The present invention relates to a rear pressure bulkhead for an aircraft made of composite material as well as to the manufacturing process thereof.
The pressure bulkhead for an aircraft is the structural component that supports the pressure of the fuselage of the aircraft at its ends. The strain that the fuselage of the aircraft is subjected to, particularly when the fuselage is depressurized, in this case adding the negative pressure of the fuselage with the strain due, for example, to the loads from the vertical stabilizer, are transmitted to the rear pressure bulkhead, making it bend and buck and even collapse if it is not stiff enough. In addition, it is necessary, mainly where modern aircraft designs are concerned, to manufacture pressure bulkheads minimizing their weight while maintaining their stiffness at the same time.
Pressure bulkheads made of metal, particularly aluminum, are known in the art, although these designs require metal stiffeners to make the bulkhead stiff enough to support the fuselage strains.
In addition, pressure bulkheads made of a composite material, mainly CFRP (Carbon Fiber Reinforced with Plastic) are known which also require stiffeners made of CFRP to support the strain coming from the fuselage.
Document U.S. Pat. No. 5,062,589 describes a pressure bulkhead for an aircraft made of a composite material and locally stiffened in its high loaded areas by means of introducing foam, thus increasing the thickness of the bulkhead in these areas. However, it is necessary to manufacture this bulkhead in several sections so that it can be correctly assembled on the skin of the aircraft fuselage.
The object of this invention is a pressure bulkhead for an aircraft made of a composite material that solves the drawbacks of the prior art.
This invention proposes a curved rear pressure bulkhead comprising three layers: the outer and inner layers, symmetrical in relation to one another, are formed by a fiber laminate, the intermediate layer or core being formed by a lightweight material. With such a sandwich-type shape, the resulting bulkhead is able to withstand the bending loads coming from the strain and pressurization of the fuselage without having to increase its stiffness by means of using any kind of stiffener.
The bulkhead made of the composite material according to this invention is furthermore made in a single piece without the need to be split into sections facilitating the assembly on the aircraft fuselage skin, therefore a great weight reduction is achieved by means of eliminating any type of joint while at the same time the assembly process is clearly simplified by reducing the assembly time due to the greater integration of the assembly process. The bulkhead of the invention comprises a ring that is attached to the ends of the sandwich part. this ring is split into several pieces so that it makes easier the assembly of the bulkhead made of composite material on the fuselage skin.
The invention also relates to the manufacturing process for manufacturing a pressure bulkhead made of a composite material, comprising the steps of:
Other features and advantages of the present invention will be understood from the following detailed description of the illustrative embodiments of its object in relation to the attached figures.
The present invention proposes a curved rear pressure bulkhead 1 made of composite material, preferably in CFRP, made from carbon fibers and epoxy resin. The main advantage of CFRP is its strength/weight ratio as it is a material used to manufacture very lightweight and strong structures that are easy to optimize in relation to those made of isotropic materials. These advantages are essential for the design of pressure bulkheads for aircrafts.
The pressure bulkhead according to the invention is made in a single piece in a 360° spherical cap shape as can be seen in
The main advantage of a bulkhead 1 made of composite material according to the invention with a sandwich-type shape compared to any conventional monolithic bulkhead 10, as shown in
The core 4 comprised between the two laminates 2, 3 is made of a lightweight material which can be formed or machined and which, according to a first preferred embodiment of the invention, is a foam. This foam minimizes typical water intake problems in sandwich-type composite structures while at the same time it is an optimal solution in terms of weight and easy machining.
According to another preferred embodiment of the invention, the core 4 comprised between the laminates 2 and 3 is made of a honeycomb-type structure that can be made of paper, metal or any other material, which structure allows exponentially increasing the stiffness of the pressure bulkhead 1 without affecting the weight of the bulkhead 1 and is lighter than the foam core 4.
The radius of the pressure bulkhead 1 will be a trade-off between the minimum weight of the bulkhead 1 and the maximum space for systems and accessibility inside the aircraft.
The pressure bulkhead 1 made of composite material is manufactured in a single piece, without the need to be split into sections 11 like a conventional bulkhead 10. To allow the assembly of the bulkhead 1 to the aircraft fuselage skin 5, the bulkhead 1 also comprises a ring 6 made by means of resin transfer molding, or RTM, or it is made of titanium, divided into several pieces 8 to make easier the attachment of the bulkhead 1 to the fuselage skin 5. As can be seen in
The present invention also proposes in a second aspect a manufacturing process for manufacturing a pressure bulkhead 1 made of composite material comprising two inner and outer laminates 2 and 3, respectively, and a core 4 made of a lightweight material, comprising the following steps:
Any modifications comprised within the scope defined by the following claims can be introduced in the preferred embodiments just described.