Preparation of zeolite A by hydrothermal treatment of clinoptilolite

Information

  • Patent Grant
  • 4247524
  • Patent Number
    4,247,524
  • Date Filed
    Monday, October 1, 1979
    44 years ago
  • Date Issued
    Tuesday, January 27, 1981
    43 years ago
Abstract
A process for producing zeolite A of the formulaNa.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y.ZH.sub.2 Owherein x=10 to 14, y/x=0.8 to 1.2 and Z=1 to 30, which comprises heating at a temperature of 60.degree. to 150.degree. C. an aqueous slurry comprising (a) at least one gram of clinoptilolite of the formulaNa.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y. ZH.sub.2 Owherein x=5 to 7, y/x=4.5 to 5.5 and Z=1 to 30, per 100 cc of slurry, (b) at least a stoichiometric amount of sodium aluminate, and (c) at least 1% by weight of sodium hydroxide until zeolite A forms and recovering zeolite A. Sodalite which may have the formulaNa.sub.6 (AlO.sub.2).sub.6 (SiO.sub.2).sub.6.2NaClcan be produced by carrying out the aforesaid process in the presence of sodium chloride.
Description

BACKGROUND OF THE INVENTION
Zeolites or molecular sieves are three-dimensional crystalline alumina-silicates with internal pore structure having both cation exchange capacity and adsorption capacity. The cation exchange capacity of zeolites is related to the aluminum content and pore size, the aluminum atom carrying a unit negative charge in the crystalline framework and thus determining the cation exchange capacity. If the hydrated radius of a cation is too large for diffusion through the pores, then exchange capacity and rate for that cation will be low. The adsorption capacity of zeolites is related to the pore size and the size of the adsorbate molecule. Materials which can be diffused into the pores will be adsorbed while larger ones will not.
Zeolites may be synthesized from concentrated silica-alumina gels under basic conditions such as described in U.S. Pat. No. 2,882,243. According to U.S. Pat. No. 3,663,165, a zeolite molecular sieve catalyst has been synthesized from kaolin clay by calcining the kaolin at 1800.degree. F. for 2 hours to form m-kaolin followed by two treatments with aqueous sodium hydroxide. The first treatment is carried out at 100.degree. F. for 12 hours while the second is carried out at 180.degree. F. for 12 hours.
Certain zeolites do occur as mineral deposits in certain parts of the world. These mineral zeolites are usually found with varying amounts of other impurities and generally have low aluminum content. A particularly abundant mineral or natural zeolite is clinoptilolite having the formula Na.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y.ZH.sub.2 O wherein x=5 to 7, y/x=4.5 to 5.5 and Z=1 to 30.
According to a Russian article by A. Yu. Krupennikova, et al published by The P. G. Melikishvili Institute of Physical and Organic Chemistry of the Academy of Sciences of the Georgian S.S.R. and entitled Phase Transitions in the Recrystallization of Clinoptilolite, clinoptilolite has been subjected to caustic treatment to produce sodalite or phillipsite apparently in accordance with the equation:
2Na.sub.6 (AlO.sub.2).sub.6 (SiO.sub.2).sub.30.24H.sub.2 O+96NaOH(Aq).fwdarw.Na.sub.12 (AlO.sub.2).sub.12 (SiO.sub.2).sub.12.27H.sub.2 O+48Na.sub.2 SiO.sub.3 (Aq)+69H.sub.2 O (I)
As is apparent, reaction (I) suffers from a dramatic weight loss and is more suitable for the production of Na.sub.2 SiO.sub.3. In fact, each pound of clinoptilolite introduced into the process produces but 0.4 pounds of zeolite A and for each pound of zeolite A produced there is an accompanying 0.57 pound of water which must be vaporized in order to isolate zeolite A.
It is a principle object of the present invention to provide a relatively simple process which produces zeolite A from clinoptilolite while achieving a high yield of zeolite A per pound of clinoptilolite introduced into the process and requiring removal of a minimal amount of water in order to isolate the zeolite.
BRIEF DESCRIPTION OF THE INVENTION
The present invention relates to a process for producing zeolite A of the formula
Na.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y.ZH.sub.2 O
wherein x=10 to 14, y/x=0.8 to 1.2 and Z=1 to 30, which comprises heating at a temperature of 60.degree. to 150.degree. C. an aqueous slurry comprising (a) at least one gram of clinoptilolite of the formula
Na.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y.ZH.sub.2 O
wherein x=5 to 7, y/x=4.5 to 5.5 and Z=1 to 30, per 100 cc of slurry, (b) at least a stoichometric amount of sodium aluminate, and (c) at least 1% by weight of sodium hydroxide until zeolite A forms and recovering zeolite A.
