Claims
- 1. A method for preparing inorganic oxides of substantially uniform particle size distribution comprising contacting aqueous solutions of a metal (+2) and metal (+3) inorganic salt and an inorganic base across a porous membrane wherein the membrane contains a plurality of pores which allows for precipitation of substantially monodispersed size inorganic oxide particles on one side of the membrane and the formation of a salt of the corresponding base on a second side of the membrane.
- 2. The method of claim 1 wherein the particle size diameter is 20, 50, 80 or 100A.
- 3. The method of claim 1 wherein the inorganic salt is of the formula MY, wherein M is selected from the group consisting of Fe, Co, Ni, Zn, Mn, Mg, Ca, Ba, Sr, Cd, Hg, Al, B, Sc, Ga, V In, and Y is selected from the group consisting of Cl, Br, I, SO.sub.4, NO.sub.3, PO.sub.4.
- 4. The method of claim 1 wherein the inorganic base is selected from the group consisting of NH.sub.4 OH, KOH, LiOH, NaOH, CsOH, and RbOH.
- 5. The method of claim 1 wherein the substantially monodispersed precipitated inorganic oxide particle size is from about 20-1000A in diameter.
- 6. The method of claim 1 wherein the substantially mono-dispersed precipitated inorganic oxide particle is of the formula M.sub.3 O.sub.4 wherein M is selected from the group consisting of Fe, Co, Ni, Zn, Mn, Mg, Ca, Ba, Sr, Cd, Hg, Al, B, Sc, Ga, V, In and mixtures thereof.
- 7. The method of claim 1 wherein the substantially mono-dispersed precipitated inorganic oxide particle is Fe.sub.3 O.sub.4.
- 8. The method of claim 1 wherein the size of the precipitated inorganic oxide particle is increased by selecting an inorganic base with a relatively rapid dissociation constant.
- 9. The method of claim 1 wherein the size of the precipitated inorganic oxide particle is reduced by selection of an inorganic base with a relatively slow dissociation constant.
- 10. The method of claim 1 wherein the size of the precipitated inorganic oxide particles is controlled by selecting a membrane of different pore size.
- 11. The method of claim 1 wherein the size of the precipitated inorganic oxide particles is controlled by varying the temperature of the inorganic salt and inorganic base solutions.
- 12. The method of claim 1 wherein the size of the precipitated particles is controlled by adjusting the concentration of the aqueous inorganic salt solution.
- 13. The method of claim 12 wherein the concentration of the aqueous inorganic salt solution is about 1-30% wt.
- 14. The method of claim 1 wherein the size of the precipitated inorganic oxide particles is further controlled by adjusting the concentration of the aqueous inorganic base.
- 15. The method of claim 14 wherein the concentration of the aqueous solution of inorganic base is about 2-4% wt.
- 16. The method of claim 1 wherein the aqueous inorganic salt solution and the aqueous inorganic base are allowed to remain in contact across said membrane for a period of about 70-80 hours.
- 17. The method of claim 1 wherein said membrane is selected from material consisting of cellulose polymer, a fluropolymer, a chlorinated olefin polymer, and a polyamide.
- 18. The method of claim 1 wherein membranes of different pore size are selected with reference to the membranes' value of molecular weight cut-off.
- 19. A method for preparing precipitated inorganic oxides of substantially uniform particle size distribution comprising:
- a. providing an aqueous solution of an inorganic metal (+2) and metal (+3) salt at a concentration of about 1-3% wt; and
- b. providing an aqueous solution of an inorganic base at a concentration of about 2-4% wt; and
- c. contacting said solutions across a porous membrane at about 25.degree. C. for a period of about 4-6 hours to precipitate a substantially mono-dispersed inorganic oxide particle on one side of the membrane and the formation a salt of the corresponding base on a second side of the membrane.
