homogeneous and after 7 residence times had the following analysis:
Viscosity: (CPS at 25.degree. C.): 2,240.
Filtration hindrance: 150 mesh: 100% pass in 16 seconds, 700 mesh: 100% pass in 300 seconds.
Comparative Example B
Batch Preparation of a Polymer Polyol Dispersion without NAD Stabiliser
Example 10 was repeated except that the NAD stabiliser was omitted. The same procedure as described in Example No. 10, resulted in a non homogeneous, lumpy reaction mixture.
EXAMPLE 14
Preparation of Polymer Polyol Dispersions from the NAD Stabilisers of Example 5
Polymer polyol dispersions were prepared according to the batch or continuous procedures described in Examples 10 and 13 respectively. The resulting polymer polyol dispersions were homogeneous and had the following analyses.
______________________________________NAD stabiliserFiltration Hindranceafter batch Sample 1 of Sample 2 ofpolymerisation: Example 5 Example 5______________________________________150 mesh 100% pass in 100% pass in 64 45 seconds seconds700 mesh 12% pass in 30% pass in 300 seconds 300 secondsFiltration hindranceafter continuouspolymerisation150 mesh 100% pass in 16 seconds --700 mesh 65% pass in 300 seconds --______________________________________
EXAMPLE 15
Preparation of Polymer Polyol Dispersions from the NAD Stabilisers from Example 6
Polymer polyol dispersions were prepared according to the batch polymerisation procedure described in Example 10. The resulting polymer polyol dispersions were homogeneous and had the following analysis:
______________________________________ Sample 1 of Sample 2 ofNAD stabilizer Example 6 Example 6______________________________________Filtration hindrance150 mesh 60% pass in 60 76% pass in seconds 300 secondsViscosity (CPS at 25.degree. C.) 2,540______________________________________
EXAMPLE 16
Preparation of Polymer Polyol Dispersions from the NAD Stabilisers from Example 7
Polymer polyol dispersions were prepared according to the batch polymerisation procedure described in Example 10. The resulting polymer polyol dispersions were homogeneous and had the following analyses:
______________________________________NAD stabiliser Sample 1 of Sample 2Filtration hindrance Example 7 Example 7______________________________________150 mesh 100% pass in 45% pass in 300 seconds 300 seconds______________________________________
EXAMPLE 17
Batch Preparation of a Polymer Polyol Dispersion from the NAD Stabiliser of Example 3
A polymer polyol dispersion was made with the same charge and procedure as in Example 10, except that the NAD stabiliser used was the product from Example 3.
The resulting polymer polyol dispersion was homogeneous and 75% of a sample passed through a 150 mesh filter.
EXAMPLE 18
Preparation of Polymer Polyol Dispersions from the NAD Stabilisers from Example 8
Polymer polyol dispersions were prepared according to the batch polymerisation procedure described in Example 10. The resulting polymer polyol dispersions were homogeneous and had the following analysis:
______________________________________NAD stabiliser Sample 1 of Sample 2 ofFiltration hindrance Example 8 Example 8______________________________________150 mesh 65% pass in 100% pass in 300 seconds 16 seconds700 mesh -- 18% pass in 300 seconds______________________________________

Number	Date	Country	Kind
84/10480	Apr 1984	GBX
PCT/GB85/00176	Apr 1985	GBX

Number	Name	Date
2777868	Mixer et al.	Jan 1957
2777869	Bailey et al.	Jan 1957
3317369	Clark et al.	May 1967
3931266	Foley et al.	Jan 1976
4093554	Jayne et al.	Jun 1978
4160776	Scardera et al.	Jul 1979
4309875	Duvernoy et al.	Dec 1981
4467105	Kotzsh et al.	Aug 1984
4490416	Westall et al.	Dec 1984
4501911	Koerner et al.	Feb 1985
4588830	Fisk et al.	May 1986

Preparation of polymer polyols

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (2)

Parent Case Info

US Referenced Citations (11)

Divisions (1)