The process of the present invention may proceed, for example, in accordance with the following postulated equation:
2Na.sub.6 (AlO.sub.2).sub.6 (SiO.sub.2).sub.30.24H.sub.2 O+48NaAl(OH).sub.4 .fwdarw.5Na.sub.12 (AlO.sub.2).sub.12 (SiO.sub.2).sub.12.27H.sub.2 O+9H.sub.2 O (II)
Reaction (II) depicting a typical reaction within the present invention, does not suffer from a dramatic weight loss and does not produce a major amount of another product. Each pound of clinoptilolite introduced into the process produces two pounds of zeolite A and there is but 0.014 pound of water produced per pound of zeolite A. Accordingly, isolation of the zeolite from water is not a troublesome problem.
DETAILED DESCRIPTION OF THE INVENTION
In accordance with the present invention, an aqueous slurry comprising (a) at least one gram of clinoptilolite per 100 cc of slurry, (b) at least a stoichiometric amount of sodium aluminate and (c) at least 1% by weight of sodium hydroxide is heated until zeolite A forms and zeolite A is then recovered.
The temperature of heating the aqueous slurry may range from about 60.degree. to 150.degree. C. and is preferably from 80.degree. to 100.degree. C.
The time of heating in accordance with the present invention is determinative of the extent of clinoptilolite conversion to zeolite A and depends upon the choice of temperature and ratio of reactants. Generally, the time ranges from about 15 minutes to 7 hours and preferred conditions involve a time of from 1 to 4 hours.
The slurry should contain at least one gram of clinoptilolite per 100 cc of slurry so as to achieve reasonable yields of zeolite A per volume of slurry heated. The upper limit of clinoptilolite present in the slurry is not critical. However, the amount present should not be so great as to afford an unworkable viscosity. Generally, the clinoptilolite content of the slurry will range from about 1 to 32 grams of clinoptilolite per 100 cc of slurry and preferably it ranges from about 8 to 16 grams per 100 cc of slurry.
The amount of sodium hydroxide present in the slurry should be at least 1% by weight in order to achieve a reasonable yield and generally ranges from about 1 to 25% by weight, preferably from 5 to 15% by weight.
Once zeolite A has been formed which may be determined by X-ray diffraction studies, the precipitated zeolite A may be recovered by means such as filtration. Subsequently, it may be water washed and then dried. Drying may be carried out at room temperature or at elevated temperature.
Sodalite which may have the formula
Na.sub.6 (AlO.sub.2).sub.6 (SiO.sub.2).sub.6.2NaCl
can be produced by the process of the present invention by adding sodium chloride to the aqueous slurry of the present invention. Examples illustrating the preparation of sodalite are included hereinafter.





The following examples illustrate the production of zeolite A and the production of sodalite but are not limiting to the scope of the invention which is set forth in the claims.
EXAMPLE 1
A solution was prepared by dissolving 100 g of sodium hydroxide and 41 g of sodium aluminate in 859 g of water to give 10 weight percent sodium hydroxide and 4.1 weight percent sodium aluminate. Three hundred cc of this solution were introduced into a 500 cc round bottom flask equipped with a mechanical stirrer, 12.0 g of clinoptilolite were added and the flask was heated in an oil bath at 95.degree. C. for 2 hours. The hot slurry was then filtered to give 21.6 g of zeolite A upon air drying at 25.degree. C. This corresponds to 180 weight percent recovery based on clinoptilolite. The product was identified by X-ray diffraction and elemental analysis.
EXAMPLES 2-4
The above procedure was repeated at the temperatures and times shown below to give the indicated recovery of zeolite A.
______________________________________ Temp. Time Weight PercentExample .degree.C. Hrs. Recovery of Zeolite A______________________________________2 95 2 1803 95 0.5 1134 95 4.5 186______________________________________
EXAMPLE 5
A solution was prepared by dissolving 100 g of sodium hydroxide and 82 g of sodium aluminate in 818 g of water to give 10 weight percent sodium hydroxide and 8.2 weight percent sodium aluminate. Twenty-four g of clinoptilolite and 300 cc of this solution were added to a 500 cc flask as described in Example 1. After 2 hrs. with stirring at 95.degree. C., 43.2 g of zeolite A was recovered (180 weight percent) after filtration and air drying at 25.degree. C.
