Patent Application
20190126400
Press hardened steels are produced via a hot stamping process in which the steel is deformed at high temperatures at which austenite is stable and then quenched in the stamping die at sufficient cooling rates such that martensite is formed. These steels are typically used in structural members in automotive applications where high strength and high intrusion resistance are required. Press hardened steels with tailored properties are attractive for such applications because they can provide both high intrusion resistance in addition to high energy absorption as the result of relatively hard and soft areas in the component. Tailored properties may be obtained through the use of tailor-welded blanks, which are blanks composed of two steel sheets with different compositions or thicknesses.
Typical commercial press hardened steels (for example, 22MnB5) have ultimate tensile strengths of approximately 1500 MPa with total elongations of approximately 6-8%. Conventional press hardened steel sheets may be joined to a steel with lower hardenability, and which transforms to a softer microstructure (ultimate tensile strengths of approximately 700 MPa) after press hardening. This combination of steel is typically called a tailor-welded blank (TWB). Press hardened TWBs result in components that have tailored properties with regions of high strength and relatively low elongation in areas that require intrusion resistance and regions of lower strength and higher elongation in areas that require energy absorption.
The present compositions can be used in press hardened steels, hot press forming steels, hot stamping steels, or any other steel that is heated to an austenitizing temperature, formed, and then quenched in a stamping die to achieve the desired final properties of the stamped component. The current application describes tailor-welded blanks composed of a high alloy steel that can exhibit very high strengths after press hardening—up to 2,000 MPa—and a lower alloyed steel that can exhibit more moderate strengths—up to 1,000 MPa—and higher elongation—up to 20%.
A tailor-welded blank comprises a higher alloyed steel (Alloy A) and a lower alloyed steel (Alloy B). After press hardening, Alloy A forms a microstructure that exhibits higher strength compared to Alloy B. In some embodiments, under some press hardening conditions, the total elongation of Alloy A may exceed that of Alloy B after press hardening.
Alloy A and Alloy B can each be made using conventional steel making, roughing, and finishing processes. Embodiments of Alloy A and Alloy B may each be bare or coated. Embodiments of Alloy A and Alloy B can be joined by laser welding, or other known joining techniques, to form a tailor-welded blank. During press hardening, the TWB is heated to temperatures above the lower critical temperature (Ac1) of Alloy A, transferred to a die, formed, and then cooled in the die to achieve the desired final properties. The Ac1 temperature for a given steel composition is the temperature which corresponds to the boundary between the ferrite+cementite phase field and the phase fields of austenite+ferrite or austenite+cementite. The Ac1 temperature for each composition of Alloy A can be determined by calculations known in the art, or empirically, for example by dilatometry. Calculations known in the art include the following three exemplary calculations:
Ac1=723−10.7XMn−16.9XNi+29.1XSi+16.9XCr+290XAs+6.38XW1 Eqtn 1:
Ac1=739−22.8XC−60.8XMn−15XNi+18.2XSi+11.7XCr+6.4XMo+5XV−28XCu2 Eqtn 2:
Ac1=754.83−32.25XC−17.76XMn+23.32XSi+17.3XCr+4.51XMo+15.62XV3 Eqtn 3:
1K. W. Andrews, Empirical Formulae for the Calculation of Some Transformation Temperatures, JISI, Vol. 203, 1965, pp. 721-727.2 TRZASKA, J. et al. Modelling of CCT Diagrams for Engineering and Constructional Steels. Journal of Materials Processing Technology, 192-193, 2007, 504-510.3KARIYA, N. High Carbon Hot-Rolled Steel Sheet and Method for Production Thereof. European patent Application EP 2.103.697.A1, 23.09.2009, 15 p.
Additionally, during press hardening, the TWB may also be heated to temperatures above the upper critical temperature (Ac3) of Alloy A, transferred to a die, formed, and then cooled in the die to achieve the desired final properties. The Ac3 temperature for a given steel composition is the temperature which corresponds to the boundary between the ferrite+austenite phase field and the austenite phase field. The Ac3 temperature for each composition of Alloy A can be determined by calculations known in the art, or empirically, for example by dilatometry. Calculations known in the art include the following exemplary calculation:
Ac3=910−203√{square root over (Xc)}−15.2XNi+44.7XSi+104XV+31.5XMo+13.1XW4 Eqtn 4:
4K. W. Andrews, Empirical Formulae for the Calculation of Some Transformation Temperatures, JISI, Vol. 203, 1965, pp. 721-727.
