Patent Application
20210194041
The present application relates generally to a pressure regulation system for use with lithium ion cells. In particular, the present application relates to use of spring layer(s) in combination with a housing to control pressure exerted on lithium ion cells with silicon-dominant anodes.
A lithium ion battery typically includes a separator and/or electrolyte between an anode and a cathode. In one class of batteries, the separator, cathode and anode materials are individually formed into sheets or films. Sheets of the cathode, separator and anode are subsequently stacked or rolled with the separator separating the cathode and anode (e.g., electrodes) to form the battery. Typical electrodes include electro-chemically active material layers on electrically conductive metals (e.g., aluminum and copper). Films can be cut into pieces which are then layered into stacks. The stacks are of alternating electro-chemically active materials with the separator between them.
Silicon has been used as the active material for the negative electrode to increase the volumetric and gravimetric energy densities of lithium ion batteries. However, during cycling, silicon particles in the anode active material expand upon charging. This expansion can deform the metal foil used as current collectors or damage the separator between the two electrodes if the cell is confined in a specific volume with little or no expansion capability. In this case, since the layers of the cell stack are confined in a tight region, the expansion can result in warping or deformation of the metal foil, thus reducing the contact area between layers in the cell stack. The expansion can compress the separator, thereby shorting the cell, or negatively affecting the ability for ions to move freely between the electrodes when the pores in the separator become compressed. As a result, the ability of a battery to accept and release electrical charge may be severely affected. Thus, preventing the electrodes and separators from deformation could serve to reduce the irreversible capacity loss and improve cycle life.
A energy storage device comprising a cell stack comprising a plurality of lithium-ion cells is provided. Each lithium-ion cell comprises a Si-dominant anode. A energy storage device further comprises a housing surrounding the cell stack, a pressure regulation system comprising a spring layer between two of the plurality of lithium-ion cells, and wherein the pressure regulation system in combination with the housing exerts an initial pressure of between about kPa and about 170 kPa on the cell stack.
In some embodiments, the spring layer comprises silicone foam, low-density polyethylene (LDPE) foam, high-density polyethylene (HDPE) foam, crosslinked polyethylene (PE) foam, polypropylene (PP) foam, natural rubber foam, polyester foam, polyurethane foam, or latex foam.
A lithium ion battery pack is also disclosed. The lithium ion battery pack comprises two or more energy storage devices described above and an outer packing material surrounding the one or more energy storage devices.
A vehicle comprising the lithium ion battery pack as described above, and electrical components electrically connected to the lithium ion battery pack,
Described herein, are embodiments of a pressure regulation system for use with lithium ion cells. A promising class of lithium ion cells include silicon electrodes (e.g., anodes and/or cathodes) that include silicon or a composite material containing silicon for battery applications (e.g., lithium ion battery applications). In most cases today, silicon is added to graphite in small quantities (<50%) to be used as a mixed active material in combination with the graphite. In silicon-dominant systems where the active material comprises about 50% or more of silicon, controlling the expansion of the electrodes and the pressure on the cells is much more important. Silicon is recognized as a potentially high energy per unit volume host material for lithium ion lithium battery applications. Batteries with silicon anodes can exhibit more rapid capacity loss upon cycling compared with batteries with graphite anodes. The repeated expansion and contraction of silicon particles during charge and discharge can lead to mechanical failure of the anode during the life of the battery. Exerting pressure on a lithium ion cell to control the amount of expansion can help mitigate the capacity loss and mechanical failure from repeated expansion and contraction based on cycling.
Embodiments of the disclosure relate to an energy storage device that includes a cell stack. The cell stack comprises a plurality of lithium ion cells. The cell stack includes, but is not limited to, a first lithium ion cell and a second lithium ion cell. The cell stack may further include a third lithium ion cell. The cell stack is surrounded by and contained within a housing. The energy storage device further includes a pressure regulation system that, in combination with the housing, is designed to allow the cells to expand and contract during normal cycling while keeping the pressure exerted on the cell within an acceptable range. The pressure regulation system includes a spring member (e.g., spring layer) positioned between two adjacent cells. Thus an energy storage device that has a plurality of cells may contain one or more spring members, each positioned in between adjacent cells. The spring member may also be positioned between the housing wall and the cell that is adjacent to the housing wall. The lithium ion cell may be a rectangular prism or have a cubical shape. Preferably, the lithium ion cell is a pouch cell.