- 20. A method for determining the concentration of a ligate in solution which comprises:
- a. providing a substantially mono-dispersed inorganic oxide particle of claim 1 wherein said particles are non-magnetic;
- b. coating said particles with an organo-metallic polymer coating which is adsorbed onto or covalently bound to the particle and which is functionalized to covalently bind to a ligand moiety having specific affinity for the ligate to be measured;
- c. covalently binding said ligand moiety to the particle;
- d. reacting the product in step (c) with a solution containing the ligate to be measured to form a ligand/ligate magnetic complex;
- e. relating the magnetic response of the product in step (d) to the concentration of the ligate causing the complexation.
- 21. The method of claim 20 wherein the ligand is an antibody.
- 22. The method of claim 21 wherein the antibody is selected from the group consisting of anti-thyroxine, anti-triiodothyronine, anti-thyroid stimulating hormone, anti-thyroid binding globulin, anti-thyroglobulin, anti-digoxin, anti-cortisol, anti-insulin, anti-theophylline, anti-vitamin B-12, anti-folate, anti-ferritin, anti-human chorionic gonadotropin, anti-follicle stimulating hormone, anti-progesterone, anti-testosterone, anti-estriol, anti-estradiol, anti-prolactin, anti-human placental lactogen, anti-gastrin and anti-human growth hormone antibodies.
- 23. The method of claim 20 wherein the ligate is selected from the group consisting of hormones, peptides, pharmacological agents, vitamins, cofactors, hematolgical substances, virus antigens, nucleic acids and nucleotides.
- 24. The method of claim 20 wherein the ligate is thyroxine and the ligand is anti-thyroxine antibody.
- 25. The method of claim 20 wherein the ligate is theophylline and the ligand is an anti-theophylline anti-body.
- 26. The method of claim 20 wherein the ligate is vitamin B-12 and the ligand is vitamin B-12 binding protein.
- 27. The method of claim 20 wherein the ligate is triiodo-thyronine and the ligand is an anti-triiodothyronine anti-body.
- 28. The method of claim 20 wherein the ligate is a thyroid stimulating hormone and the ligand is an anti-thyroid stimulating hormone anti-body.
- 29. A method for determining the concentration of a metal in solution which comprises:
- a. providing a substantially mono-dispersed inorganic oxide particle produced by the process of claim 1 wherein said particles are non-magnetic;
- b. coating said particles with an organo-metallic polymer coating which is adsorbed onto or covalently bound to the particle and which is functionalized to covalently bind to an organic moiety having specific affinity for the metal to be measured;
- c. covalently binding said organic moiety to the particle;
- d. reacting the product in step (c) with a solution containing the metal to be measured to form a magnetic complex;
- e. relating the magnetic response of the product in step (d) to the concentration of the metal causing the complexation.
- 30. The method of claim 29 wherein the organic moiety having specific affinity for a metal to be measured is 2,3-dihydroxy-benzoic acid.
- 31. The method of claim 29 wherein the metal to be measured is selected from the group consisting of W and Mo.
- 32. The method of claim 29 wherein the organic moiety having specific affinity for the metal to be measured is 2,3-dithio-benzoic acid and the metal to be measured is Mo.
- 33. A method for preparing inorganic oxides of substantially uniform particle size distribution comprising contacting aqueous solutions of an inorganic salt and a metal (+2) and metal (+3) inorganic base across a porous membrane wherein the membrane contains a plurality of pores which allows for precipitation of substantially mono-dispersed size inorganic oxide particles on one side of the membrane and the formation of a salt of the corresponding base on a second side of the membrane, wherein the size of the precipitated inorganic oxide particle is selected by adjusting the dissociation constant of the inorganic base.
- 34. The method of claim 33 wherein the particle size diameter is 20, 50, 80 or 100A.
- 35. The method of claim 33 wherein the size range of the substantially monodisperse particles varies within about +/-10% of their average size.