Alloy A employs a novel alloying strategy that uses substitutional elements to increase the strength of martensite through a combination of substitutional solute strengthening and a reduction in softening that results from autotempering. Softening as a result of autotempering is minimized by suppression of the martensite start temperature through alloying. As a result of the increased hardenability in the proposed compositions that results from various additions of manganese, chromium, molybdenum, and niobium, the novel compositions permit a substantially boron-free press hardening steel.
Alloy B employs an alloying strategy such that the intercritical temperature of this alloy may overlap with that of the higher alloyed Alloy A or overlap temperatures corresponding to full austenitization of Alloy A. As a result, after press hardening, the microstructure of Alloy B is primarily a mixture of ferrite, bainite, and martensite.
Carbon is added to reduce the martensite start temperature, provide solid solution strengthening, and to increase the hardenability of the steel. Carbon is an austenite stabilizer. In certain embodiments of Alloy A, carbon can be present in concentrations of 0.1-0.50 weight %; in other embodiments, carbon can be present in concentrations of 0.1-0.35 weight %; and in still other embodiments, carbon can be present in concentrations of about 0.22-0.25 weight %. In certain embodiments of Alloy B, carbon can be present in concentrations of 0.06-0.12 weight %; in other embodiments, carbon can be present in concentrations of 0.08-0.1 weight %; in other embodiments, carbon can be present in concentrations of 0.09-0.12 weight %; and in still other embodiments, carbon can be present in concentrations of 0.06-0.085 weight %.
Manganese is added to reduce the martensite start temperature, provide solid solution strengthening, and to increase the hardenability of the steel. Manganese is an austenite stabilizer. In certain embodiments of Alloy A, manganese can be present in concentrations of 2.0-8.0 weight %; in other embodiments, manganese can be present in concentrations of 2.0-5.0 weight %; in still other embodiments, manganese can be present in concentrations of 3.0 weight %-8.0 weight %; and in still other embodiments, manganese can be present in concentrations of greater than 3.0 weight %-5.0 weight %. In certain embodiments of Alloy B, manganese can be present in concentrations of 1.65-2.45 weight %; in other embodiments, manganese can be present in concentrations of 2.2-2.45 weight %; in other embodiments, manganese can be present in concentrations of 1.70-1.95 weight %, and in still other embodiments, manganese can be present in concentrations of 1.65-1.85 weight %.
Silicon is added to provide solid solution strengthening. Silicon is a ferrite stabilizer. In certain embodiments of Alloy A, silicon can be present in concentrations of 0.1-0.5 weight %; in other embodiments, silicon can be present in concentrations of 0.2-0.3 weight %. In certain embodiments of Alloy B, silicon can be present in concentrations of 0.1-0.25 weight %; in other embodiments, silicon can be present in concentrations of 0.1-0.2 weight %; and in other embodiments, silicon can be present in concentrations of 0.15-0.25 weight %.
Molybdenum is added to provide solid solution strengthening, to increase the hardenability of the steel, to provide microstructural refinement, and to protect against embrittlement. In certain embodiments of Alloy A, molybdenum can be present in concentrations of 0-2.0 weight %; in other embodiments, molybdenum can be present in concentrations of 0.0-0.6 weight %; in still other embodiments, molybdenum can be present in concentrations of 0.1-2.0 weight %; in other embodiments, molybdenum can be present in concentrations of 0.1-0.6 weight %; and in yet other embodiments, molybdenum can be present in concentrations of 0.4-0.5 weight %. In certain embodiments of Alloy B, molybdenum can be present in concentrations of 0.08-0.4 weight %; in other embodiments, molybdenum can be present in concentrations of 0.08-0.15 weight %; in other embodiments, molybdenum can be present in concentrations of 0.12-0.24 weight %; and in still other embodiments, molybdenum can be present in concentrations of 0.14-0.25 weight %.
Chromium can be added to reduce the martensite start temperature, provide solid solution strengthening, and increase the hardenability of the steel. Chromium is a ferrite stabilizer. In certain embodiments of Alloy A, chromium can be present in concentrations of 0-6.0 weight %; in other embodiments, chromium can be present in concentrations of 2.0-6.0 weight %; in other embodiments, chromium can be present in concentrations of 0.2-6.0 weight %; and in other embodiments chromium can be present in concentrations of 0.2-3.0 weight %. In certain embodiments of Alloy B, chromium can be present in concentrations of 0.0-0.7 weight %; in other embodiments, chromium can be present in concentrations of 0.5-0.7 weight %; in other embodiments, chromium can be present in concentrations of 0.15-0.35 weight %; and in still other embodiments, chromium can be present in concentrations of 0-0.1 weight %.