Alternatively, some of the lithium ion cells 102 can be in direct contact with each other, and therefore, a spring layer 105 can be absent from between one or more cells 102. Further, there could be two or more spring layers 105 between two adjacent cells 102. The surface of the spring member that contacts the cell preferably has a substantially similar area as the cell surface that is in contact with the spring member. More preferably, the contacting surfaces of the spring member and the cell have substantially the same size.
Optionally, the energy storage device may also include one or more heat-sink layer or heat-absorbing layer between some of the adjacent cells. The energy storage device may have a spring layer 105 positioned in between each of the several adjacent cells, and also have a heat-sink layer 104 positioned in between each of the other adjacent cells. Either a spring member 105 or a heat-sink layer 104 may be positioned between the housing wall and the adjacent cell.
The spring member or layer 105 can be of differing material, density, shape, size, and/or thickness. The amount, specification, placement of spring layers 105 can be optimized based on the types of cell system. The spring layer may be a polymeric material or an elastic material. For example, the spring layer may contain silicone, polyolefin (such as polyethylene and polypropylene), cross-linked polyolefin, polyester, polyurethane, EPDM (ethylene propylene diene monomer) rubber, natural rubber, or synthetic rubber. The spring layer should exhibit good recovery or spring back behavior. In some embodiments, the spring layer is compressed less than about 15%, about 12%, about 10%, about 9%, or about 8% of its original thickness after.
In some embodiments, the spring layer may also be a foam. The foam may be an open pore or closed pore type foam. The foam preferably has a density from about 0.05 g/cc to about 1 g/cc, about 0.1 g/cc to about 1 g/cc, about 0.1 g/cc to about 0.9 g/cc, about 0.1 g/cc to about 0.8 g/cc, about 0.1 g/cc to about 0.7 g/cc, about 0.1 g/cc to about 0.65 g/cc, about 0.1 g/cc to about 0.55 g/cc. For example, the foam may comprise silicone foam, low-density polyethylene (LDPE) foam, high-density polyethylene (HDPE) foam, crosslinked polyethylene (PE) foam, polypropylene (PP) foam, natural rubber foam, polyester foam, polyurethane foam, neoprene, PVC/NBR (polyvinyl chloride/nitrile butyl rubber), styrene-butadiene rubber (SBR), EPDM rubber foam, or latex foam. The foam spring layer may have a thickness of from about 0.5 to about 3.5 mm, about 0.6 to about 3.4 mm, about 0.7 to about 3.2 mm, or about 0.8 to about 3.1 mm.
In some embodiments, the foam spring layer may comprise silicone. In some embodiments, the foam spring layer may comprise polyurethane (PU). A high-temp PU such as PORON® is preferred. In other embodiments, the spring layer may comprise EPDM rubber foam. The EPDM rubber foam could have a density of about 0.1 to about 1 g/cc and a thickness of between about 1.5 mm to about 3.2 mm.
In some embodiments, the spring layer may be a non-porous pad. The non-porous pad may have a density in the range of about 1 to about 3 g/cc, about 1 to about 2.8 g/cc, about 1.1 to about 2.5 g/cc, or about 1.1 to about 2.3 g/cc. For example, the spring layer may include a solid EPDM rubber piece.
The pressure regulation system in combination with the housing is designed to keep the pressure exerted on the cell stack during cycling within an acceptable range. Advantageously, maintaining pressure between an initial pressure and a maximum lifetime pressure on the cell stack mitigates against the capacity loss and mechanical failure from repeated expansion and contraction of electrodes due to cycling of the cell stack. The pressure regulation system in combination with the housing exerts an initial pressure of between about 25 kPa and about 170 kPa on the cell stack. In some embodiments, the initial pressure exerted on the cell stack should be between about 30 kPa and about 165 kPa, or between about 35 kPa and about 160 kPa. The pressure regulation system in combination with the housing further exerts a pressure of no more than about 300 kPa on the cell stack during the operational life of the energy storage device. Optionally, the pressure regulation system in combination with the housing further exerts a pressure of no more than about 280 kPa, no more than about 250 kPa, no more than about 200 kPa, or no more than about 180 kPa on the cell stack during the operational life of the energy storage device. In some embodiments, the pressure regulation system in combination with the housing exerts a pressure of no less than about 30 kPa on the cell stack during the operational life of the energy storage device. Alternatively, the pressure regulation system in combination with the housing exerts a pressure of no less than about 35 kPa, no more than about 40 kPa, or no more than about 45 kPa, Depending on the electrodes and the separator of the cell, the initial pressure and the maximum pressure may vary. When the initial pressure exerted on the cell stack is on the lower end, the maximum pressure exerted should also be on the lower end.