- 36. The method of claim 33 wherein the inorganic salt is of the formula MY, wherein M is selected from the group consisting of Fe, Co, Ni, Zn, Mn, Mg, Ca, Ba, Sr, Cd, Hg, Al, B, Sc, Ga, V In, and Y is selected from the group consisting of Cl, Br, I, SO.sub.4, N.sub.3, PO.sub.4.
- 37. The method of claim 33 wherein the inorganic base is selected from the group consisting of NH.sub.4 OH, KOH, LiOH, NaOH, CsOH, and RbOH.
- 38. The method of claim 33 wherein the substantially mono-dispersed precipitated inorganic oxide particle size is from about 20-1000A in diameter.
- 39. The method of claim 33 wherein the substantially mono-dispersed precipitated inorganic oxide particle is of the formula M.sub.3 O.sub.4 wherein M is selected from the group consisting of Fe, Co, Ni, Zn, Mn, Mg, Ca, Ba, Sr, Cd, Hg, Al, B, Sc, Ga, V, In and mixtures thereof.
- 40. The method of claim 33 wherein the substantially mono-dispersed precipitated inorganic oxide particle is Fe.sub.3 O.sub.4.
- 41. The method of claim 33 wherein the size of the precipitated inorganic oxide particles is controlled by selecting a membrane of different pore size.
- 42. The method of claim 33 wherein the size of the precipitated inorganic oxide particles is controlled by varying the temperature of the inorganic salt and inorganic base solutions.
- 43. The method of claim 33 wherein the size of the precipitated particles is controlled by adjusting the concentration of the aqueous inorganic salt solution.
- 44. The method of claim 43 wherein the concentration of the aqueous inorganic salt solution is about 1-3% wt.
- 45. The method of claim 33 wherein the size of the precipitated inorganic oxide particles is further controlled by adjusting the concentration of the aqueous inorganic base.
- 46. The method of claim 45 wherein the concentration of the aqueous solution of inorganic base is about 2-4% wt.
- 47. The method of claim 33 wherein the aqueous inorganic salt solution and the aqueous inorganic base are allowed to remain in contact across said membrane for a period of about 70-80 hours.
- 48. The method of claim 33 wherein said membrane is selected from material consisting of cellulose polymer, a fluropolymer, a chlorinated olefin polymer, and a polyamide.
- 49. The method of claim 33 wherein membranes of different pore size are selected with reference to the membranes' value of molecular weight cut-off.
- 50. A method for preparing precipitated inorganic oxides of substantially uniform particle size distribution comprising:
- a. providing an aqueous solution of an inorganic metal (+2) and metal (+3) salt at a concentration of about 1-3% wt; and
- b. providing an aqueous solution of an inorganic base at a concentration of about 2-4% wt; and
- c. contacting said solutions across a porous membrane at about 25.degree. C. for a period of about 4-6 hours to precipitate a substantially mono-dispersed inorganic oxide particle on one side of the membrane and a salt of the corresponding base on a second side of the membrane, wherein the size of the precipitated inorganic oxide particle is selected by adjusting the dissociation constant of the inorganic base.
- 51. A method for preparing inorganic oxides of substantially uniform particle size distribution comprising contacting aqueous solutions of a metal (+2) and metal (+3) inorganic salt and an inorganic base across a porous membrane wherein the membrane contains a plurality of pores which allows for precipitation of substantially mono-dispersed size inorganic oxide particles on one side of the membrane and precipitation of a salt of the corresponding base on a second side of the membrane, wherein the size of the precipitated inorganic oxide particles is selected by adjusting the temperature of the inorganic salt and inorganic base solutions.
- 52. The method of claim 51 wherein the particle size diameter is 20, 50, 80 or 100A.
- 53. The method of claim 51 wherein the size range of the substantially monodisperse particles varies within about +/-10% of their average size.