Niobium can be added to increase strength and improve hardenability of the steel. In some embodiments niobium can also be added to provide improved grain refinement. In certain embodiments of Alloys A and B, niobium can be present in concentrations of 0-0.1 weight %; in other embodiments, niobium can be present in concentrations of 0.01-0.1 weight %; and in other embodiments, niobium can be present in concentrations of 0.001-0.055 weight %. In certain embodiments of Alloy B, niobium can be present in concentrations of 0.0-0.1 weight %; in other embodiments, niobium can be present in concentrations of 0.03-0.05 weight %; in other embodiments, niobium can be present in concentrations of 0.025-0.055 weight %; and in still other embodiments, niobium can be present in concentrations 0.0-0.01 weight %.
Vanadium can be added to increase strength and improve hardenability of the steel. In certain embodiments of Alloy A, vanadium can be present in concentrations of 0-0.15 weight %; and in other embodiments, vanadium can be present in concentrations of 0.01-0.15 weight %. In certain embodiments of Alloy B, vanadium can be present in concentrations of 0.0-0.05 weight %; in other embodiments, vanadium can be present in concentrations of 0-0.01 weight %; and in other embodiments, vanadium can be present in concentrations of 0.02-0.05 weight %.
Boron can be added to increase the hardenability of the steel. In certain embodiments of Alloy A, boron can be present in concentrations of 0-0.005 weight %. In certain embodiments of Alloy B, boron can be present in concentrations of 0.0-0.002 weight %.
Titanium can be added increase the strength of the steel, to control austenite grain size, and to control free nitrogen. In certain embodiments of Alloy B, titanium can be present in concentrations of 0.01-0.05 weight %; in other embodiments titanium can be present in concentrations of 0.018-0.032 weight %; and in other embodiments, titanium can be present in concentrations of 0.01-0.025 weight %.
The press hardened steels can be processed using conventional steel making, roughing, and finishing processes. For example, the steels of Alloy A and of Alloy B may each be continuously cast to produce slabs approximately 12-25 cm in thickness. Slabs may then be reheated at temperatures of 1200-1320° C., and hot rolled to a final gauge of ≥2.5 mm, with the final reduction pass occurring at a temperature of approximately 950° C. Steels may then be coiled at temperatures of 400-675° C. After cooling, the steel coils may be annealed at temperatures of 600-900° C. for times longer than 1 second, and pickled, prior to cold reduction. One or more intermediate annealing and reduction steps may be required before reaching the desired thickness. Such intermediate annealing utilizes temperatures similar to the first annealing treatment.
The alloys of the present application can also be coated with an aluminum-based coating, a zinc-based coating (either galvanized or galvannealed), after cold rolling and before hot stamping. Such coating can be applied to the steel sheet using processes known in the art, including hot dip coating or electrolytic coating. Because of the lower critical temperatures, press hardening of the present alloys after they have been coated is less likely to result in melting of the coating and the detrimental effects associated with such melting.
In embodiments of the present invention, steel blanks of a chosen Alloy A and chosen Alloy B are welded together to form a TWB, they are then heated to a temperature above Ac1 for Alloy A, transferred to a die, stamped, and cooled in accordance with standard hot-stamping procedures. In other embodiments of the present invention, steel blanks of a chosen Alloy A and chosen Alloy B are welded together to form a TWB, they are then heated to a temperature above Ac3 for Alloy A, transferred to a die, stamped, and cooled in accordance with standard hot-stamping procedures. Ultimate tensile strengths of approximately 2,000 MPa may be achieved in Alloy A under appropriate press hardening conditions. Under these same conditions, steels of Alloy B may result in ultimate tensile strengths of approximately 700-980 MPa and total elongations of 13-20%.