EXAMPLES 6-13
The above procedure was repeated at the times and temperatures shown below to give the indicated weight percent recoveries.
______________________________________ Temp. Time Weight PercentExample .degree.C. Hrs. Recovery of Zeolite A______________________________________6 95 0.5 135.47 95 1.0 168.98 95 2.0 187.59 95 4.0 195.010 80 1.0 118.811 80 2.0 143.112 80 4.0 172.713 80 7.0 190.0______________________________________
EXAMPLES 14-21
A solution was prepared by dissolving 100 g of sodium hydroxide and 164 g of sodium aluminate in 736 g of water to give 10 weight percent NaOH and 16.4 weight percent sodium aluminate. Forty-eight g of clinoptilolite and 300 cc of this solution were added to a 500 cc flask as described in Example 1. After heating and stirring at the below indicated temperatures and times, the indicated weight percent recoveries of zeolite A were obtained.
______________________________________ Temp. Time Weight PercentExample .degree.C. Hrs. Recovery of Zeolite A______________________________________14 95 0.5 128.515 95 1.0 169.216 95 2.0 190.017 95 4.0 195.018 80 1.0 134.019 80 2.0 147.020 80 4.0 182.021 80 7.0 193.0______________________________________
EXAMPLES 22-25
The procedure of Example 1 was repeated with varying amounts of sodium hydroxide as indicated below. After 4 hours of stirring at 95.degree. C., the indicated recoveries were obtained.
______________________________________ Weight Percent Weight PercentExample Sodium Hydroxide Recovery______________________________________22 1.0 10123 5.0 15824 10.0 18025 15.0 185______________________________________
EXAMPLES 26-28
The following examples illustrate the formation of sodalite in the presence of sodium chloride. The sodalite product was identified by X-ray diffraction. The procedure of Example 1 was followed but the solution contained the indicated amount of sodium chloride.
______________________________________Exam- Weight Percent Temp. Time Weight Percentple Sodium Chloride .degree.C. Hrs. Recovery of Sodalite______________________________________26 6.1 120 2.0 17827 1.5 95 2.0 17828 0.75 95 2.0 179______________________________________
Claims
  • 1. A process for producing zeolite A of the formula
  • Na.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y.ZH.sub.2 O
  • wherein x=10 to 14, y/x=0.8 to 1.2 and Z=1 to 30, which comprises heating at a temperature of 60.degree. to 150.degree. C. an aqueous slurry comprising
  • (a) from about 1 to 32 grams of natural clinoptilolite of the formula
  • Na.sub.x (AlO.sub.2).sub.x (SiO.sub.2).sub.y.ZH.sub.2 O
  • wherein x=5 to 7, y/x=4.5 to 5.5 and Z=1 to 30, per 100 cc of slurry,
  • (b) a stoichiometric amount of sodium aluminate, and
  • (c) from about 1 to 25% by weight of sodium hydroxide in water until zeolite A forms and recovering zeolite A.
  • 2. The process of claim 1 wherein said temperature is from 80.degree. to 100.degree. C.
  • 3. The process of claim 1 wherein said heating is carried out for 15 minutes to 7 hours.
  • 4. The process of claim 1 wherein said heating is carried out for 1 to 4 hours.
  • 5. The process of claim 1 wherein said slurry contains from 5 to 15% by weight of sodium hydroxide in water.
  • 6. A process for producing zeolite A of the formula
  • Na.sub.12 (AlO.sub.2).sub.12 (SiO.sub.2).sub.12.27H.sub.2 O
  • which comprises heating at a temperature of 60.degree. to 150.degree. C. an aqueous slurry comprising
  • (a) from about 1 to 32 grams of natural clinoptilolite of the formula
  • Na.sub.6 (AlO.sub.2).sub.6 (SiO.sub.2).sub.30.24H.sub.2 O
  • per 100 cc of slurry,
  • (b) a stoichiometric amount of sodium aluminate, and
  • (c) from about 1 to 25% by weight of sodium hydroxide in water until said zeolite A forms and recovering said zeolite A.
  • 7. A process according to claims 1 or 8 wherein said slurry contains from 8 to 16 grams of natural clinoptilolite per 100 cc of slurry.
US Referenced Citations (4)
Number Name Date Kind
3101251 Howell Aug 1963
3114603 Howell Dec 1963
3733390 Robson May 1973
3852411 Maness Dec 1974