Preferably, the pressure regulation system in combination with the housing would keep the expansion of the cell stack under about 15% from 0% state of charge (SOC) to 100% SOC. More preferably, the expansion of the cell stack may be kept under about 10%, about 8%, about 6%, about 4%, about 3%, or about 2%. The expansion of the cell stack may be between about 2% and about 15%, between about 3% and about 15%, between about 3% and about 12%, between about 3% and about 10%, or between about 3% and about 8%.
The lifetime expansion of the cell at 100% SOC may be kept under about 20%, under about 18%, under about 15%, under about 12%, or under about 10% by the pressure regulation system in combination with the housing. In some implementations, the lifetime expansion of the cell at 100% SOC may be between about 5% and about 20%, between about 5% and about 18%, between about 5% and about 15%, between about 5% and about 12%, or between about 5% and about 10%.
The energy storage device may be a lithium ion battery module. Two or more lithium ion battery energy storage devices surrounded by a packaging material form a battery pack. The battery pack can be incorporated into a vehicle and can power the vehicle and/or electrical components of a vehicle.
Cycle performances of the lithium ion batteries with various pressure regulating system parameters were obtained by measuring the discharge capacity of the battery from the beginning to the end of cycle life (500 cycles). The lithium ion cell used in the tests are as follows:
Cycle performance of the lithium ion battery due to the pressure effect was investigated. The cells with spring layers in between adjacent cells were clamped in between two metal plates held together with screws. A closed-cell silicone foam (Saint-Gobain® Norseal® F-20) with a thickness of 1.6 mm was used as the spring layer. A certain initial pressure on the cells at the beginning of cycle life was set for each battery module (at about 30-50% SOC), and the cells were charged at 1 C to 4.2V, and then discharged at 0.5 C for each cycle. The results show the capacity degradation (cycle life) of the cells at various initial pressure.
Cycle performance of lithium ion batteries with several different spring layers was tested. The discharge capacity of the batteries with different spring layer materials, thicknesses, number of layers of the spring layer material was measured from the beginning of life (i.e., after formation and degassing) to the end of life (i.e., 500 cycles). Some tests were with a higher 4 C charge rate. The capacity retention results are shown in
The results indicated that polyurethane, silicone, and neoprene-SBR as a spring layer work well. In addition, charging at 1 C (compared to 4 C) resulted in a better capacity retention.
As seen from Table 1 below, for groups 1 and 2 cell expansion or swelling is dependent on initial applied pressure. Between group 2 and 9 we demonstrate effect of foam pad type (with different compression vs pressure response) on swelling. Comparing groups 4 vs. 5 and 9 vs. 10 the effect of initial cell thickness in cell expansion can be seen. Finally comparing groups 7 vs. 19 we demonstrate effect of charge rate on cell expansion. Similarly, effect of the foam pad material, charge rate, initial force and cell thickness on capacity retention can also be seen in the table below.
The test conditions for high temperature cycling are summarized in Table 2 below.
For high temperature cycling its important to select spring layer materials that demonstrate excellent compression set resistance. In this case silicone and certain grades of polyurethane, such as PORON®, show excellent recovery, spring-back behavior, to their original thickness after they are subjected to compression set resistance test.
Compression set test: The test measures how much a material does not rebound after compression in percentage. The foam thickness is measured prior to the test. Then the foam is compressed to between two clamps and stored at a high temperature, such as 45° C. or 60° C., for a length of time, such as 24 hours or 1 week. The foam is then unclamped and the foam thickness is measured again and compared to the original thickness. The compression set is calculated by dividing the thickness that did not rebound by the thickness that was deflected. The lower the percentage, the better the material resists permanent deformation under a given deflection and temperature range.
As shown in
Various embodiments have been described above. Although the invention has been described with reference to these specific embodiments, the descriptions are intended to be illustrative and are not intended to be limiting. Various modifications and applications may occur to those skilled in the art without departing from the true spirit and scope of the invention as defined in the appended claims.