Three steels, Alloy A-1, Alloy B-1, and Alloy B-2 were prepared with the following nominal compositions in weight percent: Alloy A-1 is 0.22% C, 5% Mn, 0.25% Si, 0.2% Cr, Fe/impurities—balance; Alloy B-1 is 0.09% C, 2.3% Mn, 0.15% Si, 0.02% Ti, Fe/impurities—balance; and Alloy B-2 is 0.08% C, 1.7% Mn, 0.18% Si, 0.013% Ti, 0.035% V, 0.017% Mo, Fe/impurities—balance. The Ac1 temperature of Alloy A-1 is approximately 677° C. and was determined using dilatometry.
Each of the steels were melted, cast, hot rolled, and cold rolled in accordance with standard practice for stainless steels.
Samples of each of the steels were heated to the peak metal temperatures shown in
A tailor-welded blank is made of a steel of Alloy A welded to a steel of Alloy B, wherein Alloy A and Alloy B contain the compositions set forth in Table 2 below (wherein the balance of the composition for each alloy is Fe and impurities associated with steelmaking):
0-2.0
Process A: After welding, the blank is heated to a temperature above the Ac1 temperature for Alloy A, transferred to a die, formed, and then cooled in the die.
Process B: After welding, the blank is heated to a temperature above the Ac3 temperature for Alloy A, transferred to a die, formed, and then cooled in the die.
A tailor-welded blank in accordance with the tailor-welded blank of Example 2, or any or more of the following example, wherein the carbon concentration in Alloy A is 0.1-0.35 weight %, and alternatively 0.22-0.25 weigh %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-3, or any or more of the following examples, wherein the carbon concentration in Alloy B is 0.08-0.1 weight %; alternatively 0.09-0.12 weight %, or alternatively 0.06-0.085 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-4, or any or more of the following examples, wherein the manganese concentration in Alloy A is 2.0-5.0 weight %; alternatively, 3.0 weight %-8.0 weight %; or alternatively 3.0 weight %-5.0 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-5, or any or more of the following examples, wherein the manganese concentration in Alloy B is 2.2-2.45 weight %, alternatively 1.70-1.95 weight %, or alternatively 1.65-1.85 weight %.
A tailor-welded-blank in accordance with the tailor-welded blank of any one or more of Examples 2-6, or any one or more of the following examples, wherein the silicon concentration in Alloy A is 0.2-0.3 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-7, or any one or more of the following examples, wherein the silicon concentration in Alloy B is 0.1-0.2 weight %, or alternatively 0.15-0.25 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-8, or any one or more of the following examples, wherein the molybdenum concentration in Alloy A is 0.0-0.6 weight %; alternatively, 0.1-2.0 weight %; alternatively, 0.1-0.6 weight %; or alternatively 0.4-0.5 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-9, or any one or more of the following examples, wherein the molybdenum concentration in Alloy B is 0.08-0.15 weight %, alternatively 0.12-0.24 weight %, or alternatively 0.14-0.25 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-10, or any one or more of the following examples, wherein the chromium concentration is 2.0-6.0 weight %; alternatively, 0.2-6.0 weight %; or alternatively 0.2-3.0 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-11, or any one or more of the following examples, wherein the chromium concentration in Alloy B is 0.5-0.7 weight %, alternatively 0.15-0.35 weight %, or alternatively 0-0.1 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-12, or any one or more of the following examples, wherein the niobium concentration is 0.01-0.1 weight %; or alternatively 0.001-0.055 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-13, or any one or more of the following examples, wherein the niobium concentration in Alloy B is 0.03-0.05 weight %, alternatively 0.025-0.055 weight %, or alternatively 0.0-0.01 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-14, or any one or more of the following examples, wherein the vanadium concentration is 0.01-0.15 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-15, or any one or more of the following examples, wherein the vanadium concentration in Alloy B is 0.0-0.01 weight %, or alternatively 0.02-0.05 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-16, or any one or more of the following examples, wherein the titanium concentration in Alloy B is 0.018-0.032 weight %, or alternatively 0.01-0.025 weight %.
A tailor-welded blank in accordance with the tailor-welded blank of any one or more of Examples 2-17, or the following example, wherein Alloy A is coated with aluminum or zinc, or alloys thereof.
A tailor-welded blank in accordance with the tailor-welded blank of any or more of one of the Examples 2-19, wherein Alloy B is coated with aluminum or zinc, or alloys thereof.
This application claims priority to U.S. Provisional Patent Application No. 62/580,591 entitled “Press Hardened Steel with Tailored Properties,” filed on Nov. 2, 2017, the disclosure of which is incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| 62580591 | Nov 2017 | US |