- 54. The method of claim 51 wherein the inorganic salt is of the formula MY, wherein M is selected from the group consisting of Fe, Co, Ni, Zn, Mn, Mg, Ca, Ba, Sr, Cd, Hg, Al, B, Sc, Ga, V, In, and Y is selected from the group consisting of Cl, Br, I, SO.sub.4, NO.sub.3, PO.sub.4.
- 55. The method of claim 51 wherein the inorganic base is selected from the group consisting of NH.sub.4 OH, KOH, LiOH, NaOH, CsOH, and RbOH.
- 56. The method of claim 51 wherein the substantially mono-dispersed precipitated inorganic oxide particle size is from about 20-1000A in diameter.
- 57. The method of claim 51 wherein the substantially mono-dispersed precipitated inorganic oxide particle is of the formula M.sub.3 O.sub.4 wherein M is selected from the group consisting of Fe, Co, Ni, Zn, Mn, Mg, Ca, Ba, Sr, Cd, Hg, Al, B, Sc, Ga, V, In and mixtures thereof.
- 58. The method of claim 51 wherein the substantially mono-dispersed precipitated inorganic oxide particle is Fe.sub.3 O.sub.4.
- 59. The method of claim 51 wherein the size of the precipitated inorganic oxide particle is increased by selecting an inorganic base with a relatively rapid dissociation constant.
- 60. The method of claim 51 wherein the size of the precipitated inorganic oxide particle is reduced by selection of an inorganic base with a relatively slow dissociation constant.
- 61. The method of claim 51 wherein the size of the precipitated inorganic oxide particles is controlled by varying the pore size of the membrane.
- 62. The method of claim 51 wherein the size of the precipitated particles is controlled by adjusting the concentration of the aqueous inorganic salt solution.
- 63. The method of claim 62 wherein the concentration of the aqueous inorganic salt solution is about 1-3% wt.
- 64. The method of claim 51 wherein the size of the precipitated particles is further controlled by adjusting the concentration of the aqueous inorganic base.
- 65. The method of claim 51 wherein the concentration of the aqueous solution of inorganic base is about 2-4% wt.
- 66. The method of claim 51 wherein the aqueous inorganic salt solution and the aqueous inorganic base are allowed to remain in contact across said membrane for a period of about 70-80 hours.
- 67. The method of claim 51 wherein said membrane is selected from material consisting of cellulose polymer, a fluropolymer, a chlorinated olefin polymer, and a polyamide.
- 68. The method of claim 51 wherein membranes of different pore size are selected with reference to the membranes' value of molecular weight cut-off.
- 69. A method for preparing precipitated inorganic oxides of substantially uniform particle size distribution comprising:
- a. providing an aqueous solution of an inorganic metal (+2) and metal (+3) salt at a concentration of about 1-3% wt; and
- b. providing an aqueous solution of an inorganic base at a concentration of about 2-4% wt; and
- c. contacting said solutions across a porous membrane at about 25.degree. C. for a period of about 4-6 hours to precipitate a substantially mono-dispersed inorganic oxide particle on one side of the membrane and a salt of the corresponding base on a second side of the membrane, wherein the size of the precipitated inorganic oxide particle is selected by adjusting the temperature of the inorganic salt and inorganic base solutions.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of U.S. application Ser. No. 07/556,169, filed Aug. 10, 1990, now abandoned, which is a continuation-in-part of U.S. application Ser. No. 07/455,071, filed Dec. 22, 1989, now abandoned. Attention is also directed to commonly assigned, co-pending application, 07/706,478, filed Dec. 13, 1991, and commonly assigned U.S. Pat. No. 5,071,076, the disclosures of which are incorporated by reference.
US Referenced Citations (14)
Foreign Referenced Citations (1)
Number |
Date |
Country |
0125995 |
Nov 1984 |
EPX |
Continuation in Parts (2)
|
Number |
Date |
Country |
Parent |
556169 |
Aug 1990 |
|
Parent |
455071 |
Dec 1989 |
|